JP5481499B2 - 活性エネルギー線硬化型インク組成物及びこのインク組成物を用いた印刷体 - Google Patents
活性エネルギー線硬化型インク組成物及びこのインク組成物を用いた印刷体 Download PDFInfo
- Publication number
- JP5481499B2 JP5481499B2 JP2012004526A JP2012004526A JP5481499B2 JP 5481499 B2 JP5481499 B2 JP 5481499B2 JP 2012004526 A JP2012004526 A JP 2012004526A JP 2012004526 A JP2012004526 A JP 2012004526A JP 5481499 B2 JP5481499 B2 JP 5481499B2
- Authority
- JP
- Japan
- Prior art keywords
- monomer
- active energy
- energy ray
- cured film
- ink composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明の活性エネルギー線硬化型インク組成物は、活性エネルギー線重合性モノマーと、活性エネルギー線重合開始剤とを含有する。そして、活性エネルギー線重合性モノマーは、モノマーA):ガラス転移点が−30℃以下の単官能モノマーと、モノマーB):ガラス転移点が0℃以下の多官能モノマーとで構成される。
活性エネルギー線重合性単官能モノマーは、モノマーA)ホモポリマーのガラス転移点(Tg)が−30℃未満であり、エチレン性不飽和二重結合を有する活性エネルギー線重合性単官能モノマー(以下、「モノマーA)」ともいう。)を含有する。モノマーA)は硬化膜の柔軟性及び伸長性を高くすることができる。柔軟性が高いとは、インク組成物の硬化膜を形成した基材を曲げた際にインクの硬化膜が割れ難いことを意味し、伸長性が高いとは、インク組成物の硬化膜を形成した基材を引張った際にインクの硬化膜が破断し難いことを意味する(以下、同じ)。
活性エネルギー線重合性単官能モノマーは、モノマーB):ホモポリマーのガラス転移点が0℃以下であり、エチレン性不飽和二重結合を有する多官能モノマー(以下、「モノマーB)」ともいう。)を含有する。モノマーB)は硬化性の向上に寄与し、ガラス転移点が低いために「硬化性」と「柔軟性や伸長性」とのバランスが良い。硬化性とは、多官能性であるために架橋性が高く、少量の活性エネルギー線照射量で硬化膜を形成することができることを意味する。Tgが0℃を超えると、エラストマー基材等に印字した際、被印刷基材の伸びに追従できず、インク組成物の硬化物に割れや剥がれが生じ得る点で好ましくない。
活性エネルギー線重合性単官能モノマーは、モノマーC):ホモポリマーのガラス転移点が0℃以上110℃以下の脂環式構造を有する単官能モノマー(以下、「モノマーC)」ともいう。)を含有する。ガラス転移点が上記範囲で、脂環式構造を有する単官能モノマーを適量配合することにより硬化膜の柔軟性及び膜強度がバランスよく向上する。
活性エネルギー線硬化型インク組成物は、活性エネルギー線重合開始剤を含有する。活性エネルギー線は、ラジカル、カチオン、アニオン等の重合反応の契機となり得るエネルギー線であれば、遠紫外線、紫外線、近紫外線、赤外線等の光線、X線、γ線等の電磁波のほか、電子線、プロトン線、中性子線等のいずれであってもよいが、硬化速度、照射装置の入手容易さ、価格等の観点において、紫外線照射による硬化が好ましい。活性エネルギー線重合開始剤としては、活性エネルギー線の照射により活性エネルギー線硬化型インク組成物中のエチレン性不飽和二重結合を有する化合物の重合反応を促進するものであれば特に限定されず、従来公知の活性エネルギー線重合開始剤を用いることができる。活性エネルギー線重合開始剤の具体例として、例えば、チオキサントン等を含む芳香族ケトン類、α−アミノアルキルフェノン類、α−ヒドロキシケトン類、アシルフォスフィンオキサイド類、芳香族オニウム塩類、有機過酸化物、チオ化合物、ヘキサアリールビイミダゾール化合物、ケトオキシムエステル化合物、ボレート化合物、アジニウム化合物、メタロセン化合物、活性エステル化合物、炭素ハロゲン結合を有する化合物、及びアルキルアミン化合物等が挙げられる。
