Classifications

• • D—TEXTILES; PAPER
  • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
  • D21C—PRODUCTION OF CELLULOSE BY REMOVING NON-CELLULOSE SUBSTANCES FROM CELLULOSE-CONTAINING MATERIALS; REGENERATION OF PULPING LIQUORS; APPARATUS THEREFOR
  • D21C9/00—After-treatment of cellulose pulp, e.g. of wood pulp, or cotton linters ; Treatment of dilute or dewatered pulp or process improvement taking place after obtaining the raw cellulosic material and not provided for elsewhere
  • D21C9/001—Modification of pulp properties
  • D21C9/007—Modification of pulp properties by mechanical or physical means
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61P—SPECIFIC THERAPEUTIC ACTIVITY OF CHEMICAL COMPOUNDS OR MEDICINAL PREPARATIONS
  • A61P17/00—Drugs for dermatological disorders
  • A61P17/02—Drugs for dermatological disorders for treating wounds, ulcers, burns, scars, keloids, or the like
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L1/00—Compositions of cellulose, modified cellulose or cellulose derivatives
  • C08L1/02—Cellulose; Modified cellulose
• • D—TEXTILES; PAPER
  • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
  • D21C—PRODUCTION OF CELLULOSE BY REMOVING NON-CELLULOSE SUBSTANCES FROM CELLULOSE-CONTAINING MATERIALS; REGENERATION OF PULPING LIQUORS; APPARATUS THEREFOR
  • D21C5/00—Other processes for obtaining cellulose, e.g. cooking cotton linters ; Processes characterised by the choice of cellulose-containing starting materials
  • D21C5/005—Treatment of cellulose-containing material with microorganisms or enzymes
• • D—TEXTILES; PAPER
  • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
  • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
  • D21H11/00—Pulp or paper, comprising cellulose or lignocellulose fibres of natural origin only
  • D21H11/16—Pulp or paper, comprising cellulose or lignocellulose fibres of natural origin only modified by a particular after-treatment
  • D21H11/18—Highly hydrated, swollen or fibrillatable fibres
• • D—TEXTILES; PAPER
  • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
  • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
  • D21H11/00—Pulp or paper, comprising cellulose or lignocellulose fibres of natural origin only
  • D21H11/16—Pulp or paper, comprising cellulose or lignocellulose fibres of natural origin only modified by a particular after-treatment
  • D21H11/20—Chemically or biochemically modified fibres
• • D—TEXTILES; PAPER
  • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
  • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
  • D21H17/00—Non-fibrous material added to the pulp, characterised by its constitution; Paper-impregnating material characterised by its constitution
  • D21H17/005—Microorganisms or enzymes
• • D—TEXTILES; PAPER
  • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
  • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
  • D21H17/00—Non-fibrous material added to the pulp, characterised by its constitution; Paper-impregnating material characterised by its constitution
  • D21H17/63—Inorganic compounds
• • D—TEXTILES; PAPER
  • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
  • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
  • D21H17/00—Non-fibrous material added to the pulp, characterised by its constitution; Paper-impregnating material characterised by its constitution
  • D21H17/63—Inorganic compounds
  • D21H17/64—Alkaline compounds
• • D—TEXTILES; PAPER
  • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
  • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
  • D21H17/00—Non-fibrous material added to the pulp, characterised by its constitution; Paper-impregnating material characterised by its constitution
  • D21H17/63—Inorganic compounds
  • D21H17/67—Water-insoluble compounds, e.g. fillers, pigments
  • D21H17/675—Oxides, hydroxides or carbonates
• • D—TEXTILES; PAPER
  • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
  • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
  • D21H17/00—Non-fibrous material added to the pulp, characterised by its constitution; Paper-impregnating material characterised by its constitution
  • D21H17/71—Mixtures of material ; Pulp or paper comprising several different materials not incorporated by special processes
  • D21H17/74—Mixtures of material ; Pulp or paper comprising several different materials not incorporated by special processes of organic and inorganic material
• • D—TEXTILES; PAPER
  • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
  • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
  • D21H21/00—Non-fibrous material added to the pulp, characterised by its function, form or properties; Paper-impregnating or coating material, characterised by its function, form or properties
  • D21H21/14—Non-fibrous material added to the pulp, characterised by its function, form or properties; Paper-impregnating or coating material, characterised by its function, form or properties characterised by function or properties in or on the paper
  • D21H21/18—Reinforcing agents
• • D—TEXTILES; PAPER
  • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
  • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
  • D21H25/00—After-treatment of paper not provided for in groups D21H17/00 - D21H23/00
  • D21H25/02—Chemical or biochemical treatment

