WO2010082454A1 - 高周波焼入れ用鋼 - Google Patents
高周波焼入れ用鋼 Download PDFInfo
- Publication number
- WO2010082454A1 WO2010082454A1 PCT/JP2010/000017 JP2010000017W WO2010082454A1 WO 2010082454 A1 WO2010082454 A1 WO 2010082454A1 JP 2010000017 W JP2010000017 W JP 2010000017W WO 2010082454 A1 WO2010082454 A1 WO 2010082454A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- steel
- less
- content
- present
- induction hardening
- Prior art date
Abstract
Description
本願は、2009年1月16日に、日本に出願された特願2009-007757号に基づき優先権を主張し、その内容をここに援用する。
そこで、被削性と疲労強度を兼備した発明としては、特許文献3および特許文献4がある。特許文献3は、成分を調整して、フェライト組織とパーライト組織との合計の組織分率を90%以上とし、さらにフェライト組織の最大厚みが30μmになるように制御することで、被削性と疲労強度が兼備するという発明である。しかしながら、フェライト組織とパーライト組織との合計の組織分率が90%以上の鋼は多数あるが、それだけでは、被削性の向上は不十分であり、合金元素によるさらなる改良が必要である。特許文献4は、MnSのアスペクト比を10以下に小さくし、さらに鋼材の中心部まで高周波加熱するという条件を加えることで、被削性と疲労強度を向上させるという発明である。このようなMnSのアスペクト比を下げて被削性や疲労強度を上げるという手法は、従来からよく知られた方法である。しかし、この方法では不十分であり、合金元素によるさらなる改良が必要である。また、高周波焼入れ法にも制限を加えるのであれば、実用的な利用は限られてしまうという欠点がある。
さらに、質量%で、Ti:0.004%以上0.10%以下を含有してもよい。
さらに、質量%で、Cr:0.05%以上1.50%以下、及びMo:0.05%以上0.6%以下からなる群から選択された1種または2種の元素を含有してもよい。
さらに、質量%で、Nb:0.005%以上0.2%以下、及びV:0.01%以上1.0%以下からなる群から選択された1種または2種の元素を含有してもよい。
さらに、質量%で、Sb:0.0005%以上0.0150%以下、Sn:0.005%以上2.0%以下、Zn:0.0005%以上0.5%以下、Te:0.0003%以上0.2%以下、Bi:0.005%以上0.5%以下、及びPb:0.005%以上0.5%以下からなる群から選択された1種または2種以上の元素を含有してもよい。
さらに、質量%で、Mg:0.0002%以上0.003%以下、Ca:0.0003%以上0.003%以下、Zr:0.0003%以上0.005%以下、及びREM:0.0003%以上0.005%以下からなる群から選択された1種または2種以上の元素を含有してもよい。
さらに、質量%で、Ni:0.05%以上2.0%以下、およびCu:0.01%以上2.0%以下からなる群から選択された1種または2種の元素を含有してもよい。
従って、本発明では、特に歯車や自動車用のCVTやCVJなどに使用される部品の製造工程を浸炭処理から高周波焼入処理へ転換できる鋼を提供できる。
本発明の鋼成分を限定した理由を説明する。ここで成分の含有単位の%は、質量%を意味する。