本発明の活性エネルギー線硬化型インク組成物は、さらに色材を含有する。色材は、従来の油性インク組成物に通常用いられている無機顔料又は有機顔料であればどのようなものであってもよく、例えば、カーボンブラック、カドミウムレッド、モリブデンレッド、クロムイエロー、カドミウムイエロー、チタンイエロー、酸化チタン、酸化クロム、ビリジアン、チタンコバルトグリーン、ウルトラマリンブルー、プルシアンブルー、コバルトブルー、ジケトピロロピロール、アンスラキノン、ベンズイミダゾロン、アンスラピリミジン、アゾ系顔料、フタロシアニン系顔料、キナクリドン系顔料、イソインドリノン系顔料、ジオキサジン系顔料、スレン系顔料、ペリレン系顔料、ペリノン系顔料、チオインジゴ系顔料、キノフタロン系顔料、金属錯体顔料、アルミペースト、シリカ、炭酸カルシウム、炭酸マグネシウム、クレー、沈降性硫酸バリウム、パール顔料等が挙げられる。
活性エネルギー線硬化型インク組成物は、色材を分散するための分散剤を含有することが好ましい。分散剤として高分子分散剤が挙げられる。この高分子分散剤の主鎖はポリエステル系、ポリアクリル系、ポリウレタン系、ポリアミン系、ポリカプロラクトン系等からなり、高分子分散剤は、側鎖としてアミノ基、カルボキシル基、スルホン基、ヒドロキシル基等の極性基やこれらの塩を有するのが好ましい。
活性エネルギー線硬化型インク組成物は、さらに表面調整剤を含有していてもよい。表面調整剤としては特に限定されないが、具体例としては、ジメチルポリシロキサンを有するビックケミー社製「BYK−306」、「BYK−333」、「BYK−371」、「BYK−377」、エボニックデグサジャパン社製「TegoRad2100」、「TegoRad2200N」、「TegoRad2300」等が挙げられる。
また、活性エネルギー線硬化型インク組成物は、その他の添加剤として、可塑剤、重合禁止剤、光安定化剤、酸化防止剤等、種々の添加剤を含有していてもよい。溶剤は本願の目的を達成する範囲内で添加することも出来るが、含有しないことが最も好ましい。
活性エネルギー線硬化型インク組成物の粘度は、40℃において5mPa・s以上20mPa・s以下であることが好ましく、5mPa・s以上15mPa・s以下であることがより好ましい。5mPa・s未満であると、インクジェット装置を用いて吐出する場合に、吐出性が低下し得る点で好ましくない。吐出性とは連続印刷中にインクのドット抜けが生じたり、吐出の乱れ等が生じることにより正常に印字できないことを意味する。20mPa・sを超えると、インクジェット装置のヘッドに、加熱による粘度の低下機構が組み込まれたとしても、ドット抜けによる吐出不良が生じ、インク組成物が正常に吐出されなくなる可能性がある点で好ましくない。
本発明の活性エネルギー線硬化型インク組成物の製造方法は、特に限定されるものではなく、従来公知の方法を用いることができる。まず、分散機を用いて、色材を活性エネルギー線重合性モノマー、分散剤等で分散し、その後、活性エネルギー線重合開始剤、表面調整剤等を添加して均一に撹拌し、さらにフィルターで濾過することによって本発明の活性エネルギー線硬化型インク組成物が得られる。
本発明の印刷体の製造は、上記活性エネルギー線硬化型インク組成物を、エラストマー基材上又はヤング率が0.001MPa以上30MPa以下である被印刷基材上へインクジェット方式で印刷した後、活性エネルギー線で硬化することによって行われる。被印刷基材のヤング率は0.001MPa以上30MPa以下であればよいが、本発明では、ヤング率が0.001MPa以上10MPa未満である場合に好適に利用できる。印刷は、インクジェット方式であることが好ましい。スプレー方式や刷毛塗り方式であると、被印刷基材に対する装飾の自由度が低い点で好ましくない。
被印刷基材は、エラストマー基材又はヤング率が0.001MPa以上30MPa以下である被印刷基材であれば、どのような物であってもよい。エラストマー基材は、熱可塑性エラストマー(以下、「TPE」ともいう。)も含む。TPEとは、高温で可塑化されプラスチックのように射出成型や加工が可能で常温ではゴム弾性体(エラストマー)の性質を示す高分子材料をいう。
活性エネルギー線は、200〜450nmの波長域の光が好ましく、250〜430nmの波長域の光がより好ましい。光源は、特に限定されるものではなく、例えば、高圧水銀ランプ、メタルハライドランプ、低圧水銀ランプ、超高圧水銀ランプ、紫外線レーザー、太陽光、LEDランプ等が挙げられる。これらの光源を用い、積算光量が100mJ/cm2以上、好ましくは200mJ/cm2以上になるように活性エネルギー線を照射することにより、インク組成物を瞬時に硬化させることができる。
