JP5502321B2 - コンクリートおよびモルタル混和剤 - Google Patents
コンクリートおよびモルタル混和剤 Download PDFInfo
- Publication number
- JP5502321B2 JP5502321B2 JP2008516146A JP2008516146A JP5502321B2 JP 5502321 B2 JP5502321 B2 JP 5502321B2 JP 2008516146 A JP2008516146 A JP 2008516146A JP 2008516146 A JP2008516146 A JP 2008516146A JP 5502321 B2 JP5502321 B2 JP 5502321B2
- Authority
- JP
- Japan
- Prior art keywords
- cement
- copolymer
- monomer
- concrete
- acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
コンクリートおよび/またはモルタルの基本的な材料であるポルトランドセメントは、カルシウム、ケイ素、アルミニウムおよび鉄の組み合わせでなるケイ酸カルシウムセメントである。
規格C−150では、8種のポルトランドセメントが規定され、これには以下のようなローマ数字の記号が使用されている。
− I型 標準型
− IA型 標準、空気連行型
− II型 中程度の耐硫酸塩型
− IIA型 中程度の耐硫酸塩、空気連行型
− III型 早強型
− IIIA型 早強型、空気連行型
− IV型 低熱型
− V型 高耐硫酸塩型
− CEM I ポルトランドセメント:ポルトランドセメントと、5%までの微量の追加的な成分とを含む
− CEM II ポルトランドセメント−コンポジットセメント:ポルトランドセメントと、35%までの他の単一の成分とを含む
− CEM III 高炉セメント:ポルトランドセメントと、比較的高い割合の高炉スラグとを含む
− CEM IV ポゾランセメント:ポルトランドセメントと、比較的高い割合のポゾランとを含む
− CEM V コンポジットセメント:ポルトランドセメントと、比較的高い割合の高炉スラグおよびポゾランまたはフライアッシュとを含む
モルタルは、セメントおよび砂からなる石造用製品であり、一般に、4mm未満の粒径(例えば特別な装飾的な下塗り用モルタルまたは床スクリード用モルタルでは、8mm未満である場合もある)を有している。水をモルタルに混入すると、その結合要素であるセメントが活性化する。モルタルは、「コンクリート」とは異なる。コンクリートは、作用は同様であるが、セメントによって結合される粗粒の骨材を含む。コンクリートは、それのみで直立させることができるが、モルタルは、煉瓦または石を結束させるために使用される。
最も簡単な形態では、コンクリートは、ペーストと骨材との混合物である。ペーストは、セメントと水とからなっており、微細な骨材および粗粒の骨材の表面をコートする。このペーストは、水和と呼ばれる化学反応によって硬化して強度を得、これにより、コンクリートとして知られる岩石様の塊体が形成される。
混和剤は、コンクリートに含まれる、セメント、水および骨材以外の材料であり、混合の直前または混合中に添加される。混和剤は、通常、コンクリートの成分と化学的に相互作用し、生および硬化コンクリートの特性および性質ならびにその耐久性に影響を与えるものである。
特に、本発明によるコンクリート混和剤によって、最適な流動化能が得られると同時に、コンクリートの固有の稠度、流動性(もしくは流動度)およびワーカビリティを維持することができる。本発明によるコンクリート混和剤は、より早期の作業時間を示すと同時に、長期にわたるコンクリートの流動性を保持し、異なる種類のセメント、特にポルトランドセメントおよびより高い割合で他の成分を含む混合セメント、例えばCEM II、III、IVまたはV型(EN197−1)のセメント種のようなものを使用しても、作業することができる。これにより、異なる作業条件(温度、水セメント比等)であっても、セメントの種類に関係なく、コンクリートの品質パラメータを制御することができる。
i)モノマー1モル当たり25〜300モルのC2〜C3オキシアルキレン基を有するエチレン性不飽和モノマー(a)から誘導された単位0.1〜50モル%、
ii)エチレン性不飽和モノカルボン酸またはジカルボン酸のアルキル、アルケニルまたはヒドロキシアルキルエステルのモノマー(b)から誘導された単位0.1〜49.9モル%、
iii)エチレン性不飽和モノカルボン酸、その塩、エチレン性不飽和ジカルボン酸、その無水物およびその塩からなる群から選択されるモノマー(c)から誘導される単位0.1〜90モル%、ならびに
iv)任意に、30モル%までの他のモノマー
を含むコポリマーを提供する。
