KR880012664A - 저온 플래시 및 신속건조 특성을 갖는 수분산성 베이스코트중의 폴리우레탄 수지 - Google Patents
저온 플래시 및 신속건조 특성을 갖는 수분산성 베이스코트중의 폴리우레탄 수지 Download PDFInfo
- Publication number
- KR880012664A KR880012664A KR1019880004295A KR880004295A KR880012664A KR 880012664 A KR880012664 A KR 880012664A KR 1019880004295 A KR1019880004295 A KR 1019880004295A KR 880004295 A KR880004295 A KR 880004295A KR 880012664 A KR880012664 A KR 880012664A
- Authority
- KR
- South Korea
- Prior art keywords
- carboxylic acid
- weight
- groups
- carbon atoms
- active hydrogen
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (17)
- (a)적어도 두개의 히드록실 그룹을 함유한 알콜을 갖는 폴리에스테르 성분으로서, 카르복실산 성분이 탄소수 18 내지 60을 적어도 하나의 장쇄 카르복실산 적어도 약 50 중량 %의 적어도 하나의 단쇄 다카르복실산 최대 약 50%로 구성되는 폴리에스테르 성분 ; (b)적어도 하나의 활성 수소그룹과 적어도 하나의 카르복실산 작용기를 갖는 다작용성 화합물 ; (c)히드록실, 설프히드릴 1급 아미노산 및 2급 아미노산, 상술한 1급 아미노산중 하나가 하나의 활성 수소로 간주되는 것으로 구성되는 그룹으로부터 선택되는 적어도 두개의활성수소그룹을 함유하는 화합물 ; 그리고 (d)폴리이소시아네트 ; 의 반응생성물로 구성되는 다음 코팅계에 사용되는 음이온성 폴리우레탄 수지.
- 제1항에 있어서, 장쇄 카르복실산이 탄소수 36이 이합체 지방산인 폴리우렌탄 수지.
- 제1항에 있어서, 카르복실산의 상술한 카르복실산 성분의 약 0 내지 60%로 포함되는 폴리우레탄 수지.
- 제1항에 있어서, 다작용성 화합물이 디메틸올프로피온산인 폴리우레탄 수지.
- (a)(i)적어도 두개의 히드록실 그룹을 함유하는 알콜을 갖는 폴리에스테르 성분으로서, 상기한 카르복실산 성분이 탄소수 18 내지 60을 갖는 적어도 하나의 장쇄 카르복실산 적어도 약 50 중량 %의 적어도 하나의 단쇄 다카르복실산 최대 약 50%로 구성되는 폴리에스테르 성분 ; (ii)적어도 하나의 활성 수소와 적어도 하나의 카르복실산 작용기를 갖는 다작용성 화합물 ; (iii)히드록실, 설프히드릴 1급 아민, 및 2급아민, 1급아민의 하나는 하나의 활성 수소로 간주되는 것으로 구성되는 그룹에서 선택된 적어도 두개의활성 수소그룹을 함유하는 화합물 ; 그리고 (iv)폴리이소시아네트 ; 의 반응생성물로 구성되는 음이온성 폴리우레탄 주 수지를 베이스코드 조성물의 최중 고형분함량 기준 약 20 내지 80 중량 % ; (b)아미노플라스트 가교결합수지 약 5 내지 약 50 중량 % : (c)퓨움 실리카화합물, 벤토나이트 점토 및 헥토라이트 점토로 구성되는 그룹으로부터 선택된 유동성 조절체 0 내지 약 25 중량 % ; (d)(i)탄소수 18 내지 60을 갖는 적어도 하나의 장쇄 카르복실산 적어도 50 중량 %의 적어도 하나의 단쇄 다카르복실산 약 48 중량 % 미만 그리고 적어도 세개의 카르복실 그룹을 갖는 다작용성 카르복실산 또는 산 무수물 약 2 내지 25 중량 %로 구성되는 카르복실산 성분 ; 그리고 (ii)적어도 두개의 평균 작용기를 갖는 알콜 성분의 반응생성물로 구성된 측쇄 폴리에스테르 수지 0 내지 약 30 중량 % ; (e) a)안료의 안료함유 그라인드 수지 약 6 내지 약 60 중량 % ; b)(i)탄소수 18 내지 60을 갖는 장쇄 카르복실산 적어도 약 50 중량 % 및 단쇄 다카르복실산 최대 약 50%로 구성된 카르복실산 성분과 적어도 두개의 히드록실그룹을 함유하는 알콜과의 반응에 의해서 생성된 폴리에스테르 수지 성분과 ; 그리고(ii)적어도 하나의 활성 수소 및 적어도 하나의 카르복실산 작용기를 갖는 다작용성 화합물, 적어도 두개의 활성 수소그룹을 함유하는 화합물과 폴리이소시아네이트로된 혼합물로서, 상술한 카르복실산 그룹이 아민에 의해 중화된 혼합물과의 반응생성물에 의해 생성된 폴리우레탄 수지의 안료함유 그라인드 수지 약 2내지 약 75 중량 % ; c)아미노플라스트 가교결합제의 안료 페이스트 안료함유 그라인드 수지 약 20 내지 약 60 중량 % ; 로 구성되는 금속 또는 플라스틱에의 용착용 베이스코트 조성물.
