WO2004084234A1 - 遮蔽材 - Google Patents

遮蔽材

Info

Publication number
WO2004084234A1
WO2004084234A1 PCT/JP2003/003288 JP0303288W WO2004084234A1 WO 2004084234 A1 WO2004084234 A1 WO 2004084234A1 JP 0303288 W JP0303288 W JP 0303288W WO 2004084234 A1 WO2004084234 A1 WO 2004084234A1
Authority
WO
WIPO (PCT)
Prior art keywords
shielding
fiber
shielding material
metal
reinforcing
Prior art date
Application number
PCT/JP2003/003288
Other languages
English (en)
French (fr)
Inventor
Kenji Okamura
Masahiro Yamauchi
Shigeru Matsuo
Shigeya Sakaguchi
Original Assignee
Nippon Tungsten Co., Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Tungsten Co., Ltd. filed Critical Nippon Tungsten Co., Ltd.
Priority to EP03816363A priority Critical patent/EP1605470A4/en
Priority to US10/549,835 priority patent/US7518137B2/en
Priority to CNA038262940A priority patent/CN1764987A/zh
Priority to AU2003220914A priority patent/AU2003220914A1/en
Priority to JP2004569570A priority patent/JPWO2004084234A1/ja
Priority to PCT/JP2003/003288 priority patent/WO2004084234A1/ja
Publication of WO2004084234A1 publication Critical patent/WO2004084234A1/ja

Abstract

放射線または電磁波に対して高遮蔽能を有し、曲げ加工性と取扱性に優れ、且つ、難燃性である鉛を含有しない遮蔽材を提供する。放射線または電磁波に対して遮蔽能を有する金属および金属化合物と有機物との複合物を板状等に成形し、この成形体をガラス繊維、金属繊維、カーボン繊維等からなる布状シートで包み込んだ遮蔽材である。また、重金属、フェライトのような高遮蔽能を有する粒子と弾性を有する高分子有機化合物とからなる遮蔽材の表面、内部、または、表面近傍にポリエチレン、ナイロン、ポリエステル、金属などのフィルム、ナイロン繊維、金属繊維などのワイヤーメッシュ、あるいは、表面に突起を有する板状または棒状材を圧着した遮蔽材である。

Description

明 細 書 遮蔽材 技術分野
本発明は、 放射線あるいは電磁波を遮蔽するための遮蔽材に関する。 背景技術
