TW393518B - High hardness martensitic stainless steel with good pitting corrosion resistance - Google Patents

High hardness martensitic stainless steel with good pitting corrosion resistance Download PDF

Info

Publication number
TW393518B
TW393518B TW085100295A TW85100295A TW393518B TW 393518 B TW393518 B TW 393518B TW 085100295 A TW085100295 A TW 085100295A TW 85100295 A TW85100295 A TW 85100295A TW 393518 B TW393518 B TW 393518B
Authority
TW
Taiwan
Prior art keywords
less
stainless steel
high hardness
hardness
copper
Prior art date
Application number
TW085100295A
Other languages
English (en)
Inventor
Toshihiro Uehara
Original Assignee
Hitachi Metals Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=11570320&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=TW393518(B) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by Hitachi Metals Ltd filed Critical Hitachi Metals Ltd
Application granted granted Critical
Publication of TW393518B publication Critical patent/TW393518B/zh

Description

經濟部中央樣準局員工消費合作社印製 A7 ___B7 五、發明説明(,) 背篑抟Μ 本發明偽有關於一種具優良熱加工性之麻田散體不绣 鋼,其適合作為生産兼具優良抗蝕性(尤其是抗點蝕性 )和高硬度之材料,如用於開放空氣中,且可曝露於龍 頭水、雨水、冷凝露水及其類似水中的釘子、螺絲、螺 絲削邊刀、彈簧等,邇包括塑性模製用之模子、塑膠射 出膜製機的零件等。 到目前為止,釘子、螺絲、螺絲削邊刀、揮簧等須高 硬度的材料像使用含大量硪之硕鋼或合金鎸。但因上述型 態的鋼材中少量的合金元素(如鉻)會導致腐蝕,甚至 是曝露於龍頭水、兩水、冷凝露水及其類似水之低腐蝕 性琛境也易遭受腐蝕。因此産生了外表易受損傷、強度 也遭受破壤的問題。 Β —方面,須使用低腐蝕性的不銹銷。奧氏不銹網( 如SUS304、SUS316)具有優良的抗腐蝕性,但有加工硬 化性大且冷成形性不良,其甚至在施予明顯強烈的冷成 形時,硬度最大約為43HRC。因此奧氏不綉鋼不適合高 硬度的應用。此外如SUS430之奧氏不銹銷其加工硬化性 小且易冷成形,但硬度卻相當小。據此,奧氏不銹鋼也 不適合高硬度的應用。 已知麻田散體不銹鋼為高硬度不銹鋼。例如廣泛用於 汽車和其他工業之典型材料的SUS410點抗蝕性和硬度均 無法於人滿意,因為其抗蝕性不足、硬度最大也只有約 42HRC。雖然麻田散體不綉鏑SUS440C有非常高的硬度, 本紙張尺度適用中國國家標準(CNS )八4規格(210Χ 297公釐) ---------,,、裝-- (請先閱讀背面之注意事項再填寫本頁) 訂- 經濟部中央標準局員工消費合作社印製 A7 ___B7_ 五、發明説明(】) 但是其碩含量高約1%,因此硬度不超過58HRC,且就不 銹鋼的抗蝕性而言邇是不足的。S外,一般抗蝕性高的 不銹網雖然整體不太遭受腐蝕,但可能在小區域有局部 腐蝕,亦卽,導致所諝的的點蝕。這會使高硬度材料的 鏑材從腐蝕點開始破裂。 除此之外,日本專利公開(公開掲露)公報第57-70265 號提出高硬度之麻田散臞不銹綱,和日本專利公開(公 開掲露)公報第6-264194號提出具有優良抗蝕性的麻田 散體不锈鋼,和一種鑽孔出銷的螺絲。 掲露於日本專利公開(公開掲露)公報第57-70265號之 麻田散體不綉鋼,内含有1.0至3.0%的銅、和不超過2% 的錁,若有需要其中加入0.5至3.0%的鉬。但是這種網 材雖然錁加人量少,但因銅含量高,會使熱加工性不良 。在此,因組成物組成的關傜,易形成5-雄酸鹽,而 有點蝕的問題。 此外,掲露於日本專利公開(公開掲露)公報第6-264194 號之麻田散體不锈_,雖不含銅,但是大量錁和鉬。但 是瑄種鋼材的間題,在於錁含量高,所以一次退火處理 之退火後硬度不夠低。故需要數次退火處理,使製程過 於複雜。更者,甚至在退火處理數個重覆步驟後,硬度 邏不夠低,難以進行強烈的冷成形。 鑑於上述,需要一種麻田散體不綉網,能輕易進行熱 加工和冷成形,且在驟冷和回火後有優良抗黏蝕性和高 硬度。 本紙張尺度逋用中國國家標準(CNS ) Α4規格(210Χ297公釐) 1' ....... — : -j- I — I I - Hr \—Ψ v 、τ (請先閱讀背面之注意事項再填寫本頁) __B7_ 五、發明説明(4 ) 發明椹示 本發明目的在於提供一種便宜的具優良熱加工性之麻 田散體不锈鋼,其無須複雜退火處理即可施予冷成形, 且在驟冷和回火後兼具良好抗點蝕性和高硬度。 本發明深入研究發現一種内含有13%鉻的麻田散體不 锈鋼,其具有優良熱加工性、優良冷成形性、和兼具高 硬度和優良抗黏蝕性。結果,在驟冷和回火後發現下列 事項。為增加抗黏蝕性,在鏑和氮為必要成分情況下, 加入少量的銅非常有效。鉬的加入易形成δ-嫌酸鹽, 降低抗點蝕性和熱加工性。因此必須也加入少量的鏢和 大量的m,來抑制不利於本發明之s-鐵酸鹽的産生。 本發明s—個特色在於適當平衡合金元素,使得如下方 程式π)所定義之a值(以鉻當量表示)低得難以足以控 制δ-鐵酸鹽的形成,而如下方程式(2)所定義之B值則 高得足以增加抗點蝕性:
