KR101079472B1 - 도금표면품질이 우수한 고망간강의 용융아연도금강판의 제조방법 - Google Patents
도금표면품질이 우수한 고망간강의 용융아연도금강판의 제조방법 Download PDFInfo
- Publication number
- KR101079472B1 KR101079472B1 KR1020080132593A KR20080132593A KR101079472B1 KR 101079472 B1 KR101079472 B1 KR 101079472B1 KR 1020080132593 A KR1020080132593 A KR 1020080132593A KR 20080132593 A KR20080132593 A KR 20080132593A KR 101079472 B1 KR101079472 B1 KR 101079472B1
- Authority
- KR
- South Korea
- Prior art keywords
- manganese
- hot
- plating
- steel sheet
- oxide
- Prior art date
Links
- 239000011572 manganese Substances 0.000 title claims abstract description 49
- 229910052748 manganese Inorganic materials 0.000 title claims abstract description 40
- 238000004519 manufacturing process Methods 0.000 title claims abstract description 17
- PWHULOQIROXLJO-UHFFFAOYSA-N Manganese Chemical compound [Mn] PWHULOQIROXLJO-UHFFFAOYSA-N 0.000 title claims description 22
- 238000000034 method Methods 0.000 title abstract description 27
- 238000005246 galvanizing Methods 0.000 title abstract description 11
- 238000007747 plating Methods 0.000 claims abstract description 65
- 229910000617 Mangalloy Inorganic materials 0.000 claims abstract description 30
- 239000012298 atmosphere Substances 0.000 claims abstract description 28
- 230000003647 oxidation Effects 0.000 claims abstract description 27
- 238000007254 oxidation reaction Methods 0.000 claims abstract description 27
- 229910001335 Galvanized steel Inorganic materials 0.000 claims abstract description 25
- 239000008397 galvanized steel Substances 0.000 claims abstract description 25
- 238000010438 heat treatment Methods 0.000 claims abstract description 24
- 230000009467 reduction Effects 0.000 claims abstract description 16
- HCHKCACWOHOZIP-UHFFFAOYSA-N Zinc Chemical compound [Zn] HCHKCACWOHOZIP-UHFFFAOYSA-N 0.000 claims abstract description 9
- 239000011701 zinc Substances 0.000 claims abstract description 9
- 229910052725 zinc Inorganic materials 0.000 claims abstract description 9
- 229910052710 silicon Inorganic materials 0.000 claims description 6
- 229910052782 aluminium Inorganic materials 0.000 claims description 5
- 239000012535 impurity Substances 0.000 claims description 4
- 229910052758 niobium Inorganic materials 0.000 claims description 3
- 229910052799 carbon Inorganic materials 0.000 claims description 2
- 239000000463 material Substances 0.000 abstract description 18
- WPBNNNQJVZRUHP-UHFFFAOYSA-L manganese(2+);methyl n-[[2-(methoxycarbonylcarbamothioylamino)phenyl]carbamothioyl]carbamate;n-[2-(sulfidocarbothioylamino)ethyl]carbamodithioate Chemical compound [Mn+2].[S-]C(=S)NCCNC([S-])=S.COC(=O)NC(=S)NC1=CC=CC=C1NC(=S)NC(=O)OC WPBNNNQJVZRUHP-UHFFFAOYSA-L 0.000 abstract description 5
