KR20090050047A - 광확산성 폴리카보네이트 수지 판 - Google Patents
광확산성 폴리카보네이트 수지 판 Download PDFInfo
- Publication number
- KR20090050047A KR20090050047A KR1020097001502A KR20097001502A KR20090050047A KR 20090050047 A KR20090050047 A KR 20090050047A KR 1020097001502 A KR1020097001502 A KR 1020097001502A KR 20097001502 A KR20097001502 A KR 20097001502A KR 20090050047 A KR20090050047 A KR 20090050047A
- Authority
- KR
- South Korea
- Prior art keywords
- polycarbonate resin
- light
- surface layer
- weight part
- diffusion
- Prior art date
Abstract
본 발명은 광확산제를 함유하는 폴리카보네이트 수지 조성물로 이루어진 기재의 적어도 한쪽 면에, 대전 방지제를 함유하는 폴리카보네이트 수지 조성물로 이루어진 표층을 공압출 성형하여 이루어진 광확산성 폴리카보네이트 수지 판에 관한 것으로, 당해 대전 방지제가 특정한 유기 설폰산 포스포늄염이고, 당해 대전 방지제의 함유량이 표층에 사용되는 폴리카보네이트 수지 100중량부당 2.0중량부를 초과하고 10중량부 이하이고, 원하는 바에 따라, 폴리카프로락톤을, 표층에 사용되는 폴리카보네이트 수지 100중량부당 0.01 내지 15중량부로 함유함을 특징으로 하는 광확산성 폴리카보네이트 수지 판을 제공한다. 본 발명의 광확산성 폴리카보네이트 수지 판은 폴리카보네이트 수지의 투명성을 손상시키지 않고도 우수한 대전 방지성, 광확산성 및 휘도를 가지며, 고도의 광학적 성능을 필요로 하는 용도에, 특히 액정 표시 장치용 백라이트 등에 사용되는 광확산 판에 적합하게 사용된다.
광확산, 액정 표시 장치, 백라이트, 폴리카보네이트, 설폰산 포스포늄
Description
본 발명은 광확산성을 갖는 폴리카보네이트 수지로 이루어진 기재에, 특정 구조의 대전 방지제, 및 원하는 바에 따라 폴리카프로락톤을 함유하는 폴리카보네이트 수지층을 표층으로 하여 공압출 성형하여 이루어진 것을 특징으로 하는 광확산성 폴리카보네이트 수지 판에 관한 것이다.
폴리카보네이트 수지는, 기계적 특성, 내열성, 내광성이 우수하고 게다가 높은 광선 투과율을 갖는 수지로서 폭넓은 용도에 사용되고 있다. 예를 들면, 스카이돔, 톱라이트, 아케이드, 맨션의 요판, 도로 측벽판의 건축 분야에도 다량 사용되고 있다. 이러한 용도의 대부분은 유백색의 광확산 판이고, 폴리카보네이트 수지에 탄산칼슘, 황산바륨, 산화규소, 산화티탄 등의 광확산제를 혼합하는 방법(특허문헌 1), 미립자를 분산시키는 방법(특허문헌 2) 등이 제안되어 있다.
특허문헌 1: 일본 특허공보 제(소)57-24186호
특허문헌 2: 일본 특허공개공보 제(평)05-257002호
이러한 광확산성 폴리카보네이트 수지 판은, 액정 디스플레이용의 에지라이트 방식 또는 직하형 백라이트 방식의 면광원체나 스캐너의 면광원체에 사용되고 있다.
상기 특허문헌 1 및 2에 기재된 광확산 판은 빛을 확산시키는 부재로서의 최소한의 기능을 갖지만, 실제로 면광원체에 편입되었을 때에 먼지의 부착과 같은 문제가 발생하여, 사용 환경의 변화에 따라 액정 화면에 표시 얼룩이 발생하는 경우가 있어, 대전 방지 성능의 부여가 요구되고 있었다.
일반적으로, 폴리카보네이트 수지에 대전 방지 성능을 부여하는 방법으로서는, 도전성 카본블랙이나 카본 섬유를 배합하는 것이 실시되고 있다. 그러나, 이들은 흑색을 띄고 있기 때문에, 광확산 판과 같은 광학 용도로의 적용은 곤란하였다.
