JPH01241434A - 内填物に対する保香特性に優れた性質を有する紙容器における封筒貼り部の形成方法 - Google Patents

内填物に対する保香特性に優れた性質を有する紙容器における封筒貼り部の形成方法

Info

Publication number
JPH01241434A
JPH01241434A JP63068874A JP6887488A JPH01241434A JP H01241434 A JPH01241434 A JP H01241434A JP 63068874 A JP63068874 A JP 63068874A JP 6887488 A JP6887488 A JP 6887488A JP H01241434 A JPH01241434 A JP H01241434A
Authority
JP
Japan
Prior art keywords
laminated sheet
layer
surface layer
envelope
layers
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP63068874A
Other languages
English (en)
Other versions
JP2639957B2 (ja
Inventor
Hirotaka Tsunoda
裕孝 角田
Kazuki Yamada
一樹 山田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dai Nippon Printing Co Ltd
Original Assignee
Dai Nippon Printing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dai Nippon Printing Co Ltd filed Critical Dai Nippon Printing Co Ltd
Priority to JP63068874A priority Critical patent/JP2639957B2/ja
Publication of JPH01241434A publication Critical patent/JPH01241434A/ja
Application granted granted Critical
Publication of JP2639957B2 publication Critical patent/JP2639957B2/ja
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 〔産業上の利用分野〕 本発明は内填物に対する保香特性に優れた性質を有する
紙容器における封筒貼り部の形成方法に関するもので、
金属箔を積層構成中に含む紙容器用の積層シートによっ
て、内填物に対する保香特性に優れた性質を有する紙容
器を得る際の封筒貼り部を、確実に、且つ、極めて効率
良く形成し得る方法を提供するものである。
〔従来の技術〕
従来の紙容器は、紙容器を得る際に使用される成形用素
材である積層シートの有する熱溶着能によって接合部が
形成されているのが普通であり、−殻内には、容器内の
内填物と接する容器内周面層となる層がポリオレフィン
系樹脂層で形成されている成形用素材における前記ポリ
オレフィン系樹脂層の有する熱溶着能によって接合部が
形成されている。
〔発明が解決しようとする課題〕
ところで、前記容器内周面層がポリオレフィン系樹脂層
で構成されている容器は、該容器の成形用素材たる積層
シートを得る際のポリオレフィン系樹脂層の形成時や該
積層シートによる紙容器の成形時に、ポリオレフィン系
