JP5656819B2 - ポジ型感光性組成物及びそれを用いたパターン形成方法 - Google Patents
ポジ型感光性組成物及びそれを用いたパターン形成方法 Download PDFInfo
- Publication number
- JP5656819B2 JP5656819B2 JP2011287028A JP2011287028A JP5656819B2 JP 5656819 B2 JP5656819 B2 JP 5656819B2 JP 2011287028 A JP2011287028 A JP 2011287028A JP 2011287028 A JP2011287028 A JP 2011287028A JP 5656819 B2 JP5656819 B2 JP 5656819B2
- Authority
- JP
- Japan
- Prior art keywords
- group
- general formula
- acid
- alkyl group
- repeating unit
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
このため、脂環炭化水素構造を有する樹脂を含有するArFエキシマレーザー用レジストが開発されてきている。例えば、特開2003―167347号公報(特許文献1)、特開2003―223001号公報(特許文献2)には、多環酸分解性繰り返し単位と、非酸分解性繰り返し単位とを有する樹脂を含有する組成物が記載されている。しかしながら、線幅100nm以下のような微細なパターンを形成する際には、解像性能が優れていても、形成したラインパターンが倒れてしまい、デバイス製造時の欠陥となってしまうパターン倒れの問題や、レジストポリマーの疎水性に起因する現像時の現像残渣などによる現像欠陥の問題があった。
しかしながら、従来のレジスト組成物は、未だに不十分な点があり、解像力、孤立DOF、PEB温度依存性について、更なる改良が望まれている。
即ち、線幅100nm以下のような微細なパターンを形成する必要が生ずる中で、特に孤立パターン形成の際、焦点ずれ許容範囲、即ち、デフォーカスラチチュード(DOF)を確保することが難しくなっており、より広いDOF性能を有するレジスト組成物が求められている。
また、口径が大きいウエハーを使用する場合、露光後のホットプレートなどによる加熱
(PEB)における温度のばらつきが、得られるパターンに影響を及ぼすことがわかってきており、このようなPEB温度依存性を改善することが望まれている。
(1)
下記一般式(I−1b)で表される酸分解性繰り返し単位、下記一般式(II)で表される非酸分解性繰り返し単位、及び水酸基又はシアノ基を有する下記一般式(AIIa)で表される繰り返し単位を有する、酸の作用によりアルカリ現像液に対する溶解速度が増大する樹脂(A)、および活性光線又は放射線の照射により酸を発生する下記一般式(ZI)又は(ZII)で表される化合物(B)を含有することを特徴とするポジ型感光性組成物。
一般式(I−1b)に於いて、
Xa1は、水素原子、アルキル基、シアノ基又はハロゲン原子を表す。
Rx1は、直鎖若しくは分岐状アルキル基又は単環若しくは多環環状アルキル基を表す。
Rx4は、直鎖若しくは分岐状アルキル基又は単環環状アルキル基を表す。
n1は、4又は5を表す。
n2は、0〜3を表す。
一般式(II)に於いて、
Xa2は、水素原子、アルキル基、シアノ基又はハロゲン原子を表す。
A2は、単結合又は2価の連結基を表す。
ACGは、非酸脱離性炭化水素基を表す。
一般式(AIIa)中、
R 1c は、水素原子、メチル基、トリフロロメチル基又はヒドロキメチル基を表す。
R 2c 〜R 4c は、各々独立に、水素原子、水酸基又はシアノ基を表す。ただし、R 2c 〜R 4c のうち少なくとも1つは、水酸基又はシアノ基を表す。
上記一般式(ZI)及び(ZII)において、
R201、R202及びR203は、各々独立に、有機基を表す。R201〜R203のうち2つが結合して環構造を形成してもよく、環内に酸素原子、硫黄原子、エステル結合、アミド結合又はカルボニル基を含んでいてもよい。
R204及びR205は、各々独立に、アリール基、アルキル基又はシクロアルキル基を表す。
X−は、下記一般式(AN1)又は(AN2)で表される非求核性アニオンを表す。
上記一般式(AN1)及び(AN2)に於いて、
Rc1は、下記一般式で表される有機基を表す。
上記一般式に於いて、
Rc6は、炭素数4以下のパーフロロアルキレン基、1〜4個のフッ素原子及び/又は1〜3個のフロロアルキル基で置換されたフェニレン基を表す。
Axは、−O−、−CO2−、−S−、−SO3−又は−SO2N(Rd1)−を表す。Rd1は、水素原子又はアルキル基を表し、Rc7と結合して環構造を形成してもよい。
Rc7は、フッ素原子を置換基として有さない直鎖状若しくは分岐状アルキル基、フッ素原子を置換基として有さない単環若しくは多環環状アルキル基、又はフッ素原子を置換基として有さないアリール基を表す。
(2)
樹脂(A)が、ラクトン基を有する繰り返し単位を更に有することを特徴とする(1)に記載のポジ型感光性組成物。
(3)
(1)又は(2)に記載のポジ型感光性組成物により形成された感光性膜。
(4)
(1)又は(2)に記載のポジ型感光性組成物により、感光性膜を形成し、該感光性膜を露光、現像する工程を含むことを特徴とするパターン形成方法。
(5)
液浸媒体を介して露光を行うことを特徴とする(4)に記載のパターン形成方法。
本発明は、上記(1)〜(5)に記載の構成を有するものであるが、以下、他の事項も含めて記載している。
<1>下記一般式(I)で表される酸分解性繰り返し単位及び下記一般式(II)で表される非酸分解性繰り返し単位を有する、酸の作用によりアルカリ現像液に対する溶解速度が増大する樹脂(A)、および活性光線又は放射線の照射により酸を発生する化合物(B)を含有することを特徴とするポジ型感光性組成物。
Xa1は、水素原子、アルキル基、シアノ基又はハロゲン原子を表す。
A1は、単結合又は2価の連結基を表す。
ALGは、酸脱離性炭化水素基を表す。
一般式(II)に於いて、
Xa2は、水素原子、アルキル基、シアノ基又はハロゲン原子を表す。
A2は、単結合又は2価の連結基を表す。
ACGは、非酸脱離性炭化水素基を表す。
Xa1は、水素原子、アルキル基、シアノ基又はハロゲン原子を表す。
Rx1〜Rx3は、それぞれ独立に、直鎖若しくは分岐状アルキル基又は単環若しくは多環環状アルキル基を表す。Rx1〜Rx3の内の少なくとも2つが結合して、単環若しくは多環環状アルキル基を形成してもよい。
Xa1は、水素原子、アルキル基、シアノ基又はハロゲン原子を表す。
Rx1及びRx2は、それぞれ独立に、直鎖若しくは分岐状アルキル基又は単環環状アルキル基を表す。
Rx4は、直鎖若しくは分岐状アルキル基又は単環環状アルキル基を表す。
n1は、4又は5を表す。
n2は、0〜3を表す。
Xa2は、水素原子、アルキル基、シアノ基又はハロゲン原子を表す。
Rx5は、直鎖若しくは分岐状アルキル基又は単環環状アルキル基を表す。
n3は、4又は5を表す。
n4は、0〜3を表す。
R100は、水素原子又はアルキル基を表す。
R101は、アルキル基を表す。
R102は、アルキル基を表す。R102が複数個ある場合に、複数個のR102は、同一であっても異なっていてもよく、R102どうしで環を形成してもよい。
R103は、第三級炭素原子を有し、該第三級炭素原子が式中の環状構造に結合している連結基を表す。
Aは、炭素原子及び水素原子で構成される、環状構造を有する非脱離基を表す。
nは、0〜5の整数を表す。
mは、0〜n+2の整数を表す。
R100は、水素原子又はアルキル基を表す。
尚、本明細書に於ける基(原子団)の表記に於いて、置換及び無置換を記していない表記は、置換基を有さないものと共に置換基を有するものをも包含するものである。例えば、「アルキル基」とは、置換基を有さないアルキル基(無置換アルキル基)のみならず、置換基を有するアルキル基(置換アルキル基)をも包含するものである。
Xa1は、水素原子、アルキル基、シアノ基又はハロゲン原子を表す。
A1は、単結合又は2価の連結基を表す。
ALGは、酸脱離性基を表す。
一般式(II)に於いて、
Xa2は、水素原子、アルキル基、シアノ基又はハロゲン原子を表す。
A2は、単結合又は2価の連結基を表す。
ACGは、非酸脱離性炭化水素基を表す。
そして、特に一般式(I)で表される繰り返し単位及び一般式(II)で表される繰り返し単位の内の少なくとも一方が多環炭化水素構造を有さない樹脂(A1)を用いることで、パターン倒れ及び現像欠陥の点で優れたポジ型感光性組成物を提供でき、そして、特に一般式(I)で表される繰り返し単位が下記一般式(1)で表される繰り返し単位及び下記一般式(2)で表される繰り返し単位から選ばれる少なくとも1種類の繰り返し単位であり、一般式(II)で表される繰り返し単位が下記一般式(3)で表される繰り返し単位である樹脂(A2)を用いることで、解像力、孤立DOF、PEB温度依存性の点で優れたポジ型感光性組成物を提供できる。
本発明のポジ型感光性組成物に用いられる酸の作用によりアルカリ現像液に対する溶解速度が増大する樹脂(A)は、下記一般式(I)で表される酸分解性繰り返し単位及び下記一般式(II)で表される非酸分解性繰り返し単位を有する樹脂である。
また、樹脂(A)は、一般式(I)で表される繰り返し単位及び一般式(II)で表される繰り返し単位の内の少なくとも一方が多環炭化水素構造を有さない樹脂(A1)であることが好ましい。
Xa1は、水素原子、アルキル基、シアノ基又はハロゲン原子を表す。
A1は、単結合又は2価の連結基を表す。
ALGは、酸脱離性炭化水素基を表す。
一般式(II)に於いて、