- AMWRITDGCCNYAT-UHFFFAOYSA-L hydroxy(oxo)manganese;manganese Chemical compound [Mn].O[Mn]=O.O[Mn]=O AMWRITDGCCNYAT-UHFFFAOYSA-L 0.000 description 18
- 238000000137 annealing Methods 0.000 description 15
- 230000008569 process Effects 0.000 description 14
- 229910000831 Steel Inorganic materials 0.000 description 13
- 239000010959 steel Substances 0.000 description 13
- 230000015572 biosynthetic process Effects 0.000 description 8
- 239000002245 particle Substances 0.000 description 6
- 239000000758 substrate Substances 0.000 description 5
- QVGXLLKOCUKJST-UHFFFAOYSA-N atomic oxygen Chemical compound [O] QVGXLLKOCUKJST-UHFFFAOYSA-N 0.000 description 4
- 238000007796 conventional method Methods 0.000 description 4
- 239000001301 oxygen Substances 0.000 description 4
- 229910052760 oxygen Inorganic materials 0.000 description 4
- 238000005275 alloying Methods 0.000 description 3
- 230000008859 change Effects 0.000 description 3
- 239000007789 gas Substances 0.000 description 3
- IJGRMHOSHXDMSA-UHFFFAOYSA-N Atomic nitrogen Chemical compound N#N IJGRMHOSHXDMSA-UHFFFAOYSA-N 0.000 description 2
- 229910045601 alloy Inorganic materials 0.000 description 2
- 239000000956 alloy Substances 0.000 description 2
- 229910052787 antimony Inorganic materials 0.000 description 2
- 238000000151 deposition Methods 0.000 description 2
- 239000001257 hydrogen Substances 0.000 description 2
- 229910052739 hydrogen Inorganic materials 0.000 description 2
- 230000001590 oxidative effect Effects 0.000 description 2
- 238000011946 reduction process Methods 0.000 description 2
- 238000010301 surface-oxidation reaction Methods 0.000 description 2
- 229910052714 tellurium Inorganic materials 0.000 description 2
- 229910052718 tin Inorganic materials 0.000 description 2
- 238000001771 vacuum deposition Methods 0.000 description 2
- 229910052720 vanadium Inorganic materials 0.000 description 2
- 229910018137 Al-Zn Inorganic materials 0.000 description 1
- 229910018573 Al—Zn Inorganic materials 0.000 description 1
- 229910000975 Carbon steel Inorganic materials 0.000 description 1
- UFHFLCQGNIYNRP-UHFFFAOYSA-N Hydrogen Chemical compound [H][H] UFHFLCQGNIYNRP-UHFFFAOYSA-N 0.000 description 1
- 229910000794 TRIP steel Inorganic materials 0.000 description 1
- 230000004913 activation Effects 0.000 description 1
- -1 and as a result Substances 0.000 description 1
- 229910052785 arsenic Inorganic materials 0.000 description 1
- 238000005452 bending Methods 0.000 description 1
- 239000010962 carbon steel Substances 0.000 description 1
- 239000011248 coating agent Substances 0.000 description 1
- 238000000576 coating method Methods 0.000 description 1
