JP5935502B2 - 積層シート用接着剤組成物 - Google Patents
積層シート用接着剤組成物 Download PDFInfo
- Publication number
- JP5935502B2 JP5935502B2 JP2012114065A JP2012114065A JP5935502B2 JP 5935502 B2 JP5935502 B2 JP 5935502B2 JP 2012114065 A JP2012114065 A JP 2012114065A JP 2012114065 A JP2012114065 A JP 2012114065A JP 5935502 B2 JP5935502 B2 JP 5935502B2
- Authority
- JP
- Japan
- Prior art keywords
- adhesive
- sheet
- adhesive composition
- laminated
- meth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
CH2=C(R1)−CO−OZ (I)
式中、R1は水素原子、またはメチル基、Zは炭素数4〜25の炭化水素基を表す。
即ち、本発明に係る積層シート用接着剤組成物は、アクリルポリオール(A)と、ポリイソシアネート(B)とを含有してなる積層シート用接着剤組成物であって、前記アクリルポリオール(A)の数平均分子量が10,000〜100,000であり、かつ、水酸基価が1〜100mgKOH/gであり、さらに、ガラス転移温度(Tg)が−25℃を越え、10℃以下であり、前記アクリルポリオール(A)に由来する水酸基と、前記ポリイソシアネート(B)に由来するイソシアネート基との当量比NCO/OHが、0.1〜3であるものである(但し、2層以上のシート状部材を具備した太陽電池用裏面保護シートの製造に用いられ、前記シート状部材同士を接合するための接着剤層の少なくとも一部を形成する用途に用いられるものを除く)。
前記ポリイソシアネート(B)の好ましい例として、脂環式ジイソシアネート又は脂肪族ジイソシアネートから誘導されるポリイソシアネートを含むものが挙げられる。
アクリルポリオール(A)は、水酸基含有モノ(メタ)アクリレートモノマーと、水酸基を含有しないモノ(メタ)アクリレートモノマーとの共重合体が好ましく用いられる。水酸基含有モノ(メタ)アクリレートモノマーは、1分子中に1個の(メタ)アクリロイル基と1個以上の水酸基を含有するモノマーである。好ましい例として、2価アルコールと(メタ)アクリル酸との反応により得られるモノ(メタ)アクリル酸エステルモノマー、ε−カプロラクトン変性(メタ)アクリルモノマー等が挙げられる。
アクリルポリオール(A)の数平均分子量が同程度であれば、接着力向上の点から、モノ(メタ)アクリレートモノマーの共重合には関与しない部分、即ち、(メタ)アクリル酸部分にエステル結合を介して結合する部分(アルキル基やアルケニル基等の部分。以下「側鎖部分」という)の炭素の数としては、1〜17であることが好ましく、1〜9であることがより好ましく、1〜3であることが更に好ましい。前記側鎖部分は、共重合後、アクリルポリオール(A)の側鎖を形成することとなる。モノ(メタ)アクリレートモノマーの前記側鎖部分の炭素数は1〜30程度であることが一般的であるが、アクリルポリオール(A)の数平均分子量が同程度であれば、前記側鎖部分が短い程、アクリルポリオール(A)の主鎖が相対的に長くなる。その結果、硬化後の接着層の機械的性質(具体的には伸び率)が向上し、接着力が向上するものと考察される。
さらに、上述の水酸基含有(メタ)アクリレートモノマーと、水酸基を含有しないモノ(メタ)アクリレートモノマーに加えて、その他のモノマー、例えば、(メタ)アクリル酸、マレイン酸、無水マレイン酸等のカルボキシル基含有モノマーやその無水物、あるいはスチレン等のビニルモノマー等を共重合させることができる。なお、水酸基含有(メタ)アクリレートモノマー、水酸基を含有しないモノ(メタ)アクリレートモノマーは、それぞれ独立に、1種類の化合物を用いても、2種類以上の化合物を組み合わせて用いてもよい。その他のモノマーを用いる場合についても同様である。