Xa2は、水素原子、アルキル基、シアノ基又はハロゲン原子を表す。
A2は、単結合又は2価の連結基を表す。
ACGは、非酸脱離性炭化水素基を表す。
A1は、単結合又は2価の連結基を表す。好ましい2価の連結基は、−CO2−とアルキレン基とが連結した−CO2−アルキレン基−である。−CO2−アルキレン基−に於けるアルキレン基としては、メチレン、ノルボルナンから水素原子が2つ取れて2価の連結基となったもの、アダマンタンから水素原子が2つ取れて2価の連結基となったものが挙げられる。
ALGは、酸脱離性炭化水素基であり、酸の作用により式中の酸素原子から脱離してカルボキシル基を生成させるものであれば、いずれのものでも用いることができるが、好ましくは、式中の酸素原子に結合している3級炭素原子を有する炭化水素基である。
Xa1は、水素原子、アルキル基、シアノ基又はハロゲン原子を表す。
Rx1〜Rx3は、それぞれ独立に、直鎖若しくは分岐状アルキル基又は単環若しくは多環環状アルキル基を表す。Rx1〜Rx3の内の少なくとも2つが結合して、単環若しくは多環環状アルキル基を形成してもよい。
Rx1〜Rx3の直鎖若しくは分岐状アルキル基としては、メチル基、エチル基、n−プロピル基、イソプロピル基、n−ブチル基、イソブチル基、t−ブチル基などの炭素数1〜4のものが好ましい。
Rx1〜Rx3の単環若しくは多環環状アルキル基としては、シクロペンチル基、シクロヘキシル基などの炭素数3〜10の単環環状アルキル基、ノルボルニル基、テトラシクロデカニル基、テトラシクロドデカニル基、アダマンチル基などの炭素数7〜15の多環環状アルキル基が好ましい。
Rx1〜Rx3の内の少なくとも2つが結合して形成される、単環若しくは多環環状アルキル基としては、シクロペンチル基、シクロヘキシル基などの炭素数3〜10の単環環状アルキル基、ノルボルニル基、テトラシクロデカニル基、テトラシクロドデカニル基、アダマンチル基などの炭素数7〜15の多環環状アルキル基が好ましい。Rx1が、メチル基又はエチル基であり、Rx2とRx3が結合して上述の単環若しくは多環環状アルキル基を形成している様態が好ましい。
Xa1は、水素原子、アルキル基、シアノ基又はハロゲン原子を表す。
Rx1及びRx2は、それぞれ独立に、直鎖若しくは分岐状アルキル基又は単環環状アルキル基を表す。
Rx4は、直鎖若しくは分岐状アルキル基又は単環環状アルキル基を表す。
n1は、4又は5を表す。
n2は、0〜3を表す。
Rx1及びRx2としての直鎖若しくは分岐状アルキル基又は単環環状アルキル基は、一般式(I−1)に於けるRx1及びRx2としての直鎖若しくは分岐状アルキル基又は単環環状アルキル基と同様である。
Rx4に於ける、直鎖若しくは分岐状アルキル基又は単環環状アルキル基としては、前記Rx1及びRx2に於ける、直鎖若しくは分岐状アルキル基又は単環環状アルキル基と同様のものを挙げることができる。
A2は、一般式(I)に於ける、A1と同様のものである。
ACGの非酸脱離性炭化水素基は、酸の作用により式中の酸素原子から脱離しない炭化水素基であればいずれでもよいが、炭素原子と水素原子のみからなる炭化水素基であることが好ましく、極性置換基を有さないことがより好ましい。ACGの非酸脱離性炭化水素基としては、酸の作用により式中の酸素原子から脱離しない直鎖若しくは分岐状アルキル基、単環若しくは多環環状アルキル基が挙げられる。具体的には、メチル基、エチル基、n−プロピル基、イソプロピル基、イソブチル基、ネオペンチル基などの炭素数1〜10の直鎖若しくは分岐状アルキル基、シクロペンチル基、シクロヘキシル基、シクロヘプチル基などの炭素数3〜10の単環環状アルキル基、ノルボルニル基、テトラシクロデカニル基、テトラシクロドデカニル基、アダマンチル基、ジアマンチル基、テトラヒドロデカリン基などの炭素数7〜15の多環環状アルキル基が好ましい。単環若しくは多環環状アルキル基は、更に、置換基として直鎖若しくは分岐状アルキル基、単環若しくは多環環状アルキル基が置換していてもよい。
Xa2は、水素原子、アルキル基、シアノ基又はハロゲン原子を表す。
Rx5は、直鎖若しくは分岐状アルキル基又は単環環状アルキル基を表す。
n3は、4又は5を表す。
n4は、0〜3を表す。
Rx5は、一般式(I−1a)〜(I−1b)に於ける、Rx4と同様のものである。
ラクトン基としては、ラクトン構造を有していればいずれの基でも用いることができるが、好ましくは5〜7員環ラクトン構造を含有する基であり、5〜7員環ラクトン構造にビシクロ構造、スピロ構造を形成する形で他の環構造が縮環しているものが好ましい。下記一般式(LC1−1)〜(LC1−16)のいずれかで表されるラクトン構造を有する基を有する繰り返し単位を有することがより好ましい。また、ラクトン構造を有する基が主鎖に直接結合していてもよい。好ましいラクトン構造としては(LC1−1)、(LC1−4)、(LC1−5)、(LC1−6)、(LC1−13)、(LC1−14)であり、特に好ましくは(LC1−4)である。特定のラクトン構造を用いることでラインエッジラフネス、現像欠陥が良好になる。
Rb0は、水素原子、ハロゲン原子又は炭素数1〜4のアルキル基を表す。Rb0のアルキル基が有していてもよい好ましい置換基としては、水酸基、ハロゲン原子が挙げられる。
Rb0のハロゲン原子としては、フッ素原子、塩素原子、臭素原子、沃素原子を挙げることができる。
Rb0は、水素原子又はメチル基が好ましい。
Abは、単結合、アルキレン基、単環または多環の脂環炭化水素構造を有する2価の連結基、エーテル基、エステル基、カルボニル基、カルボキシル基、又はこれらを組み合わせた2価の連結基を表す。好ましくは、単結合、−Ab1−CO2−で表される2価の連結基である。Ab1は、直鎖、分岐アルキレン基、単環または多環のシクロアルキレン基であり、好ましくはメチレン基、エチレン基、シクロヘキシル基、アダマンチル基、ノルボルニル基である。
Vは、一般式(LC1−1)〜(LC1−16)のうちのいずれかで示される基を表す。
水酸基又はシアノ基を有する繰り返し単位は、水酸基又はシアノ基で置換された脂環炭化水素構造を有する繰り返し単位であることが好ましい。水酸基又はシアノ基で置換された脂環炭化水素構造の脂環炭化水素構造としては、アダマンチル基、ジアマンチル基、ノルボルナン基が好ましい。好ましい水酸基又はシアノ基で置換された脂環炭化水素構造としては、下記一般式(VIIa)〜(VIId)で表される部分構造が好ましい。
R2c〜R4cは、各々独立に、水素原子、水酸基又はシアノ基を表す。ただし、R2c〜R4cのうち少なくとも1つは、水酸基又はシアノ基を表す。好ましくは、R2c〜R4cのうち1つまたは2つが水酸基で残りが水素原子である。(VIIa)において更に好ましくはR2c〜R4cのうち2つが水酸基で残りが水素原子である。
R1cは、水素原子、メチル基、トリフロロメチル基又はヒドロキメチル基を表す。
R2c〜R4cは、一般式(VIIa)〜(VIId)に於ける、R2c〜R4cと同義である。
R50〜R55は、それぞれ独立に、水素原子、フッ素原子又はアルキル基を表す。但し、R50〜R55の内、少なくとも1つは、フッ素原子又は少なくとも1つの水素原子がフッ素原子で置換されたアルキル基を表し、R50〜R55の全てがフッ素原子であることが好ましい。
酸基を有する繰り返し単位を含有することによりコンタクトホール用途での解像性が増す。酸基を有する繰り返し単位としては、アクリル酸、メタクリル酸による繰り返し単位のような樹脂の主鎖に直接、酸基が結合している繰り返し単位、あるいは連結基を介して樹脂の主鎖に酸基が結合している繰り返し単位、さらには酸基を有する重合開始剤や連鎖移動剤を重合時に用いてポリマー鎖の末端に導入、のいずれも好ましく、連結基は単環または多環の環状炭化水素構造を有していてもよい。最も好ましくはアクリル酸、メタクリル酸による繰り返し単位である。
酸基を有する繰り返し単位の含有量は、ポリマー中の全繰り返し単位に対し、1〜20mol%が好ましく、より好ましくは3〜15mol%、更に好ましくは5〜10mol%である。
(1)塗布溶剤に対する溶解性、
(2)製膜性(ガラス転移点)、
(3)アルカリ現像性、
(4)膜べり(親疎水性、アルカリ可溶性基選択)、
(5)未露光部の基板への密着性、
(6)ドライエッチング耐性、
等の微調整が可能となる。
本発明のポジ型感光性組成物において、樹脂(A)の総量は、組成物の全固形分中60〜99質量%が好ましく、より好ましくは80〜98質量%である。
樹脂(A)は、パターン倒れ及び現像欠陥の点で、一般式(I)で表される繰り返し単位及び一般式(II)で表される繰り返し単位の内の少なくとも一方が多環炭化水素構造を有さない樹脂(A1)であることが好ましく、一般式(I)に於ける、ALG及び一般式(II)に於ける、ACGの両方が、多環炭化水素構造を有さないことがより好ましい。
なお、樹脂(A2)についても、一般式(1)で表される繰り返し単位及び下記一般式
(2)で表される繰り返し単位から選ばれる少なくとも1種類の繰り返し単位、及び、一般式(3)で表される繰り返し単位の少なくとも一方が多環炭化水素構造を有さないことが好ましく、両方が多環炭化水素構造を有さないことがより好ましい。
R100は、水素原子又はアルキル基を表す。
R101は、アルキル基を表す。
R102は、アルキル基を表す。R102が複数個ある場合に、複数個のR102は、同一であっても異なっていてもよく、R102どうしで環を形成してもよい。
R103は、第三級炭素原子を有し、該第三級炭素原子が式中の環状構造に結合している連結基を表す。
Aは、炭素原子及び水素原子で構成される、環状構造を有する非脱離基を表す。
nは、0〜5の整数を表す。
mは、0〜n+2の整数を表す。
