Classifications

• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
  • C07C29/00—Preparation of compounds having hydroxy or O-metal groups bound to a carbon atom not belonging to a six-membered aromatic ring
  • C07C29/132—Preparation of compounds having hydroxy or O-metal groups bound to a carbon atom not belonging to a six-membered aromatic ring by reduction of an oxygen containing functional group
  • C07C29/136—Preparation of compounds having hydroxy or O-metal groups bound to a carbon atom not belonging to a six-membered aromatic ring by reduction of an oxygen containing functional group of >C=O containing groups, e.g. —COOH
  • C07C29/147—Preparation of compounds having hydroxy or O-metal groups bound to a carbon atom not belonging to a six-membered aromatic ring by reduction of an oxygen containing functional group of >C=O containing groups, e.g. —COOH of carboxylic acids or derivatives thereof
  • C07C29/149—Preparation of compounds having hydroxy or O-metal groups bound to a carbon atom not belonging to a six-membered aromatic ring by reduction of an oxygen containing functional group of >C=O containing groups, e.g. —COOH of carboxylic acids or derivatives thereof with hydrogen or hydrogen-containing gases
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
  • C07C29/00—Preparation of compounds having hydroxy or O-metal groups bound to a carbon atom not belonging to a six-membered aromatic ring
  • C07C29/132—Preparation of compounds having hydroxy or O-metal groups bound to a carbon atom not belonging to a six-membered aromatic ring by reduction of an oxygen containing functional group
  • C07C29/136—Preparation of compounds having hydroxy or O-metal groups bound to a carbon atom not belonging to a six-membered aromatic ring by reduction of an oxygen containing functional group of >C=O containing groups, e.g. —COOH
  • C07C29/147—Preparation of compounds having hydroxy or O-metal groups bound to a carbon atom not belonging to a six-membered aromatic ring by reduction of an oxygen containing functional group of >C=O containing groups, e.g. —COOH of carboxylic acids or derivatives thereof
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J21/00—Catalysts comprising the elements, oxides, or hydroxides of magnesium, boron, aluminium, carbon, silicon, titanium, zirconium, or hafnium
  • B01J21/06—Silicon, titanium, zirconium or hafnium; Oxides or hydroxides thereof
  • B01J21/08—Silica
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J21/00—Catalysts comprising the elements, oxides, or hydroxides of magnesium, boron, aluminium, carbon, silicon, titanium, zirconium, or hafnium
  • B01J21/18—Carbon
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
  • B01J23/02—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the alkali- or alkaline earth metals or beryllium
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
  • B01J23/38—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of noble metals
  • B01J23/54—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of noble metals combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36
  • B01J23/56—Platinum group metals
  • B01J23/62—Platinum group metals with gallium, indium, thallium, germanium, tin or lead
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
  • B01J23/38—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of noble metals
  • B01J23/54—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of noble metals combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36
  • B01J23/56—Platinum group metals
  • B01J23/62—Platinum group metals with gallium, indium, thallium, germanium, tin or lead
  • B01J23/622—Platinum group metals with gallium, indium, thallium, germanium, tin or lead with germanium, tin or lead
  • B01J23/626—Platinum group metals with gallium, indium, thallium, germanium, tin or lead with germanium, tin or lead with tin
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
  • B01J23/70—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper
  • B01J23/89—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with noble metals
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
  • B01J23/70—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper
  • B01J23/89—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with noble metals
  • B01J23/8933—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with noble metals also combined with metals, or metal oxides or hydroxides provided for in groups B01J23/02 - B01J23/36
  • B01J23/8966—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with noble metals also combined with metals, or metal oxides or hydroxides provided for in groups B01J23/02 - B01J23/36 with germanium, tin or lead
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
  • B01J37/02—Impregnation, coating or precipitation
  • B01J37/0201—Impregnation
  • B01J37/0203—Impregnation the impregnation liquid containing organic compounds
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
  • B01J37/08—Heat treatment
  • B01J37/082—Decomposition and pyrolysis
  • B01J37/088—Decomposition of a metal salt
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
  • C07C31/00—Saturated compounds having hydroxy or O-metal groups bound to acyclic carbon atoms
  • C07C31/02—Monohydroxylic acyclic alcohols
  • C07C31/08—Ethanol

