RU2005122903A - Способ формирования функциональных покрытий - Google Patents

Способ формирования функциональных покрытий Download PDF

Info

Publication number
RU2005122903A
RU2005122903A RU2005122903/12A RU2005122903A RU2005122903A RU 2005122903 A RU2005122903 A RU 2005122903A RU 2005122903/12 A RU2005122903/12 A RU 2005122903/12A RU 2005122903 A RU2005122903 A RU 2005122903A RU 2005122903 A RU2005122903 A RU 2005122903A
Authority
RU
Russia
Prior art keywords
group
acrylate
acid
properties
controlling
Prior art date
Application number
RU2005122903/12A
Other languages
English (en)
Inventor
Мартин КУНЦ (DE)
Мартин КУНЦ
Михаэль БАУЕР (DE)
Михаэль БАУЕР
Андреас БАРАНИАЙ (DE)
Андреас БАРАНИАЙ
Original Assignee
Циба Спешиалти Кемикэлз Холдинг Инк. (Ch)
Циба Спешиалти Кемикэлз Холдинг Инк.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from PCT/EP2003/000780 external-priority patent/WO2003064061A1/en
Application filed by Циба Спешиалти Кемикэлз Холдинг Инк. (Ch), Циба Спешиалти Кемикэлз Холдинг Инк. filed Critical Циба Спешиалти Кемикэлз Холдинг Инк. (Ch)
Publication of RU2005122903A publication Critical patent/RU2005122903A/ru