R101のアルキル基は、炭素数1〜8の直鎖状又は分岐状アルキル基が好ましく、例えば、メチル基、エチル基、n−プロピル基、イソプロピル基、直鎖状又は分岐状の、ブチル基、ペンチル基、ヘキシル基、ヘプチル基、オクチル基等が挙げられる。R101のアルキル基は、フッ素原子等で置換されていてもよい。
R102のアルキル基は、炭素数1〜12の直鎖状又は分岐状アルキル基が好ましく、例えば、メチル基、エチル基、n−プロピル基、イソプロピル基、直鎖状又は分岐状の、ブチル基、ペンチル基、ヘキシル基、ヘプチル基、オクチル基、ノニル基、デシル基、ウンデシル基、ドデシル基等を挙げることができる。R102のアルキル基は、フッ素原子等で置換されていてもよい。
R103の連結基としては、例えば、−La−C*(Ra)(Rb)−基を挙げることができる。式中、Laは、単結合又はアルキレン基を表す。C*は、第三級炭素原子を表す。Ra及びRbは、各々独立に、アルキル基、シクロアルキル基又はアリール基を表す。R103の連結基は、Laが単結合で、Ra及びRbがアルキル基であることが好ましく、Laが単結合で、Ra及びRbがメチル基であることがより好ましい。
Aは、炭素原子及び水素原子で構成され、環状構造を有し、酸の作用により酸素原子から脱離しない非脱離基である。Aの非脱離基の炭素数は、6〜50が好ましく、6〜25がより好ましい。Aの非脱離基としては、例えば、シクロアルキル基、アリール基の単独及びこれらを結合した基であり、第一級炭素原子又は第二級炭素原子によって酸素原子に結合した基を挙げることができる。シクロアルキル基は、単環型でも、多環型でもよい。単環型としては、例えば、シクロプロピル基、シクロブチル基、シクロペンチル基、シクロへキシル基、シクロオクチル基等を挙げることができる。多環型としては、例えば、アダマンチル基、ノルボルニル基、イソボロニル基、カンファニル基、ジシクロペンチル基、α−ピネル基、トリシクロデカニル基、テトラシクロドデシル基、アンドロスタニル基、ジアマンチル基等を挙げることができる。アリール基は、炭素数6〜14のアリール基が好ましく、例えば、フェニル基、ナフチル基、アントリル基、フェナントリル基、ビフェニル残基(ビフェニルから水素原子が1個失われることによって形成される基)、p−テルフェニル残基(p−テルフェニルから水素原子が1個失われることによって形成される基)等を挙げることができる。Aの非脱離基は、アルキル基等で置換されていてもよい。
一般式(3)で表される繰り返し単位は、酸の作用により分解しない。
樹脂(A2)は、更に、下記一般式(4)で表される繰り返し単位を有することが好ましい。
R100は、水素原子又はアルキル基を表す。
アルカリ可溶性基としては、フェノール性水酸基、カルボン酸基、フッ素化アルコール基、スルホン酸基、スルホンアミド基、スルホニルイミド基、(アルキルスルホニル)(アルキルカルボニル)メチレン基、(アルキルスルホニル)(アルキルカルボニル)イミド基、ビス(アルキルカルボニル)メチレン基、ビス(アルキルカルボニル)イミド基、ビス(アルキルスルホニル)メチレン基、ビス(アルキルスルホニル)イミド基、トリス(アルキルカルボニル)メチレン基、トリス(アルキルスルホニル)メチレン基を有する基等が挙げられる。
好ましいアルカリ可溶性基としては、カルボン酸基、フッ素化アルコール基(好ましくはヘキサフルオロイソプロパノール)、スルホン酸基が挙げられる。
酸分解性基として好ましい基は、これらのアルカリ可溶性基の水素原子を酸で脱離する基で置換した基である。
酸分解性基としては好ましくは、クミルエステル基、エノールエステル基、アセタールエステル基、第3級のアルキルエステル基等である。更に好ましくは、第3級アルキルエステル基である。
R11は、メチル基、エチル基、n−プロピル基、イソプロピル基、n−ブチル基、イソブチル基又はsec−ブチル基を表し、Zは、炭素原子とともに多環のシクロアルキル基を形成するのに必要な原子団を表す。
R12〜R16は、各々独立に、炭素数1〜4個の、直鎖もしくは分岐のアルキル基又は多環のシクロアルキル基を表す。但し、R12〜R14のうちの少なくとも1つ、もしくはR15、R16のいずれかは、多環のシクロアルキル基を表す。
R17〜R21は、各々独立に、水素原子、炭素数1〜4個の、直鎖もしくは分岐のアルキル基又は多環のシクロアルキル基を表す。但し、R17〜R21のうちの少なくとも1つは、多環のシクロアルキル基を表す。また、R19、R21のいずれかは、炭素数1〜4個の、直鎖もしくは分岐のアルキル基又は多環のシクロアルキル基を表す。
R22〜R25は、各々独立に、水素原子、炭素数1〜4個の、直鎖もしくは分岐のアルキル基又は多環のシクロアルキル基を表す。但し、R22〜R25のうちの少なくとも1つは、多環のシクロアルキル基を表す。また、R23とR24は、互いに結合して環を形成していてもよい。
R11’及びR12’は、各々独立に、水素原子、シアノ基、ハロゲン原子又はアルキル基を表す。
Z’は、結合した2つの炭素原子(C−C)を含み、脂環式構造を形成するための原子団を表す。
R13’〜R16’は、各々独立に、水素原子、ハロゲン原子、シアノ基、−COOH、−COOR5、酸の作用により分解する基、−C(=O)−X−A’−R17’、アルキル基又はシクロアルキル基を表す。Rl3’〜R16’のうち少なくとも2つが結合して環を形成してもよい。
ここで、R5は、アルキル基、シクロアルキル基又はラクトン構造を有する基を表す。
Xは、酸素原子、硫黄原子、−NH−、−NHSO2−又は−NHSO2NH−を表す。
A’は、単結合又は2価の連結基を表す。
R17’は、−COOH、−COOR5、−CN、水酸基、アルコキシ基、−CO−NH−R6、−CO−NH−SO2−R6又はラクトン構造を有する基を表す。
R6は、アルキル基又はシクロアルキル基を表す。
nは、0又は1を表す。
(炭素数1〜4)、カルボキシル基、アルコキシカルボニル基(炭素数2〜6)が挙げられる。上記のアルキル基、アルコキシ基、アルコキシカルボニル基等が、更に有していてもよい置換基としては、水酸基、ハロゲン原子、アルコキシ基を挙げることができる。
Rは、水素原子、ハロゲン原子又は1〜4個の炭素原子を有する直鎖もしくは分岐のアルキル基を表す。複数のRは、各々同じでも異なっていてもよい。
Aは、単結合、アルキレン基、エーテル基、チオエーテル基、カルボニル基、エステル基、アミド基、スルホンアミド基、ウレタン基、又はウレア基よりなる群から選択される単独あるいは2つ以上の基の組み合わせを表す。好ましくは単結合である。
Rp1は、上記一般式(pI)〜(pV)のいずれかの基を表す。
(pV)で示される脂環式炭化水素を含む部分構造を有する繰り返し単位、一般式(II−AB)で表される繰り返し単位、及び後記共重合成分の繰り返し単位のうち少なくとも1種の繰り返し単位に含有することができる。
Rb0は、水素原子、ハロゲン原子、又は炭素数1〜4のアルキル基を表す。Rb0のアルキル基が有していてもよい好ましい置換基としては、水酸基、ハロゲン原子が挙げられる。Rb0のハロゲン原子としては、フッ素原子、塩素原子、臭素原子、沃素原子を挙げることができる。Rb0は水素原子、メチル基が好ましい。
Abは、アルキレン基、単環又は多環の脂環炭化水素構造を有する2価の連結基、単結合、エーテル基、エステル基、カルボニル基、カルボキシル基、又はこれらを組み合わせた2価の基を表す。好ましくは単結合、−Ab1−CO2−で表される連結基である。Ab1は直鎖、分岐アルキレン基、単環又は多環のシクロアルキレン基であり、好ましくはメチレン基、エチレン基、シクロヘキシル基、アダマンチル基、ノルボルニル基である。
Vは、一般式(LC1−1)〜(LC1−16)のうちのいずれかで示される基を表す。
ラクトン構造を有する基を有する繰り返し単位の具体例を以下に挙げるが、本発明はこれらに限定されない。
極性基で置換された脂環炭化水素構造の好ましい例として一般式(VIIa)、(VIIb)で表される構造があげられる。
R2c〜R4cは、各々独立に、水素原子又は水酸基、シアノ基を表す。ただし、R2c〜R4cのうち少なくとも1つは水酸基又はシアノ基を表す。好ましくはR2c〜R4cのうちの1つ又は2つが水酸基で残りが水素原子であり、更に好ましくはR2c〜R4cのうちの2つが水酸基で残りが水素原子である。
R1cは、水素原子、メチル基、トリフロロメチル基又はヒドロキメチル基を表す。
R2c〜R4cは、一般式(VIIa)におけるR2c〜R4cと同様に定義される。
Z2は、−O−又は−N(R41)−を表す。R41は、水素原子、水酸基、アルキル基又は−OSO2−R42を表す。R42は、アルキル基、シクロアルキル基又は樟脳残基を表す。R41及びR42のアルキル基は、ハロゲン原子(好ましくはフッ素原子)等で置換されていてもよい。
R50〜R55は、それぞれ独立に、水素原子、フッ素原子又はアルキル基を表す。但し、R50〜R55の内、少なくとも1つは、フッ素原子又は少なくとも1つの水素原子がフッ素原子で置換されたアルキル基を表す。
Rxaは、水素原子又は有機基(好ましくは酸分解性保護基、アルキル基、シクロアルキル基、アシル基、アルコキシカルボニル基)を表す。
Rxは、水素原子、ハロゲン原子、又は炭素数1〜4のアルキル基を表す。Rxのアルキル基が有していてもよい好ましい置換基としては、水酸基、ハロゲン原子が挙げられる。
Faは、単結合又は直鎖状若しくは分岐状のアルキレン基を表し、好ましくは単結合である。
Fbは、単環又は多環の環状炭化水素基を表す。
Fcは、単結合又は直鎖状若しくは分岐状のアルキレン基(好ましくは単結合、メチレン基)を表す。
F1は、一般式(F1)で表される基を表す。
p1は、1〜3を表す。
Fbにおける環状炭化水素基としてはシクロペンチル基、シクロヘキシル基、ノルボルニル基が好ましい。
(1)塗布溶剤に対する溶解性、
(2)製膜性(ガラス転移点)、
(3)アルカリ現像性、
