JPH02140252A - 感光材料用包装材料 - Google Patents
感光材料用包装材料Info
- Publication number
- JPH02140252A JPH02140252A JP29238288A JP29238288A JPH02140252A JP H02140252 A JPH02140252 A JP H02140252A JP 29238288 A JP29238288 A JP 29238288A JP 29238288 A JP29238288 A JP 29238288A JP H02140252 A JPH02140252 A JP H02140252A
- Authority
- JP
- Japan
- Prior art keywords
- resin
- carbon black
- weight
- acid
- light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は、遮光性フィルム、遮光性フィルムパトローネ
容器、遮光性スプール、遮光性カセット、遮光性マガジ
ン等の着色成形品の黒色着色に用いられるマスターバッ
チ用樹脂組成物に関するものである。
容器、遮光性スプール、遮光性カセット、遮光性マガジ
ン等の着色成形品の黒色着色に用いられるマスターバッ
チ用樹脂組成物に関するものである。
一般に、感光材料用着色成形品に用いる熱可塑性樹脂を
着色成形加工するには、着色顔料や着色染料等の着色物
質を原料形状のまま熱可塑性樹脂に直接添加する方法、
又は着色物質を含有した樹脂形状がペレット、フレーク
、ビーズ、顆粒等を用いて着色する方法で行っていた。
着色成形加工するには、着色顔料や着色染料等の着色物
質を原料形状のまま熱可塑性樹脂に直接添加する方法、
又は着色物質を含有した樹脂形状がペレット、フレーク
、ビーズ、顆粒等を用いて着色する方法で行っていた。
上記直接添加する方法には、常温固体状の着色物質を用
いるドライカラー法、常温液体の着色物質を用いるリキ
ッドカラー法やペーストカラー法があり、ペレット等を
用いる方法には、高濃度の着色物質を含むペレットを用
いるマスターバッチ法(コンセンレート法)や、製品の
着色濃度と同量の着色物質をベース樹脂に配合し、この
樹脂組成物を混練造粒機で溶融混練した後ペレット化し
、このペレットをそのままの用いて着色樹脂製品を成形
するコンパウンド法があった。
いるドライカラー法、常温液体の着色物質を用いるリキ
ッドカラー法やペーストカラー法があり、ペレット等を
用いる方法には、高濃度の着色物質を含むペレットを用
いるマスターバッチ法(コンセンレート法)や、製品の
着色濃度と同量の着色物質をベース樹脂に配合し、この
樹脂組成物を混練造粒機で溶融混練した後ペレット化し
、このペレットをそのままの用いて着色樹脂製品を成形
するコンパウンド法があった。
そして、これらの着色方法はそれぞれ一長一短があり、
それぞれの特徴を生かして用いられているが、取扱いの
容易さ、使用時の飛散防止、着色成形品の製造コストの
低減等の点でマスターハツチ法が優れている。
それぞれの特徴を生かして用いられているが、取扱いの
容易さ、使用時の飛散防止、着色成形品の製造コストの
低減等の点でマスターハツチ法が優れている。
本出願人は特開昭63−186740号公報において、
新しい着色マスターバッチ用樹脂組成物を提案している
。
新しい着色マスターバッチ用樹脂組成物を提案している
。
〔発明が解決しようとする課題]
ところでマスターバッチ法に用いられるマスターバッチ
用樹脂組成物は、成形品(インフレーションフィルム成
形品、シート成形品、Tダイフィルム成形品、ブロー成
形品、射出成形品等)の着色コストの低減及び物性変化
を防止するために、成形品のベースレジンとして用いら
れる熱可塑性樹脂に対するマスターバッチ樹脂の配合割
合を少なくしても、得られた成形品が均一な濃度で十分
に着色されることが必要である。
用樹脂組成物は、成形品(インフレーションフィルム成
形品、シート成形品、Tダイフィルム成形品、ブロー成
形品、射出成形品等)の着色コストの低減及び物性変化
を防止するために、成形品のベースレジンとして用いら
れる熱可塑性樹脂に対するマスターバッチ樹脂の配合割
合を少なくしても、得られた成形品が均一な濃度で十分
に着色されることが必要である。
したがって、マスターハツチ樹脂中の着色物質としての
カーボンブラックの濃度を高める必要があるが、着色物
質の濃度を高めると分散性が劣り凝集し易くなり、均一
で、高品質の着色ができなかった。
カーボンブラックの濃度を高める必要があるが、着色物
質の濃度を高めると分散性が劣り凝集し易くなり、均一
で、高品質の着色ができなかった。
また、フィルム成形速度及び射出成形サイクルの短縮化
や成形品の薄肉化に伴い、使用するベースレジンの劣化
が少ない低い成形温度であっても、ベースレジンにマス
ターハツチ樹脂が短時間で十分に均一に分散されること
が要求される。
や成形品の薄肉化に伴い、使用するベースレジンの劣化
が少ない低い成形温度であっても、ベースレジンにマス
ターハツチ樹脂が短時間で十分に均一に分散されること
が要求される。
したがって、ベースレジンの成形温度におけるマスター
バッチ樹脂の流動性を高めることが必要であるが、マス
ターバッチ樹脂中のカーボンブラックの濃度を高(する
にしたがって、マスターバッチ樹脂の流動性が低くなり
、成形時にマスターバッチ樹脂が完全に分散せず成形品
に色むらが発生したり、感光材料用包装では、遮光性不
良により光カブリを発生したり、また成形機の温度や背
圧等の変動によって成形品の色が不安定になった。
バッチ樹脂の流動性を高めることが必要であるが、マス
ターバッチ樹脂中のカーボンブラックの濃度を高(する
にしたがって、マスターバッチ樹脂の流動性が低くなり
、成形時にマスターバッチ樹脂が完全に分散せず成形品
に色むらが発生したり、感光材料用包装では、遮光性不
良により光カブリを発生したり、また成形機の温度や背
圧等の変動によって成形品の色が不安定になった。
特に、ベースレジンの流動性が高い場合は、この傾向が
顕著であった。
顕著であった。
本発明は、以上の問題点を解消し、カーボンブラックを
高濃度で含有させても、カーボンブラックの分散及び分
配が十分で、遮光能力不足や、着色むら、ウェルドライ
