US20120088103A1 - Carbon fiber bundle that develops high mechanical performance - Google Patents
Carbon fiber bundle that develops high mechanical performance Download PDFInfo
- Publication number
- US20120088103A1 US20120088103A1 US13/377,289 US201013377289A US2012088103A1 US 20120088103 A1 US20120088103 A1 US 20120088103A1 US 201013377289 A US201013377289 A US 201013377289A US 2012088103 A1 US2012088103 A1 US 2012088103A1
- Authority
- US
- United States
- Prior art keywords
- carbon fiber
- fiber
- fiber bundle
- epoxy resin
- precursor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
- VNWKTOKETHGBQD-UHFFFAOYSA-N methane Chemical compound C VNWKTOKETHGBQD-UHFFFAOYSA-N 0.000 title claims abstract description 145
- 229920000049 Carbon (fiber) Polymers 0.000 title claims abstract description 144
- 239000004917 carbon fiber Substances 0.000 title claims abstract description 144
- 239000000835 fiber Substances 0.000 claims abstract description 192
- 238000000034 method Methods 0.000 claims abstract description 44
- 229920000647 polyepoxide Polymers 0.000 claims description 35
- 239000003822 epoxy resin Substances 0.000 claims description 32
- 239000003795 chemical substances by application Substances 0.000 claims description 25
- 238000004513 sizing Methods 0.000 claims description 25
- IISBACLAFKSPIT-UHFFFAOYSA-N bisphenol A Chemical compound C=1C=C(O)C=CC=1C(C)(C)C1=CC=C(O)C=C1 IISBACLAFKSPIT-UHFFFAOYSA-N 0.000 claims description 19
- 150000001875 compounds Chemical class 0.000 claims description 18
- 239000000203 mixture Substances 0.000 claims description 18
- 230000002950 deficient Effects 0.000 claims description 14
- QVGXLLKOCUKJST-UHFFFAOYSA-N atomic oxygen Chemical compound [O] QVGXLLKOCUKJST-UHFFFAOYSA-N 0.000 claims description 13
- 229910052760 oxygen Inorganic materials 0.000 claims description 13
- 239000001301 oxygen Substances 0.000 claims description 13
- 229910052751 metal Inorganic materials 0.000 claims description 12
- 239000002184 metal Substances 0.000 claims description 12
- 230000007547 defect Effects 0.000 claims description 11
- JOYRKODLDBILNP-UHFFFAOYSA-N Ethyl urethane Chemical compound CCOC(N)=O JOYRKODLDBILNP-UHFFFAOYSA-N 0.000 claims description 9
- 125000003118 aryl group Chemical group 0.000 claims description 7
- 125000000524 functional group Chemical group 0.000 claims description 7
- 125000002887 hydroxy group Chemical group [H]O* 0.000 claims description 7
- 229930185605 Bisphenol Natural products 0.000 claims description 6
- 238000009864 tensile test Methods 0.000 claims description 6
- XEEYBQQBJWHFJM-UHFFFAOYSA-N Iron Chemical compound [Fe] XEEYBQQBJWHFJM-UHFFFAOYSA-N 0.000 claims description 4
- 238000002484 cyclic voltammetry Methods 0.000 claims description 4
- 125000005442 diisocyanate group Chemical group 0.000 claims description 4
- 238000004833 X-ray photoelectron spectroscopy Methods 0.000 claims description 3
- 239000007795 chemical reaction product Substances 0.000 claims description 3
- 238000004993 emission spectroscopy Methods 0.000 claims description 3
- HCHKCACWOHOZIP-UHFFFAOYSA-N Zinc Chemical compound [Zn] HCHKCACWOHOZIP-UHFFFAOYSA-N 0.000 claims description 2
- 125000001931 aliphatic group Chemical group 0.000 claims description 2
- 229910052784 alkaline earth metal Inorganic materials 0.000 claims description 2
- 150000001342 alkaline earth metals Chemical class 0.000 claims description 2
- 125000002947 alkylene group Chemical group 0.000 claims description 2
- 229910052782 aluminium Inorganic materials 0.000 claims description 2
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 claims description 2
- 229910052742 iron Inorganic materials 0.000 claims description 2
- 150000002739 metals Chemical class 0.000 claims description 2
- DVKJHBMWWAPEIU-UHFFFAOYSA-N toluene 2,4-diisocyanate Chemical compound CC1=CC=C(N=C=O)C=C1N=C=O DVKJHBMWWAPEIU-UHFFFAOYSA-N 0.000 claims description 2
- 239000008096 xylene Substances 0.000 claims description 2
- 229910052725 zinc Inorganic materials 0.000 claims description 2
- 239000011701 zinc Substances 0.000 claims description 2
- 229940106691 bisphenol a Drugs 0.000 claims 1
- 229920005989 resin Polymers 0.000 abstract description 28
- 239000011347 resin Substances 0.000 abstract description 28
- 239000002243 precursor Substances 0.000 description 72
- 238000011282 treatment Methods 0.000 description 29
- 238000003763 carbonization Methods 0.000 description 20
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 description 20
- 239000002131 composite material Substances 0.000 description 18
- 239000000243 solution Substances 0.000 description 16
- ZMXDDKWLCZADIW-UHFFFAOYSA-N N,N-Dimethylformamide Chemical compound CN(C)C=O ZMXDDKWLCZADIW-UHFFFAOYSA-N 0.000 description 15
- 239000002904 solvent Substances 0.000 description 13
- 238000007254 oxidation reaction Methods 0.000 description 12
- NLHHRLWOUZZQLW-UHFFFAOYSA-N Acrylonitrile Chemical compound C=CC#N NLHHRLWOUZZQLW-UHFFFAOYSA-N 0.000 description 11
- 238000000280 densification Methods 0.000 description 11
- 238000010438 heat treatment Methods 0.000 description 11
- 238000004519 manufacturing process Methods 0.000 description 11
- 239000000463 material Substances 0.000 description 11
- 230000006641 stabilisation Effects 0.000 description 11
- 238000011105 stabilization Methods 0.000 description 11
- 230000000052 comparative effect Effects 0.000 description 10
- 238000005259 measurement Methods 0.000 description 10
- 230000015572 biosynthetic process Effects 0.000 description 9
- 238000006243 chemical reaction Methods 0.000 description 9
- 238000011156 evaluation Methods 0.000 description 9
- 239000011159 matrix material Substances 0.000 description 9
- 239000003921 oil Substances 0.000 description 9
- IJGRMHOSHXDMSA-UHFFFAOYSA-N Atomic nitrogen Chemical compound N#N IJGRMHOSHXDMSA-UHFFFAOYSA-N 0.000 description 8
- 230000003647 oxidation Effects 0.000 description 8
- 238000005406 washing Methods 0.000 description 8
- 239000002344 surface layer Substances 0.000 description 7
- ZWEHNKRNPOVVGH-UHFFFAOYSA-N 2-Butanone Chemical compound CCC(C)=O ZWEHNKRNPOVVGH-UHFFFAOYSA-N 0.000 description 6
- OKTJSMMVPCPJKN-UHFFFAOYSA-N Carbon Chemical compound [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 description 6
- 230000000694 effects Effects 0.000 description 6
- 125000003700 epoxy group Chemical group 0.000 description 6
- 238000001891 gel spinning Methods 0.000 description 6
- 239000007788 liquid Substances 0.000 description 6
- BASFCYQUMIYNBI-UHFFFAOYSA-N platinum Chemical compound [Pt] BASFCYQUMIYNBI-UHFFFAOYSA-N 0.000 description 6
- 229920001296 polysiloxane Polymers 0.000 description 6
- 239000007864 aqueous solution Substances 0.000 description 5
- 230000008859 change Effects 0.000 description 5
- 239000013078 crystal Substances 0.000 description 5
- 230000007423 decrease Effects 0.000 description 5
- 238000002360 preparation method Methods 0.000 description 5
- 230000008569 process Effects 0.000 description 5
- 238000012360 testing method Methods 0.000 description 5
- NLZUEZXRPGMBCV-UHFFFAOYSA-N Butylhydroxytoluene Chemical compound CC1=CC(C(C)(C)C)=C(O)C(C(C)(C)C)=C1 NLZUEZXRPGMBCV-UHFFFAOYSA-N 0.000 description 4
- 239000004593 Epoxy Substances 0.000 description 4
- PEDCQBHIVMGVHV-UHFFFAOYSA-N Glycerine Chemical compound OCC(O)CO PEDCQBHIVMGVHV-UHFFFAOYSA-N 0.000 description 4
- 229920001577 copolymer Polymers 0.000 description 4
- 239000006185 dispersion Substances 0.000 description 4
- 238000001035 drying Methods 0.000 description 4
- 239000003792 electrolyte Substances 0.000 description 4
- 239000003995 emulsifying agent Substances 0.000 description 4
- 239000010410 layer Substances 0.000 description 4
- 229910052757 nitrogen Inorganic materials 0.000 description 4
- 239000003960 organic solvent Substances 0.000 description 4
- 229920002545 silicone oil Polymers 0.000 description 4
- 229920002803 thermoplastic polyurethane Polymers 0.000 description 4
- 150000003673 urethanes Chemical class 0.000 description 4
- ATRRKUHOCOJYRX-UHFFFAOYSA-N Ammonium bicarbonate Chemical compound [NH4+].OC([O-])=O ATRRKUHOCOJYRX-UHFFFAOYSA-N 0.000 description 3
- 229920002025 Pluronic® F 88 Polymers 0.000 description 3
- RVGRUAULSDPKGF-UHFFFAOYSA-N Poloxamer Chemical compound C1CO1.CC1CO1 RVGRUAULSDPKGF-UHFFFAOYSA-N 0.000 description 3
- KWYUFKZDYYNOTN-UHFFFAOYSA-M Potassium hydroxide Chemical compound [OH-].[K+] KWYUFKZDYYNOTN-UHFFFAOYSA-M 0.000 description 3
- HEMHJVSKTPXQMS-UHFFFAOYSA-M Sodium hydroxide Chemical compound [OH-].[Na+] HEMHJVSKTPXQMS-UHFFFAOYSA-M 0.000 description 3
- 239000001099 ammonium carbonate Substances 0.000 description 3
- 239000012298 atmosphere Substances 0.000 description 3
- 238000010000 carbonizing Methods 0.000 description 3
- 230000006835 compression Effects 0.000 description 3
- 238000007906 compression Methods 0.000 description 3
- 229910002804 graphite Inorganic materials 0.000 description 3
- 239000010439 graphite Substances 0.000 description 3
- 230000001771 impaired effect Effects 0.000 description 3
- -1 methyl glycidol Chemical compound 0.000 description 3
- 239000000178 monomer Substances 0.000 description 3
- 229910052697 platinum Inorganic materials 0.000 description 3
- 238000006116 polymerization reaction Methods 0.000 description 3
- 230000035484 reaction time Effects 0.000 description 3
- 239000000758 substrate Substances 0.000 description 3
- 238000004381 surface treatment Methods 0.000 description 3
- 230000037303 wrinkles Effects 0.000 description 3
- IVSZLXZYQVIEFR-UHFFFAOYSA-N 1,3-Dimethylbenzene Natural products CC1=CC=CC(C)=C1 IVSZLXZYQVIEFR-UHFFFAOYSA-N 0.000 description 2
- 229920002972 Acrylic fiber Polymers 0.000 description 2
- 229910000013 Ammonium bicarbonate Inorganic materials 0.000 description 2
- IAZDPXIOMUYVGZ-UHFFFAOYSA-N Dimethylsulphoxide Chemical compound CS(C)=O IAZDPXIOMUYVGZ-UHFFFAOYSA-N 0.000 description 2
- CERQOIWHTDAKMF-UHFFFAOYSA-N Methacrylic acid Chemical compound CC(=C)C(O)=O CERQOIWHTDAKMF-UHFFFAOYSA-N 0.000 description 2
- BAPJBEWLBFYGME-UHFFFAOYSA-N Methyl acrylate Chemical compound COC(=O)C=C BAPJBEWLBFYGME-UHFFFAOYSA-N 0.000 description 2
- NBIIXXVUZAFLBC-UHFFFAOYSA-N Phosphoric acid Chemical compound OP(O)(O)=O NBIIXXVUZAFLBC-UHFFFAOYSA-N 0.000 description 2
- GOOHAUXETOMSMM-UHFFFAOYSA-N Propylene oxide Chemical compound CC1CO1 GOOHAUXETOMSMM-UHFFFAOYSA-N 0.000 description 2
- 229910021607 Silver chloride Inorganic materials 0.000 description 2
- CDBYLPFSWZWCQE-UHFFFAOYSA-L Sodium Carbonate Chemical compound [Na+].[Na+].[O-]C([O-])=O CDBYLPFSWZWCQE-UHFFFAOYSA-L 0.000 description 2
- ZJCCRDAZUWHFQH-UHFFFAOYSA-N Trimethylolpropane Chemical compound CCC(CO)(CO)CO ZJCCRDAZUWHFQH-UHFFFAOYSA-N 0.000 description 2
- UKLDJPRMSDWDSL-UHFFFAOYSA-L [dibutyl(dodecanoyloxy)stannyl] dodecanoate Chemical compound CCCCCCCCCCCC(=O)O[Sn](CCCC)(CCCC)OC(=O)CCCCCCCCCCC UKLDJPRMSDWDSL-UHFFFAOYSA-L 0.000 description 2
- 230000001133 acceleration Effects 0.000 description 2
- 239000002253 acid Substances 0.000 description 2
- 235000012538 ammonium bicarbonate Nutrition 0.000 description 2
- 229910052799 carbon Inorganic materials 0.000 description 2
- 239000007809 chemical reaction catalyst Substances 0.000 description 2
- 238000000354 decomposition reaction Methods 0.000 description 2
- 239000012975 dibutyltin dilaurate Substances 0.000 description 2
- 235000011187 glycerol Nutrition 0.000 description 2
- 230000003993 interaction Effects 0.000 description 2
- 238000009830 intercalation Methods 0.000 description 2
- 230000002687 intercalation Effects 0.000 description 2
- 239000012778 molding material Substances 0.000 description 2
- 239000012299 nitrogen atmosphere Substances 0.000 description 2
- 230000003287 optical effect Effects 0.000 description 2
- 229920000642 polymer Polymers 0.000 description 2
- 239000011148 porous material Substances 0.000 description 2
- 125000002924 primary amino group Chemical group [H]N([H])* 0.000 description 2