水(211モル)を、撹拌装置を備えている反応器内に装填し、得られたシステムから撹拌下で窒素を除去し、続いて窒素雰囲気中で75℃に加熱した。メトキシポリエチレングリコールメタクリレート0.05モル(平均でエチレンオキサイド280モルを含む)、エチルアクリレート0.4モルおよびアクリル酸0.55モルを含む溶液、加硫酸アンモニウム(0.05モル)の20重量%水溶液(1)、ならびに2−メルカプトエタノール(0.1モル)の20重量%水溶液を、別々にかつ同時に、反応器中に2時間で滴下した。次に、過硫酸アンモニウム(0.02モル)の20重量%水溶液(2)を、反応器中に30分間で滴下した。得られた混合物を、その温度(75℃)で1時間熟成させ、その後、95℃に加熱した。過酸化水素(0.2モル)の35重量%水溶液を、得られた混合物中へ30分間で滴下し、このようにして得られた混合物をその温度(95℃)で2時間熟成させた。熟成の完了後、水酸化ナトリウム(0.39モル)の48重量%水溶液を混合物に添加した。このようにして、重量平均分子量130,000のコポリマーが得られた。
− セメントの種類:
a)Zementwerke AG, Gesekeセメント工場(ドイツ)のCEM I 42.5R(ポルトランドセメント)
b)Lafarge, Mannersdorfセメント工場(オーストリア)のCEMII/A−M 42.5N(他の主な成分を6〜20%含むポルトランド−コンポジット)
− 砂0/4(粒度4mm未満)、Markgraneusiedel(MGN)地域、ニーダーオーストリア州(オーストリア)
− 水(エマリッヒアムライン(ドイツ)からの水道水)
モルタル混合物の組成設計(バッチ当たり)は以下の通りである:
− セメント 450g
− 砂 1350g
− 水 225g
水/セメント(%)=0.50である。
結果を表5および表6に示す。
Claims (14)
- i)モノマー1モル当たり50〜300モルのC2〜C3オキシアルキレン基を有するエチレン性不飽和モノマー(a)から誘導された単位0.1〜50モル%、
ii)エチレン性不飽和モノカルボン酸またはジカルボン酸のアルキルまたはアルケニルエステルのモノマー(b)から誘導された単位25〜49モル%、ならびに
iii)エチレン性不飽和モノカルボン酸、その塩、エチレン性不飽和ジカルボン酸、その無水物およびその塩からなる群から選択されるモノマー(c)から誘導された単位0.1〜55モル%、
からなり、
前記モノマー(a)が、
(a−1)1モル当たり50〜300モルのC 2 〜C 3 オキシアルキレン基を有するメトキシポリアルキレングリコールと、アクリル酸またはメタクリル酸との反応によって製造されるエステル生成物、ならびに
(a−2)1モル当たり50〜300モルのC 2 〜C 3 オキシアルキレン基を有するポリアルキレングリコールと、アリルアルコールとの反応によって製造されるモノアリルエーテル、
からなる群から選択される、
重量平均分子量(Mw)が34,000〜130,000のコポリマー。 - 前記モノマー(a)が、1モル当たり80〜300モルのC 2 〜C 3 オキシアルキレン基を有するエチレン性不飽和モノマーである、請求項1に記載のコポリマー。
- 前記モノマー(b)が、マレイン酸ジエステル、フマル酸ジエステル、イタコン酸ジエステルおよびシトラコン酸ジエステルからなる群から選択され、これらの各ジエステルが、C1〜C18の直鎖または分岐鎖のアルキル基またはアルケニル基に結合されている、請求項1または2に記載のコポリマー。
- 前記コポリマーが、単位(a)を1〜30モル%含む、請求項1から4のいずれか1項に記載のコポリマー。
- 前記コポリマーが、単位(a)を5〜20モル%含む、請求項1から5のいずれか1項に記載のコポリマー。
- 請求項1から6のいずれか1項に記載のコポリマーを含むコンクリートおよび/またはモルタル混和剤組成物。
- 請求項1から6のいずれか1項に記載のコポリマー以外に、ナフタレン系、メラミン系、アミノスルホン酸系、ポリカルボン酸系の高性能減水剤、ポリエーテル系の高性能減水剤およびこれらの混合物からなる群から選択される、少なくとも1つの高性能減水剤をさらに含む請求項7に記載の組成物。
- 前記コポリマーの、1つまたは複数の前記高性能減水剤に対する混合重量比が、10:90〜90:10である、請求項8に記載の組成物。
- (i)請求項1から6のいずれか1項に記載のコポリマー、または
(ii)請求項7から9のいずれか1項に記載の混和剤組成物
をセメント混合物に添加することを含む、セメント混合物を分散させる方法。 - セメント、骨材、水、および
(i)請求項1から6のいずれか1項に記載のコポリマー、または
(ii)請求項7から9のいずれか1項に記載の混和剤組成物
を含むコンクリート組成物。 - セメント、砂、水、および
(i)請求項1から6のいずれか1項に記載のコポリマー、または
(ii)請求項7から9のいずれか1項に記載の混和剤組成物
を含むモルタル組成物。 - セメントの固形分に対して、100%の有効分としてコポリマーを0.02〜0.1重量%含む、請求項11または12に記載の組成物。
- 前記セメントが、混合セメントである、請求項11から13のいずれか1項に記載の組成物。