JP5161968B2 - ポリマー用添加剤およびその生成方法 - Google Patents
ポリマー用添加剤およびその生成方法 Download PDFInfo
- Publication number
- JP5161968B2 JP5161968B2 JP2010530319A JP2010530319A JP5161968B2 JP 5161968 B2 JP5161968 B2 JP 5161968B2 JP 2010530319 A JP2010530319 A JP 2010530319A JP 2010530319 A JP2010530319 A JP 2010530319A JP 5161968 B2 JP5161968 B2 JP 5161968B2
- Authority
- JP
- Japan
- Prior art keywords
- suspension
- additive
- baso
- polymer
- process step
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
− プロセスパラメーター、例えば温度および圧力、
− 低分子量ポリマー構成成分の移動、
− 静電気力およびその他の引力、および
− 表面構造。
・リン酸H3PO4または水溶性リン酸化合物を0.1から10重量%(P2O5として計算され、乾燥BaSO4に対するものである。)の量で、BaSO4を0.5から50重量%含有する撹拌水性懸濁液に添加し;
・その後、Na2SiO3を0.1から15重量%(SiO2として計算され、乾燥BaSO4に対するものである。)の量で、プロセス・ステップ(a)による撹拌懸濁液に添加し、但しこの懸濁液のpH値は7.5よりも低く保たれているものであり;
・次いで水溶性アルミニウム化合物を0.1から20重量%(Al2O3として計算され、BaSO4に対するものである。)の量で、プロセス・ステップ(b)による撹拌懸濁液に添加し、但しこの懸濁液のpH値は4.5よりも低くは保たれておらず;
・最後に、懸濁した固体を、プロセス・ステップ(c)による懸濁液の水相から分離し、乾燥し、
試薬を添加するためのこれらプロセス・ステップはそれぞれ、30から90分の期間にわたり、65℃よりも低い温度範囲で実施される
ことを特徴とする、ポリマー用添加剤を生成するための方法に関する。
・固形分含量35%、d50,3の体積分布のd50,3=0.4μm(CPS、USA製のディスク遠心分離機「CPSディスク遠心分離機、モデルDC2400」を用いて測定した。)である、BaSO4フィルターケーキ
・導電率が約3μS/cmの脱塩水
・硫酸5%
・384g SiO2/lであるNa2SiO3溶液
・75g Al2O3/lであるAl2(SO4)3溶液
・262g Al2O3/lであるNaAlO2溶液
・固形分含量35%、d50,3の体積分布のd50,3=0.4μm(CPS、USA製のディスク遠心分離機「CPSディスク遠心分離機、モデルDC2400」を用いて測定した。)である、BaSO4フィルターケーキ
・導電率が約3μS/cmの脱塩水
・硫酸5%
・384g SiO2/lであるNa2SiO3溶液
・75g Al2O3/lであるAl2(SO4)3溶液
・262g Al2O3/lであるNaAlO2溶液
・1,1,1−トリメチロールプロパン(TMP)
・固形分含量50%、d50,3の体積分布のd50,3=1.1μm(CPS、USA製のディスク遠心分離機「CPSディスク遠心分離機、モデルDC2400」を用いて測定した。)である、BaSO4フィルターケーキ
・導電率が約3μS/cmの脱塩水
・硫酸5%
・384g SiO2/lであるNa2SiO3溶液
・75g Al2O3/lであるAl2(SO4)3溶液
・262g Al2O3/lであるNaAlO2溶液。
以下の物質は、出発材料として働く:
・固形分含量35%、d50,3の体積分布のd50,3=0.4μm(CPS、USA製のディスク遠心分離機「CPSディスク遠心分離機、モデルDC2400」を用いて測定した。)である、BaSO4フィルターケーキ
・導電率が約3μS/cmの脱塩水
・硫酸5%
・苛性ソーダ溶液5%
以下の物質は、出発材料として働く:
・固形分含量50%、d50,3の体積分布のd50,3=1.1μm(CPS、USA製のディスク遠心分離機「CPSディスク遠心分離機、モデルDC2400」を用いて測定した。)である、BaSO4フィルターケーキ
・導電率が約3μS/cmの脱塩水
・硫酸5%
・苛性ソーダ溶液5%
・固形分含量50%、d50,3の体積分布のd50,3=1.1μm(CPS、USA製のディスク遠心分離機「CPSディスク遠心分離機、モデルDC2400」を用いて測定した。)である、BaSO4フィルターケーキ
・導電率が約3μS/cmの脱塩水
・苛性ソーダ溶液5%
・塩酸5%
・384g SiO2/lであるNa2SiO3溶液
・262g Al2O3/lであるNaAlO2溶液
・50〜55g BaS/lであるBaS溶液
・固形分含量35%、d50,3の体積分布のd50,3=0.4μm(CPS、USA製のディスク遠心分離機「CPSディスク遠心分離機、モデルDC2400」を用いて測定した。)である、BaSO4フィルターケーキ