또한, 흑색 이외의 용도로는 일반적으로 알칸설포네이트의 금속염, 알킬벤젠설폰산염 등이 대전 방지제로서 사용되고 있었지만, 이들을 폴리카보네이트 수지에 배합하면 색조가 백색 불투명하게 되므로 충분한 광투과성이 수득되지 않기 때문에, 면광원체로서 높은 휘도가 수득되지 않는 것과 같은 문제가 있었다.
발명의 개시
발명이 해결하고자 하는 과제
본 발명은 면광원체에 편입되었을 때에 휘도를 손상시키지 않고 우수한 대전 방지성을 갖는 광확산성 폴리카보네이트 수지 판을 수득하는 것을 목적으로 한다.
과제를 해결하기 위한 수단
본 발명자들은 상기 과제를 해결하기 위해 예의 검토를 한 결과, 광확산성 폴리카보네이트 수지로 이루어진 기재의 적어도 한쪽 면에, 특정 구조의 대전 방지제, 및 원하는 바에 따라 폴리카프로락톤을 함유하는 폴리카보네이트 수지층을 공압출 성형함으로써, 우수한 대전 방지성을 갖는 광확산성 폴리카보네이트 수지 판을 수득하는 것을 밝혀내고, 본 발명을 완성하였다.
즉, 본 발명은, 광확산제를 함유하는 폴리카보네이트 수지 조성물로 이루어진 기재의 적어도 한쪽 면에, 대전 방지제를 함유하는 폴리카보네이트 수지 조성물로 이루어진 표층을 공압출 성형하여 이루어진 광확산성 폴리카보네이트 수지 판으로서,
ㆍ 당해 대전 방지제가 화학식 1의 유기 설폰산 포스포늄염이고,
ㆍ 당해 대전 방지제의 함유량이 표층에 사용되는 폴리카보네이트 수지 100중량부당 2.0중량부를 초과하고 10중량부 이하인, 광확산성 폴리카보네이트 수지 판에 관한 것이다.
위의 화학식 1에서,
R1은 알킬기, 아릴기, 또는 알킬기를 치환기로서 갖는 아릴기이고,
R2 내지 R5는 수소원자, 알킬기 또는 아릴기이고, 이들은 동일하거나 상이할 수 있다.
발명의 효과
본 발명의 광확산성 폴리카보네이트 수지 판은, 폴리카보네이트 수지의 투명성을 손상시키지 않으면서도 우수한 대전 방지성, 광확산성 및 휘도를 가지며, 고도의 광학적 성능을 필요로 하는 용도, 특히 액정 표시 장치용 백라이트 등에 사용되는 광확산 판에 적합하게 사용된다.
발명을 실행하기 위한
최량의
형태
본 발명의 기재 및 표층에 사용되는 폴리카보네이트 수지는, 각종 디하이드록시디아릴 화합물과 포스겐을 반응시키는 포스겐법, 또는 디하이드록시디아릴화합물과 디페닐카보네이트 등의 탄산에스테르를 반응시키는 에스테르 교환법에 의해서 수득되는 중합체이고, 대표적인 것으로는 2,2-비스(4-하이드록시페닐)프로판(비스페놀 A)로부터 제조된 폴리카보네이트 수지를 들 수 있다.