Definitions

• the present invention relates generally to a process for the production of ethanol from acetic acid. More specifically, the present invention relates to a process including hydrogenating acetic acid utilizing a catalyst composed of platinum and tin supported on a suitable catalyst support optionally containing one or more additional hydrogenating metals to form ethanol with high selectivity.
• Ethanol is an important commodity feedstock for a variety of industrial products and is also used as a fuel additive with gasoline. For instance, ethanol can readily be dehydrated to ethylene, which can then be converted to polymer products or small-molecule based products for use in coatings, polymer manufacture and so forth. Ethanol is conventionally produced from feedstocks where price fluctuations are becoming more significant. That is, fluctuating natural gas and crude oil prices contribute to fluctuations in the cost of conventionally produced, petroleum, natural gas or corn or other agricultural product-sourced ethanol, making the need for alternative sources of ethanol all the greater when oil prices and/or agricultural product prices rise.
• United States Patent No. 5,149,680 to Kitson et al. describes a process for the catalytic hydrogenation of carboxylic acids and their anhydrides to alcohols and/or esters utilizing a platinum group metal alloy catalysts.
• the catalyst is comprised of an alloy of at least one noble metal of Group VIII of the Periodic Table and at least one metal capable of alloying with the Group VIII noble metal, admixed with a component comprising at least one of the metals rhenium, tungsten or molybdenum.
• the selectivity to a combined mixture of alcohol and ester is reported to be only in the range of about 73 to 87 percent with low conversion of carboxylic acids at about 16 to 58 percent.
• no specific example of conversion of acetic acid to ethanol is provided.
• United States Patent No. 4,804,791 to Kitson et al. describes another process for the production of alcohols by the hydrogenation of carboxylic acids.
• ethanol is produced from acetic acid or propanol is produced from propionic acid by contacting either acetic acid or propionic acid in the vapor phase with hydrogen at elevated temperature and a pressure in the range from 1 to 150 bar in the presence of a catalyst comprising as essential components (i) a noble metal of Group VIII of the Periodic Table of the elements, and (ii) rhenium, optionally on a support, for example a high surface area graphitized carbon.
• the conversion of acetic acid to ethanol ranged from 0.6 % to 69% with selectivity to ethanol was in the range of about 6% to 97%.
• this invention provides a process for the selective formation of ethanol from acetic acid comprising: hydrogenating acetic acid over a platinum/tin hydrogenating catalyst in the presence of hydrogen.
• the catalyst suitable for the process of this invention is comprised of a combination of platinum and tin supported on a suitable catalyst support optionally in combination with one or more metal catalysts selected from the group consisting of palladium, rhodium, ruthenium, rhenium, iridium, chromium, copper, molybdenum, tungsten, vanadium and zinc.
• Suitable catalyst supports include without any limitation, silica, alumina, calcium silicate, carbon, zirconia and titania.
• Conversion is expressed as a mole percentage based on acetic acid in the feed.
• the conversion of acetic acid (AcOH) is calculated from gas chromatography (GC) data using the following equation:
• Selectivity is expressed as a mole percent based on converted acetic acid. For example, if the conversion is 50 mole % and 50 mole % of the converted acetic acid is converted to ethanol, we refer to the ethanol selectivity as 50%. Selectivity is calculated from gas chromatography (GC) data using the following equation:
• Weight percent of a catalyst metal is based on metal weight and the total dry weight of metal and support.
• conversion of acetic acid to ethanol can be carried out in a variety of configurations, such as for example in a single reaction zone which may be a layered fixed bed, if so desired.
• An adiabatic reactor could be used, or a shell and tube reactor provided with a heat transfer medium could be used.
• the fixed bed can comprise a mixture of different catalyst particles or catalyst particles which include multiple catalysts as further described herein.