樹脂が熱分解を受けて脂肪族炭化水素等の揮発性成分を
生成することとなり、この揮発性成分が容器内に収容さ
れているオレンジジュース等の内填物内に移行する結果
、内填物に変味や異臭が発生するという弊害を有するば
かりでなく、前記紙容器の内周面層をなすポリオレフィ
ン系樹脂層は、内填物中の若番成分を吸着し易かったり
あるいは透過し易かったりするため、容器内の内填物の
風味が変化して損なわれ易いという欠点をも有する。
これに対して、本発明は、積層構成中に金属層を含んで
いる紙容器用積層シートによって、内填物に対する保香
特性に優れた性質を有する紙容器を形成する際の封筒貼
り部を、極めて効率良く、かつ、確実に形成する方法を
提供するものである。
〔課題を解決するための手段〕
本発明の内填物に対する保香特性に優れた性質を有する
紙容器における封筒貼り部の形成方法は、金属層を積層
構成中に含む包装材用基材と、ポリオレフィン系樹脂に
よる表面層と、４０℃以上のガラス転移温度を有する低
結晶性線状飽和ポリエステル樹脂による裏面層とを具備
する紙容器用積層シートによって、容器内周面層が前記
積層シートによる裏面層たる低結晶性線状飽和ポリエス
テル樹脂層で構成される紙容器を得る際の封筒貼り部の
形成方法であって、前記積層シートの一方の側辺部を表
面層側に反転させた反転部を、前記積層シートの他方の
側辺部が乗り越えるようにして重畳させ、該重畳部を熱
溶着することによって前記封筒貼り部を形成するもので
ある。
しかして、前記本発明方法の封筒貼り部の形成方法は、
前記積層シートの一方の側辺部を表面層側に反転させた
反転部を加熱、加圧することによって、前記反転部の表
面層同志を接着する第１工程と、前記封筒貼り予定部分
の表面層と裏面層との間の接着面となる前記紙容器用積
層シートの表面層と裏面層とのそれぞれに火炎処理を施
すことによって、前記表面層と裏面層とを熱溶融させ、
更に、前記両層が熱溶融状態にある間に、前記積層シー
トの一方の側辺部と他方の側辺部とを重畳させ、前記火
炎処理が付されている面同志の接当部分を加圧すること
によって該部分を接着する第２工程と、前記重畳部分に
おける前記積層シートの裏面層同志の接着面の接着を、
高周波誘導加熱による溶融を利用して行なう第３工程と
からなるものである。
前記構成からなる本発明方法で利用する紙容器用積層シ
ートは、積層構成中に金属層を含む包装材用基材と、前
記紙容器用積層ソートにおける表面層をなすポリオレフ
ィン系閏脂層と、同じく、前記紙容器用積層シートにお
ける裏面層をなす低結晶性線状飽和ポリエステル樹脂層
との積層シートであって、該積層ジートンこおける裏面
層をなす４０″Ｃ以上のガラス転移温度を有する低結晶
性線状飽和ポリエステル樹脂層が、該樹脂層を構成して
いる線状飽和ポリエステル樹脂のガラス転移温度未満の
温度等雰囲気中で優れた保香性能を発揮するものであり
、−殻内に紙容器内の内填物が４０℃未満に維持される
ものであることとの関係で、前記線状飽和ポリエステル
樹脂層による優れた保香性能が利用し得るものである。
尚、前記線状飽和ポリエステル樹脂層は、これが低結晶
性の樹脂で形成されているものであることから、例えば
、オレンジジュース等の内填物の充填を熱充填で行なう
場合等の加熱を受けても、前記ポリエステル樹脂層の熱
接着特性が損なわれるようなことがなく、内填物の充填
操作に続いて実施されろ紙容器用積層シートにおける表
面層と裏面層との間の熱接着による封緘部において、優
れた熱接着強度が得られものである。
前記紙容器用積層シートにおける裏面層をなすガラス移
転温度が４０℃以上の線状飽和ポリエステルｍ　脂層は
、例えば、エチレングリコール、プロピレングリコール
、１．４−ブタジオール、１．４−ジシクロヘキサンジ