상기 디하이드록시디아릴 화합물로서는, 비스페놀 A 외에도, 비스(4-하이드록시페닐)메탄, 1,1-비스(4-하이드록시페닐)에탄, 2,2-비스(4-하이드록시페닐)부탄, 2,2-비스(4-하이드록시페닐)옥탄, 비스(4-하이드록시페닐)페닐메탄, 2,2-비 스(4-하이드록시페닐-3-메틸페닐)프로판, 1,1-비스(4-하이드록시-3-제3부틸페닐)프로판, 2,2-비스(4-하이드록시-3-브로모페닐)프로판, 2,2-비스(4-하이드록시-3,5-디브로모페닐)프로판, 2,2-비스(4-하이드록시-3,5-디클로로페닐)프로판과 같은 비스(하이드록시아릴)알칸류, 1,1-비스(4-하이드록시페닐)사이클로펜탄, 1,1-비스(4-하이드록시페닐)사이클로헥산과 같은 비스(하이드록시아릴)사이클로알칸류, 4,4'-디하이드록시디페닐에테르, 4,4'-디하이드록시-3,3'-디메틸디페닐에테르와 같은 디하이드록시디아릴에테르류, 4,4'-디하이드록시디페닐설파이드와 같은 디하이드록시디아릴설파이드류, 4,4'-디하이드록시디페닐설폭사이드, 4,4'-디하이드록시-3,3'-디메틸디페닐설폭사이드와 같은 디하이드록시디아릴설폭사이드류, 4,4'-디하이드록시디페닐설폰, 4,4'-디하이드록시-3,3'-디메틸디페닐설폰과 같은 디하이드록시디아릴설폰류 등을 들 수 있다. 이들은 단독으로 사용되거나 2종류 이상 혼합하여 사용된다. 이들 외에, 피페라진, 디피페리딜하이드로퀴논, 레조르신, 4,4'-디하이드록시디페닐 등을 혼합하여 사용해도 양호하다.
또한, 상기의 디하이드록시아릴 화합물과 이하에 나타내는 3가 이상의 페놀 화합물을 혼합 사용해도 양호하다. 3가 이상의 페놀로서는 플루오로글루신, 4,6-디메틸-2,4,6-트리-(4-하이드록시페닐)-헵텐, 2,4,6-디메틸-2,4,6-트리-(4-하이드록시페닐)-헵탄, 1,3,5-트리-(4-하이드록시페닐)-벤졸, 1,1,1-트리-(4-하이드록시페닐)-에탄 및 2,2-비스-[4,4-(4,4'-디하이드록시디페닐)-사이클로헥실]-프로판 등을 들 수 있다.
표층 또는 기재에 사용되는 폴리카보네이트 수지의 점도 평균 분자량은 통상 적으로 10000 내지 100000, 바람직하게는 15000 내지 35000, 더욱 바람직하게는 17000 내지 28000이다. 이러한 폴리카보네이트 수지를 제조할 때 분자량 조절제, 촉매 등을 필요에 따라 사용할 수 있다.
본 발명에서 사용되는 광확산제는, 중합체계 및 무기계 등 화학 조성상 특별히 제한되지 않지만, 본 발명의 폴리카보네이트 수지 성분에 광확산제를 첨가하고, 압출기에 의한 용융 혼합 등 공지의 방법으로 분산시켰을 때에 매트릭스 상과 상용하지 않거나 상용하기 어려워 입자로서 존재하는 것이 필요하다.
광확산제의 구체예로는 탄산칼슘, 실리카, 실리콘, 황화아연, 산화아연, 산화티탄, 인산티탄, 티탄산마그네슘, 운모, 유리충전제, 황산바륨, 점토, 활석, 실리콘 고무상 탄성체, 폴리메틸실세스퀴옥산 등의 무기계 확산제, 아크릴계, 스티렌계, 폴리에스테르계, 폴리올레핀계, 우레탄계, 나일론계, 메타크릴레이트-스티렌계, 불소계, 노르보르넨계 등의 유기계 확산제 등을 들 수 있다. 특히, 실리카, 실리콘 또는 아크릴계가 적합하게 사용된다.
또한, 광확산제의 입자 직경으로서는, 당해 확산제를 첨가함으로써 원하는 광확산성이 수득되는 것이면 특별히 제한되지 않지만, 평균 입자 직경으로서 1 내지 30㎛ 정도의 것을 적합하게 사용할 수 있다. 1㎛ 미만이면 빛을 투과할 뿐이며, 이미 광확산 효과가 수득되기 어려워지는 경우가 있다. 한편, 30㎛을 초과하면, 충분한 광확산 효과가 수득되지 않아 시인성이 떨어지는 경우가 있다. 또한, 입자 직경 분포는 특별히 제한되지 않지만 0.1 내지 100㎛ 정도이고, 1.5 내지 25㎛의 범위에서 더욱 적합하게 사용할 수 있다. 또한, 평균 입자 직경, 입자 직경 분포 및 종류가 상이한 2종류 이상의 광확산제를 병용해도 양호하며, 입자 직경 분포가 동일하지 않고, 2개 이상의 입자 직경 분포를 갖는 것 등을 단독으로 사용하거나 병용하여 사용할 수도 있다.
