JP6380376B2 - 非水電解液二次電池 - Google Patents
非水電解液二次電池 Download PDFInfo
- Publication number
- JP6380376B2 JP6380376B2 JP2015503064A JP2015503064A JP6380376B2 JP 6380376 B2 JP6380376 B2 JP 6380376B2 JP 2015503064 A JP2015503064 A JP 2015503064A JP 2015503064 A JP2015503064 A JP 2015503064A JP 6380376 B2 JP6380376 B2 JP 6380376B2
- Authority
- JP
- Japan
- Prior art keywords
- compound
- same manner
- positive electrode
- secondary battery
- active material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
一般式(2)中、Aは、Li、Mg、Al、Co、Bからなる群より選ばれる1つ、もしくは2つ以上の元素である。αは、0<α≦0.1である。
一般式(3)中、Meは、Niを必ず含み、かつ、Co、Al、Mn、Mg、Zrからなる群より選ばれる1つ、もしくは2つ以上の元素からなる。βは、0.98≦β≦1.02である。
二次電池の製造方法の一例として、図1の二次電池の製造方法を説明する。乾燥空気または不活性ガス雰囲気において、負極および正極を、多孔質セパレータ5を介して積層、あるいは積層したものを捲回した後に、電池缶や、合成樹脂と金属箔との積層体からなる可とう性フィルム等の外装体に収容し、非水電解液を含浸させる。そして、外装体を封止前または封止後に、非水電解液二次電池の充電を行うことにより、負極上に良好な皮膜を形成させることができる。なお、多孔質セパレータ5としては、ポリプロピレン、ポリエチレン等のポリオレフィン、フッ素樹脂等の多孔性フィルムが用いられる。外装体としては、電解液に安定で、かつ十分な水蒸気バリア性を持つものであれば、適宜選択することができる。例えば、積層ラミネート型の二次電池の場合、外装体としては、アルミニウム、シリカをコーティングしたポリプロピレン、ポリエチレン等のラミネートフィルムを用いることができる。特に、体積膨張を抑制する観点から、アルミニウムラミネートフィルムを用いることが好ましい。
本実施形態におけるリチウム二次電池用電解液(以下、「非水電解液」または単に「電解液」と記載することもある。)は、添加剤として、一般式(1)で表される環状スルホン酸エステル(以下、単に「一般式(1)の化合物」と記載することもある。)を含有する。
正極は、正極集電体上に、正極活物質と正極用結着剤を含む正極活物質層を形成することで作製することができる。図1の非水電解液二次電池において、正極活物質を含有する層1に用いる正極活物質としては、スピネル構造を有するリチウムマンガン複合酸化物(「LMO」と記載することもある)と、層状岩塩構造を有するリチウム遷移金属複合化合物(「層状Li化合物」と記載することもある)の混合物が好ましい。
一般式(2)中、Aは、Li、Mg、Al、Co、Bからなる群より選ばれる1つ、または2つ以上の元素である。αは、0<α≦0.1である。具体的には、
Li(Mn0.98Li0.02)2O4、
Li(Mn0.95Li0.05)2O4、
Li(Mn0.98Mg0.02)2O4、
Li(Mn0.95Mg0.05)2O4、
Li(Mn0.98Al0.02)2O4、
Li(Mn0.95Al0.05)2O4、
Li(Mn0.98Al0.01Co0.01)2O4、
Li(Mn0.95Al0.025Co0.025)2O4、
Li(Mn0.98Li0.01Mg0.01)2O4、
Li(Mn0.95Li0.025Mg0.025)2O4、
Li(Mn0.94Li0.02Mg0.02B0.02)2O4、
Li(Mn0.98Li0.01Al0.01)2O4、
Li(Mn0.95Li0.025Al0.025)2O4、
Li(Mn0.94Li0.025Al0.025B0.01)2O4、
Li(Mn0.97Li0.01Al0.01Co0.01)2O4、
Li(Mn0.94Li0.02Al0.02Co0.02)2O4、
Li(Mn0.93Li0.02Al0.02Co0.02B0.01)2O4、
Li(Mn0.95Li0.01Mg0.01Al0.01Co0.01B0.01)2O4、
などが挙げられる。正極活物質として、1種類のLMOを単独で含んでも2種以上のLMOを組み合わせて含んでもよい。
LiNi0.80Co0.20O2、
LiNi0.80Co0.15Al0.05O2、
LiNi0.80Mn0.10Co0.10O2、
LiNi0.70Mn0.20Co0.10O2、
LiNi0.60Mn0.20Co0.20O2、
LiNi0.60Mn0.20Co0.20O2、
LiNi0.50Mn0.30Co0.20O2、
LiNi0.40Mn0.30Co0.30O2、
LiNi0.33Mn0.33Co0.33O2、
LiNi0.30Mn0.30Co0.30Mg0.10O2、
LiNi0.30Mn0.30Co0.30Zr0.10O2、
などが挙げられる。正極活物質として、1種類の層状Li化合物を単独で含んでも2種以上の層状Li化合物を組み合わせて含んでもよい。
負極は、負極集電体上に、負極活物質と負極用結着剤を含む負極活物質層を形成することで作製することができる。図1の非水電解液二次電池において、負極活物質を含有する層2に用いる負極活物質には、たとえばリチウム金属、リチウム合金、およびリチウムを吸蔵・放出できる材料からなる群から選択される一または二以上の物質を用いることができる。リチウムイオンを吸蔵・放出する材料としては、炭素材料および酸化物等を挙げることができる。
(電池の作製)