- 238000012545 processing Methods 0.000 description 2
- 239000000047 product Substances 0.000 description 2
- 239000002683 reaction inhibitor Substances 0.000 description 2
- 230000002787 reinforcement Effects 0.000 description 2
- 238000010008 shearing Methods 0.000 description 2
- HKZLPVFGJNLROG-UHFFFAOYSA-M silver monochloride Chemical compound [Cl-].[Ag+] HKZLPVFGJNLROG-UHFFFAOYSA-M 0.000 description 2
- 238000009987 spinning Methods 0.000 description 2
- 239000007858 starting material Substances 0.000 description 2
- 238000003756 stirring Methods 0.000 description 2
- 239000000126 substance Substances 0.000 description 2
- 238000012546 transfer Methods 0.000 description 2
- HECLRDQVFMWTQS-RGOKHQFPSA-N 1755-01-7 Chemical compound C1[C@H]2[C@@H]3CC=C[C@@H]3[C@@H]1C=C2 HECLRDQVFMWTQS-RGOKHQFPSA-N 0.000 description 1
- PTBDIHRZYDMNKB-UHFFFAOYSA-N 2,2-Bis(hydroxymethyl)propionic acid Chemical compound OCC(C)(CO)C(O)=O PTBDIHRZYDMNKB-UHFFFAOYSA-N 0.000 description 1
- SMZOUWXMTYCWNB-UHFFFAOYSA-N 2-(2-methoxy-5-methylphenyl)ethanamine Chemical compound COC1=CC=C(C)C=C1CCN SMZOUWXMTYCWNB-UHFFFAOYSA-N 0.000 description 1
- JAHNSTQSQJOJLO-UHFFFAOYSA-N 2-(3-fluorophenyl)-1h-imidazole Chemical compound FC1=CC=CC(C=2NC=CN=2)=C1 JAHNSTQSQJOJLO-UHFFFAOYSA-N 0.000 description 1
- NIXOWILDQLNWCW-UHFFFAOYSA-N 2-Propenoic acid Natural products OC(=O)C=C NIXOWILDQLNWCW-UHFFFAOYSA-N 0.000 description 1
- FVCSARBUZVPSQF-UHFFFAOYSA-N 5-(2,4-dioxooxolan-3-yl)-7-methyl-3a,4,5,7a-tetrahydro-2-benzofuran-1,3-dione Chemical compound C1C(C(OC2=O)=O)C2C(C)=CC1C1C(=O)COC1=O FVCSARBUZVPSQF-UHFFFAOYSA-N 0.000 description 1
- HRPVXLWXLXDGHG-UHFFFAOYSA-N Acrylamide Chemical compound NC(=O)C=C HRPVXLWXLXDGHG-UHFFFAOYSA-N 0.000 description 1
- 229920005682 EO-PO block copolymer Polymers 0.000 description 1
- IAYPIBMASNFSPL-UHFFFAOYSA-N Ethylene oxide Chemical compound C1CO1 IAYPIBMASNFSPL-UHFFFAOYSA-N 0.000 description 1
- CTKINSOISVBQLD-UHFFFAOYSA-N Glycidol Chemical compound OCC1CO1 CTKINSOISVBQLD-UHFFFAOYSA-N 0.000 description 1
- VVQNEPGJFQJSBK-UHFFFAOYSA-N Methyl methacrylate Chemical compound COC(=O)C(C)=C VVQNEPGJFQJSBK-UHFFFAOYSA-N 0.000 description 1
- FXHOOIRPVKKKFG-UHFFFAOYSA-N N,N-Dimethylacetamide Chemical compound CN(C)C(C)=O FXHOOIRPVKKKFG-UHFFFAOYSA-N 0.000 description 1
- 239000002202 Polyethylene glycol Substances 0.000 description 1
- 229920000297 Rayon Polymers 0.000 description 1
- 229910052581 Si3N4 Inorganic materials 0.000 description 1
- 239000007983 Tris buffer Substances 0.000 description 1
- XTXRWKRVRITETP-UHFFFAOYSA-N Vinyl acetate Chemical compound CC(=O)OC=C XTXRWKRVRITETP-UHFFFAOYSA-N 0.000 description 1
- BZHJMEDXRYGGRV-UHFFFAOYSA-N Vinyl chloride Chemical compound ClC=C BZHJMEDXRYGGRV-UHFFFAOYSA-N 0.000 description 1
- 229940117913 acrylamide Drugs 0.000 description 1
- 150000003926 acrylamides Chemical class 0.000 description 1
- 150000001252 acrylic acid derivatives Chemical class 0.000 description 1
- 230000009471 action Effects 0.000 description 1
- 239000000853 adhesive Substances 0.000 description 1
- 230000001070 adhesive effect Effects 0.000 description 1
- 125000002723 alicyclic group Chemical group 0.000 description 1
- 239000012670 alkaline solution Substances 0.000 description 1
- 229910000147 aluminium phosphate Inorganic materials 0.000 description 1
- XKMRRTOUMJRJIA-UHFFFAOYSA-N ammonia nh3 Chemical compound N.N XKMRRTOUMJRJIA-UHFFFAOYSA-N 0.000 description 1
- 235000012501 ammonium carbonate Nutrition 0.000 description 1
- 150000001450 anions Chemical class 0.000 description 1
- 230000002238 attenuated effect Effects 0.000 description 1
- 230000009286 beneficial effect Effects 0.000 description 1
- AXCZMVOFGPJBDE-UHFFFAOYSA-L calcium dihydroxide Chemical compound [OH-].[OH-].[Ca+2] AXCZMVOFGPJBDE-UHFFFAOYSA-L 0.000 description 1
- 239000000920 calcium hydroxide Substances 0.000 description 1
- 229910001861 calcium hydroxide Inorganic materials 0.000 description 1
- 235000011116 calcium hydroxide Nutrition 0.000 description 1
- HFNQLYDPNAZRCH-UHFFFAOYSA-N carbonic acid Chemical compound OC(O)=O.OC(O)=O HFNQLYDPNAZRCH-UHFFFAOYSA-N 0.000 description 1
- 125000003178 carboxy group Chemical group [H]OC(*)=O 0.000 description 1
- 230000015271 coagulation Effects 0.000 description 1
- 238000005345 coagulation Methods 0.000 description 1
- 239000000470 constituent Substances 0.000 description 1
- 238000010276 construction Methods 0.000 description 1
- 238000007334 copolymerization reaction Methods 0.000 description 1
- 239000008367 deionised water Substances 0.000 description 1
- 229910021641 deionized water Inorganic materials 0.000 description 1
- 229940113088 dimethylacetamide Drugs 0.000 description 1
- 239000002270 dispersing agent Substances 0.000 description 1
- 238000009826 distribution Methods 0.000 description 1
- 230000005611 electricity Effects 0.000 description 1
- 238000004945 emulsification Methods 0.000 description 1
- 239000000839 emulsion Substances 0.000 description 1
- 238000007720 emulsion polymerization reaction Methods 0.000 description 1
- HJUFTIJOISQSKQ-UHFFFAOYSA-N fenoxycarb Chemical compound C1=CC(OCCNC(=O)OCC)=CC=C1OC1=CC=CC=C1 HJUFTIJOISQSKQ-UHFFFAOYSA-N 0.000 description 1
- 125000003055 glycidyl group Chemical group C(C1CO1)* 0.000 description 1
- LNEPOXFFQSENCJ-UHFFFAOYSA-N haloperidol Chemical compound C1CC(O)(C=2C=CC(Cl)=CC=2)CCN1CCCC(=O)C1=CC=C(F)C=C1 LNEPOXFFQSENCJ-UHFFFAOYSA-N 0.000 description 1
- 229920006015 heat resistant resin Polymers 0.000 description 1
- 239000008240 homogeneous mixture Substances 0.000 description 1
- 238000009863 impact test Methods 0.000 description 1
- 230000006872 improvement Effects 0.000 description 1
- 239000012535 impurity Substances 0.000 description 1
- 230000002779 inactivation Effects 0.000 description 1
- 230000000977 initiatory effect Effects 0.000 description 1
- 239000011229 interlayer Substances 0.000 description 1
- IQPQWNKOIGAROB-UHFFFAOYSA-N isocyanate group Chemical group [N-]=C=O IQPQWNKOIGAROB-UHFFFAOYSA-N 0.000 description 1
- 238000003475 lamination Methods 0.000 description 1
- QSHDDOUJBYECFT-UHFFFAOYSA-N mercury Chemical compound [Hg] QSHDDOUJBYECFT-UHFFFAOYSA-N 0.000 description 1
- 229910052753 mercury Inorganic materials 0.000 description 1
- FQPSGWSUVKBHSU-UHFFFAOYSA-N methacrylamide Chemical compound CC(=C)C(N)=O FQPSGWSUVKBHSU-UHFFFAOYSA-N 0.000 description 1
- LVHBHZANLOWSRM-UHFFFAOYSA-N methylenebutanedioic acid Natural products OC(=O)CC(=C)C(O)=O LVHBHZANLOWSRM-UHFFFAOYSA-N 0.000 description 1
- 230000005012 migration Effects 0.000 description 1
- 238000013508 migration Methods 0.000 description 1
- 238000000465 moulding Methods 0.000 description 1
- 229940088644 n,n-dimethylacrylamide Drugs 0.000 description 1
- YLGYACDQVQQZSW-UHFFFAOYSA-N n,n-dimethylprop-2-enamide Chemical compound CN(C)C(=O)C=C YLGYACDQVQQZSW-UHFFFAOYSA-N 0.000 description 1
- 229920003986 novolac Polymers 0.000 description 1
- 230000000704 physical effect Effects 0.000 description 1
- 229920001223 polyethylene glycol Polymers 0.000 description 1
- 229940068918 polyethylene glycol 400 Drugs 0.000 description 1
- 229920005862 polyol Polymers 0.000 description 1
- 150000003077 polyols Chemical class 0.000 description 1
- 235000011118 potassium hydroxide Nutrition 0.000 description 1
- 229910052705 radium Inorganic materials 0.000 description 1
- 238000007717 redox polymerization reaction Methods 0.000 description 1
- 230000003014 reinforcing effect Effects 0.000 description 1
- 230000002040 relaxant effect Effects 0.000 description 1
- 238000007363 ring formation reaction Methods 0.000 description 1
- 238000001878 scanning electron micrograph Methods 0.000 description 1
- HQVNEWCFYHHQES-UHFFFAOYSA-N silicon nitride Chemical compound N12[Si]34N5[Si]62N3[Si]51N64 HQVNEWCFYHHQES-UHFFFAOYSA-N 0.000 description 1
- 229910000029 sodium carbonate Inorganic materials 0.000 description 1
- 235000011121 sodium hydroxide Nutrition 0.000 description 1
- 239000007787 solid Substances 0.000 description 1
- 238000004544 sputter deposition Methods 0.000 description 1
- 230000003746 surface roughness Effects 0.000 description 1
- 238000010557 suspension polymerization reaction Methods 0.000 description 1
- 238000010408 sweeping Methods 0.000 description 1
- 230000009466 transformation Effects 0.000 description 1
- 238000002166 wet spinning Methods 0.000 description 1
Classifications
-
- D—TEXTILES; PAPER
- D02—YARNS; MECHANICAL FINISHING OF YARNS OR ROPES; WARPING OR BEAMING
- D02J—FINISHING OR DRESSING OF FILAMENTS, YARNS, THREADS, CORDS, ROPES OR THE LIKE
- D02J3/00—Modifying the surface
- D02J3/02—Modifying the surface by abrading, scraping, scuffing, cutting, or nicking
-
- D—TEXTILES; PAPER
- D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
- D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
- D01F6/00—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof
- D01F6/02—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof from homopolymers obtained by reactions only involving carbon-to-carbon unsaturated bonds
- D01F6/18—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof from homopolymers obtained by reactions only involving carbon-to-carbon unsaturated bonds from polymers of unsaturated nitriles, e.g. polyacrylonitrile, polyvinylidene cyanide
-
- D—TEXTILES; PAPER
- D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
- D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
- D01F11/00—Chemical after-treatment of artificial filaments or the like during manufacture
- D01F11/10—Chemical after-treatment of artificial filaments or the like during manufacture of carbon
- D01F11/12—Chemical after-treatment of artificial filaments or the like during manufacture of carbon with inorganic substances ; Intercalation
-
- D—TEXTILES; PAPER
- D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
- D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
- D01F11/00—Chemical after-treatment of artificial filaments or the like during manufacture
- D01F11/10—Chemical after-treatment of artificial filaments or the like during manufacture of carbon
- D01F11/14—Chemical after-treatment of artificial filaments or the like during manufacture of carbon with organic compounds, e.g. macromolecular compounds
-
- D—TEXTILES; PAPER
- D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
- D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
- D01F11/00—Chemical after-treatment of artificial filaments or the like during manufacture
- D01F11/10—Chemical after-treatment of artificial filaments or the like during manufacture of carbon
- D01F11/16—Chemical after-treatment of artificial filaments or the like during manufacture of carbon by physicochemical methods
-
- D—TEXTILES; PAPER
- D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
- D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
- D01F9/00—Artificial filaments or the like of other substances; Manufacture thereof; Apparatus specially adapted for the manufacture of carbon filaments
- D01F9/08—Artificial filaments or the like of other substances; Manufacture thereof; Apparatus specially adapted for the manufacture of carbon filaments of inorganic material
- D01F9/12—Carbon filaments; Apparatus specially adapted for the manufacture thereof
-
- D—TEXTILES; PAPER
- D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
- D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
- D01F9/00—Artificial filaments or the like of other substances; Manufacture thereof; Apparatus specially adapted for the manufacture of carbon filaments
- D01F9/08—Artificial filaments or the like of other substances; Manufacture thereof; Apparatus specially adapted for the manufacture of carbon filaments of inorganic material
- D01F9/12—Carbon filaments; Apparatus specially adapted for the manufacture thereof
- D01F9/14—Carbon filaments; Apparatus specially adapted for the manufacture thereof by decomposition of organic filaments