- 239000002131 composite material Substances 0.000 description 1
- 239000012141 concentrate Substances 0.000 description 1
- 238000001816 cooling Methods 0.000 description 1
- 230000007797 corrosion Effects 0.000 description 1
- 238000005260 corrosion Methods 0.000 description 1
- 230000007547 defect Effects 0.000 description 1
- 230000000593 degrading effect Effects 0.000 description 1
- 238000010586 diagram Methods 0.000 description 1
- 238000009792 diffusion process Methods 0.000 description 1
- 238000009826 distribution Methods 0.000 description 1
- 239000000446 fuel Substances 0.000 description 1
- 150000002431 hydrogen Chemical class 0.000 description 1
- 230000006872 improvement Effects 0.000 description 1
- 229910000765 intermetallic Inorganic materials 0.000 description 1
- 238000003754 machining Methods 0.000 description 1
- 238000002844 melting Methods 0.000 description 1
- 230000008018 melting Effects 0.000 description 1
- 229910052757 nitrogen Inorganic materials 0.000 description 1
- 239000012299 nitrogen atmosphere Substances 0.000 description 1
- TWNQGVIAIRXVLR-UHFFFAOYSA-N oxo(oxoalumanyloxy)alumane Chemical compound O=[Al]O[Al]=O TWNQGVIAIRXVLR-UHFFFAOYSA-N 0.000 description 1
- 238000005240 physical vapour deposition Methods 0.000 description 1
- 239000011148 porous material Substances 0.000 description 1
- 238000010405 reoxidation reaction Methods 0.000 description 1
- 230000008719 thickening Effects 0.000 description 1
- 238000004804 winding Methods 0.000 description 1
Images
Classifications
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
- C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
- C23C2/0222—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating in a reactive atmosphere, e.g. oxidising or reducing atmosphere
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
- C23C2/06—Zinc or cadmium or alloys based thereon
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
- C23C2/36—Elongated material
- C23C2/40—Plates; Strips
Priority Applications (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
KR1020080132593A KR101079472B1 (ko) | 2008-12-23 | 2008-12-23 | 도금표면품질이 우수한 고망간강의 용융아연도금강판의 제조방법 |
JP2009280617A JP4990345B2 (ja) | 2008-12-23 | 2009-12-10 | メッキ表面品質に優れた高マンガン鋼の溶融亜鉛メッキ鋼板の製造方法 |
CN2009102543783A CN101760712B (zh) | 2008-12-23 | 2009-12-22 | 镀覆表面品质优良的高锰钢的热浸镀锌钢板的制造方法 |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
KR1020080132593A KR101079472B1 (ko) | 2008-12-23 | 2008-12-23 | 도금표면품질이 우수한 고망간강의 용융아연도금강판의 제조방법 |
Publications (2)
Publication Number | Publication Date |
---|---|
KR20100073819A KR20100073819A (ko) | 2010-07-01 |
KR101079472B1 true KR101079472B1 (ko) | 2011-11-03 |
