WO2004072126A1 - リビングラジカルポリマーの製造方法及びポリマー - Google Patents
リビングラジカルポリマーの製造方法及びポリマー Download PDFInfo
- Publication number
- WO2004072126A1 WO2004072126A1 PCT/JP2004/001707 JP2004001707W WO2004072126A1 WO 2004072126 A1 WO2004072126 A1 WO 2004072126A1 JP 2004001707 W JP2004001707 W JP 2004001707W WO 2004072126 A1 WO2004072126 A1 WO 2004072126A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- methyl
- group
- benzene
- living radical
- ethyl
- Prior art date
Description
Claims