A= - 40C + 6Si - 2Mn - 4Νί + Cr + 4Μο + 2V -2Cu - 30H + 1 1V + lOTi + 5Hb ...(1) (式中選擇設定那些加起來不是零的元素來計算A值)。 經濟部中央標準局員工消費合作社印裝 (請先閱讀背面之注意事項再填寫本頁) L______________ B= Cr + 3.3Mo + 1 . 65W + Cu + 30N ...(2) (式中選揮設定那些加起來不是零的元素來計算B值)。 上述合金成分鐘,銅的加入不足改善抗點蝕性也改善 冷加工性。由此觀點來看,儘可能銅的含量越多越好。 但若銅的含量過多,則熱加工性將被破壤。 本發明再一特色在於,因含有13%鉻之高硬度麻田散 本紙張尺度適用中國國家標準(CNS ) A4規格(210X297公釐) 經濟部中央標準局員工消費合作社印裝 A7 B7 五、發明説明(‘) 體不綉鋼中含有如钼和氮之易使加工性惡化的元素,故 鎳和銅兩者含量各別須在一特定的範圍,並使錁/銅比 大於0.2,這樣一來,除了具有優良抗點蝕性和冷加工性 外,邇可得到令人滿意的熱加工性。 本發明再一特色在於保持適當低量的磺,大董加入氮 ,以在不減低抗點蝕性情況下達到高硬度。 特定而言,本發明第一觀點在於具有優良抗點蝕性之 高硬度麻田散體不锈鋼,該銅材以重量計,實質上包括 超遇0.15%但不多於0.40%的碩、不超遇2.0%的矽、 不超遇2.0%的錳、不低於11.0%但少於15.0%的絡、 1.0至3.0%的鉬或以Mo + l/ 2W表示之箱和鎢0.02至0. 15% 氤、0.1至1.5%的錁,0.1%至2.0%的銅、其餘均為鐵 成分,其中内含的鍊和銅存在如下方程式(3)的蘭係, 而以下方程式(1)定義之Μ直不超過10,和以下方程式(2) 定義之Β值不小於20: A= - 40C + 6Si - 2Hn - 4Hi + Cr + 4Ho + 2tf -2Cu - 30H + 11V + lOTi + 5Hb …(1) (式中選擇設定那些加起來不是零的元素來計算A值) B= Cr + 3.3Ho + 1 . 65W + Cu + 30N …(2) (式中灌擇設定那些加起來不是零的元素來計算B值)。 N i / Cu >0.2 ...(3)0 根據本發明第一觀點之具有優良抗點蝕性之高硬度麻 田散體不銹鋼,其較佳的組成若以重董計,實質上包括 超過0.15%但不多於0.40%的碩、不超遇2.0%的矽、不 本紙張尺度適用中國國家標準(CNS ) A4規格(210X297公釐) —^n i^i— ~ nn flu ABIffi \ V u^. 、T (請先閱讀背面之注意事項再填寫本頁) - A7 B7 五、發明説明(丄) 超遇2.0%的錳、比0.2%多但低於1.0%的錁、不低於 11.0%但少於15.0:ί的絡、1.0至3.0%的ft或鎢以MO + 1/2W 表示之鉬和鎢、不低於0.1%但少於1.0%的銅、0.02至 0.15%的氮、其餘均為鐵•以下方程式(1)定義之A值 不超遇10,和以下方程式(2)定義之B值不小於20:
A= - 40C + 6Si - 2Hn - 4Hi + Cr + 4Mo + 2V -2Cu - 30H + 11V + lOTi + 5Hb ...(1) (式中遘擇設定那些加起來不是零的元素來計算A值)。 B= Cr + 3.3Mo + 1.65W + Cu + 30H ...(2) (式中蘧擇設定那些加起來不是零的元素來計算B值>。 根據本發明第一觀黏之具有優良抗黏蝕性之高硬度麻 田散黼不銹鋼,其更佳的組成若以重量計,實質上包括 超過0.20%至0.35%的硪、不超«2.0%的矽、不 超遇2.0%的錳、0.3%至0.75的錁、不低於11.0%但少 於15.0的鉻、1.0至3.0%的SB或以Ho + l/2W表示之鉬和 鎢、不低於0.1%但少於1.0¾的鋦、〇.〇2至0.15%的氮 、其餘均為鐵,以下方程式Π)定義之A值不超遇1〇, 和以下方程式(2>定義之B值不小於20 : 經濟部中央標準局員工消費合作社印製 (請先閱讀背面之注意事項再填寫本頁} -
A= - 40C + 6Si - 2Hn - 4Hi + Cr + 4Mo + 2V -2Cu - 30H + UV + lOTi + 5Hb ...(1) (式中選擇設定那些加起來不是零的元素來計算A值> B= Cr + 3.3Mo + 1.65W + Cu + 30H ...(2) (式中灌擇設定那些加起來不是零的元素來計算B值>。 根據本發明第二觀點之具有優良抗點蝕性之高硬度麻 本紙張尺度適用令國國家楼準(CNS ) A4規格(210X297公釐) 經濟部中央標準局員工消費合作社印製 A7 __B7 五、發明説明(6 ) 田散體不綉網,若以重量計的話,實質上包括超過0.1 5% 但少於0.40%的碩、不超過2.0%的矽、不超遇2.0%的 錳、不低於11.0%但少於15.0的鉻、1.0至3.0%的鉬或 以Mo + l/ 2W表示之鉬和鎢、0.02至0.15%的氮、0.1至 1.5%的錁、0.1至2%的銅、不超過總重0.25%之至少 選自包括钒、鈦、和鈮之族群之一、其餘均為鐵成分, 錁和銅包含於符合以下方程式(3)表示的閬像之範圍内 ,以下方程式(1)定義之A值不超過10,以下方程式(2) 定義之B值不小於20 :
A= - 40C + 6Si - 2Hn - 4Ni + Cr + 4Mo + 2W -2Cu - 30H + 11V + lOTi + 5Nb ...(1) (式中遘擇設定那些加起來不是零的元素來計算A值) B= Cr + 3.3Mo + 1 . 65W + Cu + 30H ...(2) (式中遘擇設定那些加起來不是零的元素來計算B值)。 N i / Cu >0.2 …(3)〇 根據本發明第二觀點之具有優良抗點蝕性之高硬度麻 田散體不锈銅,其較佳的組成若以重量計的話,實質上 包括超過0.15%但不多於0.40%的碩、不超過2.0%的 矽、不超過2.0%的錳、超過0.2%但少於1.0%的錁、 不低於11.0%但少於15.0的鉻、1.0至3.0%的鉬或以 Mo + l/2W表示之鉬和錫、不低於0.1%但低於1.0%的銅、 0.02至0.15%的氮、不超過缠重0.25%之至少選自包括 釩、鈦、和鈮之族群之一、其餘均為鐵,以下方程式(1) 定義之A值不超過10,以下方程式(2)定義之B值不小 -8 - 本紙張尺度適用中國國家標準(CNS ) A4規格(210 X 297公釐) ---------*, Ί-----„---訂·------I (請先閲讀背面之注意事項再填寫本頁) 經濟部中央標準局員工消費合作社印製 A7 B7 五、發明説明(r ) 於20 :
A= - 40C + 6Si - 2Mn - 4Hi + Cr + 4Ho + 2W -2Cu - 30H + 11V + lOTi + 5Nb ...(1) (式中選捧設定那些加起來不是零的元素來計算A值) B= Cr + 3.3Mo + 1.65W + Cu + 30N ...(2) (式中遘擇設定那些加起來不是零的元素來計算B值)。 根據本發明第二覼點之具有優良抗點蝕性之高硬度麻 田散體不綉銷,其更佳的組成若以重董計的話,實質上 包括0.20至0.35%的硪、不超過2.0%的矽、不超過2.0% 的錳、0.3至0.75%的錁、不低於11.0%但少於15.0的 鉻、1.0至3.0%的鉬或鎢以MO + 1/ 2W表示之鉬和鎢、不 低於0.1%但低於1.0%的銅、0.02至0.15%的氰、不超 遇總重0.25%之至少選自包括釩、鈦、和鈮之族群之一 、其餘均為鐵,以下方程式(1)定義之A值不超過10, 以下方程式(2)定義之B值不小於20:
A= - 40C + 6Si - 2Mn - 4Ηι + Cr + 4Mo + 2W -2Cu - 30N + 11V + lOTi + 5Hb ...(1) (式中遘擇設定那些加起來不是零的元素來計算A值) B= Cr + 3.3Mo + 1 .65W + Cu + 30N ...(2) (式中遘擇設定那些加起來不是零的元素來計算B值)。 除了上述組成,根據本發明第一或第二觀點之不銹網 和較佳組成之不锈鋼,進一步含有不超過總重0.1%之 至少選自包括珊、鎂、鈣和鋁之族群之一,且若有需要 ,為增加隳冷和回火後的硬度,其邇含有不超過5%的 本紙張尺度適用中國國家標準(CNS ) A4規格(210X 297公釐) * * * * i ^ 、裝-----^--訂------'v (讀先閱讀背面之注意事項再填寫本頁) 經濟部中央標準局員工消費合作社印製 A7 _ B7 五、發明説明(g ) 鈷。 本發明之不锈鋼,除了含有任何一種上述組成外,較 佳之聚冷和回火後的硬度不低於50HRC,且在3010中以 3. 5%鹽水除氣之點蝕霄位Ve,100 不低於150毫伏特(與 飽和甘汞電槿相比)。這些待點,可藉由上述任何一種 本發明之新穎組成物來達成。 另一方面,本發明之不锈鋼的特色也在其硬度會在一 次簡單退火連到夠低。一般,特別是冷成形(如冷拉伸、 冷滾輥、冷鍛造、滾絲和冷彎曲)進行時,退火後硬度 必須不超遇250維氏硬度(HV)。傳統相同的網材在退火 後硬度很難降低不超過300HV,較佳是不超過250HV,除 非進行數次退火步驟,以較複雜的熱處理來進行退火。 本發明之銷材,在700至890T之一次退火步驟後的硬度 不超遇300HV。較佳當錁的上限不超過1.0%,退火後硬 度將降低至不超過250HV。 太發明;>軎住奮旃形篚 本發明不綉鋼中之各種元素的功能將詳述如下。 硪使得驟冷後的麻田散體不锈銷結構中含有13%的鉻 。而且碩與會形成破化物的元素(carbide-forming elements)形成磺化物,而該固體溶液狀態的部分在麻田 散體介質中會有效地增加硬度。但若磺量超遇0.40%, 則在介質中形成太多的硪化鉻,而介質中的鉻含量會降 低抗蝕性。3 —方面,若硪含量不超過0.1 5%,則不僅 不會有足夠的硬度。也會因5-鐵酸鹽的形成而降低抗 本紙張尺度適用中國國家標準(CNS ) A4規格(210'〆297公釐) ---------\'、裝-----„--訂------k (請先閲讀背面之注意事項再填寫本頁) A7 B7 經濟部中央標準局員工消費合作社印聚 五、發明説明( 9 ) Ί ,丨 點 蝕 性 和 熱 加 工 性 〇 因 此 硪 含 量 設定在 大於 0 . 1 5 %但不 1 超 遇 0 . 40% 0 較 佳 之 硪 範 圍 在 0 . 20至 0 . 35¾ 〇 1 加 入 少 量 的 矽 和 錳 以 便 脱 氣 〇 但若加 入超 過 2 . 0%的 -S 請 1 種元素 先 1 矽 和 錳 » 也 不 會 進 - 步 改 善 脱 氣 的效果 〇因 此 每 閱 讀 1 之 範 圍 設 定 不 超 過 2 . 0% 〇 此外, 因為矽元素易産生鐵 背 面 | 之 酸 麵 9 錳 元 素 易 産 生 奥 氏 結 構 (a u s t e n i t e s t Γ U C t u r e ) 注 意 I 因 此 即 使 這 類 元 素 為 少 量 也 多 多 少少會 影馨 介 質 結構。 事 項 1 1 再 為 此 線 故 t 矽 和 鍤 較 佳 維 持 在 不 超過1 . 0%。 寫 本 i 錁 可 抑 制 δ -鐵酸鹽的形成, 改善抗點蝕性, 尤其後 頁 '—^ 1 I 來 因 銅 的 加 入 會 産 生 熱 加 工 性 的 降低, 故錁 在 避 免降低 一 1 1 熱 加 工 性 上 特 別 有 效 〇 因 此 > 視 加入的 銅量 來 決 定所需 1 加 入 的 錁 量 〇 1 訂 本 發 明 含 有 13%鉻的高硬度麻 田散體 不銹 銷 中 ,除了 1 銅 外 9 其 他 元 素 均 會 惡 化 熱 加 工 性,如 鉬和 氮 9 特別必 1 I 須 限 制 錁 / 銅 比 值 超 過 0 . 2 , 較佳是不少於0 .3 9 而且基 1 I 於 下 述 理 由 邇 要 限 制 錁 含 量 〇 若 錁含量 低於 0 . 196 ,不 1 1 能 得 到 充 分 的 效 果 〇 但 若 錁 超 過 1.5¾. 會降低麻田散 I 體 轉 換 點 9 而 在 m 冷 後 難 以 得 到 完美的 麻田 散 體 結構, 1 1 且 在 退 火 後 增 加 硬 度 » 因 此 使 冷 加工性 變差 〇 因 此設定 1 錁 含 董 在 0 . 1至1 .5% 〇 較 佳 之 錁 含量超 過0 . 2 96 , 但不 1 超 過 1 . 0% , 更佳的範圍在0 .3至 0 . 75% 〇 1 鉻 在 增 加 抗 蝕 性 上 來 説 非 常 重 要的, 待別 是 抗 點蝕性 1 因 為 其 會 形 成 惰 性 的 表 面 膜 〇 若絡的 含量 少 於 11.0¾ 1 I * 則 抗 蝕 性 不 足 〇 但 若 鉻 的 含 董 超過15 .096 9 那 麽會産 1 1 -1 1- Γ 1 本紙張尺度適用中國國家標準(CNS ) A4規格(210X 297公釐) A7 B7 經濟部中央標準局員工消費合作社印製 五、發明説明( ) *- 1 * I 生 δ -鐵酸鹽, 因此惡化抗點蝕性和熱加工性。 因此設定 1 鉻 含 量 不 少 於 11 .0% 9 但 低 於 15.0¾ 〇 較佳 之 鉻 含量 範 1 圔 為 1 3 .0 至 1 4 .0¾ 〇 請 1 先 1 本 發 明 不 锈 銷 中 钼 也 為 必 要 元 素 1 因 為其 會 使 惰性 表 閱 1 面 膜 安 定 • 因 而 增 加 抗 點 蝕 性 〇 當 鎢 和 鉬一 起 也 會有 效 背 | 之 增 加 抗 黏 蝕 性 • 但 若 單 獼 加 入 鎢 • 則 效 果不 佳 〇 較佳 當 注 意 | 加 入 鎢 時 * 部 分 m 的 量 以 相 當 量 的 m 來 取代 (1/2當量 鎢 事 項 1 1 再 / 相 當 於 1 當 量 m )〇 單獨加入鉬、 或加入鉬和鎢兩者(以 填 寫 本 k Mo + 1 /2W來表示) • 低 於 1 . 0%的含量, 則使得抗點蝕性 頁 1 1 惡 化 〇 但 若 鉬 或 m 和 鎢 兩 者 加 入 量 超 遇3 . 096 , 會産 1 1 生 δ -鐵酸鹽, 反而惡化了抗點蝕性和熱加工性。 因此 1 m 或 m 和 箱 兩 者 的 加 入 置 $ 設 定 在 1 . 0至3 .096 之間 0 1 訂 較 佳 範 画 為 1 . 5至2 .5¾ 〇 1 若 鉻 鉬 和 氮 的 含 量 為 少 量 的 話 9 銅 元素 在 增 加抗 點 1 I 蝕 性 上 是 非 常 有 效 的 〇 若 銅 加 入 量 低 於 0.1¾. 不能達 1 1 到 充 份 效 果 〇 但 若 銅 加 入 量 超 過 2 . 0% , 不僅惡化熱加 1 1 X 性 9 邇 使 驟 冷 後 硬 度 不 足 〇 因 此 銅 加 入* 設 定 在不 少 心- 1 於 〇. 1 %但低於1 .096 的 範 匯 » 更 佳 範 圍 在0 . 