Links

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D3/00—Pretreatment of surfaces to which liquids or other fluent materials are to be applied; After-treatment of applied coatings, e.g. intermediate treating of an applied coating preparatory to subsequent applications of liquids or other fluent materials
    • B05D3/02—Pretreatment of surfaces to which liquids or other fluent materials are to be applied; After-treatment of applied coatings, e.g. intermediate treating of an applied coating preparatory to subsequent applications of liquids or other fluent materials by baking
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D7/00—Processes, other than flocking, specially adapted for applying liquids or other fluent materials to particular surfaces or for applying particular liquids or other fluent materials
    • B05D7/02—Processes, other than flocking, specially adapted for applying liquids or other fluent materials to particular surfaces or for applying particular liquids or other fluent materials to macromolecular substances, e.g. rubber
    • B05D7/04—Processes, other than flocking, specially adapted for applying liquids or other fluent materials to particular surfaces or for applying particular liquids or other fluent materials to macromolecular substances, e.g. rubber to surfaces of films or sheets
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D1/00—Processes for applying liquids or other fluent materials
    • B05D1/40—Distributing applied liquids or other fluent materials by members moving relatively to surface
    • B05D1/42—Distributing applied liquids or other fluent materials by members moving relatively to surface by non-rotary members
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D3/00—Pretreatment of surfaces to which liquids or other fluent materials are to be applied; After-treatment of applied coatings, e.g. intermediate treating of an applied coating preparatory to subsequent applications of liquids or other fluent materials
    • B05D3/02—Pretreatment of surfaces to which liquids or other fluent materials are to be applied; After-treatment of applied coatings, e.g. intermediate treating of an applied coating preparatory to subsequent applications of liquids or other fluent materials by baking
    • B05D3/0254—After-treatment
    • B05D3/029—After-treatment with microwaves
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D3/00—Pretreatment of surfaces to which liquids or other fluent materials are to be applied; After-treatment of applied coatings, e.g. intermediate treating of an applied coating preparatory to subsequent applications of liquids or other fluent materials
    • B05D3/06—Pretreatment of surfaces to which liquids or other fluent materials are to be applied; After-treatment of applied coatings, e.g. intermediate treating of an applied coating preparatory to subsequent applications of liquids or other fluent materials by exposure to radiation
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D3/00—Pretreatment of surfaces to which liquids or other fluent materials are to be applied; After-treatment of applied coatings, e.g. intermediate treating of an applied coating preparatory to subsequent applications of liquids or other fluent materials
    • B05D3/14—Pretreatment of surfaces to which liquids or other fluent materials are to be applied; After-treatment of applied coatings, e.g. intermediate treating of an applied coating preparatory to subsequent applications of liquids or other fluent materials by electrical means
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D3/00—Pretreatment of surfaces to which liquids or other fluent materials are to be applied; After-treatment of applied coatings, e.g. intermediate treating of an applied coating preparatory to subsequent applications of liquids or other fluent materials
    • B05D3/14—Pretreatment of surfaces to which liquids or other fluent materials are to be applied; After-treatment of applied coatings, e.g. intermediate treating of an applied coating preparatory to subsequent applications of liquids or other fluent materials by electrical means
    • B05D3/141—Plasma treatment
    • B05D3/142—Pretreatment
    • B05D3/144—Pretreatment of polymeric substrates
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D5/00—Processes for applying liquids or other fluent materials to surfaces to obtain special surface effects, finishes or structures
    • B05D5/04—Processes for applying liquids or other fluent materials to surfaces to obtain special surface effects, finishes or structures to obtain a surface receptive to ink or other liquid
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D5/00—Processes for applying liquids or other fluent materials to surfaces to obtain special surface effects, finishes or structures
    • B05D5/12—Processes for applying liquids or other fluent materials to surfaces to obtain special surface effects, finishes or structures to obtain a coating with specific electrical properties
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D7/00—Processes, other than flocking, specially adapted for applying liquids or other fluent materials to particular surfaces or for applying particular liquids or other fluent materials
    • B05D7/02—Processes, other than flocking, specially adapted for applying liquids or other fluent materials to particular surfaces or for applying particular liquids or other fluent materials to macromolecular substances, e.g. rubber
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
    • C08F285/00—Macromolecular compounds obtained by polymerising monomers on to preformed graft polymers
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
    • C08F287/00—Macromolecular compounds obtained by polymerising monomers on to block polymers
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
    • C08F291/00—Macromolecular compounds obtained by polymerising monomers on to macromolecular compounds according to more than one of the groups C08F251/00 - C08F289/00
    • C08F291/18—Macromolecular compounds obtained by polymerising monomers on to macromolecular compounds according to more than one of the groups C08F251/00 - C08F289/00 on to irradiated or oxidised macromolecules