• the fixed bed may also include a layer of particulate material making up a mixing zone for the reactants.
• a reaction mixture including acetic acid, hydrogen and optionally an inert carrier gas is fed to the bed as a stream under pressure to the mixing zone. The stream is subsequently supplied (by way of pressure drop) to the reaction zone or layer.
• Reaction zone comprises a catalytic composition including a suitable hydrogenating catalyst where acetic acid is hydrogenated to produce ethanol. Any suitable particle size may be used depending upon the type of reactor, throughput requirements and so forth.
• a hydrogenating catalyst employed contains a combination of platinum and tin on a suitable catalyst support.
• the catalysts that are suitable in the process of this invention contain optionally a third metal supported on the same catalyst support.
• the following metals may be mentioned as those metals suitable as a third metal without any limitation: palladium, rhodium, ruthenium, rhenium, iridium, chromium, copper, molybdenum, tungsten, vanadium, zinc and a mixture thereof.
• a suitable weight ratio of a combination of platinum and tin on a suitable support can be used as a hydrogenating catalyst.
• a combination of platinum and tin (Pt/Sn) in the weight ratio of about 0.1 - 2 are particularly preferred. More preferably, a weight ratio of Pt/Sn is about 0.5 -1.5 and most preferably the weight ratio of Pt/Sn is about 1.
• Preferred examples of metals that can be used with Pt/Sn as a third metal include without any limitation any of the other metals listed above, such as for example rhodium, iridium, copper, molybdenum and zinc.
• catalyst supports known in the art can be used to support the catalysts of this invention.
• supports include without any limitation, zeolite, iron oxide, silica, alumina, titania, zirconia, magnesium oxide, calcium silicate, carbon, graphite and a mixture thereof.
• Preferred supports are silica, alumina, calcium silicate, carbon, zirconia and titania. More preferably silica is used as a catalyst support in the process of this invention. It is also important to note that higher the purity of silica better it is preferred as a support in this invention.
• Another preferred catalyst support is calcium silicate.
• the preferred catalyst support is carbon.
• Various forms of carbon known in the art that are suitable as catalyst support can be used in the process of this invention.
• Particularly preferred carbon support is a graphitized carbon, particularly the high surface area graphitized carbon as described in Great Britain Patent No. 2,136,704.
• the carbon is preferably in particulate form, for example, as pellets. The size of the carbon particles will depend on the pressure drop acceptable in any given reactor (which gives a minimum pellet size) and reactant diffusion constraint within the pellet (which gives a maximum pellet size).
• the carbon catalyst supports that are suitable in the process of this invention are preferably porous carbon catalyst supports. With the preferred particle sizes the carbon will need to be porous to meet the preferred surface area characteristics.
• the catalyst supports including the carbon catalyst supports may be characterized by their BET, basal plane, and edge surface areas.
• the BET surface area is the surface area determined by nitrogen adsorption using the method of Brunauer Emmert and Teller J. Am. Chem. Soc. 60,309 (1938).
• the basal plane surface area is the surface area determined from the heat of adsorption on the carbon of n-dotriacontane from n-heptane by the method described in Proc. Roy. Soc. A314 pages 473-498, with particular reference to page 489.
• the edge surface area is the surface area determined from the heat of adsorption on the carbon of n-butanol from n-heptane as disclosed in the Proc. Roy. Soc. article mentioned above with particular reference to page 495.
• the preferred carbon catalyst supports for use in the present invention have a BET surface area of at least 100 m 2 /g, more preferably at least 200 m 2 / g, most preferably at least 300 m 2 Ig.
• the BET surface area is preferably not greater than 1000 m 2 /g, more preferably not greater than 750 m 2 /g.
• the preferred carbon support may be prepared by heat treating a carbon- containing starting material.
• the starting material may be an oleophillic graphite e.g. prepared as disclosed in Great Britain Patent No. 1,168,785 or may be a carbon black.