ン等の外観不良が発生しない感光材料用マスターハツチ
用樹脂組成物を提供することを目的とする。
高濃度で含有させても、カーボンブラックの分散及び分
配が十分で、遮光能力不足や、着色むら、ウェルドライ
ン等の外観不良が発生しない感光材料用マスターハツチ
用樹脂組成物を提供することを目的とする。
本発明は上記目的を達成するためになされたもので、変
性ポリオレフィン樹脂を5〜90重量%、平均粒子径1
5〜120mμ、吸油量50m/100 g以上、揮発
成分が3.5%以下のカーボンブラックを5〜70重量
%含有することを特徴として構成されている。
性ポリオレフィン樹脂を5〜90重量%、平均粒子径1
5〜120mμ、吸油量50m/100 g以上、揮発
成分が3.5%以下のカーボンブラックを5〜70重量
%含有することを特徴として構成されている。
本発明において、変性ポリオレフィン樹脂とは、後述の
ポリオレフィン樹脂を不飽和カルボン酸もしくはその誘
導体で変性したものである。
ポリオレフィン樹脂を不飽和カルボン酸もしくはその誘
導体で変性したものである。
ポリオレフィン樹脂の代表例をあげると、高圧法分岐状
低密度ポリエチレン樹脂、中密度ポリエチレン樹脂、高
密度ポリエチレン樹脂、直鎖状低密度ポリエチレン樹脂
(エチレン・αオレフイン共重合体樹脂)、ホモポリプ
ロピレン樹脂、プロピレン・エチレンランダム共重合体
樹脂、プロピレン・エチレンブロック共重合体樹脂、プ
ロピレン・αオレフイン共重合体樹脂、エチレン酢酸ビ
ニル共重合体樹脂、エチレン・アクリル酸メチル共重合
体樹脂、エチレン・アクリル酸エチル共重合体樹脂、α
−オレフィン(ブテン−1、イソブチン、4メチルペン
テン−1、ヘキセン−1等)重合体樹脂等がある。
低密度ポリエチレン樹脂、中密度ポリエチレン樹脂、高
密度ポリエチレン樹脂、直鎖状低密度ポリエチレン樹脂
(エチレン・αオレフイン共重合体樹脂)、ホモポリプ
ロピレン樹脂、プロピレン・エチレンランダム共重合体
樹脂、プロピレン・エチレンブロック共重合体樹脂、プ
ロピレン・αオレフイン共重合体樹脂、エチレン酢酸ビ
ニル共重合体樹脂、エチレン・アクリル酸メチル共重合
体樹脂、エチレン・アクリル酸エチル共重合体樹脂、α
−オレフィン(ブテン−1、イソブチン、4メチルペン
テン−1、ヘキセン−1等)重合体樹脂等がある。
変性ポリオレフィン樹脂の製造に用いる変性剤である不
飽和カルボン酸の代表例をあげると、アクリル酸、メタ
クリル酸、クロトン酸、イソクロトン酸、フマル酸、マ
レイン酸、イタコン酸、シトラコン酸、ナジック酸、ハ
イミック酸、アンゲリカ酸、テトラヒドロフタル酸、ソ
ルビン酸、メサコン酸等がある。
飽和カルボン酸の代表例をあげると、アクリル酸、メタ
クリル酸、クロトン酸、イソクロトン酸、フマル酸、マ
レイン酸、イタコン酸、シトラコン酸、ナジック酸、ハ
イミック酸、アンゲリカ酸、テトラヒドロフタル酸、ソ
ルビン酸、メサコン酸等がある。
不飽和カルボン酸の誘導体の代表例としては、酸無水物
、エステル、アミド、イミド、酸ハライド、金属塩など
があり、無水マレイン酸、無水イタコン酸、無水シトラ
コン酸、無水ナジック酸、無水メチルナジック酸、無水
ハイミック酸、アクリル酸メチル、メタクリル酸メチル
、メタクリル酸エチル、アクリル酸エチル、アクリル酸
nブチル、アクリル酸グリシジル、メタクリル酸nブチ
ル、アクリル酸イソブチル、メタクリル酸イソブチル、
マレイン酸モノエチルエステル、マレイン酸ジエチルエ
ステル、フマル酸モノメチルエステル、フマル酸ジメチ
ルエステル、イタコン酸モノメチルエステル、イタコン
酸ジメチルエステル、アクリルアミド、メタクリルアミ
ド、マレイン酸モノアミド、マレイン酸ジアミド、フマ
ル酸モノアミド、フマル酸ジアミド、マレイミド、アク
リル酸ナトリウム、メタクリル酸ナトリウム、アクリル
酸カリウム、メタクリル酸カリウム等がある。
、エステル、アミド、イミド、酸ハライド、金属塩など
があり、無水マレイン酸、無水イタコン酸、無水シトラ
コン酸、無水ナジック酸、無水メチルナジック酸、無水
ハイミック酸、アクリル酸メチル、メタクリル酸メチル
、メタクリル酸エチル、アクリル酸エチル、アクリル酸
nブチル、アクリル酸グリシジル、メタクリル酸nブチ
ル、アクリル酸イソブチル、メタクリル酸イソブチル、
マレイン酸モノエチルエステル、マレイン酸ジエチルエ
ステル、フマル酸モノメチルエステル、フマル酸ジメチ
ルエステル、イタコン酸モノメチルエステル、イタコン
酸ジメチルエステル、アクリルアミド、メタクリルアミ
ド、マレイン酸モノアミド、マレイン酸ジアミド、フマ
ル酸モノアミド、フマル酸ジアミド、マレイミド、アク
リル酸ナトリウム、メタクリル酸ナトリウム、アクリル
酸カリウム、メタクリル酸カリウム等がある。
特に、無水マレイン酸が好ましい。
変性方法としては公知の種々の方法を採用することがで
きる。
きる。
例えば、有機過酸化物(ヘンシイルバーオキサイド、t
−ブチルパーベンゾエート、t−ブチルアセテ−1〜、
t−ブチルパーオキシイソプロピルカーボネート、2,
5−ジ−メチル−2,5−ジ(ヘンシイルバーオキシ)
ヘキサン、t−ブチル−ジ−パーアジペート、t−ブチ
ルパーオキシ3.5.5−トリメチルヘキサノエート、
メチルエチルケトンパーオキサイド、シクロヘキサノン
パーオキサイド、ジーも一ブチルパーオキサイド等、特
に2,5−ジ−メチル−2,5−ジ(tブチルパーオキ
シ)ヘキサン、2,5−メチル2.5−ジー(し−ブチ
ルパーオキシ)ヘキシン3、■、3−ビス−(t−ブチ
ルパーオキシイソプロビル)ベンセンが好ましい。
−ブチルパーベンゾエート、t−ブチルアセテ−1〜、
t−ブチルパーオキシイソプロピルカーボネート、2,
5−ジ−メチル−2,5−ジ(ヘンシイルバーオキシ)
ヘキサン、t−ブチル−ジ−パーアジペート、t−ブチ
ルパーオキシ3.5.5−トリメチルヘキサノエート、
メチルエチルケトンパーオキサイド、シクロヘキサノン
パーオキサイド、ジーも一ブチルパーオキサイド等、特
に2,5−ジ−メチル−2,5−ジ(tブチルパーオキ
シ)ヘキサン、2,5−メチル2.5−ジー(し−ブチ
ルパーオキシ)ヘキシン3、■、3−ビス−(t−ブチ
ルパーオキシイソプロビル)ベンセンが好ましい。
添加量はポリオレフィン樹脂100重量部に対して0.