・導電率が約3μS/cmの脱塩水
・苛性ソーダ溶液5%
・塩酸5%
・384g SiO2/lであるNa2SiO3溶液
・262g Al2O3/lであるNaAlO2溶液
・50〜55g BaS/lであるBaS溶液
以下の物質は、出発材料として働く:
・固形分含量35%、d50,3の体積分布のd50,3=0.4μm(CPS、USA製のディスク遠心分離機「CPSディスク遠心分離機、モデルDC2400」を用いて測定した。)である、BaSO4フィルターケーキ
・導電率が約3μS/cmの脱塩水
・硫酸5%
・384g SiO2/lであるNa2SiO3溶液
・75g Al2O3/lであるAl2(SO4)3溶液
・262g Al2O3/lであるNaAlO2溶液
比較例1〜5および実施例1〜4の硫酸バリウムサンプルを基に、PETフィルムを以下の通り生成した。
比較例1〜5および実施例1〜4の硫酸バリウムサンプルを基に、PETフィルムを以下のように生成した。
比較例1〜5および実施例1〜4の材料ならびにシリカベースの添加剤を同じ手法で最初に押し出して、5%PETマスターバッチを得、それによって、そこから厚さ約100μmのPET流延フィルムを、押出機にフラットフィルム・アタッチメントを用いることにより最初に生成し、その後、二軸方向に延伸することにより、厚さ約10μmのBOPETフィルムが得られる。そのようにするために、10×10cmと測定される、押し出されたフラットフィルムの切出し部分を、100℃の温度で、一定の延伸速度および延伸倍率3×3で延伸する。
Claims (18)
- (a)リン酸H3PO4または水溶性リン酸化合物を0.1から10重量%(P2O5として計算され、乾燥BaSO4に対するものである。)の量で、BaSO4を0.5から50重量%含有する撹拌水性懸濁液に添加し;
(b)その後、Na2SiO3を0.1から15重量%(SiO2として計算され、乾燥BaSO4に対するものである。)の量で、プロセス・ステップ(a)による撹拌懸濁液に添加し、但し懸濁液のpH値は7.5よりも低く保たれているものであり;
(c)次いで水溶性アルミニウム化合物を0.1から20重量%(Al2O3として計算され、BaSO4に対するものである。)の量で、プロセス・ステップ(b)による撹拌懸濁液に添加し、但し懸濁液のpH値は4.5よりも低くは保たれないものであり;
(d)最後に、懸濁した固体を、プロセス・ステップ(c)による懸濁液の水相から分離し、乾燥し;
プロセス・ステップ(a)、(b)、および(c)の各々は、30から90分の期間にわたって65℃よりも低い温度範囲でそれぞれ実施される
ことを特徴とする、ポリマー用添加剤を生成するための方法。 - プロセス・ステップ(a)、(b)、および(c)が、55から65°Cよりも低い温度範囲で実施されることを特徴とする、請求項1に記載の方法。
- プロセス・ステップ(a)、(b)、および(c)がそれぞれ、50から70分の期間にわたって実施されることを特徴とする、請求項1または請求項2に記載の方法。
- プロセス・ステップ(c)の生成物を、有機コーティング剤でコーティングするためのプロセス・ステップにかけ、有機コーティング剤が架橋、分散、もしくは解膠剤、またはこれらの混合物から選択されるものであることを特徴とする、請求項1から請求項3の一項に記載の方法。
- 有機コーティング剤でコーティングするための前記プロセス・ステップが、5から60分の期間にわたって40から80℃の温度で実施される、請求項4に記載の方法。
- 有機コーティング剤が、有機酸のアルカリ金属塩、ポリホスフェート、ポリ(メタ)アクリレート、ポリエーテル、陰イオン的に変性されたポリエーテル、脂肪アルコールポリグリコールエーテル、多価アルコール、変性ポリウレタン、もしくは陰イオン活性脂肪族エステルのアルカリ金属またはアルカリ土類金属塩、またはこれらの混合物を含む群から選択される、請求項4または請求項5に記載の方法。
- プロセス・ステップ(d)の生成物を、10μmよりも小さい粒度が得られるように、衝撃式または流体エネルギージェットミルで破砕ステップにかけることを特徴とする、請求項1から請求項6の一項に記載の方法。
- プロセス・ステップ(d)の生成物を、破砕ステップを継続して10μmよりも小さい粒度が得られることを特徴とする、請求項1から請求項7の一項に記載の方法。
- 請求項1から8のいずれか一項に記載の方法により得ることができる、ポリマー用添加剤。
- ポリマーのアンチブロッキング特性を改善するための、請求項9に記載の添加剤の使用。
- ポリマーの光学特性を改善するための、請求項9に記載の添加剤の使用。
- 請求項9に記載の添加剤の含量を、完成された生成物に対して200から10000ppmの範囲で含むポリマー組成物。
- フィルムを形成するための、請求項12に記載のポリマー組成物の使用。
- 請求項13に記載の方法により得ることができるフィルム。
- ポリマー繊維の加工特性を改善するための、請求項9に記載の添加剤の使用。
- ポリマー繊維の曳糸性を改善するための、請求項9に記載の添加剤の使用。
- コーティング剤が改善された光学特性を有するための、請求項9に記載の添加剤の使用。
- PCBインクが改善された光学特性を有するための、請求項9に記載の添加剤の使用。