• oleophillic graphites contain carbon in the form of very fine particles in flake form and are therefore not very suitable materials for use as catalyst supports. We prefer to avoid their use. Similar considerations apply to carbon blacks which also have a very fine particle size.
• the preferred materials are activated carbons derived from vegetable materials e.g. coconut charcoal, or from peat or coal or from carbonizable polymers.
• the materials subjected to the heat treatment preferably have particle sizes not less than these indicated above as being preferred for the carbon support.
• the preferred starting materials have the following characteristics: BET surface area of at least 100, more preferably at least 500 m 2 /g.
• the preferred heat treatment procedure for preparing carbon supports having the defined characteristics comprise successively (1) heating the carbon in an inert atmosphere at a temperature of from 900 0 C to 3300 0 C, (2) oxidizing the carbon at a temperature between 300 0 C and 1200 0 C, (3) heating in an inert atmosphere at a temperature of between 900 0 C and 3000 0 C.
• the oxidation step is preferably carried out at temperatures between 300° and 600 0 C when oxygen (e.g. as air) is used as the oxidizing agent.
• oxygen e.g. as air
• the duration of the heating in inert gas is not critical. The time needed to heat the carbon to the required maximum temperature is sufficient to produce the required changes in. the carbon.
• the oxidation step must clearly not be carried out under conditions such that the carbon combusts completely. It is preferably carried out using a gaseous oxidizing agent fed at a controlled rate to avoid over oxidation.
• gaseous oxidizing agents are steam, carbon dioxide, and gases containing molecular oxygen e.g. air.
• the oxidation is preferably carried out to give a carbon weight loss of at least 10 weight percent based on weight of carbon subjected to the oxidation step, more preferably at least 15 weight percent.
• the weight loss is preferably not greater than 40 weight percent of the carbon subjected to the oxidation step, more preferably not greater than 25 weight percent of the carbon.
• the rate of supply of oxidizing agent is preferably such that the desired weight loss takes place over at least 2 hours, more preferably at least 4 hours.
• inert atmosphere may be supplied by nitrogen or an inert gas.
• the loading levels of platinum and tin are generally referenced with the content of platinum and the weight ratio of Pt/Sn and is in the range of about 0.1 to 2.
• the weight ratio of Pt/Sn is 0.1
• the amount of platinum can be 0.1 or 1 weight percent and thus 1 or 10 weight percent of tin is present on the catalyst support.
• the weight ratio of Pt/Sn is about 0.5, and thus the amount of platinum on the catalyst support can be either 0.5 or 1 weight percent and that of tin is either one or two weight percent.
• the weight ratio of Pt/Sn is one.
• the amount of platinum on a support is 0.5, one or two weight percent and that of tin is also 0.5, one or two weight percent.
• low weight ratios of Pt/Sn can also be employed.
• a weight ratio of Pt/Sn of 0.2 can also be employed.
• the amount of platinum on the support can be 0.5 or one weight percent whereas 2.5 or five weight percent of tin is employed.
• the amount of third metal loading if present on a support is not very critical in this invention and can vary in the range of about 0.1 weight percent to about 10 weight percent.
• a metal loading of about 1 weight percent to about 6 weight percent based on the weight of the support is particularly preferred.
• the metal impregnation can be carried out using any of the known methods in the art. Typically, before impregnation the supports are dried at 120 0 C and shaped to particles having size distribution in the range of about 0.2 to 0.4 mm. Optionally the supports may be pressed, crushed and sieved to a desired size distribution. Any of the known methods to shape the support materials into desired size distribution can be employed.
• the metal solutions are added in excess until complete wetness or excess liquid impregnation so as to obtain desirable metal loadings.
• the hydrogenation catalysts used in the process of this invention are at least bimetallic containing platinum and tin.
• one metal acts as a promoter metal and the other metal is the main metal.
• combination of platinum and tin is considered to be main metal for preparing hydrogenation catalysts of this invention.