001〜1.0重量部が一般的である。)の存在下で前
記ポリオレフィン樹脂と前記不飽和カルボン酸又はその
誘導体をポリオレフィン樹脂の融点以上の温度(通常は
150〜330°C)で溶融混練することによって行な
われる。このため各種の酸化防止剤を併用することがポ
リオレフィン樹脂の酸化劣化防止の点で好ましい。
001〜1.0重量部が一般的である。)の存在下で前
記ポリオレフィン樹脂と前記不飽和カルボン酸又はその
誘導体をポリオレフィン樹脂の融点以上の温度(通常は
150〜330°C)で溶融混練することによって行な
われる。このため各種の酸化防止剤を併用することがポ
リオレフィン樹脂の酸化劣化防止の点で好ましい。
該不飽和カルボン酸又はその誘導体の配合割合は、通常
原料樹脂であるポリオレフィン樹脂100重量部に対し
て0.01〜5重量部、より好ましいのは0.05〜3
重量部である。
原料樹脂であるポリオレフィン樹脂100重量部に対し
て0.01〜5重量部、より好ましいのは0.05〜3
重量部である。
酸化防止剤として好ましい代表例をあげると、2.6−
ジーt−ブチル−P−クレゾール(B I T )、4
ヒドロキシ−2,2,6,6−チトラメチルビヘリジン
、テ1〜ラキス(2,2,6,6−テトラメチル−4−
ビヘリジル)L2,3.4−ブタンテトラカルポキシレ
−1・、3.9−ビス〔1,1−ジメチル−2−(トリ
ス(1、2,2゜6.6−ベンタメチルー4−ピペリジ
ルオキシカルボニル)ブチルカルボニルオキシ)エチル
) −2,4゜8.10−テトラオキザスピロ(5,5
)ウンデカン、ビス(24−ジ−t−ブチルフェニル)
−ペンタエリスリトール−シフオスファイト、トリス(
2+4 ’;t−ブチルフェニル)フォスファイト、
ビス(2,6ジーt−ブチル−4−メチルフェニル)−
ペンタエリスリトール−シフオスファイト、n−オクタ
デシル−3−(3’ 、5’−ジ−t−ブチル4゛ヒド
ロキシフエニル)プロピオネート、2,6ジーt−ブチ
ル4−メチルフェノール、 1..13−)リス(2−
メチル−4−ヒドロキシ−5−t−ブチルフェニル)ブ
タン、L3,5+−ジメチル−2,4,6−)リス(3
15−ジt−ブチルー4−ヒドロキシヘンシル)ベンゼ
ン、テトラキス〔メチレン−3(3’、5’−ジ−t−
ヒドロキシフェニル)プロピオネートコメタン、ステア
リル−β−(3,5−ジ−t−ブチル−4−ヒドロキシ
フェニル)プロピオネート、トコフェロール類(ビタミ
ンE)等がある。
ジーt−ブチル−P−クレゾール(B I T )、4
ヒドロキシ−2,2,6,6−チトラメチルビヘリジン
、テ1〜ラキス(2,2,6,6−テトラメチル−4−
ビヘリジル)L2,3.4−ブタンテトラカルポキシレ
−1・、3.9−ビス〔1,1−ジメチル−2−(トリ
ス(1、2,2゜6.6−ベンタメチルー4−ピペリジ
ルオキシカルボニル)ブチルカルボニルオキシ)エチル
) −2,4゜8.10−テトラオキザスピロ(5,5
)ウンデカン、ビス(24−ジ−t−ブチルフェニル)
−ペンタエリスリトール−シフオスファイト、トリス(
2+4 ’;t−ブチルフェニル)フォスファイト、
ビス(2,6ジーt−ブチル−4−メチルフェニル)−
ペンタエリスリトール−シフオスファイト、n−オクタ
デシル−3−(3’ 、5’−ジ−t−ブチル4゛ヒド
ロキシフエニル)プロピオネート、2,6ジーt−ブチ
ル4−メチルフェノール、 1..13−)リス(2−
メチル−4−ヒドロキシ−5−t−ブチルフェニル)ブ
タン、L3,5+−ジメチル−2,4,6−)リス(3
15−ジt−ブチルー4−ヒドロキシヘンシル)ベンゼ
ン、テトラキス〔メチレン−3(3’、5’−ジ−t−
ヒドロキシフェニル)プロピオネートコメタン、ステア
リル−β−(3,5−ジ−t−ブチル−4−ヒドロキシ
フェニル)プロピオネート、トコフェロール類(ビタミ
ンE)等がある。
国内市販の変性ポリオレフィン樹脂の代表例としては下
記の商品があるが、本発明は、これらに限定されるもの
でなく世界中のものを使用できる。
記の商品があるが、本発明は、これらに限定されるもの
でなく世界中のものを使用できる。
MODIC(モディック)・・・三菱油化KK、 AD
MER(アトマー)・・・三井石油化学工業K K、
N0VATECΔP(ツバチックΔP)・・・三菱化成
KK、 IDEMITSUPLYTAC(出光ポリタッ
ク)・・・出光石油化学KK、MITSUI LONP
LY (三井ロンプライ)・・・三井東圧化学KK、ハ
イミラン(アイオノマー樹脂)・・・三井デュポンポリ
ケミカルKK等。
MER(アトマー)・・・三井石油化学工業K K、
N0VATECΔP(ツバチックΔP)・・・三菱化成
KK、 IDEMITSUPLYTAC(出光ポリタッ
ク)・・・出光石油化学KK、MITSUI LONP
LY (三井ロンプライ)・・・三井東圧化学KK、ハ
イミラン(アイオノマー樹脂)・・・三井デュポンポリ
ケミカルKK等。
変性ポリオレフィン樹脂として好ましい具体的代表樹脂
をあげると変性高圧法分岐状低密度ポリエチレン樹脂、
変性直鎖状低密度ポリエチレン樹脂(変性エチレン・α
オレフイン共重合体樹脂)、変性高密度ポリエチレン樹
脂、変性プロピレンエチレン共重合体樹脂(ブロック・
ランダムを含む)、変性ホモポリプロピレン樹脂、変性
エチレン・酢酸ビニル合重合体樹脂、変性エチレンアク
リル酸エチル共重合体樹脂等がある。
をあげると変性高圧法分岐状低密度ポリエチレン樹脂、
変性直鎖状低密度ポリエチレン樹脂(変性エチレン・α
オレフイン共重合体樹脂)、変性高密度ポリエチレン樹
脂、変性プロピレンエチレン共重合体樹脂(ブロック・
ランダムを含む)、変性ホモポリプロピレン樹脂、変性
エチレン・酢酸ビニル合重合体樹脂、変性エチレンアク
リル酸エチル共重合体樹脂等がある。
これらの変性ポリオレフィン樹脂のメルトインデックス
(ASTM 01238)は、カーボンブラックの分散
性から1 g/10分以上、好ましくは2 g/10分
以上、特に好ましいのは3 g/10分以上である。
(ASTM 01238)は、カーボンブラックの分散
性から1 g/10分以上、好ましくは2 g/10分
以上、特に好ましいのは3 g/10分以上である。
平均粒子径15〜120mμ、吸油量50m1/100
g以上、揮発成分が3.5%以下のカーボンブラックと
しては、グラファイト、ランプブラック、アセチレンブ
ラック、ボーンブラック、ファーネスブラック、チャン
ネルブラック、サーマルブラック等の公知のカーボンブ
ラックから分散性、写真感光材料に対する悪影響防止等
を考慮し上記の特性範囲のものを厳選して用いる。