本実施例の電池の作製について説明する。正極集電体として厚み20μmのアルミニウム箔を用い、正極活物質としてLi(Mn0.95Li0.01Mg0.01Al0.01Co0.01B0.01)2O4とLiNi0.80Co0.20O2との重量比75:25の混合物を用いた。さらに、正極用結着剤としてPVdF(株式会社クレハ製KFポリマー)を用い、導電付与材としてアセチレンブラック(ティムカル・グラファイト・アンド・カーボン社製)を用いた。また、負極集電体として厚み10μmの銅箔を用い、この銅箔上に負極活物質として黒鉛を用いた。さらに、負極用結着剤としてPVdF(株式会社クレハ製KFポリマー)を用い、導電付与材としてアセチレンブラック(ティムカル・グラファイト・アンド・カーボン社製)を用いた。そして、負極と正極とをポリエチレンからなるセパレータを介して積層し、二次電池を作製した。
まず室温にて充電および放電を1回ずつ行った。この時の充放電条件は、CCCV充電レート1.0C、CC放電レート1.0C、充電終止電圧4.2V、放電終止電圧3.0Vとした。なお、1.0Cとは、満充電状態から1時間で放電しきる電流値である。
実施例1において、化合物No.1の代わりにメチレンメタンジスルホン酸エステルを用いた以外は実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を測定した。結果を表2に示す。なお、表中、メチレンメタンジスルホン酸エステルは「化合物A」と記載する。
正極活物質としてLi(Mn0.95Li0.01Mg0.01Al0.01Co0.01B0.01)2O4とLiNi0.50Mn0.30Co0.20O2との重量比30:70の混合物を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表2に示す。
正極活物質としてLi(Mn0.95Li0.01Mg0.01Al0.01Co0.01B0.01)2O4とLiNi0.80Co0.20O2との重量比75:25の混合物を用い、化合物No.1の代わりに化合物No.5を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表2に示す。
正極活物質としてLi(Mn0.95Li0.01Mg0.01Al0.01Co0.01B0.01)2O4とLiNi0.50Mn0.30Co0.20O2との重量比30:70の混合物を用い、化合物No.1の代わりに化合物No.5を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表2に示す。
正極活物質としてLi(Mn0.95Li0.01Mg0.01Al0.01Co0.01B0.01)2O4とLiNi0.80Co0.20O2との重量比75:25の混合物を用い、化合物No.1の代わりに化合物No.7を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表2に示す。
正極活物質としてLi(Mn0.95Li0.01Mg0.01Al0.01Co0.01B0.01)2O4とLiNi0.50Mn0.30Co0.20O2との重量比30:70の混合物を用い、化合物No.1の代わりに化合物No.7を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表2に示す。
正極活物質としてLi(Mn0.95Li0.01Mg0.01Al0.01Co0.01B0.01)2O4とLiNi0.80Co0.20O2との重量比75:25の混合物を用い、化合物No.1の代わりに化合物No.8を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表2に示す。
正極活物質としてLi(Mn0.95Li0.01Mg0.01Al0.01Co0.01B0.01)2O4とLiNi0.50Mn0.30Co0.20O2との重量比30:70の混合物を用い、化合物No.1の代わりに化合物No.8を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表2に示す。
正極活物質としてLi(Mn0.93Li0.07)2O4とLiNi0.80Co0.20O2との重量比85:15の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表2に示す。
正極活物質としてLi(Mn0.93Li0.07)2O4とLiNi0.80Co0.20O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表2に示す。
正極活物質としてLi(Mn0.93Li0.07)2O4とLiNi0.80Co0.15Al0.05O2との重量比85:15の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表2に示す。
正極活物質としてLi(Mn0.93Li0.07)2O4とLiNi0.80Co0.15Al0.05O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表2に示す。
正極活物質としてLi(Mn0.93Li0.07)2O4とLiNi0.80Mn0.10Co0.10O2との重量比85:15の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表2に示す。
正極活物質としてLi(Mn0.93Li0.07)2O4とLiNi0.80Mn0.10Co0.10O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表2に示す。
正極活物質としてLi(Mn0.93Li0.07)2O4とLiNi0.70Mn0.20Co0.10O2との重量比85:15の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表2に示す。
正極活物質としてLi(Mn0.93Li0.07)2O4とLiNi0.70Mn0.20Co0.10O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表2に示す。