Cには、高周波焼入後の表面硬さを確保する作用と鋼(芯部)に所望の強度を確保する作用がある。Cの含有量が0.40%を下回ると、前記作用による所望の効果が得られない。一方、0.75%を越えてCを含有させると、靭性が劣化するようになり、圧延材が置き割れするなど製造上の問題が生じる。従って、C含有量は0.40%~0.75%と定めるが、上記効果をより安定に確保するためには0.50%~0.65%に調整するのが好ましい。
Alは、本発明の鋼において最も重要な元素であるので、詳細に説明する。
C:0.50%以上0.60%以下、Si:0.002%以上0.80%以下、Mn:0.50%以上0.9%以下、S:0.005%以上0.1%以下、Al:0.010%以上3.5%以下、N:0.001%以上0.035%以下、及びP:0.030%以下を含有し、残部としてFeおよび不可避不純物を含むように成分を調整した多数のインゴットを製造して50φの圧延素材を製造した。このように成分調整して圧延素材の硬さを200~220HV程度の範囲内とした。これらの素材から45φ×15mmの円盤試料を作製した。
これらの試料に対し、表1に示す条件で被削性試験(片山 昌 著「失敗しない被削材・工具材の見方・選び方」日刊工業新聞社、東京、2007年発行P.27に記載の試験方法)を行った。一定のドリルの回転速度(m/min)で、総深さ1000mmの穴を円盤試料に開けた。切削中にドリルが破損しなかった場合、新しいドリルを用いて、更に早いドリルの回転速度で総深さ1000mmの穴を開けた。この作業を、切削中にドリルが破損するまで行った。そして、切削中にドリルが破損しなかった回転速度のうち、最大の回転速度(ドリルによる穴の総深さが1000mmに達する最大の切削速度(m/min))を被削性の評価に用いた。これは工具寿命を評価する試験であり、最大の切削速度が速いほど、工具が破損しにくく、鋼が被削性に優れていることが分かる。
上記の実験結果から、工具寿命を向上するためのAl量は、0.10%超3.0%以下とする。
Al2O3は、硬度が約3000HVであり、ハイスドリル工具鋼(硬度約700HV)よりも硬く磨耗しにくい。また、通常、鋼材と工具が同じ材質(鉄)である場合、接触部分で凝着が生じて、工具が磨耗しやすくなる(凝着磨耗)。これに対してAl2O3が介在すると、同じ材質(鉄)同士の接触が低減でき、工具の磨耗を抑制できる。従って、このAl2O3膜が凝着摩耗を抑制することで工具寿命が向上したと推察した。
従来のPbを含む快削鋼では、Pbの融点は約330℃と低いために、切削加工中の昇温により容易に溶融し、工具と切屑の界面で潤滑作用を起こして凝着を抑制する。さらにPbの溶融による延性低下のため、刃先付近での延性破壊を起こしやすくし、切削に必要な塑性加工エネルギーを小さくすることにより被削性が向上する。しかし、健康には好ましくなくPbを使用しない快削元素が求められる。従来のSを含む快削鋼では、MnSが高温で大きく変形して工具と切屑の界面へ付着することによる潤滑作用と、工具刃先においてMnSが破壊の起点となり延性破壊を促進することの二つ効果で被削性が向上する。しかし、MnSは熱間鍛造時に展伸されるので、鍛造方向に対し垂直方向の延靭性などの機械特性を低下させる問題がある。
これに対して、本発明の鋼では、工具表面にAl2O3膜が形成され、工具の磨耗が抑制されると考えられる。
一般に、鋼材の硬さが硬い場合、工具寿命が低下するが、同じ程度の硬さの鋼材を比較すると、本発明の鋼では、工具寿命を延ばす効果がある。
Al量の好ましい範囲は0.11%以上3.0%以下である。より好ましくは、Al量は0.15%以上2.9%以下であり、さらに好ましくは、Al量は0.2%以上1.1%以下である。
Al含有量が多くなると、A1点が高くなるが、Al含有量が3.0%超の場合、高周波焼入れでは相変態が生じなくなってしまう。従って、高周波焼入れの点からも、Al含有量を3.0%以下とする必要がある。