g以上、揮発成分が3.5%以下のカーボンブラックと
しては、グラファイト、ランプブラック、アセチレンブ
ラック、ボーンブラック、ファーネスブラック、チャン
ネルブラック、サーマルブラック等の公知のカーボンブ
ラックから分散性、写真感光材料に対する悪影響防止等
を考慮し上記の特性範囲のものを厳選して用いる。
すなわち、平均粒子径が15 mp未満であると、分散
性が劣り、凝集し易くなり、均一で、高品質の着色が不
可能である。又ブツ(固型物)の発生が多くなり遮光性
フィルムではピンボールの発生が多くなる。
性が劣り、凝集し易くなり、均一で、高品質の着色が不
可能である。又ブツ(固型物)の発生が多くなり遮光性
フィルムではピンボールの発生が多くなる。
また、120mμを越えると、遮光能力が低下し、且つ
高価になる。
高価になる。
吸油量が50d/100g未満であると、カーボンブラ
ックが樹脂中に分散しにくくなり、ブツが発生しやすく
なる。
ックが樹脂中に分散しにくくなり、ブツが発生しやすく
なる。
揮発分が3.5%をこえると、写真感光材料の品質を劣
化させ、カブリや感光度の増減等の故障となる。さらに
成形品に銀条や発泡等の故障が発生する。
化させ、カブリや感光度の増減等の故障となる。さらに
成形品に銀条や発泡等の故障が発生する。
そして、このようなカーボンブラックは5〜50重量%
郡部れている。
郡部れている。
5重量%未満では製品着色がコスト高になり、50重量
%をこえるとカーボンブラックの分散性が悪化しブツの
発生が多くなる。又マスターバッチの流動性が大巾に低
下する。
%をこえるとカーボンブラックの分散性が悪化しブツの
発生が多くなる。又マスターバッチの流動性が大巾に低
下する。
国内のカーボンブラックの代表的供給メーカーを示すと
、三菱化成工業K K (MITSUBISIII C
HEMrC八1、INへUSTRIES LTD)、旭
カーボンKK(八5AHI CへRBON Co、 L
TD)、東海カーボンK K (TOKAT CARB
ON Co、 LTD)、昭和キャボットK K (S
IIOWA CABOT)FK)、電気化学工業K K
(DENKI KAGAKU KOCYD KK)、
化炭カーボンK K (IIOKUTAN CARBO
N Go、 LTD)、日鉄化学工業K K (NIT
TETSU CIIEMICAL INDUSTRI計
Co、 LTD)、東洋コンチネンタルカーボン有限会
社(TOYOC0NTINENTAL CARBON
LTD)等がある。
、三菱化成工業K K (MITSUBISIII C
HEMrC八1、INへUSTRIES LTD)、旭
カーボンKK(八5AHI CへRBON Co、 L
TD)、東海カーボンK K (TOKAT CARB
ON Co、 LTD)、昭和キャボットK K (S
IIOWA CABOT)FK)、電気化学工業K K
(DENKI KAGAKU KOCYD KK)、
化炭カーボンK K (IIOKUTAN CARBO
N Go、 LTD)、日鉄化学工業K K (NIT
TETSU CIIEMICAL INDUSTRI計
Co、 LTD)、東洋コンチネンタルカーボン有限会
社(TOYOC0NTINENTAL CARBON
LTD)等がある。
本発明のマスターバッチ用樹脂組成物には、変性ポリオ
レフィン樹脂に他の各種の熱可塑性樹脂や、ベースレジ
ンと同一の樹脂を含めることができる。
レフィン樹脂に他の各種の熱可塑性樹脂や、ベースレジ
ンと同一の樹脂を含めることができる。
このベースレジンとは、マスターハツチ樹脂とブレンド
して着色される成形品の主成分となる熱可塑性樹脂で、
特開昭63−186740号公報等に記載されている。
して着色される成形品の主成分となる熱可塑性樹脂で、
特開昭63−186740号公報等に記載されている。
例えば、直鎖状低密度ポリエチレン樹脂、LDPE樹脂
、EVA樹脂、EEA樹脂、EAA樹脂、変性ポリエチ
レン樹脂、変性ポリプロピレン樹脂、アイオノマー樹脂
、ホモポリプロピレン樹BN、プロピレン−αオレフイ
ンランダム共重合体樹脂、プロピレン−αオレフインブ
ロック共重合体樹脂、超低密度ポリエチレン樹脂、MD
PE樹脂、HD P E樹脂、ポリスチレン樹脂、塩化
ビニル樹脂、塩化ビニリデン樹脂、ABS樹脂、ポリビ
ニルアルコール樹脂、エチレン−酢酸ビニル共重合体ケ
ン化物、ポリカーボネート樹脂、ポリアミド樹脂、ポリ
エステル樹脂、等従来感光物質用包装材料に用いられて
いる樹脂を選択して使用することができる。特に各種直
鎖状ポリエチレン樹脂、LDPE樹脂、HD P E樹
脂、EEA樹脂、各種ポリプロピレン樹脂、各種ポリス
チレン樹脂が写真感光材料用として多く用いられている
。
、EVA樹脂、EEA樹脂、EAA樹脂、変性ポリエチ
レン樹脂、変性ポリプロピレン樹脂、アイオノマー樹脂
、ホモポリプロピレン樹BN、プロピレン−αオレフイ
ンランダム共重合体樹脂、プロピレン−αオレフインブ
ロック共重合体樹脂、超低密度ポリエチレン樹脂、MD
PE樹脂、HD P E樹脂、ポリスチレン樹脂、塩化
ビニル樹脂、塩化ビニリデン樹脂、ABS樹脂、ポリビ
ニルアルコール樹脂、エチレン−酢酸ビニル共重合体ケ
ン化物、ポリカーボネート樹脂、ポリアミド樹脂、ポリ
エステル樹脂、等従来感光物質用包装材料に用いられて
いる樹脂を選択して使用することができる。特に各種直
鎖状ポリエチレン樹脂、LDPE樹脂、HD P E樹
脂、EEA樹脂、各種ポリプロピレン樹脂、各種ポリス
チレン樹脂が写真感光材料用として多く用いられている
。
各種ポリプロピレン樹脂の代表例を以下に示す。
(1)プロピレンホモポリマー
(2)プロピレン−エチレンブロック共重合体樹脂(3
)プロピレン−エチレンランダム共重合体樹脂(4)プ
ロピレン−αオレフインブロック共重合体樹脂 (5)プロピレン−αオレフインランダム共重合体樹脂 上記各種ポリプロピレン樹脂と他の代表的ブレンド樹脂 (6)各種ポリエチレン樹脂とのブレンド樹脂(7)各
種の無機フィラーとのブレンド樹脂(8)各種無水マレ
イン酸等の不飽和カルボン酸等により1部あるいは全部
と変性した樹脂(9)各種造核剤とのブレンド樹脂 (10)各種遮光性物質とのブレンド樹脂(11)各種
ゴム(EPRXEPDM等)とのブレンド樹脂 (12)上記以外の各種熱可塑性樹脂とのブレンド樹脂 (13)上記以外の各種添加剤(滑剤、分散剤等)との
ブレンド樹脂 このようなベースレジンと同一の樹脂は、90重重量以
内含まれることが好ましい。90重量%を越えると、ベ
ースレジンが変性ポリオレフィン樹脂でないかぎり、カ
ーボンブラックの分散性の良好な変性ポリオレフィン樹
脂量が5重量%未満になるため、カーボンブラックの分