正極活物質としてLi(Mn0.93Li0.07)2O4とLiNi0.60Mn0.20Co0.20O2との重量比85:15の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表2に示す。
正極活物質としてLi(Mn0.93Li0.07)2O4とLiNi0.60Mn0.20Co0.20O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表2に示す。
正極活物質としてLi(Mn0.93Li0.07)2O4とLiNi0.60Mn0.20Co0.20O2との重量比30:70の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表2に示す。
正極活物質としてLi(Mn0.93Li0.07)2O4とLiNi0.50Mn0.30Co0.20O2との重量比85:15の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表2に示す。
正極活物質としてLi(Mn0.93Li0.07)2O4とLiNi0.50Mn0.30Co0.20O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表2に示す。
正極活物質としてLi(Mn0.93Li0.07)2O4とLiNi0.50Mn0.30Co0.20O2との重量比30:70の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表2に示す。
正極活物質としてLi(Mn0.95Li0.025Mg0.025)2O4とLiNi0.80Co0.20O2との重量比85:15の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表3に示す。
正極活物質としてLi(Mn0.95Li0.025Mg0.025)2O4とLiNi0.80Co0.20O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表3に示す。
正極活物質としてLi(Mn0.95Li0.025Mg0.025)2O4とLiNi0.80Co0.15Al0.05O2との重量比85:15の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表3に示す。
正極活物質としてLi(Mn0.95Li0.025Mg0.025)2O4とLiNi0.80Co0.15Al0.05O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表3に示す。
正極活物質としてLi(Mn0.95Li0.025Mg0.025)2O4とLiNi0.80Mn0.10Co0.10O2との重量比85:15の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表3に示す。
正極活物質としてLi(Mn0.95Li0.025Mg0.025)2O4とLiNi0.80Mn0.10Co0.10O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表3に示す。
正極活物質としてLi(Mn0.95Li0.025Mg0.025)2O4とLiNi0.70Mn0.20Co0.10O2との重量比85:15の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表3に示す。
正極活物質としてLi(Mn0.95Li0.025Mg0.025)2O4とLiNi0.70Mn0.20Co0.10O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表3に示す。
正極活物質としてLi(Mn0.95Li0.025Mg0.025)2O4とLiNi0.60Mn0.20Co0.20O2との重量比85:15の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表3に示す。
正極活物質としてLi(Mn0.95Li0.025Mg0.025)2O4とLiNi0.60Mn0.20Co0.20O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表3に示す。
正極活物質としてLi(Mn0.95Li0.025Mg0.025)2O4とLiNi0.60Mn0.20Co0.20O2との重量比30:70の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表3に示す。
正極活物質としてLi(Mn0.95Li0.025Mg0.025)2O4とLiNi0.50Mn0.30Co0.20O2との重量比85:15の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表3に示す。
正極活物質としてLi(Mn0.95Li0.025Mg0.025)2O4とLiNi0.50Mn0.30Co0.20O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表3に示す。
正極活物質としてLi(Mn0.95Li0.025Mg0.025)2O4とLiNi0.50Mn0.30Co0.20O2との重量比30:70の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表3に示す。
正極活物質としてLi(Mn0.94Li0.025Al0.025B0.01)2O4とLiNi0.80Co0.20O2との重量比85:15の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表3に示す。
正極活物質としてLi(Mn0.94Li0.025Al0.025B0.01)2O4とLiNi0.80Co0.20O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表3に示す。
