Classifications

• • C—CHEMISTRY; METALLURGY
  • C03—GLASS; MINERAL OR SLAG WOOL
  • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
  • C03C27/00—Joining pieces of glass to pieces of other inorganic material; Joining glass to glass other than by fusing
• • C—CHEMISTRY; METALLURGY
  • C03—GLASS; MINERAL OR SLAG WOOL
  • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
  • C03C27/00—Joining pieces of glass to pieces of other inorganic material; Joining glass to glass other than by fusing
  • C03C27/06—Joining glass to glass by processes other than fusing
  • C03C27/10—Joining glass to glass by processes other than fusing with the aid of adhesive specially adapted for that purpose
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
  • C09J153/00—Adhesives based on block copolymers containing at least one sequence of a polymer obtained by reactions only involving carbon-to-carbon unsaturated bonds; Adhesives based on derivatives of such polymers
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
  • C09J153/00—Adhesives based on block copolymers containing at least one sequence of a polymer obtained by reactions only involving carbon-to-carbon unsaturated bonds; Adhesives based on derivatives of such polymers
  • C09J153/005—Modified block copolymers
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
  • C09J153/00—Adhesives based on block copolymers containing at least one sequence of a polymer obtained by reactions only involving carbon-to-carbon unsaturated bonds; Adhesives based on derivatives of such polymers
  • C09J153/02—Vinyl aromatic monomers and conjugated dienes
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
  • C09J153/00—Adhesives based on block copolymers containing at least one sequence of a polymer obtained by reactions only involving carbon-to-carbon unsaturated bonds; Adhesives based on derivatives of such polymers
  • C09J153/02—Vinyl aromatic monomers and conjugated dienes
  • C09J153/025—Vinyl aromatic monomers and conjugated dienes modified
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
  • C09J5/00—Adhesive processes in general; Adhesive processes not provided for elsewhere, e.g. relating to primers
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10K—ORGANIC ELECTRIC SOLID-STATE DEVICES
  • H10K50/00—Organic light-emitting devices
  • H10K50/80—Constructional details
  • H10K50/84—Passivation; Containers; Encapsulations
  • H10K50/842—Containers
  • H10K50/8426—Peripheral sealing arrangements, e.g. adhesives, sealants
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L2666/00—Composition of polymers characterized by a further compound in the blend, being organic macromolecular compounds, natural resins, waxes or and bituminous materials, non-macromolecular organic substances, inorganic substances or characterized by their function in the composition
  • C08L2666/02—Organic macromolecular compounds, natural resins, waxes or and bituminous materials
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10K—ORGANIC ELECTRIC SOLID-STATE DEVICES
  • H10K2102/00—Constructional details relating to the organic devices covered by this subclass
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10K—ORGANIC ELECTRIC SOLID-STATE DEVICES
  • H10K59/00—Integrated devices, or assemblies of multiple devices, comprising at least one organic light-emitting element covered by group H10K50/00
  • H10K59/80—Constructional details
  • H10K59/87—Passivation; Containers; Encapsulations
  • H10K59/871—Self-supporting sealing arrangements
  • H10K59/8722—Peripheral sealing arrangements, e.g. adhesives, sealants
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/28—Web or sheet containing structurally defined element or component and having an adhesive outermost layer
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/28—Web or sheet containing structurally defined element or component and having an adhesive outermost layer
  • Y10T428/2852—Adhesive compositions

