JP5289472B2 - クリヤ塗装ステンレス鋼板及びその製造方法 - Google Patents
クリヤ塗装ステンレス鋼板及びその製造方法 Download PDFInfo
- Publication number
- JP5289472B2 JP5289472B2 JP2011013932A JP2011013932A JP5289472B2 JP 5289472 B2 JP5289472 B2 JP 5289472B2 JP 2011013932 A JP2011013932 A JP 2011013932A JP 2011013932 A JP2011013932 A JP 2011013932A JP 5289472 B2 JP5289472 B2 JP 5289472B2
- Authority
- JP
- Japan
- Prior art keywords
- coating film
- clear
- parts
- resin composition
- stainless steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(1)上層がクリヤ塗膜と下層が化成処理塗膜で形成されるクリヤ塗装ステンレス鋼板において、化成処理塗膜がアミノシラン系、エポキシシラン系の1種類または2種類より実質的になり、化成処理塗膜付着量が2〜50mg/m2であり、クリヤ塗膜が架橋性官能基を有するガラス転移点が30〜90℃、数平均分子量3000〜50000のアクリル樹脂を主成分として該アクリル樹脂を架橋硬化させるためのブロックイソシアネート樹脂及びアミノ樹脂を含む熱硬化性樹脂組成物であり、前記クリヤ塗膜は、熱硬化性樹脂組成物の固形物100質量部あたり、融点が70〜160℃であって粒径が0.1〜7.0μmであるポリオレフィン系ワックスを固形分量で0.25〜5質量部含有し、前記熱硬化性樹脂組成物はオルガノシリカゾル、非晶質シリカ及び樹脂ビーズを含有せず、クリヤ塗膜厚さが1〜10μmであることを特徴とするクリヤ塗装ステンレス鋼板。
(2)上層がクリヤ塗膜と下層が化成処理塗膜で形成されるクリヤ塗装ステンレス鋼板において、化成処理塗膜がアミノシラン系、エポキシシラン系の1種類または2種類より実質的になり、化成処理塗膜付着量が2〜50mg/m2であり、クリヤ塗膜が架橋性官能基を有するガラス転移点が30〜90℃、数平均分子量3000〜50000のアクリル樹脂を主成分として該アクリル樹脂を架橋硬化させるためのブロックイソシアネート樹脂及びアミノ樹脂を含む熱硬化性樹脂組成物であり、前記クリヤ塗膜は、熱硬化性樹脂組成物の固形物100質量部あたり、融点が70〜160℃であって粒径が0.1〜7.0μmであるポリオレフィン系ワックスを固形分量で0.25〜5質量部含有し、前記熱硬化性樹脂組成物はその固形物100質量部あたり、オルガノシリカゾルを2〜10質量部含有する一方、非晶質シリカ及び樹脂ビーズを含有せず、クリヤ塗膜厚さが1〜10μmであることを特徴とする耐疵付き性に優れたクリヤ塗装ステンレス鋼板。
(3)上層がクリヤ塗膜と下層が化成処理塗膜で形成されるクリヤ塗装ステンレス鋼板において、化成処理塗膜がアミノシラン系、エポキシシラン系の1種類または2種類より実質的になり、化成処理塗膜付着量が2〜50mg/m2であり、クリヤ塗膜が架橋性官能基を有するガラス転移点が30〜90℃、数平均分子量3000〜50000のアクリル樹脂を主成分として該アクリル樹脂を架橋硬化させるためのブロックイソシアネート樹脂及びアミノ樹脂を含む熱硬化性樹脂組成物であり、前記クリヤ塗膜は、熱硬化性樹脂組成物の固形物100質量部あたり、融点が70〜160℃であって粒径が0.1〜7.0μmであるポリオレフィン系ワックスを固形分量で0.25〜5質量部含有し、前記熱硬化性樹脂組成物はその固形物100質量部あたり、非晶質シリカを0.5〜5質量部含有する一方、オルガノシリカゾル及び樹脂ビーズを含有せず、クリヤ塗膜厚さが1〜10μmであることを特徴とする耐指紋汚染性および疵付き性に優れたクリヤ塗装ステンレス鋼板。