従来から、 放射線の遮蔽材としては、 密度が高く遮蔽能力に優れていること から鉛および鉛合金が多く用いられてきた。 ところが、 この鉛および鉛合金は 厚みが増すと変形加工が困難であることから、 塑性加工を要する箇所のための 遮蔽材として使用し難いという問題があった。 近年、 変形加工が可能な鉛遮蔽 材として、 細い繊維状のいわゆる鉛毛の集合体が使用されるようになった； し かしながら、 この鉛毛を使用することにより、 変形は容易になるが、 加工の程 度が大きくなるにつれて密度が下がり、 そのため、 遮蔽性能は低下するという 問題が生じた。 また、 鉛そのものが人体に対して有害であることからも、 その 使用は制限されるようになってきている。 そのため、 遮蔽材として鉛を使用し ない材料が求められるようになった。
また、 電磁波の遮蔽には重金属板や酸化鉄のようなそれ自体が遮蔽能を有す る遮蔽粉末を練り込んだ樹脂が用いられている。 しかしながら、 これは、 変形 加工が困難であり、 また、 遮蔽粉末を練り込んだ樹脂は破れやすく取り扱いに 特別の注意を要する欠点がある。
これら従来の鉛に代わる遮蔽材の欠点を解消するために、 環境衛生上と柔軟 性についての要求を満たすべく金属と有機物の複合物からなる遮蔽材が、 特開 平 0 8— 1 2 2 4 9 2号公報に開示されている。
しかしながら、 金属と有機物の複合物は、 実際には、 取り扱いに際して破損 したり亀裂が入ったりするために、 従前と同様に、 取り扱いに際して特別の注 意を払う必要がある。 その対策として、 髙強度の有機物を選択したり、 その含 有量を増やすこともできるが、 その反面柔軟性が失われ、 また、 密度が下がり 遮蔽性能の低下を招く。 さらに、 金属と有機物の複合物は、 火災や異常過熱の 際に燃えやすいという欠点もある。 発明の開示
本発明の概念的な目的は、 係る従来の遮蔽材の欠点を解消することにある。 具体的には、 本発明の第 1の目的は、 鉛を使用せずに、 放射線遮蔽能力または 電磁波遮蔽能力の高い遮蔽材を得ることにある。
本発明の他の目的は、 高密度で嵩張ることのない遮蔽材を得ることにある。 また、 本発明の他の目的は、 強度を向上させ、 引き裂きや衝撃に容易に破壊 しなくなり、 取り扱いが簡単になる遮蔽物と有機物との複合物からなる遮蔽材 を得ることにある。
さらに、 本発明の他の目的は、 曲げ加工中、 あるいは、 折り曲げに際して割 れ難い鉛を使用しない遮蔽材を得ることにある。
本発明に係る遮蔽材は、 放射線、 電磁波を遮蔽する機能を有する分散用粉末 と分散基材としての有機物との複合物からなる柔軟性を有する板状体のような 成形体を難燃性繊維シートによつて包み込むことにより、 難燃性と取り扱い時 の強度を向上させたものである。 また、 本発明の遮蔽材は、 柔軟性に富むため に変形加工が容易であり、 複雑な形状を有する遮蔽対象物を隙間なく遮蔽する ことができ、 複雑な表面形状を有する対象物からの各種放射線あるいは電磁波 を遮蔽することができる。
また、 本発明に係る遮蔽材は、 放射線あるいは電磁波に対して遮蔽機能を有 する粒子と弾性を有する高分子有機化合物粒子との複合体の表面あるいは内部 に補強材を配して一体化したことによって、 曲げあるいは折り曲げ加工に対す る強度を向上させたものである。
有機物基材に分散混合すべき遮蔽物質と、 有機物は、 要求される遮蔽能力や 使用温度などの適用環境から適宜選択することができる。 とくに、 放射線の遮 蔽に関しては、 放射線の遮蔽能力は主に遮蔽部材の密度に比例する。 例えば、 タングステンまたはモリブデンは密度が大きく、 遮蔽能力が非常に高く、 同じ 体積の鉛の 1 . 4倍程度の遮蔽能を有す。 また、 同じく炭化タングステンやそ の他のタンダステン合金やタンダステン化合物、 その他の重金属化合物もタン ダステンやモリブデンなどのその他の高密度の粉末と混合しても同等の効果を 得ることができる。