Definitions

• the present invention relates to a method for encapsulating an electronic device according to the preamble of claim 1 and to the use of a pressure-sensitive adhesive for encapsulating an electronic device according to the preamble of claim 6.
• Arrangements and products are designed to be rigid or flexible depending on the desired application, whereby there is an increasing demand for flexible arrangements.
• the preparation of such arrangements takes place for example by printing methods, such as
• PVD Physical vapor deposition
• PECVD plasma enhanced chemical or physical deposition
• sputtering sputtering
• plasma etching vapor deposition
• vapor deposition the patterning is usually done by masks.
• Electrophoretic or electrochromic structures or displays, organic or polymeric light-emitting diodes (OLEDs or PLEDs) in display and display devices or as illumination, electroluminescent lamps, light-emitting electrochemical devices may be mentioned as examples of (commercial) electronic applications which are already interesting in their market potential Cells (LEECs), organic solar cells, preferably dye or polymer solar cells, inorganic solar cells, preferably thin-film solar cells, in particular based on silicon, germanium, copper, indium and selenium, organic field-effect transistors, organic switching elements, organic optical amplifiers, organic laser diodes, organic or inorganic sensors or also organically or inorganically based RFID transponders.
• LECs Light-emitting electrochemical devices
• Permeants can be a variety of low molecular weight organic or inorganic compounds, especially water vapor and oxygen.
• inorganic and / or organic (opto) electronics in particular in organic (opto) electronics, there is a particular need for flexible adhesive solutions which represent a permeation barrier for permeants, such as oxygen and / or water vapor.
• permeants such as oxygen and / or water vapor.
• the flexible adhesive solutions should therefore not only achieve good adhesion between two substrates, but in addition properties such as high shear and peel strength, chemical resistance, aging resistance, high transparency, easy processability and high Fulfill flexibility and flexibility.
• a common approach in the art is therefore to place the electronic assembly between two water vapor and oxygen impermeable substrates. This is followed by a seal at the edges.
• glass or metal substrates are used which offer a high permeation barrier but are very susceptible to mechanical stress. Furthermore, these substrates cause a relatively large thickness of the entire assembly. In the case of metal substrates, there is also no transparency.
• surface substrates such as transparent or non-transparent films, used, which can be multi-layered. Here, both combinations of different polymers, as well as inorganic or organic layers can be used. The use of such surface substrates allows a flexible, extremely thin structure. In this case, a wide variety of substrates, such as films, fabrics, nonwovens and papers or combinations thereof are possible for the various applications.
• a good adhesive for the sealing of (opto) electronic components has a low permeability to oxygen and in particular to water vapor, has sufficient adhesion to the assembly and can flow well on this. Low adhesion to the assembly reduces the barrier effect at the interface, allowing oxygen and water vapor to enter regardless of the properties of the adhesive. Only if the contact between mass and substrate is continuous, the mass properties are the determining factor for the barrier effect of the adhesive.
• the oxygen transmission rate OTR Olygen Transmission Rate
• the water vapor transmission rate WVTR Water Vapor Transmission Rate
• the respective rate indicates the area- and time-related flow of oxygen or water vapor through a film under specific conditions of temperature and partial pressure and possibly other measurement conditions such as relative humidity. The lower these values are, the better the respective material is suitable for encapsulation.
• the indication of the permeation is based not only on the values for WVTR or OTR but also always includes an indication of the mean path length of the permeation, such as. the thickness of the material, or a normalization to a certain path length.
• the permeability P is a measure of the permeability of a body to gases and / or liquids. A low P value indicates a good barrier effect.
• the permeability P is a specific value for a defined material and a defined permeant under steady state conditions at a given permeation path length, partial pressure and temperature.
• the solubility term S in the present case describes the affinity of the barrier adhesive to the permeant. For example, in the case of water vapor, a small value for S of hydrophobic materials is achieved.
• the diffusion term D is a measure of the mobility of the permeant in the barrier material and is directly dependent on properties such as molecular mobility or free volume.
• permeability P usually increases with an increase in molecular mobility, such as when the temperature is increased or the glass transition point is exceeded.
• a low solubility term S is usually insufficient to achieve good barrier properties.
• a classic example of this is in particular siloxane elastomers.
• the materials are extremely hydrophobic (small solubility term), but have a comparatively low barrier to water vapor and oxygen due to their freely rotatable Si-O bond (large diffusion term). For a good barrier effect, therefore, a good balance between solubility term S and diffusion term D is necessary.
• liquid adhesives and adhesives based on epoxides have hitherto been used (WO98 / 21287 A1, US 4,051,195 A, US 4,552,604 A). These have a low diffusion term D due to strong cross-linking. Their main application is edge bonding of rigid arrangements, but also moderately flexible arrangements. Curing takes place thermally or by means of UV radiation. A full-surface bonding is hardly possible due to the shrinkage caused by the curing, since it during the Curing leads to tensions between the adhesive and the substrate, which in turn can lead to delamination.
• liquid adhesives have a number of disadvantages.
• VOCs low-molecular-weight components
• the adhesive must be applied consuming each individual component of the arrangement.
• the purchase of expensive dispensers and fixators is necessary to ensure accurate positioning.
• the type of application also prevents a rapid continuous process and also by the subsequently required lamination step, the achievement of a defined layer thickness and bond width can be made difficult within narrow limits by the low viscosity.
• thermal-crosslinking systems are limited in the low temperature range or in 2-component systems by the pot life, ie the processing time until a gelling has taken place.
• the sensitive (opto) limit electronic structures the usability of such systems - the maximum applicable temperatures (opto) electronic structures are often at 60 0 C, as can already from this temperature is to start a preliminary damage .
• flexible arrangements which contain organic electronics and are encapsulated with transparent polymer films or composites of polymer films and inorganic layers have narrow limits here. This also applies to laminating under high pressure. In order to achieve an improved durability, a waiver of a temperature-stressing step and lamination under lower pressure is advantageous here.
• US 2006/0100299 A1 discloses a UV-curable pressure-sensitive adhesive tape for encapsulating an electronic device.
• the pressure-sensitive adhesive tape has an adhesive based on a combination of a polymer having a softening point greater than 60 ° C., a polymerizable epoxy resin having a softening point of below 30 ° C. and a photoinitiator.
• the polymers may be polyurethane, polyisobutylene, polyacrylonitrile, polyvinylidene chloride, poly (meth) acrylate or polyester, but especially an acrylate.
• adhesive resins, plasticizers or fillers are included.
• Acrylic compounds have a very good resistance to UV radiation and various chemicals, but have very different bond strengths on different substrates. While the bond strength on polar substrates such as glass or metal is very high, the bond strength on nonpolar substrates such as polyethylene or polypropylene is rather low. Here there is a particular danger of diffusion at the interface. In addition, these masses are very polar, which favors a diffusion of water vapor in particular, despite subsequent networking. The use of polymerisable epoxy resins further strengthens this tendency.
• Pressure-sensitive adhesive tapes generally require a certain amount of time, sufficient pressure and a good balance between the viscous component and the elastic component as a result of the relatively high molecular weight polymers, in contrast to liquid adhesives, for good wetting and adhesion to the surface.
