JP7486877B2 - リチウム二次電池用正極活物質、この製造方法、これを含むリチウム二次電池用正極及びリチウム二次電池 - Google Patents
リチウム二次電池用正極活物質、この製造方法、これを含むリチウム二次電池用正極及びリチウム二次電池 Download PDFInfo
- Publication number
- JP7486877B2 JP7486877B2 JP2020556267A JP2020556267A JP7486877B2 JP 7486877 B2 JP7486877 B2 JP 7486877B2 JP 2020556267 A JP2020556267 A JP 2020556267A JP 2020556267 A JP2020556267 A JP 2020556267A JP 7486877 B2 JP7486877 B2 JP 7486877B2
- Authority
- JP
- Japan
- Prior art keywords
- positive electrode
- active material
- electrode active
- transition metal
- lithium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本出願は、2018年5月11日付韓国特許出願第2018-0054292号に基づく優先権の利益を主張し、当該韓国特許出願の文献に開示された全ての内容は本明細書の一部として含まれる。
[化学式1]
Li1+aNixCoyMnzM1 WO2
前記化学式1において、0≦a≦0.3、0.65≦x<1、0<y≦0.35、0<z≦0.35、0≦w≦0.02、y<zであり、M1は、Al、Zr、Mg、Zn、Y、Fe及びTiからなる群から選択された少なくとも一つである。
従来、リチウム二次電池の正極活物質としては、作用電圧が高く、容量特性に優れたリチウムコバルト系酸化物が用いられたが、前記リチウムコバルト系酸化物は、脱リチウムによる結晶構造の不安定化のため熱的特性が劣化し、高価であるため中大型デバイスの動力源として大量使用するには限界があった。前記リチウムコバルト系酸化物を代替するためにリチウムニッケルコバルトマンガン系酸化物を用いたが、前記リチウムニッケルコバルトマンガン系酸化物の場合、製造コストを低減するためにコバルトの含量を減少するに伴い、放電容量及び出力特性が減少されるという問題点があった。
[化学式1]
Li1+aNixCoyMnzM1 WO2
前記化学式1において、
0≦a≦0.3、0.65≦x<1、0<y≦0.35、0<z≦0.35、0≦w≦0.02、y<zであり、
M1は、Al、Zr、Mg、Zn、Y、Fe及びTiからなる群から選択された少なくとも一つである。
次に、本発明に係る正極活物質の製造方法に対して説明する。
具体的に、ニッケル原料物質としては、Ni(OH)2、NiO、NiOOH、NiCO3・2Ni(OH)2・4H2O、NiC2O2・2H2O、Ni(NO3)2・6H2O、NiSO4、NiSO4・6H2O、脂肪酸ニッケル塩またはニッケルハロゲン化物などを挙げることができ、これらのうち1種以上の混合物が用いられてよい。
次に、本発明に係る正極活物質を含む、リチウム二次電池用正極を提供する。
また、本発明は、前記正極を含む電気化学素子を製造することができる。前記電気化学素子は、具体的に電池、キャパシタなどであってよく、より具体的にはリチウム二次電池であってよい。
(正極活物質の製造)
NiSO4及びMnSO4をニッケル:マンガンのモル比が95:5となるようにする量で、水中で混合して2.3M濃度の第1遷移金属含有溶液を準備した。
前記で製造された正極活物質、デンカブラック導電材、及びポリビニリデンフルオライド(PVDF)バインダを95:2.5:2.5の重量比で混合し、これをN‐メチルピロリドン(NMP)溶媒中で混合して正極スラリーを製造した。前記で製造された正極スラリーをアルミニウムホイルに塗布した後、ロールプレスを行い、120℃で12時間乾燥して正極を製造した。
負極活物質として天然黒鉛、カーボンブラック導電材、及びスチレン‐ブタジエンゴム(SBR)バインダを96:2:2の重量比で混合して負極スラリーを製造した。これを銅ホイル上に塗布し、110℃で2時間真空乾燥して負極を製造した後、ロールプレスを行った。
前記で製造した正極、負極と、厚さ20μmのポリエチレン分離膜(F20BHE、東燃社)を用いて通常の方法でコインセル形態の電池を製造した後、エチレンカーボネート:ジメチルカーボネートを1:1(体積%)で混合した溶媒に、1MのLiPF6を溶解させた電解液を注入し、コインセル形態のリチウム二次電池を製造した。