Family
ID=42492088
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
KR1020080132593A KR101079472B1 (ko) | 2008-12-23 | 2008-12-23 | 도금표면품질이 우수한 고망간강의 용융아연도금강판의 제조방법 |
Country Status (3)
Country | Link |
---|---|
JP (1) | JP4990345B2 (ja) |
KR (1) | KR101079472B1 (ja) |
CN (1) | CN101760712B (ja) |
Families Citing this family (33)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
BR112012031466B1 (pt) * | 2010-06-10 | 2019-07-09 | Tata Steel Ijmuiden Bv | Método de produção de uma chapa de aço austenítica excelente em resistência à fratura retardada e tira ou chapa |
KR101242859B1 (ko) * | 2010-11-05 | 2013-03-12 | 주식회사 포스코 | 도금성 및 도금밀착성이 우수한 고망간 용융아연도금강판 및 그 제조방법 |
CN102888578B (zh) * | 2011-07-19 | 2014-12-24 | 宝山钢铁股份有限公司 | 一种具有优良表面摩擦特性的热镀锌钢板的生产方法 |
KR101329925B1 (ko) * | 2011-08-26 | 2013-11-14 | 주식회사 포스코 | 도금밀착성이 우수한 고망간강 및 이로부터 용융아연도금강판을 제조하는 방법 |
KR101428151B1 (ko) * | 2011-12-27 | 2014-08-08 | 주식회사 포스코 | 고망간 열연 아연도금강판 및 그 제조방법 |
KR101360613B1 (ko) * | 2011-12-28 | 2014-02-11 | 주식회사 포스코 | 도금성 및 도금밀착성이 우수한 용융아연도금강판 및 그 제조방법 |
KR101360734B1 (ko) * | 2011-12-28 | 2014-02-10 | 주식회사 포스코 | 도금성 및 도금 밀착성이 우수한 용융아연도금강판 및 그 제조방법 |
KR20130076589A (ko) * | 2011-12-28 | 2013-07-08 | 주식회사 포스코 | 도금표면 품질 및 도금밀착성이 우수한 고강도 용융아연도금강판 및 그 제조방법 |
JP5982906B2 (ja) | 2012-03-19 | 2016-08-31 | Jfeスチール株式会社 | 高強度溶融亜鉛めっき鋼板の製造方法 |
JP5982905B2 (ja) | 2012-03-19 | 2016-08-31 | Jfeスチール株式会社 | 高強度溶融亜鉛めっき鋼板の製造方法 |
KR20160143893A (ko) | 2012-06-15 | 2016-12-14 | 제이에프이 스틸 가부시키가이샤 | 고강도 강판 및 고강도 용융 아연 도금 강판 그리고 그것들의 제조 방법 |
JP5962540B2 (ja) * | 2012-07-23 | 2016-08-03 | Jfeスチール株式会社 | 高強度鋼板の製造方法 |
JP5962541B2 (ja) * | 2012-07-23 | 2016-08-03 | Jfeスチール株式会社 | 高強度鋼板の製造方法 |
KR101510505B1 (ko) * | 2012-12-21 | 2015-04-08 | 주식회사 포스코 | 우수한 도금성과 초고강도를 갖는 고망간 용융아연도금강판의 제조방법 및 이에 의해 제조된 고망간 용융아연도금강판 |
JP5915569B2 (ja) * | 2013-03-01 | 2016-05-11 | Jfeスチール株式会社 | 溶融亜鉛めっき鋼板の製造方法および連続溶融亜鉛めっき装置 |
MX2015011463A (es) | 2013-03-04 | 2016-02-03 | Jfe Steel Corp | Lamina de acero de alta resistencia y metodo para la produccion de la misma y lamina de acero galvanizada de alta resistencia y metodo para la produccion de la misma. |
JP5935720B2 (ja) * | 2013-03-05 | 2016-06-15 | Jfeスチール株式会社 | 高強度溶融亜鉛めっき鋼板の製造方法および高強度溶融亜鉛めっき鋼板 |
CN103320589B (zh) * | 2013-06-11 | 2014-11-05 | 鞍钢股份有限公司 | 一种防止高镍钢坯加热过程氧化的方法 |
CN103572190B (zh) * | 2013-09-24 | 2016-08-10 | 河北钢铁股份有限公司唐山分公司 | 热镀锌生产中锌锅的净化处理方法 |
JP5884196B2 (ja) * | 2014-02-18 | 2016-03-15 | Jfeスチール株式会社 | 高強度溶融亜鉛めっき鋼板の製造方法 |
JP6020605B2 (ja) * | 2015-01-08 | 2016-11-02 | Jfeスチール株式会社 | 合金化溶融亜鉛めっき鋼板の製造方法 |
KR101746996B1 (ko) * | 2015-12-24 | 2017-06-28 | 주식회사 포스코 | 도금 밀착성이 우수한 고망간 용융 알루미늄계 도금강판 |