• the subsequent crosslinking of the adhesives leads to a shrinkage of the mass. This can lead to a reduction of the adhesion at the interface and in turn increase the permeability.
• WO 2007/087281 A1 discloses a transparent flexible pressure-sensitive adhesive tape based on polyisobutylene (PIB) for electronic applications, in particular OLED.
• PIB polyisobutylene
• polyisobutylene having a molecular weight of more than 500,000 g / mol and a hydrogenated cyclic resin is used.
• the use of a photopolymerizable resin and a photoinitiator is possible.
• Adhesives based on polyisobutylene have a good barrier to water vapor due to their low polarity, but even at high molecular weights, a relatively low cohesiveness, which is why even at room temperature and especially at elevated temperatures, under stress a creeping tendency can be determined and they therefore a have low shear strength.
• the proportion of low molecular weight components can not be reduced arbitrarily, otherwise the adhesion is significantly reduced and the interfacial permeation increases.
• the polarity of the mass is increased again and thus increases the solubility term.
• a PSA with pronounced crosslinking although good cohesion, but the Auffzen is impaired.
• the pressure-sensitive adhesive can not sufficiently adapt to the roughness of a substrate surface, whereby the permeation at the interface is increased.
• a pressure-sensitive adhesive with pronounced crosslinking can only dissipate deformation energy to a lesser extent, as occurs under load. Both phenomena reduce the bond strength.
• a slightly cross-linked pressure-sensitive adhesive can flow well onto rough surfaces and dissipate deformation energy, so that the requirements for the Adhesion can be met, however, the PSA resists due to a reduced cohesion insufficient stress.
• Transfer adhesive is used.
• the adhesive contains a functional
• Sealing of the construction to the outside is another adhesive used with low permeability.
• block copolymers are known from the prior art US 2002/0188053 A1).
• polymers are used on this basis for the sealing of electrophoretic displays by the active substances are coated after their application with a solution of the polymer, which acts after drying as a sealing layer and fixation.
• These polymers have no self-adhesive properties and achieve adhesion to the other components of the electrophoretic display structure only by wetting from the solution. This requires the use of solvents, generates emissions and is difficult to dose.
• the object of the present invention is to provide a method for encapsulating an electronic device against permeants, in particular water vapor and oxygen, that is simple to perform and at the same time achieves good encapsulation. Furthermore, the life of (opto) electronic arrangements should be increased by the use of a suitable, in particular flexible, adhesive.
• the present invention is based initially on the finding that, despite the disadvantages described above, it is possible to use a pressure-sensitive adhesive for encapsulating an electronic arrangement in which the disadvantages described above with regard to PSAs do not occur or only diminish. It has been found that a pressure-sensitive adhesive based on butylene block copolymers, in particular of isobutylene block copolymers, is particularly suitable for encapsulating electronic arrangements. According to the invention, a pressure-sensitive adhesive based on butylene block copolymers is accordingly provided and applied to the areas of the electronic arrangement to be encapsulated. Since the adhesive is a pressure-sensitive adhesive, the application is particularly simple since there is no need for prefixing or the like. Depending on the configuration of the pressure-sensitive adhesive, no subsequent treatment is required. Also, the amount of PSA can be easily metered by administration as a pressure-sensitive adhesive tape and there are no solvent emissions.
• a pressure-sensitive adhesive based on butylene block copolymers means, in particular, a pressure-sensitive adhesive in which the total proportion of the block copolymers is at least 40% by weight, preferably at least 55% by weight.
• PSAs are characterized in particular by their permanent tackiness and flexibility.
• a material that exhibits permanent tack must have a suitable combination of adhesive and cohesive properties at all times. This characteristic distinguishes the pressure-sensitive adhesives, for example, from reactive adhesives which hardly provide cohesion in the unreacted state. For good adhesion properties, it is necessary to adjust pressure-sensitive adhesives so that there is an optimum balance of adhesive and cohesive properties.
• encapsulation is not only a complete enclosure with said PSA but also a partial application of the PSA to the areas of the (opto) to be encapsulated.
• electronic arrangement such as a one-sided coverage or a frame of an electronic structure.
• Permeability of permeants such as water vapor and oxygen reached, in particular of water vapor.
• a further reduction in oxygen permeability is additionally achieved.
• the formation of at least two domains within the block copolymer gives, in particular compared to adhesives based on polyisobutylene, a very good cohesion and, at the same time, improved barrier properties.
• the properties can be advantageously adapted to the requirements.
• Isobutylene block copolymers have good resistance to chemicals and
• transparent adhesives are also present, which in particular
• Isobutylene block copolymers therefore, in addition to good processability and coatability, characterized by good product properties in terms of adhesion and cohesion from as well as by a good barrier effect against oxygen and a very good barrier to water vapor, in particular compared to pressure-sensitive adhesives based on acrylates, silicones, polyisobutylene, vinylaromatic block copolymers of styrene (A blocks) and 1, 3-dienes (B blocks) and their hydrogenated variants or vinyl acetate.
• PSA can be easily integrated into an electronic device, especially in such an arrangement that requires high flexibility.
• Further particularly advantageous properties of the pressure-sensitive adhesive are similarly good adhesion to different substrates, high shear strength and high flexibility.
• the mass can be easily and quickly at low pressure, as is customary in the application of PSAs, be integrated into the encapsulation process of the (opto) electronic structure.
• the disadvantages usually associated with the avoided processing steps, such as thermal and mechanical stresses, can thus be minimized.
• Encapsulation by lamination of at least parts of the (opto) electronic structures with a sheet-like barrier material is possible with very good barrier effect in a simple roll-to-roll process.
• a sheet-like barrier material eg glass, especially thin glass, metal oxide coated films, metal foils, multilayer substrate materials
• the flexibility of the entire structure depends, in addition to the flexibility of the PSA, on other factors, such as the geometry and thickness of the (opto) electronic structures or the sheet-like barrier materials.
• the high flexibility of the PSA makes it possible to realize very thin, flexible and flexible (opto) electronic structures.
• flexible is meant the property of following the curvature of a curved article such as a drum of certain radius, in particular a radius of 1 mm, without damage.
• the temperature should preferably more than 30 0 C, more preferably be more than 50 0 C to promote the Auff lake accordingly. However, the temperature should not be selected too high in order not to damage the (opto) electronic arrangement. The temperature should be less than 100 ° C. if possible. The optimum temperature range, temperatures between 50 ° C and 70 0 C have been found. It is also advantageous if the PSA is heated before, during or after application additionally or alternatively.
• the PSA may be provided as part of an adhesive tape. This mode of administration allows a particularly simple and uniform application of the PSA.
• adheresive tape encompasses a carrier material which is provided on one or both sides with a pressure-sensitive adhesive
• Support material comprises all flat structures, for example films or film sections expanded in two dimensions, strips of extended length and limited width, strip sections, diecuts, multilayer arrangements and the like.
• Different carriers are used for different applications, e.g. Films, fabrics, nonwovens and papers can be combined with the adhesives.
• adhesive tape also includes so-called “transfer tapes”, i. an adhesive tape without a carrier.
• transfer adhesive tape the adhesive is applied before application between flexible liners, which are provided with a
• Separating layer are provided and / or have anti-adhesive properties.
• a liner is first removed, the adhesive is applied and then the second liner is removed.