(4)上層がクリヤ塗膜と下層が化成処理塗膜で形成されるクリヤ塗装ステンレス鋼板において、化成処理塗膜がアミノシラン系、エポキシシラン系の1種類または2種類より実質的になり、化成処理塗膜付着量が2〜50mg/m2であり、クリヤ塗膜が架橋性官能基を有するガラス転移点が30〜90℃、数平均分子量3000〜50000のアクリル樹脂を主成分として該アクリル樹脂を架橋硬化させるためのブロックイソシアネート樹脂及びアミノ樹脂を含む熱硬化性樹脂組成物であり、前記クリヤ塗膜は、熱硬化性樹脂組成物の固形物100質量部あたり、融点が70〜160℃であって粒径が0.1〜7.0μmであるポリオレフィン系ワックスを固形分量で0.25〜5質量部含有し、前記熱硬化性樹脂組成物はその固形物100質量部あたり、オルガノシリカゾルを2〜10質量部、非晶質シリカを0.5〜5質量部含有する一方、樹脂ビーズを含有せず、クリヤ塗膜厚さが1〜10μmであることを特徴とする耐指紋汚染性および疵付き性に優れたクリヤ塗装ステンレス鋼板。
(5)熱硬化性樹脂組成物が、前記アミノ樹脂の硬化触媒としてP−トルエンスルホン酸系触媒を熱硬化性樹脂組成物の固形物100質量部あたり、0.5〜5質量部含有することを特徴とする生産性・耐指紋性・耐疵付き性に優れた上記(1)〜(4)のいずれかに記載のクリヤ塗装ステンレス鋼板。
(6)上層がクリヤ塗膜と下層が化成処理塗膜で形成されるクリヤ塗装ステンレス鋼板において、化成処理塗膜がアミノシラン系、エポキシシラン系の1種類または2種類より実質的になり、化成処理塗膜付着量が2〜50mg/m2であり、クリヤ塗膜が架橋性官能基を有するガラス転移点が30〜90℃、数平均分子量3000〜50000のアクリル樹脂を主成分として該アクリル樹脂を架橋硬化させるためのブロックイソシアネート樹脂及びアミノ樹脂を含む熱硬化性樹脂組成物であり、前記クリヤ塗膜は、熱硬化性樹脂組成物の固形物100質量部あたり、融点が70〜160℃であって粒径が0.1〜7.0μmであるポリオレフィン系ワックスを固形分量で0.25〜5質量部含有し、前記熱硬化性樹脂組成物はその固形物100質量部あたり、アクリル樹脂ビーズを0.5〜8質量部含有する一方、オルガノシリカゾル、非晶質シリカ及びアクリル樹脂ビーズ以外の樹脂ビーズを含有せず、クリヤ塗膜厚さが1〜10μmであることを特徴とするクリヤ塗装ステンレス鋼板。
(7)上層がクリヤ塗膜と下層が化成処理塗膜で形成されるステンレス鋼板の製造方法であって、アミノシラン系、エポキシシラン系の1種類または2種類よりなる化成処理塗膜を付着量が2〜50mg/m2となるように塗布し、その後クリヤ塗膜として架橋性官能基を有するガラス転移点が30〜90℃、数平均分子量3000〜50000のアクリル樹脂を主成分として該アクリル樹脂を架橋硬化させるためのブロックイソシアネート樹脂及びアミノ樹脂を含む熱硬化性樹脂組成物をクリヤ塗膜厚さが1〜10μmとなるように塗布し、前記熱硬化性樹脂組成物は、その固形物100質量部あたり、融点が70〜160℃であって粒径が0.1〜7.0μmであるポリオレフィン系ワックスを固形分量で0.25〜5質量部含有し、前記熱硬化性樹脂組成物はオルガノシリカゾル、非晶質シリカ及び樹脂ビーズを含有しないことを特徴とするクリヤ塗装ステンレス鋼板の製造方法。