Definitions

• the present invention relates to a process for the production of gel-based composite materials, the materials obtained by this process as well as the use thereof in several applications.
• a composite material is basically a combination of two or more materials, each of which retains its own distinctive properties. The resulting material has characteristics that are not characteristic of the components in isolation. Most commonly, composite materials have a bulk phase, which is continuous, called the matrix; and a dispersed, non-continuous, phase called the reinforcement. Some other examples of basic composites include concrete (cement mixed with sand and aggregate), reinforced concrete (steel rebar in concrete), and fibreglass (glass strands in a resin matrix).
• reinforcing materials are strong, while the matrix is usually a ductile, or tough, material. If the composite is designed and fabricated correctly, it combines the strength of the reinforcement with the toughness of the matrix to achieve a combination of desirable properties not available in any single conventional material. For example: polymer/ceramic composites have a greater modulus than the polymer component, but aren't as brittle as ceramics.
• the reinforcement material is of primary importance in the strengthening mechanism of a composite, it is convenient to classify composites according to the characteristics of the reinforcement.
• the following three categories are commonly used: a) "fibre reinforced", wherein the fibre is the primary load-bearing component.
• the strength of the composite depends primarily on the amount, arrangement and type of fibre (or particle) reinforcement in the resin.
• the composite is often formulated with fillers and additives that change processing or performance parameters.
• Advanced composites utilize a combination of resins and fibres, customarily carbon/graphite, kevlar, or fibreglass with an epoxy resin.
• the fibres provide the high stiffness, while the surrounding polymer resin matrix holds the structure together.
• the fundamental design concept of composites is that the bulk phase accepts the load over a large surface area, and transfers it to the reinforcement material, which can carry a greater load.
• These materials were first developed for use in the aerospace industry because for certain application they have a higher stiffness to weight or strength-to-weight ratio than metals. This means metal parts can be replaced with lighter weight parts manufactured from advanced composites.
• Cellulose is the structural component of the primary cell wall of green plants and is the most common organic compound on Earth. It is of high interest in many applications and industries.
• Pulp fibres are built up mainly from cellulose and other organic components (hemicellulose and lignin).
• the cellulose macromolecules (composed of 1-4 glycosidic linked ⁇ -D-Glucose molecules) are linked together by hydrogen bonds to form a so called primary fibril (micelle) which has crystalline and amorphous domains.
• Several primary fibrils (around 55) form a so called microfibril. Around 250 of these microfibrils form a fibril.
• the fibrils are arranged in different layers (which can contain lignin and/or hemicellulose) to form a fibre.
• the individual fibres are bound together by lignin as well.
• lignin When fibres become refined under applied energy they become fibrillated as the cell walls are broken and torn into attached strips, i.e. into fibrils. If this breakage is continued to separate the fibrils from the body of the fibre, it releases the fibrils.
• the breakdown of fibres into microfibrils is referred to as "microfibrillation”. This process may be continued until there are no fibres left and only fibrils of nano size (thickness) remain.
• nano-fibrillar gel cellulose fragments or nano-fibrillar gels.
• the breakdown to primary fibrils may be referred to as "nano- fibrillation", where there may be a smooth transition between the two regimes.
• the primary fibrils form in an aqueous environment a gel (meta stable network of primary fibrils) which may be referred to as "nano-fibrillar gel".
• the gel formed from the nano-fibrils can be considered to contain nanocellulose.
• Nano-fibrillar gels are desirable as they usually contain very fine fibrils, considered to be constituted in part of nanocellulose, showing a stronger binding potential to themselves, or to any other material present, than do fibrils which are not so fine or do not exhibit nanocellulosic structure.
• cellulose gels can be formed into composite materials, which can be produced easier/faster by the addition of fillers and/or pigments to such gels, and result in an improved rurraability, and which are environmentally friendlier compared with many other composite materials.
• a process for the production of composite materials comprising nano-fibrillar cellulose gels, which is characterized by the following steps: a) providing cellulose fibres;
• step c) combining the cellulose fibres of step a) and the at least one filler and/or pigment of step b);
• step f) combining the gel of step d) with the at least one further filler and/or pigment of step e).
• Nano-fibrillar cellulose in the context of the present invention means fibres, which are at least partially broken down to primary fibrils. If these primary fibrils are in an aqueous environment, a gel (meta stable network of primary fibrils considered in the limit of fineness to be essentially nanocellulose) is formed, which is designated as "nano-fibrillar gel", wherein there is a smooth transition between nano fibres and nano-fibrillar gel, comprising nano-fibrillar gels containing a varying extent of nano- fibrils, all of which are comprised by the term nano-fibrillar cellulose gels according to the present invention.