- D01F9/20—Carbon filaments; Apparatus specially adapted for the manufacture thereof by decomposition of organic filaments from polyaddition, polycondensation or polymerisation products
- D01F9/21—Carbon filaments; Apparatus specially adapted for the manufacture thereof by decomposition of organic filaments from polyaddition, polycondensation or polymerisation products from macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds
- D01F9/22—Carbon filaments; Apparatus specially adapted for the manufacture thereof by decomposition of organic filaments from polyaddition, polycondensation or polymerisation products from macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds from polyacrylonitriles
-
- D—TEXTILES; PAPER
- D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
- D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
- D01F9/00—Artificial filaments or the like of other substances; Manufacture thereof; Apparatus specially adapted for the manufacture of carbon filaments
- D01F9/08—Artificial filaments or the like of other substances; Manufacture thereof; Apparatus specially adapted for the manufacture of carbon filaments of inorganic material
- D01F9/12—Carbon filaments; Apparatus specially adapted for the manufacture thereof
- D01F9/14—Carbon filaments; Apparatus specially adapted for the manufacture thereof by decomposition of organic filaments
- D01F9/32—Apparatus therefor
-
- D—TEXTILES; PAPER
- D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
- D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
- D06M10/00—Physical treatment of fibres, threads, yarns, fabrics, or fibrous goods made from such materials, e.g. ultrasonic, corona discharge, irradiation, electric currents, or magnetic fields; Physical treatment combined with treatment with chemical compounds or elements
- D06M10/04—Physical treatment combined with treatment with chemical compounds or elements
- D06M10/06—Inorganic compounds or elements
-
- D—TEXTILES; PAPER
- D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
- D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
- D06M10/00—Physical treatment of fibres, threads, yarns, fabrics, or fibrous goods made from such materials, e.g. ultrasonic, corona discharge, irradiation, electric currents, or magnetic fields; Physical treatment combined with treatment with chemical compounds or elements
- D06M10/04—Physical treatment combined with treatment with chemical compounds or elements
- D06M10/08—Organic compounds
- D06M10/10—Macromolecular compounds
-
- D—TEXTILES; PAPER
- D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
- D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
- D06M11/00—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with inorganic substances or complexes thereof; Such treatment combined with mechanical treatment, e.g. mercerising
- D06M11/73—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with inorganic substances or complexes thereof; Such treatment combined with mechanical treatment, e.g. mercerising with carbon or compounds thereof
- D06M11/76—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with inorganic substances or complexes thereof; Such treatment combined with mechanical treatment, e.g. mercerising with carbon or compounds thereof with carbon oxides or carbonates
-
- D—TEXTILES; PAPER
- D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
- D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
- D06M15/00—Treating fibres, threads, yarns, fabrics, or fibrous goods made from such materials, with macromolecular compounds; Such treatment combined with mechanical treatment
- D06M15/19—Treating fibres, threads, yarns, fabrics, or fibrous goods made from such materials, with macromolecular compounds; Such treatment combined with mechanical treatment with synthetic macromolecular compounds
- D06M15/37—Macromolecular compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds
- D06M15/53—Polyethers
-
- D—TEXTILES; PAPER
- D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
- D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
- D06M15/00—Treating fibres, threads, yarns, fabrics, or fibrous goods made from such materials, with macromolecular compounds; Such treatment combined with mechanical treatment
- D06M15/19—Treating fibres, threads, yarns, fabrics, or fibrous goods made from such materials, with macromolecular compounds; Such treatment combined with mechanical treatment with synthetic macromolecular compounds
- D06M15/37—Macromolecular compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds
- D06M15/55—Epoxy resins
-
- D—TEXTILES; PAPER
- D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
- D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
- D06M15/00—Treating fibres, threads, yarns, fabrics, or fibrous goods made from such materials, with macromolecular compounds; Such treatment combined with mechanical treatment
- D06M15/19—Treating fibres, threads, yarns, fabrics, or fibrous goods made from such materials, with macromolecular compounds; Such treatment combined with mechanical treatment with synthetic macromolecular compounds
- D06M15/37—Macromolecular compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds
- D06M15/564—Polyureas, polyurethanes or other polymers having ureide or urethane links; Precondensation products forming them
- D06M15/568—Reaction products of isocyanates with polyethers
-
- D—TEXTILES; PAPER
- D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
- D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
- D06M2101/00—Chemical constitution of the fibres, threads, yarns, fabrics or fibrous goods made from such materials, to be treated
- D06M2101/40—Fibres of carbon
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/29—Coated or structually defined flake, particle, cell, strand, strand portion, rod, filament, macroscopic fiber or mass thereof
- Y10T428/2913—Rod, strand, filament or fiber
- Y10T428/2918—Rod, strand, filament or fiber including free carbon or carbide or therewith [not as steel]
Definitions
- the present invention relates to a carbon fiber bundle that has excellent mechanical characteristics and that is particularly used for obtaining a fiber-reinforced resin using a high-tenacity heat resistant resin as a matrix for use in the construction of airplanes.
- a resin in order to improve the mechanical characteristics of resin-base molded products, a resin has been commonly used in combination with a fiber serving as a reinforcement material.
- a composite molding material formed of a carbon fiber that is excellent in specific strength and specific elasticity in combination with a high-performance resin develops extremely high mechanical characteristics. Because of this, such a molding material has been willingly used as a constructional material for airplanes, high speed moving bodies, etc.
- a material that is stronger and that has higher rigidity as well as having excellent specific strength and specific rigidity. Given these circumstances, the desire is for further improvement of the performance of carbon fiber, such as improved strength and elastic modulus.
- Patent Literature 1 proposes a method of drawing a coagulated fiber that still contains a solvent in a solvent-containing drawing bath, thereby improving uniformity in structure and orientation, in order to obtain an acrylic fiber bundle used as a precursor of a carbon-fiber by a dry-wet spinning method.
- Drawing a coagulated fiber in a bath containing a solvent is a method commonly known as a solvent drawing technique that enables a stable drawing process by using solvent plasticization. Accordingly, this method is considered as an extremely excellent technique for obtaining a fiber that has high uniformity in structure and orientation.
- the solvent within a filament is rapidly squeezed out from the filament simultaneously upon drawing. The resultant structure of the filament tends to be less dense and thus a desired filament that has a dense structure cannot be obtained.
- Patent Literature 2 which pays attention to fine pores distributed in a coagulated fiber, proposes a technique for obtaining a precursor fiber in which excellent strength is developed by dry-densification of a coagulated fiber that has a high-dense structure.
- the fine pore distribution which is obtained by a mercury press-in method, reflects the bulk state from the surface layer to the interior of the filament. This is an extremely excellent method for evaluating the overall density of a fiber structure. From the precursor fiber bundle that has at least a certain level density as a whole, a very strong carbon fiber can be obtained in which defect point formation is suppressed.
- observation of fractures in the carbon fiber shows that fractures have originated from near the surface layer at an extremely high ratio. This means that a defective point is present near the surface layer. In other words, this technique is insufficient for manufacturing a precursor fiber bundle that is excellent in density near the surface layer.
- Patent Literature 3 proposes a method for manufacturing an acrylonitrile-based precursor fiber bundle that is not only high in whole density but that is also extremely high in surface density.
- Patent Literature 4 proposes, taking into consideration that an oil solution enters the surface-layer portion of a fiber and inhibits densification, a technique for suppressing permeation of an oil solution by focusing on microscopic voids of the surface-layer portion.
- a technique for suppressing the entry of an oil solution and a technique for suppressing defective point formation are both difficult to put into practical use since very complicated steps are required. Therefore, in the techniques discussed above, the effect of stably suppressing the entry of an oil solution into the surface layer portion is insufficient and the effect of reinforcing a carbon fiber is still far from a sufficient level.
- An object of the present invention is to provide a carbon fiber bundle for obtaining a fiber-reinforced resin that has high mechanical characteristics.
- the present invention is directed to a carbon fiber bundle formed of single carbon fibers, each of which has no surface uneven structure of 0.6 ⁇ m or more in length extending in the longitudinal direction of the single fiber; which has an uneven structure having a difference in height (Rp ⁇ v) of 5 to 25 nm between the highest portion and the lowest portion of the surface of the single fiber and an average roughness Ra of 2 to 6 nm, and which has a ratio of the major axis to the minor axis (major axis/minor axis) of a cross-section of the single fiber of 1.00 to 1.01, in which a mass of the single fiber per unit length falls within the range of 0.030 to 0.042 mg/m, a strand strength is 5900 MPa or more, a strand elastic modulus measured by the ASTM method is 250 to 380 GPa and a knot tenacity is 900 N/mm 2 or more.
- knot tenacity can be obtained by dividing the tensile breaking stress of a knotted carbon fiber bundle by the cross-sectional area of the fiber bundle (mass and density per unit length).
- the carbon fiber bundle of the present invention it is possible to provide a fiber-reinforced resin that has high mechanical characteristics.
- a carbon fiber bundle that has even better performance is obtained by acquiring “surface energy of surface formed by fracture” such that it reaches 30N/m or more.
- a carbon-fiber composite material that has extremely high mechanical performance can be obtained by forming a carbon fiber bundle which has an ipa value of 0.05 to 0.25 ⁇ A/cm 2 that is obtained by an electrochemical measuring method (cyclic voltammetry), and in which the amount of an oxygen-containing functional group (O1S/C1S) in a carbon fiber surface, that is obtained by X-ray photoelectron spectroscopy, is within the range of 0.05 to 0.10.