(4)膜べり(親疎水性、アルカリ可溶性基選択)、
(5)未露光部の基板への密着性、
(6)ドライエッチング耐性、
等の微調整が可能となる。
(1) 上記一般式(pI)〜(pV)で表される脂環式炭化水素を含む部分構造を有する繰り返し単位を含有するもの(側鎖型)。好ましくは(pI)〜(pV)の構造を有する
(メタ)アクリレート繰り返し単位を有するもの。
(2) 一般式(II−AB))で表される繰り返し単位を有するもの(主鎖型)。但し、(2)においては例えば、更に以下のものが挙げられる。
(3) 一般式(II−AB)で表される繰り返し単位、無水マレイン酸誘導体による繰り返し単位及び(メタ)アクリレートによる繰り返し単位を有するもの(ハイブリッド型)。
樹脂(A2)中、一般式(3)で表される繰り返し単位の含有量は、全繰り返し単位中、1〜50モル%が好ましく、2〜40モル%がより好ましく、5〜30モル%が更により好ましい。
樹脂(A2)中、一般式(4)で表される繰り返し単位の含有量は、全繰り返し単位中、1〜20モル%が好ましく、2〜15モル%がより好ましく、3〜15モル%が更により好ましい。
樹脂(A2)として好ましくは、繰り返し単位のすべてが(メタ)アクリレート繰り返し単位で構成されたものである。この場合、繰り返し単位のすべてがメタクリレート、繰り返し単位のすべてがアクリレート、メタクリレート/アクリレート混合のいずれのものでも用いることができるが、アクリレート繰り返し単位が全繰り返し単位の50mol%以下であることが好ましい。より好ましくは、一般式(1)で表される繰り返し単位及び一般式(2)で表される繰り返し単位から選ばれる繰り返し単位の総量10〜60モル%、一般式(3)で表される繰り返し単位5〜30モル%、一般式(4)で表される繰り返し単位3〜15モル%、一般式(pI)〜(pV)で表される脂環式炭化水素を含む部分構造を有する繰り返し単位25〜50モル%、上記ラクトン構造を含有する繰り返し単位25〜50モル%、上記極性基で置換された脂環炭化水素構造を有する繰り返し単位5〜30モル%含有する共重合ポリマー、または更に一般式(F1)で表される構造を含有する繰り返し単位を5〜20モル%含む共重合ポリマーである。
重合反応は窒素やアルゴンなど不活性ガス雰囲気下で行われることが好ましい。重合開始剤としては市販のラジカル開始剤(アゾ系開始剤、パーオキサイドなど)を用いて重合を開始させる。ラジカル開始剤としてはアゾ系開始剤が好ましく、エステル基、シアノ基、カルボキシル基を有するアゾ系開始剤が好ましい。好ましい開始剤としては、アゾビスイソブチロニトリル、アゾビスジメチルバレロニトリル、ジメチル2,2’−アゾビス(2−メチルプロピオネート)などが挙げられる。所望により開始剤を追加、あるいは分割で添加し、反応終了後、溶剤に投入して粉体あるいは固形回収等の方法で所望のポリマーを回収する。反応の濃度は5〜50質量%であり、好ましくは10〜30質量%である。反応温度は、通常10℃〜150℃であり、好ましくは30℃〜120℃、さらに好ましくは50〜100℃である。
本発明のポジ型感光性組成物は、活性光線又は放射線の照射により酸を発生する化合物
(「酸発生剤」ともいう)を含有する。
そのような酸発生剤としては、光カチオン重合の光開始剤、光ラジカル重合の光開始剤、色素類の光消色剤、光変色剤、あるいはマイクロレジスト等に使用されている活性光線又は放射線の照射により酸を発生する公知の化合物及びそれらの混合物を適宜に選択して使用することができる。
R201、R202及びR203は、各々独立に、有機基を表す。
X−は、非求核性アニオンを表し、好ましくはスルホン酸アニオン、カルボン酸アニオン、ビス(アルキルスルホニル)アミドアニオン、トリス(アルキルスルホニル)メチドアニオン、BF4 −、PF6 −、SbF6 −などが挙げられ、好ましくは炭素原子を含有する有機アニオンである。
Rc1は、有機基を表す。
Rc1における有機基としては、炭素数1−30のものが挙げられ、好ましくは置換していてもよいアルキル基、アリール基、またはこれらの複数が、単結合、−O−、−CO2−、−S−、−SO3−、−SO2N(Rd1)−などの連結基で連結された基を挙げることができる。Rd1は、水素原子又はアルキル基を表し、結合しているアルキル基、アリール基と環構造を形成してもよい。
Rc1の有機基として、より好ましくは1位がフッ素原子またはフロロアルキル基で置換されたアルキル基、フッ素原子またはフロロアルキル基で置換されたフェニル基である。フッ素原子またはフロロアルキル基を有することにより、光照射によって発生した酸の酸性度が上がり、感度が向上する。Rc1において炭素原子を5個以上有する時、少なくとも1つの炭素原子は水素原子が全てフッ素原子で置換されているのではなく、水素原子を有していることが好ましく、水素原子の数がフッ素原子より多いことがより好ましい。炭素数5以上のパーフロロアルキル基を有さないことにより生態への毒性が軽減する。
Rc6は、炭素数4以下、より好ましくは2〜4、更に好ましくは2〜3のパーフロロアルキレン基、1〜4個のフッ素原子及び/又は1〜3個のフロロアルキル基で置換されたフェニレン基を表す。
Axは、連結基(好ましくは、単結合、−O−、−CO2−、−S−、−SO3−、−SO2N(Rd1)−)を表す。Rd1は、水素原子又はアルキル基を表し、Rc7と結合して環構造を形成してもよい。
Rc7は、水素原子、フッ素原子、直鎖状若しくは分岐状アルキル基、単環若しくは多環環状アルキル基又はアリール基を表す。アルキル基、環状アルキル基、アリール基は、置換していてもよいが、置換基としてフッ素原子を有さないことが好ましい。
Rc3、Rc4及びRc5は、各々独立に、有機基を表す。
Rc3、Rc4及びRc5の有機基として、好ましくはRc1における好ましい有機基と同じものを挙げることができる。
Rc3とRc4が結合して環を形成していてもよい。Rc3とRc4が結合して形成される基としては、アルキレン基、アリーレン基が挙げられる。好ましくは炭素数2〜4のパーフロロアルキレン基である。Rc3とRc4が結合して環を形成することにより光照射によって発生した酸の酸性度が上がり、感度が向上し、好ましい。
R201、R202及びR203としての有機基の炭素数は、一般的に1〜30、好ましくは1〜20である。
また、R201〜R203のうち2つが結合して環構造を形成してもよく、環内に酸素原子、硫黄原子、エステル結合、アミド結合、カルボニル基を含んでいてもよい。R201〜R203の内の2つが結合して形成する基としては、アルキレン基(例えば、ブチレン基、ペンチレン基)を挙げることができる。
R201、R202及びR203としての有機基の具体例としては、後述する化合物(ZI−1)、(ZI−2)、(ZI−3)における対応する基を挙げることができる。
アリールスルホニウム化合物は、R201〜R203の全てがアリール基でもよいし、R201〜R203の一部がアリール基で、残りがアルキル基、シクロアルキル基でもよい。
アリールスルホニウム化合物としては、例えば、トリアリールスルホニウム化合物、ジアリールアルキルスルホニウム化合物、アリールジアルキルスルホニウム化合物、ジアリールシクロアルキルスルホニウム化合物、アリールジシクロアルキルスルホニウム化合物を挙げることができる。
アリールスルホニウム化合物のアリール基としてはフェニル基、ナフチル基などのアリール基、インドール残基、ピロール残基、などのヘテロアリール基が好ましく、更に好ましくはフェニル基、インドール残基である。アリールスルホニム化合物が2つ以上のアリール基を有する場合に、2つ以上あるアリール基は同一であっても異なっていてもよい。
アリールスルホニウム化合物が必要に応じて有しているアルキル基は、炭素数1〜15の直鎖若しくは分岐状アルキル基が好ましく、例えば、メチル基、エチル基、プロピル基、n−ブチル基、sec−ブチル基、t−ブチル基等を挙げることができる。
アリールスルホニウム化合物が必要に応じて有しているシクロアルキル基は、炭素数3〜15のシクロアルキル基が好ましく、例えば、シクロプロピル基、シクロブチル基、シクロヘキシル基等を挙げることができる。
R201〜R203のアリール基、アルキル基、シクロアルキル基は、アルキル基(例えば炭素数1〜15)、シクロアルキル基(例えば炭素数3〜15)、アリール基(例えば炭素数6−から14)、アルコキシ基(例えば炭素数1〜15)、ハロゲン原子、水酸基、フェニルチオ基を置換基として有してもよい。好ましい置換基としては炭素数1〜12の直鎖若しくは分岐状アルキル基、炭素数3〜12のシクロアルキル基、炭素数1〜12の直鎖、分岐又は環状のアルコキシ基であり、特に好ましくは炭素数1〜4のアルキル基、炭素数1〜4のアルコキシ基である。置換基は、3つのR201〜R203のうちのいずれか1つに置換していてもよいし、3つ全てに置換していてもよい。また、R201〜R203がアリール基の場合に、置換基はアリール基のp−位に置換していることが好ましい。
化合物(ZI−2)は、式(ZI)におけるR201〜R203が、各々独立に、芳香環を含有しない有機基を表す場合の化合物である。ここで芳香環とは、ヘテロ原子を含有する芳香族環も包含するものである。
R201〜R203としての芳香環を含有しない有機基は、一般的に炭素数1〜30、好ましくは炭素数1〜20である。
R201〜R203は、各々独立に、好ましくはアルキル基、シクロアルキル基、アリル基、ビニル基であり、更に好ましくは直鎖、分岐、環状2−オキソアルキル基、アルコキシカルボニルメチル基、特に好ましくは直鎖、分岐2−オキソアルキル基である。
R201〜R203としてのシクロアルキル基は、好ましくは、炭素数3〜10のシクロアルキル基(シクロペンチル基、シクロヘキシル基、ノルボニル基)を挙げることができる。R201〜R203としてのシクロアルキル基は、環状2−オキソアルキル基であることがより好ましい。