• nano-fibrillar gel metal stable network of primary fibrils considered in the limit of fineness to be essentially nanocellulose
• fibrillating in the context of the present invention means any process which predominantly breaks down the fibres and fibrils along their long axis resulting in the decrease of the diameter of the fibres and fibrils, respectively.
• the fibrillation of cellulose fibres in the presence of at least one filler and/or pigment provides a nano-fibrillar cellulose gel.
• the fibrillation is performed until the gel is formed, wherein the formation of the gel is verified by the monitoring of the viscosity in dependence of the shearing rate.
• a certain curve reflecting a decrease of the viscosity is obtained.
• Cellulose fibres which can be used in the process of the present invention may be such contained in natural, chemical, mechanical, chemimechanical,
• thermomechanical pulps are Especially useful are pulps selected from the group comprising eucalyptus pulp, spruce pulp, pine pulp, beech pulp, hemp pulp, cotton pulp, bamboo pulp, bagasse, and mixtures thereof.
• all or part of this cellulose fibre may be issued from a step of recycling a material comprising cellulose fibres.
• the pulp may also be recycled and/or deinked pulp.
• the size of the cellulose fibres in principle is not critical.
• Useful in the present invention generally are any fibres commercially available and processable in the device used for their fibrillation.
• cellulose fibres may have a length of from 50 mm to 0.1 ⁇ .
• Such fibres, as well as such having a length of preferably 20 mm to 0.5 ⁇ , more preferably from 10 mm to 1 mm, and typically from 2 to 5 mm, can be advantageously used in the present invention, wherein also longer and shorter fibres may be useful.
• the cellulose fibres are provided in the form of a suspension, especially an aqueous suspension.
• a suspension especially an aqueous suspension.
• such suspensions have a solids content of from 0.2 to 35 wt-%, more preferably 0.25 to 10 wt-%, even more preferably 0.5 to 5 wt-%, especially 1 to 4 wt-%, most preferably 1.3 to 3 wt-%, e.g. 1.5 wt-%.
• the at least one filler and/or pigment of steps b) and e) are independently selected from the group comprising precipitated calcium carbonate (PCC); natural ground calcium carbonate (GCC); surface modified calcium carbonate; dolomite; talc;
• Precipitated calcium carbonate which may have vateritic, calcitic or aragonitic crystal structure, and/or natural ground calcium carbonate, which may be selected from marble, limestone and/or chalk, are especially preferred.
• ultrafine discrete prismatic, scalenohedral or rhombohedral precipitated calcium carbonate may be advantageous.
• the filler(s) and/or pigment(s) can be provided in the form of a powder, although they are preferably added in the form of a suspension, such as an aqueous
• the solids content of the suspension is not critical as long as it is a pumpable liquid.
• the filler and/or pigment particles of step b) have a median particle size of from 0.01 to 15 ⁇ , preferably 0.1 to 10 ⁇ , more preferably 0.3 to 5 ⁇ , especially from 0.5 to 4 um and most preferably 0.7 to 3.2 ⁇ ⁇ ⁇ , e.g. 2 ⁇ .
• a Sedigraph 5100 device from the company Micromeritics, USA was used. The measurement was performed in an aqueous solution of 0.1 wt-% Na 4 P 2 0 7 . The samples were dispersed using a high-speed stirrer and ultrasound.
• a Malvern Zetasizer Nano ZS from the company Malvern, UK was used. The measurement was performed in an aqueous solution of 0.1 wt% Na 4 P 2 0 7 . The samples were dispersed using a high-speed stirrer and ultrasound.
• the filler(s) and/or pigment(s) added in step e) is a rather fine product in terms of the particle size, and especially preferably comprises at least a fraction of particles having a median diameter d 50 in the nanometer range, contrary to the pigment(s) and/or filler(s) used in the gel formation, which are rather coarse ones.
• the filler and/or pigment particles of step e) have a median particle size of from 0.01 to 5 ⁇ , preferably 0.05 to 1.5 ⁇ , more preferably 0.1 to 0.8 ⁇ and most preferably 0.2 to 0.5 ⁇ , e.g. 0.3 ⁇ , wherein the particle size is determined as mentioned above.
• the filler(s) and/or pigment(s) may be associated with dispersing agents such as those selected from the group comprising homopolymers or copolymers of polycarboxylic acids and/or their salts or derivatives such as esters based on, e.g., acrylic acid, methacrylic acid, maleic acid, fumaric acid, itaconic acid; e.g. acryl amide or acrylic esters such as methylmethacrylate, or mixtures thereof; alkali polyphosphates, phosphonic-, citric- and tartaric acids and the salts or esters thereof; or mixtures thereof.
• dispersing agents such as those selected from the group comprising homopolymers or copolymers of polycarboxylic acids and/or their salts or derivatives such as esters based on, e.g., acrylic acid, methacrylic acid, maleic acid, fumaric acid, itaconic acid; e.g. acryl amide or acrylic esters such as methylmethacrylate
• the combination of fibres and at least one filler and/or pigment of steps b) and/or e) can be carried out by adding the filler and/or pigment to the fibres in one or several steps.
• the fibres can be added to the filler and/or pigment in one or several steps.
• the filler and/or pigment of step b) as well as the fibres can be added entirely or in portions before or during the fibrillating step. However, the addition before fibrillating is preferred.
• the size of the filler(s) and/or pigment(s) as well as the size of the fibres can change.
• the weight ratio of fibres to flller(s) and/or pigment(s) of step b) on a dry weight basis is from 1 :33 to 10: 1, more preferably 1 : 10 to 7:1, even more preferably 1 :5 to 5:1, typically 1 :3 to 3 :1, especially 1 :2 to 2:1 and most preferably 1 :1.5 to 1.5:1 , e.g. 1 :1.