• platinum is the main metal and tin is the promoter metal depending upon various reaction parameters including but not limited to catalyst support employed, reaction temperature and pressure, etc.
• the main metal can be combined with a promoter metal such as tungsten, vanadium, molybdenum, chromium or zinc.
• main metal can also act as a promoter metal or vice versa.
• nickel can be used as a promoter metal when iron is used as a main metal.
• chromium can be used as a main metal in conjunction with copper (i.e., Cu-Cr as main bimetallic metals), which can further be combined with promoter metals such as cerium, magnesium or zinc.
• the bimetallic catalysts are generally impregnated in two steps. First, the "promoter” metal is added, followed by "main” metal. Each impregnation step is followed by drying and calcination.
• the bimetallic catalysts may also be prepared by co-impregnation. For instance, the platinum/tin catalysts of this invention are generally co-impregnated on a support catalyst. In the case of trimetallic Cu/Cr- containing catalysts as described above, a sequential impregnation may be used, starting with the addition of the "promoter" metal.
• the second impregnation step may involve co-impregnation of the two principal metals, i.e., Cu and Cr.
• Cu-Cr-Co on SiO 2 may be prepared by a first impregnation of chromium nitrate, followed by the co-impregnation of copper and cobalt nitrates. Again, each impregnation is followed by drying and calcinations. In most cases, the impregnation may be carried out using metal nitrate solutions. However, various other soluble salts which upon calcination releases metal ions can also be used.
• metal salts for impregnation include metal oxalate, metal hydroxide, metal oxide, metal acetate, ammonium metal oxide, such as ammonium heptamolybdate hexahydrate, metal acids, such as perrhenic acid solution, and the like.
• a hydrogenation catalyst wherein the catalyst support is graphite with a bimetallic loading of platinum and tin.
• the loading of platinum is about 0.5 weight percent to about 1 weight percent and the loading of tin is about 0.5 weight percent to about 5 weight percent.
• platinum/tin loading levels of 1/1, 1/5, 0.5/0.5, and 0.5/2.5 weight percent on graphite can be used.
• a hydrogenation catalyst wherein the catalyst support is high purity low surface area silica with a bimetallic loading of platinum and tin.
• the loading platinum is about 0.5 weight percent to about 1 weight percent and the loading of tin is about 0.5 weight percent to about 5 weight percent.
• platinum/tin loading levels of 1/1, 1/5, 0.5/0.5, and 0.5/2.5 weight percent on high purity low surface area silica can be used.
• a hydrogenation catalyst wherein the catalyst support is calcium silicate with a bimetallic loading of platinum and tin.
• the loading platinum is about 0.5 weight percent to about 1 weight percent and the loading of tin is about 0.5 weight percent to about 5 weight percent.
• platinum/tin loading levels of 1/1, 1/5, 0.5/0.5, and 0.5/2.5 weight percent on calcium silicate can be used.
• a hydrogenation catalyst wherein the catalyst support is a silica-alumina with a bimetallic loading of platinum and tin.
• the loading platinum is about 0.5 weight percent to about 1 weight percent and the loading of tin is about 0.5 weight percent to about 5 weight percent.
• platinum/tin loading levels of 1/1, 1/5, 0.5/0.5, and 0.5/2.5 weight percent on calcium silicate can be used.
• acetic acid can selectivity be converted to ethanol at very high rates.
• the selectivity to ethanol in general is very high and may be at least 60 percent.
• acetic acid is selectively converted to ethanol at a selectivity of at least 80 percent or more preferably at a selectivity of at least 90 percent. Most preferably ethanol selectivity is at least 95 percent.
• the conversion of acetic acid using the catalysts of this invention is at least 60% with selectivity to ethanol at least 80%, preferably 90% and most preferably 95%.
• the active catalysts of the invention are the non-promoted catalysts containing platinum and tin supported on silica with platinum and tin loadings of 1 weight percent each.
• acetic acid can be converted using these catalysts at conversions of around 90% with ethanol selectivity of at least 90%, more preferably selectivity to ethanol of at least 95%.
• the hydrogenation is carried out at a pressure just sufficient to overcome the pressure drop across the catalytic bed.