R201〜R203としての直鎖、分岐、環状の2−オキソアルキル基は、好ましくは、上記のアルキル基、シクロアルキル基の2位に>C=Oを有する基を挙げることができる。
R201〜R203としてのアルコキシカルボニルメチル基におけるアルコキシ基としては、好ましくは炭素数1〜5のアルコキシ基(メトキシ基、エトキシ基、プロポキシ基、ブトキシ基、ペントキシ基)を挙げることができる。
R201〜R203は、ハロゲン原子、アルコキシ基(例えば炭素数1〜5)、水酸基、シアノ基、ニトロ基によって更に置換されていてもよい。
R1c〜R5cは、各々独立に、水素原子、アルキル基、シクロアルキル基、アルコキシ基又はハロゲン原子を表す。
R6c及びR7cは、各々独立に、水素原子、アルキル基又はシクロアルキル基を表す。
Rx及びRyは、各々独立に、アルキル基、シクロアルキル基、アリル基又はビニル基を表す。
R1c〜R5c中のいずれか2つ以上、及びRxとRyは、それぞれ結合して環構造を形成しても良く、この環構造は、酸素原子、硫黄原子、エステル結合、アミド結合を含んでいてもよい。R1c〜R5c中のいずれか2つ以上、及びRxとRyが結合して形成する基としては、ブチレン基、ペンチレン基等を挙げることができる。
X−は、非求核性アニオンを表し、一般式(I)に於けるX−の非求核性アニオンと同様のものを挙げることができる。
R1c〜R7cとしてのシクロアルキル基は、好ましくは、炭素数3〜8個のシクロアルキル基(例えば、シクロペンチル基、シクロヘキシル基)を挙げることができる。
R1c〜R5cとしてのアルコキシ基は、直鎖、分岐、環状のいずれであってもよく、例えば炭素数1〜10のアルコキシ基、好ましくは、炭素数1〜5の直鎖及び分岐アルコキシ基(例えば、メトキシ基、エトキシ基、直鎖又は分岐プロポキシ基、直鎖又は分岐ブトキシ基、直鎖又は分岐ペントキシ基)、炭素数3〜8の環状アルコキシ基(例えば、シクロペンチルオキシ基、シクロヘキシルオキシ基)を挙げることができる。
好ましくはR1c〜R5cのうちいずれかが直鎖若しくは分岐状アルキル基、シクロアルキル基、又は直鎖、分岐、環状アルコキシ基であり、更に好ましくはR1c〜R5cの炭素数の和が2〜15である。これにより、より溶剤溶解性が向上し、保存時にパーティクルの発生が抑制される。
Rx及びRyとしてのシクロアルキル基は、R1c〜R7cとしてのシクロアルキル基と同様のものを挙げることができる。Rx及びRyとしてのシクロアルキル基は、環状2−オキソアルキル基であることがより好ましい。
直鎖若しくは分岐、環状2−オキソアルキル基は、R1c〜R7cとしてのアルキル基、シクロアルキル基の2位に>C=Oを有する基を挙げることができる。
アルコキシカルボニルメチル基におけるアルコキシ基については、R1c〜R5cとしてのアルコキシ基と同様のものを挙げることができる。
Rx、Ryは、好ましくは炭素数4個以上のアルキル基であり、より好ましくは6個以上、更に好ましくは8個以上のアルキル基である。
R204〜R207は、各々独立に、アリール基、アルキル基又はシクロアルキル基を表す。
R204〜R207のアリール基としてはフェニル基、ナフチル基が好ましく、更に好ましくはフェニル基である。
R204〜R207としてのアルキル基は、好ましくは、炭素数1〜10の直鎖若しくは分岐アルキル基(例えば、メチル基、エチル基、プロピル基、ブチル基、ペンチル基)を挙げることができる。
R204〜R207としてのシクロアルキル基は、好ましくは、炭素数3〜10のシクロアルキル基(シクロペンチル基、シクロヘキシル基、ノルボニル基)を挙げることができる。
R204〜R207は、置換基を有していてもよい。R204〜R207が有していてもよい置換基としては、例えば、アルキル基(例えば炭素数1〜15)、シクロアルキル基(例えば炭素数3〜15)、アリール基(例えば炭素数6〜15)、アルコキシ基(例えば炭素数1〜15)、ハロゲン原子、水酸基、フェニルチオ基等を挙げることができる。
X−は、非求核性アニオンを表し、一般式(I)に於けるX−の非求核性アニオンと同様のものを挙げることができる。
Ar3及びAr4は、各々独立に、アリール基を表す。
R206は、アルキル基、シクロアルキル基又はアリール基を表す。
R207及びR208は、各々独立に、アルキル基、シクロアルキル基、アリール基又は電子吸引性基を表す。R207として、好ましくは、アリール基である。R208として、好ましくは、電子吸引性基であり、より好ましくは、シアノ基、フロロアルキル基である。
Aは、アルキレン基、アルケニレン基又はアリーレン基を表す。
更に、活性光線又は放射線の照射により、下記一般式(AC1)〜(AC3)で表される酸を発生する化合物が好ましい。
酸発生剤の組成物中の含量は、ポジ型感光性組成物の全固形分を基準として、0.1〜20質量%が好ましく、より好ましくは0.5〜10質量%、更に好ましくは1〜7質量%である。
本発明のポジ型感光性組成物は、酸の作用により分解する基を有さない樹脂(B2)を含有してもよい。
「酸の作用により分解する基を有さない」とは、本発明のポジ型感光性組成物が通常用いられる画像形成プロセスにおいて酸の作用による分解性が無いかまたは極めて小さく、実質的に酸分解による画像形成に寄与する基を有さないことである。このような樹脂として、アルカリ可溶性基を有する樹脂、アルカリの作用により分解し、アルカリ現像液への溶解性が向上する基を有する樹脂が挙げられる。
当該樹脂としては、(メタ)アクリル酸誘導体から導かれる繰り返し単位及びは脂環オレフィン誘導体から導かれる繰り返し単位から選ばれる繰り返し単位を少なくとも1種類有する樹脂が好ましい。
当該樹脂に含有されるアルカリ可溶性基としては、カルボキシル基、フェノール性水酸基、1位または2位が電子吸引性基で置換された脂肪族水酸基、電子吸引性基で置換されたアミノ基(例えばスルホンアミド基、スルホンイミド基、ビススルホニルイミド基)、電子吸引性基で置換されたメチレン基またはメチン基(例えばケトン基、エステル基から選ばれる少なくとも2つで置換されたメチレン基、メチン基)が好ましい。
樹脂(B2)に含有されるアルカリの作用により分解し、アルカリ現像液中での溶解度が増大する基としては、ラクトン基、酸無水物基が好ましく、より好ましくはラクトン基である。
樹脂(B2)には上記以外の他の繰り返し単位を有してもよい。他の繰り返し単位としては、ドライエッチング耐性、親疎水性、相互作用性などを考慮し、適当な官能基を導入することができる。
他の繰り返し単位としては、水酸基、シアノ基、カルボニル基、エステル基などの極性官能基を有する繰り返し単位、単環または多環環状炭化水素構造を有する繰り返し単位、シリコン原子、ハロゲン原子、フロロアルキル基を有する繰り返し単位またはこれらの複数の官能基を有する繰り返し単位を挙げることができる。
本発明のポジ型感光性組成物には、アルカリ可溶性基、親水基及び酸分解性基(酸の作用により分解し、アルカリ可溶性基または親水性基を放出する基)から選ばれるすくなくとも1つを有する、分子量3000以下の溶解制御化合物(以下、「(C)成分」或いは「溶解制御化合物」ともいう)を加えてもよい。
溶解制御化合物としては、カルボキシル基、スルホニルイミド基、α位がフロロアルキル基で置換された水酸基などのようなアルカリ可溶性基を有する化合物、水酸基やラクトン基、シアノ基、アミド基、ピロリドン基、スルホンアミド基、などの親水性基を有する化合物、または酸分解性基を有する化合物が好ましい。酸分解性基としては、カルボキシル基あるいは水酸基を酸分解性基保護基で保護した基が好ましい。溶解制御化合物としては220nm以下の透過性を低下させないため、芳香環を含有しない化合物を用いるか、芳香環を有する化合物を組成物の固形分に対し20wt%以下の添加量で用いることが好ましい。
好ましい溶解制御化合物としてはアダマンタン(ジ)カルボン酸、ノルボルナンカルボン酸、コール酸などの脂環炭化水素構造を有するカルボン酸化合物、またはそのカルボン酸を酸分解性保護基で保護した化合物、糖類などのポリオール、またはその水酸基を酸分解性保護基で保護した化合物が好ましい。
本発明のポジ型感光性組成物は、露光から加熱までの経時による性能変化を低減あるいは、露光によって発生した酸の膜中拡散性を制御するために、塩基性化合物を含有することが好ましい。
好ましい含窒素塩基性化合物構造として、下記式(A)〜(E)で示される部分構造を有する化合物を挙げることができる。
R250、R251及びR252は、各々独立に、水素原子、炭素数1〜20のアルキル基、炭素数3〜20のシクロアルキル基又は炭素数6〜20のアリール基であり、R250とR251は互いに結合して環を形成してもよい。これらは置換基を有していてもよく、置換基を有するアルキル基及びシクロアルキル基としては、炭素数1〜20のアミノアルキル基又は炭素数3〜20のアミノシクロアルキル基、炭素数1〜20のヒドロキシアルキル基又は炭素数3〜20のヒドロキシシクロアルキル基が好ましい。
また、これらはアルキル鎖中に酸素原子、硫黄原子、窒素原子を含んでも良い。
一般式(E)に於いて、
R253、R254、R255及びR256は、各々独立に、炭素数1〜6のアルキル基又は炭素数3〜6のシクロアルキル基を示す。
本発明のポジ型感光性組成物は、更に、フッ素及び/又はシリコン系界面活性剤(フッ素系界面活性剤、シリコン系界面活性剤及びフッ素原子と珪素原子の両方を含有する界面活性剤)のいずれか、あるいは2種以上を含有することが好ましい。
本発明のポジ型感光性組成物がフッ素及び/又はシリコン系界面活性剤を含有することにより、250nm以下、特に220nm以下の露光光源の使用時に、良好な感度及び解像度で、密着性及び現像欠陥の少ないレジストパターンを与えることが可能となる。