• the dosage of filler and/or pigment in step b) may be critical. If there is too much of the filler and/or pigment, this may influence the formation of the gel. Thus, if no gel formation is observed in specific combination, it might be necessary to reduce the amount of filler and/or pigment.
• the combination is stored for 2 to 12 hours, preferably 3 to 10 hours, more preferably 4 to 8 hours, e.g. 6 hours, prior to fibrillating it, as this ideally results in swelling of the fibres facilitating the fibrillation.
• Fibre swelling may be facilitated by storage at increased pH, as well as by addition of cellulose solvents like e.g. copper(II)ethylenedi amine, iron-sodium-tartrate or lithium-chlorine/dimethylacetamine, or by any other method known in the art.
• cellulose solvents like e.g. copper(II)ethylenedi amine, iron-sodium-tartrate or lithium-chlorine/dimethylacetamine, or by any other method known in the art.
• Fibrillating is carried out by means of any device useful therefore.
• the device is a homogenizer. It may also be an ultra fine friction grinder such as a Supermasscolloider from Masuko Sangyo Co. Ltd, Japan or one as described in US 6,214,163 or US 6,183,596.
• Suitable for the use in the present invention are any commercially available homogenizers, especially high pressure homogenizers, wherein the suspensions are pressed under high pressure through a restricted opening, which may comprise a valve, and are discharged from the restricted opening at high pressure against a hard impact surface directly in front of the restricted opening.
• the pressure may be generated by a pump such as a piston pump, and the impact surface may comprise an impact ring extending around the annular valve opening.
• homogenizer which can be used in the present invention is Ariete NS2006L of GEA Niro Soavi.
• homogenizers such as of the APV Gaulin Series, HST HL Series or the Alfa Laval SHL Series can be used.
• the weight ratio of fibres to filler and/or pigment of step e) on a dry weight basis is from 1 :9 to 99:1, preferably from 1 :3 to 9:1 , more preferably from 1 :2 to 3:1 , e.g. 2:1.
• the filler and/or pigment of steps b) and e) are present in an amount of from 10 wt-% to 95 wt-%, preferably from 15 wt-% to 90 wt-%, more preferably from 20 to 75 wt-%, even more preferably from 25 wt-% to 67 wt-%, especially from 33 to 50 wt.-% on a dry weight basis of the composite material.
• the combination of the gel of step d) with the at least one further filler and/or pigment of step e) may be carried out just by mixing the combination, e.g. by means of a spatula.
• the resulting combination may be dewatered.
• any commonly used method of dewatering known to the person skilled in the art may be used, such as e.g. heat drying, pressure drying, vacuum drying, freeze drying, or drying under supercritical conditions.
• the dewatering step may be carried out in well-known devices such as in a filter press, e.g. as described in the Examples.
• nano -fibrillar cellulose gels as defined above for the production of a compacted composite material is a further aspect of the invention, wherein the gel is combined with at least one further filler and/or pigment and the resulting
• Another aspect of the present invention is the composite material obtained by the process according to the invention, or by the use of the nano-fibrillar cellulose gels for the production of the composite material as mentioned.
• the composite material can be advantageously used in applications such as in plastics, paints, rubber, concrete, ceramics, pannels, housings, foils, films, coatings, extrusion profiles, adhesives, food, or in wound-healing applications, and can readily replace certain materials such as plastics used as e.g. construction material, packaging, etc.
• OC-GCC Omyacarb 10-AV available from Omya AG; Fine calcium carbonate powder manufactured from a high purity, white marble; the weight median particle size is 10 ⁇ measured by Malvern Mastersizer X.
• HO-ME Hydrocarb ® HO - ME available from Omya AG; Selected, natural ground calcium carbonate (marble), microcrystalline, rhombohedral particle shape of high fineness in the form of a pre-dispersed slurry (solids content 62 wt-%); the weight median particle size is 0,8 ⁇ measured by Sedigraph 5100.
• Nano-GCC Natural ground calcium carbonate (marble from Vermont); dispersed slurry (solids content 50 wt-%); the volume median particle size is d 50 of 246 nm measured by Malvern Zetasizer Nano ZS.
• Pulp Eucalyptus pulp with 25 °SR.
• the resulting mixtures subsequently were fibriUated in an ultra-fme friction grinder (Supermasscolloider from Masuko Sangyo Co. Ltd, Japan (Model MKCA 6-2) in single passes at a "gap" of -50 ⁇ (dynamic 0-point) with the following setup: 5 passes at 2500 rpm,
• the gel of sample 1 was mixed with the corresponding amount of additional GCC as mentioned in Table 2 and blended by hand with a spatula. Subsequently, the formulations were put into a small filter press (filter paper of Whatman Schleicher & Schuell, 589/2, white ribbon; filter press: fann filter press, series 3000, fann instrument company, Houston Texas, USA) in such amounts that a final thickness of the specimen of about 3 mm (calculated via densities) was achieved.
• a PMMA disc thickness: 10 mm, diameter: 78 mm (fitting the inner diameter of the filter press) was placed on top of the formulation which again was covered by additional material of the same formulation (around 10-20 wt% of the amount of formulation already present). The filter press then was closed and the following pressure profile was applied:
• the "semi-dry" disc solids content: about 50 wt%) was taken out of the filter press and cut into five identical rectangles (40 mm x 10 mm). These rectangles were placed between two filter papers and two aluminium plates weighted with steel balls (about 3000 g), and dried in an oven at about 80 °C over night.