従って、固溶Alの含有量(AlNを除くAl量)が0.1%超であることが好ましい。このため、以下の関係式を満たすことが好ましい。
[%Al]―(27/14)×[%N]―0.001>0.10%
ここで、式中、[ ]は、元素の含有量(質量%)を意味する。また、上記式は、鋼を製造する際に熱処理などを行い、鋼中のNが全てAlと結合していると仮定して得られる式である。
Siは、製鋼時の脱酸材として含有させるとともに鋼材の強度向上元素であり、要求強度に応じてその含有量を調節される。但し、Si含有量は脱酸作用を有効ならしめるためには0.002%以上の含有量が必要である。一方、3.0%超では鋼材の靭性、延性が低くなると同時に、鋼中に硬質介在物が多数生成し、鋼材の被削性も低下する。そのため、Si含有量は0.002%以上3.0%以下と定める。Si量の好ましい範囲は0.3%以上3.0%以下である。より好ましくは、Si量は0.4%以上2.5%以下であり、さらに好ましくは、Si量は0.5%以上2.2%以下である。Si量は0.6%以上2.1%以下にすると、強度に優れる。Si量は0.8%以上2.0%以下にすると、さらに強度に優れる。
Mnは、Siと同様に鋼材の強度向上元素であって、要求強度に応じてその含有量が調節される。従って、この作用を有効ならしめるために0.20%以上の含有量を確保する必要がある。但し、Mn含有量が2.0%超では、焼入性が向上し過ぎて、素材製造時にベイナイト組織あるいは島状マルテンサイト組織の生成が促進され、加工性が低下するようになる。したがって、Mnの範囲は、0.20%以上2.0%以下である。
本実施形態の鋼を切削して部品形状をつくり、その後、高周波焼入する場合、切削工程までは鋼が比較的軟らかく、高周波焼入れにより、所望の硬さとなることが好ましい。このような優れた加工性を実現するためには、Mnの含有量を0.40~1.5%とすることが好ましく、0.45~1.0%とすることが更に好ましい。
Sは、最低限の被削性を確保するために0.002%以上は必要である。一方、Sが0.1%超で含有する場合、靭性や疲労強度の劣化をもたらす。したがって、Sは0.002%以上0.1%以下とする。歯車の用途で用いる場合、S含有量は、好ましくは0.005~0.06%であり、更に好ましくは0.01~0.05%である。
Pは、硬化層の靭性を劣化させる。特にP含有量が0.030%超では、著しい靭性の劣化をもたらすようになるので、P含有量は0.030%以下と定める。P含有量は、好ましくは0.0001%~0.030%であり、更に好ましくは0.0001%~0.020%に調整するのが良い。
0.035%超のNの添加は、熱間脆性を著しく劣化させ、圧延鋼材の製造が極めて困難になる。したがって、Nは0.035%以下に制限する。
また、Nは、Alと反応して、AlNを生成し、結晶粒の粗大化を抑制する効果がある。一般に、高周波加熱は通常の熱処理炉での加熱とは異なり、加熱時間が極めて短時間なため、それ程大きな結晶粒は生成し難い。しかし、結晶粒の微細化を積極的に図りたい場合には、N含有量を0.0001%~0.035%とすることが好ましく、更に好ましくは0.001%~0.015%程度の量のNを添加することが良い。0.002%~0.007%程度の量にすれば、なお好ましい。
B:0.0004%以上0.005%以下
Bは、ふたつの点で重要な元素である。ひとつは、鋼に焼入性を付与する作用である。Bは0.0004%以上あれば、オーステナイト粒界に十分に偏析し、焼入性が発現する。微量で焼入性が得られ、かつ安価な点で有用である。もうひとつは、結晶粒界の強度を高める作用である。表層を高周波焼入により硬化すると、脆化し、結晶粒界で破壊する。Bはこれを抑制する作用がある。この場合もオーステナイト粒界に十分に偏析することが必要であるため、0.0004%以上の添加が必要となる。0.005%超の添加は、かえって鋼材を脆くする。したがって、Bは0.0004%以上0.005%以下とする。