正極活物質としてLi(Mn0.94Li0.025Al0.025B0.01)2O4とLiNi0.80Co0.15Al0.05O2との重量比85:15の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表3に示す。
正極活物質としてLi(Mn0.94Li0.025Al0.025B0.01)2O4とLiNi0.80Co0.15Al0.05O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表3に示す。
正極活物質としてLi(Mn0.94Li0.025Al0.025B0.01)2O4とLiNi0.80Mn0.10Co0.10O2との重量比85:15の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表3に示す。
正極活物質としてLi(Mn0.94Li0.025Al0.025B0.01)2O4とLiNi0.80Mn0.10Co0.10O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表3に示す。
正極活物質としてLi(Mn0.94Li0.025Al0.025B0.01)2O4とLiNi0.70Mn0.20Co0.10O2との重量比85:15の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表3に示す。
正極活物質としてLi(Mn0.94Li0.025Al0.025B0.01)2O4とLiNi0.70Mn0.20Co0.10O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表3に示す。
正極活物質としてLi(Mn0.94Li0.025Al0.025B0.01)2O4とLiNi0.60Mn0.20Co0.20O2との重量比85:15の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表3に示す。
正極活物質としてLi(Mn0.94Li0.025Al0.025B0.01)2O4とLiNi0.60Mn0.20Co0.20O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表3に示す。
正極活物質としてLi(Mn0.94Li0.025Al0.025B0.01)2O4とLiNi0.60Mn0.20Co0.20O2との重量比30:70の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表3に示す。
正極活物質としてLi(Mn0.94Li0.025Al0.025B0.01)2O4とLiNi0.50Mn0.30Co0.20O2との重量比85:15の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表3に示す。
正極活物質としてLi(Mn0.94Li0.025Al0.025B0.01)2O4とLiNi0.50Mn0.30Co0.20O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表3に示す。
正極活物質としてLi(Mn0.94Li0.025Al0.025B0.01)2O4とLiNi0.50Mn0.30Co0.20O2との重量比30:70の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表3に示す。
正極活物質としてLi(Mn0.94Li0.02Al0.02Co0.02)2O4とLiNi0.80Co0.20O2との重量比85:15の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表4に示す。
正極活物質としてLi(Mn0.94Li0.02Al0.02Co0.02)2O4とLiNi0.80Co0.20O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表4に示す。
正極活物質としてLi(Mn0.94Li0.02Al0.02Co0.02)2O4とLiNi0.80Co0.15Al0.05O2との重量比85:15の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表4に示す。
正極活物質としてLi(Mn0.94Li0.02Al0.02Co0.02)2O4とLiNi0.80Co0.15Al0.05O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表4に示す。
正極活物質としてLi(Mn0.94Li0.02Al0.02Co0.02)2O4とLiNi0.80Mn0.10Co0.10O2との重量比85:15の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表4に示す。
正極活物質としてLi(Mn0.94Li0.02Al0.02Co0.02)2O4とLiNi0.80Mn0.10Co0.10O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表4に示す。
正極活物質としてLi(Mn0.94Li0.02Al0.02Co0.02)2O4とLiNi0.70Mn0.20Co0.10O2との重量比85:15の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表4に示す。
正極活物質としてLi(Mn0.94Li0.02Al0.02Co0.02)2O4とLiNi0.70Mn0.20Co0.10O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表4に示す。
正極活物質としてLi(Mn0.94Li0.02Al0.02Co0.02)2O4とLiNi0.60Mn0.20Co0.20O2との重量比85:15の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表4に示す。
