WO2007060978A1 - 等速ジョイント用グリース組成物及び等速ジョイント - Google Patents

等速ジョイント用グリース組成物及び等速ジョイント Download PDF

Info

Publication number
WO2007060978A1
WO2007060978A1 PCT/JP2006/323289 JP2006323289W WO2007060978A1 WO 2007060978 A1 WO2007060978 A1 WO 2007060978A1 JP 2006323289 W JP2006323289 W JP 2006323289W WO 2007060978 A1 WO2007060978 A1 WO 2007060978A1
Authority
WO
WIPO (PCT)
Prior art keywords
constant velocity
velocity joint
component
mass
grease
Prior art date
Application number
PCT/JP2006/323289
Other languages
English (en)
French (fr)
Inventor
Mitsuhiro Kakizaki
Shinya Kondo
Shinichi Takabe
Takaaki Shibata
Original Assignee
Kyodo Yushi Co., Ltd.
Ntn Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kyodo Yushi Co., Ltd., Ntn Corporation filed Critical Kyodo Yushi Co., Ltd.
Priority to EP06833111A priority Critical patent/EP1953213B1/en
Priority to CN2006800479306A priority patent/CN101341236B/zh
Publication of WO2007060978A1 publication Critical patent/WO2007060978A1/ja
Priority to US12/124,916 priority patent/US8377858B2/en
Priority to US13/681,859 priority patent/US8530396B2/en

Abstract

　下記の成分（ａ）～（ｇ）を含む等速ジョイント用グリース組成物及びこれを封入した等速ジョイントを提供する。 （ａ）下記一般式（１）で表されるジウレア系増ちょう剤、 Ｒ1ＮＨ-ＣＯ-ＮＨ-Ｃ6Ｈ4-ｐ-ＣＨ2-Ｃ6Ｈ4-ｐ-ＮＨ-ＣＯ-ＮＨＲ2　　（１） （式中、Ｒ1とＲ2は同一もしくは異なる、炭素数８～２０のアルキル基を表す。） （ｂ）エステル系合成油、（ｃ）鉱油および／または合成炭化水素油、（ｄ）ジアルキルジチオカルバミン酸モリブデン、（ｅ）二硫化モリブデン、（ｆ）ポリテトラフルオロエチレン、及び（ｇ）ジチオリン酸亜鉛化合物。本発明のグリース組成物は、等速ジョイントの低温時の回転抵抗変動を低減する。