メタツール等のアルコール成分と、７ジビン酸、セバシ
ン酸等の脂肪族ジカルボン酸や、テレフタル酸、イソフ
タル酸、ジフェニルカルボン酸等の芳香族ジカルボン酸
によるジカルボン酸成分、具体的には、エチレングリコ
ールとテレフタル酸、エチレングリコールとイソフタル
酸とテレフタル酸、１，４−ジシクロヘキサンジメタツ
ールとイソフタル酸とテレフタル酸、プロピレングリコ
ールとイソフタル酸とテレフタル酸等の共縮合重合体を
利用して形成し得るが、酸成分中の脂肪族ジカルボン酸
成分が１０重量％以上になる共縮合重合体の場合には、
この共縮合重合体による飽和ポリエステル樹脂層はその
保香性能が低下する傾向を有しているので好ましくない
。
また、前記４０℃以上のガラス転移温度を有する低結晶
性線状飽和ポリエステル樹脂層は、これが厚さ５μｍ未
満になると樹脂層の安定性が悪く、ヒートシールによる
密封性が悪くなり、また、２００μｍを越えるようにな
ると、得られる紙容器用積層シートが固くなって、折り
曲げ加工特性が悪くなることから、通常は、厚さ５〜２
００μｍの範囲内で形成されていることが好ましい。
本発明方法で利用する前記紙容器用積層シートにおける
表面層は、これらの積層シートによって成形される紙容
器に外部からの耐水性を付与するものであると同時に、
前述の各積層シートの裏面層との間に火炎シール法にょ
る熱溶着性能をもたらすものであり、例えば、低密度ホ
リエチレン、中密度ポリエチレン、高密度ポリエチレン
、エチレン　−酢酸ビニル共重合体、エチレンーアクリ
ル酸共重合体、エチレン−アクリル酸メチル共！　合体
、　”　＋レン　−α・オレフィン共重合体、更にはポ
リプロピレン等によって、厚さ３〜１５０μｍ程度に形
成されているものであろう 前記紙容器用積層シートは、前記４０″Ｃ以上のガラス
転移温度を有する低結晶性線状飽和ポリエステル樹脂層
からなる裏面層と、ポリオレフィン系樹脂による表面層
とが、積層構成中に金属層を含む包装材用基材に積６１
されているものであって、紙容器に成形されるに適した
積層シートとなり得る包装材用基材、例えば、アルミニ
ュウム箔１紙層、オレフィン系樹脂層、ボリエステル延
伸フィルム層等を利用した厚さ４０〜１０００μｍ程度
の包装材用基材が使用されるものである。
なお、前述の４０℃以上のガラス転移温度を有する低結
晶性線状飽和ポリエステル樹脂層からなる裏面層は、曲
記包装材用基材に対して、例えば、接着性ポリオレフィ
ン系樹脂やインシアネート系接着剤等の接着剤層を利用
して積層されるのが一般的である。
また、前記紙容器用積層シートは、例えば、ブリックタ
イプ、ゲーベルトップタイプ、更には円筒体等の紙容器
に成形されるものであり、主として胴貼り部分をなす封
筒貼り部が、積層シート端面が容器内周囲に露出するこ
とのない構造の接合部とされるもので、該接合部分にお
ける積層シートの表面層同志の接着を、熱バー等による
熱接着で、また、積層シートの表面層と裏面層との間の
接着を、火災処理による熱溶融接着で、更に、積層ンー
トの裏面層同志の接着を、高周波誘導加熱による熱溶融
接着で行なうものである。
前記火災処理による熱溶融接着が行われる前記封筒貼り
予定部分の積層ンートの表面層（ポリオレフィン系樹脂
層）と裏面層（低結晶性線状飽和ポリエステル樹脂層）
とに施される火災処理は、通常１０ｓ＋ｇ程度の細幅状
からなるソール予定部分に対して施されるものであって
、処理面の温度が１８０〜２５０℃程度、ガス圧５ｍｍ
Ａｑ１空気圧３５〜６０ｖｒｔｉ　Ａｑ程度の火災処理
装置によって、処理速度２００ｍ　／　ｗｉｎ、程度で
実施されるもので、火災処理された表面層すなわちポリ
オレフィン系樹脂層は、該樹脂層の１部分が溶融。