正極活物質としてLi(Mn0.94Li0.02Al0.02Co0.02)2O4とLiNi0.60Mn0.20Co0.20O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表4に示す。
正極活物質としてLi(Mn0.94Li0.02Al0.02Co0.02)2O4とLiNi0.60Mn0.20Co0.20O2との重量比30:70の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表4に示す。
正極活物質としてLi(Mn0.94Li0.02Al0.02Co0.02)2O4とLiNi0.50Mn0.30Co0.20O2との重量比85:15の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表4に示す。
正極活物質としてLi(Mn0.94Li0.02Al0.02Co0.02)2O4とLiNi0.50Mn0.30Co0.20O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表4に示す。
正極活物質としてLi(Mn0.94Li0.02Al0.02Co0.02)2O4とLiNi0.50Mn0.30Co0.20O2との重量比30:70の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表4に示す。
正極活物質としてLi(Mn0.95Li0.01Mg0.01Al0.01Co0.01B0.01)2O4とLiNi0.80Co0.20O2との重量比85:15の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表4に示す。
正極活物質としてLi(Mn0.95Li0.01Mg0.01Al0.01Co0.01B0.01)2O4とLiNi0.80Co0.20O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表4に示す。
正極活物質としてLi(Mn0.95Li0.01Mg0.01Al0.01Co0.01B0.01)2O4とLiNi0.80Co0.15Al0.05O2との重量比85:15の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表4に示す。
正極活物質としてLi(Mn0.95Li0.01Mg0.01Al0.01Co0.01B0.01)2O4とLiNi0.80Co0.15Al0.05O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表4に示す。
正極活物質としてLi(Mn0.95Li0.01Mg0.01Al0.01Co0.01B0.01)2O4とLiNi0.80Mn0.10Co0.10O2との重量比85:15の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表4に示す。
正極活物質としてLi(Mn0.95Li0.01Mg0.01Al0.01Co0.01B0.01)2O4とLiNi0.80Mn0.10Co0.10O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表4に示す。
正極活物質としてLi(Mn0.95Li0.01Mg0.01Al0.01Co0.01B0.01)2O4とLiNi0.70Mn0.20Co0.10O2との重量比85:15の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表4に示す。
正極活物質としてLi(Mn0.95Li0.01Mg0.01Al0.01Co0.01B0.01)2O4とLiNi0.70Mn0.20Co0.10O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表4に示す。
正極活物質としてLi(Mn0.95Li0.01Mg0.01Al0.01Co0.01B0.01)2O4とLiNi0.60Mn0.20Co0.20O2との重量比85:15の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表4に示す。
正極活物質としてLi(Mn0.95Li0.01Mg0.01Al0.01Co0.01B0.01)2O4とLiNi0.60Mn0.20Co0.20O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表4に示す。
正極活物質としてLi(Mn0.95Li0.01Mg0.01Al0.01Co0.01B0.01)2O4とLiNi0.60Mn0.20Co0.20O2との重量比30:70の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表4に示す。
正極活物質としてLi(Mn0.95Li0.01Mg0.01Al0.01Co0.01B0.01)2O4とLiNi0.50Mn0.30Co0.20O2との重量比85:15の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表4に示す。
正極活物質としてLi(Mn0.95Li0.01Mg0.01Al0.01Co0.01B0.01)2O4とLiNi0.50Mn0.30Co0.20O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表4に示す。
正極活物質としてLi(Mn0.95Li0.01Mg0.01Al0.01Co0.01B0.01)2O4とLiNi0.50Mn0.30Co0.20O2との重量比30:70の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表4に示す。
正極活物質としてLi(Mn0.98Li0.02)2O4とLiNi0.50Mn0.30Co0.20O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表5に示す。