アクリルポリオールの数平均分子量が10,000未満の場合、エージング工程前の接着剤層の凝集力が不足する傾向にあり、エージング工程前の接着力が小さくなる恐れがある。工業的生産の場合、ロール状に巻き取った状態の積層体は、通常、巻き芯を天地方向にしてエージングされる。エージング工程前の接着力が小さいと、エージングの最中に巻きが崩れ易く、工業的生産には不適である。また、10,000未満では、エージング工程後の凝集力が不足する傾向にあり、これに伴って耐湿熱性が低くなり、デラミネーション等を生じる恐れがある。
また、アクリルポリオールの数平均分子量が100,000を超えると、接着剤の粘度が高くなり、塗工性に問題が生じたり、シート状部材への濡れ性が低下する傾向にあり、その結果エージング工程前の接着力が小さくなる恐れがある。エージングによって初期接着力は、エージング前に比して大きくなるとはいうものの、その後の耐湿熱性試験により徐々に低下し、3000時間経過後は使用下限を下回る恐れがある。
ポリイソシアネート(B)は、例えば、周知のジイソシアネートから誘導された化合物であり、公知の化合物を制限なく利用することができる。例えば、2,4−トリレンジイソシアネート(別名:2,4−TDI)、2,6−トリレンジイソシアネート(別名:2,6−TDI)、キシリレンジイソシアネート(別名:XDI)、ジフェニルメタンジイソシアネート(別名:MDI)、イソホロンジイソシアネート、1,5−ナフタレンジイソシアネート、ヘキサメチレンジイソシアネート(別名:HDI)、ビス(4−イソシアネートシクロヘキシル)メタン、若しくは水添化ジフェニルメタンジイソシアネート等のジイソシアネートから誘導された化合物、即ち、前記ジイソシアネートのヌレート体、トリメチロールプロパンアダクト体、ビウレット型、イソシアネート残基を有するプレポリマー(ジイソシアネートとポリオールから得られる低重合体)、イソシアネート残基を有するウレトジオン体、アロファネート体、若しくはこれらの複合体、及びブロックイソシアネートが挙げられる。ポリイソシアネート(B)は、単一の化合物を単独で、あるいは2種以上を組み合わせて使用できる。
また、硬化速度の速さを重要視する場合には、キシリレンジイソシアネート(別名:XDI)のような、芳香環を有するが、NCOと芳香環の間にアルキレン基があるイソシアネートを使用することが好ましい。硬化速度が速いとエージング時間を短縮できるという点で好ましい。
NCO/OH比=ポリイソシネート必要量(重量部)×(561/OH価)×(NCO%/(42×100))×(100/ポリオール量(固形分重量)) 数式(1)
アクリルポリオールのTgが低すぎると、エージング前の接着剤層はまだ硬化が不十分なので、接着剤組成物から形成した接着剤層は柔らかい。そして、その柔らかさによってシート状部材間において、ある程度の接着力は発現できる。しかし、エージング後に接着剤層が十分硬化しても、原料のアクリルポリオールのTgの低さ故に接着剤層の凝集力不足が顕在化し、大きな接着力を確保することが難しくなる傾向にある。さらに、積層体を長時間、高温高湿度下に置くと接着剤層の凝集力不足が原因で接着力が徐々に低下する傾向にある。
一方、アクリルポリオールのTgが高すぎると、基材への濡れ性が不足する傾向にある。エージング前に比してエージング後の接着力が多少大きくはなるものの、架橋後の硬化接着剤層が硬くなりすぎてしまうので、エージング工程後の接着力が悪化する傾向にある。
本発明において、上述した優れた効果が得られた理由は、アクリルポリオールのTgが低すぎず、かつ、高すぎない温度範囲(具体的には、−40℃越え、10℃以下)とし、その上でさらに、特定の水酸基価、特定のNCO/OH当量比、及び特定の数平均分子量の範囲とすることによって相乗的に分子運動レベルでのアクリルポリオールの運動の活発さを活かし、接着対象への濡れ性と投錨性を向上することができたことによるものと考察している。特に、NCO/OH当量比を0.1〜3の範囲、特に1〜3の範囲で制御することによって、適度な架橋度のバランスを実現しエージング工程後に高い接着力を示すことができたと考察している。しかも、驚くべきことに、エージング前においても高い接着力を発現できることを見出した。さらには、エージング工程後、高温高湿度下に置いた後も高い接着力を維持できることを見出した。