酸化されて、前記樹脂層の表面張力が当該積層シートの
裏面層の表面張力と同一程度となる程度に火災処理され
るのが好ましく、また、火災処理された裏面層すなわち
４０℃以上のガラス転移温度を有する低結晶性線状飽和
ポリエステル樹脂層は、前記火災処理によって樹脂層表
面が荒らされ、微細な多数の凹凸群が前記樹脂層面に生
成されるように火災処理されるのが好ましい。
尚、前記火炎処理と、該火炎処理が施された面同志を重
畳、加圧する際の加圧処理との間のタイムラグが大きく
なりすぎると、加圧時の接合面の温度が低下し、得られ
るシール強度が小さくなるので、前記タイムラグは０．
５秒以内に設定するのが好ましい。
また、前記積層シートの封筒貼り部における積層シート
の裏面層同志の接合部の形成に際して利用される前述の
高周波誘導加熱は、先の火炎処理による熱溶融接着によ
って形成されている筒状体に対して施されるものであっ
て、例えば、１０〜１０００　ＫＨｚで、０．０５〜３
０秒程度の照射で十分であるが、前記照射を筒状体の内
周面側から行なった場合には、裏面層同志の強力な接着
を得ることが困難となるため、先の高周波誘導加熱は、
火炎処理による熱溶融接着によって形成されている筒状
体の外周面側、すなわち、ポリオレフィン系樹脂による
表面層側から行なうのが好ましい。
〔実　施　例〕 以下、本発明の内填物に対する保香特性に優れた性質を
有する紙容器における封筒貼り部の形成方法の具体的な
構成を実施例をもって説明する。
実施例１ 第３図において、符号１で表示される包装材用基材、す
なわち、坪量４００９／ｒｒ？の耐酸紙／厚さ１５μｍ
のアイオノマー樹脂「ノ・イミラン１６５２　：三井デ
ュポンポリケミカル■製」層／厚さ９μｍのアルミニュ
ウム箔／厚さ１２μｍの二’ｌ’１ｌｌＷ伸ホ！Ｊエチ
レンテレフタレートフィルム層からなる積層構成の包装
材用基材１に対して、該包装材用基材１の耐酸紙面に、
厚さ３０μｍのポリオレフィン系樹脂「ミラフン１６Ｐ
二三井石油化学工業■製」層からなる表面層２を形成し
、また、前記包装材用基材１の二軸延伸ポリエチレンテ
レフタレートフィルム層面に、厚す３０μｍのエチレン
−α−オレフィン共重合体樹脂「ウルトゼックス２０２
０Ｌ　：三井石油化学工業■製」層／厚さ１０μｍの接
着性ポリオレフィン樹脂「アトマーＡＴ　４６９Ｃ：三
井石油化学工業株製」層／厚さ２０μｍの線状飽和ポリ
エステル樹脂ｒＰＥＴ　Ｇ　６７６３　ニガラス転移温
度８１℃，イーストマンコダック社製」層からなる三層
共押し出しフィルム３を、該フィルム３におけるポリエ
ステル樹脂層４が裏面層となるようにして積層すること
によって、本発明方法で使用する紙容器用積層シートの
１実施例品５を得た。
次いで、前記積層シート５の側辺部を、表面層２同志が
接当するようにして幅約ｌｏａｍに至って反転させ、該
反転部の上、下に、３２０℃のヒートシールバーを接当
して積層シート面が３００℃になるまで２ｋｇ／ｃｔｉ
の圧力を付加し、加熱、加圧することによって、前記表
面層２同志を接着させ、第２図に示されるような積層シ
ート５０、すなわち、積層シート５の一方の側辺部が表
面層２側に反転され、該反転部の表面層２同志が熱溶着
、接着された接着部Ａを有する端面処理されている積層
シート面０を得た。
次いで、前記端面処理されている積層シート５０の他方
の側辺部における裏面層４０幅約１０龍に至る部分と、
前記端面処理されている一方の側辺部の前記反転部を越
えた幅約１０ｇ＋＋ｗに至る部分の表面層２とを火炎処
理に付し、更に、前記火炎処理が付された表面層と裏面
層とを接当させることからなる側辺部同士の重畳部を形
成し、引き続いて、ゴムロールによる加圧を前記重畳部