Landscapes

• Chemical & Material Sciences (AREA)
• Life Sciences & Earth Sciences (AREA)
• Engineering & Computer Science (AREA)
• Health & Medical Sciences (AREA)
• Inorganic Chemistry (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Organic Chemistry (AREA)
• Medicinal Chemistry (AREA)
• Biochemistry (AREA)
• Mechanical Engineering (AREA)
• Wood Science & Technology (AREA)
• General Chemical & Material Sciences (AREA)
• Microbiology (AREA)
• Polymers & Plastics (AREA)
• Bioinformatics & Cheminformatics (AREA)
• Dermatology (AREA)
• Nuclear Medicine, Radiotherapy & Molecular Imaging (AREA)
• Pharmacology & Pharmacy (AREA)
• Animal Behavior & Ethology (AREA)
• General Health & Medical Sciences (AREA)
• Public Health (AREA)
• Veterinary Medicine (AREA)
• Compositions Of Macromolecular Compounds (AREA)
• Paper (AREA)
• Processes Of Treating Macromolecular Substances (AREA)
• Paints Or Removers (AREA)
• Adhesives Or Adhesive Processes (AREA)
• Wrappers (AREA)
• Medicinal Preparation (AREA)
• Materials For Medical Uses (AREA)
• Silicon Compounds (AREA)

Priority Applications (23)

Applications Claiming Priority (4)

Related Child Applications (2)

Publications (1)

Family

ID=42316028

Family Applications (1)

Country Status (26)

Cited By (8)

Families Citing this family (21)

Citations (4)

Family Cites Families (273)