Description

等速ジョイント用グリース組成物及び等速ジョイント
技術分野
[0001] 本発明は、等速ジョイントの低温時の回転抵抗変動を低減する等速ジョイント用ダリ ース組成物及びこれを封入した等速ジョイントに関する。詳しくは、自動車用ドライブ シャフトに使用されている固定型等速ジョイントまたはスライド型等速ジョイントの低温 時の回転抵抗変動を低減するのに好適な等速ジョイント用グリース組成物及びこれ を封入した等速ジョイントに関する。
背景技術
[0002] 今日、自動車産業界においては、軽量化及び居住空間の確保の観点から、 FF車 の生産が増加している。また、その機能性の観点力 4WD車も増加している。これら FF車や 4WD車では、前輪にて動力の伝達と操舵を行うため、例えば、ハンドルを一 杯に切った状態でも円滑な動力伝達が必要であり、交差する二軸間で交差角が種 々変化しても回転運動を等速で伝達する部品として等速ジョイントが不可欠である。 近年、自動車の高性能化がますます進み、高出力車が増カロしていることから、等速 ジョイントにかかる負荷も増大し、その潤滑条件がより過酷になる傾向がある。一方で 、自動車の乗り心地の向上も更に高度なレベルを要求される傾向にある。その乗り心 地の向上は、厳暑地から厳寒地に至るまで、あらゆる気候の地域において必要とさ れる。
[0003] 厳寒地では、極低温状態で自動車を始動させることも考えられる。この条件下にお いて、等速ジョイントが回転する際に、等速ジョイントを構成する部品間の摩擦抵抗の 違いから回転抵抗に変動が生じる場合がある。回転抵抗に変動が生じると、ステイツ クスリップ音を発生させる場合があり、乗り心地を低下させる要因になる。
従来、潤滑剤としては基油として鉱物油、添加剤としてモリブデン化合物を含有す る等速ジョイント用グリース糸且成物が開示されて 、る（例えば特許文献 1および 2参照 ) oしかし、極低温時に種々の要因が重なりあった際には、これらの等速ジョイント用 グリース組成物では回転抵抗変動を低減する性能が不十分となる場合があり、より安 定した性能への改善が望まれる。
[0004] 特許文献 1 :特開平 10— 273692
特許文献 2 :特開 2003— 165988
発明の開示
発明が解決しょうとする課題
[0005] 本発明の目的は、等速ジョイントの低温時の回転抵抗変動を低減する等速ジョイン ト用グリース組成物を提供することである。
本発明の他の目的は、上記等速ジョイント用グリース組成物を封入した等速ジョイン トを提供することである。
課題を解決するための手段
[0006] 本発明者らは上記目的を達成するために鋭意研究した結果、特定の成分を含有し たグリース組成物が等速ジョイントの低温時の回転抵抗変動を低減するとの知見を得 、本発明を完成した。
[0007] 即ち、本発明は以下に示す等速ジョイント用グリース組成物、及びこれを封入した 等速ジョイントを提供するものである。
[0008] 1.下記の成分 (a)〜(g)を含むことを特徴とする等速ジョイント用グリース糸且成物。
(a)下記一般式（1)で表されるジゥレア系増ちよう剤、
R^H-CO-NH-C H -p-CH - C H - p- NH- CO- NHR (1)
6 4 2 6 4
(式中、 R1と R2は同一もしくは異なる、炭素数 8〜20のアルキル基を表す。 )
(b)エステル系合成油、
(c)鉱油および Zまたは合成炭化水素油、
(e)二硫ィ匕モリブデン、
(f)ポリテトラフルォロエチレン、及び
(g)ジチォリン酸亜鉛ィ匕合物。
[0009] 2.全糸且成物中、成分（a)の含有量が 1〜20質量％、成分 (b)の含有量が 5〜40質 量％、成分 (c)の含有量力 0〜80質量％、成分 (d)の含有量が 0. 1〜10質量％、 成分 (e)の含有量が 0. 1〜10質量％、成分 (f)の含有量が 0. 1〜10質量％ぉよび 成分 ）の含有量が 0. 1〜10質量％であることを特徴とする上記 1に記載の等速ジ ョイント用グリース組成物。
3.成分 (b)が 3価以上の多価アルコールとカルボン酸力 得られる合成エステル油 であることを特徴とする上記 1または 2に記載の等速ジョイント用ダリース組成物。
4.成分 (b)の合成エステル油の流動点が—40°C以下であることを特徴とする上記 1 〜3のいずれか 1項に記載の等速ジョイント用グリース組成物。
5.成分 (b)の合成エステル油の 40°Cにおける動粘度が 40mm2/s以上であることを 特徴とする上記 1〜4のいずれ力 1項に記載の等速ジョイント用グリース組成物。
6.等速ジョイントのトルク伝達部材が球体である上記 1〜 5の 、ずれか 1項に記載の 等速ジョイント用ダリ一ス糸且成物。
7.等速ジョイントが固定型等速ジョイントである上記 1〜6のいずれ力 1項に記載の等 速ジョイント用ダリ一ス糸且成物。
8.等速ジョイントがスライド型等速ジョイントである上記 1〜6のいずれか 1項に記載 の等速ジョイント用グリース糸且成物。
9.上記 1〜8の 、ずれか 1項に記載の等速ジョイント用ダリース組成物を封入してな る等速ジョイント。
発明の効果
[0010] 本発明の等速ジョイント用グリース糸且成物は、自動車用ドライブシャフトに使用され て 、る固定型等速ジョイントまたはスライド型等速ジョイントなどの等速ジョイントの低 温時における回転抵抗変動を低減するために非常に有用である。また、本発明はそ の優秀な性能を有する等速ジョイント用グリース組成物を封入してなる等速ジョイント をも提供する。