特に、本発明の鋼では、Al含有量が0.1%超であるため、BNが生成しにくく、上記したBの作用効果が得られやすい。
B含有量は、好ましくは、0.0005~0.004%であり、更に好ましくは0.001~0.0035%である。この場合、焼入性にも優れ、機械特性も優れた鋼ができる。
Tiは、ふたつの点で重要な元素である。ひとつは、高周波加熱後の結晶粒径を微細化する作用である。もうひとつは、NをTiNとして析出させることによって、BN生成による固溶B量の減少を抑制する働きである。通常、後者の目的では、Tiの添加量はN量の3.43倍を必要とするが、本発明の鋼では、Alを多く含有しているため、それほどのTi量は必要がない。Ti含有量が0.004%未満では、両者の効果が小さい。一方、Ti含有量が0.10%超では、粗大なTi介在物が生成し、疲労破壊の起点になる。したがって、Ti含有量は、0.004%以上0.10%以下とする。
Ti含有量は、好ましくは、0.005~0.08%であり、更に好ましくは0.01~0.03%である。この場合、固溶Bの焼入性を有効に活用でき、結晶粒微細化もできる。
CrとMoは、鋼材の強度向上元素であって、要求強度および部品の大きさに応じて所定量含有してもよい。
但し、Cr含有量が0.05%未満では、前記作用による所望の効果を得ることができない。一方、Cr含有量が1.50%超では、焼入性が向上し過ぎて、素材(鋼)の製造時にベイナイト組織あるいは島状マルテンサイト組織の生成が促進され、加工性が低下するようになる。従って、添加する際は0.05%以上1.50%以下とする。ただし、高周波加熱時にセメンタイトを容易に溶解させ、固溶Cを均一にする必要がある場合には、Cr含有量を0.05%以上0.2%以下にすることが好ましい。
Moは、0.05%未満では効果が得られない。一方、Mo含有量が0.6%超では、焼入性が向上し過ぎて、素材(鋼)の製造時にベイナイト組織あるいは島状マルテンサイト組織の生成が促進され、加工性が低下するようになる。従って、添加する際は0.05%以上0.6%以下とする。
鋼材の強度を向上させるという目的の場合、CrとMoは共通の作用があるので、いずれか1種または2種を添加すればよい。
NbとVは、鋼中で炭窒化物を析出することにより結晶粒界をピン止めし、結晶粒を微細化させる。その結果、結晶粒界の強度を高める。
Nbが0.005%未満では、析出量が少ないために粒成長の抑制力が足りない、一方、Nbが0.2%超では、鋼の熱間脆性が増し、製造が困難となる。したがって、Nbは0.005%以上0.2%以下とする。
Vが0.01%未満では、析出量が少ないために粒成長の抑制力が足りない。一方、Vが1.0%超では、鋼の熱間脆性が増し、製造が困難となる。したがって、Vは0.01%以上1.0%以下とする。
NbとVは、同様の働きをする元素であるので、いずれか1種または2種を添加すればよい。
NiもCuも鋼の鋼材の強度向上元素であって、要求強度および部品の大きさに応じて所定量添加してもよい。
但し、Ni含有量が0.05%未満では、前記作用による所望の効果を得ることができない。一方、Ni含有量が2.0%超では、焼入性が向上し過ぎて、素材(鋼)の製造時にベイナイト組織あるいは島状マルテンサイト組織の生成が促進され、加工性が低下するようになる。従って、Niは0.05%以上2.0%以下とする。
Cu含有量が0.01%未満では、前記作用による所望の効果を得ることができない。一方、Cu含有量が2.0%超では、焼入性が向上し過ぎて、素材(鋼)の製造時にベイナイト組織あるいは島状マルテンサイト組織の生成が促進され、加工性が低下するようになる。従って、Cuは0.01%以上2.0%以下とする。なお、Cuは熱間脆性を起す弊害もあるので、Cuを添加する場合には、Cuの1/2程度の量のNiを同時に添加することが好ましい。