• 2010
  • 2010-04-27 PT PT101611739T patent/PT2386683E/pt unknown
  • 2010-04-27 ES ES10161173.9T patent/ES2464733T3/es active Active
  • 2010-04-27 DK DK10161173.9T patent/DK2386683T3/da active
  • 2010-04-27 SI SI201030619T patent/SI2386683T1/sl unknown
  • 2010-04-27 PL PL10161173T patent/PL2386683T3/pl unknown
  • 2010-04-27 EP EP10161173.9A patent/EP2386683B1/en active Active
• 2011
  • 2011-04-25 TW TW100114241A patent/TWI534322B/zh not_active IP Right Cessation
  • 2011-04-26 CN CN201180020949.2A patent/CN102869831B/zh not_active Expired - Fee Related
  • 2011-04-26 SI SI201131302T patent/SI2563967T1/sl unknown
  • 2011-04-26 EP EP17188196.4A patent/EP3266931B1/en active Active
  • 2011-04-26 CA CA2796132A patent/CA2796132C/en active Active
  • 2011-04-26 RU RU2012150441/12A patent/RU2566894C2/ru active
  • 2011-04-26 AU AU2011246521A patent/AU2011246521B2/en not_active Ceased
  • 2011-04-26 JP JP2013506620A patent/JP5961605B2/ja not_active Expired - Fee Related
  • 2011-04-26 PT PT117194993T patent/PT2563967T/pt unknown
  • 2011-04-26 WO PCT/EP2011/056540 patent/WO2011134938A1/en not_active Ceased
  • 2011-04-26 DK DK11719499.3T patent/DK2563967T3/en active
  • 2011-04-26 MY MYPI2012004747A patent/MY159207A/en unknown
  • 2011-04-26 PL PL11719499T patent/PL2563967T3/pl unknown
  • 2011-04-26 SG SG2012075610A patent/SG184556A1/en unknown
  • 2011-04-26 US US13/640,513 patent/US11155697B2/en not_active Expired - Fee Related
  • 2011-04-26 KR KR1020177017876A patent/KR101902722B1/ko not_active Expired - Fee Related
  • 2011-04-26 ES ES19162026T patent/ES2812241T3/es active Active
  • 2011-04-26 NZ NZ603756A patent/NZ603756A/en not_active IP Right Cessation
  • 2011-04-26 KR KR1020187027003A patent/KR101945685B1/ko not_active Expired - Fee Related
  • 2011-04-26 PL PL17188196T patent/PL3266931T3/pl unknown
  • 2011-04-26 EP EP11719499.3A patent/EP2563967B1/en active Active
  • 2011-04-26 DK DK17188196.4T patent/DK3266931T3/en active
  • 2011-04-26 TR TR2019/04595T patent/TR201904595T4/tr unknown
  • 2011-04-26 ES ES17188196T patent/ES2717327T3/es active Active
  • 2011-04-26 HU HUE11719499A patent/HUE034675T2/en unknown
  • 2011-04-26 EP EP19162026.9A patent/EP3524730B1/en not_active Not-in-force
  • 2011-04-26 HR HRP20171379TT patent/HRP20171379T1/hr unknown
  • 2011-04-26 KR KR1020127030744A patent/KR101753886B1/ko not_active Expired - Fee Related
  • 2011-04-26 BR BR112012027633-6A patent/BR112012027633B1/pt not_active IP Right Cessation
  • 2011-04-26 ES ES11719499.3T patent/ES2642664T3/es active Active
  • 2011-04-26 MX MX2012012449A patent/MX2012012449A/es active IP Right Grant
  • 2011-04-27 UY UY0001033355A patent/UY33355A/es active IP Right Grant
• 2012
  • 2012-10-25 CL CL2012002984A patent/CL2012002984A1/es unknown
• 2016
  • 2016-06-23 JP JP2016124301A patent/JP6224175B2/ja not_active Expired - Fee Related
• 2017
  • 2017-10-03 JP JP2017193239A patent/JP6755848B2/ja not_active Expired - Fee Related
• 2018
  • 2018-03-09 HK HK18103365.1A patent/HK1244038B/en not_active IP Right Cessation
• 2020
  • 2020-02-28 JP JP2020032839A patent/JP7143355B2/ja active Active
• 2021
  • 2021-09-22 US US17/481,627 patent/US20220002523A1/en not_active Abandoned
• 2022
  • 2022-05-30 JP JP2022087468A patent/JP2022116220A/ja active Pending

Patent Citations (5)

Also Published As

Similar Documents

Legal Events