- the uneven surface structure present on the surface of a carbon fiber and extending in the longitudinal direction thereof and a sizing agent attached onto the surface play very important roles in developing mechanical characteristics of a fiber-reinforced resin material that uses the carbon fiber as a reinforcement material. This is because the uneven surface structure and the sizing agent attached onto the surface are directly involved in formation of the interfacial phase between a carbon fiber and a resin as well as characteristics thereof.
- the mechanical performance of the fiber-reinforced resin material is influenced by the performance of each of the three constituent factors, i.e., the fiber, the matrix resin and the interfacial phase. Even if only one of the three factors is unsatisfactory, the fiber-reinforced resin material cannot develop excellent mechanical performance.
- a carbon fiber obtained by a general manufacturing method for a carbon fiber bundle generally has an uneven surface structure that is formed almost parallel to the fiber-axis direction.
- the uneven structure has an undulation structure that is almost parallel to the fiber axis and that extends in the fiber axis.
- the depth of the uneven structure is usually about 50 nm to several hundreds of nm and the length thereof is usually about 0.6 ⁇ m to several ⁇ m and sometimes, several tens of ⁇ m.
- Such an uneven surface structure is usually called as surface wrinkle.
- the carbon fiber bundle of the present invention does not have an uneven surface structure that has a length of 0.6 ⁇ m or more and that extends in the longitudinal direction of a single fiber.
- the carbon fiber bundle of the present invention has an uneven structure that is smaller than the uneven structure mentioned above on the surface of a single fiber.
- the depth of the uneven surface structure present on a single carbon fiber is defined by the difference in height (Rp ⁇ v) between the highest portion and the lowest portion on the surface of a fiber and the average roughness Ra, in an area range surrounded by a length of 1.0 ⁇ m in the fiber-circumference direction and a length 1.0 ⁇ m in the fiber-axis direction.
- the (Rp ⁇ v) and Ra can be obtained by scanning the surface of a single fiber by use of a scanning atomic force microscope (AFM).
- AFM scanning atomic force microscope
- the difference in height (Rp ⁇ v) be 5 to 25 nm and that the average roughness Ra be 2 to 6 nm. It is more preferable that the difference in height (Rp ⁇ v) be 5 to 18 nm and that Ra be 2 to 5 nm.
- each of the single fibers that constitutes a carbon fiber has no uneven surface structure that has a length of 0.6 ⁇ m or more and that extends in the longitudinal direction of the fiber, on the surface of a single fiber.
- stress tends to be concentrated on such a large uneven surface structure.
- the fracture toughness of carbon fiber tissue around such an uneven structure is low. Accordingly, in the uneven surface structure of this size, interfacial failure tends to originate from a point near the uneven structure even if the level of stress applied to a composite material is not very large. As a result, mechanical performance of the composite material significantly decreases.
- a more specific embodiment of the uneven surface structure of each of the single fibers constituting a carbon fiber bundle of the present invention is as follows.
- carbon-fiber surface has an uneven structure of 0.6 ⁇ m or more in length called a wrinkle structure, that has an assembly of several fibrils as a unit and that extends in the longitudinal direction of the fiber, and an uneven microscopic structure that is smaller than the uneven structure called a wrinkle structure and that is present in each fibril body itself.
- an uneven structure that has a length of 0.6 ⁇ m or more and that extends in the longitudinal direction of a fiber is not present but only an uneven microscopic structure that is smaller than the uneven structure and that is present in each fibril body itself is present. Furthermore, such an uneven microscopic structure has a length of 300 nm or less.
- the uneven structure is defined by (Rp ⁇ v) and Ra as mentioned above.
- the uneven structure is an undulation structure having a difference in height (Rp ⁇ v) of 5 to 25 nm and an average roughness Ra of 2 to 6 nm, which are present in an area range surrounded by a length (1.0 ⁇ m) in the fiber-circumference direction of a single-fiber surface and a length (1.0 ⁇ m) in the fiber-axis direction.
- (Rp ⁇ v) is 5 to 18 nm and Ra is 2 to 5 nm.
- the direction of the uneven microscopic structure is not particularly limited and may be parallel or perpendicular to the fiber-axis direction or may be present at an angle with the fiber-axis direction.
- the ratio of the major axis and the minor axis (major axis/minor axis) of a single fiber cross-section is 1.00 to 1.01. This means that the single fiber must have a complete circular or nearly complete circular cross-section. This is because if the cross-section is a complete circle, the portion near the fiber surface has excellent structural uniformity, with the result that concentration of stress can be reduced.
- the ratio is preferably 1.00 to 1.005.
- the mass of the single fiber per unit length is 0.030 to 0.042 mg/m. If the mass of the single fiber per unit length (single fiber weight per unit area) is low, the fiber diameter is small, and structural irregularity along the cross-section is small. This means that mechanical performance in the direction perpendicular to the fiber axis is high. Accordingly, in a composite material, tolerance to stress applied in the direction perpendicular to the fiber axis is improved and the mechanical performance of a composite material can be enhanced.
- the strand strength of a carbon fiber bundle must be 5900 MPa or more.
- the strand strength of a carbon fiber bundle is preferably 6000 MPa or more and more preferably 6100 MPa or more. The higher the strand strength, the better; however, taken into consideration the balance between the strand strength and the compressive strength of a composite material, 10000 MPa is sufficient.
- the strand elastic modulus of a carbon fiber bundle must be 250 to 380 GPa, which are values measured by the ASTM method.
- the elastic modulus is less than 250 GPa, the elastic modulus of a carbon fiber bundle will be insufficient and sufficient mechanical characteristics cannot develop.
- the elastic modulus exceeds 380 GPa, the graphite crystal size of the surface and interior of a carbon fiber will increase.
- the strength along the cross-section of the fiber and the compressive strength in the fiber-axis direction decrease and performance balance between tension and compression of a composite material cannot be maintained.
- excellent composite material cannot be obtained.
- inactivation of the surface proceeds as the graphite crystal size increases, and the adhesiveness with a matrix resin decreases.
- mechanical performance such as tensile strength of the composite material in the direction of 90°, interlayer shearing strength, in-plane shearing strength and 0° compressive strength significantly decreases.
- the knot tenacity which is obtained by dividing the tensile stress at break of a knotted carbon fiber bundle by the cross-sectional area of the fiber bundle (mass and density per unit length), is 900 N/mm 2 or more. More preferably, the knot tenacity is 1000 N/mm 2 or more and further preferably, 1100 N/mm 2 or more.
- the knot tenacity serves as an index that reflects the mechanical performance of a fiber bundle except in the fiber-axis direction. In particular, the performance in the direction perpendicular to the fiber axis can be simply checked by the knot tenacity. In the composite material, since a material is often formed by pseudo-isotropic lamination, a complicated stress field is formed.
- a “surface energy of surface formed by fracture” is preferably 30 N/m or more.
- the surface energy of surface formed by fracture is obtained by forming a hemispherical defect having a predetermined size by a laser on the surface of a single fiber, and by breaking the fiber at the hemispherical defective site in a tensile test and by calculating from the breaking strength of the fiber and the size of the hemispherical defect in accordance with the following Griffith Equation (1).
- ⁇ is the breaking strength
- E is the ultrasonic elastic modulus of a carbon fiber bundle
- C is the size of a hemispherical defect.
- the “surface energy of surface formed by fracture” is more preferably, 31 N/m or more and further preferably 32 N/m or more.
- the surface energy of surface formed by fracture herein is used as a break-proof index of a carbon fiber for representing substrate strength.
- the carbon fiber is a material showing brittle fracture and the tensile strength is controlled by the defective point. If carbon fibers have the same defective points, the breaking strength increases as the substrate strength increases.
- a matrix resin for a high-performance composite material often has high adhesiveness with a carbon fiber, with the result that the critical fiber length, which serves as an index for stress transfer, diminishes. As a result, the strength in a further shorter length is reflected in the strength of the composite material.
- the substrate strength is conceivably an important index.
- the surface energy produced by breaking exceeds 50 N/m, it is necessary to reduce the degree of orientation in the fiber-axis direction. Accordingly, the surface energy produced by breaking should be 50 N/m or less.
- the ipa value obtained by an electrochemical measuring method is preferably 0.05 to 0.25 ⁇ A/cm 2 .
- the ipa value is influenced by the number of oxygen-containing functional groups of a carbon fiber, surface roughness involved in formation of an electric double layer and the microscopic graphite structure of a carbon fiber surface.
- a carbon fiber whose surface is largely etched and a carbon fiber that has an intercalation compound which is formed by inserting an anion between layers of a graphite crystal have a large ipa value.
- the interface between a carbon fiber and a resin is important.
- a carbon fiber that has a surface in which an appropriate oxygen-containing functional group is present and in which a small electric double layer is formed is found to form the most appropriate interface. If an ipa value is 0.05 ⁇ A/cm 2 or more, it indicates that the surface has a sufficient number of oxygen-containing functional groups, and it exhibits sufficient adhesiveness to an interface. In contrast, if an ipa value is 0.25 ⁇ A/cm 2 or less, the surface is not excessively etched and an intercalation compound is not formed. Such a surface can tightly adhere to a matrix resin, with the result that the surface can sufficiently adhere to the interface with a resin.
- the ipa value is more preferably 0.07 to 0.20 ⁇ A/cm 2 and further preferably 0.10 to 0.18 ⁇ A/cm 2 .
- the amount of an oxygen containing functional group in a carbon fiber surface (obtained by X-ray photoelectron spectroscopy) be within the range of 0.05 to 0.15. This is because it is important to have an appropriate adhesiveness with a matrix resin at the interface.
- a Si amount measured by ICP emission spectrometry is desirably 200 ppm or less.
- an oil solution containing silicone oil is attached onto a precursor fiber bundle.
- Silicone oil has extremely excellent heat resistance properties and can impart excellent mold release characteristics.
- silicone oil is considered most suitable as an oil solution for a carbon-fiber precursor bundle, which is a multifilament bundle formed by assembling a large number of filaments each having an extremely small diameter and each being further subjected to a high-temperature treatment performed at a temperature of 200° C. or more for several tens of minutes to several hours.
- carbonization treatment performed after stabilization treatment the silicone oil is mostly decomposed and scattered.
- the amount of silicone compound remaining on the surface of a carbon fiber becomes extremely low. Furthermore, the remaining silicone compound, which is present near the surface of a carbon fiber, has been found to contribute to the formation of voids. Therefore, if the amount of such a silicone compound is reduced as much as possible, carbon fiber having few voids can be manufactured. As a result, the strength of a carbon fiber bundle can be increased.
- the more preferable Si amount is 150 ppm or less and a further preferable Si amount is 100 ppm or less.
- the starting material for obtaining a carbon fiber bundle of the present invention is not particularly limited; however, the starting material that can be obtained from an acrylonitrile-based precursor fiber (hereinafter, appropriately referred to as “precursor fiber”) is preferred from the viewpoint of developing mechanical performance.
- precursor fiber an acrylonitrile-based precursor fiber
- the acrylonitrile-based copolymer constituting the precursor fiber is obtained from acrylonitrile (96 mass % or more) and several types of copolymerizable monomers. More preferably, the composition ratio of acrylonitrile is 97 mass % or more.
- copolymer components except acrylonitrile that are properly used include acrylic acid derivatives such as acrylic acid, methacrylic acid, itaconic acid, methyl acrylate and methyl methacrylate; and acryl amide derivatives such as acryl amide, methacryl amide, N-methyolacrylamide and N,N-dimethyl acrylamide and vinyl acetate. These may be used alone or in combination.
- a preferable copolymer is an acrylonitrile-based copolymer obtained by copolymerization of a monomer that has one or more carboxyl groups as an essential component.
- any polymerization method may be used, including, for example, redox polymerization performed in an aqueous solution, suspension polymerization performed in non-homogeneous system and emulsion polymerization using a dispersant. Difference between the polymerization methods does not limit the present invention.
- the precursor fiber is preferably manufactured by dissolving the aforementioned acrylonitrile based polymer in an organic solvent such as dimethyl acetamide, dimethyl sulfoxide or dimethyl formamide to prepare dope. Since these organic solvents do not contain a metal component, the content of a metal component in the resultant carbon fiber bundle can be reduced.
- the solid substance concentration of the dope is preferably 20 mass % or more and more preferably 21 mass % or more.
- the spinning method may be either wet spinning or dry-wet spinning. More preferably, dry-wet spinning is employed.
- dry-wet spinning the dope that is prepared is at first spun from a spinneret having numerous ejection holes arranged therein into the air and is then introduced into a congealed liquid filled with a solution mixture of an organic solvent and water whose temperature is controlled so that the dope will coagulate. The coagulated fiber is taken out, washed and drawn.