2至0 .896 〇 1 1 附 帶 一 提 的 是 • 若 銅 含 量 不 超 過 2 . 096 ,刖會有熱加 1 X 不 足 的 範 圍 出 現 〇 如 上 述 限 制 錁 的 理 由· 必 須 限制 銅 1 的 含 量 使 錁 和 銅 的 關 係 符 合 N i/C u> 0 .2 , 特 別 是不 小 1 於 0 . 3。 1 在 麻 田 散 體 介 質 中 之 固 am 歴 溶 液 狀 態 的 氮元 素 會 在驟 冷 1 I 後 增 加 硬 度 • 同 時 還 可 有 效 增 加 抗 點 蝕 性。 此 外 由於 氡 1 1 -12- Γ 1 本紙張尺度適用中國國家標準(CNS ) A4規格(210X 297公釐) A7 B7 經濟部中央標準局員工消費合作社印製 五、發明説明( ) 1- • 1 可 抑 制 δ -嫌酸鹽的形成, 且在抑制< 5 - 鐵 酸 鹽 的 形 成 的 1 同 時 • 氮 取 代 錁 足 以 省 去 使 用 部 分 昂 貴 的 鍊 合 金 元 素 以 1 産 生 便 宜 的 銷 材 〇 若 氮 小 於 0 . 02¾ • 不 能 逹 成 充 分 效 果 請 1 先 1 〇 但 若 m 含 董 超 過 0 . 15¾ 9 則 損 害 銷 材 鑄 塊 之 堅 固 性 P 閱 讀 1 並 使 製 造 性 不 良 〇 因 此 設 定 氮 含 量 在 0 . 02 至 0 . 15% 之 間 背、 面 I 之 〇 較 佳 氮 含 量 範 圓 在 0 . 05 至 0 . 15% 〇 注 意 I 釩 鈦 和 鈮 元 素 不 是 必 要 加 入 的 元 素 » 但 其 會 有 效 事 項 1 [ 再 形 成 第 —* 碩 化 物 » 並 使 預 -奥氏顆粒尺寸較小, 改善了 填 寫 本 i 硬 度 和 延 展 性 〇 因 此 加 入 钒 > 鈦 和 鈮 元 素 之 —* 二 或 頁 '---- 1 I 多 者 是 必 須 的 〇 若 加 入 超 遇 總 量 0 . 25% 之 一 Λ 二 或 多 者 1 1 之 釩 鈦 Λ 和 鈮 元 素 • 刖 會 形 成 粗 糙 之 第 一 m 化 物 » 而 1 使 得 冷 加 工 性 惡 化 〇 因 此 9 設 定 一 二 或 多 者 之 釩 鈦 1 訂 和 鈮 元 素 的 含 量 不 超 過 總 量 之 0 . 25% 〇 1 硼 m m 和 鋁 元 素 不 是 必 要 加 入 的 元 素 9 但 其 會 有 1 | 效 形 成 氧 化 物 和 硫 化 物 > 以 降 低 預 - 奧 氏 m 粒 邊 界 之 硫 1 i 氣 隔 離 * 改 善 熱 加 工 性 〇 故 硼 Λ 鎂 m 和 鋁 之 一 或 二 1 1 或 多 者 元 素 的 加 入 是 必 須 的 〇 若 硼 > m 鈣 和 鋁 之 一 或 I 二 或 多 者 元 素 的 加 入 量 超 過 總 量 0 . 10% t 則 缠 的 效 果 不 1 1 1 會 進 一 步 增 加 但 清 潔 度 反 而 會 降 低 故 惡 化 熱 和 冷 加 1 工 性 〇 因 此 較 佳 設 定 rtu 硼 m 、 鈣 和 鋁 之 一 或 二 或 多 者 元 1 素 的 加 入 量 不 超 過 m 量 0 . 1096 0 1 為 達 到 優 良 的 抗 點 蝕 性 » 上 述 合 金 元 素 除 了 要 符 合 各 1 別 成 分 的 範 圍 外 » 也 要 符 合 本 發 明 銷 材 之 特 定 方 程 式 〇 1 1 如 方 程 式 (1 >所表示之A 值, 是代表本發明鋼材之鉻當 1 1 -13- Γ 1 本紙張尺度適用中國國家標準(CNS ) A4規格(210X 297公釐) 經濟部中央標準局員工消費合作社印製 A7 __^_B7_ 五、發明説明(^ ) 量,且A值也是δ-鐵酸鹽易形成吝的重要指檫。A值 偽由係數乘以易形成鐵酸鹽之鉻、矽、鉬、鎢、釩、鈦 、和鈮元素之重量% (所謂係數是視這些元素的實驗效 果而各別決定的)減去係數乘以易形成奥氏體之硪、錳 、錁、銅和氮之重量%的值(所謂傜數是視這些元素的 實驗效果而各別決定的)。實驗結果得知,本發明網材 之A值若超過10,則會形成δ-嫌酸鹽,並大大降低抗 黏蝕性,並在》冷後進一步降低熱加工性和硬度。因此 ,設定方程式(1)所表示之Α值不超過10。 由方程式(2)所表示之B值,也是影镳本發明網材之 抗點蝕性的重要指標,且該值為傺數乘以鉻、鉬、銪、 銅和氮之重量%的和(所諝傜數是各別元素對改善抗點 蝕性的直接貢獻,且該傷數視這些元素實驗效果而各別 決定的)。若本發明鋼材之B值小於20 ,則不會得到優良 之抗點蝕性。因此,設定方程式(2)所表示之B值不小 於20。 除了上述元素外,本發明銷材可加入不超遇5重量% 的鈷。 在介質之固體溶液狀態中的鈷,會在驟冷和回火後增 加硬度。但是,因為鈷是昂貴元素,所以不需大置加入。 由於磷和硫為雜質元素,若逭些元素以混合含量(這 在一般熔融過程是不可避免的)出現,則不會發生問頭。 故對磷和硫沒有特殊限制。但以抗點蝕性的觀點來看, 這些元素的含量當然是越低越好。 本紙張尺度適用中國國家標準(CNS ) A4規格(210X297公釐) ---------~參-----^—1T------4 (請先閱讀背面之注意事項再填寫本頁) A7 A7 經濟部中央標準局員工消費合作社印裝 B7 ------ "" 〜^ 五、發明説明(β ) 本發明網材之限铜•胃& 以適笛方法進G 88 # ίπ @ A,# 8 8月8 ® # tb sUs 3〇4冷成形材料和SUS410»冷和回火材料更高的硬度。 特別是當鋼材用於釘子、螺絲、削邊刀、彈簧等用途時 ,網材硬度須不小於50HRC,以使道些産物完全發展本 身的能力。本發明期材在不低於約100〇t〇ffi度’经_冷 & I嫌度不小於50HRC,然後在不离於約3001C進行傕粗 回火,或在約4〇〇至5001進行高租回火。順帶一提的是 ,在此必須注意螺絲、釘子、媒釘等之抗延遲破裂性, 藉由適當遘擇回火溢度也可能將低硬度。 另外,以缠當方法進行鼸冷和回火•本發明網材在維 持离硬度之餘,缠有優良抗黏蝕性。已知點蝕S位意指 抗點蝕的程度。為了鋼材甚至適用於開放空氣和可能_ 露在水鼸頭水、雨水、冷凝露水、或其類似水中之元件 、零件、工具等,有優良的抗點蝕性,銷材在30t:中以 3.5%馥水除氣之點蝕電位V c.10〇不低於150毫伏特(與 飽和甘汞霣極相比)。使本發明網材在不低於約1000^ «冷,並在不超遇約300¾下進行冷-溫度回火,則本發 明銅材之Vc*100不小於150毫伏特(與飽和甘汞電極相比) 。在此「黏蝕j常在銷材被觀察到,意指在一雇形成腐 蝕的小點上,會導致網材表面的分散點。點蝕的發生不 僅破壤外觀,邇會從腐蝕黏開始破裂。 根據JIS G0577之霣化學腐蝕評估和_試來拥量點蝕 霉位。換句話説,當霣流密度變成100撤安培/公分2 -15- 本紙張尺度適用中國國家標準(CNS ) A4規格(210X297公釐) ------------- .· AI. (請先閱讀背面之注意事¾再填'寫本頁j 訂* ' 經濟部中央標準局員工消費合作社印製 A7 B7 五、發明説明(w) 時.