(8)上層がクリヤ塗膜と下層が化成処理塗膜で形成されるステンレス鋼板の製造方法であって、アミノシラン系、エポキシシラン系の1種類または2種類よりなる化成処理塗膜を付着量が2〜50mg/m2となるように塗布し、その後クリヤ塗膜として架橋性官能基を有するガラス転移点が30〜90℃、数平均分子量3000〜50000のアクリル樹脂を主成分として該アクリル樹脂を架橋硬化させるためのブロックイソシアネート樹脂及びアミノ樹脂を含む熱硬化性樹脂組成物をクリヤ塗膜厚さが1〜10μmとなるように塗布し、前記熱硬化性樹脂組成物は、その固形物100質量部あたり、融点が70〜160℃であって粒径が0.1〜7.0μmであるポリオレフィン系ワックスを固形分量で0.25〜5質量部含有し、前記熱硬化性樹脂組成物はその固形物100質量部あたり、オルガノシリカゾルを2〜10質量部含有する一方、非晶質シリカ及び樹脂ビーズを含有しないことを特徴とする耐疵付き性に優れたクリヤ塗装ステンレス鋼板の製造方法。
(9)上層がクリヤ塗膜と下層が化成処理塗膜で形成されるステンレス鋼板の製造方法であって、アミノシラン系、エポキシシラン系の1種類または2種類よりなる化成処理塗膜を付着量が2〜50mg/m2となるように塗布し、その後クリヤ塗膜として架橋性官能基を有するガラス転移点が30〜90℃、数平均分子量3000〜50000のアクリル樹脂を主成分として該アクリル樹脂を架橋硬化させるためのブロックイソシアネート樹脂及びアミノ樹脂を含む熱硬化性樹脂組成物をクリヤ塗膜厚さが1〜10μmとなるように塗布し、前記熱硬化性樹脂組成物は、その固形物100質量部あたり、融点が70〜160℃であって粒径が0.1〜7.0μmであるポリオレフィン系ワックスを固形分量で0.25〜5質量部含有し、前記熱硬化性樹脂組成物が、その固形物100質量部あたり、非晶質シリカを0.5〜5質量部含有する一方、オルガノシリカゾル及び樹脂ビーズを含有しないことを特徴とする耐指紋汚染性および疵付き性に優れたクリヤ塗装ステンレス鋼板の製造方法。
(10)上層がクリヤ塗膜と下層が化成処理塗膜で形成されるステンレス鋼板の製造方法であって、アミノシラン系、エポキシシラン系の1種類または2種類よりなる化成処理塗膜を付着量が2〜50mg/m2となるように塗布し、その後クリヤ塗膜として架橋性官能基を有するガラス転移点が30〜90℃、数平均分子量3000〜50000のアクリル樹脂を主成分として該アクリル樹脂を架橋硬化させるためのブロックイソシアネート樹脂及びアミノ樹脂を含む熱硬化性樹脂組成物をクリヤ塗膜厚さが1〜10μmとなるように塗布し、前記熱硬化性樹脂組成物は、その固形物100質量部あたり、融点が70〜160℃であって粒径が0.1〜7.0μmであるポリオレフィン系ワックスを固形分量で0.25〜5質量部含有し、前記熱硬化性樹脂組成物が、その固形物100質量部あたり、オルガノシリカゾルを2〜10質量部、非晶質シリカを0.5〜5質量部含有する一方、樹脂ビーズを含有しないことを特徴とする耐指紋汚染性および疵付き性に優れたクリヤ塗装ステンレス鋼板の製造方法。
(11)熱硬化性樹脂組成物が、前記アミノ樹脂の硬化触媒としてP−トルエンスルホン酸系触媒を熱硬化性樹脂組成物の固形物100質量部あたり、0.5〜5質量部含有することを特徴とする生産性・耐指紋性・耐疵付き性に優れた上記(7)〜(10)のいずれかに記載のクリヤ塗装ステンレス鋼板の製造方法。
(12)上層がクリヤ塗膜と下層が化成処理塗膜で形成されるステンレス鋼板の製造方法であって、アミノシラン系、エポキシシラン系の1種類または2種類よりなる化成処理塗膜を付着量が2〜50mg/m2となるように塗布し、その後クリヤ塗膜として架橋性官能基を有するガラス転移点が30〜90℃、数平均分子量3000〜50000のアクリル樹脂を主成分として該アクリル樹脂を架橋硬化させるためのブロックイソシアネート樹脂及びアミノ樹脂を含む熱硬化性樹脂組成物をクリヤ塗膜厚さが1〜10μmとなるように塗布し、前記熱硬化性樹脂組成物は、その固形物100質量部あたり、融点が70〜160℃であって粒径が0.1〜7.0μmであるポリオレフィン系ワックスを固形分量で0.25〜5質量部含有し、前記熱硬化性樹脂組成物が、その固形物100質量部あたり、アクリル樹脂ビーズを0.5〜8質量部含有する一方、オルガノシリカゾル、非晶質シリカ及びアクリル樹脂ビーズ以外の樹脂ビーズを含有しないことを特徴とするクリヤ塗装ステンレス鋼板の製造方法。