• the pressure-sensitive adhesive can thus be used directly to join two
• the carrier material of an adhesive tape in the present case are preferably polymer films, film composites or provided with organic and / or inorganic layers Foils or film composites used.
• Such films / film composites can consist of all common plastics used for film production, but are not to be mentioned as examples by way of non-limiting example:
• Polyethylene polypropylene - especially the oriented polypropylene (OPP) produced by mono- or biaxial stretching, cyclic olefin copolymers (COC), polyvinyl chloride (PVC), polyesters - in particular polyethylene terephthalate (PET) and polyethylene naphthalate (PEN), ethylene vinyl alcohol (EVOH), polyvinylidene chloride (PVDC), polyvinylidene fluoride (PVDF), polyacrylonitrile (PAN), polycarbonate (PC), polyamide (PA), polyethersulfone (PES) or polyimide (PI).
• OPP oriented polypropylene
• COC cyclic olefin copolymers
• PVC polyvinyl chloride
• PET polyethylene terephthalate
• PEN polyethylene naphthalate
• EVOH ethylene vinyl alcohol
• PVDC polyvinylidene chloride
• PVDF polyvinylidene fluoride
• PAN polyacrylonit
• the support may also be combined with organic or inorganic coatings or layers. This can be achieved by conventional methods, e.g. Painting, printing, steaming, sputtering, co-extrusion or lamination happen.
• organic or inorganic coatings or layers e.g. Paint, printing, steaming, sputtering, co-extrusion or lamination happen.
• oxides or nitrides of silicon and of aluminum, indium-tin oxide (ITO) or sol-gel coatings may be mentioned here.
• these films / film composites in particular the polymer films provided with a Permeationsbarriere for oxygen and water vapor, the permeation barrier exceeds the requirements for the packaging area (WVTR ⁇ 10 "1 g / (m 2 d); OTR ⁇ 10 " 1 cm 3 / (m 2 d bar)).
• the determination of the permeability to oxygen (OTR) and water vapor (WVTR) is carried out according to DIN 53380 Part 3 or ASTM F-1249.
• the oxygen permeability is measured at 23 ° C and a relative humidity of 50%.
• the water vapor permeability is determined at 37.5 ° C and a relative humidity of 90%.
• the results are normalized to a film thickness of 50 ⁇ m.
• the films / film composites may be formed transparent in a preferred embodiment, so that the overall structure of such adhesive article is transparent.
• Transparency means an average transmission in the visible range of light of at least 75%, preferably higher than 90%.
• the elastic and viscous properties and the barrier effect can be varied by a (subsequent) crosslinking reaction in a specific embodiment of the PSA.
• This can be adapted to the (opto) electronic arrangement both thermally, as well as by electromagnetic radiation, preferably UV radiation, electron radiation or Gamma radiation take place.
• electromagnetic radiation preferably UV radiation, electron radiation or Gamma radiation take place.
• the high flexibility of the PSA should be preserved.
• the crosslinking takes place, if necessary, before the application of the PSA to the electronic device.
• a pressure-sensitive adhesive is used, which is transparent in certain embodiments in the visible light of the spectrum (wavelength range of about 400 nm - 800 nm). The desired transparency can be achieved in particular by the use of colorless adhesive resins.
• Such a pressure-sensitive adhesive is thus also suitable for full-surface use over an (opto) electronic structure.
• a full-surface bonding offers, with an approximately central arrangement of the electronic structure in relation to an edge seal, the advantage that the permeant would have to diffuse through the entire surface before it reaches the structure. The permeation path is thus significantly increased.
• the permeation paths extended in this embodiment compared to edge sealing, for example by liquid adhesives, have a positive effect on the overall barrier, since the permeation path is inversely proportional to the permeability.
• transparency means an average transmission of the adhesive in the visible range of light of at least 75%, preferably higher than 90%
• maximum transmission of the entire assembly also depends on the type of carrier used and on the carrier Type of construction.
• UV-blocking denotes an average transmittance of not more than 20%, preferably not more than 10%, more preferably not more than 1% in the corresponding wavelength range.
• UVA radiation formed UV blocking, preferably in the wavelength range of 280 nm to 400 nm (UVA and UVB radiation), more preferably in the wavelength range of 190 nm to 400 nm (UVA, UVB and UVC radiation).
• the UV-blocking effect of the PSA can be achieved in particular by adding UV blockers or suitable fillers to the PSA.
• Suitable UV blockers are, for example, HALS (Hinder Armine Light Stabilizer) such as Tinuvin from Ciba or benzimidazole derivatives.
• HALS Hader Armine Light Stabilizer
• Tinuvin from Ciba or benzimidazole derivatives Particularly suitable as the filler is titanium dioxide, in particular nanoscale titanium dioxide, since this allows transparency to be maintained in the visible range.
• the PSA shows by the Butylenblöcke used, in particular the polyisobutylene, especially in comparison to PSAs based on non-hydrogenated or partially hydrogenated copolymer blocks a very good resistance to weathering and UV light. This resistance is improved in particular by using hydrogenated resins.
• the pressure-sensitive adhesive used is preferably based on at least one butylene block copolymer, preferably on at least one isobutylene block copolymer, and also contains an adhesive resin.
• other block copolymers are used, as described below.
• Block copolymers are preferably used as the (iso) butylene block copolymer, on the one hand blocks preferably of vinylaromatics (A blocks), such as, for example, styrene, and on the other those formed by polymerization of (iso) butylene alone or of (iso) Butylene in combination with n-butene or 1, 3-dienes, such as isoprene or butadiene, (B blocks) included.
• a blocks vinylaromatics
• B blocks n-butene or 1, 3-dienes, such as isoprene or butadiene
• B blocks The proportions of the 1,3-dienes may be partially, selectively or fully hydrogenated.
• B blocks usually have a low polarity. Pure (poly) isobutylene blocks are preferably used as B blocks.
• polystyrene blocks as A blocks can be used as vinyl aromatic polymer blocks based on other aromatic homo- and copolymers (preferably C-8 to C-12 aromatics) with glass transition temperatures above 75 ° C, such as ⁇ -methylstyrene-containing aromatic blocks.
• the same or different A blocks may be included.
• the block copolymers have the structure (AB) nX, where A is, for example, the preferred vinyl aromatic blocks, B for example the preferred polyisobutylene blocks and X is a coupling site, n can assume values of 1 to 8. N preferably assumes values of 2 to 8.
• the block copolymers may thus have linear A-B-A structure, or be of a radial construction.
• the coupling site may be a simple C-C bond, but other coupling sites may be provided, e.g. Compounds with a metal atom or the like.
• block copolymers which, in addition to the above-described blocks A and B, contain at least one further block, e.g. A-B-C block copolymers.
• mixtures of AB block copolymers (2 blocks) and ABA block copolymers (3 blocks) are used.
• the use of these mixtures makes it possible to produce pressure-sensitive adhesives having improved flow behavior and adhesion.
• the ratio of the 3-block to the 2-block may vary in the range between 1:19 and 19: 1.
• isobutylene block copolymers are available, for example, under the name SiBStar from Kaneka or Oppanol IBS from BASF.
• the pressure-sensitive adhesive of the invention may comprise further block copolymers as constituent.
• Block copolymers described below, the adhesion of the adhesive to a substrate can be further increased.
• Vinylaromatic block copolymers based on block copolymers comprising polymer blocks predominantly formed from vinylaromatics (A2 blocks), preferably styrene, and those predominantly formed by polymerization of 1,3-dienes (B2 blocks), preferably butadiene, isoprene or a mixture of both, are preferably used Monomers, use. These B2 blocks usually have a low polarity. Both homo- and copolymer blocks are preferably usable as B2 blocks.
• the block copolymers resulting from the A2 and B2 blocks may contain the same or different B2 blocks, which may be partially, selectively or fully hydrogenated.
• the block copolymers may have linear A2-B2-A2 structures. Also usable are block copolymers of radial shape as well as star-shaped and linear
• Multiblock copolymers As further components A2-B2 diblock copolymers may be present. All of the aforementioned polymers can be used alone or in admixture with each other. Preference is given to using partially hydrogenated or hydrogenated polymers in order to obtain good weathering and UV stability.
• polystyrene blocks which are preferred as further block copolymers