に施すことによって、第１図にて符号Ｂで表示される接
着部を形成し、前記積層シートにおける裏面層が内周面
層で構成されている筒状体を得た。
なお、油脂火災処理は、積層シートの表面層に対しては
、ガス圧５朋Ａｑ、空気圧３９ｓｎＡｑの予備処理用第
１バーナーと、ガス圧５　ａｍ　Ａｑ　、空気圧４７＊
ｍＡｑの第２バーナーとによって、また、積層シートの
裏面層に対しては、ガス圧５　ｍｔｘ　Ａｑ　。
空気圧４０ｕ＋Ａｑの予備処理用対１バーナーと、ガス
圧５ｍｓ＋Ａｑの空気圧６０朋Ａｑ第２バーナーとによ
って、コンベアスピード２００ｍ　／　ｍｉｎ、で実施
したもので、火災処理面の加熱温度は２５０℃である。
しかる後に、前述の筒状体において、該筒状体を構成す
る積層シートの一方の側辺部に形成されている反転部の
裏面層４と他方の側辺部の裏面層４とが接当する幅約１
ＯＩＩＩ＋の重畳部に対して、第１図にて矢印′で示さ
れる側から、６００ＫＨｚ、　２．０秒間の高周波誘導
加熱を、該部分に加圧を付しながら施すことにより、符
号Ｃで表示される接着部を形成し、前述の積層シート５
における裏面層４が内周面層とされている筒状体の封筒
貼り部を形成した。
得られた筒状体における前記封筒貼り部の接合面の剥離
を手指先で行なったところ、紙層内での断層破壊が生じ
てしまい、積層シートの裏面層同志の間、及び表面層と
裏面層との間の界面を剥離することはできなかった。
比較例１ 前記実施例１で使用した紙容器用積層シートと同一の構
成の積層シートによって、前記積層ジートンこおける表
面層と裏面層との間の接着部を、積層シートの側辺部同
士による幅約１０龍の重畳部の上、下に、３２０℃のヒ
ートシールバーを接当し、積層シート面が３００″Ｃに
なるまで、２　ｋｇ　／　ｃａの圧力を付加しながら加
熱することによって形成した。
比較例２ 前記実施例１で使用した紙容器用積層シートと同一構成
の積層シート２枚を利用し、両積層シートの側辺部にお
ける裏面層のそれぞれを、幅１ｏ朋に至って、前記実施
例１で使用したものと同じ条件ｅこよる火災処理に付し
、引き続いて、前記火炎処理面同志が接当するようにし
て、前記２枚の積層シートを重畳させ、次いで、前記重
畳部を加圧することによって、前記積層シートの裏面層
同志の接合部を形成することによって、２枚の積層シー
トを接合した。
比較例３ 前記実施例１で使用した紙容器用積層シートを同一の構
成の積層シートによって、該積層シートの側辺部同志に
よる幅１０ｊＩＩ１１の重畳部を、前記積層シートの表
面層と裏面層とが接当するようにして形成し、該重畳部
に前記実施例１で使用したものと同一条件による高周波
誘導加熱を筒状体の外側表面側から付すことによって、
内周面層が裏面層で形成されている筒状体を得た。
前記比較例１〜３によって得られた各積層シートの接着
部の剥離を手指先で実施したところ、各接着部の接合界
面での剥離が容易に行なえた。
〔発明の作用、効果〕
本発明の内填物に対する保香特性に優れた性質を有する
紙容器における封筒貼り部の形成方法は、金属層を積層
構成中に含む包装材用基材と、ポリオレフィン系樹脂に
よる表面層と、４゜℃以上のガラス転移温度を有する低
結晶性線状飽和ポリエステル樹脂による裏面層とを具備
する紙容器用積層ンートによって、容器内周面層が前記
積層シートによる裏面層で構成される紙容器を得る際の
封筒貼り部の形成方法であって、前記積層シートの一方
の側辺部を表面層側に反転させた反転部を、前記積層シ
ートの他方の側辺部が乗り越えるようにして重畳させ、
該重畳部を熱溶着することによって前記紙容器における
封筒貼り部を形成するもので、前記積層シートの一方の
側辺部を表面層側に反転させた反転部を加熱、加圧する
ことによって、前記反転部における積層ンートの表面層
