KR890013084A - 티오카르바민산 s-알킬에스테르계 렌즈용 수지, 그 수지로 이루어진 플라스틱렌즈 및 렌즈의 제조방법 - Google Patents

티오카르바민산 s-알킬에스테르계 렌즈용 수지, 그 수지로 이루어진 플라스틱렌즈 및 렌즈의 제조방법 Download PDF

Info

Publication number
KR890013084A
KR890013084A KR1019890001913A KR890001913A KR890013084A KR 890013084 A KR890013084 A KR 890013084A KR 1019890001913 A KR1019890001913 A KR 1019890001913A KR 890001913 A KR890001913 A KR 890001913A KR 890013084 A KR890013084 A KR 890013084A
Authority
KR
South Korea
Prior art keywords
alkyl ester
lens according
thiocarbamic acid
polyisocyanate
mercapto compound
Prior art date
Application number
KR1019890001913A
Other languages
English (en)
Other versions
KR920006006B1 (ko
Inventor
데루유끼 나가다
고오주 오까자기
도오루 미우라
노부유끼 가지모도
요시노부 가네무라
가쯔요시 사사가와
Original Assignee
사와무라 하루오
미쯔이도오아쯔 가가꾸 가부시기가이샤
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 사와무라 하루오, 미쯔이도오아쯔 가가꾸 가부시기가이샤 filed Critical 사와무라 하루오
Publication of KR890013084A publication Critical patent/KR890013084A/ko
Application granted granted Critical
Publication of KR920006006B1 publication Critical patent/KR920006006B1/ko

Abstract

내용 없음.

Description

티오카르바민산 S-알킬에스테르계 렌즈용 수지, 그 수지로 이루어진 플라스틱렌즈 및 렌즈의 제조방법
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음

Claims (27)

1종 또는 2종 이상의 폴리이소시아네이트와 1종 또는 2종 이상의 히드록시기를 가진 메르캅토화합물을 반응시켜서 얻게되는 티오카르바민산 S-알킬에스테르계 렌즈용 수지.
제1항에 기재한 티오카르바민산 S-알킬에스테르계 렌즈용 수지로 이루어진 플라스틱렌즈.
1종 또는 2종 이상의 플리이소시아테이트와 1종 또는 2종 이상의 히드록시를 가진 메르캅토 화합물과의 혼합물에 내부이형제를 첨가해서, 주형중합해서 얻게되는 티오카르바민산 S-알킬에스테르계 렌즈의 제조 방법.
제3항에 기재한 렌즈의 제조방법에 의해서 얻게된 티오카르바민산 S-알킬에스테르계 플라스틱렌즈.
제1항에 있어서, 폴리이소시아네이트가 황원자를 함유하고 있는 폴리이소시아네이트인 티오카르바민산 S-알킬에스테르계 렌즈용 수지.
제2항에 있어서, 폴리이소시아네이트가 유황원자를 함유하고 있는 폴리이소시아네이트인 티오카르바민산 S-알킬에스테르계 플라스틱렌즈.
제3항에 있어서, 폴리이소시아네이트가 유황원자를 함유하고 있는 폴리이소시아네이트인 렌즈의 제조방법.
제4항에 있어서, 폴리이소시아네이트가 유황원자를 함유하고 있는 폴리이소시아네이트인 티오카르바민산 S-알킬에스테르계 플라스틱렌즈.
제1항에 있어서, 히드록시기를 가진 메르캅토 화합물이 메르캅토기 이외에 적어도 1개의 유황원자를 함유하고 있는 메르캅토 화합물인 티오카르바민산 S-알킬에스테르계 렌즈용 수지.
제2항에 있어서, 히드록시기를 가진 메르캅토 화합물이 메르캅토기 이외에 적어도 1개의 유황원자를 함유하고 있는 메르캅토 화합물인 티오카르바민산 S-알킬에스테르계 플라스틱렌즈.
제3항에 있어서, 히드록시기를 가진 메르캅토 화합물이 메르캅토기 이외에 적어도 1개의 유황원자를 함유하고 있는 메르캅토 화합물인 렌즈의 제조방법.
제4항에 있어서, 히드록시기를 가진 메르캅토 화합물이 메르캅토기 이외에 적어도 1개의 유황원자를 함유하고 있는 메르캅토 화합물인 티오카르바민산 S-알킬에스테르계 플라스틱렌즈.
제1항에 있어서, 폴리이소시아네이트와 히드록시기를 가진 메르캅토 화합물과의 사용비율이 관능기(SH+OH) 1몰에 대해 NCO기 0.5∼3.0몰의 범위내인 티오카르바민산 S-알킬에스테르계 렌즈용 수지.
제2항에 있어서, 폴리이소시아네이트와 히드록시기를 가진 메르캅토 화합물과의 사용비율이 관능기(SH+OH) 1몰에 대해 NCO기 0.5∼3.0몰의 범위내인 티오카르바민산 S-알킬에스테르계 플라스틱렌즈.
제3항에 있어서, 폴리이소시아네이트와 히드록시기를 가진 메르캅토 화합물과의 사용비율이 관능기(SH+OH) 1몰에 대해 NCO기 0.5 ~ 3.0몰의 범위 내인 티오카르바민산 S-알킬에스테르계 렌즈의 제조방법.
제4항에 있어서, 폴리이소시아네이트와 히드록시기를 가진 메르캅토 화합물과의 사용비율이 관능기(SH+OH) 1몰에 대해 NCO기 0.5∼3.0몰의 범위내인 티오카르바민산 5-알킬에스테르계 플라스틱렌즈.
제3항에 있어서, 내부 이형제가 불소계 노니온 계면활성제인 렌즈의 제조방법.
제3항에 있어서, 내부 이형제가 실리콘계 노니온 계면활성제인 렌즈의 제조방법.
제3항에 있어서, 내부 이형제가 알킬 제4급 암모늄염인 렌즈의 제조방법.
제3항에 있어서, 내부 이형제가 산성인산 에스테르인 렌즈의 제조방법.
제4항에 있어서, 내부 이형제가 불소계 노니온 계면활성제인 티오카르바민산 S-알킬에스테르계 플라스틱 렌즈.
제4항에 있어서, 내부 이형제가 실리콘계 노니온 계면활성제인 티오카르바민산 S-알킬에스테르계 플라스틱 렌즈.
제4항에 있어서, 내부 이형제가 알킬 제4급 암모늄염인 티오카르바민산 S-알킬에스테르계 플라스틱 렌즈.
제4항에 있어서, 내부 이형제가 산성인산 에스테르인 티오카르바민산 S-알킬에스테르계 플라스틱렌즈.
제3항에 있어서, 내부 이형제의 사용량이 폴리이소시아네이트와 히드록실기를 가진 메르캅토 화합물의 합계량에 대해서 0.1∼10,000ppm인 렌즈의 제조방법.
제4항에 있어서, 내부 이형제의 사용량이 폴리이소시아네이트와 히드록실기를 가진 메르캅토 화합물의 합계량에 대해서 0.1∼10,000ppm인 티오카르바민산 S-알킬에스테르계 플라스틱렌즈.
제3항에 있어서, 주형중합이 -50℃∼200℃의 온도에서 행하여지는 렌즈의 제조방법.
※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019890001913A 1988-02-18 1989-02-18 티오카르바민산 s-알킬에스테르 계렌즈용수지, 그 수지로 이루어진 플라스틱렌즈 및 렌즈의 제조방법 KR920006006B1 (ko)