- any method may be used as long as the solvent can be removed.
- the temperature of the drawing tank preferably falls within the range of 40 to 80° C. If the temperature is less than 40° C., a stable drawing cannot be secured and it causes the drawing to be poor, with the result that a uniform fibril structure cannot be formed. In contrast, if the temperature exceeds 80° C., excessively strong plasticizing action occurs by heat, and a solvent is rapidly removed from a fiber surface and the result is nonuniform drawing.
- a more preferable temperature is 50 to 75° C.
- the concentration of the drawing tank is preferably 30 to 60 mass %. This is because if the concentration is less than 30 mass %, a stable drawing cannot be secured; whereas, if the concentration is beyond 60 mass %, an excessively large plasticization effect is obtained and interference with a stable drawing occurs.
- a more preferable concentration is 33 to 55 mass %.
- the draw ratio in the drawing tank is preferably 2 to 4 times. If the draw ratio is less than twice, drawing is insufficient and a desired fibril structure cannot be formed. In contrast, if the draw ratio is beyond 4 times, a fibril structure itself is broken. The result is a precursor fiber bundle that has extremely low density.
- the draw ratio is more preferably 2.2 to 3.8 times and further preferably, 2.5 to 3.5 times.
- the orientation degree of the fiber can be further enhanced. If a relaxing step is slightly performed, distortion caused by drawing in the previous step can be removed.
- drawing is performed in hot water at a ratio of 1.1 to 2.0 times.
- an oil solution composed of a silicone-based compound is attached so as to apply 0.8 to 1.6 mass % and the resultant fiber is subjected to dry densification.
- the dry densification is not particularly limited as long as dry densification is performed by a known drying method.
- a method of passing a fiber through a plurality of heated rolls is employed.
- the acrylic fiber bundle after the dry densification process has been performed is, if necessary, drawn in pressurized steam of 130 to 200° C., in a dry heat medium of 100 to 200° C., between heated rolls of 150 to 220° C. or on a heat board up to 1.8 to 6.0 times. After the orientation degree is further improved and densification is performed, the fiber bundle is rolled up to obtain a precursor fiber bundle.
- a carbon fiber bundle of the present invention can be manufactured from the above-mentioned precursor fiber bundle as follows.
- the precursor fiber bundle is fed to an oven for stabilization that is a type of furnace that circulates hot air at a temperature of 220 to 260° C. for 30 to 100 minutes to obtain a stabilized fiber having a density of 1.335 to 1.360 g/cm 3 .
- an operation for extending the fiber by 0 to 10% is performed.
- the stabilization reaction consists of a cyclization reaction with heat and an oxidation reaction with oxygen. It is important to balance the two reactions. In order to balance the two reactions, time for performing stabilization treatment is preferably 30 to 100 minutes.
- reaction time is less than 30 minutes, a single fiber has a portion in which the oxidation reaction does not sufficiently proceed, within the fiber, with the result that a large structural variety is generated along the cross-section of the single fiber.
- the obtained carbon fiber has a structure that is non-uniformly formed and fails to develop high mechanical performance.
- the reaction time exceeds 100 minutes, a larger amount of oxygen will be present near the surface of a single fiber. Thereafter, in the following heat treatment performed at a high temperature, a reaction that consumes an excessive amount of oxygen occurs to form a defective point. Because of this, high strength cannot be obtained.
- a more preferable stabilization treatment time is 40 to 80 minutes.
- the density of a stabilized fiber is less than 1.335 g/cm 3 .
- stabilization treatment is insufficient.
- a decomposition reaction occurs to form a defective point. Because of this, high strength cannot be obtained.
- the density of a stabilized fiber exceeds 1.360 g/cm 3 , the oxygen content of the fiber increases.
- a reaction that consumes an excessive amount of oxygen occurs to form a defective point. Because of this, high strength cannot be obtained.
- a more preferable density range of a stabilized fiber is 1.340 to 1.350 g/cm 3 .
- Appropriate extension of a fiber performed in an oven for stabilization is required in order to maintain and improve the orientation degree of a fibril structure that constitute a fiber. If the extension is less than 0%, the orientation degree of a fibril structure cannot be maintained; the orientation degree along the fiber axis is not sufficient for forming a carbon fiber structure; excellent mechanical performance cannot develop. In contrast, if the extension exceeds 10%, the fibril structure itself will be broken, with the result that formation of a carbon fiber structure will be impaired and the fracture point will change to a defective point. As a result, a carbon fiber that has high strength cannot be obtained. A more preferable extension rate is 3 to 8%.
- a stabilized fiber is passed through a first carbonization furnace of an inert atmosphere such as nitrogen that has a temperature gradient of 300 to 800° C., while extending it by 2 to 7%.
- a preferable processing temperature is 300 to 800° C. and the stabilized fiber is processed under linear temperature gradient conditions.
- the initiation temperature is preferably 300° C. or more. If the highest temperature exceeds 800° C., the fiber that is processed becomes very fragile and it is difficult to operate the following step.
- a more preferable temperature range is 300 to 750° C.
- the temperature gradient is not particularly limited; however a linear gradient is preferably employed.
- extension rate is less than 2%, orientation of a fibril structure cannot be maintained and the orientation degree along the fiber axis in formation of a carbon fiber structure will not be sufficient, with the result that excellent mechanical performance cannot develop.
- extension rate exceeds 7%, a fibril structure itself is broken, with the result that formation of a carbon fiber structure will be impaired and a fracture point will change to a defective point. As a result, a carbon fiber having high strength cannot be obtained.
- a more preferable extension rate is 3 to 5%.
- a preferable heat treatment time is 1.0 to 3.0 minutes. If the treatment time is less than 1.0 minute, the temperature will abruptly increase, and this will be accompanied by a severe decomposition reaction. As a result, a carbon fiber that has high strength cannot be obtained. If the treatment time exceeds 3.0 minutes, effect of plasticization in the former step will be produced, with the result that the orientation degree of a crystal will tend to decrease. As a result the mechanical performance of the resultant carbon fiber will be impaired.
- a more preferable heat treatment time is 1.2 to 2.5 minutes.
- the stabilized fiber is subjected to a second carbonization furnace that has an inert atmosphere such as nitrogen having a temperature gradient of 1000 to 1600° C. and is treated under heat under tension to obtain a carbon fiber. Furthermore, if necessary, the carbon fiber is optionally subjected to a third carbonization furnace having a desired temperature gradient and is treated with heat in an inert atmosphere under tension.
- a second carbonization furnace that has an inert atmosphere such as nitrogen having a temperature gradient of 1000 to 1600° C. and is treated under heat under tension to obtain a carbon fiber.
- the carbon fiber is optionally subjected to a third carbonization furnace having a desired temperature gradient and is treated with heat in an inert atmosphere under tension.
- the temperature for carbonization treatment is determined depending upon the desired elastic modulus of a carbon fiber.
- the highest temperature of carbonization treatment is preferably low.
- elastic modulus can be increased by increasing the treatment time.
- the highest temperature can be reduced.
- the gradient of temperature can be set to change gradually by increasing the treatment time. This is effective in suppressing defective point formation.
- the temperature of the second carbonization furnace varies depending upon the temperature of the first carbonization furnace; however, the temperature is acceptable as long as it is a temperature of 1000° C. or more and preferably 1050° C. or more.
- the temperature gradient is not particularly limited; however it is preferably set to change linearly.
- the heat treatment time is preferably 1.3 to 5.0 minutes and more preferably 2.0 to 4.2 minutes.
- the fiber significantly shrinks during processing. Thus, it is important to perform heat treatment under tension.
- An extension rate is preferably ⁇ 6.0 to 0.0%. If the extension rate is less than ⁇ 6.0%, the orientation of a crystal in the fiber-axis direction is not satisfactory and sufficient performance cannot be obtained. In contrast, if the extension rate exceeds 0.0%, the structure so far formed itself is broken and defective points are significantly formed, with the result that the strength is significantly reduced. More preferably, the extension rate ranges ⁇ 5.0% to ⁇ 1.0%.
- the carbon fiber bundle is subjected to surface oxidization treatment.
- the surface treatment method include known methods, i.e., oxidation treatments such as electrolytic oxidation, chemical oxidation and air oxidation. Any one of these methods may be employed.
- the electrolytic oxidation treatment industrially widely used is preferred since surface oxidization treatment can be stably performed.
- performing the electrolytic oxidation treatment while varying electric quantity is the simplest method. In this case, even if the electric quantity is the same, the ipa value significantly varies depending upon the electrolyte and the concentration thereof that is used.
- electrolytic oxidation treatment can be performed preferably in an aqueous alkaline solution of pH>7 with a carbon fiber as an anode while supplying an electric quantity of 10 to 200 coulomb/g.
- electrolyte examples include ammonium carbonate, ammonium bicarbonate, calcium hydroxide, sodium hydroxide and potassium hydroxide.
- the carbon fiber bundle of the present invention is subjected to sizing treatment.
- the sizing agent is dissolved in an organic solvent or dispersed in water with the help of an emulsifier to prepare an emulsion solution.
- the above preparation is applied to a carbon fiber bundle in accordance with a roller dip method, a roller contact method, etc.
- the carbon fiber bundle is dried.
- sizing treatment can be performed.
- the amount of the sizing agent attached to the surface of a carbon fiber can be controlled by controlling the concentration of the sizing agent solution and the squeeze amount thereof.
- drying can be performed by use of hot air, a hot plate, a heating roller and various infrared heaters.
- the most preferable sizing agent composition to be applied to the surface of the carbon fiber of the present invention is a urethane modified epoxy resin, which is a reaction product of (a) an epoxy resin that contains a hydroxy group (hereinafter appropriately referred to as a component (a)), (b) a polyhydroxy compound (hereinafter appropriately referred to as a component (b)) and (c) a diisocyanate that contains an aromatic ring (hereinafter appropriately referred to as a component (c)). Furthermore, a mixture of a urethane modified epoxy resin, which is a reaction product that is obtained by introducing a larger amount of component (a) than is required for a reaction system, and component (a) that remains is mentioned.
- component (d) a urethane modified epoxy resin obtained by using an epoxy resin having no hydroxy group
- component (d) a mixture of a urethane modified epoxy resin obtained by using an epoxy resin having no hydroxy group
- component (d) a mixture of a urethane modified epoxy resin, component (a) and component (d) is mentioned.
- An epoxy group has a very strong interaction with an oxygen-containing functional group present in a carbon fiber surface and thus can strongly allow a sizing-agent component to adhere to the carbon fiber surface. Furthermore, since a urethane bonding unit, which is produced from a polyhydroxy compound and a diisocyanate that contains an aromatic ring, is contained, flexibility and strong interaction with a carbon fiber surface due to the polarity of a urethane bond and an aromatic ring can be imparted. Accordingly, the urethane modified epoxy resin that has an epoxy group and the above urethane bonding unit is a compound that is capable of strongly bonding to a carbon fiber surface and that has flexibility. In other words, such a sizing agent composition forms a flexible interface layer that strongly adheres to a carbon fiber surface. Thus, the mechanical performance of the composite material obtained by impregnating a carbon fiber with a matrix resin and cuing the resin can be improved.
- the component (a) is not particularly limited, and the number of hydroxy groups contained in the component (a) is not limited.
- glycidol, methyl glycidol, bisphenol type F epoxy resin, bisphenol type A epoxy resin and oxycarboxylic acid glycidyl ester epoxy resin can be used.
- a particular preferable resin is a bisphenol type epoxy resin. Since these resins have an aromatic ring, they interact strongly with a carbon fiber surface. Furthermore, in view of heat resistance and rigidity, an epoxy resin having an aromatic ring is often used as the matrix resin in a composite material. This is because compatibility with such a matrix resin is excellent.
- component (a) two types or more epoxy resins can be used.
- component (b) is preferably constituted of any one from among an adduct of bisphenol A with an alkylene oxide, an aliphatic polyhydroxy compound and a polyhydroxymonocarboxy compound or a mixture of these. This is because these compounds can soften the aforementioned urethane modified epoxy resins. Specific examples thereof include an adduct of bisphenol A with 4 to 14 mol of ethylene oxide, an adduct of bisphenol A with 2 to 14 mol of propylene oxide, an adduct of bisphenol A with ethylene oxide-propylene oxide block copolymer, polyethylene glycol, trimethylolpropane and dimethylolpropionic acid.
- component (c) is not particularly limited and a particular preferable component is toluene diisocyanate or xylene diisocyanate.
- an epoxy resin that serves as component (d) is not particularly limited.