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J7/00—Chemical treatment or coating of shaped articles made of macromolecular substances
    • C08J7/12—Chemical modification
    • C08J7/16—Chemical modification with polymerisable compounds
    • C08J7/18—Chemical modification with polymerisable compounds using wave energy or particle radiation
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D151/00—Coating compositions based on graft polymers in which the grafted component is obtained by reactions only involving carbon-to-carbon unsaturated bonds; Coating compositions based on derivatives of such polymers
    • C09D151/003—Coating compositions based on graft polymers in which the grafted component is obtained by reactions only involving carbon-to-carbon unsaturated bonds; Coating compositions based on derivatives of such polymers grafted on to macromolecular compounds obtained by reactions only involving unsaturated carbon-to-carbon bonds
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D151/00—Coating compositions based on graft polymers in which the grafted component is obtained by reactions only involving carbon-to-carbon unsaturated bonds; Coating compositions based on derivatives of such polymers
    • C09D151/006—Coating compositions based on graft polymers in which the grafted component is obtained by reactions only involving carbon-to-carbon unsaturated bonds; Coating compositions based on derivatives of such polymers grafted on to block copolymers containing at least one sequence of polymer obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D151/00—Coating compositions based on graft polymers in which the grafted component is obtained by reactions only involving carbon-to-carbon unsaturated bonds; Coating compositions based on derivatives of such polymers
    • C09D151/08—Coating compositions based on graft polymers in which the grafted component is obtained by reactions only involving carbon-to-carbon unsaturated bonds; Coating compositions based on derivatives of such polymers grafted on to macromolecular compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D4/00—Coating compositions, e.g. paints, varnishes or lacquers, based on organic non-macromolecular compounds having at least one polymerisable carbon-to-carbon unsaturated bond ; Coating compositions, based on monomers of macromolecular compounds of groups C09D183/00 - C09D183/16
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D5/00—Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced; Filling pastes
    • C09D5/16—Antifouling paints; Underwater paints
    • C09D5/1606—Antifouling paints; Underwater paints characterised by the anti-fouling agent
    • C09D5/1637—Macromolecular compounds
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D5/00—Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced; Filling pastes
    • C09D5/18—Fireproof paints including high temperature resistant paints
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D3/00—Pretreatment of surfaces to which liquids or other fluent materials are to be applied; After-treatment of applied coatings, e.g. intermediate treating of an applied coating preparatory to subsequent applications of liquids or other fluent materials
    • B05D3/06—Pretreatment of surfaces to which liquids or other fluent materials are to be applied; After-treatment of applied coatings, e.g. intermediate treating of an applied coating preparatory to subsequent applications of liquids or other fluent materials by exposure to radiation
    • B05D3/061—Pretreatment of surfaces to which liquids or other fluent materials are to be applied; After-treatment of applied coatings, e.g. intermediate treating of an applied coating preparatory to subsequent applications of liquids or other fluent materials by exposure to radiation using U.V.
    • B05D3/065—After-treatment
    • B05D3/067—Curing or cross-linking the coating
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D3/00—Pretreatment of surfaces to which liquids or other fluent materials are to be applied; After-treatment of applied coatings, e.g. intermediate treating of an applied coating preparatory to subsequent applications of liquids or other fluent materials
    • B05D3/08—Pretreatment of surfaces to which liquids or other fluent materials are to be applied; After-treatment of applied coatings, e.g. intermediate treating of an applied coating preparatory to subsequent applications of liquids or other fluent materials by flames
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D3/00—Pretreatment of surfaces to which liquids or other fluent materials are to be applied; After-treatment of applied coatings, e.g. intermediate treating of an applied coating preparatory to subsequent applications of liquids or other fluent materials
    • B05D3/14—Pretreatment of surfaces to which liquids or other fluent materials are to be applied; After-treatment of applied coatings, e.g. intermediate treating of an applied coating preparatory to subsequent applications of liquids or other fluent materials by electrical means
    • B05D3/141—Plasma treatment
    • B05D3/142—Pretreatment
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D5/00—Processes for applying liquids or other fluent materials to surfaces to obtain special surface effects, finishes or structures
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2323/00—Characterised by the use of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Derivatives of such polymers
    • C08J2323/02—Characterised by the use of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Derivatives of such polymers not modified by chemical after treatment
    • C08J2323/04—Homopolymers or copolymers of ethene
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2323/00—Characterised by the use of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Derivatives of such polymers
    • C08J2323/02—Characterised by the use of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Derivatives of such polymers not modified by chemical after treatment
    • C08J2323/10—Homopolymers or copolymers of propene
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/31504—Composite [nonstructural laminate]