本発明のポジ型感光性組成物は、各成分を所定の溶剤に溶解して用いる。
使用し得る溶剤としては、例えば、エチレンジクロライド、シクロヘキサノン、シクロペンタノン、2−ヘプタノン、γ−ブチロラクトン、メチルエチルケトン、エチレングリコールモノメチルエーテル、エチレングリコールモノエチルエーテル、2−メトキシエチルアセテート、エチレングリコールモノエチルエーテルアセテート、プロピレングリコールモノメチルエーテル、プロピレングリコールモノメチルエーテルアセテート、トルエン、酢酸エチル、乳酸メチル、乳酸エチル、メトキシプロピオン酸メチル、エトキシプロピオン酸エチル、ピルビン酸メチル、ピルビン酸エチル、ピルビン酸プロピル、N,N−ジメチルホルムアミド、ジメチルスルホキシド、N−メチルピロリドン、テトラヒドロフラン等の有機溶剤を挙げることができる。
(S1)水酸基を含有する溶剤と、水酸基を含有しない溶剤とを混合した混合溶剤、
(S2)エステル構造を有する溶剤とケトン構造を有する溶剤とを混合した混合溶剤、
(S3)エステル構造を有する溶剤とラクトン構造を有する溶剤とを混合した混合溶剤、
(S4)エステル構造を有する溶剤とラクトン構造を有する溶剤と水酸基を含有する溶剤とを混合した混合溶剤、
(S5)エステル構造を有する溶剤とカーボネート構造を有する溶剤と水酸基を含有する溶剤とを混合した混合溶剤。
これにより組成物保存時のパーティクル発生を軽減でき、また、塗布時の欠陥の発生を抑制することができる。
水酸基を含有しない溶剤としては、例えば、プロピレングリコールモノメチルエーテルアセテート、エチルエトキシプロピオネート、2−ヘプタノン、γ−ブチロラクトン、シクロヘキサノン、酢酸ブチル、N−メチルピロリドン、N,N−ジメチルアセトアミド、ジメチルスルホキシド等を挙げることができ、これらの内で、プロピレングリコールモノメチルエーテルアセテート、エチルエトキシプロピオネート、2−ヘプタノン、γ−ブチロラクトン、シクロヘキサノン、酢酸ブチルが特に好ましく、プロピレングリコールモノメチルエーテルアセテート、エチルエトキシプロピオネート、2−ヘプタノン、シクロヘキサノンが最も好ましい。
ケトン構造を有する溶剤としてはシクロヘキサノン、2−ヘプタノンなどが挙げられ、好ましくはシクロヘキサノンである。
エステル構造を有する溶剤としてはプロピレングリコールモノメチルエーテルアセテート、エチルエトキシプロピオネート、酢酸ブチルなどが挙げられ、好ましくはプロピレングリコールモノメチルエーテルアセテートである。
ラクトン構造を有する溶剤としてはγ−ブチロラクトンが挙げられる。
カーボネート構造を有する溶剤としてはプロピレンカーボネート、エチレンカーボネートが挙げられ、好ましくはプロピレンカーボネートである。
エステル構造を有する溶剤とケトン構造を有する溶剤との混合比(質量)は、1/99〜99/1、好ましくは10/90〜90/10、更に好ましくは40/60〜80/20である。エステル構造を有する溶剤を50質量%以上含有する混合溶剤が塗布均一性の点で特に好ましい。
エステル構造を有する溶剤とラクトン構造を有する溶剤との混合比(質量)は、70/30〜99/1、好ましくは80/20〜99/1、更に好ましくは90/10〜99/1である。エステル構造を有する溶剤を70質量%以上含有する混合溶剤が経時安定性の点で特に好ましい。
エステル構造を有する溶剤とラクトン構造を有する溶剤と水酸基を含有する溶剤を混合する際は、エステル構造を有する溶剤を30〜80質量%、ラクトン構造を有する溶剤を1〜20質量%、水酸基を含有する溶剤を10〜60質量%含有することが好ましい。
エステル構造を有する溶剤とカーボネート構造を有する溶剤と水酸基を含有する溶剤を混合する際は、エステル構造を有する溶剤を30〜80質量%、カーボネート構造を有する溶剤を1〜20質量%、水酸基を含有する溶剤を10〜60質量%含有することが好ましい。
最適な溶剤を選択することにより現像欠陥性能を改良することができる。
本発明のポジ型感光性組成物には、必要に応じてさらに染料、可塑剤、上記(E)成分以外の界面活性剤、光増感剤、及び現像液に対する溶解性を促進させる化合物等を含有させることができる。
樹脂(A2)を含有するポジ型感光性組成物A2は、組成物Aについて上述した各成分を組成物Aの場合と同様に、使用することができるが、以下に述べる成分を添加することが好ましい。
(D)酸の作用により分解してアルカリ現像液中での溶解度が増大する、分子量3000以下の溶解阻止化合物
組成物A2は、酸の作用により分解してアルカリ現像液中での溶解度が増大する、分子量3000以下の溶解阻止化合物(以下、「溶解阻止剤」ともいう)を含有することが好ましい。
溶解阻止剤としては、220nm以下の透過性を低下させないため、Proceeding of SPIE, 2724,355 (1996)に記載されている酸分解性基を含むコール酸誘導体の様な、酸分解性基を有する脂環族又は脂肪族化合物が好ましい。酸分解性基、脂環式構造としては、前記樹脂(A2)のところで説明したものと同様のものが挙げられる。
本発明における溶解阻止剤の分子量は、3000以下であり、好ましくは300〜3000、更に好ましくは500〜2500である。
組成物A2は、更に(E)界面活性剤を含有することが好ましく、フッ素系及び/又はシリコン系界面活性剤(フッ素系界面活性剤、シリコン系界面活性剤、フッ素原子と珪素原子の両方を有する界面活性剤)のいずれか、あるいは2種以上を含有することがより好ましい。
フッ素系及び/又はシリコン系界面活性剤としては、例えば特開昭62−36663号公報、特開昭61−226746号公報、特開昭61−226745号公報、特開昭62−170950号公報、特開昭63−34540号公報、特開平7−230165号公報、特開平8−62834号公報、特開平9−54432号公報、特開平9−5988号公報、特開2002−277862号公報、米国特許第5405720号明細書、同5360692号明細書、同5529881号明細書、同5296330号明細書、同5436098号明細書、同5576143号明細書、同5294511号明細書、同5824451号明細書記載の界面活性剤を挙げることができ、下記市販の界面活性剤をそのまま用いることもできる。
使用できる市販の界面活性剤として、例えばエフトップEF301、EF303、(新秋田化成(株)製)、フロラードFC430、431、4430(住友スリーエム(株)製)、メガファックF171、F173、F176、F189、F113、F110、F177、F120、R08(大日本インキ化学工業(株)製)、サーフロンS−382、SC101、102、103、104、105、106(旭硝子(株)製)、トロイゾルS−366(トロイケミカル(株)製)、GF−300、GF−150(東亜合成化学(株)製)、サーフロンS−393(セイミケミカル(株)製)、エフトップEF121、EF122A、EF122B、RF122C、EF125M、EF135M、EF351、352、EF801、EF802、EF601((株)ジェムコ製)、PF636、PF656、PF6320、PF6520(OMNIVA社製)、FTX−204D、208G、218G、230G、204D、208D、212D、218、222D((株)ネオス製)等のフッ素系界面活性剤又はシリコン系界面活性剤を挙げることができる。またポリシロキサンポリマーKP−341(信越化学工業(株)製)もシリコン系界面活性剤として用いることができる。
フルオロ脂肪族基を有する重合体としては、フルオロ脂肪族基を有するモノマーと(ポリ(オキシアルキレン))アクリレート及び/又は(ポリ(オキシアルキレン))メタクリレートとの共重合体が好ましく、不規則に分布しているものでも、ブロック共重合していてもよい。また、ポリ(オキシアルキレン)基としては、ポリ(オキシエチレン)基、ポリ(オキシプロピレン)基、ポリ(オキシブチレン)基などが挙げられ、また、ポリ(オキシエチレンとオキシプロピレンとオキシエチレンとのブロック連結体)やポリ(オキシエチレンとオキシプロピレンとのブロック連結体)など同じ鎖長内に異なる鎖長のアルキレンを有するようなユニットでもよい。さらに、フルオロ脂肪族基を有するモノマーと(ポリ(オキシアルキレン))アクリレート(又はメタクリレート)との共重合体は2元共重合体ばかりでなく、異なる2種以上のフルオロ脂肪族基を有するモノマーや、異なる2種以上の(ポリ(オキシアルキレン))アクリレート(又はメタクリレート)などを同時に共重合した3元系以上の共重合体でもよい。
前記各成分を溶解させて組成物A2を調製する際に使用することができる溶剤としては、例えば、アルキレングリコールモノアルキルエーテルカルボキシレート、アルキレングリコールモノアルキルエーテル、乳酸アルキルエステル、アルコキシプロピオン酸アルキル、炭素数4〜10の環状ラクトン、炭素数4〜10の、環を含有しても良いモノケトン化合物、アルキレンカーボネート、アルコキシ酢酸アルキル、ピルビン酸アルキル等を挙げることができる。
アルキレングリコールモノアルキルエーテルとしては、例えば、プロピレングリコールモノメチルエーテル、プロピレングリコールモノエチルエーテル、プロピレングリコールモノプロピルエーテル、プロピレングリコールモノブチルエーテル、エチレングリコールモノメチルエーテル、エチレングリコールモノエチルエーテルを好ましく挙げられる。
アルコキシプロピオン酸アルキルとしては、例えば、3−エトキシプロピオン酸エチル、3−メトキシプロピオン酸メチル、3−エトキシプロピオン酸メチル、3−メトキシプロピオン酸エチルを好ましく挙げられる。
アルコキシ酢酸アルキルとしては、例えば、酢酸−2−メトキシエチル、酢酸−2−エトキシエチル、酢酸−2−(2−エトキシエトキシ)エチル、酢酸−3−メトキシ−3−メチルブチル、酢酸−1−メトキシ−2−プロピルが好ましく挙げられる。