Sbは、フェライトを適度に脆化し被削性を向上させる。Sb含有量が0.0005%未満では、効果は認められない。またSb含有量が0.0150%を超えると、Sbのマクロ偏析が過多となり、鋼の製造が困難になる。よってSbを添加する場合は、その含有量を0.0005%以上0.0150%以下とする。
Snは、フェライトを脆化させて工具寿命を延ばすと共に、表面粗さを向上させる効果がある。しかしながら、Sn含有量が0.005%未満の場合、その効果は認められない。また、Sn含有量が2.0%超の場合、鋼の製造が困難になる。したがって、Snを添加する場合は、その含有量を0.005%以上2.0%以下とする。
Znは、フェライトを脆化させて工具寿命を延ばすと共に、表面粗さを向上させる効果がある。しかしながら、Zn含有量が0.0005%未満の場合、その効果は認められない。また、Zn含有量が0.5%超の場合、鋼の製造が困難になる。よって、Znを添加する場合は、その含有量を0.0005%以上0.5%以下とする。
Teは、被削性向上元素である。また、MnTeを生成したり、MnSと共存することでMnSの変形能を低下させ、MnS形状の伸延を抑制する働きがある。このように、Teは異方性の低減に有効な元素である。しかしながら、Te含有量が0.0003%未満の場合、これらの効果は認められない。また、Te含有量が0.2%を超えると、その効果が飽和するだけでなく、熱間延性が低下して疵の原因となる。よって、Teを添加する場合は、その含有量を0.0003%以上0.2%以下とする。
Biは、被削性向上元素である。しかしながら、Bi含有量が0.005%未満の場合、その効果が得られない。また、Bi含有量が0.5%超の場合、被削性向上効果が飽和するだけでなく、熱間延性が低下して疵の原因となる。よって、Biを添加する場合は、その含有量を0.005%以上0.5%以下とする。
Pbは、被削性向上元素である。しかしながら、Pb含有量が0.005%未満の場合、その効果が認められない。また、Pb含有量が0.5%超の場合、被削性向上効果が飽和するだけでなく、熱間延性が低下して疵の原因となる。よって、Pbを添加する場合は、その含有量を0.005%以上0.5%以下とする。
鋼部品中に存在する伸長したMnSは、鋼部品の機械特性に異方性を与えたり、金属疲労の破壊起点になるという欠点がある。部品によっては、疲労強度を極度に要求される場合があり、この場合には、MnSの形態を制御するため、Mgの添加が有効である。Mgは、鋼中で(Mg,Mn)Sを生成し、硬質になるため、圧延中に延伸しないことから形態制御できる。MnSを形態制御するためには、Mgは少なくとも0.0002%含有する必要がある。一方、Mg含有量が0.003%超では、酸化物を粗大化させ、かえって疲労強度を劣化させる。よって、Mgを添加する場合は、その含有量を0.0002~0.003%とする。
CaもMnSを形態制御するのに役立つ元素である。Caは、鋼中で(Ca,Mn)Sを生成し、硬質になるため、圧延中に延伸しないことから形態制御できる。MnSを形態制御するためには、Caは少なくとも0.0003%含有する必要がある。一方、Ca含有量が0.003%超では、酸化物を粗大化させ、かえって疲労強度を劣化させる。よって、Caを添加する場合は、その含有量を0.0003~0.003%とする。
ZrもMnSを形態制御するのに有効な元素である。Zrは、鋼中で(Zr,Mn)Sを生成し、硬質になるため、圧延中に延伸しないことから形態制御できる。MnSを形態制御するためには、Zrは少なくとも0.0003%含有する必要がある。一方、Zr含有量が0.005%超では、酸化物を粗大化させ、かえって疲労強度を劣化させる。よって、Zrを添加する場合は、その含有量を0.0003~0.005%とする。
