JP5093832B2 - 光拡散性に優れた熱可塑性樹脂組成物およびそれからなる光拡散板 - Google Patents
光拡散性に優れた熱可塑性樹脂組成物およびそれからなる光拡散板 Download PDFInfo
- Publication number
- JP5093832B2 JP5093832B2 JP2005333948A JP2005333948A JP5093832B2 JP 5093832 B2 JP5093832 B2 JP 5093832B2 JP 2005333948 A JP2005333948 A JP 2005333948A JP 2005333948 A JP2005333948 A JP 2005333948A JP 5093832 B2 JP5093832 B2 JP 5093832B2
- Authority
- JP
- Japan
- Prior art keywords
- thermoplastic resin
- light
- light diffusing
- resin composition
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
よび蛍光増白剤(D)0〜0.1重量部からなることを特徴とする光拡散性に優れた熱可
塑性樹脂組成物であって、環状亜リン酸エステル系酸化防止剤(C)が2,4,8,10−テトラ−t−ブチル−6−[3−(3−メチル−4ヒドロキシ−5−t−ブチルフェニル)プロポキシ]ジベンゾ[d,f][1,3,2]ジオキサホスフェピンである、光拡散性に優れた熱可塑性樹脂組成物ならびにそれを成形してなる光拡散板を提供するものである。
なお、熱可塑性樹脂(A)の透明性の程度は、光を透過し、かつ当該樹脂の成形体を観察者と光源等の対象物の間に介在させた場合に観察者が対象物を認識できる程度の性能をいう。
ポリカーボネート樹脂:
住友ダウ社製カリバー200−30
(粘度平均分子量:17200、以下PC−1と略記)
住友ダウ社製カリバー200−3
(粘度平均分子量:28000、以下PC−2と略記)
光拡散剤:
日興リカ社製MSP−S020
(ポリメチルシルセスオキサン系拡散剤、以下LD−1と略記)
ガンツ化成社製GM−0449S
(アクリル系拡散剤、以下LD−2と略記)
酸化防止剤:
住友化学社製スミライザーGP
(環状亜リン酸エステル系酸化防止剤、以下AO−1と略記)
クラリアントジャパン株式会社製サンドスタブP−EPQ
(リン系酸化防止剤 以下AO−2と略記)
蛍光増白剤:
クラリアントジャパン社製 HOSTARUX KSN
1.熱安定性の評価
射出成形機を用いて平板試験片を作成する際に、樹脂をシリンダー内に15分間滞留させた後、通常の射出成形を行い3ショット目の平板試験片の光学測定を行い熱安定性の評価を行った。
本発明における遮蔽率とは、可視光線波長領域である、380〜720nmにおける透過しない光の量を表し、下記一般式において算出され、紫外可視分光光度計(日本分光社製V−570)により測定される。
遮蔽率(%)={1−(透過光量/34000)}×100
当該測定方法により算出された遮蔽率が、60〜85%の範囲にあるものを合格(○)、そうでないものを不合格(×)とした。かかる範囲を外れると、ランプ間輝度が低下し、十分な輝度が得られないため好ましくない。
2本の冷陰極管を平板試験片(90mmx50mmx2mm厚み)の裏側に配置し、ランプ間の垂直方向にある試験片表面上の輝度を測定した。尚、輝度とは、ある方向に向かう光度の、その方向に垂直な面における単位面積当たりの割合のことをいい、一般に、発光面の明るさの程度を表す[単位:(cd/m2)]。
初期の射出成形試験片の評価の基準としては、ランプ間輝度の測定値が2500Cd/m2以上であるものを合格(○)、2500cd/m2未満であるものを不合格(×)とした。
滞留後の試験片の評価の基準としては、初期の射出成形試験片と同様の輝度の測定を行い、その低下量が50Cd/m2未満であるものを合格(○)、50Cd/m2以上であるものを不合格(×)とした。
射出成形により作成した平板試験片を用いて、村上色彩研究所社製スペクトロフォトメーターCMS−35SPにより、b*を測定した。b*とは、黄色から青色の程度を表し、b*が小さい程、黄味が少なくなり、青味が強くなる。