ピルビン酸アルキルとしては、例えば、ピルビン酸メチル、ピルビン酸エチル、ピルビン酸プロピルが好ましく挙げられる。
好ましく使用できる溶剤としては、常温常圧下で、沸点130℃以上の溶剤が挙げられる。具体的には、シクロペンタノン、γ−ブチロラクトン、シクロヘキサノン、乳酸エチル、エチレングリコールモノエチルエーテルアセテート、プロピレングリコールモノメチルエーテルアセテート、3−エトキシプロピオン酸エチル、ピルビン酸エチル、酢酸−2−エトキシエチル、酢酸−2−(2−エトキシエトキシ)エチル、プロピレンカーボネートが挙げられる。
本発明に於いては、上記溶剤を単独で使用してもよいし、2種類以上を併用してもよい。
水酸基を含有する溶剤としては、例えば、エチレングリコール、エチレングリコールモノメチルエーテル、エチレングリコールモノエチルエーテル、プロピレングリコール、プロピレングリコールモノメチルエーテル、プロピレングリコールモノエチルエーテル、乳酸エチル等を挙げることができ、これらの内でプロピレングリコールモノメチルエーテル、乳酸エチルが特に好ましい。
水酸基を含有しない溶剤としては、例えば、プロピレングリコールモノメチルエーテルアセテート、エチルエトキシプロピオネート、2−ヘプタノン、γ−ブチロラクトン、シクロヘキサノン、酢酸ブチル、N−メチルピロリドン、N,N−ジメチルアセトアミド、ジメチルスルホキシド等を挙げることができ、これらの内で、プロピレングリコールモノメチルエーテルアセテート、エチルエトキシプロピオネート、2−ヘプタノン、γ−ブチロラクトン、シクロヘキサノン、酢酸ブチルが特に好ましく、プロピレングリコールモノメチルエーテルアセテート、エチルエトキシプロピオネート、2−ヘプタノンが最も好ましい。
水酸基を含有する溶剤と水酸基を含有しない溶剤との混合比(質量)は、1/99〜99/1、好ましくは10/90〜90/10、更に好ましくは20/80〜60/40である。水酸基を含有しない溶剤を50質量%以上含有する混合溶剤が塗布均一性の点で特に好ましい。
組成物A2は、更に、酸分解性基を含有していない、(G)水に不溶でアルカリ現像液に可溶な樹脂を含有することができ、これにより感度が向上する。
本発明においては、分子量1000〜20000程度のノボラック樹脂類、分子量3000〜50000程度のポリヒドロキシスチレン誘導体をこのようなアルカリ可溶性樹脂として用いることができるが、これらは250nm以下の光に対して吸収が大きいため、一部水素添加して用いるか、又は全樹脂量の30質量%以下の量で使用することが好ましい。
また、カルボキシル基をアルカリ可溶性基として有する樹脂も用いることができる。カルボキシル基を有する樹脂中にはドライエッチング耐性向上のために単環、又は多環の脂環炭化水素基を有していることが好ましい。具体的には酸分解性を示さない脂環式炭化水素構造を有するメタクリル酸エステルと(メタ)アクリル酸の共重合体あるいは末端にカルボキシル基を有する脂環炭化水素基の(メタ)アクリル酸エステルの樹脂などを挙げることができる。
組成物A2は、(H)カルボン酸オニウム塩を含有しても良い。カルボン酸オニウム塩としては、カルボン酸スルホニウム塩、カルボン酸ヨードニウム塩、カルボン酸アンモニウム塩などを挙げることができる。特に、(H)カルボン酸オニウム塩としては、ヨードニウム塩、スルホニウム塩が好ましい。更に、本発明の(H)カルボン酸オニウム塩のカルボキシレート残基が芳香族基、炭素−炭素2重結合を含有しないことが好ましい。特に好ましいアニオン部としては、炭素数1〜30の直鎖、分岐、単環又は多環環状アルキルカルボン酸アニオンが好ましい。さらに好ましくはこれらのアルキル基の一部または全てがフッ素置換されたカルボン酸のアニオンが好ましい。アルキル鎖中に酸素原子を含んでいても良い。これにより220nm以下の光に対する透明性が確保され、感度、解像力が向上し、疎密依存性、露光マージンが改良される。
組成物A2には、必要に応じてさらに染料、吸光剤、可塑剤、光増感剤、及び現像液に対する溶解性を促進させる化合物等を含有させることができる。
組成物A2中の全固形分濃度は、一般的には1〜10質量%、より好ましくは1〜8質量%、さらに好ましくは1.0〜7.0質量%である。
本発明のポジ型感光性組成物は、各成分を所定の溶剤、好ましくは前記混合溶剤に溶解し、フィルター濾過した後、次のように所定の支持体上に塗布して用いる。フィルター濾過に用いるフィルターは0.1ミクロン以下、より好ましくは0.05ミクロン以下、更に好ましくは0.03ミクロン以下のポリテトラフロロエチレン製、ポリエチレン製、ナイロン製のものが好ましい。
当該感光性膜に、所定のマスクを通して活性光線又は放射線を照射し、好ましくはベーク(加熱)を行い、現像、リンスする。これにより良好なパターンを得ることができる。
さらに、上記アルカリ現像液にアルコール類、界面活性剤を適当量添加して使用することもできる。
アルカリ現像液のアルカリ濃度は、通常0.1〜20質量%である。
アルカリ現像液のpHは、通常10.0〜15.0である。
リンス液としては、純水を使用し、界面活性剤を適当量添加して使用することもできる。
また、現像処理または、リンス処理の後に、パターン上に付着している現像液またはリンス液を超臨界流体により除去する処理を行うことができる。
液浸液は、露光波長に対して透明であり、かつレジスト上に投影される光学像の歪みを最小限に留めるよう、屈折率の温度係数ができる限り小さい液体が好ましいが、特に露光光源がArFエキシマレーザー(波長;193nm)である場合には、上述の観点に加えて、入手の容易さ、取り扱いのし易さといった点から水を用いるのが好ましい。
また、さらに屈折率が向上できるという点で屈折率1.5以上の媒体を用いることもできる。この媒体は、水溶液でもよく有機溶剤でもよい。
また、液浸液の屈折率を高めることにより、リソグラフィー性能を高めることが可能である。このような観点から、屈折率を高めるような添加剤を水に加えたり、水の代わりに重水(D2O)を用いてもよい。
トップコートは、193nm透明性という観点からは、芳香族を含有しないポリマーが好ましく、具体的には、炭化水素ポリマー、アクリル酸エステルポリマー、ポリメタクリル酸、ポリアクリル酸、ポリビニルエーテル、シリコン含有ポリマー、フッ素含有ポリマーなどが挙げられる。トップコートから液浸液へ不純物が溶出すると光学レンズを汚染するという観点からは、トップコートに含まれるポリマーの残留モノマー成分は少ない方が好ましい。
トップコートと液浸液との間には屈折率の差がない方が、解像力が向上する。ArFエキシマレーザー(波長:193nm)において、液浸液として水を用いる場合には、ArF液浸露光用トップコートは、液浸液の屈折率に近いことが好ましい。屈折率を液浸液に近くするという観点からは、トップコート中にフッ素原子を有することが好ましい。また、透明性・屈折率の観点から薄膜の方が好ましい。
但し、実施例1〜8、10〜25及び実施例2B、3B、6B〜16Bは、それぞれ、参考例1〜8、10〜25及び参考例2B、3B、6B〜16Bに読み替えるものとする。
窒素気流下シクロヘキサノン8.6gを3つ口フラスコに入れ、これを80℃に加熱した。これに、ノルボルナンラクトンメタクリレート7.8g、3−ヒドロキシアダマンチルメタクリレート3.5g、2−メチルー2−アダマンチルメタクリレート8.2g、シクロヘキシルメタクリレート2.5g、開始剤V−601(和光純薬製)をモノマーに対し5mol%をシクロヘキサノン79gに溶解させた溶液を6時間かけて滴下した。滴下終了後、さらに80℃で2時間反応させた。反応液を放冷後ヘキサン700ml/酢酸エチル300mlの混合液に20分かけて滴下し、析出した粉体をろ取、乾燥すると樹脂(RA−1)が19g得られた。得られた樹脂の重量平均分子量は、標準ポリスチレン換算で10000、分散度(Mw/Mn)は、1.89であった。
<パターン倒れ及び現像欠陥評価>
下記表1に示す成分を溶剤に溶解させ固形分濃度9質量%の溶液を調製し、これを0.03μmのポリエチレンフィルターでろ過してポジ型レジスト溶液を調製した。調製したポジ型レジスト溶液を下記の方法で評価し、結果も表1に示した。
以下、表1中の酸発生剤を示す。
〔塩基性化合物〕
TPI:2,4,5−トリフェニルイミダゾール
TPSA:トリフェニルスルホニウムアセテート
DIA:2,6−ジイソプロピルアニリン
TEA:トリエタノールアミン
TPA:トリペンチルアミン
DBA:N,N−ジブチルアニリン
PBI:2−フェニルベンズイミダゾール
TMEA:トリス(メトキシエトキシエチル)アミン
PEA:N−フェニルジエタノールアミン
〔界面活性剤〕
W−1:メガファックF176(大日本インキ化学工業(株)製)(フッ素系)
W−2:メガファックR08(大日本インキ化学工業(株)製)(フッ素及びシリコン系)
W−3:ポリシロキサンポリマーKP−341(信越化学工業(株)製)(シリコン系)
W‐4:トロイゾルS−366(トロイケミカル(株)製)
〔溶剤〕
S1:プロピレングリコールメチルエーテルアセテート
S2:2−ヘプタノン
S3:シクロヘキサノン
S4:γ−ブチロラクトン
S5:プロピレングリコールメチルエーテル
S6:乳酸エチル
S7:プロピレンカーボネート
スピンコーターにてヘキサメチルジシラザン処理を施したシリコン基板上にブリューワーサイエンス社製反射防止膜DUV−42を600オングストローム均一に塗布し、100℃で90秒間ホットプレート上で乾燥した後、190℃で240秒間加熱乾燥を行った。その後、各ポジ型レジスト溶液をスピンコーターで塗布し110℃で90秒乾燥を行い160nmのレジスト膜を形成させた。