광확산제의 배합량으로는 기재의 폴리카보네이트 수지 100중량부당 0.1 내지 10중량부가 적합하다. 배합량이 0.1중량부 미만이면 충분한 광확산 효과가 수득되기 어려워지는 경우가 있다. 한편, 10중량부를 초과하면 빛의 투과성이 손상되어 충분한 광확산 성능이 수득되지 않게 되는 경우가 있다. 더욱 바람직하게는, 0.3 내지 5중량부의 범위이다.
본 발명에서 사용되는 대전 방지제는 화학식 1의 유기설폰산의 포스포늄염이다.
화학식 1
위의 화학식 1에서,
R1는 알킬기, 아릴기, 또는 알킬기를 치환기로서 갖는 아릴기이고, 바람직하게는 아릴기 또는 알킬기를 치환기로서 갖는 아릴기, 더욱 바람직하게는 알킬기를 치환기로서 갖는 아릴기이다. 여기서, 알킬기 및 치환기로서 사용되는 알킬기의 탄소수는 1 내지 40, 바람직하게는 8 내지 18이다. 아릴기를 치환기로서 갖는 알킬기의 수는 바람직하게는 1 내지 3개, 더욱 바람직하게는 1개이다. 또한, 아릴기 로는 페닐기 및 나프틸기를 들 수 있다.
한편, R2 내지 R5는 수소원자, 알킬기 또는 아릴기이고, 이들은 동일하거나 상이할 수 있다. 여기서, 알킬기의 탄소수는 바람직하게는 1 내지 10이다. 또한 아릴기로는 페닐기를 들 수 있다.
화학식 1의 대전 방지제 중에서도 특히 화학식 2의 알킬벤젠설폰산포스포늄염(타케모토유시사에서 제조한 S-418)을 적합하게 사용할 수 있다.
본 발명의 표층에 사용되는 대전 방지제의 배합량은 표층의 폴리카보네이트 수지 100중량부당 2중량부를 초과하고 10중량부 이하이다. 배합량이 2중량부 이하인 경우에는 대전 방지성이 떨어지고, 10중량부를 초과하면 열안정성이 저하되므로 바람직하지 않다. 더욱 바람직하게는, 2.2 내지 5중량부의 범위이다.
본 발명에서 사용되는 폴리카프로락톤은, ε-카프로락톤을 촉매 존재하에 개환 중합하여 제조되는 중합체이고, 특히 2-옥세파논의 호모 중합체가 적합하게 사용된다. 당해 중합체는 시판품으로서 용이하게 입수 가능하고, 다우 케미칼사 제조의 톤 중합체, 솔베이사 제조의 CAPA 등이 사용된다. 폴리카프로락톤의 점도 평균 분자량은 바람직하게는 10000 내지 100000이 적합하고, 더욱 바람직하게는 40000 내지 90000이다.
또한, 폴리카프로락톤에는, ε-카프로락톤의 개환 중합시 1,4-부탄디올 등과 공존시켜 변성한 것이나 분자 말단을 에테르 또는 에스테르기 등으로 치환한 변성 폴리카프로락톤도 포함된다. 당해 폴리카프로락톤을 대전 방지제와 병용함으로써, 효과 발현의 기구는 불명하지만, 대전 방지성에 대한 상승 효과가 밝혀지며, 투명성의 저하를 초래하지 않는 우수한 효과를 갖는다.
폴리카프로락톤의 배합량은 표층의 폴리카보네이트 수지 100중량부당 0.01 내지 15중량부이다. 배합량이 0.01중량부 미만이면, 충분한 대전 방지성의 상승 효과가 수득되지 않으므로 바람직하지 못하다. 한편, 15중량부를 초과하면, 투명성의 저하가 일어나므로 바람직하지 못하다. 더욱 바람직한 조성 비율은 0.1 내지 7중량부이다.