これらのプラスチックフィルムを支持体とし、アクリル系、フッ素系塗料がコーティングされてなるフィルムや、ポリフッ化ビニリデンやアクリル樹脂などが共押出しにより積層されてなる多層フィルムなどを使用することができる。さらに、ウレタン系接着剤層などを介して上記のプラスチックフィルムが複数積層されたシート状部材を用いてもよい。
上記のプラスチックフィルムは、表面がコロナ放電、プラズマ処理、フレーム処理等の物理的処理や、フィルム表面を酸やアルカリなどで改質する化学的処理、フィルム表面に微細な凹凸をつけ、いわゆるシボ状態にするマット加工等などによって、易接着面とされているものを好適に用いることができる。無論、本発明の積層シート用接着剤組成物を、表面未処理素材に適用してもよいことは言うまでもない。
太陽電池用裏面保護シートとして要求される性能、価格、生産性等を勘案して、種々の製造方法を選択したり、さらに組み合わせたりすることができる。
以下、実施例により、本発明をさらに詳細に説明するが、以下の実施例は本発明の権利範囲を何ら制限するものではない。なお、実施例中における各評価は下記の方法に従った。なお、実施例中、部は重量部、%は重量%、水酸基価はmgKOH/gをそれぞれ示す。数平均分子量、ガラス転移温度、水酸基価は以下のようにして求めた。
数平均分子量の測定は、東ソー社製GPC(ゲルパーミエーションクロマトグラフィー)「HPC−8020」を用い、カラムはSHODEX KF−806L 2本、KF−804L 1本、KF−802 1本を用い、溶媒はテトラヒドロフランを用いた。数平均分子量は標準ポリスチレン換算で行った。
ガラス転移温度(Tg)の測定は、セイコーインスツルメンツ社製DSC「RDC220」を用いて行った。下記手法で合成したポリカーボネートウレタンポリオールA−1〜A−21溶液を乾燥した試料、約10mgをアルミニウムパンに量り採り、DSC装置にセットして液体窒素で−100℃まで冷却した後、10℃/minで昇温して得られたDSCチャートからガラス転移温度を求めた。
水酸基価は、試料約2gをピリジン約10mlに溶解した後、予め調整した無水酢酸/ピリジンの体積比が15/85である混合溶液5mlを加え、20時間放置した。その後、水1mlとエタノール10mlを加え、0.1Nの水酸化カリウム(エタノール溶液)で滴定して求めた。指示薬にはフェノールフタレインを用いた。
(合成例1) コンデンサー、窒素導入管、滴下ロート、及び温度計を備えた4口フラスコに、酢酸エチル100重量部を仕込み、80℃に昇温した。次いで、ブチルアクリレート47.2重量部、エチルメタアクリレート51.0重量部、2−ヒドロキシエチルアクリレート1.8重量部、及びアゾビスイソブチルニトリル2.0重量部を予め混合したモノマー液を、滴下ロートより2時間かけて滴下した。その後、1時間反応させ、次いでアゾビスイソブチルニトリル0.2重量部を加えて1時間反応させる工程を、モノマーの転化率が98%以上になるまで行ってから冷却した。そして、酢酸エチルを加えて固形分50%の溶液を得た。
(合成例2〜21) 重合開始剤アゾビスイソブチルニトリルの添加量により分子量を調節した以外は、合成例1と同様にして、表1に示す合成例2〜21のアクリルポリオールを得た。なお、合成例17については、特許文献2にて合成例1として示される組成のアクリルポリオールである。なお、表1中の略語は、下記の通りである。
BA:ブチルアクリレート、EMA:エチルメタアクリレート、EA:エチルアクリレート、St:スチレン、CHMA:シクロヘキシルメタクリレート、2EHA:2−エチルヘキシルアクリレート、HEA:2−ヒドロキシエチルアクリレート、4HBA:4−ヒドロキシブチルアクリレート、HEMA:ヒドロキシエチルメタクリレート