• polystyrene blocks which are preferred as further block copolymers
• polystyrene blocks which are preferred as further block copolymers
• polystyrene blocks which are preferred as further block copolymers
• polystyrene blocks which are preferred as further block copolymers
• polystyrene blocks which are preferred as further block copolymers
• polymer blocks based on other aromatic-containing homo- and copolymers (preferably C-8 to C-12 aromatics) having glass transition temperatures above 75.degree. ⁇ -methylstyrene-containing aromatic blocks.
• the same or different A2 blocks may be included.
• block copolymers which, in addition to the above-described blocks A2 and B2, contain at least one further block, such as e.g. A2-B2-C2 block copolymers.
• B2 blocks with A2 blocks of a different chemical nature that exhibit a glass transition temperature above room temperature, such as polymethylmethacrylate.
• vinylaromatic block copolymers are known, for example, under the name Kraton from Kraton, (Kraton D 1101 and 1 102 as styrene-butadiene-styrene block copolymers (SBS), Kraton D 1 107 or 1 163 as styrene-isoprene-styrene block copolymers (SiS ), or Kraton G 1652 as a hydrogenated styrene-butadiene-styrene block copolymer), under the name Europrene Fa.
• Kraton from Kraton Kraton D 1101 and 1 102 as styrene-butadiene-styrene block copolymers (SBS), Kraton D 1 107 or 1 163 as styrene-isoprene-styrene block copolymers (SiS ), or Kraton G 1652 as a hydrogenated styrene
• Polimeri Europe styrene block copolymers with isoprene, butadiene or their hydrogenation products
• Septon the Fa. Kuraray hydrogenated styrene isoprene styrene block copolymers
• A2-B2-C2-vinylaromatic block copolymers are obtainable, for example, under the name SBM from Arkema.
• the Isobutylenblockcopolymere and other Vinylaromatenblockcopolymere each have a proportion of the above-described A blocks or A2 blocks of 10 wt .-% to 35 wt .-% to.
• the proportion of the block copolymers in total based on the total PSA is at least 20 wt .-%, preferably at least 30 wt .-%, more preferably at least 35 wt .-%. Too low a proportion of block copolymers has the consequence that the cohesion of the PSA is relatively low.
• the maximum proportion of the block copolymers in total, based on the total pressure-sensitive adhesive mass, is at most 90% by weight, preferably at most 75% by weight, very particularly preferably at most 70% by weight. Too high a proportion of block copolymers, in turn, has the consequence that the PSA is barely tacky.
• the proportion of (iso) Butylenblockcopolymere in the total proportion of the block copolymers is at least 40 wt .-%, preferably at least 55 wt .-%. Too small an amount of (iso) butylene block copolymer has the consequence that the barrier effect against water vapor and oxygen is reduced.
• the pressure-sensitive adhesive comprises, in addition to the at least one (iso) butylene block copolymer, as described above, at least one tackifier resin in order to increase the adhesion in the desired manner.
• the adhesive resin should be compatible with the elastomeric block of the block copolymers.
• Tackifiers which may be used in the PSA include, for example, unhydrogenated, partially or completely hydrogenated rosin-based rosin derivatives, hydrogenated polymers of dicyclopentadiene, non-hydrogenated, partially, selectively or fully hydrogenated hydrocarbon resins based on C5, C5 / C9 or C9 - Monomerströmen, polyterpene resins based on ⁇ -pinene and / or ss-pinene and / or ⁇ -limonene, hydrogenated polymers of preferably pure C8 and C9 aromatics are used.
• the aforementioned adhesive resins can be used both alone and in admixture. Both solid and liquid resins can be used at room temperature.
• hydrogenated resins having a degree of hydrogenation of at least 90%, preferably of at least 95%, are preferred.
• non-polar resins having a DACP value (diacetone alcohol cloud point) above 30 0 C and a MMAP value (mixed methylcylohexane aniline point) of greater than 50 0 C, in particular with a DACP value above 37 ° C and a MMAP value greater than 60 0 C preferred.
• the DACP value and the MMAP value each indicate the solubility in a particular solvent.
• additives can typically be used:
• Plasticizers such as plasticizer oils, or low molecular weight liquid polymers, such as low molecular weight
• Process stabilizers such as C radical scavengers • Sunscreens, such as UV absorbers or hindered
• Base of pure hydrocarbons for example unsaturated polydienes such as natural or synthetically produced polyisoprene or polybutadiene, chemically substantially saturated elastomers such as saturated ethylene-propylene copolymers, ⁇ -olefin copolymers, polyisobutylene, butyl rubber, ethylene-propylene rubber, as well as chemically functionalized
• the PSAs used according to the invention are preferably crosslinked to the surface before or, if appropriate, also after flowing on, the aim being those crosslinking levels which furthermore allow a high degree of flexibility and good adhesion of the material.
• the pressure-sensitive adhesive preferably has an elongation at break of at least 20%. Such elongation at break is particularly preferred with regard to the most flexible possible configuration of the PSA. The elongation at break is determined at a strain rate of 300 mm / min and a temperature of 23 ° C.
• the PSA is crosslinked with UV radiation or electron beams.
• UV radiation or electron beams A detailed description of the state of the art and the most important process parameters relating to crosslinking are known to the person skilled in the art, for example, from “Chemistry and Technology of UV and EB formulation for Coatings, Inks and Paints” (Vol.1, 1991, SITA, London) Other methods are used which allow high-energy irradiation.
• crosslinking agents and / or promoters for crosslinking can be added to the viscoelastic material, in particular by UV, electron beam and / or thermally excitable crosslinkers and / or promoters.
• Suitable crosslinkers for radiation crosslinking are monomers or polymers which contain, for example, the following functional groups: acrylate or methacrylate, epoxide, hydroxyl, carboxyl, vinyl, vinyl ether, oxetane, thiol, acetoacetate, isocyanates, allyl or generally unsaturated compounds.
• the monomers or polymers used can be di- or multifunctional, depending on the degree of crosslinking requirements.
• the PSAs are crosslinked with thermally activatable crosslinkers.
• thermally activatable crosslinkers preference is given to adding peroxides, acid or acid anhydrides, metal chelates, difunctional or polyfunctional epoxides, difunctional or polyfunctional hydroxides and difunctional or polyfunctional isocyanates, as described, for example, for acid anhydrides in EP 131 1559 B1.
• block copolymers which have been functionalized with these crosslinking groups.
• block copolymers such as Kraton FG series (eg Kraton FG 1901 or Kraton FG 1924), Asahi Tuftec M 1913 or Tuftec M 1943 or Septon HG252 (SEEPS-OH).
• the (iso) butylene block copolymers themselves can also be provided with functional groups, for example with maleic acid and / or malonic anhydride.
• Further preferred block copolymers are available, for example, under the name Epofriend A 1005, A 1010 or A 1020 from Daicel.
• these block copolymers can be crosslinked thermally or by radiation.
• suitable crosslinking agents for example polyfunctional isocyanates, amines, epoxides, alcohols, thiols, phenols, guanidines, mercaptans, carboxylic acids or acid anhydrides
• these block copolymers can be crosslinked thermally or by radiation.
• a combination of acid- or acid anhydride-modified block copolymer for example Kraton FG series
• an epoxidized block copolymer for example Daicel Epofriend series
• a mixture of the functionalized monomers or polymers is also usable.
• the PSA also contains fillers, by way of example but not by way of limitation oxides, hydroxides, carbonates, nitrides, halides, carbides or mixed oxide / hydroxide / halide compounds of aluminum, silicon, zirconium, titanium, Tin, zinc, iron or (alkaline) alkali metals.
• fillers for example but not by way of limitation oxides, hydroxides, carbonates, nitrides, halides, carbides or mixed oxide / hydroxide / halide compounds of aluminum, silicon, zirconium, titanium, Tin, zinc, iron or (alkaline) alkali metals.
• These are essentially clays, e.g. Aluminas, boehmite, bayerite, gibbsite, diaspore and the like.
• Particularly suitable are layered silicates such as bentonite, montmorillonite, hydrotalcite, hectorite, kaolinite, boehmite, mica, vermiculite or mixtures
• a filler is referred to herein as nanoscale if it has a maximum extent of about 100 nm, preferably of about 10 nm, in at least one dimension.
• Particular preference is given to using mass-transparent fillers with a platelet-shaped crystallite structure and a high aspect ratio with homogeneous distribution.