また、 電磁波を遮蔽するためには、 有機物に混合する遮蔽用分散材としては、 鉄材、 酸化鉄、 酸化チタン、 チタン酸バリウムのような金属化合物の磁性体の 粉末が適している。 電磁波を遮蔽するためには、 その表面で反射させるか、 あ るいは、 遮蔽材に吸収させるかの何れかの作用を利用するものであるが、 とく に、 電磁波測定器への適用に際しては、 反射による遮蔽では、 反射した電磁波 が他の機器に影響を与える可能性があるために、 できるだけ吸収による遮蔽が 望ましい。 そのため、 磁性体の金属化合物を使用した場合は、 電磁波を熱に変 換して遮蔽材に取り込む働きがあるので好適である。
また、 本発明で使用する有機物は、 柔軟性を有し、 前記金属および金属の酸 化物と馴染みやすい材料が適しており、 エラストマ一樹脂、 加硫ゴム、 軟質プ ラスチックなどを用いるのがよい。
上記遮蔽能を有する複合物の成形体を包み込む難燃性布状シートとしては、 ガラス繊維、 金属繊維、 力一ボン繊維、 あるい'は、 セラミックス繊維など難燃 性繊維を布状に編んだもののような、 引き裂きに強く、 柔軟性を持ち、 難燃性 を有する繊維部材が使用できる。 この繊維部材を前記の遮蔽機能を有する複合 物の成形体を密封状態で包み込むことにより、 前記複合物を構成する有機物へ の酸素の供給を遮断し、 さらに難燃性を高める。 この際、 上記繊維からなる布 状のシートは、 塩ィヒビニールのような非通気性のコーティング材でコートする のが良い。
本発明の遮蔽材の製造に際しての難燃性を有する布状物への成形遮蔽材.の包 み込みは、 任意の種々の方法を採用できる。 例えば、 難燃性布材を袋状に整形 加工を行い、 混合物の成形体を袋内に封入する方法、 あらかじめ混合材を布材 で包み、 最終形状に一体成形する方法、 2枚以上の布材の間に混合物の成形体 を挿入しておき、 外周部をとじ合わせ一体にする方法などを採用できる。 布材 を綴じ合わせるには、 外周部を高強度のナイロン、 ガラス繊維、 金属繊維など の糸で鏠合する方法や、 ウェルダーによって加熱、 加圧圧着する方法、 さらに は、 接着剤を使用して張り合わせる方法も採用できる。
さらに、 補強材としては、 ポリエチレン、 ナイロン、 ポリエステル、 金属な どのラミネートフィルム、 ナイロン繊維、 金属繊維などのワイヤーメッシュ、 あるいは、 表面に突起を有する板状または棒状材を適用できる。 これらの補強 材を適用することによって、 曲げやせん断に強く、 少ない体積で補強された遮 蔽材とすることができる。 したがって、 補強材の適用によっても遮蔽材として の密度の低下はごく少なく、 その放射線あるいは電磁波に対する遮蔽能の低下 はほとんどない。 補強材は、 遮蔽材の形状に合わせて切断して使用する。
遮蔽材と補強材を一体化する手段としては、 遮蔽材に補強材を接触させた状 態で熱を加えて部分的に溶融して一体化する方法、 両者を接着剤にて接着して 一体化する方法、 遮蔽材に補強材を貼り付ける方法、 2つ以上の遮蔽材の間に 補強材を挟み熱および圧力を掛け一体化させる方法など、 さまざまな方法を採 ることができる。
また、 補強材と一体化した遮蔽材を、 前記の布状シートに包み込んだ構造の ものに適用することによって、 折り畳んでの搬送や保管に際しての破れや割れ に対する対抗性を増大できる。 図面の簡単な説明
図 1は遮蔽材の片側表面に補強材を施した例を、 図 2は遮蔽材の内部に補強 材を施した例を、 図 3は、 遮蔽材の表面近傍に補強材を埋め込んだ例を、 図 4 は一定以上曲がらない機能を有する補強材を片面に施した遮蔽材の例を、 （a ) . においては通常時、 また、 （b ) は折り畳んだ状態を、 さらに、 図 5は、 図 4に 示す補強材を遮蔽材の両面に施した例をそれぞれ示す。 発明を実施するための最良の形態