• the reaction may be carried out in the vapor or liquid state under a wide variety of conditions. Preferably, the reaction is carried out in the vapor phase.
• Reaction temperatures may be employed, for example in the range of about 200 0 C to about 300 0 C, preferably about 225°C to about 275 0 C.
• the pressure is generally uncritical to the reaction and subatmospheric, atmospheric or superatmospheric pressures may be employed. In most cases, however, the pressure of the reaction will be in the range of about 1 to 30 atmospheres absolute, most preferably the pressure of reaction zone is in the range of about 10 to 25 atmospheres absolute.
• the reaction consumes two moles of hydrogen per mole of acetic acid to produce a mole of ethanol
• the actual molar ratio of acetic acid to hydrogen in the feed stream may be varied between wide limits, e.g. from about 100: 1 to 1 : 100. It is preferred however that such ratio be in the range of about 1 :20 to 1 :2. More preferably the molar ratio of acetic acid to hydrogen is about 1 :5.
• the raw materials used in connection with the process of this invention may be derived from any suitable source including natural gas, petroleum, coal, biomass and so forth. It is well known to produce acetic acid through methanol carbonylation, acetaldehyde oxidation, ethylene oxidation, oxidative fermentation, and anaerobic fermentation and so forth. As petroleum and natural gas have become more expensive, methods for producing acetic acid and intermediates such as methanol and carbon monoxide from alternate carbon sources have drawn more interest. Of particular interest is the production of acetic acid from synthesis gas (syngas) that may be derived from any suitable carbon source.
• Syngas synthesis gas
• United States Patent No. RE 35,377 Steinberg et al. provides a method for the production of methanol by conversion of carbonaceous materials such as oil, coal, natural gas and biomass materials.
• the process includes hydrogasif ⁇ cation of solid and/or liquid carbonaceous materials to obtain a process gas which is steam pyrolized with additional natural gas to form synthesis gas.
• the syngas is converted to methanol which may be carbonylated to acetic acid.
• the method likewise produces hydrogen which may be used in connection with this invention as noted above. See also.
• United States Patent No. 5,821,111 Grady et al. which discloses a process for converting waste biomass through gasification into synthesis gas as well as United States Patent No. 6,685,754 Kindig et al., the disclosures of which are incorporated herein by reference.
• the acetic acid may be vaporized at the reaction temperature, and then it can be fed along with hydrogen in undiluted state or diluted with a relatively inert carrier gas, such as nitrogen, argon, helium, carbon dioxide and the like.
• a relatively inert carrier gas such as nitrogen, argon, helium, carbon dioxide and the like.
• acetic acid in vapor form may be taken directly as crude product from the flash vessel of a methanol carbonylation unit of the class described in United States Patent No. 6,657,078 oiScates et al., the disclosure of which is incorporated herein by reference.
• the crude vapor product may be fed directly to the reaction zones of the present invention without the need for condensing the acetic acid and light ends or removing water, saving overall processing costs.
• Contact or residence time can also vary widely, depending upon such variables as amount of acetic acid, catalyst, reactor, temperature and pressure. Typical contact times range from a fraction of a second to more than several hours when a catalyst system other than a fixed bed is used, with preferred contact times, at least for vapor phase reactions, between about 0.5 and 100 seconds.
• the catalyst is employed in a fixed bed reactor e.g. in the shape of an elongated pipe or tube where the reactants, typically in the vapor form, are passed over or through the catalyst.
• a fixed bed reactor e.g. in the shape of an elongated pipe or tube where the reactants, typically in the vapor form, are passed over or through the catalyst.
• Other reactors such as fluid or ebullient bed reactors, can be employed, if desired.
• a process for selective and direct formation of ethanol from acetic acid comprising: contacting a feed stream containing acetic acid and hydrogen at an elevated temperature with a suitable hydrogenating catalyst containing about 0.5 weight percent to about 1 weight percent of platinum and about 0.5 weight percent to about 5 weight percent of tin on a suitable catalyst support and optionally a third metal supported on said support and wherein said third metal is selected from the group consisting of cobalt, ruthenium and palladium.