KR101899680B1 (ko) * | 2016-12-21 | 2018-09-17 | 주식회사 포스코 | 표면품질과 도금밀착성이 우수한 고강도 용융아연 도금강판 및 그 제조방법 |
CN108796383A (zh) * | 2017-04-27 | 2018-11-13 | 宝山钢铁股份有限公司 | 一种含钛高强度高韧性无磁钢及其制造方法 |
CN108929991B (zh) | 2017-05-26 | 2020-08-25 | 宝山钢铁股份有限公司 | 一种热浸镀高锰钢及其制造方法 |
CN107299306B (zh) * | 2017-07-20 | 2019-10-29 | 首钢集团有限公司 | 一种中锰钢热浸镀的方法 |
JP6777045B2 (ja) * | 2017-08-09 | 2020-10-28 | Jfeスチール株式会社 | 高強度溶融亜鉛めっき鋼板の製造方法 |
KR102529740B1 (ko) | 2021-06-18 | 2023-05-08 | 주식회사 포스코 | 내식성 및 표면 품질이 우수한 고내식 도금 강판 및 이의 제조방법 |
KR102513355B1 (ko) | 2021-09-30 | 2023-03-23 | 주식회사 포스코 | 내식성 및 표면 외관이 우수한 도금 강판 및 이의 제조방법 |
KR102491029B1 (ko) | 2021-09-30 | 2023-01-20 | 주식회사 포스코 | 내식성 및 백색도가 우수한 도금 강판 및 이의 제조방법 |
KR102513354B1 (ko) | 2021-09-30 | 2023-03-23 | 주식회사 포스코 | 내식성 및 굽힘성이 우수한 도금 강판 및 이의 제조방법 |
KR102513353B1 (ko) | 2021-09-30 | 2023-03-23 | 주식회사 포스코 | 내식성 및 용접성이 우수한 도금 강판 및 이의 제조방법 |
CN115156845A (zh) * | 2022-06-16 | 2022-10-11 | 唐山钢铁集团高强汽车板有限公司 | 一种防止镀层粘辊的镀锌热成形钢生产方法 |
Citations (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
KR100742833B1 (ko) | 2005-12-24 | 2007-07-25 | 주식회사 포스코 | 내식성이 우수한 고 망간 용융도금강판 및 그 제조방법 |
Family Cites Families (11)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3925579A (en) * | 1974-05-24 | 1975-12-09 | Armco Steel Corp | Method of coating low alloy steels |
JPH04297527A (ja) * | 1991-03-26 | 1992-10-21 | Nippon Steel Corp | 強度−延性バランスの優れた高強度溶融亜鉛メッキ鋼板の製造方法 |
JP3277063B2 (ja) * | 1994-01-25 | 2002-04-22 | 日新製鋼株式会社 | 高張力熱延鋼板の溶融めっき方法 |
JP2000169948A (ja) * | 1998-12-03 | 2000-06-20 | Nippon Steel Corp | 合金化溶融亜鉛めっき鋼板およびその製造方法 |
JP4729850B2 (ja) * | 2003-02-10 | 2011-07-20 | Jfeスチール株式会社 | めっき密着性に優れた合金化溶融亜鉛めっき鋼板およびその製造方法 |
FR2876711B1 (fr) * | 2004-10-20 | 2006-12-08 | Usinor Sa | Procede de revetement au trempe a chaud dans un bain de zinc des bandes en acier fer-carbone-manganese |
DE102004059566B3 (de) * | 2004-12-09 | 2006-08-03 | Thyssenkrupp Steel Ag | Verfahren zum Schmelztauchbeschichten eines Bandes aus höherfestem Stahl |
JP3907656B2 (ja) * | 2004-12-21 | 2007-04-18 | 株式会社神戸製鋼所 | 溶融亜鉛めっき方法 |
JP4747656B2 (ja) * | 2005-04-20 | 2011-08-17 | Jfeスチール株式会社 | 高張力溶融亜鉛めっき鋼板の製造方法および高張力合金化溶融亜鉛めっき鋼板の製造方法 |
JP4816068B2 (ja) * | 2005-12-26 | 2011-11-16 | Jfeスチール株式会社 | めっき密着性に優れた溶融亜鉛めっき鋼板の製造方法 |
DE102006039307B3 (de) * | 2006-08-22 | 2008-02-21 | Thyssenkrupp Steel Ag | Verfahren zum Beschichten eines 6-30 Gew.% Mn enthaltenden warm- oder kaltgewalzten Stahlbands mit einer metallischen Schutzschicht |
-
2008
- 2008-12-23 KR KR1020080132593A patent/KR101079472B1/ko active IP Right Grant
-
2009
- 2009-12-10 JP JP2009280617A patent/JP4990345B2/ja not_active Expired - Fee Related
- 2009-12-22 CN CN2009102543783A patent/CN101760712B/zh not_active Expired - Fee Related