実施例 1
表 1は、 本発明の遮蔽材を放射線用遮蔽材に適用した例を示す。
同表において、 N o . 1〜8は本発明の実施例を示し、 N o . 9〜1 3は比 較例を示し、 それぞれを柔軟性、 遮蔽能力、 難燃性、 取扱性それに総合評価に よって評価したものである。
遮蔽能を付与するための分散粒子として、 0. 5〜： L 00 m程度の粒子径 を有するタングステン粉末、 モリブデン粉末、 酸化ハフニウムを使用し、 有機 物として、 ォレフィン系エラストマ一、 加硫ゴム、 スチレン系エラストマ一、 イソプレン系エラス卜マ一、 ポリエステル系エラストマ一を約 40体積％の割 合で混練して得た複合物を、 140〜180での温間プレス方法にて成形し、 3mmX 30 OmmX 100 Ommの板状材とした。 次に、 布材として表に示 すように、 塩化ビニルでコーティングしたガラスクロスシ一ト、 シリコンコー ティングしたガラスクロスシート、 シリコンコーティングしたカーボン繊維シ ート、 PTFE (ボリテトラフルォロエチレン) でコーティングした夕ングス テンワイヤシート、 PTFEでコーティングしたスチールワイヤシート、 シリ コンコ一ティングした炭化珪素粉末含有ナイロンシー卜を内部に厚さ 3 mmX 30 OmmX 1000 mmの空洞を有する袋に整形した。 この空洞に前記板状 体を挿入し、 袋の空いた口をポリエステル糸で縫合して遮蔽材を得た。 この遮 蔽材を遮蔽部材を固定したまま長期間使用するのではなく、 遮蔽場所を変えな がら、 その遮蔽を要する場所の形状に応じて変形成形し、 放射線遮蔽部材とし て原子力発電施設内点検作業に使用した。
本発明の実施例である No. 1〜8は柔軟性、 遮蔽能力、 難燃性、 環境への 影響、 取り扱い性の全てにおいて適しており、 放射線遮蔽部材として良好な性 質を示した。
本発明の遮蔽材は高密度のタングステン粉末を含むために放射線遮蔽性に優 れており、 同じ厚さの含鉛材料試料 No. 9と No. 10よりも X線遮蔽能力 に優れていた。
また、 試料 No. 1 1は、 鉄粉を塩化ビニル（以下 「塩ビ」 と略記する）コー ティングガラスクロスシートに詰めたものであるが、 内部で粉末が片寄り遮蔽 能力もムラがあり実用できなかった。
試料 No. 12の試料はタングステン一エラストマ一樹旨複合物であるが、 折り畳みや引き裂きに極めて弱いために取り扱いが難しく、 容易に破損した。 試料 No. 13の試料は布状の材料としてポリエチレンを用いたが、 短時間 の火炎との接触により容易に着火した。
【表 1】
試 板状部材の材質 布状物の材質 柔 遮 難 環境 取 ネ公 料 軟 蔽 燃 への σ
N 性 能 性 扱 評 o. 力 い 価
1 タンク"ステン粉末 塩ビコ -ティンダカ"ラスクロスシ-ト 〇 〇 〇 〇 〇 〇 一才レフイン系エラストマ一
2 タンク'ステン粉末 塩ビコ -ティング'力'ラスクロスシ-ト 〇 〇 〇 〇 〇 〇
-加硫コ"ム
3 モリフ'、テ'、ン粉末 塩ビコ -テインク"力'、ラスクロスシ-ト 〇 〇 〇 〇 〇 〇
-ォレフイン系 Jラストマ-
4 タンタル粉末 シリコンコ-ティング、力"ラスクロスシ- 〇 〇 〇 〇 〇 〇
-加硫コ'ム
5 酸化 Λフ;:ゥム粉末 シリコンコ-ティング力-ホ"ン繊維 〇 〇 〇 〇 〇 〇
-加硫コ"ム
6 タンク、、ステン粉末 PTFEコ-ティング'タングステンワイヤ 〇 〇 〇 . 〇 〇 〇