본 발명의 광확산성 폴리카보네이트 수지 판에서, 실용상, 광확산성 이외에도, 요구되는 성능에 의해, 공지의 각종 첨가제, 중합체 등을 필요에 따라 기재 및/또는 표층에 첨가할 수 있다. 예를 들면, 장기간 빛에 노출되었을 때의 수지 성형품의 변색을 억제하기 위해 힌다드 아민계의 내광안정제를, 또한, 선명한 색조를 수득하기 위해 벤조옥사졸계의 형광 증백제 및 이들을 병용하여 첨가해도 양호하다.
본 발명의 광확산성 폴리카보네이트 수지 판에는, 상기 이외의 공지의 첨가제, 예를 들면, 페놀계 또는 인계 열안정제[2,6-디-t-부틸-4-메틸페놀, 2-(1-메틸사이클로헥실)-4,6-디메틸페놀, 4,4'-티오비스-(6-t-부틸-3-메틸페놀), 2,2-메틸렌비스-(4-에틸-6-t-메틸페놀), n-옥타데실-3-(3,5-디-t-부틸-4-하이드록시페닐)프로피오네이트, 트리스(2,4-디-t-부틸페닐)포스파이트, 4,4'-비페닐렌디포스핀산테트 라키스-(2,4-디-t-부틸페닐) 등], 윤활제[파라핀 왁스, n-부틸스테아레이트, 합성 밀랍, 천연 밀랍, 글리세린모노에스테르, 몬탄산 왁스, 폴리에틸렌 왁스, 펜타에리스리톨테트라스테아레이트 등], 착색제[예를 들면, 염료], 충전제[탄산칼슘, 점토, 실리카, 유리 섬유, 유리구, 유리 플레이크, 카본 섬유, 활석, 운모, 각종 위스카류 등], 유동성 개량제, 전착제[에폭시화 대두유, 유동 파라핀 등], 추가로 다른 열가소성 수지나 각종 내충격 개량제(폴리부타디엔, 폴리아크릴산에스테르, 에틸렌ㆍ프로필렌계 고무 등의 고무에, 메타아크릴산에스테르, 스티렌, 아크릴로니트릴 등의 화합물을 그래프트 중합하여 이루어진 고무 강화 수지 등이 예시된다)를 필요에 따라 첨가할 수 있다.
본 발명의 실시 형태 및 순서를 이하에 나타낸다.
광확산제 및 기재에 사용하는 폴리카보네이트 수지를 임의의 배합량으로 계량하여, 텀블러, 리본 블렌더, 고속 믹서 등에 의해 일괄 혼합한 후, 혼합물을 통상의 1축 또는 2축 압출기를 사용하여 용융 혼련하여 펠렛화시키는 방법; 또는 각각의 성분을 별도로 계량하여, 복수의 공급 장치로부터 압출기내에 투입하여 용융 혼합하는 방법; 또는 폴리카보네이트 수지에 대해 광확산제를 고농도로 배합하고, 용융 혼합하여 펠렛화하여 마스터배치로 한 후, 당해 마스터배치와 폴리카보네이트 수지를 원하는 비율로 혼합하는 방법이 있을 수 있다.
또한, 이러한 성분을 용융 혼합할 때 압출기에 투입하는 위치, 압출 온도, 스크류 회전수, 공급량 등과 같이, 상황에 따라 임의의 조건을 선택하여 펠렛화할 수 있다. 이것에 의해 기재용의 펠렛이 수득된다.
또한, 대전 방지제와 표층에 사용하는 폴리카보네이트 수지를, 임의의 배합량으로 계량하여, 상기와 동일한 방법을 사용하여 표층용의 펠렛을 수득할 수 있다.
이것에 의해 수득된 기재용, 표층용의 펠렛을 각각, 2 내지 3기의 1축 또는 2축 압출기로 용융 혼련한 후, 공압출용 다이의 기재 피드 블럭 및 표층 피드 블럭에 각각 공급하여 적층 시트를 수득한다.