Patent Citations (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
KR100742833B1 (ko) | 2005-12-24 | 2007-07-25 | 주식회사 포스코 | 내식성이 우수한 고 망간 용융도금강판 및 그 제조방법 |
Also Published As
Publication number | Publication date |
---|---|
CN101760712B (zh) | 2012-08-22 |
JP2010150660A (ja) | 2010-07-08 |
KR20100073819A (ko) | 2010-07-01 |
CN101760712A (zh) | 2010-06-30 |
JP4990345B2 (ja) | 2012-08-01 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
KR101079472B1 (ko) | 도금표면품질이 우수한 고망간강의 용융아연도금강판의 제조방법 | |
KR101329925B1 (ko) | 도금밀착성이 우수한 고망간강 및 이로부터 용융아연도금강판을 제조하는 방법 | |
JP3738754B2 (ja) | 電着塗装用アルミニウムめっき構造部材及びその製造方法 | |
TWI494442B (zh) | Alloyed molten galvanized steel sheet and manufacturing method thereof | |
EP2794950B1 (en) | Hot-dip galvanized steel sheet having excellent adhesiveness at ultra-low temperatures and method of manufacturing the same | |
JP5830541B2 (ja) | めっき性、めっき密着性及びスポット溶接性に優れた溶融亜鉛めっき鋼板及びその製造方法 | |
ZA200703345B (en) | Method for the hot-dip coating of iron-carbon-manganese steel strip in a zinc bath | |
WO2003074751A1 (fr) | Plaque d'acier a surface traitee et procede de production correspondant | |
KR101207767B1 (ko) | 도금성이 우수한 고망간 고알루미늄 용융아연도금강판 및 그 제조방법 | |
CN113025937A (zh) | 一种热浸镀锌钢板及其制备方法 | |
KR20190073200A (ko) | 용접성이 우수한 고강도 냉연강판 및 도금강판과 그 제조 방법 | |
JP2019505670A (ja) | めっき性に優れた高強度溶融亜鉛系めっき鋼材及びその製造方法 | |
EP3034646A1 (en) | Production method for high-strength hot-dip galvanized steel sheets and production method for high-strength alloyed hot-dip galvanized steel sheets | |
JP5978826B2 (ja) | 表面安定性に優れた高強度溶融亜鉛めっき鋼板の製造方法 | |
KR101242859B1 (ko) | 도금성 및 도금밀착성이 우수한 고망간 용융아연도금강판 및 그 제조방법 | |
KR101115741B1 (ko) | 도금성이 우수한 고망간강 용융아연도금강판의 제조방법 | |
KR100985285B1 (ko) | 표면품질이 우수한 고강도 극저탄소 강판, 합금화용융아연도금 강판 및 그 제조방법 | |
JP2005272967A (ja) | めっき欠陥の少ない溶融Al系めっき鋼板の製造方法 | |
JP2003253416A (ja) | 合金化溶融亜鉛めっき鋼板 | |
KR20110087800A (ko) | 고망간 용융아연 열연도금강판, 용융아연도금강판 및 그 제조방법 | |
CN115109967B (zh) | 一种热浸镀高强钢板及其制备方法 | |
JP4702974B2 (ja) | 加工性に優れた合金化溶融亜鉛めっき高張力鋼板及びその製造方法 | |
JP2525165B2 (ja) | 高強度蒸着亜鉛めっき鋼板の製造方法 | |
KR101359161B1 (ko) | 내식성이 우수한 열간 프레스 성형용 도금강판 | |
JPH0688192A (ja) | 加工性に優れた合金化溶融亜鉛めっき鋼板及びその製造方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
A201 | Request for examination | ||
E902 | Notification of reason for refusal | ||
E701 | Decision to grant or registration of patent right | ||
GRNT | Written decision to grant | ||
FPAY | Annual fee payment |
Payment date: 20141020 Year of fee payment: 4 |
|
FPAY | Annual fee payment |
Payment date: 20151027 Year of fee payment: 5 |
|
FPAY | Annual fee payment |
Payment date: 20161027 Year of fee payment: 6 |
|
FPAY | Annual fee payment |
Payment date: 20171026 Year of fee payment: 7 |