(1) 塗膜のクリヤ性
色差計CR−300(ミノルタ社製)にて塗膜の着色状態を、板温193℃で焼き付けた素材とクリヤ塗装した材料の色差Δb値にて測定した。(Δb大→黄大)
JIS K5600 5−4 引っかき硬度(鉛筆法)に従って評価した。(4以上を合格とした。)
5:6H以上(合格)
4:5H(合格)
3:4H(不合格)
2:3H(不合格)
1:2H以下(不合格)
供試材を天然暴露試験3ヶ月行い、塗膜の雨筋のつき具合を評価した。
5:跡が全く無い (合格)
4:跡が僅かに認められる (合格)
3:跡がやや目立つ (不合格)
2:跡が濃く残る (不合格)
1:剥離する (不合格)
供試材を40℃で72時間マジックリンにつけ塗膜の状態を観察、評価した。
5:跡が全く無い (合格)
4:跡が僅かに認められる (合格)
3:跡がやや目立つ (不合格)
2:跡が濃く残る (不合格)
1:剥離する (不合格)
5%硫酸と5%NaOHを供試材に2mL滴下し、蓋をしたのち、16時間後の塗膜の状態を観察、評価した。
5:跡が全く無い (合格)
4:跡が僅かに認められる (合格)
3:跡がやや目立つ (不合格)
2:跡が濃く残る (不合格)
1:剥離する (不合格)
SWOM試験1000hr後の光沢保持率(%)にて評価した。
5:光沢保持率80〜100% (合格)
4:光沢保持率60〜80% (合格)
3:光沢保持率40〜60% (不合格)
2:光沢保持率20〜40% (不合格)
1:光沢保持率0〜20% (不合格)
JIS Z2247に従って評価した。(SUS430グラファイトグリースを使用した場合、9.3mmであったため、それ以上を合格とした。)
塗膜にクロスカットを施し、JIS Z2371の方法に従い塩水噴霧試験500hr行い、塗膜の剥離状態を目視により評価した。
5:剥離率5%未満 (合格)
4:剥離率5%以上10%未満 (合格)
3:剥離率10%以上15%未満 (不合格)
2:剥離率15%以上20%未満 (不合格)
1:剥離率20%以上 (不合格)
(1) 光沢
JIS K5600 4−7(鏡面光沢度)に準じ測定し、110以上を合格とした。
5:130以上(合格)
4:110〜130(合格)
3:90〜110(不合格)
2:70〜90(不合格)
1:70以下(不合格)
沸騰水に1時間浸漬し、30分放置後の付着性を碁盤目試験で評価した。評価はJIS K5600 5−6に準じ、8点以上を合格とした。
5:(合格):10点
4:(合格):8〜9点
3:(不合格):7〜6点
2:(不合格):5〜4点
1:(不合格):3点以下
JIS K5600 5−2に準じて評価した。
5:9mm以上(合格)
4:7〜9mm(合格)
3:5〜7mm(不合格)
2:3〜5mm(不合格)
1:3mm以下(不合格)
(1)塗膜の加工性
JIS K5600 5−2(耐カッピング性)に従って評価した。
5:7mm以上(合格)
4:5〜7mm(合格)
3:3〜5mm(不合格)
2:1〜3mm(不合格)
1:1mm以下(不合格)
JIS K5600 5−4 引っかき硬度(鉛筆法)に従って評価した。
5:6H以上(合格)
4:5H(合格)
3:4H(不合格)
2:3H(不合格)
1:2H以下(不合格)
JIS K5600 4−7 鏡面光沢度に従って評価した。
5:90以上(合格)
4:70〜90(合格)
3:50〜70(不合格)
2:30〜50(不合格)
1:30以下(不合格)
研磨剤入り家庭用洗剤「ジフ」(日本リーバ製)をガーゼを4枚重ねた上に滴下し1kgの荷重で100回こすり、疵付き性を評価する。
5:疵がない(合格)
4:ほとんど疵が目立たない(合格)
3:はっきりと疵が確認できる(不合格)