• the preferred hydrogenation catalyst contains about one (1) weight percent platinum and about one (1) weight percent tin.
• the hydrogenation catalysts is layered in a fixed bed and the reaction is carried out in the vapor phase using a feed stream of acetic acid and hydrogen in the molar range of about 1 :20 to 1 :5 and at a temperature in the range of about 225 0 C to 275 0 C and at a pressure of reaction zones in the range of about 10 to 25 atmospheres absolute, and the contact time of reactants is in the range of about 0.5 and 100 seconds.
• Powdered and meshed high purity low surface area silica (100 g) of uniform particle size distribution of about 0.2 mm was dried at 12O 0 C in an oven under nitrogen atmosphere overnight and then cooled to room temperature.
• the resulting slurry was dried in an oven gradually heated to HO 0 C (>2 hours, 10°C/min.).
• the impregnated catalyst mixture was then calcined at 500 0 C (6 hours, l°C/min).
• Example B The procedures of Example B was substantially repeated except for utilizing a solution of platinum nitrate (Chempur) (1.64 g) in distilled water (16 ml) and a solution of tin oxalate (Alfa Aesar) (1.74 g) in dilute nitric acid (IN, 8.5 ml).
• Example B The procedures of Example B was substantially repeated except for utilizing a solution of platinum nitrate (Chempur) (1.64 g) in distilled water (16 ml) and a solution of tin oxalate (Alfa Aesar) (1.74 g) in dilute nitric acid (IN, 8.5 ml), and utilizing calcium silicate as a catalyst support.
• the analysis of the products was carried out by online GC.
• the front channel was equipped with an FID and a CP-SiI 5 (20 m) + WaxFFap (5 m) column and was used to quantify:
• the middle channel was equipped with a TCD and Porabond Q column and was used to quantify:
• the back channel was equipped with a TCD and Molsieve 5 A column and was used to quantify:
• the retention time of the different components was determined by spiking with individual compounds and the GCs were calibrated either with a calibration gas of known composition or with liquid solutions of known compositions. This allowed the determination of the response factors for the various components.
• the catalyst utilized was 1 weight percent platinum and 1 weight percent tin on silica prepared in accordance with the procedure of Example C.
• a feed liquid was comprised essentially of acetic acid.
• the reaction feed liquid was evaporated and charged to the reactor along with hydrogen and helium as a carrier gas with an average combined gas hourly space velocity (GHSV) of about 2500 hr "1 at a temperature of about 25O 0 C and pressure of 22 bar.
• the resulting feed stream contained a mole percent of acetic acid from about 4.4% to about 13.8% and the mole percent of hydrogen from about 14% to about 77%.
• a portion of the vapor effluent was passed through a gas chromatograph for analysis of the contents of the effluents. The selectivity to ethanol was 93.4% at a conversion of acetic acid of 85%.
• the catalyst utilized was 1 weight percent platinum and 1 weight percent tin on calcium silicate prepared in accordance with the procedure of Example D.
• Example 1 The procedure as set forth in Example 1 is substantially repeated with an average combined gas hourly space velocity (GHSV) of 2,500 hr "1 of the feed stream of the vaporized acetic acid and hydrogen at a temperature of 25O 0 C and pressure of 22 bar. A portion of the vapor effluent is passed through a gas chromatograph for analysis of the contents of the effluents.
• GHSV gas hourly space velocity
• the acetic acid conversion is greater than 70% and ethanol selectivity is 99%.
• the catalyst utilized was 1 weight percent tin on low surface area high purity silica prepared in accordance with the procedure of Example F.
• the procedure as set forth in Example 1 is substantially repeated with an average combined gas hourly space velocity (GHSV) of 2,500 hr "1 of the feed stream of the vaporized acetic acid and hydrogen at a temperature of 25O 0 C and pressure of 22 bar.
• GHSV gas hourly space velocity
• a portion of the vapor effluent is passed through a gas chromatograph for analysis of the contents of the effluents.
• the acetic acid conversion is less than 10% and ethanol selectivity is less than 1%.