• the fillers with platelet-like crystallite structure and aspect ratios well above 100 usually have only a thickness of a few nm, but the length or the width of the crystallites can be up to some ⁇ m.
• Such fillers are also referred to as nanoparticles.
• the particulate configuration of the fillers with small dimensions is also particularly advantageous for a transparent design of the PSA.
• fillers in the adhesive matrix By building labyrinth-like structures using the previously described fillers in the adhesive matrix, the diffusion path of, for example, oxygen and water vapor is extended such that its permeation through the adhesive layer is reduced.
• these fillers can be superficially modified with organic compounds.
• the use of such fillers per se is known, for example, from US 2007/0135552 A1 and WO 02/026908 A1.
• fillers which can interact with oxygen and / or water vapor in a particular manner are also used.
• penetrating oxygen or water vapor is then bound to these fillers chemically or physically.
• These fillers are also referred to as getter, scavenger, desiccant or absorber.
• Such fillers include, by way of example but not limitation, oxidizable metals, halides, salts, silicates, oxides, hydroxides, sulfates, sulfites, carbonates of metals and transition metals, perchlorates, and activated carbon, including its modifications.
• Examples are cobalt chloride, calcium chloride, calcium bromide, lithium chloride, zinc chloride, zinc bromide, silica (silica gel), alumina (activated aluminum), calcium sulfate, copper sulfate, sodium dithionite, sodium carbonate, magnesium carbonate, titanium dioxide, bentonite, montmorillonite, diatomaceous earth, zeolites and oxides of (Erd ) Alkali metals, such as barium oxide, calcium oxide, iron oxide and Magesiumoxid or carbon nanotubes.
• organic absorbers such as, for example, polyolefin copolymers, polyamide copolymers, PET copolyesters or other absorbers based on hybrid polymers, which are usually used in combination with catalysts such as, for example, cobalt.
• Further organic absorbers are, for example, slightly crosslinked polyacrylic acid, ascorbates, glucose, gallic acid or unsaturated fats and oils.
• the proportion is preferably at least 5 wt .-%, more preferably at least 10 wt .-% and most preferably at least 15 Wt .-%.
• the proportion is therefore in a design maximum 95 wt .-%, preferably at most 70 wt .-%, more preferably at most 50 wt .-%.
• the finest possible distribution and the highest possible surface area of the fillers are advantageous. This allows a higher efficiency and a higher loading capacity and is achieved in particular with nanoscale fillers.
• the preparation and processing of the PSA can be carried out from solution, dispersion and from the melt.
• the preparation and processing takes place from solution or from the melt.
• Particularly preferred is the production of the adhesive from solution.
• the components of the PSA are dissolved in a suitable solvent, for example toluene or mixtures of gasoline and acetone, and applied to the carrier by generally known methods.
• a suitable solvent for example toluene or mixtures of gasoline and acetone
• melt processing these may be application methods via a die or calender.
• coatings with doctor blades, knives, rollers or nozzles are known, to name but a few.
• the PSA contains no longer volatile organic compounds (VOC) than 50 ⁇ g carbon per gram mass, in particular not more than 10 ⁇ g C / g, measured according to VDA 277.
• VOC volatile organic compounds
• the PSA can either be used for the full-surface bonding of (optoelectronic arrangements or, after appropriate fabrication, diecuts, rolls or other shaped articles of the PSA or the PSA tape can be produced Corresponding diecuts and molded articles of the PSA / PSA tape are then preferably applied to the substrate to be bonded
• the choice of the shape of the stamped product or of the molded article is not restricted and is chosen depending on the type of (optoelectronic) arrangement Compared to liquid adhesives, by increasing the permeation path length by lateral penetration of the permeants is beneficial for the mass barrier properties, since the permeation path length is inversely proportional to permeation.
• the thickness of the carrier is preferably in the range of about 1 micron to about 350 microns, more preferably between about 2 microns and about 250 microns and more preferably between about 12 ⁇ m and about 150 ⁇ m.
• the optimum thickness depends on the (opto) electronic arrangement, the end use and the type of execution of the PSA. Very thin carriers in the range of 1 to 12 microns are used in (opto) electronic structures, which should achieve a low total thickness, but it is the cost of integration into the structure increased.
• Very thick carriers between 150 and 350 microns are used when an increased permeation barrier by the carrier and the rigidity of the structure in the foreground; the protective effect is increased by the carrier, while the flexibility of the structure is reduced.
• the preferred range between 12 and 150 ⁇ m represents an optimal compromise for most (opto) electronic structures as an encapsulation solution.
• FIG. 1 shows a first (opto) electronic arrangement in a schematic representation
• Fig. 3 shows a third (opto) electronic arrangement in a schematic representation.
• This arrangement 1 shows a first embodiment of an (opto) electronic arrangement 1.
• This arrangement 1 has a substrate 2 on which an electronic structure 3 is arranged.
• the substrate 2 itself is formed as a barrier for permeants and thus forms part of the encapsulation of the electronic structure 3.
• another cover 4 designed as a barrier is arranged above the electronic Structure 3.
• a pressure-sensitive adhesive 5 is provided circumferentially next to the electronic structure 3 on the substrate 2.
• the pressure-sensitive adhesive 5 connects the cover 4 to the substrate 2.
• the pressure-sensitive adhesive 5 also allows the spacing of the cover 4 from the electronic structure 3 by means of a correspondingly thick embodiment.
• the PSA 5 is based on the PSA according to the invention as described above in a general form and is described in more detail below in exemplary embodiments.
• the PSA 5 not only performs the function of bonding the substrate 2 to the cover 4, but also provides a barrier layer for permeants so as to encapsulate the electronic structure 2 against permeants such as water vapor and oxygen.
• the PSA 5 is presently also provided in the form of a diecut from a double-sided adhesive tape. Such a punched product enables a particularly simple application.
• FIG. 2 shows an alternative embodiment of an (opto) electronic device 1.
• an electronic structure 3 which is arranged on a substrate 2 and encapsulated by the substrate 2 from below.
• the pressure-sensitive adhesive 5 is now arranged over its entire surface.
• the electronic structure 3 is thus completely encapsulated from above by the pressure-sensitive adhesive 5.
• a cover 4 is then applied.
• this cover 4 does not necessarily have to meet the high barrier requirements, since the barrier is already provided by the pressure-sensitive adhesive.
• the cover 4 may, for example, only perform a mechanical protective function, but it may also be additionally provided as a permeation barrier.
• FIG. 3 shows a further alternative embodiment of an (opto) electronic arrangement 1.
• two pressure-sensitive adhesives 5a, b are now provided, which in the present case are of identical design.
• the first pressure-sensitive adhesive 5a is arranged over the entire surface of the substrate 2.
• the electronic structure 3 is provided, which is fixed by the PSA 5a.
• the composite of PSA 5a and electronic structure 3 is then completely covered with the further PSA 5b, so that the electronic structure 3 is encapsulated on all sides by the PSAs 5a, b.
• the cover 4 is provided above the PSA 5b again the cover 4 is provided.
• neither the substrate 2 nor the cover 4 necessarily have barrier properties. However, they can nevertheless be provided to further restrict the permeation of permeants to the electronic structure 3.
• the pressure-sensitive adhesive 5 is here and preferably applied in each case with a homogeneous layer thickness.
• the transition is fluid and it may remain small un-filled or gas-filled areas. Possibly.
• the PSA is locally compressed to different degrees, so that by flow processes a certain compensation of the height difference can be made to the edge structures.
• the dimensions shown are not to scale, but rather serve only a better representation.
• the electronic structure itself is usually relatively flat (often less than 1 micron thick).
• the application of the PSA 5 takes place in all embodiments shown in the form of a pressure-sensitive adhesive tape.
• This can basically be a double-sided pressure-sensitive adhesive tape with a carrier or a transfer adhesive tape.
• an embodiment is selected as a transfer adhesive tape.