-スチレン系エラストマ - -シ-ト
7 タンク"ステン粉末 PTFEコーテインク '、スチールワイヤーシ 〇 〇 〇 〇 〇 〇
-イリフ。レン系ヱラストマ- -ト
8 タンク'ステン粉末 シリコン〕-テインク"炭化珪素粉 〇 〇 〇 〇 〇 〇
-ホ。リエステル系エラストマ- 末含有ナイ Dンシ-ト
9 鉛 なし X 〇 〇 X 〇 X
10 鉛毛 塩ビ力"ラスクロスシ-ト 〇 X 〇 X 〇 X
1 1 タンク'ステン粉末 塩ビ力"ラスクロスシ-ト 〇 X 〇 〇 〇 X
12 タン ステン粉末 なし 〇 〇 X 〇 X X 一才レフイン ^エラス卜マー
13 タンク"ステン粉末 ホ。リエチレンフィルム 〇 〇 X 〇 〇 X
-ォレフイン系エラストマ - 例 2
表 2は、 本発明を電磁波遮蔽材に適用した例を示す。
同表に示す実施例である N o . 2 1〜2 3は、 電磁波遮蔽用分散材として酸 化鉄粉と鉄粉を選択し、 有機物として加硫ゴム、 ォレフィン系エラストマ一を 選択し、 これらを約 4 0体積％の割合で混合した複合物を実施例 1と同様の条 件で処理して、 I mmX 1 0 0 O mmX 1 0 0 0 mmの板状材を用意した。 布材として塩ビでコーティングしたガラスクロスシートを選択し、 2枚用意 し、 その 2枚の間に複合物板状部材を挟んだ状態でガラスクロスシートの外周 部をウェルダーにより加熱、 圧着して板状複合物を挟んだ状態で一体とし、 遮 蔽材を得た。
この遮蔽材を複数作製し簡易的な電磁波暗室の外壁に貼り付けることによつ て電磁波遮蔽部材として使用した。
電磁波暗室の外壁は凹凸があるために、 柔軟な材料にて隙間なく覆う必要が あり、 また、 設備を移設させたり、 他の設備の遮蔽などに使うために、 取り扱 いに特別の注意が要らないよう引き裂きなどに対して強い材料である必要があ る。 また、 遮蔽能力が小さいと充分な遮蔽効果を得るために厚い部材を使用す る必要があり、 持ち運びや設備への設置、 保管などの際に不利となるために、 なるべく単位体積あたりの遮蔽能が高いものが望ましい。 本発明に係る試料 N o . 2 1〜2 3は係る用途に適切な電磁波遮蔽材であった。 さらには、 柔軟性 がありながら、 破れにくさ、 難燃性なども同時に有していた。
表 2に示す N o . 2 4〜2 7は比較例を示す。 上記本発明の実施例である N o . 2 1〜2 3は、 これらの比較例に対して、 柔軟性、 遮蔽能力、 難燃性、 環 境への影響、 取り扱い性の全ての点において、 電磁波遮蔽部材として優れたも のであった。
比較例の N o . 2 4は複合物板状部材でなく鉄粉を塩ビコ一ティングガラス クロスシートに詰めたものであるが、 内部で粉末が偏在し、 遮蔽能力もムラが あり使用できなかった。 N o . 2 5は酸化鉄一エラストマ一樹脂複合物である が、 取り扱いが難しく、 容易に破損した。 また、 N o . 2 6は布状の材料とし てポリエチレンを用いたが、 短時間の火炎との接触により容易に着火した。 ま た、 鉄板である N o . 2 7は設備に対して形状がなじまず、 限られた設備形状 にしか使用できなかった。
【表 2】
B式 板状部材の材質 布状物の材質 采 遮 難 取 &<& 料 軟 蔽 燃 り a
N 性 能 性 扱 評 o. 力 い 価
21 酸化鉄粉末 塩ビコ -ティンゲ力'ラスクロスシ-ト 〇 〇 〇 〇 〇 -加硫コ"ム
22 酸化鉄粉末 塩ビコ -ティング、力"ラスクロスシ-ト 〇 〇 〇 〇 〇
-才レフイン系 Iラストマ-
23 鉄粉-ォレフィン系 Iラストマ- シリコンコ テインク'力、、ラスクロスシ-ト 〇 〇 〇 〇 〇