近年の経済発展に伴い、等速ジョイントの使用環境が拡大し、要求性能も多様ィ匕し てきている中、厳寒地における等速ジョイントの円滑な作動も重要視される。しかし、 低温時の回転抵抗変動を十分低減することが可能な等速ジョイント用グリース組成物 は未だに提案されていない。このような状況下において、本発明の低温時の回転抵 抗変動を低減する等速ジョイント用グリース組成物は極めて有用な発明と言える。
[0011] 本発明は特定の成分を含有してなる等速ジョイント用グリース糸且成物が上記目的を 達成し得るという知見に基づいてなされたものである。本発明の等速ジョイント用ダリ ース組成物が低温時の回転抵抗変動の低減効果に優れている理由としては、増ちよ う剤として特定のゥレア化合物、基油として特定の合成油を使用し、添加剤として特 定のモリブデンィ匕合物、ジチォリン酸亜鉛ィ匕合物、ポリテトラフルォロエチレンを添カロ したことにより低温時の流動性、粘性および潤滑性等が最適化され回転抵抗変動が 低減したと考えられる。
発明を実施するための最良の形態
[0012] 以下、本発明について詳細に説明する。
本発明の等速ジョイント用グリース糸且成物とは、等速ジョイントに用いるためのダリー ス状組成物をいう。ここで、等速ジョイントとは、交差する二軸間で交差角が種々変化 しても回転運動を等速度で伝達する部品をいう。また、グリースとは基油中に増ちよう 剤を分散させて半固体または固体状にしたものをいう。
本発明に係る等速ジョイント用グリース組成物は、成分 (a)〜成分 (g)を必須成分と して含むことを特徴とする。以下、これらの各成分について説明する。
[0013] まず、本発明に使用する成分 (a)のジゥレア系増ちよう剤は、下記一般式（1)で表さ れるものである。
R^H-CO-NH-C H -p-CH - C H - p- NH- CO- NHR2 (1)
6 4 2 6 4
(式中、 R1と R2は同一もしくは異なる炭素数 8〜20のアルキル基を表す。 )
[0014] 成分 (a)のジゥレア系増ちよう剤は、例えば、所定のジイソシァネートと、所定のモノ ァミンとを反応させることにより得ることができる。ジイソシァネートは、具体的には、ジ フエ-ルメタン 4, 4'ージイソシァネートである。
モノアミンとしては、脂肪族ァミン、芳香族ァミン、脂環式ァミン又はこれらの混合物 が挙げられる。脂肪族ァミンの具体例としては、ォクチルァミン、ドデシルァミン、へキ サデシルァミン、ォクタデシルァミン及びォレイルァミンが挙げられる。芳香族ァミンの 具体例としては、ァ-リン及び p トルィジンが挙げられる。脂環式ァミンの具体例とし ては、シクロへキシルァミンが挙げられる。上述したモノアミンのうち、ォクチルァミン、 ドデシルァミン、へキサデシルァミン、ォクタデシルァミン又はこれらの混合物を用い て得られるジゥレア系増ちよう剤が好まし 、。 [0015] 全糸且成物の質量をベースとする成分 (a)のジゥレア系増ちよう剤の含有量は、その 種類により異なる。本発明のグリース組成物のちょう度は、 250〜350の範囲にある のが好適であり、従って、成分 (a)のジゥレア系増ちよう剤の含有量は、このようなちょ う度を得るのに必要な量であるのが好ましい。全組成物の質量をベースとする成分 (a )のジゥレア系増ちよう剤の含有量は、例えば、 1〜20質量0 /0とすることができ、 2〜2 0質量％とするのが好ましいが、これらに限定される訳ではない。
[0016] 本発明に使用する成分 (b)のエステル系合成油は、トリメリト酸エステルおよびポリ オールエステルに代表される力 特に 3価以上の多価アルコールとカルボン酸力 得 られる合成エステル油であって、流動点が 40°C以下であるもの、 40°Cにおける動 粘度が 40mm2/s以上のものが好まし 、。全組成物の質量をベースとする成分 (b)の エステル系合成油の含有量は、例えば、 5〜40質量％とすることができ、 10〜40質 量％とするのが好ま 、が、これらに限定される訳ではな 、。
[0017] 本発明に使用する成分 (c)の鉱油および Zまたは合成炭化水素油は、基油として 、鉱油、合成油を単独で用いてもよぐあるいは、これらを組み合せて用いてもよい。 全糸且成物の質量をベースとする成分 (c)鉱油および Zまたは合成炭化水素油の含 有量は、残部、即ち、任意成分を含む他の全成分を加えた残りの量とすることができ る。
[0018] 本発明に使用する成分 (d)のジアルキルジチォ力ルバミン酸モリブデンとしては、 下記一般式（2)で表されるものが好ま 、。
(R3R4N-CS-S) -Mo O S (2)
2 2 m n
(式中、 R3及び R4は、それぞれ独立して、例えば、炭素数 1〜24、好ましくは、炭素 数 2〜 18のァノレキノレ基であり、 mは 0〜3、 nは 1〜4であり、 m+n=4である） 全組成物の質量をベースとする成分（d)のジアルキルジチォカルノミン酸モリブデ ンの含有量は、好ましくは 0. 1〜10質量％であり、さらに好ましくは 0. 5〜5質量％ である。
[0019] 本発明に使用する成分 (e)の二硫ィ匕モリブデンは、一般に、等速ジョイントにおける 固体潤滑剤として広く用いられている。その潤滑機構としては、層状格子構造を持ち 、すべり運動により薄層状に容易に剪断し、摩擦抵抗を低下させることが知られてい る。また、等速ジョイントの焼き付き防止にも効果がある。