散性が悪化しブツが発生したりピンホールが発生して、
インフレーションフィルム成形等では製造が困難になる
。さらにカーボンブラックの分散性が悪化した結果、遮
光性が完全に確保できなくなったり、外観を悪化させて
商品価値を低下させる。
)プロピレン−エチレンランダム共重合体樹脂(4)プ
ロピレン−αオレフインブロック共重合体樹脂 (5)プロピレン−αオレフインランダム共重合体樹脂 上記各種ポリプロピレン樹脂と他の代表的ブレンド樹脂 (6)各種ポリエチレン樹脂とのブレンド樹脂(7)各
種の無機フィラーとのブレンド樹脂(8)各種無水マレ
イン酸等の不飽和カルボン酸等により1部あるいは全部
と変性した樹脂(9)各種造核剤とのブレンド樹脂 (10)各種遮光性物質とのブレンド樹脂(11)各種
ゴム(EPRXEPDM等)とのブレンド樹脂 (12)上記以外の各種熱可塑性樹脂とのブレンド樹脂 (13)上記以外の各種添加剤(滑剤、分散剤等)との
ブレンド樹脂 このようなベースレジンと同一の樹脂は、90重重量以
内含まれることが好ましい。90重量%を越えると、ベ
ースレジンが変性ポリオレフィン樹脂でないかぎり、カ
ーボンブラックの分散性の良好な変性ポリオレフィン樹
脂量が5重量%未満になるため、カーボンブラックの分
散性が悪化しブツが発生したりピンホールが発生して、
インフレーションフィルム成形等では製造が困難になる
。さらにカーボンブラックの分散性が悪化した結果、遮
光性が完全に確保できなくなったり、外観を悪化させて
商品価値を低下させる。
カーボンブラックの分散性と良くするために、マスター
ハツチ用樹脂組成物中にポリオレフィンワックスを含有
させることが好ましい。
ハツチ用樹脂組成物中にポリオレフィンワックスを含有
させることが好ましい。
ポリオレフィンワックスとしては、直鎖状低密度ポリエ
チレンワックス、分岐状低密度ポリエチレンワックス、
ポリプロピレンワックス、パラフィンワックス、ポリイ
ソブチレンワックス、カルボン酸含有ポリオレフィンワ
ックス、ポリオレフィンワックス等でその分子量が50
0〜20,000のものが特に好ましい。
チレンワックス、分岐状低密度ポリエチレンワックス、
ポリプロピレンワックス、パラフィンワックス、ポリイ
ソブチレンワックス、カルボン酸含有ポリオレフィンワ
ックス、ポリオレフィンワックス等でその分子量が50
0〜20,000のものが特に好ましい。
このようなポリオレフィンワックスは70重量%以内含
まれることが好ましい。70重重量を越えると、カーボ
ンブラックを高濃度に含むマスターバッチ用樹脂ペレッ
ト化が困難になる。
まれることが好ましい。70重重量を越えると、カーボ
ンブラックを高濃度に含むマスターバッチ用樹脂ペレッ
ト化が困難になる。
成形性向上、成形品の良好な離形性、カーボンブラック
のベースレジンへの均一な分散性付与、金型の腐蝕防止
等の為に、高級脂肪酸及び/又は高級脂肪酸化合物を含
有することが好ましい。
のベースレジンへの均一な分散性付与、金型の腐蝕防止
等の為に、高級脂肪酸及び/又は高級脂肪酸化合物を含
有することが好ましい。
高級脂肪酸としては、特に好ましい代表例をあげると、
ステアリン酸、オレイン酸、バルミチン酸、ヘヘニン酸
、ラウリン酸、リルン酸、エルカ酸、等の炭素数が6〜
34個、好ましくは10〜23個の飽和脂肪酸や不飽和
脂肪酸がある。
ステアリン酸、オレイン酸、バルミチン酸、ヘヘニン酸
、ラウリン酸、リルン酸、エルカ酸、等の炭素数が6〜
34個、好ましくは10〜23個の飽和脂肪酸や不飽和
脂肪酸がある。
高級脂肪酸の化合物(金属石けん等)としては上記高級
脂肪酸とマグネシウム、亜鉛、カルシウム、ナトリウム
、バリウム、アルミニウム等の化合物、及び脂肪酸アミ
ド等の滑性効果の優れた高級脂肪酸化合物、例えばオレ
イン酸アミド、エルカ酸アミド、ステアリン酸アミド、
エチレン・ビス・ステアロアミド、ビス脂肪酸アミド等
がある。
脂肪酸とマグネシウム、亜鉛、カルシウム、ナトリウム
、バリウム、アルミニウム等の化合物、及び脂肪酸アミ
ド等の滑性効果の優れた高級脂肪酸化合物、例えばオレ
イン酸アミド、エルカ酸アミド、ステアリン酸アミド、
エチレン・ビス・ステアロアミド、ビス脂肪酸アミド等
がある。
このような高級脂肪酸及び/又は高級脂肪酸化合物は、
10重量%以内含まれることが好ましい。
10重量%以内含まれることが好ましい。
10重量%を越えると、ブリードアウトして写真感光材
料や食品や医薬品等被包装物に付着して種々のトラブル
を発生させる(例えば、写真感光材料では現像阻害等を
起こす。)。
料や食品や医薬品等被包装物に付着して種々のトラブル
を発生させる(例えば、写真感光材料では現像阻害等を
起こす。)。
さらにスクリューと樹脂間でスリップが発生し一定量の
樹脂の押出しが不可能になる。滑性の優れているオレイ
ン酸アミド等は1重量%以下が好ましい。
樹脂の押出しが不可能になる。滑性の優れているオレイ
ン酸アミド等は1重量%以下が好ましい。
本発明のマスターバッチ用樹脂組成物には、本発明の効
果を損なわない範囲で、以下に記載する各種添加剤を加
えてもよい。
果を損なわない範囲で、以下に記載する各種添加剤を加
えてもよい。
(添加剤種類) (代 表 例)(1)可塑剤
;フタル酸エステル、グリコールエステル、脂肪酸
エステル、リ ン酸エステル等 (2)安定剤 ;鉛系、カドミウム系、亜鉛系、アル
カリ土類金属系、有機スズ 系等 (3)帯電防止剤;陽イオン活性剤、アニオン活性剤、
非イオン活性剤、両面活性 剤等 (4)難燃剤 ;燐酸エステル、ハロゲン化燐酸エス
テル、ハロゲン化物、無機 物、含燐ポリオール等 (5)充填剤 ;アルミナ、カオリン、クレー炭酸カ
ルシウム、マイカ、タル ク、酸化チタン、シリカ等 (6)補強剤 ;ガラスロービング、金属繊維、ガラ
ス繊維、ガラスミルドファ イバー、炭素繊維等 (7)着色剤 ;無機顔料(AI、Fe2O3+Ti
0z+ZnO。
;フタル酸エステル、グリコールエステル、脂肪酸
エステル、リ ン酸エステル等 (2)安定剤 ;鉛系、カドミウム系、亜鉛系、アル
カリ土類金属系、有機スズ 系等 (3)帯電防止剤;陽イオン活性剤、アニオン活性剤、
非イオン活性剤、両面活性 剤等 (4)難燃剤 ;燐酸エステル、ハロゲン化燐酸エス
テル、ハロゲン化物、無機 物、含燐ポリオール等 (5)充填剤 ;アルミナ、カオリン、クレー炭酸カ
ルシウム、マイカ、タル ク、酸化チタン、シリカ等 (6)補強剤 ;ガラスロービング、金属繊維、ガラ
ス繊維、ガラスミルドファ イバー、炭素繊維等 (7)着色剤 ;無機顔料(AI、Fe2O3+Ti
0z+ZnO。