(実施例2〜4、7〜17、参考例1〜3、比較例1〜6) 固形分換算で100重量部の主剤であるアクリルポリオール(A)に対し、硬化剤であるポリイソシアネート(B)を表2に示す配合比にて配合すると共に、添加剤としてグリシジル基含有シランカップリング剤(「KBM−403」信越化学社製)を3.0重量部、及びジラウリン酸ジオクチル錫(「ネオスタン U−810」、日東化成社製)を0.01重量部配合し、さらに酢酸エチルで固形分が30%になるように調整した。
実施例2〜4、7〜17、参考例1〜3、及び比較例1〜6の各接着剤組成物を用い、ポリエステルフィルム[東レ社製、ルミラーX−10S、厚み50μm]のコロナ処理面に、接着剤組成物を乾燥塗布量:4〜5g/m2となる量でドライラミネーターによって塗布した。そして、溶剤を揮散させた後、もう1枚のポリエステルフィルム[東レ社製、ルミラーX−10S、厚み50μm]のコロナ処理面にラミネートした。その後、40℃で3日間の硬化処理(エージング)を行うことにより接着剤を硬化させて、積層フィルム1を作製した。
実施例2〜4、参考例2及び比較例1〜3の接着剤組成物を用い、前述の積層フィルム1の作製法に準じ、[コロナ処理ポリエステルフィルム/接着剤層/アルミホイル]なる構成の積層フィルム2を作製した。
実施例2〜4、参考例2及び比較例1〜3の接着剤組成物を用い、前述の積層フィルム1の作製法に準じ、シリカ蒸着ポリエステルフィルムの蒸着層が接着剤層に接するようにして、[コロナ処理ポリエステルフィルム/接着剤層/シリカ蒸着ポリエステルフィルム]なる構成の積層フィルム3を作製した。
また、表4、表5に、実施例2〜4、参考例2および比較例1〜3を用いた積層フィルム2、3の初期接着力と85℃、湿度85%雰囲気下において1000時間、2000時間、及び3000時間暴露後の接着力を示す。以下に具体的な評価方法を説明する。
エージング前、及びエージング後の前記積層フィルム1、2、3をそれぞれ200mm×15mmの大きさに切断し、25℃、湿度65%の環境下で6時間静置後、ASTM−D1876−61の試験法に準じ、引張り試験機を用いて、25℃、湿度65%の環境下で、荷重速度300mm/分でT型剥離試験をおこなった。PETフィルム/PETフィルム間、PETフィルム/アルミホイル間、PETフィルム/シリカ蒸着ポリエステルフィルム間の剥離強度(N/15mm巾)を5個の試験片の平均値で示す。
<耐湿熱性試験後の接着力試験>
エージング後の前記積層体をそれぞれ200mm×15mmの大きさに切断し、85℃、湿度85%の環境下で1000時間、2000時間、3000時間静置した。その後、25℃、湿度65%の環境下で6時間静置後、ASTM−D1876−61の試験法に準じ、引張り試験機を用いて、25℃、湿度65%の環境下で、荷重速度300mm/分でT型剥離試験をおこなった。PETフィルム/PETフィルム間、PETフィルム/アルミホイル間、PETフィルム/シリカ蒸着ポリエステルフィルム間の剥離強度(N/15mm巾)を5個の試験片の平均値で示す。
[エージング前の接着力試験]
◎ 実用上優れる:3N/15mm以上
○ 実用域:2〜3N/15mm
△ 実用下限:1〜2N/15mm
× 実用不可:1N/15mm未満
[エージング後の試験、耐湿熱性試験後の接着力試験]
◎ 実用上優れる:5N/15mm以上
○ 実用域:4〜5N/15mm
△ 実用下限:2〜4N/15mm
× 実用不可:2N/15mm未満
Claims (2)
- アクリルポリオール(A)と、ポリイソシアネート(B)とを含有してなる積層シート用接着剤組成物であって、
前記アクリルポリオール(A)の数平均分子量が25,000〜100,000であり、かつ、水酸基価が1〜100mgKOH/gであり、さらに、ガラス転移温度(Tg)が−5℃を越え、10℃以下であり、
前記アクリルポリオール(A)に由来する水酸基と、前記ポリイソシアネート(B)に由来するイソシアネート基との当量比NCO/OHが、0.1〜3である(但し、2層以上のシート状部材を具備した太陽電池用裏面保護シートの製造に用いられ、前記シート状部材同士を接合するための接着剤層の少なくとも一部を形成する用途に用いられるものを除く)積層シート用接着剤組成物。 - 前記ポリイソシアネート(B)が、脂環式ジイソシアネート又は脂肪族ジイソシアネートから誘導されるポリイソシアネートを含むことを特徴とする請求項1に記載の積層シート用接着剤組成物。