全組成物の質量をベースとする成分 (e)の二硫ィ匕モリブデンの含有量は、好ましく は、 0. 1〜10質量％であり、さらに好ましくは 0. 5〜5質量％である。その添カ卩量は、 摩擦係数や等速ジョイントの振動特性などに悪影響を及ぼさない程度のものとするの がよい。
[0020] 本発明に使用する成分 (f)のポリテトラフルォロエチレンは、グリース以外にもゴム、 塗料、インク、潤滑剤等の分野でも一般的に使用されているものであり、分子量が数 千〜数 10万のものが用いられる。ポリテトラフルォロエチレンの凝集エネルギーは他 の高分子化合物に比べて小さぐしかも臨界界面張力が非常に低いため、摺動部に 存在するポリテトラフルォロエチレン粒子は摺動によるせん断応力によって微小薄片 となり、摺動部の相手材に展着しやすい性質を持っており、これにより優れた潤滑性 を与えるものと考えられる。全組成物の質量をベースとする成分 (f)のポリテトラフル ォロエチレンの含有量は、好ましくは 0. 1〜10質量0 /0であり、さらに好ましくは 0. 5 〜5質量％である。
[0021] 本発明に使用する成分 (g)のジチォリン酸亜鉛ィ匕合物は、ジアルキルジチォリン酸 亜鉛、ジァリールジチォリン酸亜鉛等である。全組成物の質量をベースとする成分 (g )のジチォリン酸亜鉛ィ匕合物の含有量は、好ましくは 0. 1〜： LO質量％であり、さらに 好ましくは 0. 5〜5質量％である。
本発明のグリース組成物には、上記成分に加えて、他の極圧添加剤、酸化防止剤 、鲭止め剤、防食剤等、通常グリース組成物に使用される添加剤を含有させることが できる。
[0022] 本発明に係る等速ジョイントのトルク伝達部材が球体である等速ジョイントとは、例え ば、ツエッパ型、バーフィールド型などの固定型等速ジョイントやダブルオフセット型、 クロスグループ型などのスライド型等速ジョイントなどが挙げられる。これらは、トルク 伝達部材としてボールを用い、等速ジョイントの外輪及び内輪に形成されたトラック上 に配置され、ケージを介して組み込まれる構造を成して 、る。
[0023] 本発明に係る等速ジョイントが固定型等速ジョイントである等速ジョイントとは、例え ば、上述のツエッパ型、バーフィールド型などの固定型等速ジョイントなどが挙げられ 、 45度以上の大きな作動角を取ることが可能である。
本発明に係る等速ジョイントがスライド型等速ジョイントである等速ジョイントとは、例 えば、上述のダブルオフセット型、クロスグループ型などのスライド型等速ジョイントが 挙げられ、作動角を固定型等速ジョイントほど取ることはできないが、軸線方向にスラ イドすることが可會である。
[0024] 以下、実施例によって本発明をさらに詳述するが、下記実施例は本発明を制限す るものではなぐ本発明の趣旨を逸脱しない範囲で変更実施することは全て本発明 の技術範囲に包含されて 、る。
実施例
[0025] 〔実施例 1〜4、比較例 1〜4〕
グリース 成物の調製
(c)鉱油（100°Cで l lmm2Zsの動粘度を有するもの） 3, 700g中で、ジフヱ-ルメ タン- 4, 4，-ジイソシァナート 250g (lモル）、ォクチルァミン 129g (lモル）及びォクタ デシルァミン 270g ( 1モル)を反応させ、生成した (a)ジゥレア系化合物を均一に分散 させてベースグリースを得た。このベースグリースに、表 1又は表 2に示す配合となる ように基油と添加剤を加え、三段ロールミルにて混練し、 JIS 2220混和ちよう度 300 に調整した。
[0026] 表 1に実施例及び表 2に比較例の試験品配合割合とその 40°Cにおける回転トル ク変動の結果を示した。
[0027] [表 1]
Figure imgf000009_0001
[0028] [表 2]
Figure imgf000009_0002
[0029] * 1)エステル油：トリメリット酸トリアルキルエステル、流動点 50°C、 40°C動粘度 53
2 /
mm Z s
* 2)合成炭化水素油：ポリアルファオレフイン油、 40°C動粘度 420mm2Zs
* 3)ジアルキルジチォ力ルバミン酸モリブデン：
(R3R4N-CS-S) -Mo O S (式中、 R3及び R4は炭素数 1〜4のアルキル基であり
2 2 m n
、 mは 0〜3、 nは 1〜4であり、 m+n=4である）
* 4)二硫化モリブデン（平均粒径 0. 45 ^ m) * 5)ポリテトラフルォロエチレン（平均粒径 0. 2 μ η
* 6)ジチォリン酸亜鉛ィ匕合物：ジアルキルジチォリン酸亜鉛
[0030] 回転トルク変動試験
—40°C雰囲気下にて等速ジョイントを放置し、 Θ =40degにて回転起動した時の 出力軸側のトルク変動幅を測定する。なお、本試験は固定型等速ジョイントを用いて 評価を行った。出力軸側のトルク変動幅については、平均トルクに対する以下の評 価基準で判断した。
〇:合格 （変動幅 20%未満）
X：不合格 (変動幅 20%以上）
[0031] ¾
以上から、本発明の実施例 1〜4の等速ジョイント用グリース組成物力 成分 (b)、 ( d)、（f)又は (g)を含まない比較例 1〜4のものに比べ、低温時の回転抵抗変動を低 減するのに非常に優れた性能を示していることがわかる。