同志を接着する第１工程と、前記封筒貼り予定部分の表
面層と裏面層との間の接着面となる前記積層シートの表
面層と裏面層とのそれぞれに火災処理を施すことによっ
て、前記表面層と裏面層とを熱溶融させ、更に、前記両
層が熱溶融状態にある間に、前記積層シートの一方の側
辺部と他方の側辺部とを重畳し、前記火災処理が付され
た面同志の接当部分を加圧することによって該部分を接
着する第２工程と、高周波誘導加熱を利用して、前記重
畳部分における前記積層シートの裏面層同志の接当面の
接着を行なう第３工程とからなるものである。
而して、前記本発明方法においては、金属層を積層構成
中に含む包装材用基材と、ポリオレフィン系樹脂による
表面層と、４０℃以上のガラス転移温度を有する低結晶
性線状飽和ポリエステル樹脂Ｐこよる裏面層とを具備す
る紙容器用積層シートによって、容器内周面層が前記積
層シートによる裏面層で構成される紙容器を得る際の封
筒貼り部を、前記積層シート中の金属層を容器内周面に
露出されることなく形成するものであるから、内填物に
対する保香特性と衛生性とに優れた性質を有する紙容器
が得られるものである。
また、前記本発明方法では、前述の封筒貼り部における
積層シートの表面層と裏面層との間の接着に際しては火
炎処理を利用するものであるから、火炎処理されたポリ
オレフィン系ｔｌ脂層は、該樹脂層の１部分が溶融、酸
化されて、前記樹脂層の表面張力が、当該積層ンートの
裏面層の表面張力と同一程度となっており、また、火炎
処理された裏面層即ち４０’Ｃ以上のガラス転移温度を
有する低結晶性線状飽和ポリエステル樹脂層、該樹脂層
表面が荒らされ、微細な多数の凹凸群が前記樹脂層面に
生成されているので、火炎処理ンこ続く加圧工程で、表
面が溶融状態にあるポリオレフィン系樹脂層が低結晶性
線状飽和ポリエステル樹脂層の表面の凹凸の凹部内に深
く食い込むようにして侵入し、両者の間の強固な接合が
得られるものである。
更に本発明方法では、前述の封筒貼り部における積層ン
ートの裏面層同志の接着に際しては、高周波誘導加熱を
利用するものであるから、４０”Ｃ以上のガラス転移温
度を有する低結晶性線状飽和ポリエステル樹脂層同志の
間に強固な接合が得られるものである。
従って、本発明方法では、内填物に対する保香特性と衛
生性とに優れた性質を有する紙容器における封筒貼り部
を、極めて効率の良い熱シール方法で、確実に形成し得
るものである。
【図面の簡単な説明】
第１図は、本発明方法によって形成された紙容器用積層
シートの封筒貼り部の模型断面図、第２図は、本発明の
封筒貼り部の形成方法の途中工程を示す模型断面図、第
３図は、本発明方法で使用する紙容器用積層シートの１
実施例品の模型断面図である。 １：金属層を積層構成中に含む包装材用基材、２：ポリ
オレフィン系樹脂による表面層、４：４０℃以上のガラ
ス転移温度を有する低結晶性線状飽和ポリエステル樹脂
による裏面層、Ａ：積層シート５の一方の側辺部を表面
層２側に反転させた反転部の表面層２．２同志の接着部
、Ｂ：封筒貼り部における積層シート５の裏面層４と表
面層２との間の接着部、Ｃ：封筒貼り部における積層シ
ート５の裏面層４．４同志の接着部。 特許出願人　　大日本印刷株式会社 代　理　人　　　市　　川　　理　　吉新　　　井　　
　清　　　子 第１図 第２図 第３図 手糸売ネ甫正書　（自発） 昭和６３年　５月３１日 １　事件の表示 昭和６３年特許願第６８８７４号 ２　発明の名称 内填物に対する保香特性に優れた性質を有する紙容器に
おける封筒貼り部の形成方法３　補正をする者 事件との関係　特許出願人 （２８９）大日本印刷株式会社 ４　　代　　理　　人 （外１名） ５　補正の対象 （１）　　明細書第７頁第７行目の「温度等」を「温度