- 제5항에 있어서, 폴리우레탄 수지가 장쇄 카르복실산으로서 탄소수 36의 이합체 지방산으로 되는 베이스코트 조성물.
- 제5항에 있어서, 다작용성 카르복실산(d)이 트리멜리트산 무수물인 베이스코트 조성물.
- 제5항에 있어서, 헥토라이트 점토가 정제된 나트륨리튬 마그네슘 실리케이트인 베이스코트 조성물.
- (a)(i)(1)탄소수 18 내지 60을 갖는 적어도 하나의 장쇄 카르복실산 적어도 50 중량 %의 및 단쇄 다카르복실산 최대 약 50 중량 %로 되는 카르복실산 성분과 적어도 두개의 히드록실 그룹을 갖는 알콜과의 반응에 의해 생성된 폴리에스테르 수지성분 ; 그리고 (2)적어도 하나의 활성 수소그룹과 적어도 하나의 카르복실산 작용기를 갖는 적어도 하나의 다작용성 화합물, 적어도 두개의 활성 수소그룹을 갖는 적어도 하나의 화합물 및 폴리이소시아네이트의 혼합물로서 상술한 카르복실산 그룹이 아민으로 중화된 혼합물과의 반응생성물로 이루어진 음이온성 폴리우레탄 조성물 ; (ii)가교 결합제 ; (iii)유동성 조절제 ; (iv)임의로, (1)탄소수 18 내지 60을 갖는 장쇄 카르복실산 적어도 50 중량 %, 단쇄 디카르복실산 약 48 중량 % 미만 및 적어도 세개의 카르복실산 그룹을 갖는 다작용성 카르복실산 또는 산 무수물 약 2 내지 25 중량 %로 구성되는 카르복실산 성분과 ; 그리고 (2)적어도 두개의 평균 알콜 작용기를 갖는 알콜 함유 화합물과의 반응생성물로 구성된 측쇄 폴리에스테르 수지 ; 그리고 (v)안료 ; 로 이루어진 수용성 베이스코트 조성물 ; 그리고 (b)상기한 베이스코트 조성물이 오버코팅용 클리어 톱코트 조성물로 되는 다층 페인트 조성물.
- 제9항에 있어서, 장쇄 카르복실산이 탄소수 36의 이합체 지방산인 조성물.
- (a)안료의 안료함유 그라인드 수지 약 6 내지 약 60 % ; (b)(i)탄소수 18 내지 60을 갖는 장쇄 카르복실산 적어도 50 중량 % 및 단쇄 다카르복실산 최대 약 50%로 구성된 카르복실산 성분과 그리고 적어도 두개의 히드록실 그룹을 갖는 알콜과의 반응에 의해 생성된 폴리에스테르 수지성분 ; 그리고 (ii)적어도 하나의 카르복실산 작용기를 갖는 적어도 하나의 다작용성 화합물, 적어도 두개의 활성 수소그룹을 갖는 적어도 하나의 화합물, 그리고 폴리이소시아네이트로된 혼합물로서, 상술한 카르복실산 그룹이 아민으로 중화된 혼합물과의 반응생성물에 의해 제조된 폴리우레탄 수지의 안료함유 그라인드 수지 약 20 내지 약 75중량 % ; 그리고 (c)아미노플라스트 가교 결합제의 안료함유 그라인드 수지 약 20 내지 약 60 중량 % ; 로 이루어진 수용성 베이스코트에 사용되는 안료함유 그라인드 수지.
- (a)용액중의 가교 결합제를 용액중의 유동성 조절제에 가하고 그리고 충분히 교반하고 ; (b)(i)탄소수 18 내지 60을 갖는 장쇄산 적어도 50 중량 %와 단쇄 디카르복실산 최대 약 50 중량 %로 구성된 카르복실산 성분과 적어도 두개의 히드록실 그룹을 갖는 알콜과의 반응에 의해 생성된 폴리에스테르 수지 ; 그리고 (ii)적어도 하나의 활성수소 작용기와 적어도 하나의 카르복실산 작용기를 갖는 다작용성 화합물, 적어도 두개의 활성 수소그룹을 갖는 적어도 하나의 화합물 및 폴리이소시아네이트로 된 혼합물로서, 상술한 카르복실산 그룹이 아민으로 중화된 혼합물과의 반응생성물로 구성되는 음이온성 폴리우레탄 수지 분산물을 (a) 단계의 혼합물에 교반하면서 첨가하여 충분히 교반하고 ; (c)(i)탄소수 18 내지 60을 갖는 장쇄 카르복실산 적어도 50 중량 %, 단쇄 다카르복실산 약 48 중량 % 미만 그리고 적어도 세개의 카르복실산 그룹을 갖는, 다작용성 카르복실산 약 2 내지 25 중량 %로 구성되는 카르복실산 성분 ; (ii)적어도 두개의 평균 작용기를 갖는 알콜성분 ; (iii)물 ; 그리고 (iv)아민 함유 화합물과의 반응생성물로 구성되는 분자쇄 폴리에스테르 수지 분산액을 예비혼합하여 얻은 예비혼합된 슬러리를 (c)단계후에 얻어지는 혼합물에 가하고 ; (d)상기 (b)단계로 얻은 혼합물에 안료-페이스트를 가하여, 충분히 교반하고 ; (e)상기 (d)단계에서 얻은 혼합물에 안료-페이스트를 가하여, 충분히 교반하고 ; (f)상기 (c)단계에서 얻은 혼합물의 pH와 점도를 조절하는 순차적인 단계로 이루어진 다층 코팅에 사용되는 수용성 베이스크트 조성물의 제조방법.