Landscapes

• Chemical & Material Sciences (AREA)
• Organic Chemistry (AREA)
• Engineering & Computer Science (AREA)
• Materials Engineering (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Physics & Mathematics (AREA)
• Thermal Sciences (AREA)
• Organic Low-Molecular-Weight Compounds And Preparation Thereof (AREA)
• Catalysts (AREA)
• Low-Molecular Organic Synthesis Reactions Using Catalysts (AREA)

Priority Applications (13)

Applications Claiming Priority (2)

Publications (2)

Family

ID=41354066

Family Applications (1)

Country Status (22)

Cited By (39)

Families Citing this family (202)

Citations (7)

Family Cites Families (77)

• 2008
  • 2008-07-31 US US12/221,141 patent/US7863489B2/en not_active Expired - Fee Related
• 2009
  • 2009-07-20 CN CN200980134831.5A patent/CN102149661B/zh not_active Expired - Fee Related
  • 2009-07-20 DK DK09788951.3T patent/DK2318343T3/da active
  • 2009-07-20 PT PT09788951T patent/PT2318343E/pt unknown
  • 2009-07-20 CA CA2732359A patent/CA2732359C/en not_active Expired - Fee Related
  • 2009-07-20 WO PCT/US2009/004195 patent/WO2010014151A2/en not_active Ceased
  • 2009-07-20 AU AU2009277189A patent/AU2009277189B2/en not_active Ceased
  • 2009-07-20 RU RU2011107274/04A patent/RU2011107274A/ru not_active Application Discontinuation
  • 2009-07-20 JP JP2011521095A patent/JP5611205B2/ja not_active Expired - Fee Related
  • 2009-07-20 KR KR1020117004459A patent/KR101650966B1/ko not_active Expired - Fee Related
  • 2009-07-20 EP EP11179239A patent/EP2392557A3/en not_active Withdrawn
  • 2009-07-20 EP EP11179217A patent/EP2392556A3/en not_active Withdrawn
  • 2009-07-20 SG SG10201506032XA patent/SG10201506032XA/en unknown
  • 2009-07-20 NZ NZ598774A patent/NZ598774A/xx not_active IP Right Cessation
  • 2009-07-20 ES ES09788951T patent/ES2382984T3/es active Active
  • 2009-07-20 UA UAA201101076A patent/UA100576C2/ru unknown
  • 2009-07-20 CN CN201110295829.5A patent/CN102311311B/zh not_active Expired - Fee Related
  • 2009-07-20 SG SG2012006938A patent/SG178732A1/en unknown
  • 2009-07-20 PL PL09788951T patent/PL2318343T3/pl unknown
  • 2009-07-20 CN CN201110294935.1A patent/CN102304018B/zh not_active Expired - Fee Related
  • 2009-07-20 EP EP09788951A patent/EP2318343B1/en not_active Not-in-force
  • 2009-07-20 AT AT09788951T patent/ATE547391T1/de active
  • 2009-07-20 NZ NZ591029A patent/NZ591029A/xx not_active IP Right Cessation
  • 2009-07-31 AR ARP090102961A patent/AR074712A1/es not_active Application Discontinuation
  • 2009-07-31 TW TW098125951A patent/TWI432406B/zh not_active IP Right Cessation
• 2010
  • 2010-09-16 US US12/884,005 patent/US8071821B2/en not_active Expired - Fee Related
• 2011
  • 2011-01-30 IL IL210945A patent/IL210945A0/en not_active IP Right Cessation
  • 2011-01-31 ZA ZA2011/00792A patent/ZA201100792B/en unknown
  • 2011-07-11 US US13/179,955 patent/US8669400B2/en not_active Expired - Fee Related
  • 2011-07-19 CO CO11090456A patent/CO6541518A2/es not_active Application Discontinuation
• 2012
  • 2012-02-15 JP JP2012030784A patent/JP5611252B2/ja not_active Expired - Fee Related

Patent Citations (8)

Also Published As

Similar Documents

Legal Events