- an epoxy resin having two or more epoxy groups in a molecule is employed. This is because the surface of a carbon fiber strongly interacts with an epoxy group and thus these compounds strongly adhere to the surface.
- the type of epoxy group is not particularly limited and a glycidyl type, an alicyclic epoxy group, etc. can be employed.
- Examples of preferable epoxy resin that can be used include a bisphenol type-F epoxy resin, a bisphenol type-A epoxy resin, a novolak-type epoxy resin, a dicyclopentadiene type epoxy resin (Epiclon HP-7200 series: manufactured by DIC Corporation), tris(hydroxyphenyl)methane-type epoxy resin (Epicoat 1032H60, 1032S50: manufactured by Japan Epoxy Resins Co., Ltd.), DPP Novolak type epoxy resin (Epicoat 157S65, 157S70: manufactured by Japan Epoxy Resins Co., Ltd.) and bisphenol A alkylene oxide-added epoxy resin.
- component (d) may be added simultaneously with component (a). Alternatively, after completion of the urethanization reaction, component (d) may be added.
- HYDRAN N320 manufactured by DIC
- the carbon fiber bundle of the present invention that has a strand elastic modulus of 250 GPa or more is obtained through a carbonizing process performed at relatively high temperature. Accordingly, it is beneficial that the carbon fiber is obtained from a precursor fiber that contains as few impurities such as a metal as possible.
- the amount of metal content in the resultant carbon fiber bundle is preferable small.
- the total amount of metal components including alkaline metal, alkaline earth metal, zinc, iron and aluminum is preferably 50 ppm or less. These metals react with carbon, melt or vaporize at a temperature beyond 1000° C., and this constitutes a reason why defective points are formed. Highly strong carbon fiber cannot be manufactured.
- the uneven surface structure can be measured based on the shape of the surface as follows:
- Ra ⁇ 1/( Lx ⁇ Ly ) ⁇ Ly 0 ⁇ LX 0
- Center surface A plane which is parallel to the plane that has a minimum deviation of the height from the place to the actual surface and that divides the actual surface equally into two based on volume. In other words, the portion that is surrounded by the plane and the actual surface, volumes V1 and V2 that correspond to both side portions of the plane are equal to each other.
- the ratio of the major axis and the minor axis (major axis/minor axis) of the cross section of single fibers that constitute a carbon fiber bundle was determined as follows:
- a carbon fiber bundle for measurement was passed through a tube formed of a vinyl chloride resin that has an inner diameter of 1 mm.
- the tube was cut in the shape of a circle by a knife to prepare samples. Subsequently, each sample was allowed to adhere to a SEM sample stand so that the cross-section faced up; Au was deposited in a thickness of about 10 nm by sputtering; and a fiber cross-section was observed by a scanning electron microscope (product name: XL20, manufactured by Philips) under the following conditions: an acceleration voltage of 7.00 kV and a migration distance of 31 mm to measure the major axis and minor axis of the cross section of the single fiber.
- Knot tenacity was measured as follows:
- a grip portion of 25 mm in length was attached to prepare a test sample.
- a load of 0.1 ⁇ 10 ⁇ 3 N/denier was applied to unidirectionally arrange carbon fiber bundles.
- a single knot was formed almost in the center.
- Tension was performed at a crosshead rate of 100 mm/min. Twelve bundles were used for a test. The smallest value and the largest value were removed and the average value of 10 bundles was obtained and used as a measurement value.
- a single carbon fiber was cut into pieces in the length of 20 cm. Each of the single-fiber pieces was allowed to adhere and immobilize onto a mount for a tensile test for a single fiber of 10-mm sample length shown in JIS R7606. An extra portion extruded from the mount was cut and removed. In this manner, samples were prepared.
- a laser (one pulse) having a wavelength of 435 nm, the intensity of which was attenuated by 10% by an attenuator, was applied to the center of a sample in the fiber-axis direction and in the perpendicular direction of the fiber axis to form a hemispherical defect.
- the sample that was attached to a mount was further sandwiched by films and the space within the films was filled with viscous liquid and then subjected to a tensile test.
- a film of about 5 mm in width and about 15 mm in length was prepared and allowed to adhere to the upper portion of both surfaces of the sample mount with an adhesive and sandwiched so as to wrap the sample including the mount.
- a tensile test was performed at a tension rate of 0.5 mm/min to measure the breaking load.
- the obtained SEM image was imported into a personal computer and analyzed by image analyzing software. In this manner, the size of a hemispherical defect and the cross-sectional area of a fiber were measured.
- breaking strength (a) breaking load/fiber cross-sectional area
- size of a hemispherical defect (C) were plotted. The slope of the data was obtained.
- Equation (1) surface energy of surface formed by fracture was obtained from the slope and ultrasonic elastic modulus (E) of a carbon fiber bundle.
- An Ipa value was measured by the following method.
- An electrolyte is adjusted to pH3 with a 5% aqueous phosphoric acid solution and bubbled with nitrogen to eliminate the effect of dissolved oxygen.
- a sample carbon fiber was dipped in the electrolyte as one of the electrodes, whereas, a platinum electrode having a sufficient surface area is used as the other electrode.
- a reference electrode an Ag/AgCl electrode was employed as a reference electrode.
- a sample was formed of a 12000-filament tow having a length of 50 mm.
- the potential to be applied between the carbon fiber electrode and the platinum electrode ranges from ⁇ 0.2 V from +0.8 V and a scanning speed thereof was set to be 2.0 mV/sec.
- a current-voltage curve was drawn by an X-Y recorder.
- a current value i was read with a potential of +0.4 V applied to the Ag/AgCl reference electrode that was used as a reference potential, and an ipa value was calculated in accordance with the following expression (3).
- ipa 1( ⁇ A)/sample length(cm) ⁇ 4 ⁇ weight per unit area(g/cm) ⁇ number of filaments/density(g/cm 3 ) ⁇ 1/2 (3)
- the apparent surface area was calculated from sample length, sample density obtained by the method described in JIS R7601 and mass per unit area. Current value i was divided by the obtained value to obtain an ipa value. The measurement was performed by cyclic voltammetry analyzer Type P-1100 manufactured by Yanagimoto Mfg. Co., Ltd.
- a sample of a carbon fiber bundle was placed in a platinum crucible whose tare was known and calcified in a muffle furnace of 600 to 700° C. The mass thereof was measured to obtain ash content. Subsequently, a predetermined amount of sodium carbonate was added, and the mixture was melted by a burner and dissolved with deionized water in a 50 ml poly measuring flask. The sample was measured by ICP emission spectrometry to determine the amount of Si.
- the dope was ejected from a spinneret having 0.15 mm diameter with 2000 ejection holes arranged therein in a dry-wet spinning manner.
- the dope was ejected into the air, passed through a space of about 5 mm and then solidified in a congealed liquid filled with an aqueous solution containing 79.0 mass % dimethyl formamide and controlled at a temperature of 10° C. to obtain a coagulated fiber.
- the coagulated fiber was drawn (1.1 times) in the air and drawn (2.5 times) in a drawing tank filled with an aqueous solution containing 35 mass % dimethyl formamide and controlled at 60° C.
- the fiber bundle in which a solvent was present was washed with clean water and then drawn (1.4 times) in hot water of 95° C.
- an oil solution containing an amino modified silicone as a main component was attached so as to apply 1.1 mass %, dried and densified.
- the fiber bundle was drawn (2.6 times) between heated rolls to further improve the orientation degree and densification. Thereafter, the bundle was wound up to obtain an acrylonitrile-based precursor fiber bundle.
- the denier of the fiber was 0.77 dtex.
- Precursor fiber bundle (2) was obtained under the same conditions as in precursor fiber bundle (1) except that the draw ratio before washing with water was set to be 2.9 times and the draw ratio in hot water after washing was set to be 1.2 times.
- Precursor fiber bundle (3) was obtained under the same conditions as in precursor fiber bundle (2) except that the denier of the precursor fiber was set to be 0.67 dtex.
- Precursor fiber bundle (4) was obtained under the same conditions as in precursor fiber bundle (2) except that the denier of the precursor fiber was set to be 0.90 dtex.
- Precursor fiber bundle (5) was obtained under the same conditions as in precursor fiber bundle (1) except that the draw ratio before washing with water was set to be 4.1 times, the draw ratio in hot water after washing was set to be 0.9 times and drawing that was performed between heated rolls was set to be 2.4 times.
- Precursor fiber bundle (6) was obtained under the same conditions as in precursor fiber bundle (1) except that the draw ratio before washing with water was set to be 1.9 times and the draw ratio in hot water after washing was set to be 2.0 times.
- Precursor fiber bundle (7) was obtained under the same conditions as in precursor fiber bundle (2) except that the denier of the precursor fiber was set to be 1.0 dtex.
- a plurality of precursor fiber bundles (1), (2), (3), (4), (5), (6) or (7) were arranged in parallel and introduced in an oven for stabilization. Air heated to 220 to 280° C. was sprayed to the precursor fiber bundles to perform stabilization treatment. In this manner, stabilized fiber bundles having a density of 1.345 g/cm 3 were obtained.
- the extension rate was set to be 6% and stabilization treatment time was 70 minutes.
- the stabilized fiber bundles were passed through a first carbonization furnace having a temperature gradient of 300 to 700° C. in nitrogen while the extension rate was increased by 4.5%.
- the temperature gradient was set so as to change linearly.
- the treatment time was 2.0 minutes.
- heat treatment was performed using a second carbonization furnace having a nitrogen atmosphere in which the temperature gradient of 1000 to 1600° C. could be set, at the predetermined temperatures shown in Table 2 or Table 3.
- heat treatment was performed using a third carbonization furnace having a nitrogen atmosphere in which the temperature gradient of 1200 to 2400° C. could be set, at the predetermined temperatures shown in Table 2 or Table 3 to obtain carbon fiber bundles.
- the total extension rate of the fiber bundles through the treatments in the second carbonization furnace and third carbonization furnace was ⁇ 4.0%, and the treatment time in total was set to be 3.5 minutes.
- the fiber bundles were fed to a 10 mass % aqueous ammonium bicarbonate solution.
- Current was supplied between a carbon fiber bundle serving as an anode and a counter pole so as to obtain a quantity of electricity of 40 coulombs per carbon fiber (1 g) to be treated.
- the fiber bundles were washed with warm water of 90° C. and dried.
- Hydran N320 (hereinafter referred to as “sizing agent 1”) was attached onto the fiber bundles in the amount of 0.5 mass % and wound by a bobbin to obtain a carbon fiber bundle.
- a mold-releasing paper coated with epoxy resin #410 that can be used at 180° C. [manufactured by Mitsubishi Rayon Co., Ltd.] in the B stage, 156 carbon fiber bundles released from a bobbin were arranged in parallel and passed through a heat compression roller. In this manner, the carbon fiber bundles were impregnated with epoxy resin.
- a protecting film was laminated on the resultant bundles to prepare a prepreg arranged in a unidirection (hereinafter referred to as a “UD prepreg”) having a resin content of about 33 mass %, a carbon fiber mass per unit area of 125 g/m 2 and a width of 500 mm.
- a laminate board was prepared by using the UD prepreg and the tensile strength of the laminate board at angle 0° was evaluated by the evaluation method in accordance with ASTM D3039.
- a single fiber does not have an uneven surface structure that has a length of 0.6 ⁇ m or more and that extends in the longitudinal direction of a fiber but has a microscopic uneven structure that has a length of 300 nm or less.
- a dope which was prepared in the same manner as in Production Example 1, was ejected from a spinneret having 0.13 mm diameter with 2000 of ejection holes arranged therein in a dry-wet spinning manner.
- the dope was ejected into the air, passed through a space of about 5 mm and then solidified in a congealed liquid filled with an aqueous solution containing 77.0 mass % dimethyl formamide and controlled at a temperature of 5° C. to obtain a coagulated fiber.
- the coagulated fiber was drawn (1.3 times) in the air and drawn (2.0 times) in a drawing tank filled with an aqueous solution controlled at 60° C.
- the fiber bundle in which a solvent was present was washed with clean water and then drawn (2.0 times) in hot water of 95° C.
- an oil solution containing an amino modified silicone as a main component was attached so as to apply 1.0 mass %, dried and densified.
- the fiber bundle was drawn (1.9 times) between heated rolls to further improve the orientation degree and densification. Thereafter, the bundle was wound up to obtain the precursor fiber bundle.
- the denier of the fiber was 0.77 dtex.