このレジスト膜に対し、マスクを通してArFエキシマレーザーステッパー(ASML社製 NA=0.75、2/3輪帯)で露光し、露光後直ぐに120℃で90秒間ホットプレート上で加熱した。さらに2.38質量%テトラメチルアンモニウムヒドロキシド水溶液で23℃で60秒間現像し、30秒間純水にてリンスした後、乾燥し、ラインパターンを得た。
80nmのラインアンドスペース1:1のマスクパターンを再現する露光量を最適露光量とし、最適露光量からさらに露光量を増大させて形成されるラインパターンの線幅を細らせた際に、パターンが倒れずに解像する線幅をもって定義した。値が小さいほど、より微細なパターンが倒れずに解像することを表し、パターン倒れが発生しにくく、解像力が高いことを示す。
現像欠陥評価方法:
ポジ型レジスト溶液をスピンコーターによりヘキサメチルジシラザン処理を施した6インチのシリコン基板上に均一に塗布し、120℃で90秒間ホットプレート上で加熱、乾燥を行い、0.20μmのレジスト膜を形成した。このレジスト膜を、露光せずに110℃で90秒間ホットプレート上で加熱した。更に2.38質量%濃度のテトラメチルアンモニウムヒドロキシド水溶液で23℃で60秒間現像し、30秒間純水にてリンスした後、乾燥した。このようにして得られたサンプルウェハーを、KLA2112機(KLAテンコール(株)製)により現像欠陥数を測定した(Threshold12、Pixcel Size=0.39)。
下記表1に示す成分を溶剤に溶解させ、それぞれについて固形分濃度7質量%の溶液を調製し、これを0.1μmのポリエチレンフィルターで濾過してポジ型レジスト組成物を調製した。調製したポジ型レジスト組成物を下記の方法で評価し、結果を表1に示した。
210nmの孤立ラインパターンを130nmの線幅に再現する露光量において、焦点位置を変動させ、線幅130nm±13nm(±10%)の範囲を満足する焦点の変動幅
(μm)を示す。
80nmのラインパターンを再現する最小露光量により解像できるラインパターンの幅
(nm)、即ち、限界解像力を示す。
120℃で90秒間後加熱した際にマスクサイズ80nmのラインアンドスペース1/1を再現する露光量を最適露光量とし、次に最適露光量で露光を行った後に、後加熱温度に対して、+2℃及び−2℃(122℃、118℃)の2つの温度で後加熱を行い、各々得られたラインアンドスペースを測長し、それらの線幅L1及びL2を求めた。PEB温度依存性をPEB温度変化1℃あたりの線幅の変動と定義し、下記の式により算出した。
PEB温度依存性(nm/℃)=|L1−L2|/4
値が小さいほど温度変化に対する性能変化が小さく良好であることを示す。
<ポジ型感光性組成物(ポジ型レジスト溶液)の調製>
実施例1〜25の成分を溶剤に溶解させ固形分濃度7質量%の溶液を調製し、これを0.03μmのポリエチレンフィルターで濾過してポジ型レジスト溶液を調製した。調製したポジ型レジスト溶液を下記の方法で評価した。
<解像性評価>
シリコンウエハー上に有機反射防止膜ARC29A(日産化学社製)を塗布し、205℃、60秒ベークを行い78nmの反射防止膜を形成した。その上に調製したポジ型レジスト溶液を塗布し、115℃、60秒ベークを行い150nmのレジスト膜を形成した。
こうして得られたウエハーを液浸液としては純水を使用し、2光束干渉露光を行った(ウェット露光)。尚、2光束干渉露光(ウエット)では、図1に示すように、レーザー1、絞り2、シャッター3、3枚の反射ミラー4,5、6、集光レンズ7を使用し、プリズム8、液浸液(純水)9を介して、ウエハーステージ11上の反射防止膜及びレジスト膜を有するウエハー10に露光を行った。レーザー1の波長は、193nmを用い、65nmのラインアンドスペースパターンを形成するプリズム8を使用した。露光直後に115℃、90秒加熱した後、テトラメチルアンモニウムハイドロオキサイド水溶液(2.38%)で60秒間現像し、純水でリンスした後、スピン乾燥して得たレジストパターンについて走査型電子顕微鏡(日立製S−9260)を用い、観察した。実施例1〜24のポジ型レジスト溶液を用いたところ65nmのラインアンドスペースパターンがパターン倒れを発生せずに解像した。実施例25のポジ型レジスト溶液を用いたところ65nmのラインアンドスペースパターンは解像するものの、一部のパターンでパターン倒れが観測された。
本発明のポジ型感光性組成物は、液浸液を介した露光方法においても良好な画像形成能を有することが明らかである。
下記モノマー(U−1)、(U−2)、(U−3)及び(U−4)を、モル比45:30:20:5の割合でテトラヒドロフランに溶解し、固形分50質量%の溶液を調製した。これを3つ口フラスコに仕込み、窒素気流下80℃で加熱した。反応温度が安定したところで和光純薬工業(株)製ラジカル開始剤V−60を5モル%加え反応を開始させた。6時間加熱した後、反応混合物をテトラヒドロフランで2倍に希釈した後、反応液の5倍量のヘキサンに投入し白色粉体を析出させた。析出した粉体を濾過取り出しし、乾燥、目的物である樹脂(RB−1)を得た。
同様にして下記の本発明の樹脂(RB−2)〜(RB−21)及び比較例の樹脂(RP−1)〜(RP−3)を得た。溶解する溶剤はテトラヒドロフランに限定されない。例えば、シクロヘキサノン、プロピレングリコールモノメチルエーテルを使用しても同様の樹脂を得ることができる。
<パターン倒れ及び現像欠陥評価>
下記表2に示す成分を溶剤に溶解させ固形分濃度9質量%の溶液を調製し、これを0.03μmのポリエチレンフィルターでろ過してポジ型レジスト溶液を調製した。調製したポジ型レジスト溶液を実施例1〜25及び比較例1及び2と同様にして評価した。
下記表2に示す成分を溶剤に溶解させ、それぞれについて固形分濃度7質量%の溶液を調製し、これを0.1μmのポリエチレンフィルターで濾過してポジ型レジスト組成物を調製した。調製したポジ型レジスト組成物を実施例1〜25及び比較例1及び2と同様にして評価した。
結果を表2に示した。
N−2:トリ−n−オクチルアミン
N−3:N,N−ジヒドロキシエチルアニリン
N−4:2,4,5−トリフェニルイミダゾール
N−5:2,6−ジイソプロピルアニリン
N−6:ヒドロキシアンチピリン
N−7:トリスメトキシメトキシエチルアミン
N−8:トリエタノールアミン
W−2:メガファックR08(大日本インキ化学工業(株)製)(フッ素及びシリコン系)
W−4:トロイゾルS−366(トロイケミカル(株)製)
a群
SL−1:プロピレングリコールモノメチルエーテルアセテート
SL−2:プロピレングリコールモノメチルエーテルプロピオネート
SL−3:2−ヘプタノン
b群
SL−4:乳酸エチル
SL−5:プロピレングリコールモノメチルエーテル
SL−6:シクロヘキサノン
c群
SL−7:γ−ブチロラクトン
SL−8:プロピレンカーボネート
2 絞り
3 シャッター
4、5、6 反射ミラー
7 集光レンズ
8 プリズム
9 液浸液
10 反射防止膜及びレジスト膜を有するウエハー
11 ウエハーステージ
Claims (5)
- 下記一般式(I−1b)で表される酸分解性繰り返し単位、下記一般式(II)で表される非酸分解性繰り返し単位、及び水酸基又はシアノ基を有する下記一般式(AIIa)で表される繰り返し単位を有する、酸の作用によりアルカリ現像液に対する溶解速度が増大する樹脂(A)、および活性光線又は放射線の照射により酸を発生する下記一般式(ZI)又は(ZII)で表される化合物(B)を含有することを特徴とするポジ型感光性組成物。
一般式(I−1b)に於いて、
Xa1は、水素原子、アルキル基、シアノ基又はハロゲン原子を表す。
Rx1は、直鎖若しくは分岐状アルキル基又は単環若しくは多環環状アルキル基を表す。
Rx4は、直鎖若しくは分岐状アルキル基又は単環環状アルキル基を表す。
n1は、4又は5を表す。
n2は、0〜3を表す。
一般式(II)に於いて、
Xa2は、水素原子、アルキル基、シアノ基又はハロゲン原子を表す。
A2は、単結合又は2価の連結基を表す。
ACGは、非酸脱離性炭化水素基を表す。
一般式(AIIa)中、
R 1c は、水素原子、メチル基、トリフロロメチル基又はヒドロキメチル基を表す。
R 2c 〜R 4c は、各々独立に、水素原子、水酸基又はシアノ基を表す。ただし、R 2c 〜R 4c のうち少なくとも1つは、水酸基又はシアノ基を表す。
上記一般式(ZI)及び(ZII)において、
R201、R202及びR203は、各々独立に、有機基を表す。R201〜R203のうち2つが結合して環構造を形成してもよく、環内に酸素原子、硫黄原子、エステル結合、アミド結合又はカルボニル基を含んでいてもよい。
R204及びR205は、各々独立に、アリール基、アルキル基又はシクロアルキル基を表す。
X−は、下記一般式(AN1)又は(AN2)で表される非求核性アニオンを表す。
上記一般式(AN1)及び(AN2)に於いて、
Rc1は、下記一般式で表される有機基を表す。
上記一般式に於いて、
Rc6は、炭素数4以下のパーフロロアルキレン基、1〜4個のフッ素原子及び/又は1〜3個のフロロアルキル基で置換されたフェニレン基を表す。
Axは、−O−、−CO2−、−S−、−SO3−又は−SO2N(Rd1)−を表す。Rd1は、水素原子又はアルキル基を表し、Rc7と結合して環構造を形成してもよい。
Rc7は、フッ素原子を置換基として有さない直鎖状若しくは分岐状アルキル基、フッ素原子を置換基として有さない単環若しくは多環環状アルキル基、又はフッ素原子を置換基として有さないアリール基を表す。 - 樹脂(A)が、ラクトン基を有する繰り返し単位を更に有することを特徴とする請求項1に記載のポジ型感光性組成物。
- 請求項1又は2に記載のポジ型感光性組成物により形成された感光性膜。
- 請求項1又は2に記載のポジ型感光性組成物により、感光性膜を形成し、該感光性膜を露光、現像する工程を含むことを特徴とするパターン形成方法。
- 液浸媒体を介して露光を行うことを特徴とする請求項4に記載のパターン形成方法。