• the thickness of the pressure-sensitive adhesive is preferably between about 1 ⁇ m and about 150 microns, more preferably between about 5 microns and about 75 microns and more preferably between about 12 microns and 50 microns.
• High layer thicknesses between 50 .mu.m and 150 .mu.m are used when improved adhesion to the substrate and / or a damping effect within the (opto) electronic structure is to be achieved.
• the disadvantage here however, the increased permeation cross section.
• Low layer thicknesses between 1 ⁇ m and 12 ⁇ m reduce the permeation cross section, so that the lateral permeation and the total thickness of the (opto) electronic structure.
• Adhesive force The determination of the bond strength was carried out as follows: A steel surface, a polyethylene terephthalate (PET) and a polyethylene plate (PE) was used as a defined primer.
• the glued surface element to be examined was cut to a width of 20 mm and a length of about 25 cm, provided with a handling section and immediately thereafter pressed five times with a steel roller of 4 kg at a feed rate of 10 m / min on the selected primer.
• the previously bonded surface element at an angle of 180 ° at room temperature and at 300 mm / min was removed from the primer with a tensile tester (Zwick) and measured the force required for this purpose.
• the measured value (in N / cm) was the average of three individual measurements. Holding Power
• Shear life was determined as follows: A polished steel surface was used as the defined primer. The bondable surface element to be examined was cut to a width of 13 mm and a length of about 5 cm, and immediately thereafter four times with a steel roll of 2 kg at a feed rate of 10 m / min on the selected adhesion base with an area of 20 ⁇ 13 mm 2 is pressed. Immediately thereafter, the glued surface element was loaded at an angle of 180 ° with 10 N at 23 ° C / 50% RH. Measured is the time after which the glued surface element has completely detached from the primer. The measured value (in min) results as a median of three individual measurements. After 10,000 minutes, the test is aborted.
• the determination of the elastic fraction was carried out as follows: A polished steel surface was used as the defined primer.
• the bondable surface element to be examined was cut to a width of 10 mm and a length of about 5 cm and immediately thereafter three times with a steel roll of 2 kg at a feed rate of 10 m / min on the selected adhesion base with an area of 10 x 13 mm pressed.
• the glued surface element was loaded at an angle of 180 ° with 1 N and with 5 N, at a temperature of 40 0 C.
• the slide is measured after 15 minutes, then the sample is relieved and the sliding distance determined after a total of 30 minutes.
• the ratio of the two measured values is a measure of elastic and viscous portions of the adhesive.
• the measured values are an average of two individual measurements.
• the transmission of the adhesive was determined via the VIS spectrum.
• the images of the VIS spectrum were carried out on a UVIKON 923 from Kontron.
• the wavelength range of the measured spectrum covers all frequencies between 800 nm and 400 nm at a resolution of 1 nm.
• the adhesive was applied to a PET carrier and before the measurement, a blank channel measurement of the carrier was carried out as a reference over the entire wavelength range. For the indication of the result, the transmission measurements in the specified range were averaged. permeation
• the determination of the permeability to oxygen (OTR) and water vapor (WVTR) was carried out according to DIN 53380 part 3 or ASTM F-1249.
• the PSA was applied to a permeable membrane with a layer thickness of 50 microns.
• the oxygen permeability was measured at 23 ° C and a relative humidity of 50% using a Mocon OX-T ran 2/21 measuring device.
• the water vapor permeability was determined at 37.5 ° C and a relative humidity of 90%.
• the adhesive was coated in a layer thickness of 50 ⁇ m between two 23 ⁇ m PET carriers and tested for a bending radius of 1 mm at a bend of 180 °. The test is passed if the layer does not break or peel off.
• a calcium test was used. For this purpose, a 20 ⁇ 20 mm 2 large, thin calcium layer is deposited on a glass plate under a nitrogen atmosphere. The thickness of the calcium layer is about 100 nm.
• the test is based on the reaction of calcium with water vapor and oxygen, as described for example by AG Erlat et. al. in "47th Annual Technical Conference Proceedings - Society of Vacuum Coaters", 2004, pp. 654-659, and by ME Gross et al., in "46th Annual Technical Conference Proceedings - Society of Vacuum Coaters", 2003, pages 89-92 are.
• the light transmission of the calcium layer is monitored, which increases by the conversion into calcium hydroxide and calcium oxide. Achieving 90% of the transmission of the structure without calcium layer is referred to as end of life.
• the measuring conditions selected are 23 ° C and 50% relative humidity.
• the samples were glued with a layer thickness of the PSA of 25 microns over the entire surface and free of bubbles. Determination of the VOC value (volatile organic compounds)
• the VOC value is determined according to VDA 277.
• VOC gaseous (volatile organic compounds)
• VOC - Volative Organic Components the sum of the gaseous (volatile organic compounds) (VOC - Volative Organic Components) is determined from small sample quantities on a laboratory scale. It is a sample ( ⁇ 1 g) in a glass jar (10 ml) for 5 hours at 120 0 C conditioned. A defined amount of the gas space from the gas-tight vessel is then examined by means of the combination gas chromatograph (GC) / flame ionization detector (FID) on the hydrocarbons contained therein.
• GC gas chromatograph
• FID flame ionization detector
• the pressure-sensitive adhesives in Examples 1 to 4 were prepared from solution.
• the individual components were dissolved in toluene (solids content 40%), coated on an untreated PET film and dried at 120 ° C for 15 minutes, so that an adhesive layer with a basis weight of 50 g / m 2 was formed.
• samples were prepared in the same way, but the coating was not carried out on a PET film but on a 1.5 g / m 2 siliconized release paper, so that after transfer to the permeable membrane made a measurement of the pure PSA could be.
• Comparative example 100 parts Oppanol B10 polyisobutylene having an average molecular weight of 40,000 g / mol
• the SEBS contained about 36% diblock content.
• An acrylate having the composition 78% EHA, 19% stearyl acrylate and 3% acrylic acid in acetone and gasoline was polymerized and from the solution to an untreated PET carrier (or for the permeation measurements on a with 1, 5 g / m 2 siliconized release paper) coated, dried at 120 ° C for 15 min and crosslinked with 0.2% aluminum chelate, based on the proportion of polymer.
• the thickness of the adhesive layer is 50 ⁇ m.
• a mixture of 60% Levamelt 456 (ethylene vinyl acetate) and 40% Foral FG85 are dissolved in acetone and removed from the solution onto an untreated PET support (or for permeation measurements on a 1.5 g / m 2 siliconized release paper ) and dried at 120 0 C for 15 min.
• the thickness of the adhesive layer is 50 ⁇ m.
• a commercially available UV-curing epoxy of Epo-Tek OG142 was spread on a PET film in a thickness of 50 microns and cured at 160 W / cm with a medium pressure mercury vapor lamp at a web speed of 10 m / min. For the determination of permeation, the pattern was coated on siliconized release paper and stripped.
• Examples 1 to 3 show good adhesion at high shear strengths.
• the bond strengths in Example 3 have been increased by the addition of a partially hydrogenated vinyl aromatic block copolymer (SBBS) to the isobutylene block copolymer as part of the PSA.
• SBBS partially hydrogenated vinyl aromatic block copolymer
• Comparative Example C1 shows a pressure-sensitive adhesive based on an SBBS block copolymer.
• the adhesive properties are very similar to those of Example 3, but the barrier effect is worse.
• the uncrosslinked PiB PSA VO shows a much lower elastic content.
• SSZ permanent shear stress
• the creep tendency of the polyisobutylene-based pressure-sensitive adhesive shows itself.
• a cohesive failure occurs. Due to the physical crosslinking via the styrene domains in the styrene-isobutylene-based compositions, this creep tendency is suppressed at room temperature.
• the permeability of the pressure-sensitive adhesives according to the invention in Examples 1 to 3 is much lower compared to V1 to V4 while the transmission in the visible range of the light is similar.
• the water vapor permeability of the crosslinked epoxide and the block copolymers is similar, the oxygen permeability is higher.
• the transmission is in a similar range for all examples.
• compositions based on the PSAs described here show, in comparison to acrylates in particular with comparable drying parameters, very low VOC values. Values. These have a positive effect on the service life and performance of Ito layers in (opto) electronic structures.