決定當時電位為點蝕罨位v e, 1()()。 當視用途來適當選擇本發明網材之製法,待別是熱處 理的條件時,上述特擞值可以提供一種適當的組合。例 如顯示,在冷成形後施予熱處理之釘子、螺絲、削邊刀 等,可能提供一種在退火後不超過250HV之低硬度的鏑 材,並在驟冷和回火後有外低於50HRC之高硬度,且唯恐 發生點蝕,鏑材具有不小於150毫伏待之高點蝕電位(輿 飽和甘汞霉極相比。 未經冷成形之機械形成的螺絲、螺釘、削邊刀等,在 隳冷和回火後,可藉由低溫回火,使之兼具高硬度和高 點蝕電位。此外,用於如模子工具之銷材,在骤冷和回 火後之高硬度視應用而定。當用於工具之鋼材,曝露在 不低於約300"C之高溫時,則在驟冷和回火後必須有高 硬度。這些例子裡,驟冷和回火後之高硬度可藉由例如 約400至500t:之高溫回火來達成。 置施例 本發明結合下列實施例來做説明。鋼材的化學組成列 於表1和表2 ,其經由真空熔融而得,每種鋼材取10公 斤鑄塊。表中,列有限制在本發明範圍内之1到38號鋼 材的組成、A值、B值、和錁/銅tfc ,另外比較用網材 之4 0到5 2號鋼材的組成、A值、B值、和錁/銅比之則 不在本發明範國内。 每種薄塊加熱至8601C然後在退火爐中一侮冷 (annealing),藉由此熱加工形成30毫米方條。接箸將方 -16- 本紙張尺度逋用中國國家標準(CNS ) Α4規格(210Χ297公釐) n. II. __ - - - - ...... --I 、*1 HI -----LI----- 丁 , 0¾ 、τ (請先閱讀背面之注意事項再填寫本頁) A7 B7 五、發明説明(d ) 條加熱至105〇υ,維持該溫度30分鐘,再藉由冷卻油施 予驟冷(quenching)。然後在 180¾ 回火(tempering ) 1小時· 由雒氏硬度測試機澜量退火後的硬度,然後再用洛氏 硬度測試機測量驟冷和回火後的硬度。另外根據JIS G 0 5 7 7,在3 0 1C中以3 . 5 %鹽水除氣測量抗點蝕性,並且 當電流密度為1〇〇撤安培/公分2時,測量電位ve,1Q() 為點蝕《位。若經熱加工後鋼材表面或角落有龜裂則 記作X,若鋼材沒有龜裂則記作〇,並以此作為熱可加 工性的評估結果。評估結果列於表3。 m- I^i ^^^1 n i m n. · I ^^1— I nn 0¾-a (請先閱讀背面之注意事項再填寫本頁) 經濟部中央標準局員工消費合作社印裝 本紙張尺度適用中國國家標準(CNS ) A4規格(210X297公釐) 五、發明説明(d )
A B 經濟部中央標準局員工消費合作社印製
•Η Η I 1 1 1 1 1 1 1 1 1 1 1 1 1 > 1 1 1 1 1 1 1 1 1 1 1 1 1 1 0.077 0.101 0.092 0.062 0.098 0.045 0.044 0.091 0.083 | 0.092 0.075 0.081 0.090 0.077 S CD y〇 rn σ> 〇» σ» 寸 in 5 σ> V£) CN σ> <N m 卜 in CJ Ο o o O o o o o 〇 o O o o o Ο X t—4 00 m CN rH o\ CO cn cn Ch ro 00 00 r—1 CN ΟΛ 00 _ (N rH CN 04 rH »—f iH iH <N CM »-1 CN CN r—1 CN fN 細 s 1 1 » 1 1 〇 • o 1 1 1 in o 1 1 1 1 u ο VO KO UD CN CD r〇 cr» in cr» VO m 00 in 卜 in KO CN m -α m m ro m rn m 咕 m CN m m m m m ••Η cr» 甘 GO V£> 00 in CN cn 呀 00 00 CN in in CN U5 VO ro \£> o o 〇 o o o o o o 〇 o o o o Β ro in <N s CN r〇 〇\ 00 CN cn in CN 却 s; in in tn iN in m 完 o 〇 O O o 〇 o o o o o o o W m 寸 <N CN in 04 cn 寸 <N \D 二 〇> OJ cn ΓΟ r〇 ro 呀 m o o o o 〇 o rH o 〇 o o o O o υ 寸 rf CM \D CN cr» CN 呀 m n m σ> 卜 m <N CN CN ro CN o o 〇 o o o o o 〇 o 〇 o 〇 〇 m m m rH <N r〇 寸 tn KD 卜 CD o r—4 (N 一 *裝 訂" (請先閱讀背面之注意事項再填寫本頁) 本紙張尺度適用中國國家標準(CNS〉A4規格(210X 297公釐) -18- 五、發明説明() A7 B7 經濟部中央標準局員工消費合作社印褽 (》¥ I 槲 附記 本發明 之銷材 錁/銅1 卜 rH rH 〇 rH 00 o o o rH o 00 fH σ\ o CT\ 〇 o cr> o in 寸 〇 σ\ (N o CO 04 〇 eo «-Η η CN <N (N \o 寸 cs in 00 甘 CN CN CN m CN CO in s m CN VO (N CN CN (N VO 却 OJ ro CN VD m ro CN VO m (N ro m CN CN 班 <c VO GO 00 in KO 卜 s in ID 00 CN 〇> \o 00 m in m VD σ\ 00 UD cn CO CN 卜 o 卜 GO VD 叶 ro 00 04 in cn Φ Pm 其餘量 s Ο U 1 1 1 1 1 1 1 \ 1 1 1 1 1 1 rH < 1 1 t 1 I 1 1 1 I 1 1 1 1 ttJ α 1 1 1 1 1 1 1 1 1 1 1 1 1 1 茗 1 1 1 1 1 1 1 1 1 1 1 1 1 I CQ 1 1 » 1 1 1 1 1 1 1 1 1 1 1 JQ 2ϊ 1 1 1 1 1 1 1 1 1 1 1 嘗 1 1 0 0 — 1/. 1 訂k. (請先閱讀背面之注意事項再填寫本頁) 本紙張尺度適用中國國家標準(CNS ) A4規格(210X297公釐) -19-
A