24 酸化鉄粉 塩ビコ-ティング、力、、ラスクロスシ-ト 〇 X 〇 〇 X
25 酸化鉄-ォレフィン系 Iラストマ- なし 〇 〇 X X X
26 酸化鉄-加硫コ'ム ホ。リエチレン 〇 〇 X 〇 X
27 鉄板 なし X 〇 〇 X X
実施例 3
添付各図は、 本発明の遮蔽材への補強材の適用例を示す。
遮蔽機能を有する粒子と弹性を有する高分子化合物との混合物からなる遮蔽 材 1には、 補強材 2がー体的に取り付けられているが、 その形態は図 1に示す ように補強材 2がフィルム状、 メッシュ状の場合、 遮蔽材 1の表面に貼り付け る形態と、 図 2に示すように遮蔽材 1の内部に補強材 2を埋め込む形態がある。 また、 図 3に示すように、 表面に突起 2 1を有する補強材 2 0の場合には、 突起 2 1を下側にして遮蔽材 1の表面近傍に埋め込み一体化することができる。 さらに、 図 4 ( a ) に示す表面に突起 2 1を有する補強材 2 0は、 図 4 ( b ) に示すように、 突起 2 1が遮蔽材 1の湾曲を制限し、 遮蔽材 1を特定方 向に一定以上曲がらないようにする。 例えば、 この補強材 2 0を一方向に長い 遮蔽部材マツト中央部に取り付けることにより、 折り畳んでの搬送や保管する 際も、 折り曲げ部の曲率を一定以上に確保できるためにそこから破れや割れを 生じることがない。
本実施例では、 金属として放射線遮蔽能力の高いタングステン粉末と、 有機 物として熱可塑性エラストマ一であるォレフィン系エラス卜マー粉末を混合、 加熱、 加圧し、 タングステン粉末 6 0 (体積％)、 ォレフィン系エラストマ一 4 0 (体積％) の板状の複合物を得た。 また、 補強材として樹脂成分を主とする 粘着性ラミネートシートを選択し、 複合物の形状に合わせて切断した。 つぎに、 板状の複合物の両面にラミネ一卜シートを貼り、 一体として柔軟性を持つ板状 の遮蔽部材を得た。
得られたこの遮蔽部材を、 従来含鉛材料が使用されている手荷物検查用の X 線透過装置のカーテンとして使用した。
この遮蔽部材は高密度のタングステン粉末を含むために放射線遮蔽性に優れ ており、 同じ厚さの含鉛材料よりも X線遮蔽能力に優れていた。 また、 柔軟性 が高く、 折り曲げて変形させることが可能であつた。 荷物が食品などの場合で も鉛など有害な材料を使用していないために食物への鉛汚染の問題もなく使用 することができた。 さらに引き裂きに対する強度が従来の遮蔽部材ょり高く、 取り付けが極めて容易であり、 含鉛材料のカーテンと比較して同等以上の寿命 を得ることができた。 実施例 4
遮蔽材として実施例 3と同様にして板状材を選択した。 補強材 2 0として図 4に示すような表面に突起 2 1を有する樹脂製の板材を選択し、 板状材の大き さに 2枚切断した。 つぎに、 複合物と補強部材の両者を接着剤にて貼り合わせ、 図 5に示すように両面に溝状の凹凸を有する遮蔽材 1が得られた。 得られた遮 蔽材を、 放射線遮蔽部材として原子力発電所施設内点検作業時に用いた。 この 用途は遮蔽部材を固定したまま長時間使用するのではなく、 作業箇所に応じて 遮蔽場所を変えながら使用した。
この遮蔽材は、 充分な柔軟性を持っているためにさまざまな形状に対応して 遮蔽を行うことができた。 また、 搬送の際に折り畳むことがあつたが、 補強材 によって湾曲部が一定以上の曲率を確保することができ、 複合物は割れを生じ なかった。 また、 遮蔽性は同じ厚さの鉛毛マットに対して 2倍程度の能力があ つた。
比較例として、 同様の遮蔽材をそのまま放射線遮蔽部材として原子力発電所 施設内点検作業時に用いたところ、 搬送時に複合物に割れが生じ、 使用に耐え なかった。 実施例 5