Landscapes

  • Chemical & Material Sciences (AREA)
  • Organic Chemistry (AREA)
  • Engineering & Computer Science (AREA)
  • Wood Science & Technology (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Materials Engineering (AREA)
  • Health & Medical Sciences (AREA)
  • Polymers & Plastics (AREA)
  • Medicinal Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Plasma & Fusion (AREA)
  • Toxicology (AREA)
  • General Chemical & Material Sciences (AREA)
  • Application Of Or Painting With Fluid Materials (AREA)
  • Treatments Of Macromolecular Shaped Articles (AREA)
  • Paints Or Removers (AREA)
  • Graft Or Block Polymers (AREA)

Claims (33)

1. Способ формирования функциональных покрытий на неорганическом или органическом субстрате, отличающийся тем, что
а) неорганический или органический субстрат подвергают воздействию низкотемпературной плазмы, коронного разряда, высокоэнергетического излучения и/или огневой обработке,
б) на неорганический или органический субстрат наносят 1) по меньшей мере один активируемый инициатор или 2) по меньшей мере один активируемый инициатор и по меньшей мере одно соединение с этиленовой ненасыщенностью в виде расплавов, растворов, суспензий или эмульсий, причем активируемый инициатор и/или соединение с этиленовой ненасыщенностью содержит по меньшей мере одну управляющую функциями группу, предназначенную для придания обработанному субстрату желаемых поверхностных свойств, и
в) покрытый субстрат нагревают и/или подвергают воздействию электромагнитного излучения, придавая ему желаемые поверхностные свойства.
2. Способ по п.1, отличающийся тем, что формируют следующие управляющие функциями группы:
i) гидрофильную или гидрофобную группу для управления гидрофильными/гидрофобными свойствами,
ii) кислую, нейтральную или основную функциональную группу для управления кислотными/основными свойствами,
iii) функциональную группу с высокой или низкой инкрементной рефракцией для управления показателем преломления,
iv) функциональную группу, влияющую на рост клеток и/или организмов, для управления биологическими свойствами,
v) функциональную группу, влияющую на способность к воспламенению, для управления огнезащитными свойствами, и/или
vi) функциональную группу, влияющую на электропроводность, для управления антистатическими свойствами.
3. Способ по п.2, отличающийся тем, что в качестве гидрофильной группы используют полярную группу, например, спиртовую, эфирную, кислотную, сложноэфирную или альдегидную группу, кетогруппу, сахарную, фенольную, уретановую, акрилатную, винилэфирную, эпоксидную, амидную, ацетальную, кетальную или ангидридную группу, кватернизованную аминогруппу, имидную, карбонатную или нитрогруппу, соль кислоты или (поли)гликолевую мономерную единицу.
4. Способ по п.2, отличающийся тем, что в качестве гидрофильной группы используют акриловую кислоту, акриламид, ацетоксистирол, ангидрид акриловой кислоты, акрилсуццинимид, алкилглицидиловый эфир, аллилметоксифенол, полиэтиленгликоль(400)диакрилат, диэтиленгликольдиакрилат, диуретандиметакрилат, дивинилгликоль, этиленгликольдиглицидиловый эфир, глицидилакрилат, гликольметакрилат, 4-гидроксибутилметакрилат, 2-гидроксиэтилакрилат, 2-гидроксиэтилметакрилат, N-(2-гидроксипропил)метакриламид, метакрилоксиэтилглюкозид, нитростирол, сульфоэтилметакрилат, натриевую соль 3-сульфопропилакрилата, 4-винилбензойную кислоту, винилметилсульфон, винилфенилацетат или винилкарбамид.
5. Способ по п.2, отличающийся тем, что в качестве гидрофобной группы используют неполярную группу, например, разветвленную или неразветвленную алкановую, алкеновую или алкиновую группу, частично или полностью галогенированную алкановую, алкеновую или алкиновую группу, алкилированную аминогруппу, линейную или разветвленную силановую или силоксановую группу, или частично или полностью галогенированную ароматическую или не ароматическую циклическую группу.
6. Способ по п.2, отличающийся тем, что в качестве гидрофобной группы используют трет-бутилакрилат, стирол, бутилтриметоксисилан, циклогексилакрилат, декандиолдиметакрилат, дивинилбензол, 2-(2-этоксиэтокси)этилакрилат, 1Н,1Н-гептафторобутилакрилат, бензилакрилат, 1Н,1Н,7Н-додекафторгептилметакрилат, нафтилакрилат, пентабромфенилакрилат, трифторэтилакрилат или винитрифенилсилан.
7. Способ по п.2, отличающийся тем, что в качестве управляющей кислотными/основными свойствами функциональной группы используют группу карбоновой кислоты, сульфокислоты, фосфорной или серной кислоты, фенольную, аминокислотную, аминную, пиридиновую, пиримидиновую, пиперидиновую, пиррольную или имидазольную группу.
8. Способ по п.2, отличающийся тем, что в качестве управляющей кислотными/основными свойствами функциональной группы используют алкиламин, 2-аминоэтилметакрилат, 4-винилпиридин, винилпирролидон, винилимидазол, морфолиноэтилакрилат, акриловую кислоту, 2-пропен-1-сульфокислоту, сорбиновую, коричную или малеиновую кислоту.
9. Способ по п.2, отличающийся тем, что в качестве управляющей показателем преломления группы используют бензильную группу, частично или полностью галогенированную бензильную группу, частично или полностью галогенированную алкановую, алкеновую или алкиновую группу.
10. Способ по п.2, отличающийся тем, что в качестве управляющей показателем преломления группы используют бензилакрилат, 1Н,1Н,7Н-додекафторгептилметакрилат, 1Н,1Н-гептафторбутилакрилат или трифторэтилакрилат.