CdS等)、有機顔料染料等
(8)発泡剤 ;無機発泡剤(炭酸アンモニア、重炭
酸ソーダ)、有機発泡剤 にトロソ系、アゾ系)等 (9)加硫剤 ;加硫促進剤、促進助剤等(10)劣
化防止剤;紫外線吸収剤、金属不活性化剤、過酸化物分
解剤等 (11)造核剤 ;各種有機造核剤、各種無機造核剤
等 (12)カップリング剤;シラン系、チタネート系、ク
ロム系、アルミニウム系等 (13)各種の熱可塑性樹脂、エラス1〜マー、ゴム等
本発明のマスターハツチ用樹脂組成物は、全量をバンバ
リーミキサ−、ニーター、2本ロール、又は3本ロール
等の混練機で混練した後、単軸又は2軸押出機等でペレ
ット化する方法や、カーボンブラックとポリオレフィン
ワックスと高級脂肪酸及び/又は高級脂肪酸化合物を上
記混練機で混練した後、変性ポリオレフィン樹脂とベー
スレジンを加えてペレット化する方法等従来公知の各種
の方法により製造される。
酸ソーダ)、有機発泡剤 にトロソ系、アゾ系)等 (9)加硫剤 ;加硫促進剤、促進助剤等(10)劣
化防止剤;紫外線吸収剤、金属不活性化剤、過酸化物分
解剤等 (11)造核剤 ;各種有機造核剤、各種無機造核剤
等 (12)カップリング剤;シラン系、チタネート系、ク
ロム系、アルミニウム系等 (13)各種の熱可塑性樹脂、エラス1〜マー、ゴム等
本発明のマスターハツチ用樹脂組成物は、全量をバンバ
リーミキサ−、ニーター、2本ロール、又は3本ロール
等の混練機で混練した後、単軸又は2軸押出機等でペレ
ット化する方法や、カーボンブラックとポリオレフィン
ワックスと高級脂肪酸及び/又は高級脂肪酸化合物を上
記混練機で混練した後、変性ポリオレフィン樹脂とベー
スレジンを加えてペレット化する方法等従来公知の各種
の方法により製造される。
本発明のマスターパッチ用樹脂組成物は、前記ベースレ
ジンと配合され、各種の溶融成形法、例えば射出成形法
、圧縮成形法、回転成形法、押出成形法(T−グイ法、
中空成形法、バイブ押出法、異形ダイ押出法、インフレ
ーションフィルム成形法等)により、各種の着色された
感光材料用包装材料、支°持体等の製品、特に写真感光
材料用包装材料に用いられる。
ジンと配合され、各種の溶融成形法、例えば射出成形法
、圧縮成形法、回転成形法、押出成形法(T−グイ法、
中空成形法、バイブ押出法、異形ダイ押出法、インフレ
ーションフィルム成形法等)により、各種の着色された
感光材料用包装材料、支°持体等の製品、特に写真感光
材料用包装材料に用いられる。
この感光材料用包装材料の代表例を以下に示すが本発明
は、これらに限定されず各種の用途に有効に用いられる
。
は、これらに限定されず各種の用途に有効に用いられる
。
1、マガジン、インスタントフィルムバック、プラスチ
ックパトローネ、カセッ1−、カートリッジ 2、スプール、リール、コア、巻芯、巻芯補強キャップ 3、遮光紙、リーダーペーパー、顔料塗工紙、中性紙、
無塵紙、合成紙、不織布 4、インスタントフィルムユニット(感材組立物)5、
紙箱(インロー型、舟首嵌合型、e tc)、段ボール
箱 6、遮光袋(平袋、自立袋、ガゼツト袋e tc)7、
緩衝材(挟紙、発泡シート、エアキャップ、保護あて紙
) 8、接着剤、粘着剤、ボットメルト、接合剤、粘着テー
プ 9、防湿材、防水材 10、マーキング材(インク、ラヘルetc)11、イ
ンフレーションフィルム、Tダイフィルム、キヤステン
グフィルム、エクストルージョンコートフィルム、スト
レッチフィルム、−軸延伸フィルム、二軸延伸フィルム 12、積層フィルム、共押出しフィルム、ブロッキンク
積層フィルム、クロスラミネートフィルム13、段ボー
ル 14、遮光材(リボン、カーテン、遮光フィルム、遮光
パッド) 15、プラスチックケース(フィルムパトローネ用容器
とキャップ、マイクロフィルム用ヒンジ付ケース、映画
用プラスチックケース) その他、特開昭63−186740号公報記載の磁気材
料、電気製品用成形品等の包装材料用にも適用可能であ
る。
ックパトローネ、カセッ1−、カートリッジ 2、スプール、リール、コア、巻芯、巻芯補強キャップ 3、遮光紙、リーダーペーパー、顔料塗工紙、中性紙、
無塵紙、合成紙、不織布 4、インスタントフィルムユニット(感材組立物)5、
紙箱(インロー型、舟首嵌合型、e tc)、段ボール
箱 6、遮光袋(平袋、自立袋、ガゼツト袋e tc)7、
緩衝材(挟紙、発泡シート、エアキャップ、保護あて紙
) 8、接着剤、粘着剤、ボットメルト、接合剤、粘着テー
プ 9、防湿材、防水材 10、マーキング材(インク、ラヘルetc)11、イ
ンフレーションフィルム、Tダイフィルム、キヤステン
グフィルム、エクストルージョンコートフィルム、スト
レッチフィルム、−軸延伸フィルム、二軸延伸フィルム 12、積層フィルム、共押出しフィルム、ブロッキンク
積層フィルム、クロスラミネートフィルム13、段ボー
ル 14、遮光材(リボン、カーテン、遮光フィルム、遮光
パッド) 15、プラスチックケース(フィルムパトローネ用容器
とキャップ、マイクロフィルム用ヒンジ付ケース、映画
用プラスチックケース) その他、特開昭63−186740号公報記載の磁気材
料、電気製品用成形品等の包装材料用にも適用可能であ
る。
〔作用]
本発明のマスターハツチ用樹脂組成物では、カーボンブ
ラックの濃度を高くしてもマスターパッチ用樹脂組成物
の流動性が良く、ベースレジンと短時間で均一に分散し
、カーボンブラックによる均一な着色が行なわれる。
ラックの濃度を高くしてもマスターパッチ用樹脂組成物
の流動性が良く、ベースレジンと短時間で均一に分散し
、カーボンブラックによる均一な着色が行なわれる。
実施例1
(1)変性ポリオレフィン樹脂(三井石油化学工業KK
製変性EVA樹脂rADMERVE 300J M I
9.08710分、密度0.95g/cJ )
39.7重量%(2)平均粒子径21mμ、
9118.0、吸油量76mf/100g、揮発分0.
8重量%のファーネスカーボンブラック「三菱カラー用
カーボンブラック#44」40重量%(3) L〜1、
叶Eワックス(分子量約2,000) 20重量%(
4)ステアリン酸カルシウム 0.3重量%上記
(1)〜(4)を高速混合機で十分混合した後、得られ
た混合物を池貝鉄工製二軸押出機(POM 30)でス
トランド状に押出し、ペレタイザーにより粒状(ベレッ
ト)化し、カーボンブラック含有量40重量%のカーボ
ンブラックマスターパッチ用樹脂組成物を得た。
製変性EVA樹脂rADMERVE 300J M I
9.08710分、密度0.95g/cJ )
39.7重量%(2)平均粒子径21mμ、
9118.0、吸油量76mf/100g、揮発分0.