7 B 五、發明説明(d ) 經濟部中央標準局員工消費合作社印製 (驪迪二 0 1 1 1 1 1 1 卜 o o 1 1 η ο ο CN Ο Ο CN 〇 o 1 1 1 1 1 1 1 1 1 0.09 1 1 CN rH ο 1 m ο ο 卜 o o 1 1 1 1 1 078 091 069 068 073 083 079 071 085 086 093 103 095 093 084 065 聰 〇 Ο o o o o o Ο Ο Ο Ο o o o o o 寸 VO 卜 n ro vr> CN CN in 00 ιπ CS ιη νο ιπ 卜 m VO 寸 • in in in VD KO 1 •H rH f-H o r-H o ο ο ο ο ο o o o o o ΓΟ ΓΜ 00 GO cr» Γ0 咕 P; (Ν m cn KD ro ro CN 兮 in CN CN f-H <N (N <N CN rH CN CN CN CM r—f CN <N 1 1 1 1 1 1 1 1 1 1 1 〇 〇 1 KD 00 • o 1 1 νο 00 in (N OJ 00 in 才 σ\ νο ιο κο CM 〇\ in cn σ\ σ> 卜 m m m m m m Γ〇 rn ΓΟ m ro cn cn rt* CN m σ\ in in CN m in in σ» VO m κο <N VO 兮 in ro in VO ο rH o rH o ο ο ο ο o o 〇 o o o 叶 (N rr 呀 in 〇> CO in CN 00 ΓΟ νο (Ν 叶 CN VO V£> rH CT» <N ro K〇 ο o o 〇 o o *Η ο Ο Ο o o 〇 o o o σ» Γ〇 CN m 寸 CN m ΟΛ r〇 〇> m (Ν ID cn Γ〇 寸 ιη VD Γ〇 00 in m m OJ in m VO in cn 寸 ο o o o 〇 o Ο ο ο Ο o o o o o o 卜 CN 00 <N in <N 寸 CM VD <N 00 (N \ο OJ 寸 CN 二 VO CN o cn 00 r〇 呀 CM KO CN in CN ΓΝ3 m ο o o 〇 〇 o Ο ο ο Ο o o 〇 〇 〇 o ιη KO 卜 GO <Ν CN m ΓΜ 寸 CM in CM vo CN GO CM CT» CN -20- --------\ 裝-- (請先閲讀背面之注意事項再填寫本頁) 本紙張尺度適用中國國家標準(CNS ) A4规格(210X297公釐) 五、發明説明(β A7 B7 經濟部中央標隼局員工消費合作社印製 (篛逝)I 塒 m 〇 KD 〇 in o 00 <N in KD rH rH in tH σ\ <N rH ΟΛ o ΓΝ 00 o cn 寸 o in rH CD 〇\ o o tH 卜 σ、 ο GO CN 守 CN in CN σ» CN <N 5 CN CN ro Ch ro CN ro fN 卜 m CN 卜 r〇 CM r〇 ro CN <Tk ro CN CN 寸 <N in \o 叶 CN y〇 VO ro CN CN CD CN CN 00 寸 m (Ν 卜 f—1 cr» rH in 呀 00 m <N ro 卜 cr» ro \o 卜 卜 00 cn 卜 KD a\ in (N <N ro <N <Tk S 卜 ro CN VD CN 呀 ID _ 遨 = 1 1 1 1 1 音 1 1 1 1 1 1 1 1 1 1 音 1 1 1 瞧 1 1 1 1 1 1 1 1 1 1 ro 〇 〇 1 1 » 1 1 1 1 1 1 1 1 1 1 1 ΟΛ tH 〇 o o 1 1 1 1 1 1 1 1 1 1 1 1 1 1 in <N 〇 o • o 1 1 1 1 1 l 1 1 1 1 » 1 l 香 CN r-4 〇 〇 〇 1 1 1 1 1 1 1 1 1 1 in o • o VO o o in o • o 1 寸 ο • ο 1 1 審 1 L.· .裝 訂 L (請先閲讀背面之注意事項再填寫本頁) 本紙張尺度適用中國國家標準(CNS ) Α4規格(210X297公釐) -21
A B 五、發明説明(〆) 經濟部中央標準局員工消費合作社印製 « m 链 m 1 1 1 1 1 1 1 KD o o 1 1 1 1 1 I > 1 1 1 1 1 1 1 1 1 1 1 1 1 0.087 0.114 0.099 0.089 0.071 0.063 0.089 0.082 0.023 .0.032 0.042 0.036 0.063 0.013 :3 U ch in ο cn o m in o S o KO in o o o 00 VO o VO o ro o 寸 Ο Ο Γ〇 CN Ο m 作 ο CT> rt* Ο 0 00 σ> r—1 CN CN r-i 00 04 iH CN cs Οί ro <N σ\ CN (N iH VO Γ〇 t-H »—( (Ν σ» 00 ο rn m κο CN • »-4 萁 1 1 審 1 1 t 1 1 1 1 1 I 1 1 U U \ο CN Γ〇 2 <N \£> m vn rn 00 in m fH CN CD 00 m s r〇 iH ro «X) α» rn m κο ιπ CN 00 in η •Η »Η ID • r〇 fH •H in m ο O in o 00 to o <N m o CN VO o V£) in o 00 in o CN CN 〇 <Ν ο ο Τ—1 ο Ο 1 <N IT) • o σ> vo o 卜 • ο o *x> in o 00 o o VO in o CN 呀 o Οί νο ο ιπ ο η ιη ο Ο Οί 甘 Ο •H W in • o m 吻 o 00 in ο vo in O CN rn O o in in o o in rn O CN ιη ο νο cn ο σ» κο Ο ν〇 ιη ο m ο U σ\ CN « o CN 04 〇 vo CN 〇 in Cvl o rn o 00 CN 〇 o in CM 〇 O ιΗ Ο Γ〇 (Ν ο ο α» rg Ο 00 r〇 Ο 鋼材 编號 CN r〇 m 叶 rn to rn VO rn 5 GO ro 5 τΗ (Ν rr Γ〇 ιη -- -----I--—1/ ^ 11 (請先閱讀背面之注意事項再填寫本頁) 訂'·
Ik 本紙張尺度適用中國國家標準(CNS ) A4規格(210X297公釐) -22- 五、發明説明(Η ) A7 B7 經濟部中央標準局員工消費合作社印製 附記 1_ ! 本發明 之銷材 比較 網材 錁/銅 η σ\ ο tn •H • o o 卜 ο rn O 〇> 00 o CN 00 〇 in 〇 Ch KO 一 o m O f—1 σ> 〇 CM 〇 〇 ο Η 8 CCt 22.99 卜 in in CN 00 σ\ m rj \o CO m <N σι 00 Γ〇 cs CD rg in CN in CN ro <N σ\ 卜 m 呀 Ch fH CO o CM σ\ CN ID ΓΊ Γ〇 卜 (Ν κο rH 00 rH 班 <c r—1 VO in 卜 VD VO m σ\ 卜 〇 f-H 00 rt* 〇 in KD yx> iH 〇 a\ o X£> CO CN 〇 rH 1 v〇 卜 in fH 卜 ID ro 寸 〇 卜 寸 卜 m rH Ο 00 rr (D U4 其餘量 r Ο U 1 1 1 1 1 rn 1—1 • <N 〇 (N <N rH 1 1 1 1 1 1 rH < CM 〇 o i-H 〇 o <N o o rH o o CN o o 1 1 1 1 1 1 1 1 1 (0 u 1 0.0013 0.0007 1 1 1 1 1 1 1 1 1 1 1 § 1 0.0011 0.0014 0.0012 1 1 0.0023 1 1 1 1 1 1 1 CQ 0.0031 1 0.0011 1 0.0010 1 1 1 1 1 1 1 1 1 XI S3 1 1 1 1 卜 〇 〇 1 1 1 1 1 1 1 1 I. n I I! —1/, \ I I I I I I、?