- a carbon fiber bundle was prepared under the same carbonizing conditions as in Example 5 except that the third carbonization furnace was not used. Furthermore, a laminate board was prepared in the same manner and mechanical performance was evaluated to obtain the results shown in Table 2. Note that, it was confirmed that the single fiber has no uneven surface structure having a length of 0.6 ⁇ m or more and extending in the longitudinal direction of the fiber and has an uneven microscopic structure having a length of 300 nm or less.
- Carbon fiber bundles were obtained in the same manner as in Example 2 except that the carbonizing conditions were changed.
- the evaluation results are shown in Table 4. Note that, in any one of Examples, it was confirmed that the single fiber has no uneven surface structure having a length of 0.6 ⁇ m or more and extending in the longitudinal direction of the fiber and has an uneven microscopic structure having a length of 300 nm or less.
- Carbon fiber bundles were obtained in the same manner as in Example 5 except that the surface treatment conditions were changed. The evaluation results are shown in Table 5. Note that in any of the Examples, it was confirmed that the single fiber has no uneven surface structure having a length of 0.6 ⁇ m or more and extending in the longitudinal direction of the fiber and has an uneven microscopic structure having a length of 300 nm or less.
- Carbon fiber bundles were obtained in the same manner as in Example 5 except that the types and amounts attached of sizing agents were changed.
- the evaluation results are shown in Table 5. Note that in any one of the Examples, it was confirmed that the single fiber has no uneven surface structure having a length of 0.6 ⁇ m or more and extending in the longitudinal direction of the fiber and has an uneven microscopic structure having a length of 300 nm or less.
- sizing agent 2 sizing agent 2
- sizing agent 3 sizing agent 3
- sizing agent 4 were prepared as follows:
- polyol (3.2 mol) consisting of 1.8 mol of an adduct of bisphenol A with 8 mol of propylene oxide, 0.8 mol of trimethylolpropane and 0.6 mol of dimethyloipropionic acid were placed. Furthermore, 0.5 g of 2,6-di(t-butyl) 4-methylphenol (BHT) as a reaction inhibitor and 0.2 g of dibutyltin dilaurate as a reaction catalyst were added and stirred until a homogeneous mixture was obtained. Herein, if necessary, methyl ethyl ketone was added as a viscosity moderator.
- BHT 2,6-di(t-butyl) 4-methylphenol
- metaxylene diisocyanate (3.4 mol) was added dropwise and polymerization of a urethane prepolymer was performed while stirring at a reaction temperature of 50° C. for a reaction time of 2 hours. Then, Epicoat 834 (manufactured by JER) (0.25 mol) was added and reacted with an isocyanate group at an end of the urethane prepolymer to obtain an epoxy modified urethane resin.
- the epoxy modified urethane resin (90 parts by mass) and “Pluronic F88” (10 parts by mass) manufactured by ADEKA Corporation as an emulsifier were blended to prepare an aqueous dispersion.
- the epoxy modified urethane resin (80 parts by mass) and Pluronic F88 (20 parts by mass) manufactured by ADEKA Corporation as an emulsifier were mixed to prepare an aqueous dispersion.
- the carbon fiber bundle of the present invention can be used as a constructional material for airplanes and high speed moving bodies.
Landscapes
- Engineering & Computer Science (AREA)
- Textile Engineering (AREA)
- Chemical & Material Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- General Chemical & Material Sciences (AREA)
- Inorganic Chemistry (AREA)
- Manufacturing & Machinery (AREA)
- Health & Medical Sciences (AREA)
- Toxicology (AREA)
- Inorganic Fibers (AREA)
- Reinforced Plastic Materials (AREA)
- Treatments For Attaching Organic Compounds To Fibrous Goods (AREA)
- Artificial Filaments (AREA)
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2009-139336 | 2009-06-10 | ||
JP2009139336 | 2009-06-10 | ||
PCT/JP2010/059828 WO2010143681A1 (ja) | 2009-06-10 | 2010-06-10 | 機械的性能発現に優れた炭素繊維束 |
Related Parent Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2010/059828 A-371-Of-International WO2010143681A1 (ja) | 2009-06-10 | 2010-06-10 | 機械的性能発現に優れた炭素繊維束 |
Related Child Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US16/158,646 Continuation US20190040549A1 (en) | 2009-06-10 | 2018-10-12 | Carbon fiber bundle that develops high mechanical performance |
Publications (1)
Publication Number | Publication Date |
---|---|
US20120088103A1 true US20120088103A1 (en) | 2012-04-12 |
Family
ID=43308936
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US13/377,289 Abandoned US20120088103A1 (en) | 2009-06-10 | 2010-06-10 | Carbon fiber bundle that develops high mechanical performance |
US16/158,646 Pending US20190040549A1 (en) | 2009-06-10 | 2018-10-12 | Carbon fiber bundle that develops high mechanical performance |
Family Applications After (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US16/158,646 Pending US20190040549A1 (en) | 2009-06-10 | 2018-10-12 | Carbon fiber bundle that develops high mechanical performance |
Country Status (10)
Country | Link |
---|---|
US (2) | US20120088103A1 (pt) |
EP (1) | EP2441866B1 (pt) |
JP (1) | JP4908636B2 (pt) |
KR (1) | KR101340225B1 (pt) |
CN (1) | CN102459728B (pt) |
BR (1) | BRPI1012996A2 (pt) |
CA (1) | CA2764662C (pt) |
ES (1) | ES2534650T3 (pt) |
TW (1) | TWI396786B (pt) |
WO (1) | WO2010143681A1 (pt) |
Cited By (13)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2013249562A (ja) * | 2012-06-01 | 2013-12-12 | Dic Corp | 繊維集束剤ならびに集束されたガラス繊維及び炭素繊維 |
JP2015161056A (ja) * | 2014-02-28 | 2015-09-07 | 三菱レイヨン株式会社 | 炭素繊維用アクリロニトリル前駆体繊維束及びその製造方法 |
JP2016196711A (ja) * | 2015-04-03 | 2016-11-24 | Dic株式会社 | 繊維集束剤ならびに集束されたガラス繊維及び炭素繊維 |
JP2019023378A (ja) * | 2018-11-16 | 2019-02-14 | 三菱ケミカル株式会社 | 炭素繊維用アクリロニトリル前駆体繊維束及びその製造方法 |
US10792194B2 (en) | 2014-08-26 | 2020-10-06 | Curt G. Joa, Inc. | Apparatus and methods for securing elastic to a carrier web |
US10837127B2 (en) | 2012-04-18 | 2020-11-17 | Mitsubishi Chemical Corporation | Carbon fiber bundle and method of producing carbon fiber bundle |
US20200378035A1 (en) * | 2014-10-08 | 2020-12-03 | Georgia Tech Research Corporation | Method for making High strength and high modulus carbon fibers |
US11313054B2 (en) * | 2016-05-24 | 2022-04-26 | Toray Industries, Inc. | Carbon fiber bundle |
US11493070B2 (en) * | 2015-03-12 | 2022-11-08 | Ut-Battelle, Llc | Laser nanostructured surface preparation for joining materials |
US20230087214A1 (en) * | 2021-09-22 | 2023-03-23 | Hao-Chia WU | Method for splitting carbon fiber tow |
US11701268B2 (en) | 2018-01-29 | 2023-07-18 | Curt G. Joa, Inc. | Apparatus and method of manufacturing an elastic composite structure for an absorbent sanitary product |
US11744744B2 (en) | 2019-09-05 | 2023-09-05 | Curt G. Joa, Inc. | Curved elastic with entrapment |
US11925538B2 (en) | 2019-01-07 | 2024-03-12 | Curt G. Joa, Inc. | Apparatus and method of manufacturing an elastic composite structure for an absorbent sanitary product |
Families Citing this family (30)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP5708965B2 (ja) * | 2009-06-10 | 2015-04-30 | 三菱レイヨン株式会社 | アクリロニトリル系前駆体繊維束および炭素繊維束の製造方法 |
JP2012122164A (ja) * | 2010-12-08 | 2012-06-28 | Mitsubishi Rayon Co Ltd | 機械的特性発現に優れた炭素繊維 |
JP5592906B2 (ja) | 2012-02-08 | 2014-09-17 | トヨタ自動車株式会社 | 燃料電池用のガス拡散層と燃料電池、および燃料電池用のガス拡散層の製造方法 |
JP6105332B2 (ja) * | 2012-03-09 | 2017-03-29 | 帝人株式会社 | 強化繊維及びそれからなる強化繊維束 |
JP5842916B2 (ja) * | 2012-03-29 | 2016-01-13 | 三菱レイヨン株式会社 | 炭素繊維熱可塑性樹脂プリプレグ、炭素繊維複合材料、ならびに製造方法 |
CN103790019B (zh) * | 2012-10-26 | 2016-05-04 | 中国石油化工股份有限公司 | 一种环氧基碳纤维上浆剂乳液及其制备和应用 |
CN103772638B (zh) * | 2012-10-26 | 2016-05-04 | 中国石油化工股份有限公司 | 由聚氨酯结构改性的双酚f环氧树脂组合物及其制备和应用 |
CN103788322B (zh) * | 2012-10-26 | 2016-09-14 | 中国石油化工股份有限公司 | 由聚氨酯结构改性的双酚a环氧树脂组合物及其制备和应用 |
CN103790020B (zh) * | 2012-10-26 | 2016-06-29 | 中国石油化工股份有限公司 | 聚氨酯结构改性的环氧树脂上浆剂乳液及其制备和应用 |
DE102013206983A1 (de) * | 2013-04-18 | 2014-10-23 | Bayerische Motoren Werke Aktiengesellschaft | Verfahren und Vorrichtung zur Herstellung von unidirektionalen Kohlenstofffasergelegen |
JP6105427B2 (ja) * | 2013-07-26 | 2017-03-29 | 東邦テナックス株式会社 | 炭素繊維 |
KR102189516B1 (ko) * | 2013-07-30 | 2020-12-11 | 도레이 카부시키가이샤 | 탄소 섬유 다발 및 내염화 섬유 다발 |
JP5766864B2 (ja) * | 2013-10-24 | 2015-08-19 | 三菱エンジニアリングプラスチックス株式会社 | 樹脂組成物、樹脂成形品、および樹脂成形品の製造方法 |
JP5900663B2 (ja) * | 2013-12-03 | 2016-04-06 | 三菱レイヨン株式会社 | 繊維強化樹脂積層体 |
CN104390996A (zh) * | 2014-11-12 | 2015-03-04 | 吉林大学 | 一种碳纤维表面元素组成和结构的测试分析方法 |
JP5963063B2 (ja) * | 2014-12-15 | 2016-08-03 | 三菱レイヨン株式会社 | 炭素繊維束 |
US10344403B2 (en) * | 2014-12-29 | 2019-07-09 | Cytec Industries Inc. | Densification of polyacrylonitrile fiber |
DE102015111491A1 (de) * | 2015-07-15 | 2017-01-19 | Schott Ag | Verfahren und Vorrichtung zum Abtrennen von Glas- oder Glaskeramikteilen |
JP5999462B2 (ja) * | 2016-03-07 | 2016-09-28 | 三菱レイヨン株式会社 | 機械的特性発現に優れた炭素繊維 |
JP6229209B2 (ja) * | 2016-06-23 | 2017-11-15 | 三菱ケミカル株式会社 | 炭素繊維束 |
US10625441B2 (en) * | 2016-11-16 | 2020-04-21 | Mitsubishi Gas Chemical Company, Inc. | Method for manufacturing formed article |
US10787755B2 (en) * | 2017-06-05 | 2020-09-29 | The Boeing Company | Method and apparatus for manufacturing carbon fibers |
WO2019026724A1 (ja) * | 2017-07-31 | 2019-02-07 | 東レ株式会社 | シートモールディングコンパウンド、プリプレグおよび繊維強化複合材料 |
EP3662000A1 (en) * | 2017-08-01 | 2020-06-10 | SABIC Global Technologies B.V. | Carbon fiber tow with improved processability |