2:疵で塗膜の光沢がなくなっている(不合格)
1:塗膜が削れ素地に達している(不合格)
指で塗面を1kg重の力で押え、指紋の付き方を確認し、付着した指紋をガーゼでふき取る。
5:指紋が付かない(合格)
4:ほとんど指紋が目立たない(合格)
3:うっすらと指紋が確認でき、除去は容易(不合格)
2:うっすらと指紋が確認でき、除去は困難(不合格)
1:はっきりと指紋が確認できる(不合格)
(1)意匠性・外観
インバーダル材(ステンレス)と意匠性を比較する。
5:全く差が無い (合格)
4:ほとんど差がない (合格)
3:差がやや目立つ (不合格)
2:差が目立つ (不合格)
1:はっきりと差がわかる (不合格)
43℃の状態で144時間後の塗料の状態を観察、評価した。
5:全く異常が無い (合格)
4:やや塗料状態に異常がある (合格)
3:僅かに粘度上昇が認められる(不合格)
2:やや増粘傾向がみられる (不合格)
1:完全にゲル、増粘している (不合格)
Claims (12)
- 上層がクリヤ塗膜と下層が化成処理塗膜で形成されるクリヤ塗装ステンレス鋼板において、化成処理塗膜がアミノシラン系、エポキシシラン系の1種類または2種類より実質的になり、化成処理塗膜付着量が2〜50mg/m2であり、クリヤ塗膜が架橋性官能基を有するガラス転移点が30〜90℃、数平均分子量3000〜50000のアクリル樹脂を主成分として該アクリル樹脂を架橋硬化させるためのブロックイソシアネート樹脂及びアミノ樹脂を含む熱硬化性樹脂組成物であり、前記クリヤ塗膜は、熱硬化性樹脂組成物の固形物100質量部あたり、融点が70〜160℃であって粒径が0.1〜7.0μmであるポリオレフィン系ワックスを固形分量で0.25〜5質量部含有し、前記熱硬化性樹脂組成物はオルガノシリカゾル、非晶質シリカ及び樹脂ビーズを含有せず、クリヤ塗膜厚さが1〜10μmであることを特徴とするクリヤ塗装ステンレス鋼板。
- 上層がクリヤ塗膜と下層が化成処理塗膜で形成されるクリヤ塗装ステンレス鋼板において、化成処理塗膜がアミノシラン系、エポキシシラン系の1種類または2種類より実質的になり、化成処理塗膜付着量が2〜50mg/m2であり、クリヤ塗膜が架橋性官能基を有するガラス転移点が30〜90℃、数平均分子量3000〜50000のアクリル樹脂を主成分として該アクリル樹脂を架橋硬化させるためのブロックイソシアネート樹脂及びアミノ樹脂を含む熱硬化性樹脂組成物であり、前記クリヤ塗膜は、熱硬化性樹脂組成物の固形物100質量部あたり、融点が70〜160℃であって粒径が0.1〜7.0μmであるポリオレフィン系ワックスを固形分量で0.25〜5質量部含有し、前記熱硬化性樹脂組成物はその固形物100質量部あたり、オルガノシリカゾルを2〜10質量部含有する一方、非晶質シリカ及び樹脂ビーズを含有せず、クリヤ塗膜厚さが1〜10μmであることを特徴とする耐疵付き性に優れたクリヤ塗装ステンレス鋼板。
- 上層がクリヤ塗膜と下層が化成処理塗膜で形成されるクリヤ塗装ステンレス鋼板において、化成処理塗膜がアミノシラン系、エポキシシラン系の1種類または2種類より実質的になり、化成処理塗膜付着量が2〜50mg/m2であり、クリヤ塗膜が架橋性官能基を有するガラス転移点が30〜90℃、数平均分子量3000〜50000のアクリル樹脂を主成分として該アクリル樹脂を架橋硬化させるためのブロックイソシアネート樹脂及びアミノ樹脂を含む熱硬化性樹脂組成物であり、前記クリヤ塗膜は、熱硬化性樹脂組成物の固形物100質量部あたり、融点が70〜160℃であって粒径が0.1〜7.0μmであるポリオレフィン系ワックスを固形分量で0.25〜5質量部含有し、前記熱硬化性樹脂組成物はその固形物100質量部あたり、非晶質シリカを0.5〜5質量部含有する一方、オルガノシリカゾル及び樹脂ビーズを含有せず、クリヤ塗膜厚さが1〜10μmであることを特徴とする耐指紋汚染性および疵付き性に優れたクリヤ塗装ステンレス鋼板。