8重量%のファーネスカーボンブラック「三菱カラー用
カーボンブラック#44」40重量%(3) L〜1、
叶Eワックス(分子量約2,000) 20重量%(
4)ステアリン酸カルシウム 0.3重量%上記
(1)〜(4)を高速混合機で十分混合した後、得られ
た混合物を池貝鉄工製二軸押出機(POM 30)でス
トランド状に押出し、ペレタイザーにより粒状(ベレッ
ト)化し、カーボンブラック含有量40重量%のカーボ
ンブラックマスターパッチ用樹脂組成物を得た。
このマスターハツチ用樹脂ペレッl−7,5重量%と、
M 12.1g/10分、密度0.920g/cJのL
−L DPE樹脂ベレッl〜([ウルトゼックス20
21LJ三井石油化学製) 92.5重量%をよく混合
した樹脂ペレットをインフレーションフィルム成形機(
プラコー製100mmφリングダイ)を用いてカーボン
濃度3重量%の厚さ501Mの遮光フィルムを成形した
。
M 12.1g/10分、密度0.920g/cJのL
−L DPE樹脂ベレッl〜([ウルトゼックス20
21LJ三井石油化学製) 92.5重量%をよく混合
した樹脂ペレットをインフレーションフィルム成形機(
プラコー製100mmφリングダイ)を用いてカーボン
濃度3重量%の厚さ501Mの遮光フィルムを成形した
。
その結果カーボンブラックの分散がよく、均一に着色さ
れた各種写真感光材料に悪影響を及ぼさない遮光性、物
理強度、ヒートシール適性、フィルム成形性の優れた、
ブッやフィッシュアイ、ピンホールの少ない、帯電防止
性も有する防湿・遮光袋用として最適の遮光性インフレ
ーションフィルムが得られた。
れた各種写真感光材料に悪影響を及ぼさない遮光性、物
理強度、ヒートシール適性、フィルム成形性の優れた、
ブッやフィッシュアイ、ピンホールの少ない、帯電防止
性も有する防湿・遮光袋用として最適の遮光性インフレ
ーションフィルムが得られた。
実施例2
実施例1と同一のカーボンブラックマスターハツチ樹脂
ペレット0.5重量%と、MIが25g/10分、密度
が0.926g/c+flのLD P E樹脂ペレット
99.5重量%をよく混合した樹脂ペレットを用い、東
芝機械■製成形機はrls 75EJ型絞圧75t、金
型は取り数2個のホットランナ−タイプで写真フィルム
パトロニネ用容器キャップ(特開昭63−193143
号公報第2図相当)を射出成形した。その結果カーボン
ブラックの分散がよく、均一に着色された射出成形性の
優れた、パトローネ人撮影用ネガ写真フィルム(フジカ
ラーHR100)にカブリ等の悪影響を及ぼさない黒色
写真フィルムパトローネ用容器キャップが得られた。
ペレット0.5重量%と、MIが25g/10分、密度
が0.926g/c+flのLD P E樹脂ペレット
99.5重量%をよく混合した樹脂ペレットを用い、東
芝機械■製成形機はrls 75EJ型絞圧75t、金
型は取り数2個のホットランナ−タイプで写真フィルム
パトロニネ用容器キャップ(特開昭63−193143
号公報第2図相当)を射出成形した。その結果カーボン
ブラックの分散がよく、均一に着色された射出成形性の
優れた、パトローネ人撮影用ネガ写真フィルム(フジカ
ラーHR100)にカブリ等の悪影響を及ぼさない黒色
写真フィルムパトローネ用容器キャップが得られた。
実施例3
実施例1と同一のカーボンブラックマスターハツチ樹脂
ペレット2.5重量%と、Mlが40g/10分、密度
が0.900g/crfi、エチレン含有量が2重量%
のプロピレン−エチレンランダム共重合体樹脂97.3
重量%と有機造核剤(ジベンジリデンソルビトール化合
物)0.2重量%をよく混合した樹脂ペレットを用い、
成形機として住人重機製[ネスクールJ、型紋圧150
t、金型は取り数24個のホットランナ−タイプで円筒
状に側壁平均厚さが0.7mm、カーボンブラック含有
量が0.4重量%の写真フィルムパトローネ用容器本体
(特開昭63−204252号公報第1図相当)を成形
した。その結果均一に着色された、ウェルドラインの発
生が少ない、ショートショット、糸ヒキ、ゲート跡の発
生が少ないパトローネ人撮影用ネガ写真フィルム(フジ
カラーIll?100)にカブリ等の悪影響を及ぼさな
い黒色写真フィルムパj・ローネ用容器本体が得られた
。
ペレット2.5重量%と、Mlが40g/10分、密度
が0.900g/crfi、エチレン含有量が2重量%
のプロピレン−エチレンランダム共重合体樹脂97.3
重量%と有機造核剤(ジベンジリデンソルビトール化合
物)0.2重量%をよく混合した樹脂ペレットを用い、
成形機として住人重機製[ネスクールJ、型紋圧150
t、金型は取り数24個のホットランナ−タイプで円筒
状に側壁平均厚さが0.7mm、カーボンブラック含有
量が0.4重量%の写真フィルムパトローネ用容器本体
(特開昭63−204252号公報第1図相当)を成形
した。その結果均一に着色された、ウェルドラインの発
生が少ない、ショートショット、糸ヒキ、ゲート跡の発
生が少ないパトローネ人撮影用ネガ写真フィルム(フジ
カラーIll?100)にカブリ等の悪影響を及ぼさな
い黒色写真フィルムパj・ローネ用容器本体が得られた
。
実施例4
実施例1と同一のカーボンブラックマスターハツチ樹脂
ペレット2.5重量%と実施例3と同じMIが40g/
10分、密度が0.900g/cIII、 xチレン含
有量が2重量%のプロピレン−エチレンランダム共重合
体樹脂87.3重量%と、MlがLog/10分、密度
力0.925g/cn!のエチレン−4メチルペンテン
−Iよりなる直鎖状低密度ポリエチレン(三井石油化学
製LIZ 25100J) 10重量%と有機造核剤(
ジベンジリデンソルビトール化合物)0.2重量%をよ
く混合した樹脂ペレットを用い成形機として住友重機「
ネスクール」、型紋圧150t、金型は取り数2個のコ
ールドランナータイプでマイクロフィルム収納ケース(
実開昭54−100617号公報第3図相当)を射出成
形法で成形した。その結果ソリ、ウェルドライン、ヒケ
の少ない、ショートショットが発生しない均一に着色さ
れた遮光性と密封嵌合性の優れた離型性のよい商品価値
の高い、マイクロフィルムやインスタントフィルム等の
写真感光材料収納に最適のヒンジ付遮光性収納ケースが
得られた。
ペレット2.5重量%と実施例3と同じMIが40g/
10分、密度が0.900g/cIII、 xチレン含
有量が2重量%のプロピレン−エチレンランダム共重合
体樹脂87.3重量%と、MlがLog/10分、密度
力0.925g/cn!のエチレン−4メチルペンテン
−Iよりなる直鎖状低密度ポリエチレン(三井石油化学
製LIZ 25100J) 10重量%と有機造核剤(
ジベンジリデンソルビトール化合物)0.2重量%をよ
く混合した樹脂ペレットを用い成形機として住友重機「
ネスクール」、型紋圧150t、金型は取り数2個のコ
ールドランナータイプでマイクロフィルム収納ケース(
実開昭54−100617号公報第3図相当)を射出成
形法で成形した。その結果ソリ、ウェルドライン、ヒケ
の少ない、ショートショットが発生しない均一に着色さ
れた遮光性と密封嵌合性の優れた離型性のよい商品価値