印刷体の耐久性をより向上するには、本発明のインク組成物の硬化膜の表面に、表面保護剤からなる表面保護層がさらに形成されていることが好ましい。特に、印刷体を屋外に晒す場合には、塵、埃、泥、すす、ピッチ等が付着したり、また、酸化や紫外線等による劣化で表面にひび割れ等が生じたり、光沢を損なったりするので、硬化膜の表面に、表面保護剤からなる表面保護層が形成されていることが好ましい。なお、表面保護層は、インク組成物の硬化膜からなる層の表面に形成される場合に限らず、被印刷基材の表面に直接形成されていてもよいし、被印刷基材の表面に形成された、後述するプライマー層の表面に形成されていてもよい。
エラストマー基材又はヤング率が0.001MPa以上30MPa以下である被印刷基材と本発明の活性エネルギー線硬化型インク組成物の硬化膜との接着性を高めるため、基材表面と硬化膜との間にプライマー層が形成されていてもよい。
まず、白色以外の黄色・紅色・藍色・黒色については、表1−1及び1−2に示す割合の分散剤を単官能モノマーに溶解し、表1−1及び1−2に示す割合の顔料を加えた。ここで使用する単官能モノマーの量は、顔料濃度が12%となるようにする。そして、混合液を、ペイントシェーカーを用いて顔料の体積平均径が300nm以下となるように分散し、分散体を得た。粒子径は、レーザー散乱法を利用した粒度分布測定器である、マイクロトラック粒度分析計UPA150(日機装社製)を用いて測定した。また、白色インクについては顔料濃度が40%となるように行う以外は同様の方法で行った。
続いて、他の原料を表1−1及び1−2に示す割合になるように混合し、50℃に加温しながら1時間撹拌した。その後、溶け残りがないことを確認し、室温に戻した後、予め調製した分散体を加えて1時間撹拌した。その後、メンブレンフィルターを用いて濾過を行い、実施例1〜31及び比較例1〜9のインク組成物を調製した。
厚さ1mmのSBRシート及び厚さ0.3mmの熱可塑性ポリウレタンシート(以下「TPUシート」という。)を基材として印刷体を製造した。基材の表面に、表3に示す加飾印刷層を構成する組成物を平均膜厚が表3に示した厚さとなるように解像度720dpiの条件でインクジェット法で印字した(層構成については表4−1及び4−2に記載のとおりであり、これにより実施例1〜43を作製した)。そして、SubZeroシステム(UVランプシステム,Integration Technology社製,Dバルブ,出力100W/cm)を用いて、積算光量が640mJ/cm2、ピーク照度が640mW/cm2、搬送速度が18m/minの条件でインク組成物を硬化した。積算光量及びピーク照度の測定は、紫外線光量計UV−351(オーク製作所社製)を用いて行った。これにより、加飾印刷層を作製した。
比較例1〜9について、解像度720dpiで印字し、加飾印刷層を作製した。
密着性の評価は、次のようにして行った。硬化後の加飾印刷層にセロハン粘着テープを貼り付け、加飾印刷層とセロハン粘着テープとを充分に密着した後、セロハンテープを90度で剥離したときの加飾印刷層の基材への密着の程度を判断した。結果を表4−1〜4−3に示す。剥がれがない場合を“○”とし、剥がれがある場合を“×”とした。
硬化性の評価は、硬化後の塗膜を指で触れ、硬化速度及びインクの付着を確認することにより行った。結果を表4−1〜4−3に示す。硬化が早くインクが付着しない場合を“○”とし、硬化に時間はかかるがインクが付着しない場合を“△”とし、硬化が遅くインクが付着する場合を“×”とした。
タックの評価は、室温で行った。
印刷体を室温下におき、塗膜を指で触れ、べたつきの有無を確認した。結果を表4−1〜4−3に示す。べたつきがない場合を“○”とし、ややべたつきがある場合を“△”、べたつきが強い場合を“×”とした。
耐屈曲性の評価は、90°曲げ試験によって行った。90°曲げ試験は、実施例及び比較例の印刷体を90°に折り曲げたときに硬化膜の亀裂の有無を目視で評価することにより行った。結果を表4−1〜4−3に示す。亀裂がない場合を“○”とし、極一部に亀裂が見られた場合を“△”とし、全面に亀裂が見られた場合を“×”とした。