REMもまたMnSを形態制御するのに効果的な元素である。REMは、鋼中で(REM,Mn)Sを生成し、硬質になるため、圧延中に延伸しないことから形態制御できる。MnSを形態制御するためには、REMは少なくとも0.0003%含有する必要がある。一方、REM含有量が0.005%超では、酸化物を粗大化させ、かえって疲労強度を劣化させる。よって、REMを添加する場合は、その含有量を0.0003~0.005%とする。
なお、REMは、希土類金属元素を示し、Sc,Y,La,Ce,Pr,Nd,Pm,Sm,Eu,Gd,Tb,Dy,Ho,Er,Tm,Yb,及びLuから選択される1種以上である。
以下、実施例に基づいて本発明を詳細に説明する。
表2~4に示す鋼を溶解、圧延し、50φの棒鋼を作製した。
一方で、これらの素材(圧延後の鋼材)から45φ×15mmの円盤試料を作製した。これらの円盤試料に対し、表1に示す条件で被削性試験を行った。前述したように、ドリルによる穴の総深さが1000mmに達する最大の切削速度(m/min)を求め、被削性を評価した。これは工具寿命を評価する試験である。
一方、これらの素材から17.5φ×52.5mmの円柱試料を作製した。これらの円柱試料に対して、硬化層深さが2mmになる条件にて高周波焼入を行った。その後、横断面を切断、研磨し、表層から0.5mm部位に300gの荷重でビッカース硬さを10点測定し、表層硬さの平均値を求めた。これは、特に歯車などの各種部品に使われる場合に、高周波焼入れ用鋼の強度を評価する指標である。
試験によって得られた圧延鋼材の平均硬さ、工具寿命および高周波焼入後の表層平均硬さの結果を表5,6に示す。
試番1A,1Bは本発明例である。工具寿命が優れ、かつ表層硬さもHV600以上あり、十分な強度特性をもたらす鋼材である。試番1C,1Dは比較例である。試番1Cは、Al量が本発明範囲を下回ったため、工具寿命が低下した例である。試番1Dは、Al量が本発明範囲内であるので工具寿命は優れるが、C量が本発明範囲を下回ったため、高周波焼入後の表層硬さが低くなった例である。
試番2Aは本発明例である。Al量が本発明範囲内であり、かつPbも含有するので、工具寿命が優れる。かつ表層硬さもHV600以上あり、十分な強度特性をもたらす鋼材である。試番2Bは比較例である。Al量が本発明範囲を下回ったため、工具寿命が劣化した例である。
試番3A,3B,3C,3Dは本発明例である。工具寿命が優れ、かつ表層硬さもHV600以上あり、十分な強度特性をもたらす鋼材である。試番3Eは比較例である。Al量が本発明範囲を下回ったため、工具寿命が劣化した例である。
試番4Aは本発明例である。Al量が本発明範囲内であり、かつSbも含有するので、工具寿命が優れる。かつ表層硬さもHV600以上あり、十分な強度特性をもたらす鋼材である。試番4Bは比較例である。Al量が本発明範囲を下回ったため、工具寿命が劣化した例である。
試番5Aは本発明例である。Al量が本発明範囲内であり、かつBiも含有するので、工具寿命が優れる。かつ表層硬さもHV600以上あり、十分な強度特性をもたらす鋼材である。試番5Bは比較例である。Al量が本発明範囲を下回ったため、工具寿命が劣化した例である。
試番6Aは本発明例である。工具寿命が優れ、かつ表層硬さもHV600以上あり、十分な強度特性をもたらす鋼材である。試番6B比較例である。Al量が本発明範囲を下回ったため、工具寿命が劣化した例である。
試番7Aは本発明例である。Al量が本発明範囲内であり、かつSnも含有するので、工具寿命が優れる。かつ表層硬さもHV600以上あり、十分な強度特性をもたらす鋼材である。試番7Bは比較例である。Al量が本発明範囲を下回ったため、工具寿命が劣化した例である。
試番8A,8B,8C,8D,8E,8F,8G,8Hは本発明例である。工具寿命が優れ、かつ表層硬さもHV600以上あり、十分な強度特性をもたらす鋼材である。試番8iは比較例である。Al量が本発明を下回ったため、工具寿命が劣化した例である。試番8Jは比較例である。Al量が本発明を上回ったため、工具寿命が劣化した例である。