Landscapes

• Chemical & Material Sciences (AREA)
• Organic Chemistry (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Engineering & Computer Science (AREA)
• Geochemistry & Mineralogy (AREA)
• Ceramic Engineering (AREA)
• Life Sciences & Earth Sciences (AREA)
• General Chemical & Material Sciences (AREA)
• Materials Engineering (AREA)
• Optics & Photonics (AREA)
• Physics & Mathematics (AREA)
• Adhesives Or Adhesive Processes (AREA)
• Electroluminescent Light Sources (AREA)
• Adhesive Tapes (AREA)

Priority Applications (6)

Applications Claiming Priority (2)

Publications (1)

Family

ID=41530580

Family Applications (1)

Country Status (9)

Cited By (8)

Families Citing this family (73)

Citations (4)

Family Cites Families (30)

• 2008
  • 2008-12-03 DE DE102008060113A patent/DE102008060113A1/de not_active Withdrawn
• 2009
  • 2009-11-04 TW TW098137381A patent/TWI488242B/zh not_active IP Right Cessation
  • 2009-11-18 CN CN200980132496.5A patent/CN102132439B/zh active Active
  • 2009-11-18 WO PCT/EP2009/065393 patent/WO2010063579A1/de not_active Ceased
  • 2009-11-18 EP EP09756304.3A patent/EP2279537B1/de not_active Not-in-force
  • 2009-11-18 US US12/996,716 patent/US8460969B2/en not_active Expired - Fee Related
  • 2009-11-18 PL PL09756304T patent/PL2279537T3/pl unknown
  • 2009-11-18 JP JP2011538934A patent/JP6074141B2/ja not_active Expired - Fee Related
  • 2009-11-18 KR KR1020107027853A patent/KR101660817B1/ko not_active Expired - Fee Related
• 2016
  • 2016-11-07 JP JP2016216894A patent/JP6407940B2/ja not_active Expired - Fee Related