- 제12항에 있어서, 장쇄 카르복실산이 탄소수 36의 이합체 지방산인 방법.
- (a)(i)(1)탄소수 18 내지 60을 갖는 장쇄카르복실산 적어도 50 중량 %와 단쇄 디카르복실산 최대 50%로 구성되는 카르복실산 성분과 적어도 두개의 히드록실 그룹을 갖는 알콜과의 반응에 의해 생성된 폴리에스테르 수지성분과 ; 그리고 (2)적어도 하나의 활성수소 작용 작용기와 적어도 하나의 카르복실산 작용기를 갖는 다작용성 화합물, 적어도 두개의 활성 수소그룹을 갖는 적어도 하나의 화합물, 그리고 폴리이소시아네이트의 혼합물로서 상술한 카르복실산 그룹이 아민으로 중화된 혼합물과의 반응생성물로부터 얻은 폴리우레탄 수지 ; (ii)가교 결합제 ; (iii)유동성 조절제 ; 그리고 (iv)안료 페이스트 ; (v)임의로, 알루늄 및/또는 운모 ; (vi)임의로, 분지된 폴리에스테르 수지 ; 로 구성되는 수용성 코팅 조성물 첫째층을 프라임된 기재에 적용하고, (b)상술한 첫째층을 약 실은 내지 약 145℉ 온도에서 약 30초 내지 약 10분 플래시 건조하고; 그리고 (c)상술한 베이스코트상에 클리어 톱코트의 적어도 한층을 적용하고; 그리고 (d)상술한 베이스코트와 톱코트를 딱딱하고, 내구성 막으로 경화시키는 것으로 이루어진 다층 코팅으로 자동차 기재를 코팅하는 방법.
- 제14항에 있어서, 장쇄 카르복실산이 탄소수 36의 이합체 지방산인 방법.
- (a)(i)적어도 두개의 히드록실 그룹을 갖는 알콜을 함유하는 폴리에스테르 성분에 있어서, 카르복실성분이 탄소수 18 내지 60을 갖는 장쇄 카르복실산 적어도 약 50 중량 %와 단쇄 디카르복실산 최대 약 50%로 구성되는 폴리에스테르 성분 ; (ii)적어도 하나의 활성수소 작용기와 적어도 하나의 카르복실산 작용기를 갖는 다작용성 화합물 ; (iii)적어도 두개의 활성 수소그룹을 갖는 화합물 ; (iv)폴리이소시아네이트 ; 그리고 (v)유리 카르복실산 그룹을 중화하기 위한 아민 함유 화합물 ; 의 반응생성물로 구성되는 첫째 음이온성 폴리우레탄 수지의 베이스코트 조성물의 최종 고형분 함량 기준 약 20 내지 80 중량 % ; (b)아미노플라스트 가교 결합수지 약 5 내지 약 50 중량 % ; (c)퓨움 실리카 성분, 벤토나이트 점토 및 헥토라이트 점토로 구성되는 그룹으로부터 선택된 유동성조절제 약 0.1 내지 약 25 중량 % ; (d)(i)탄소수 18 내지 60을 갖는 장쇄 카르복실산 적어도 50 중량 %, 단쇄 다카르복실산 약 48 중량 % 미만, 그리고 적어도 세개의 카르복실산 그룹을 갖는 다작용성 카르복실산 또는 산무수물 약 2 내지 5 중량 %로 구성되는 카르복실산 성분 ; 그리고 (iii)적어도 2개의 평균 작용기를 갖는 알콜 성분과의 반응생성물로 이루어진 분자쇄폴리에스테르 수지 0 내지 약 35 중량 % ; (e)안료 약 2 내지 75 중량 %로 구성되는 베이스코트 조성물은 클리어 톱코팅으로 코팅되기전에 플래시 건조하고, 베이스코트 조성과 톱코팅은 딱딱하고 내구성막으로 경화시킨 것으로 이루어진 적어도 하나의 수용성 베이스코트 조성물로 코팅된 기판으로된 다충 코팅된 금속 또는 플라시틱 기판.
- 제16항에 있어서, 장쇄 카르복실산이 탄소수 36의 이합체 지방산인 기판.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.