τ (請先閱讀背面之注意事項再填寫本頁) 本紙張尺度適用中國國家標準(CNS ) A4規格(210X297公釐) B7 經濟部中央標準局員工消費合作杜印製 五、發明説明(β ) 1 1 1 1 I I I 1 1 1 1 1 I I \ CN m KO 卜 寸 σ\ CN m ?Η VO in κο 00 ιη 叶 o o Ο ο ο Ο m • • • • 〇 o o Ο ο ο Ο (N tN CD ιη 〇Λ 00 1 I IO κο 00 卜 ο tH o <Ν <Ν Ο ο m o r〇 m cn rn 00 <N <N rH OJ τΗ τΗ CN 1 1 1 1 1 1 1 CN CN VO ΟΛ 00 K〇 却 00 5; ιη 00 OJ (Ν m rH rn m fN Γ〇 cn ΓΟ CN VO rn rn 寸 ΓΟ σ» 00 ιη Oi o O ο ο *Η rH cn in νο ιη CN in 吻 VD σ> (Ν in 卜 o o o ο ο ο Ο m 叶 VO rn m ro 00 VO σ\ σ\ o o CN ο ο ο ο m r- r-4 rH <N KD CN 04 m σ» (Ν to CN m 〇 o o ο σ Ο Ο VO 卜 00 σ» ο r-4 CN m 寸 rr ιη ιη (請先閱讀背面之注意事項再填寫本頁) 本紙張尺度適用中國國家標準(CNS ) A4規格(210X297公釐) -24- 五、發明説明(4) A7 B7 經濟部中央標準局員工消費合作社印製 (»¥3 槲 8 ιΗ 〇 VO 00 o KD rH o ro r〇 • o 卜 rn • CM in 卜 • σ\ r—1 00 CN m CM CN in CN in σ> in in <N 00 in <NJ o r>J m o K〇 ΟΛ 〇y in r〇 *H o K£> CN 00 m κ 1 • 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 麵 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 ,1 I I 訂 I I I ;^ (請先閲讀背面之注意事項再填寫本頁) 本紙張尺度適用中國國家標準(CNS ) A4規格(210X 297公釐) 五、發明説明(艸)
7 7 A B 經濟部中央標準局員工消費合作社印装 表3 合金 编號 驟冷和回火 後的硬度 (HRC) 點蝕霣位 Vc4〇〇毫伏 待(與飽和甘 汞霉極相比) 退火後 的硬度 (HV) 熱可 加工性 附記 1 55.2 237.3 223 〇 本發明 銅材 2 55.0 240.6 221 〇 Μ 3 54.9 238.2 219 〇 ” 4 54.1 235.6 232 〇 11 5 54.8 233.4 222 〇 ” 6 56.3 203-1 213 〇 " 7 55.8 198.5 215 〇 ” 8 51.9 213.6 203 〇 (1 9 51.2 198.3 225 〇 " 10 55.6 249.2 222 〇 " 11 53.8 224.7 227 〇 ” 12 54.2 228.8 247 〇 Μ 13 54.6 225.2 211 〇 " 14 55.0 181.4 203 〇 " 15 50.7 223.1 236 〇 ” 16 50.5 233.8 278 〇 " 17 50.9 210.2 244 〇 If 18 54.8 203.7 286 〇 " 19 55.1 225.6 292 〇 ” 20 55.4 226.8 231 〇 ” 21 55.1 231.7 241 〇 ” 22 54.8 218.4 242 〇 II 23 55.0 226.9 245 〇 ” 24 54.9 227.6 244 〇 " 25 55.3 241.3 239 〇 " 本紙張尺度逍用中國國家標準(CNS ) A4規格(210X297公釐) ~26 I- 1111 ~、裝 111111 訂· I (請先閲讀背面之注意事項再填寫本頁) 393518 B7 經濟部中央標準局員工消費合作社印製 五、發明説明(<) 表 3(接鑛) 合金 骤冷和回火 點蝕轚位 退火後 熱可 附記 编號 後的硬度 Vc· 1〇〇毫伏 的硬度 加工性 (HRC) 特(輿飽和甘 汞《極相比) (HV) 26 56.1 246.8 236 〇 本發明 銅材 27 54.3 256.1 226 〇 II 28 54.9 226.0 232 〇 " 29 55.1 203.3 224 〇 It 30 55.5 235.5 229 〇 If 31 55.4 263.7 228 〇 Μ 32 55.1 246.3 241 〇 " 33 54.7 251.4 235 〇 ft 34 54.3 239.3 227 〇 " 35 55.2 229.4 229 〇 Η 36 55.7 220.2 247 〇 ” 37 55.6 244.1 232 〇 38 55.2 251.8 231 〇 ” 40 56.2 99.1 213 〇 比較 鋼材 41 42.0 136.4 204 〇 II 42 48.1 92.5 211 〇 •言 43 47.6 54.9 206 X ” 44 50.3 69.8 221 〇 II 45 56.4 62.4 216 〇 ” 46 50.3 232.2 434 〇 " 47 47.8 121.3 203 X " 48 50.3 36.2 201 〇 1» ' 49 49.8 163.4 232 X " 50 49.4 188.3 282 X Μ 51 54.6 179.8 405 〇 " 52 53.2 177.6 378 〇 (請先閲讀背面之注意事項再填寫本頁) 本紙張尺度適用中國國家標準(CNS ) A4規格(21 OX 297公釐) 一27 經濟部中央標準局員工消費合作社印製 39S518 五、發明説明(>〇 如表3得知,本發明之1到38號網材,在驟冷和回火 後有不低於50HRC的高硬度,而且具有不低於150毫伏特 之高黏蝕轚位V c· 1〇〇 (輿飽和甘汞霣極相tb)。此意味 本發明銷材兼具抗點蝕性和高硬度。亦知,除了编號18 和19網材外,本發明之其他1到38號鏑材,在退火後硬 度不超過250HV,因此在冷卻加工中足以成形。雖然篇 號18和19銷材内包含的鎳近於允許範困的上限,且在退 火後仍有高硬度,但退火後的硬度不超過300HV,可以 進行輕度的冷卻加工。據此,编號18和19銷材無須進行 高度冷卻之冷卻加工,比起其他编號的銷材在驟冷和回火 後,也有令人滿意的優良抗點蝕性和高強度。 另外,本發明之1到38號銷材有優良的熱加工性,因 此能夠經由熱加工製造(如锻造和熱棍)令人滿意的材料。 