이하, 본 발명을 실시예에 의해 설명하지만, 본 발명은 이들 실시예에 한정되는 것이 아니다. 한편, 특별히 언급하지 않는 한, 실시예에서의 「%」,「부」는 각각 중량 기준에 근거한다.
또한, 사용한 원재료는 이하와 같다.
폴리카보네이트 수지:
스미토모다우사에서 제조한 CALIBRE 200-13(점도 평균 분자량: 21500, 이하「PC」라고 약기)
폴리카프로락톤:
솔베이사에서 제조한 CAPA6500C(점도 평균 분자량: 50000, 이하「PCL」이라고 약기)
광확산제:
닛쿄리카사에서 제조한 MSP-S020(폴리메틸실세스퀴옥산계 확산제, 이하「LD- 1」이라고 약기)
간츠카세이사에서 제조한 GM0449S(아크릴계 확산제, 이하「LD-2」라고 약기)
대전방지제:
타케모토유시사에서 제조한 S-418(알킬벤젠설폰산포스포늄염, 이하「대전 방지제」라고 약기)
상기의 각종 원료를 표 1 내지 3에 기재된 기재 또는 표층재용의 배합 비율로 각각 텀블러에 투입하고, 10분 동안 건식 혼합한 후, 2축 압출기(니혼세코쇼사에서 제조한 TEX30α)를 사용하여 용융 온도 260℃에서 혼련하여, 기재 또는 표층재용의 펠렛을 수득하였다.
수득된 기재 및 표층재용의 펠렛을 각각 125℃×2시간의 건조 조건으로 사전에 건조를 실시하였다.
기재용 압출기(타나베플라스틱사에서 제조한 VS40 단축 압출기(L/D=32, 40φ))에 사전 건조를 실시한 기재용 펠렛을 투입하여 260℃의 조건하에 공압출용 다이의 기재 피드 블럭으로부터 공급하였다. 또한, 동시에 표층용 압출기(플라기켄사에서 제조한 PEX-25-24형 단축 압출기(L/D=24, 25φ))에 사전 건조시킨 표층용 펠렛을 투입하여 260℃의 조건하에 표층재 피드로부터 용융 압출을 실시하고 공압출 시트를 수득하였다.
본 발명에 있어서의 각종 평가 항목 및 측정 방법에 관해 설명한다.
1. 표면 고유 저항(Rs):
수득된 공압출 시트를 90×50×2mm로 재단하고, 23℃ 및 50% 상대습도의 조 건으로 24시간 동안 상태 조절한 후, 초절연계(시시도세이덴키사에서 제조한 SME-8311)를 사용하여 측정 전압 500V, 샘플링 시간 60초의 조건으로 표면 저항치를 측정하였다. 표면 고유 저항(Rs)이 1×1014 미만인 경우를 합격으로 하였다.
2. 반감기:
수득된 공압출 시트를 90×50×2mm로 재단하고, 시시도사 제조의 스태틱 오네스트미터(Static Honestmeter)ㆍH-0110으로 반감기를 측정하였다. 우선, 10KV의 전하를, 시험편의 내전압이 일정하게 될 때까지 인가를 계속한다. 그 후, 차지(charge)를 멈추고 대전압의 감쇠를 관찰하여, 초기의 대전압이 반감하기까지의 시간을 측정하고 반감기로 하였다. 반감기가 10초 이하인 것을 합격으로 하였다.
3. 휘도의 측정:
2개의 냉음극관을 재단한 공압출 시트(90×50×2mm의 두께)의 이면에 배치하고, 램프간의 수직 방향에 있는 시험편 표면 위의 휘도를 측정하였다. 또한, 휘도란, 어떤 방향으로 향하는 광도의, 해당 방향에 수직인 면에서의 단위 면적당 비율을 말하며, 일반적으로 발광면의 밝기의 정도를 나타낸다(cd/㎡). 또한, 평가의 기준으로서, 램프간 휘도의 측정치가 2500cd/㎡ 이상인 것을 합격(O), 2500cd/㎡ 미만인 것을 불합격(X)으로 하였다. 또한, 측정 방법의 개략을 도 1에 도시한다.