遮蔽率、輝度、および成形性の評価において、全てを満足するものを合格(○)そうでないものを不合格(×)とした。
表1に示す配合比率により、ポリカーボネート樹脂(PC−1)、光拡散剤(LD−1)および環状リン酸エステル系酸化防止剤(AO−1)をスーパーフローター(カワタ社製)により乾式混合した。次いで、二軸押出機(神戸製鋼所社製KTX−37(軸直径=37mmφ、L/D=30)により、250〜290℃の温度条件にて溶融混練を行った。得られたペレットを、射出成形機(日本製鋼所社製J100E2P)を用い、シリンダー設定温度300℃の条件にて縦90mm、横50mm、厚み2mmの平板試験片を作成した。熱安定性試験に関しては、同様の射出成形機を用い320℃の温度条件にてシリンダー内に15分滞留後、通常の射出成形条件にて3ショット目の試験片にて光学測定を行った。
光学性能について遮蔽率およびランプ間輝度が良好な結果であり、滞留後の輝度の低下も非常に少ない結果となった。結果を表1に示す。
ポリカーボネート樹脂の種類をPC−2に変更する以外は、実施例2と同様の操作を行い、平板試験片を作成した。光学性能についても遮蔽率およびランプ間輝度が良好な結果であり、滞留後の輝度の低下も良好であった。結果を表2に示す。
光拡散剤の種類をLD−2に変更し、その添加量を実施例8では1.5部に、実施例9では6部に変更する以外は、実施例2と同様の操作を行い、平板試験片を作成した。 光学性能についても遮蔽率およびランプ間輝度が良好な結果であり、滞留後の輝度の低下も良好であった。結果を表2に示す。
実施例2に蛍光増白剤を0.01部追加する以外は、実施例2と同様の操作を行い、平板試験片を作成した。遮蔽率およびランプ間輝度も良好な結果であった。また、色調は、実施例2との比較においてb*の低下が見られ、目視においても鮮やかな青味を呈していた。結果を表3に示す。
比較例1では光拡散剤としてLD−1を0.03部とし、比較例2では光拡散剤としてLD−1を0.05部、比較例3では光拡散剤としてLD−2を15部に変更する以外は、実施例2と同様の操作を行い、平板試験片を作成した。評価結果を表4に示す。
比較例1及び比較例2は光拡散剤の配合量が本発明の構成要件よりも少ない場合、また比較例4は光拡散剤の配合量が本発明の構成要件よりも多い場合の例であるが、全ての試験片でランプ間輝度が劣り不合格となった。
比較例4〜8については実施例1〜5と同様組成であるが環状亜リン酸エステル系酸化防止剤を添加していない組成として、実施例2と同様の操作を行い、平板試験片を作成した。評価結果を表5に示す。
比較例4〜6は本発明の構成要件の環状亜リン酸エステル系酸化防止剤が添加されていないため、滞留後の輝度の低下が規定範囲を超え不合格となった。
また、比較例7〜8については実施例4〜5と同様組成で環状亜リン酸エステル系酸化防止剤(AO−1)を一般のリン系酸化防止剤(AO−2)に変更した場合であり、実施例2と同様の操作を行い、平板試験片を作成した。評価結果を表2に示す。
比較例7〜8は、構成要件の酸化防止剤の種類が異なるために、滞留後の輝度の低下が規定範囲を超え不合格となった。
B:ランプの光線
C:光拡散板
D:ランプ(冷陰極管)
Claims (5)
- 透明な熱可塑性樹脂(A)100重量部に対して、光拡散剤(B)(架橋(メタ)アクリル系重合体粒子からなる光拡散剤を除く)0.1〜10重量部、環状亜リン酸エステル系酸化防止剤(C)0.01〜1重量部および蛍光増白剤(D)0〜0.1重量部からなることを特徴とする光拡散性を有する熱可塑性樹脂組成物であって、環状亜リン酸エステル系酸化防止剤(C)が2,4,8,10−テトラ−t−ブチル−6−[3−(3−メチル−4ヒドロキシ−5−t−ブチルフェニル)プロポキシ]ジベンゾ[d,f][1,3,2]ジオキサホスフェピンである、光拡散性に優れた熱可塑性樹脂組成物。
- 透明な熱可塑性樹脂(A)がポリカーボネート樹脂、ポリメチルメタクリレート、メチルメタクリレート・スチレン共重合体、ポリアリレート、スチレン系共重合樹脂またはシクロオレフィンポリマーから選択される1種もしくは2種以上であることを特徴とする請求項1に記載の光拡散性に優れた熱可塑性樹脂組成物。
- 請求項1または請求項2に記載の光拡散性に優れた熱可塑性樹脂組成物から成形されてなる光拡散板。
- 液晶ディスプレイ用である請求項3に記載の光拡散板。
- 液晶ディスプレイの直下型バックライト用である請求項3に記載の光拡散板。