B —方面,编號40至52之比較例鋼材.其中組成、A 值、B值和鍊/銅比之一或多値數值不在本發明範臞内 ,則可得知其一或多値性質(如驟冷和回火後硬度、抗 點蝕性、退火後硬度和熱加工性)不如本發明銷材。 特別是编號40至45、47和48號比較例銷材,其中A值 和B值之一或二是在限制範困外·則黏蝕®位低,表示 抗黏蝕性不佳〇 S外编43、47和49之錁/銅比低,而高 銅含量之编號49和50,熱加工性不良,材料可製造性不 佳。此外,高鎳含量之编號46、51和52之比較例銅材, 在退火後之硬度高於300HV,不能進行冷加工,故難以 進行材料、零件、元件等的加工。 -28' 本紙張尺度適用中國國家標準(CNS ) A4規格(210X297公釐) ^;·、裝-----K I 訂-------k (請先閲讀背面之注意事項再填寫本頁) S93^18_^ 五、發明説明(>7 ) 1里_應甩 如上所述,本發明之麻田散體不锈網具有優良熱加工 性、退火後低硬度、在驟冷和回火後有優良抗點蝕性和 高硬度。本發明也可提供一種兼具上述四種優點之適當 的組成。因此,應用本發明銷材於零件、元件、工具 等時,本發明可在開放空氣中使用,也可曝露於水龍頭 、雨水、冷凝露水、或其類似水中.其是一種成本低又 大大改善耐久性和使用赛命的材料。因此從工莱應用觀 點來看,本發明具有優異的效果。 (請先閱讀背面之注意事項再填寫本頁) 經濟部中央標準局員工消費合作社印製 -29- 本紙張尺度適用中國國家標準(CNS ) A4規格(210 X 297公釐)

Claims (1)

  1. A8 B8
    第85100295號「具良好抗點蝕性之高硬度麻田散體之不銹鋼」 専利案
    A申請専利範圍: 1. 一種具良好抗點蝕性之高硬度麻田散體不銹鋼,該網 材以重董計,實質上包括超過0·15%但不多於0.40% 的碳,不超過2.0%的矽、不超過2.0%錳、不低於11.0 %但少於15.0%的鉻、1.0至3.0%的鉬或以MO+1/2W 表示之鉬和鎢,〇· 02至0. 15%的氮,0.1至1.5%的鎳 、0.1至2.0%的銅、其餘均爲嫌,鎳和銅包含於符合 以下方程式(3)表示的關係之範園中,而以下方程式(1) 定義之Α値不超過10,和以下方程式(2)定義之Β値不 小於20 : A= - 40C + 6Si - 2Hn - 4Ni + Cr + 4Uo + 2W -2Cu - 30N + 11V + lOTi + 5Nb ...(1) (式中選擇設定那些加起來不是零的元素來計算A値) B= Cr + 3.3Mo + 1.65W + Cu + 30N ...(2) (式中選擇設定那些加起來不是零的元素來計算B値) Ni / Cu >0.2 …(3 )。 2. 如申請専利範困第1項之具良好抗點蝕性之高硬度麻 田散體不銹鋼,其中組成物中以重量計,鎳爲比0.2% 多但不大於1.0%,銅爲不低於0. 1 %但少於1 . 0%。 3 .如申請專利範圍第1項之具良好抗點蝕性之高硬度麻 (請先聞讀背面之注意事項再填寫本頁) -訂 經濟部智慧財產局員工消費合作社印製 本紙張尺度逋用中國國家梂準(CNS ) A4規格(210X297公釐) A8 B8
    第85100295號「具良好抗點蝕性之高硬度麻田散體之不銹鋼」 専利案
    A申請専利範圍: 1. 一種具良好抗點蝕性之高硬度麻田散體不銹鋼,該網 材以重董計,實質上包括超過0·15%但不多於0.40% 的碳,不超過2.0%的矽、不超過2.0%錳、不低於11.0 %但少於15.0%的鉻、1.0至3.0%的鉬或以MO+1/2W 表示之鉬和鎢,〇· 02至0. 15%的氮,0.1至1.5%的鎳 、0.1至2.0%的銅、其餘均爲嫌,鎳和銅包含於符合 以下方程式(3)表示的關係之範園中,而以下方程式(1) 定義之Α値不超過10,和以下方程式(2)定義之Β値不 小於20 : A= - 40C + 6Si - 2Hn - 4Ni + Cr + 4Uo + 2W -2Cu - 30N + 11V + lOTi + 5Nb ...(1) (式中選擇設定那些加起來不是零的元素來計算A値) B= Cr + 3.3Mo + 1.65W + Cu + 30N ...(2) (式中選擇設定那些加起來不是零的元素來計算B値) Ni / Cu >0.2 …(3 )。 2. 如申請専利範困第1項之具良好抗點蝕性之高硬度麻 田散體不銹鋼,其中組成物中以重量計,鎳爲比0.2% 多但不大於1.0%,銅爲不低於0. 1 %但少於1 . 0%。 3 .如申請專利範圍第1項之具良好抗點蝕性之高硬度麻 (請先聞讀背面之注意事項再填寫本頁) -訂 經濟部智慧財產局員工消費合作社印製 本紙張尺度逋用中國國家梂準(CNS ) A4規格(210X297公釐) A8 B8 C8 D8__ 六、申請專利範園 田散體不銹鋼,其中組成物中以重量計,碳爲0.20至 0.35%、鎳爲0.3至0.751銅爲不低於0.1 %但少於1·〇% 〇 4. 如申請専利範画第1項之具良好抗點蝕性之高硬度麻 田散體不銹鋼,其中組成物中以重量計,不超過總重 0.25%之至少選自包括釩、鈦、和鈮之族群之一。 5. 如申請専利範圔第1項之具良好抗點蝕性之高硬度麻 田散體不銹鋼,其中組成物中以重量計,鎳爲超過〇. 2ft 但不多於1 . 0%,銅爲不低於0 . 1 %但低於1 . p%,不超過 總重0.2 5%之至少選自包括釩、鈦,和鈮之族群之一 〇 6. 如申請專利範圍第1項之具良好抗黏蝕性之高硬度麻 田散體不銹鋼,其中組成物中以重量計*碳爲0,20至 0.3 516,氮爲0.02至0.1 5%,不超過總重0.2 5*之至少 選自包括釩、鈦,和鈮之族群之一。 7. 如申請專利範園第1至6項中任一項之具良好抗點蝕 性之高硬度麻田散體不銹鋼,其中不銹鋼另外含有不 超過總重0.1 %之至少選自包括硼、鎂、鈣和鋁之族群 之一。 8_如申請専利範圍第1至6項中任一項之具良好抗點蝕 性之高硬度麻田散賸不銹網,其中在驟冷和回火後的 硬度不低於50HRC。 9.如申請專利範圍第1至6項中任一項之具良好抗點蝕 本紙張尺度逋用中國國家橾芈(CNS ) Λ4規格(210X297公釐) (請先閱讀背面之注意事項再填寫本頁) -丨訂 經濟部智慧財產局員工消費合作社印製 A8 B8 C8 D8 393518 六、申請專利範圍 性之高硬度麻田散賸不銹網,其中在3〇 t中以35% 鹽水除氣之點触電位Vc,1()()不低於150毫伏特(與飽和 甘汞電極相比)。 10.如申請専利範園第1至6項中任一項之具良好抗黏蝕 性之高硬度麻田散想不誘網,其中在至89〇艺之 一次退火步驟後的硬度不超過2 50維氏硬度<HV)。 (請先閲讀背面之注意事項再填寫本頁) 經濟部智慧財產局員工消費合作社印製 本紙張尺度適用中國國家榇準(CNS ) A4说格(210X297公釐)
TW085100295A 1995-01-13 1996-01-11 High hardness martensitic stainless steel with good pitting corrosion resistance TW393518B (en)