試番9Aは本発明例である。Al量が本発明範囲内であり、かつZnも含有するので、工具寿命が優れる。かつ表層硬さもHV600以上あり、十分な強度特性をもたらす鋼材である。試番9Bは比較例である。Al量が本発明範囲を下回ったため、工具寿命が劣化した例である。
試番10A,10B,10Cは本発明例である。工具寿命が優れ、かつ表層硬さもHV600以上あり、十分な強度特性をもたらす鋼材である。試番10Dは比較例である。Al量が本発明を下回ったため、工具寿命が劣化した例である。
試番11A,11B,11C,11D,11E,11F,11Gは本発明例である。Al量が本発明範囲内であるので、工具寿命が優れる。かつ表層硬さもHV600以上あり、十分な強度特性をもたらす鋼材である。試番11Hは比較例である。Al量が本発明範囲を下回ったため、工具寿命が劣化した例である。
試番12Aは本発明例である。Al量が本発明範囲内であり、かつTeも含有するので、工具寿命が優れる。かつ表層硬さもHV600以上あり、十分な強度特性をもたらす鋼材である。試番12Bは比較例である。Al量が本発明を下回ったため、工具寿命が劣化した例である。
試番13A,13B,13Cは本発明例である。工具寿命が優れ、かつ表層硬さもHV600以上あり、十分な強度特性をもたらす鋼材である。試番13Dは比較例である。Al量が本発明範囲を下回ったため、工具寿命が劣化した例である。試番13Eは比較例である。Siが本発明範囲を超えて含まれるため、硬質介在物が増え、工具寿命が劣化した例である。
試番14は、比較例である。Cが本発明範囲を超えて含有されたため、靭性が劣化し、圧延後置き割れが発生した例である。
Claims (8)
- 質量%で、
C:0.40%以上0.75%以下、
Si:0.002%以上3.0%以下、
Mn:0.20以上2.0%以下、
S:0.002%以上0.1%以下、
Al:0.10%超3.0%以下、
P:0.030%以下、及び
N:0.035%以下を含有し、
残部としてFeおよび不可避不純物を含むことを特徴とする高周波焼入れ用鋼。 - さらに、質量%で、
B:0.0004%以上0.005%以下を含有することを特徴とする請求項1記載の高周波焼入れ用鋼。 - さらに、質量%で、
Ti:0.004%以上0.10%以下を含有することを特徴とする請求項1記載の高周波焼入れ用鋼。 - さらに、質量%で、
Cr:0.05%以上1.50%以下、及び
Mo:0.05%以上0.6%以下からなる群から選択された1種または2種の元素を含有することを特徴とする請求項1記載の高周波焼入れ用鋼。 - さらに、質量%で、
Nb:0.005%以上0.2%以下、及び
V:0.01%以上1.0%以下からなる群から選択された1種または2種の元素を含有することを特徴とする請求項1記載の高周波焼入れ用鋼。 - さらに、質量%で、
Sb:0.0005%以上0.0150%以下、
Sn:0.005%以上2.0%以下、
Zn:0.0005%以上0.5%以下、
Te:0.0003%以上0.2%以下、
Bi:0.005%以上0.5%以下、及び
Pb:0.005%以上0.5%以下からなる群から選択された1種または2種以上の元素を含有することを特徴とする請求項1記載の高周波焼入れ用鋼。 - さらに、質量%で、
Mg:0.0002%以上0.003%以下、
Ca:0.0003%以上0.003%以下、
Zr:0.0003%以上0.005%以下、及び
REM:0.0003%以上0.005%以下からなる群から選択された1種または2種以上の元素を含有することを特徴とする請求項1記載の高周波焼入れ用鋼。 - さらに、質量%で、
Ni:0.05%以上2.0%以下、
およびCu:0.01%以上2.0%以下からなる群から選択された1種または2種の元素を含有することを特徴とする請求項1記載の高周波焼入れ用鋼。