伸び率の評価は、次のようにして行った。実施例及び比較例の印刷体を、ダンベル状6号形(JIS K6251−5)の試験片として、JIS K7161法にしたがい25℃で引張速度100mm/分で引張試験した際に、硬化膜の割れが生じる硬化膜破断点伸びを測定した。硬化膜破断点伸びは、(硬化膜の割れが生じたときの印刷体の長さ−印刷体の元の長さ)/印刷体の元の長さ×100から算出した。結果を表4−1〜4−3に示す。
実施例及び比較例の印刷体を、伸び率が100%から200%までの範囲を繰り返すように印刷体の伸縮を100mm/minの歪み速度で50回繰り返したときに、硬化膜の割れが生じるか否かを確認した。伸び率は、(硬化膜の割れが生じたときの印刷体の長さ−印刷体の元の長さ)/印刷体の元の長さ×100から算出した。結果を表4−1〜4−3に示す。硬化膜の割れが生じなかったときを“○”とし、極一部に亀裂がみられたときを“△”とし、亀裂や剥離がみられたときを“×とした。”
耐水性は、印刷体を室温の水道水に1週間浸漬し、その後の印刷体を濡れたままにて上記90°曲げ試験を行うことによって評価した。また、1週間浸漬し、乾燥後の印刷体の外観を評価した。結果を表4−1〜4−3に示す。90°曲げ試験については、上記〔耐屈曲性の評価〕と同様の方法で評価した。外観については、変化がない場合を“○”とし、変化は見られたものの塗膜の剥離は見られない場合を“△”とし、塗膜の剥離が見られた場合を“×”とした。
耐傷性の評価は、ポリブラシでサンプルを100往復擦ったときの外観を評価することによって行った。結果を表4−1〜4−3に示す。外観に変化がない場合を“○”とし、塗膜に傷が見られた場合を“△”とし、塗膜の剥離が見られた場合を“×”とした。
テーブル評価に供するため、厚さ1mmのSBRシートを基材として印刷体を製造した。表5に示すプライマー層を構成する組成物について、バーコーター#20を用いて乾燥後の平均膜厚が10μmとなるように上記ゴム基材上に塗布した。そして、120℃の条件で1分間乾燥させた。上記の工程を経て、プライマー層を得た。
上記印刷体について、実施例1等で評価した項目のほか、耐傷性については、ポリブラシでサンプルを100往復擦ったときの外観だけでなく、真鍮ブラシでサンプルを100回(片道)擦ったときの外観、及び室温で塗膜を爪で引っかいたときの外観も評価した。結果を表7に示す。外観に変化がない場合を“○”とし、塗膜に傷が見られた場合を“△”とし、塗膜の剥離が見られた場合を“×”とした。
Claims (13)
- 活性エネルギー線重合性モノマーとして、下記のモノマーA)と、モノマーB)と、モノマーC)及び/又はその他のモノマーと、からなるインクジェット用の活性エネルギー線硬化型インク組成物であって、
モノマーA):ガラス転移点が−30℃以下の単官能モノマー、
モノマーB):ガラス転移点が−30℃以下の、ポリプロピレングリコールジアクリレート、ポリエチレングリコールジアクリレート及びエチレンオキサイド付加変性ビスフェノールAジアクリレートから選択されるいずれか1以上のモノマー、
モノマーC):ガラス転移点が0℃以上110℃以下の脂環式構造を有する単官能モノマー、
その他のモノマー:フェノキシエチルアクリレート、ラウリルアクリレート、2−ヒドロキシエチルアクリレート、ステアリルアクリレート、ジシクロペンテニルアクリレート、ジシクロペンタニルアクリレート、1−アダマンチルアクリレート、1,4−ブタンジオールジアクリレート、テトラエチレングリコールジアクリレート、ジメチロールトリシクロデカンジアクリレート、トリメチロールプロパントリアクリレート、ペンタエリスリトールトリアクリレート、より選択される一つ以上のモノマー、
前記活性エネルギー線重合性モノマーのうち、
前記モノマーA)を2〜65質量%、
前記モノマーB)を2〜30質量%、含有し、
前記活性エネルギー線硬化型インク組成物を厚さ1mmのスチレンブタジエンゴム(以下、「SBR」という。)シート上に厚さ10μmの硬化膜として形成し、この硬化膜が形成された硬化膜形成基材を、ダンベル状6号形(JIS K6251−5)の試験片として、JIS K7161法にしたがい25℃で引張速度100mm/分で引張試験した際に、前記硬化膜の割れが生じる硬化膜破断点伸びが200%以上である、活性エネルギー線硬化型インク組成物。 - 活性エネルギー線重合性モノマーとして、下記のモノマーA)と、モノマーB)と、モノマーC)及び/又はその他のモノマーと、からなるインクジェット用の活性エネルギー線硬化型インク組成物であって、