EP3661712A1 (en) * | 2017-08-01 | 2020-06-10 | SABIC Global Technologies B.V. | Method and system for producing unidirctional carbon fiber tape as well as method for surface treating carbon fibers |
JP6477821B2 (ja) * | 2017-10-11 | 2019-03-06 | 三菱ケミカル株式会社 | 炭素繊維束 |
JP6575696B1 (ja) * | 2017-10-31 | 2019-09-18 | 東レ株式会社 | 炭素繊維束およびその製造方法 |
CN109957969B (zh) * | 2017-12-25 | 2022-01-07 | 比亚迪股份有限公司 | 一种碳纤维上浆剂、其制备方法、增强碳纤维及碳纤维复合材料 |
EP3553132A1 (en) * | 2018-04-13 | 2019-10-16 | SABIC Global Technologies B.V. | Fiber reinforced composition with good impact performance and flame retardance |
TWI767796B (zh) * | 2021-07-22 | 2022-06-11 | 臺灣塑膠工業股份有限公司 | 碳纖維的製造方法和碳纖維複合瓶 |
Citations (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS59187625A (ja) * | 1983-04-01 | 1984-10-24 | Asahi Chem Ind Co Ltd | 先細尖端繊維の製造方法 |
US4603157A (en) * | 1984-05-23 | 1986-07-29 | Mitsubishi Rayon Co., Ltd. | Intermediate for composite material |
US4832932A (en) * | 1985-12-19 | 1989-05-23 | Mitsubishi Rayon Co., Ltd. | Carbon fiber for composite material |
US5298576A (en) * | 1991-02-25 | 1994-03-29 | Toray Industries, Inc. | Sizing agent for carbon fiber and carbon fiber treated with said sizing agent |
US5858486A (en) * | 1995-02-27 | 1999-01-12 | Sgl Carbon Composites, Inc. | High purity carbon/carbon composite useful as a crucible susceptor |
JP2004197230A (ja) * | 2002-12-16 | 2004-07-15 | Mitsubishi Rayon Co Ltd | 高機械物性と低導電性を発現する繊維強化樹脂用炭素繊維束及びチョップド炭素繊維束並びに炭素繊維強化樹脂組成物 |
JP2004211240A (ja) * | 2002-12-27 | 2004-07-29 | Mitsubishi Rayon Co Ltd | 炭素繊維、炭素繊維用アクリロニトリル系前駆体繊維、およびそれらの製造方法 |
JP2006183159A (ja) * | 2004-12-27 | 2006-07-13 | Toray Ind Inc | 炭素繊維前駆体繊維用シリコーン油剤、炭素繊維前駆体繊維、耐炎化繊維および炭素繊維およびそれらの製造方法 |
JP2009046770A (ja) * | 2007-08-16 | 2009-03-05 | Mitsubishi Rayon Co Ltd | アクリロニトリル系炭素繊維前駆体繊維 |
Family Cites Families (10)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
GB8727410D0 (en) * | 1987-11-23 | 1987-12-23 | Ici Plc | Inorganic oxide fibres |
JPH04240220A (ja) * | 1991-01-21 | 1992-08-27 | Mitsubishi Rayon Co Ltd | 炭素繊維用プレカーサー |
IT1252680B (it) | 1991-11-13 | 1995-06-23 | Sviluppo Settori Impiego Srl | Procedimento per la realizzazione di corpi di materiale polimerico comprendenti un nucleo di materiale espanso racchiuso da un guscio esterno, e dispositivo utilizzato in tale procedimento |
US5436275A (en) | 1993-11-30 | 1995-07-25 | Japan Exlan Company Limited | Porous acrylonitrile polymer fiber |
JPH11124744A (ja) | 1997-10-20 | 1999-05-11 | Toray Ind Inc | 炭素繊維前駆体繊維および炭素繊維の製造方法 |
GB2378918B (en) * | 2000-05-09 | 2003-12-24 | Mitsubishi Rayon Co | Acrylonitrile-based fiber bundle for carbon fiber precursor and method for preparation thereof |
TW591157B (en) * | 2001-05-25 | 2004-06-11 | Mitsubishi Rayon Co | Sizing agent for carbon fiber, its water dispersing solution, carbon fiber with sizing handling, sheet matter with using the carbon fiber and carbon fiber reinforced composite |
JP2005133274A (ja) | 2003-10-10 | 2005-05-26 | Mitsubishi Rayon Co Ltd | 炭素繊維と同炭素繊維を含む複合材料 |
ATE497551T1 (de) * | 2004-12-27 | 2011-02-15 | Toray Industries | Ölavivage für carbonfaser-präkursorfaser, carbonfaser sowie verfahren zur herstellung von carbonfaser |
JP4957251B2 (ja) * | 2005-12-13 | 2012-06-20 | 東レ株式会社 | 炭素繊維、炭素繊維製造用ポリアクリロニトリル系前駆体繊維の製造方法、および、炭素繊維の製造方法 |
-
2010
- 2010-06-10 ES ES10786212.0T patent/ES2534650T3/es active Active
- 2010-06-10 CA CA2764662A patent/CA2764662C/en active Active
- 2010-06-10 WO PCT/JP2010/059828 patent/WO2010143681A1/ja active Application Filing
- 2010-06-10 JP JP2010524014A patent/JP4908636B2/ja active Active
- 2010-06-10 CN CN2010800251194A patent/CN102459728B/zh active Active
- 2010-06-10 KR KR1020127000670A patent/KR101340225B1/ko active IP Right Grant
- 2010-06-10 TW TW099118900A patent/TWI396786B/zh active
- 2010-06-10 BR BRPI1012996A patent/BRPI1012996A2/pt not_active Application Discontinuation
- 2010-06-10 EP EP10786212.0A patent/EP2441866B1/en active Active
- 2010-06-10 US US13/377,289 patent/US20120088103A1/en not_active Abandoned
-
2018
- 2018-10-12 US US16/158,646 patent/US20190040549A1/en active Pending
Patent Citations (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS59187625A (ja) * | 1983-04-01 | 1984-10-24 | Asahi Chem Ind Co Ltd | 先細尖端繊維の製造方法 |
US4603157A (en) * | 1984-05-23 | 1986-07-29 | Mitsubishi Rayon Co., Ltd. | Intermediate for composite material |
US4832932A (en) * | 1985-12-19 | 1989-05-23 | Mitsubishi Rayon Co., Ltd. | Carbon fiber for composite material |
US5298576A (en) * | 1991-02-25 | 1994-03-29 | Toray Industries, Inc. | Sizing agent for carbon fiber and carbon fiber treated with said sizing agent |
US5858486A (en) * | 1995-02-27 | 1999-01-12 | Sgl Carbon Composites, Inc. | High purity carbon/carbon composite useful as a crucible susceptor |
JP2004197230A (ja) * | 2002-12-16 | 2004-07-15 | Mitsubishi Rayon Co Ltd | 高機械物性と低導電性を発現する繊維強化樹脂用炭素繊維束及びチョップド炭素繊維束並びに炭素繊維強化樹脂組成物 |
JP2004211240A (ja) * | 2002-12-27 | 2004-07-29 | Mitsubishi Rayon Co Ltd | 炭素繊維、炭素繊維用アクリロニトリル系前駆体繊維、およびそれらの製造方法 |
JP2006183159A (ja) * | 2004-12-27 | 2006-07-13 | Toray Ind Inc | 炭素繊維前駆体繊維用シリコーン油剤、炭素繊維前駆体繊維、耐炎化繊維および炭素繊維およびそれらの製造方法 |
JP2009046770A (ja) * | 2007-08-16 | 2009-03-05 | Mitsubishi Rayon Co Ltd | アクリロニトリル系炭素繊維前駆体繊維 |
Cited By (16)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US11970791B2 (en) | 2012-04-18 | 2024-04-30 | Mitsubishi Chemical Corporation | Carbon fiber bundle and method of producing carbon fiber bundle |
US10837127B2 (en) | 2012-04-18 | 2020-11-17 | Mitsubishi Chemical Corporation | Carbon fiber bundle and method of producing carbon fiber bundle |
JP2013249562A (ja) * | 2012-06-01 | 2013-12-12 | Dic Corp | 繊維集束剤ならびに集束されたガラス繊維及び炭素繊維 |
JP2015161056A (ja) * | 2014-02-28 | 2015-09-07 | 三菱レイヨン株式会社 | 炭素繊維用アクリロニトリル前駆体繊維束及びその製造方法 |
US10792194B2 (en) | 2014-08-26 | 2020-10-06 | Curt G. Joa, Inc. | Apparatus and methods for securing elastic to a carrier web |
US11690767B2 (en) | 2014-08-26 | 2023-07-04 | Curt G. Joa, Inc. | Apparatus and methods for securing elastic to a carrier web |
US11773514B2 (en) * | 2014-10-08 | 2023-10-03 | Georgia Tech Research Corporation | Method for making high strength and high modulus carbon fibers |
US20200378035A1 (en) * | 2014-10-08 | 2020-12-03 | Georgia Tech Research Corporation | Method for making High strength and high modulus carbon fibers |
US11493070B2 (en) * | 2015-03-12 | 2022-11-08 | Ut-Battelle, Llc | Laser nanostructured surface preparation for joining materials |
JP2016196711A (ja) * | 2015-04-03 | 2016-11-24 | Dic株式会社 | 繊維集束剤ならびに集束されたガラス繊維及び炭素繊維 |
US11313054B2 (en) * | 2016-05-24 | 2022-04-26 | Toray Industries, Inc. | Carbon fiber bundle |
US11701268B2 (en) | 2018-01-29 | 2023-07-18 | Curt G. Joa, Inc. | Apparatus and method of manufacturing an elastic composite structure for an absorbent sanitary product |
JP2019023378A (ja) * | 2018-11-16 | 2019-02-14 | 三菱ケミカル株式会社 | 炭素繊維用アクリロニトリル前駆体繊維束及びその製造方法 |
US11925538B2 (en) | 2019-01-07 | 2024-03-12 | Curt G. Joa, Inc. | Apparatus and method of manufacturing an elastic composite structure for an absorbent sanitary product |
US11744744B2 (en) | 2019-09-05 | 2023-09-05 | Curt G. Joa, Inc. | Curved elastic with entrapment |
US20230087214A1 (en) * | 2021-09-22 | 2023-03-23 | Hao-Chia WU | Method for splitting carbon fiber tow |
Also Published As
Publication number | Publication date |
---|---|
JPWO2010143681A1 (ja) | 2012-11-29 |
CA2764662A1 (en) | 2010-12-16 |
EP2441866B1 (en) | 2015-02-18 |
BRPI1012996A2 (pt) | 2018-01-16 |
CA2764662C (en) | 2013-07-30 |
KR20120024954A (ko) | 2012-03-14 |
KR101340225B1 (ko) | 2013-12-10 |
CN102459728B (zh) | 2013-09-18 |
EP2441866A1 (en) | 2012-04-18 |
JP4908636B2 (ja) | 2012-04-04 |
TWI396786B (zh) | 2013-05-21 |
TW201107547A (en) | 2011-03-01 |
CN102459728A (zh) | 2012-05-16 |
EP2441866A4 (en) | 2013-05-22 |
WO2010143681A1 (ja) | 2010-12-16 |
ES2534650T3 (es) | 2015-04-27 |
US20190040549A1 (en) | 2019-02-07 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US20190040549A1 (en) | Carbon fiber bundle that develops high mechanical performance | |
JP5708965B2 (ja) | アクリロニトリル系前駆体繊維束および炭素繊維束の製造方法 | |
EP2441865B1 (en) | Acrylonitrile swollen yarn for carbon fiber, precursor fiber bundle, flame-proof fiber bundle, carbon fiber bundle, and production methods thereof | |
US10023979B2 (en) | Bundle of carbon fibers and method of manufacturing the same | |
KR101902087B1 (ko) | 탄소 섬유 열가소성 수지 프리프레그, 탄소 섬유 복합 재료 및 제조 방법 | |
JP5963063B2 (ja) | 炭素繊維束 | |
JP4023226B2 (ja) | 炭素繊維束の処理方法 | |
JP2012122164A (ja) | 機械的特性発現に優れた炭素繊維 | |
JP6229209B2 (ja) | 炭素繊維束 | |
JP2018048437A (ja) | 炭素繊維束 | |
JP5999462B2 (ja) | 機械的特性発現に優れた炭素繊維 | |
JP6590040B2 (ja) | 機械的特性発現に優れた炭素繊維 | |
CN113597484B (zh) | 碳纤维束及其制造方法 | |
JP2016194191A (ja) | 機械的特性発現に優れた炭素繊維 | |
JP6040786B2 (ja) | 炭素繊維束 | |
WO2024090196A1 (ja) | 炭素繊維束、および、それを用いた炭素繊維強化複合材料 | |
JP2016125173A (ja) | 炭素繊維束およびその製造方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: MITSUBISHI RAYON CO., LTD., JAPAN Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:SUGIURA, NAOKI;OKUYA, TAKAHIRO;HASHIMOTO, HIROSHI;AND OTHERS;REEL/FRAME:027383/0970 Effective date: 20111201 |
|
AS | Assignment |
Owner name: MITSUBISHI CHEMICAL CORPORATION, JAPAN Free format text: CHANGE OF NAME;ASSIGNOR:MITSUBISHI RAYON CO., LTD.;REEL/FRAME:043028/0747 Effective date: 20170403 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- AFTER EXAMINER'S ANSWER OR BOARD OF APPEALS DECISION |