金属として電磁波吸収能の高いフェライト粉末を選択し、 有機物として加硫 ゴム粉末を選択し、 実施例 1と同様の方法にてフェライト 6 0 (体積％)、 加硫 ゴム 4 0 (体積％) からなる板状の遮蔽材を得た。 この複合物を厚さ l mm、 5 0 0 mm四方の板状に成形した。 つぎに、 この遮蔽材 2枚で太さ 0 . 0 5 m mでピッチが 1 mmで格子状の銅製の網を 1枚はさみ、 加熱しながら両面から プレスを行い 3者を一体化させ、 遮蔽材を得た。 銅製の網は一体となった複合 物中央部に埋没し、 強固に接合されていた。
得られた電波遮蔽部材を簡易電磁波測定室の壁および天井に隙間なく設置し たところ、 外部からの周波数 2 MH z以上の電波は全く入らずに、 ノイズのな い正確な測定ができた。 また、 設置の際に折り曲げてそのまま使用したが、 破 れなどは全く入らずに、 また、 測定室の形に添う柔軟性を有していた。 産業上の利用可能性
本発明の遮蔽材は、 電磁波や核設備からの放射線を遮蔽する任意の箇所と部 材に簡便に適用できる。
また、 本発明の遮蔽材は、 毒性がないことから食品へ残留した金厲の探知装 置や、 空港の X線による荷物検查機カーテンのような用途に適用できる。

Claims

請 求 の 範 囲
I . 放射線または電磁波を遮蔽する能力を有する分散材と有機物の複合物から なる柔軟性を有する成形体が、 難燃性繊維からなる布状シートによって包み込 まれている遮蔽材。
2 . 分散材が重金属の粉末である放射線遮蔽用の請求の範囲第 1項に記載の遮 蔽材。
3 . 分散材が電磁波を吸収する金属鉄、 酸化鉄または誘電体である電磁波遮蔽 用の請求の範囲第 1項に記載の遮蔽材。
4. 難燃性繊維が、 ガラス繊維、 金属繊維、 カーボン繊維、 セラミックス繊維 の中の何れかである請求の範囲第 1項から第 3項のいずれかに記載の遮蔽材。
5 . 難燃性繊維からなる布状シートが非通気性のコ一ティング材によってコ一 卜されている請求の範囲第 1項から第 4項のいずれかに記載の遮蔽材。
6 . 放射線または電磁波を遮蔽する能力を有する分散材を分散した弾性を有す る高分子有機化合物からなる遮蔽材に、 曲げに対する補強能力を有する補強材 を取り付けた遮蔽材。
7 . 分散材が重金属または磁性体であり、 弾性を有する高分子有機化合物がェ ラストマー樹脂または加硫ゴムである請求の範囲第 6項に記載の遮蔽材。
8 . 補強材がポリエチレン、 ナイロン、 ポリエステル、 金属などのフィルム、 ナイロン繊維、 金属繊維などのワイヤーメッシュ、 あるいは、 表面に突起を有 する板状または棒状材のいずれか 1種または 2種以上である請求の範囲第 6項 または第 7項に記載の遮蔽材。
9 . 補強材の遮蔽材への取り付け箇所が遮蔽材の表面、 内部、 または、 表面近 傍である請求の範囲第 6項から第 8項のいずれかに記載の遮蔽材。
1 0 . 補強材の遮蔽材への取り付け状態が圧着状態で取り付けられている請求 の範囲第 6項から第 8項のいずれかに記載の遮蔽材。
I I . 補強材が二分された遮蔽材の間に圧着状態で取り付けられている請求の 範囲第 6項から第 8項のいずれかに記載の遮蔽材。
1 2 . 遮蔽材が、 ガラス繊維、 金属繊維、 ナイロン繊維などの高強度の繊維を 織り込んだ布状シートに包み込んだ構造を有するものである請求の範囲第 6項 から第 1 1項のいずれかに記載の遮蔽材。
PCT/JP2003/003288 2003-03-18 2003-03-18 遮蔽材 WO2004084234A1 (ja)