モノマーA):ガラス転移点が−30℃以下の単官能モノマー、
モノマーB):ガラス転移点が−30℃以下の、ポリプロピレングリコールジアクリレート、ポリエチレングリコールジアクリレート及びエチレンオキサイド付加変性ビスフェノールAジアクリレートから選択されるいずれか1以上のモノマー、
モノマーC):ガラス転移点が0℃以上110℃以下の脂環式構造を有する単官能モノマー、
その他のモノマー:フェノキシエチルアクリレート、ラウリルアクリレート、2−ヒドロキシエチルアクリレート、ステアリルアクリレート、ジシクロペンテニルアクリレート、ジシクロペンタニルアクリレート、1−アダマンチルアクリレート、1,4−ブタンジオールジアクリレート、テトラエチレングリコールジアクリレート、ジメチロールトリシクロデカンジアクリレート、トリメチロールプロパントリアクリレート、ペンタエリスリトールトリアクリレート、より選択される一つ以上のモノマー、
前記活性エネルギー線重合性モノマーのうち、
前記モノマーA)を2〜65質量%、
前記モノマーB)を2〜30質量%、含有し、
前記活性エネルギー線硬化型インク組成物を厚さ1mmのSBRシート上に厚さ10μmの硬化膜として形成し、この硬化膜が形成された硬化膜形成基材の伸び率が100%から200%までの範囲を繰り返すように前記硬化膜形成基材の伸縮を100mm/minの歪み速度で50回繰り返したときに、前記硬化膜の割れが生じない、活性エネルギー線硬化型インク組成物。 - 前記モノマーB)が、プロピレングリコールの繰り返し数nが7〜14のポリプロピレングリコールジアクリレート、エチレングリコールの繰り返し数nが7〜14のポリエチレングリコールジアクリレート及びビスフェノールAの11モル〜32モルのエチレンオキサイド付加変性物のジアクリレート、より選択されるいずれか1以上のモノマーである請求項1又は2に記載の活性エネルギー線硬化型インク組成物。
- 前記活性エネルギー線重合性モノマーのうち、前記モノマーC)を20〜65質量%含有する、請求項1から3のいずれかに記載の活性エネルギー線硬化型インク組成物。
- 前記モノマーA)がイソオクチルアクリレート、トリデシルアクリレート及びエトキシジエチレングリコールアクリレートから選択されるいずれか1以上のモノマーである、請求項1から4のいずれかに記載の活性エネルギー線硬化型インク組成物。
- 前記モノマーC)がイソボルニルアクリレート、4−t−ブチルシクロヘキシルアクリレート、シクロヘキシルアクリレート及びジシクロペンテニルオキシエチルアクリレートから選択されるいずれか1以上のモノマーである、請求項1から5のいずれかに記載の活性エネルギー線硬化型インク組成物。
- さらに色材を含有する、請求項1から6のいずれかに記載の活性エネルギー線硬化型インク組成物。
- 請求項1から7のいずれかに記載の活性エネルギー線硬化型インク組成物を、厚さ1mmのスチレンブタジエンゴム(以下、「SBR」という。)シート上に厚さ10μmの硬化膜として形成し、この硬化膜が形成された硬化膜形成基材を、ダンベル状6号形(JIS K6251−5)の試験片として、JIS K7161法にしたがい25℃で引張速度100mm/分で引張試験した際に、前記硬化膜の割れが生じる硬化膜破断点伸びが300%以上である、活性エネルギー線硬化型インク組成物。
- エラストマー基材又はヤング率が0.001MPa以上30MPa以下である被印刷基材へのインクジェット用インクとして用いられる、請求項1から8のいずれかに記載の活性エネルギー線硬化型インク組成物。
- エラストマー基材上又はヤング率が0.001MPa以上30MPa以下である被印刷基材上に、請求項1から9のいずれかに記載の活性エネルギー線硬化型インク組成物の硬化膜であるインク硬化膜層が形成された印刷体。
- 前記インク硬化膜層の表面を保護する表面保護層が前記インク硬化膜層の表面に形成されている、請求項10に記載の印刷体。
- 前記エラストマー基材又は前記被印刷基材の表面と前記インク硬化膜層との間にプライマー層が形成されている、請求項10又は11に記載の印刷体。
- 請求項1から8のいずれかに記載の活性エネルギー線硬化型インク組成物を、エラストマー基材上又はヤング率が0.001MPa以上30MPa以下である被印刷基材上へインクジェット方式で印刷した後、紫外線で硬化する、印刷体の製造方法。