표 1 및 표 2에 기재된 바와 같이, 본 발명의 구성을 만족하는 경우(실시예 1 내지 13)에는 모든 평가 항목에 있어서 충분한 성능을 갖고 있었다.
한편, 표 3에 기재된 바와 같이, 본 발명의 구성을 만족하지 않는 경우에는 어느 경우도 어떠한 결점을 갖고 있었다.
ㆍ 비교예 1은 표층 재료에 사용하는 대전 방지제의 배합량이 규정량에 미치지 않는 경우인데, 그 결과 표면 고유 저항 및 반감기가 떨어졌다.
ㆍ 비교예 2는 표층 재료에 사용하는 대전 방지제의 배합량이 규정량을 초과하는 경우인데, 그 결과 색상이 나빠지고 목표의 휘도가 수득되지 않았다.
ㆍ 비교예 3은 비교예 1의 기재에 사용한 광확산제를 LD-1에서 LD-2로 변경한 예인데, 표층 재료에 사용하는 대전 방지제의 배합량이 규정량에 미치지 않기 때문에, 그 결과 표면 고유 저항 및 반감기가 떨어졌다.
ㆍ 비교예 4는 비교예 2의 기재에 사용한 광확산제를 LD-1에서 LD-2로 변경한 예인데, 표층 재료에 사용하는 대전 방지제의 배합량이 규정량을 초과하기 때문에, 그 결과 색상이 나빠져 목표의 휘도가 수득되지 않았다.
ㆍ 비교예 5는 표층 재료에 사용하는 폴리카프로락톤의 배합량이 규정량을 초과하는 경우인데, 투명성이 떨어지기 때문에, 그 결과 목표로 하는 휘도가 수득되지 않았다.
도면의 간단한 설명
도 1은 본 발명에 있어서의 램프간 휘도의 측정 방법을 도시한 도면이다.
부호의 설명
A: 휘도계
B: 램프의 광선
C: 광확산 판
D: 램프(냉음극관)
Claims (5)
- 광확산제를 함유하는 폴리카보네이트 수지 조성물로 이루어진 기재의 적어도 한쪽 면에, 대전 방지제를 함유하는 폴리카보네이트 수지 조성물로 이루어진 표층을 공압출 성형하여 이루어진 광확산성 폴리카보네이트 수지 판으로서,ㆍ 당해 대전 방지제가 화학식 1의 유기 설폰산 포스포늄염이고,ㆍ 당해 대전 방지제의 함유량이 표층에 사용되는 폴리카보네이트 수지 100중량부당 2.0중량부를 초과하고 10중량부 이하인, 광확산성 폴리카보네이트 수지 판.화학식 1
위의 화학식 1에서,R1는 알킬기, 아릴기, 또는 알킬기를 치환기로서 갖는 아릴기이고,R2 내지 R5는 수소원자, 알킬기 또는 아릴기이고, 이들은 동일하거나 상이할 수 있다. - 제1항에 있어서, 상기 표층에 사용되는 폴리카보네이트 수지 조성물이 폴리카프로락톤을 추가로 함유하고, 당해 폴리카프로락톤의 함유량이 표층에 사용되는 폴리카보네이트 수지 100중량부당 0.01 내지 15중량부인, 광확산성 폴리카보네이트 수지 판.
- 제1항 또는 제2항에 있어서, 상기 대전 방지제가 화학식 2의 알킬벤젠설폰산포스포늄염인, 광확산성 폴리카보네이트 수지 판.화학식 2
- 제1항 또는 제2항에 있어서, 상기 대전 방지제의 배합량이 표층의 폴리카보네이트 수지 100중량부당 2.2 내지 5중량부인, 광확산성 폴리카보네이트 수지 판.
- 제2항에 있어서, 상기 폴리카프로락톤의 배합량이, 표층에 사용되는 폴리카보네이트 수지 100중량부당 0.1 내지 7중량부인, 광확산성 폴리카보네이트 수지 판.