正極活物質の製造時、NiSO4及びMnSO4をニッケル:マンガンのモル比が95:5となるようにする量で、水中で混合して2.3M濃度の第1遷移金属含有溶液を準備し、さらに、NiSO4、CoSO4、及びMnSO4をニッケル:コバルト:マンガンのモル比が55:20.5:24.5となるようにする量で、水中で混合して2.3M濃度の第2遷移金属含有溶液を準備した。前記第1遷移金属含有溶液及び第2遷移金属含有溶液を用いて、平均組成がNi0.65Co0.15Mn0.2(OH)2である正極活物質前駆体を製造し、これを用いることを除き、前記実施例1と同様の方法を用いて正極活物質及びこれを含む正極及びリチウム二次電池を製造した。
正極活物質の製造時、NiSO4及びMnSO4をニッケル:マンガンのモル比が95:5となるようにする量で、水中で混合して2.3M濃度の第1遷移金属含有溶液を準備し、さらに、NiSO4、CoSO4、及びMnSO4をニッケル:コバルト:マンガンのモル比が55:13.5:31.5となるようにする量で、水中で混合して2.3M濃度の第2遷移金属含有溶液を準備した。前記第1遷移金属含有溶液及び第2遷移金属含有溶液を用いて、Ni0.65Co0.10Mn0.25(OH)2である正極活物質前駆体を製造し、これを用いることを除き、前記実施例1と同様の方法を用いて正極活物質及びこれを含む正極及びリチウム二次電池を製造した。
正極活物質の製造時、NiSO4及びMnSO4をニッケル:マンガンのモル比が95:5となるようにする量で、水中で混合して2.3M濃度の第1遷移金属含有溶液を準備し、さらに、NiSO4、CoSO4、及びMnSO4をニッケル:コバルト:マンガンのモル比が55:17:28となるようにする量で、水中で混合して2.3M濃度の第2遷移金属含有溶液を準備した。前記第1遷移金属含有溶液及び第2遷移金属含有溶液を用いて、Ni0.65Co0.125Mn0.225(OH)2である正極活物質前駆体を製造し、これを用いることを除き、前記実施例1と同様の方法を用いて正極活物質及びこれを含む正極及びリチウム二次電池を製造した。
NiSO4、CoSO4、及びMnSO4をニッケル:コバルト:マンガンのモル比が70:10:20となるようにする量で、水中で混合して2.3M濃度の遷移金属含有溶液を準備した。
反応全体に亘って反応器内のpHをpH11.2に維持することを除き、前記実施例1と同様の方法を用いて正極活物質及びこれを含む正極及び二次電池を製造した。
NiSO4、CoSO4、及びMnSO4をニッケル:コバルト:マンガンのモル比が65:15:20となるようにする量で、水中で混合して2.3M濃度の遷移金属含有溶液を準備し、これを用いて、Ni0.65Co0.15Mn0.20(OH)2である正極活物質前駆体を製造し、これを用いることを除き、前記比較例1と同様の方法を用いて正極活物質及びこれを含む正極及びリチウム二次電池を製造した。
NiSO4、CoSO4、及びMnSO4をニッケル:コバルト:マンガンのモル比が65:12.5:22.5となるようにする量で、水中で混合して2.3M濃度の遷移金属含有溶液を準備し、これを用いて、Ni0.65Co0.125Mn0.225(OH)2である正極活物質前駆体を製造し、これを用いることを除き、前記比較例1と同様の方法を用いて正極活物質及びこれを含む正極及びリチウム二次電池を製造した。
NiSO4、CoSO4、及びMnSO4をニッケル:コバルト:マンガンのモル比が65:20:15となるようにする量で、水中で混合して2.3M濃度の遷移金属含有溶液を準備し、これを用いて、Ni0.65Co0.20Mn0.15(OH)2である正極活物質前駆体を製造し、これを用いることを除き、前記比較例1と同様の方法を用いて正極活物質及びこれを含む正極及びリチウム二次電池を製造した。
NiSO4、CoSO4、及びMnSO4をニッケル:コバルト:マンガンのモル比が65:17.5:17.5となるようにする量で、水中で混合して2.3M濃度の遷移金属含有溶液を準備し、これを用いて、Ni0.65Co0.175Mn0.175(OH)4である正極活物質前駆体を製造し、これを用いることを除き、前記比較例1と同様の方法を用いて正極活物質及びこれを含む正極及びリチウム二次電池を製造した。
NiSO4及びMnSO4をニッケル:マンガンのモル比が95:5となるようにする量で、水中で混合して2.3M濃度の第1遷移金属含有溶液を準備した。
NiSO4及びMnSO4をニッケル:マンガンのモル比が95:5となるようにする量で、水中で混合して2.3M濃度の第1遷移金属含有溶液を準備した。
前記実施例1及び比較例1及び2で製造した正極活物質粒子を切断して透過電子顕微鏡(TEM)を用いて正極活物質の断面を撮影し、前記正極活物質の表面の結晶構造を制限視野回折パターン(selected area diffraction pattern,SADP)を介して確認した。