11. Способ по п.2, отличающийся тем, что в качестве управляющей биологическими свойствами группы используют группу с противообрастающими свойствами, например, метакрилат меди(II), малеат дибутилолова, метакрилат олова(II) или диметакрилат цинка.
12. Способ по п.2, отличающийся тем, что в качестве управляющей биологическими свойствами группы используют группу, способствующую росту биологических систем, такую как сукцинимидная, глюкозидная или сахарная группа.
13. Способ по п. 12, отличающийся тем, что в качестве группы, способствующей росту биологических систем, используют N-ацилоксисукцинимид или 2-метакрилоксиэтилглюкозид.
14. Способ по п.2, отличающийся тем, что в качестве управляющей огнезащитными свойствами группы используют полностью или частично хлорированную или бромированную алкановую группу, азотсодержащую или фосфорсодержащую группу.
15. Способ по п.2, отличающийся тем, что в качестве управляющей огнезащитными свойствами группы используют трибромнеопентилметакрилат, бис(2-метакрилоксиэтил)фосфат или моноакрилоксиэтилфосфат.
16. Способ по п.2, отличающийся тем, что в качестве управляющей антистатическими свойствами группы используют третичную аминогруппу, этоксилированную аминогруппу, алканоламидную, глицеринстеаратную, сорбитановую или сульфонатную группу.
17. Способ по п.2, отличающийся тем, что в качестве управляющей антистатическими свойствами группы используют 2-диизопропиламиноэтилметакрилат, 3-диметиламинонеопентилакрилат или олеилбис(2-гидроксиэтил)амин, стеарилакрилат, винилстеарат.
18. Способ по п.1, отличающийся тем, что неорганический или органический субстрат является синтетическим или натуральным полимером, оксидом металла, стеклом, полупроводником, кварцем или металлом, или содержит их.
19. Способ по п.1, отличающийся тем, что органический субстрат является гомополимером, блок-сополимером, привитым полимером, сополимером и/или соответствующей смесью, или содержит их.
20. Способ по п.1, отличающийся тем, что органический субстрат является поликарбонатом, сложным полиэфиром, галогенсодержащим полимером, полиакрилатом, полиолефином, полиамидом, полиуретаном, полистиролом, полиарамидом, простым полиэфиром или полисилоксаном/силиконом, или содержит эти полимеры.
21. Способ по п.1, отличающийся тем, что инициатор является соединением или комбинацией соединений из классов пероксидов, перкарбонатов, персульфатов, бензпинаколов, дибензилов, дисульфидов, азосоединений, окислительно-восстановительных систем, бензоинов, бензилкеталей, ацетофенонов, гидроксиалкилфенонов, аминоалкилфенонов, ацилфосфиноксидов, ацилфосфинсульфидов, ацилоксииминокетонов, пероксисоединений, галогенированных ацетофенонов, фенилглиоксалатов, бензофенонов, оксимов и сложных эфиров оксимов, тиоксантонов, ферроценов, титаноценов, солей сульфония, солей йодония, солей диазония, ониевых солей, боратов, триазинов, бисимидазолов, полисиланов и красителей, а также соответствующих соинициаторов и/или сенсибилизаторов.
22. Способ по п.1, отличающийся тем, что инициатор содержит по меньшей мере одну группу с этиленовой ненасыщенностью, в частности, винильную, винилиденовую, акрилатную, метакрилатную, аллильную группу или группу простого винилового эфира.
23. Способ по п.1, отличающийся тем, что соединение с этиленовой ненасыщенностью используют в виде мономера, олигомера и/или полимера.
24. Способ по п.1, отличающийся тем, что соединение с этиленовой ненасыщенностью является моно-, ди-, три-, тетра- или многофункциональным акрилатом, метакрилатом или простым виниловым эфиром.
25. Способ по п.1, отличающийся тем, что в качестве плазменного газа используют воздух, воду, инертный газ, химически активный газ или смесь указанных газов.
26. Способ по п.1, отличающийся тем, что концентрация инициаторов в используемой на стадии б) жидкости составляет от 0,01 до 20 %, предпочтительно от 0,1 до 5%.
27. Способ по п.1, отличающийся тем, что концентрация ненасыщенных соединений в используемой на стадии б) жидкости составляет от 0,1 до 30 %, предпочтительно от 0,1 до 10%.
28. Способ по п.1, отличающийся тем, что используемые на стадии б) жидкости дополнительно могут содержать другие вещества, например антивспениватели, эмульгаторы, поверхностно-активные вещества, противообрастающие средства, смачивающие агенты и другие, обычно используемые в лакокрасочной промышленности добавки.
29. Способ по п.1, отличающийся тем, что толщина нанесенного слоя в сухом состоянии находится в интервале от толщины мономолекулярного слоя до 2 мм, предпочтительно от 2 нм до 1000 мкм, особенно предпочтительно от 2 до 1000 нм.
30. Способ по п.1, отличающийся тем, что облучение на стадии в) осуществляют источниками электромагнитных волн, длина которых находится в интервале от 200 до 20000 нм, или электронными лучами, причем необязательно реализуют стадию предварительной сушки.
31. Способ по п.1, отличающийся тем, что на стадии в) облучают всю поверхность или часть поверхности.
32. Способ по п.1, отличающийся тем, что на стадии в) облучают часть поверхности, после чего удаляют необлученный материал.
33. Субстраты с функциональными покрытиями, получаемыми способом по одному из предыдущих пунктов.
RU2005122903/12A 2002-12-20 2003-12-15 Способ формирования функциональных покрытий RU2005122903A (ru)