- 上層がクリヤ塗膜と下層が化成処理塗膜で形成されるクリヤ塗装ステンレス鋼板において、化成処理塗膜がアミノシラン系、エポキシシラン系の1種類または2種類より実質的になり、化成処理塗膜付着量が2〜50mg/m2であり、クリヤ塗膜が架橋性官能基を有するガラス転移点が30〜90℃、数平均分子量3000〜50000のアクリル樹脂を主成分として該アクリル樹脂を架橋硬化させるためのブロックイソシアネート樹脂及びアミノ樹脂を含む熱硬化性樹脂組成物であり、前記クリヤ塗膜は、熱硬化性樹脂組成物の固形物100質量部あたり、融点が70〜160℃であって粒径が0.1〜7.0μmであるポリオレフィン系ワックスを固形分量で0.25〜5質量部含有し、前記熱硬化性樹脂組成物はその固形物100質量部あたり、オルガノシリカゾルを2〜10質量部、非晶質シリカを0.5〜5質量部含有する一方、樹脂ビーズを含有せず、クリヤ塗膜厚さが1〜10μmであることを特徴とする耐指紋汚染性および疵付き性に優れたクリヤ塗装ステンレス鋼板。
- 前記熱硬化性樹脂組成物が、前記アミノ樹脂の硬化触媒としてP−トルエンスルホン酸系触媒を熱硬化性樹脂組成物の固形物100質量部あたり、0.5〜5質量部含有することを特徴とする生産性・耐指紋性・耐疵付き性に優れた請求項1〜4のいずれかに記載のクリヤ塗装ステンレス鋼板。
- 上層がクリヤ塗膜と下層が化成処理塗膜で形成されるクリヤ塗装ステンレス鋼板において、化成処理塗膜がアミノシラン系、エポキシシラン系の1種類または2種類より実質的になり、化成処理塗膜付着量が2〜50mg/m2であり、クリヤ塗膜が架橋性官能基を有するガラス転移点が30〜90℃、数平均分子量3000〜50000のアクリル樹脂を主成分として該アクリル樹脂を架橋硬化させるためのブロックイソシアネート樹脂及びアミノ樹脂を含む熱硬化性樹脂組成物であり、前記クリヤ塗膜は、熱硬化性樹脂組成物の固形物100質量部あたり、融点が70〜160℃であって粒径が0.1〜7.0μmであるポリオレフィン系ワックスを固形分量で0.25〜5質量部含有し、前記熱硬化性樹脂組成物はその固形物100質量部あたり、アクリル樹脂ビーズを0.5〜8質量部含有する一方、オルガノシリカゾル、非晶質シリカ及びアクリル樹脂ビーズ以外の樹脂ビーズを含有せず、クリヤ塗膜厚さが1〜10μmであることを特徴とするクリヤ塗装ステンレス鋼板。
- 上層がクリヤ塗膜と下層が化成処理塗膜で形成されるステンレス鋼板の製造方法であって、アミノシラン系、エポキシシラン系の1種類または2種類よりなる化成処理塗膜を付着量が2〜50mg/m2となるように塗布し、その後クリヤ塗膜として架橋性官能基を有するガラス転移点が30〜90℃、数平均分子量3000〜50000のアクリル樹脂を主成分として該アクリル樹脂を架橋硬化させるためのブロックイソシアネート樹脂及びアミノ樹脂を含む熱硬化性樹脂組成物をクリヤ塗膜厚さが1〜10μmとなるように塗布し、前記熱硬化性樹脂組成物は、その固形物100質量部あたり、融点が70〜160℃であって粒径が0.1〜7.0μmであるポリオレフィン系ワックスを固形分量で0.25〜5質量部含有し、前記熱硬化性樹脂組成物はオルガノシリカゾル、非晶質シリカ及び樹脂ビーズを含有しないことを特徴とするクリヤ塗装ステンレス鋼板の製造方法。
- 上層がクリヤ塗膜と下層が化成処理塗膜で形成されるステンレス鋼板の製造方法であって、アミノシラン系、エポキシシラン系の1種類または2種類よりなる化成処理塗膜を付着量が2〜50mg/m2となるように塗布し、その後クリヤ塗膜として架橋性官能基を有するガラス転移点が30〜90℃、数平均分子量3000〜50000のアクリル樹脂を主成分として該アクリル樹脂を架橋硬化させるためのブロックイソシアネート樹脂及びアミノ樹脂を含む熱硬化性樹脂組成物をクリヤ塗膜厚さが1〜10μmとなるように塗布し、前記熱硬化性樹脂組成物は、その固形物100質量部あたり、融点が70〜160℃であって粒径が0.1〜7.0μmであるポリオレフィン系ワックスを固形分量で0.25〜5質量部含有し、前記熱硬化性樹脂組成物はその固形物100質量部あたり、オルガノシリカゾルを2〜10質量部含有する一方、非晶質シリカ及び樹脂ビーズを含有しないことを特徴とする耐疵付き性に優れたクリヤ塗装ステンレス鋼板の製造方法。