前記実施例1~4及び比較例1~6で製造した二次電池に対して充放電効率評価を行い、その結果を下記表1に示した。
前記実施例1~2及び比較例1~6で製造したリチウム二次電池の低温(-10℃)出力特性を確認した。具体的に、前記実施例1~2及び比較例1~6で製造したリチウム二次電池を常温(25℃)で0.33C定電流で充電させた後、22.5分間0.4C定電流で放電させ、1,350秒間の電圧降下を測定し、これを下記表2に示した。
前記実施例1~4及び比較例1~8で製造した正極を含む二次電池の寿命特性及び抵抗特性を測定した。具体的に、前記実施例1~4及び比較例1~8で製造した二次電池を、それぞれ45℃で1Cの定電流で4.25Vまで3Cカットオフ(cut off)で充電した。その後、1C定電流で3.0Vになるまで放電をした。前記充電及び放電挙動を1サイクルとし、このようなサイクルを300回繰り返して行った後、前記実施例1~4及び比較例1~8による二次電池のサイクルによる容量維持率及び抵抗増加率を測定した。前記寿命特性の場合、300サイクル目での容量を初期容量で割った後、100を掛けてその値を計算しており、前記抵抗特性の場合、300サイクル目での抵抗を初期抵抗で割った後、100を掛けてその値を計算した後、これを下記表3及び図5に示した。
Claims (12)
- 平均組成が下記化学式1で表されるリチウム遷移金属酸化物を含み、前記リチウム遷移金属酸化物内のコバルト含量がマンガン含量より少ない正極活物質であって、
前記リチウム遷移金属酸化物は、ニッケルが粒子の中心から表面まで漸進的に減少し且つコバルト及びマンガンが粒子の中心から表面まで漸進的に増加する濃度勾配を有し、
前記正極活物質は、1次粒子が凝集されてなる2次粒子の形態であり、
前記正極活物質の表面の少なくとも8箇所の地点でTEM分析を介して測定したc軸方向と測定地点における粒子の中心から表面に向かう粒子成長方向がなす角度が85゜から95゜を満たす比率が60%以上であり、
[化学式1]
Li1+aNixCoyMnzM1 WO2
前記化学式1において、
0≦a≦0.3、0.65≦x<1、0<y≦0.35、0<z≦0.35、0≦w≦0.02、y<zであり、
M1は、Al、Zr、Mg、Zn、Y、Fe及びTiからなる群から選択された少なくとも一つである、正極活物質。 - 前記リチウム遷移金属酸化物のコバルト:マンガンのモル比が1:1超過1:10以下である、請求項1に記載の正極活物質。
- 前記正極活物質は、表面部に前記正極活物質の中心から表面方向に成長した柱状構造の1次粒子を含む、請求項1または2に記載の正極活物質。
- 前記化学式1で表されるリチウム遷移金属酸化物は、リチウムを除いた遷移金属の総モル数に対してコバルトを15モル%以下で含む、請求項1から3のいずれか一項に記載の正極活物質。
- 前記化学式1で表されるリチウム遷移金属酸化物は、リチウムを除いた遷移金属の総モル数に対してマンガンを20モル%以上35モル%未満で含む、請求項1から4のいずれか一項に記載の正極活物質。
- 請求項1から5のいずれか一項に記載の正極活物質を製造するための正極物質の製造方法であって、
ニッケル原料物質を含む第1遷移金属含有溶液と、
前記第1遷移金属含有溶液と異なる遷移金属濃度を有し、且つ、ニッケル原料物質、コバルト原料物質及びマンガン原料物質を含む第2遷移金属含有溶液とを準備する段階、
前記第1遷移金属含有溶液及び第2遷移金属含有溶液の混合比率を漸進的に変化させながら、前記第1遷移金属含有溶液と第2遷移金属含有溶液とを混合して正極活物質前駆体を製造する段階、及び
前記正極活物質前駆体及びリチウム含有原料物質を混合して焼成し、正極活物質を合成する段階、を含み、
前記正極活物質前駆体を製造する段階は、混合溶液内のニッケル含量が減少するに伴い、pHが漸進的に低くなるように調節される、正極活物質の製造方法。 - 前記第1遷移金属含有溶液のニッケル:コバルト:マンガンのモル比が(80~100):(0~10):(0~20)である、請求項6に記載の正極活物質の製造方法。
- 前記第2遷移金属含有溶液のニッケル:コバルト:マンガンのモル比が(50~80):(10~30):(10~35)である、請求項6に記載の正極活物質の製造方法。
- 前記pHは、pH13からpH9の範囲で漸進的に減少する、請求項6から8のいずれか一項に記載の正極活物質の製造方法。
- 前記正極活物質前駆体及び前記リチウム含有原料物質の混合時、ドーピング元素M1原料物質をさらに加え、M1は、Al、Zr、Mg、Zn、Y、Fe及びTiからなる群から選択された少なくとも一つである、請求項6から9のいずれか一項に記載の正極活物質の製造方法。
- 請求項1から5のいずれか一項に記載の正極活物質を含む、リチウム二次電池用正極。
- 請求項11に記載の正極を含む、リチウム二次電池。