Claims

請求の範囲
[1] 下記の成分 (a)〜 (g)を含むことを特徴とする等速ジョイント用グリース糸且成物。
(a)下記一般式（1)で表されるジゥレア系増ちよう剤、
R^H-CO-NH-C H -p-CH - C H - p- NH- CO- NHR2 (1)
6 4 2 6 4
(式中、 R1と R2は同一もしくは異なる、炭素数 8〜20のアルキル基を表す。 )
(b)エステル系合成油、
(c)鉱油および Zまたは合成炭化水素油、
(e)二硫ィ匕モリブデン、
(f)ポリテトラフルォロエチレン、及び
(g)ジチォリン酸亜鉛ィ匕合物。
[2] 全組成物中、成分 (a)の含有量力^〜 20質量％、成分 (b)の含有量が 5〜40質量
%、成分 (c)の含有量が 40〜80質量％、成分 (d)の含有量が 0. 1〜10質量％、成 分 (e)の含有量が 0. 1〜10質量％、成分 (f)の含有量が 0. 1〜10質量％および成 分 (g)の含有量が 0. 1〜10質量％であることを特徴とする請求項 1に記載の等速ジ ョイント用グリース組成物。
[3] 成分 (b)が 3価以上の多価アルコールとカルボン酸力 得られる合成エステル油で あることを特徴とする請求項 1または 2に記載の等速ジョイント用グリース組成物。
[4] 成分 (b)の合成エステル油の流動点が— 40°C以下であることを特徴とする請求項
1〜3のいずれか 1項に記載の等速ジョイント用グリース組成物。
[5] 成分 (b)の合成エステル油の 40°Cにおける動粘度が 40mm2/s以上であることを特 徴とする請求項 1〜4のいずれ力 1項に記載の等速ジョイント用グリース組成物。
[6] 等速ジョイントのトルク伝達部材が球体である請求項 1〜5の 、ずれか 1項に記載の 等速ジョイント用ダリ一ス糸且成物。
[7] 等速ジョイントが固定型等速ジョイントである請求項 1〜6のいずれか 1項に記載の 等速ジョイント用ダリ一ス糸且成物。
[8] 等速ジョイントがスライド型等速ジョイントである請求項 1〜6のいずれか 1項に記載 の等速ジョイント用グリース糸且成物。 請求項 1〜8のいずれか 1項に記載の等速ジョイント用グリース組成物を封入してな る等速ジョイント。
PCT/JP2006/323289 2005-11-22 2006-11-22 等速ジョイント用グリース組成物及び等速ジョイント WO2007060978A1 (ja)