正極活物質としてLi(Mn0.95Mg0.05)2O4とLiNi0.50Mn0.30Co0.20O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表5に示す。
正極活物質としてLi(Mn0.95Al0.05)2O4とLiNi0.50Mn0.30Co0.20O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表5に示す。
正極活物質としてLi(Mn0.95Al0.025Co0.025)2O4とLiNi0.50Mn0.30Co0.20O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表5に示す。
正極活物質としてLi(Mn0.98Li0.01Mg0.01)2O4とLiNi0.50Mn0.30Co0.20O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表5に示す。
正極活物質としてLi(Mn0.94Li0.02Mg0.02B0.02)2O4とLiNi0.50Mn0.30Co0.20O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表5に示す。
正極活物質としてLi(Mn0.98Li0.01Al0.01)2O4とLiNi0.50Mn0.30Co0.20O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表5に示す。
正極活物質としてLi(Mn0.95Li0.025Al0.025)2O4とLiNi0.50Mn0.30Co0.20O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表5に示す。
正極活物質としてLi(Mn0.97Li0.01Al0.01Co0.01)2O4とLiNi0.50Mn0.30Co0.20O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表5に示す。
正極活物質としてLi(Mn0.93Li0.02Al0.02Co0.02B0.01)2O4とLiNi0.50Mn0.30Co0.20O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表5に示す。
正極活物質としてLi(Mn0.95Li0.01Mg0.01Al0.01Co0.01B0.01)2O4とLiNi0.40Mn0.30Co0.30O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表5に示す。
正極活物質としてLi(Mn0.95Li0.01Mg0.01Al0.01Co0.01B0.01)2O4とLiNi0.33Mn0.33Co0.33O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表5に示す。
正極活物質としてLi(Mn0.95Li0.01Mg0.01Al0.01Co0.01B0.01)2O4とLiNi0.30Mn0.30Co0.30Mg0.10O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表5に示す。
正極活物質としてLi(Mn0.95Li0.01Mg0.01Al0.01Co0.01B0.01)2O4とLiNi0.30Mn0.30Co0.30Zr0.10O2との重量比50:50の混合物を用い、化合物No.1の代わりに化合物No.9を用いた以外は、実施例1と同様に二次電池を作製し、実施例1と同様に電池の特性を調べた。結果を表5に示す。
2 負極活物質層
3 正極集電体
4 負極集電体
5 多孔質セパレータ
6 ラミネート外装体
7 ラミネート外装体
8 負極タブ
9 正極タブ
Claims (5)
- 正極および負極が対向配置された電極素子と、非水電解液と、前記電極素子および前記非水電解液を内包する外装体とを有し、
前記非水電解液が、一般式(1)で表される環状スルホン酸エステルを含み、
前記正極における正極活物質が、スピネル構造を有するリチウムマンガン複合酸化物と、層状岩塩構造を有するリチウム遷移金属複合化合物の混合物であり、
前記正極活物質の混合比が、(リチウムマンガン複合酸化物)/(リチウムマンガン複合酸化物+リチウム遷移金属複合化合物)の重量比で、15wt%から50wt%であることを特徴とする非水電解液二次電池。
- 前記一般式(1)中のR1が水素原子であり、R2がCmH2m+1(m=1〜3)であり、R3が−CH2−であることを特徴とする請求項1に記載の非水電解液二次電池。
- 前記スピネル構造を有するリチウムマンガン複合酸化物が、一般式(2)で表されることを特徴とする請求項1または2に記載の非水電解液二次電池;
Li(Mn1−αAα)2O4 (2)
(式(2)中、Aは、Li、Mg、Al、Co、Bからなる群より選ばれる1つ、または2つ以上の元素である。αは、0<α≦0.1である。)。 - 前記層状岩塩構造を有するリチウム遷移金属複合化合物が、一般式(3)で表されることを特徴とする請求項1乃至3のいずれか1項に記載の非水電解液二次電池。
LiβMeO2 (3)
(式(3)中、Meは、Niを必ず含み、かつ、Co、Al、Mn、Mg、Zrからなる群より選ばれる1つ、または2つ以上の元素からなる。βは、0.98≦β≦1.02である。) - 電極素子と非水電解液と外装体とを有する非水電解液二次電池の製造方法であって、
正極活物質を含む正極と、負極と、を対向配置して電極素子を作製する工程と、
前記電極素子と、非水電解液と、を外装体の中に封入する工程と、
を含み、
前記非水電解液が式(1)で表される環状スルホン酸エステルを含み、
前記正極活物質がスピネル構造を有するリチウムマンガン複合酸化物と、層状岩塩構造を有するリチウム遷移金属複合化合物とを含み、
前記正極活物質の混合比が、(リチウムマンガン複合酸化物)/(リチウムマンガン複合酸化物+リチウム遷移金属複合化合物)の重量比で、15wt%から50wt%であることを特徴とする、非水電解液二次電池の製造方法;