- 上層がクリヤ塗膜と下層が化成処理塗膜で形成されるステンレス鋼板の製造方法であって、アミノシラン系、エポキシシラン系の1種類または2種類よりなる化成処理塗膜を付着量が2〜50mg/m2となるように塗布し、その後クリヤ塗膜として架橋性官能基を有するガラス転移点が30〜90℃、数平均分子量3000〜50000のアクリル樹脂を主成分として該アクリル樹脂を架橋硬化させるためのブロックイソシアネート樹脂及びアミノ樹脂を含む熱硬化性樹脂組成物をクリヤ塗膜厚さが1〜10μmとなるように塗布し、前記熱硬化性樹脂組成物は、その固形物100質量部あたり、融点が70〜160℃であって粒径が0.1〜7.0μmであるポリオレフィン系ワックスを固形分量で0.25〜5質量部含有し、前記熱硬化性樹脂組成物が、その固形物100質量部あたり、非晶質シリカを0.5〜5質量部含有する一方、オルガノシリカゾル及び樹脂ビーズを含有しないことを特徴とする耐指紋汚染性および疵付き性に優れたクリヤ塗装ステンレス鋼板の製造方法。
- 上層がクリヤ塗膜と下層が化成処理塗膜で形成されるステンレス鋼板の製造方法であって、アミノシラン系、エポキシシラン系の1種類または2種類よりなる化成処理塗膜を付着量が2〜50mg/m2となるように塗布し、その後クリヤ塗膜として架橋性官能基を有するガラス転移点が30〜90℃、数平均分子量3000〜50000のアクリル樹脂を主成分として該アクリル樹脂を架橋硬化させるためのブロックイソシアネート樹脂及びアミノ樹脂を含む熱硬化性樹脂組成物をクリヤ塗膜厚さが1〜10μmとなるように塗布し、前記熱硬化性樹脂組成物は、その固形物100質量部あたり、融点が70〜160℃であって粒径が0.1〜7.0μmであるポリオレフィン系ワックスを固形分量で0.25〜5質量部含有し、前記熱硬化性樹脂組成物が、その固形物100質量部あたり、オルガノシリカゾルを2〜10質量部、非晶質シリカを0.5〜5質量部含有する一方、樹脂ビーズを含有しないことを特徴とする耐指紋汚染性および疵付き性に優れたクリヤ塗装ステンレス鋼板の製造方法。
- 前記熱硬化性樹脂組成物が、前記アミノ樹脂の硬化触媒としてP−トルエンスルホン酸系触媒を熱硬化性樹脂組成物の固形物100質量部あたり、0.5〜5質量部含有することを特徴とする生産性・耐指紋性・耐疵付き性に優れた請求項7〜10のいずれかに記載のクリヤ塗装ステンレス鋼板の製造方法。
- 上層がクリヤ塗膜と下層が化成処理塗膜で形成されるステンレス鋼板の製造方法であって、アミノシラン系、エポキシシラン系の1種類または2種類よりなる化成処理塗膜を付着量が2〜50mg/m2となるように塗布し、その後クリヤ塗膜として架橋性官能基を有するガラス転移点が30〜90℃、数平均分子量3000〜50000のアクリル樹脂を主成分として該アクリル樹脂を架橋硬化させるためのブロックイソシアネート樹脂及びアミノ樹脂を含む熱硬化性樹脂組成物をクリヤ塗膜厚さが1〜10μmとなるように塗布し、前記熱硬化性樹脂組成物は、その固形物100質量部あたり、融点が70〜160℃であって粒径が0.1〜7.0μmであるポリオレフィン系ワックスを固形分量で0.25〜5質量部含有し、前記熱硬化性樹脂組成物が、その固形物100質量部あたり、アクリル樹脂ビーズを0.5〜8質量部含有する一方、オルガノシリカゾル、非晶質シリカ及びアクリル樹脂ビーズ以外の樹脂ビーズを含有しないことを特徴とするクリヤ塗装ステンレス鋼板の製造方法。