の高い、マイクロフィルムやインスタントフィルム等の
写真感光材料収納に最適のヒンジ付遮光性収納ケースが
得られた。
実施例5
実施例1のカーボンブラックマスターハツチ樹脂組成物
中の(1)の変性ポリオレフィン樹脂として無水マレイ
ン酸グラフト変性ポリエチレン樹脂MI Log/10
分、密度0.92g/cイを用いた他は同一の樹脂組成
、同一インフレーションフィルム成形機を用いてカーボ
ンブラック濃度3重量%、厚さ50庫の遮光フィルムを
成形した。その結果カーボンブラックの分散がよく、均
一に着色された各種写真感光材料にカブリ等の悪影響を
及ぼさない、遮光性、物理強度、フィルム成形性、ヒー
トシール適性の優れた、ブツの発生が少ない、フィンシ
ュアイやピンホールの発生しない、帯電防止性も有する
防湿・遮光袋用として最適の遮光性インフレーションフ
ィルムが得られた。このマスターバッチ樹脂組成物を実
施例2〜4の各種成形品に適用した結果、成形性、均一
着色性、物理強度、外観の優れた製品が得られた。
中の(1)の変性ポリオレフィン樹脂として無水マレイ
ン酸グラフト変性ポリエチレン樹脂MI Log/10
分、密度0.92g/cイを用いた他は同一の樹脂組成
、同一インフレーションフィルム成形機を用いてカーボ
ンブラック濃度3重量%、厚さ50庫の遮光フィルムを
成形した。その結果カーボンブラックの分散がよく、均
一に着色された各種写真感光材料にカブリ等の悪影響を
及ぼさない、遮光性、物理強度、フィルム成形性、ヒー
トシール適性の優れた、ブツの発生が少ない、フィンシ
ュアイやピンホールの発生しない、帯電防止性も有する
防湿・遮光袋用として最適の遮光性インフレーションフ
ィルムが得られた。このマスターバッチ樹脂組成物を実
施例2〜4の各種成形品に適用した結果、成形性、均一
着色性、物理強度、外観の優れた製品が得られた。
実施例6
実施例1のカーボンブラックマスターパッチ樹脂組成物
中に(1)の変性ポリオレフィン樹脂として変性L−L
DPE樹脂(三井石油化学工業KK製rADMERNE
050J M I 3.5g/10分、密度0.93
g/c+fl)を用いた他は同一の樹脂組成、同一イン
フレーションフィルム成形機を用いてカーボンブラック
濃度3重量%、厚さ50Jmの遮光性フィルムを成形し
た。その結果カーボンブラックの分散性がよく、均一に
着色された各種写真感光材料に悪影響を及ぼさない遮光
性、物理強度、フィルム成形性、ヒートシール適性の優
れた、ブツの発生が少ない、フィッシュアイやピンホー
ルの発生しない、帯電防止性も有する防湿・遮光袋用と
して最適の遮光性インフレーションフィルムが得られた
。このマスターバッチ樹脂組成物を実施例2〜4の各種
成形品に適′用した結果、成形性、均一着色性、物理強
度、外観に優れた製品が得られた。
中に(1)の変性ポリオレフィン樹脂として変性L−L
DPE樹脂(三井石油化学工業KK製rADMERNE
050J M I 3.5g/10分、密度0.93
g/c+fl)を用いた他は同一の樹脂組成、同一イン
フレーションフィルム成形機を用いてカーボンブラック
濃度3重量%、厚さ50Jmの遮光性フィルムを成形し
た。その結果カーボンブラックの分散性がよく、均一に
着色された各種写真感光材料に悪影響を及ぼさない遮光
性、物理強度、フィルム成形性、ヒートシール適性の優
れた、ブツの発生が少ない、フィッシュアイやピンホー
ルの発生しない、帯電防止性も有する防湿・遮光袋用と
して最適の遮光性インフレーションフィルムが得られた
。このマスターバッチ樹脂組成物を実施例2〜4の各種
成形品に適′用した結果、成形性、均一着色性、物理強
度、外観に優れた製品が得られた。
実施例7
(1)変性ポリオレフィン樹脂として、三菱油化KK製
変性PP樹脂(rMODIc P−300MJ M 1
10g/10分、密度0.89g/c[)
29.5重量%(2)平均粒子径20mp
、pH8,0、吸油量110mfi/100g、揮発分
0.8重量%のファーネスカーボンブラック「三菱カラ
ー用カーボンブラック#40J 40重量%(3)三井
石油化学KK製低密度ポリエチレンワックス「ハイワッ
クス4400GJ (分子量約4,000)20重量% (4)ステアリン酸亜鉛 0.3重量%オ
レイン酸アミド 0.2重量%上記(1)
〜(4)を高速混合機で十分混合した後得られた混合物
を池貝鉄工製二軸押出機rPOM 30Jでストランド
状に押出し、ペレタイザーにより粒状(ペレット)化し
、カーボンブラック含有量40重量%のペレット状のカ
ーボンブラックマスターバッチ樹脂組成物を得た。
変性PP樹脂(rMODIc P−300MJ M 1
10g/10分、密度0.89g/c[)
29.5重量%(2)平均粒子径20mp
、pH8,0、吸油量110mfi/100g、揮発分
0.8重量%のファーネスカーボンブラック「三菱カラ
ー用カーボンブラック#40J 40重量%(3)三井
石油化学KK製低密度ポリエチレンワックス「ハイワッ
クス4400GJ (分子量約4,000)20重量% (4)ステアリン酸亜鉛 0.3重量%オ
レイン酸アミド 0.2重量%上記(1)
〜(4)を高速混合機で十分混合した後得られた混合物
を池貝鉄工製二軸押出機rPOM 30Jでストランド
状に押出し、ペレタイザーにより粒状(ペレット)化し
、カーボンブラック含有量40重量%のペレット状のカ
ーボンブラックマスターバッチ樹脂組成物を得た。
このマスターハツチ樹脂ペレットの他は実施例4と同一
のプロピレン−エチレン共重合体樹脂とL−LDPE樹
脂と有機造核剤を混合した樹脂ペレットを用い実施例4
と同一の射出成形機で同一のヒンジ付遮光性収納ケース
を成形した。その結果実施例4よりもさらに優れた品質
のヒンジ付遮光性収納ケースが得られた。
のプロピレン−エチレン共重合体樹脂とL−LDPE樹
脂と有機造核剤を混合した樹脂ペレットを用い実施例4
と同一の射出成形機で同一のヒンジ付遮光性収納ケース
を成形した。その結果実施例4よりもさらに優れた品質
のヒンジ付遮光性収納ケースが得られた。
この変性PP樹脂を含むマスターバッチ樹脂組成物を実
施例1〜3の各種成形品に適用した結果、成形性、均一
着色性、物理強度、外観の優れた製品が得られた。
施例1〜3の各種成形品に適用した結果、成形性、均一
着色性、物理強度、外観の優れた製品が得られた。
本発明は以上のような構成とすることにより、カーボン
ブラックを高濃度で含有させたものであっても、成形時
にカーボンブラックの分散性が良く、着色むら、ブツ等
が発生することなく、物理強度や遮光性等が非常に優れ
、常に良好な外観が得られる。
ブラックを高濃度で含有させたものであっても、成形時
にカーボンブラックの分散性が良く、着色むら、ブツ等
が発生することなく、物理強度や遮光性等が非常に優れ
、常に良好な外観が得られる。
Claims (1)
- 変性ポリオレフィン樹脂を5〜90重量%、平均粒子径
15〜120mμ、吸油量50ml/100g以上、揮
発成分が3.5%以下のカーボンブラックを5〜70重
量%含有することを特徴とするマスターバッチ用樹脂組
成物