」に補正する。 （２）　　同書第８頁第１行〜第９行目の「操作に続い
て・・・・・・・・・・・・ジシクロヘキサンジメタ」
を、下記の通りに補正する。 記 「操作に続いて実施される紙容器用積層シートにおける
裏面層が関与する部分の封緘部の形成において、優れた
熱接着強度が得られるものである。 前記紙容器用積層シートにおける裏面層をなすガラス転
わ温度が４０℃以上の線状飽和ポリエステル樹脂層は、
例えば、エチレングリコール、プロピレングリコール、
１，４−ブタジオール、１．４−ジシクロヘキサンジメ
タ」（３）同書中の次の各箇所の「火災処理」を「火炎
処理」に補正する。 ２）第１２頁第　４行目 ３）第１２頁第７〜８行目、 ４）第１２頁第１１行目、 ５）第１２頁第１３行目、 ６）第１２頁第１７行目、 ７）第１２頁第１７〜１８行目、 ８）第１３頁第　２行目、 ９）第１３頁第　４行目、 １０）第１７頁第　６行目、 １１）第１７頁第１４行目 １２）第１９頁第　９行目、 １３）第２１頁第１３行目、 １４）第２１頁第１７行目、 （４）同書第１４頁第１６行目の「三井デュポンポリケ
ミカル」を、「三井デュポンポリケミカル」に補正する
。 （５）同書第１８頁第３行目のｒＫＨｚ、　２．０秒間
」を、ｒＫＨｚ　、　２．０秒間」に補正する。 １）第１１頁第１８行目、 （６）同書第１９頁第８行目の「幅１０ｍｍに至って、
」を、「幅１０ｍｍに亙って、」に補正する。 （７）同書第１７頁第１１〜１２行目の「空気圧４０　
ｍｍＡｑの・・・・・・・・・・・・第２バーナーとに
」を、下記の通りに補正する。 記 「空気圧４０　＋ｎｍ八ｑへ予備処理用第１バーナーと
、ガス圧５　ｍｍＡｑ、空気圧６０　ｍｍＡｑの第２バ
ーナーとに」 （８）同書第２３頁第８行目の「チル樹脂層、」を、「
チル樹脂層は、」に補正する。 以　　　上

Claims (1)

    【特許請求の範囲】
  1. 紙容器用積層シートの一方の側辺部を表面層側に反転さ
    せた反転部を、前記積層シートの他方の側辺部が乗り越
    えるようにして重畳させ、該重畳部を熱溶着することに
    よって、容器内周面層が前記積層シートによる裏面層で
    構成される紙容器における封筒貼り部を形成する方法に
    おいて、金属層を積層構成中に含む包装材用基材と、ポ
    リオレフィン系樹脂による表面層と、４０℃以上のガラ
    ス転移温度を有する低結晶性線状飽和ポリエステル樹脂
    による裏面層とを具備する紙容器用積層シートの一方の
    側辺部を表面層側に反転させた反転部を加熱、加圧する
    ことによって、前記反転部の表面層同志を接着し、次い
    で、前記封筒貼り予定部分の表面層と裏面層との間の接
    着面となる前記紙容器用積層シートの表面層と裏面層と
    のそれぞれに火炎処理を施すことによって、前記表面層
    と裏面層とをそれぞれ熱溶融させ、更に、前記両層が熱
    溶融状態にある間に前記積層シートの一方の側辺部と他
    方の側辺部とを重畳した後、前記火炎処理が付されてい
    る面同志の接当部分を加圧することによって該部分を接
    着し、しかる後に、高周波誘導加熱を利用して、前記重
    畳部分における前記積層シートの裏面層同志の接当面の
    接着を行なうことを特徴とする内填物に対する保香特性
    に優れた性質を有する紙容器における封筒貼り部の形成
    方法。
JP63068874A 1988-03-23 1988-03-23 内填物に対する保香特性に優れた性質を有する紙容器における封筒貼り部の形成方法 Expired - Lifetime JP2639957B2 (ja)