JP2020056033A - 発泡シートおよび物品に適したポリプロピレン組成物 - Google Patents
発泡シートおよび物品に適したポリプロピレン組成物 Download PDFInfo
- Publication number
- JP2020056033A JP2020056033A JP2019211530A JP2019211530A JP2020056033A JP 2020056033 A JP2020056033 A JP 2020056033A JP 2019211530 A JP2019211530 A JP 2019211530A JP 2019211530 A JP2019211530 A JP 2019211530A JP 2020056033 A JP2020056033 A JP 2020056033A
- Authority
- JP
- Japan
- Prior art keywords
- polypropylene
- melt strength
- hms
- range
- high melt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
高溶融強度ポリプロピレン(HMS‐PP)と;
粒径d50が1μm〜30μmの範囲内の核形成剤(NA;nucleating agent)と
を含む、ポリプロピレン組成物(PC;polypropylene composition)を提供する。
(a)80.0〜99.90重量部の高溶融強度ポリプロピレン(HMS‐PP)と、
(b)0.10〜5.0重量部の、本明細書に記載のように決定される粒径d50が1μm〜30μmの範囲内の核形成剤(NA)と、
(c)任意に1〜20重量部のさらなる高溶融強度ポリプロピレン(HMS‐PP’)と
を含み、
高溶融強度ポリプロピレン(HMS‐PP)と、核形成剤(NA)と、存在する場合にはさらなる高溶融強度ポリプロピレン(HMS‐PP’)との総量は、ポリプロピレン組成物(PC)に基づいて少なくとも85重量%である。
本発明により提供されるポリプロピレン組成物(PC)の主成分は、高溶融強度ポリプロピレン(HMS‐PP)である。高溶融強度ポリプロピレンは分岐ポリプロピレンであり、したがってポリプロピレンの骨格が側鎖を含むのに対し非分岐ポリプロピレンすなわち直鎖ポリプロピレンは側鎖を含まない点で直鎖ポリプロピレンと異なる。側鎖は、ポリプロピレンのレオロジに大きく影響する。したがって直鎖ポリプロピレンと高溶融強度ポリプロピレンとは、応力下の流動挙動によって明確に区別されうる。
(a)F30溶融強度が20.0超〜50.0cNなど、20.0cNを超え、21.0cNを超えるのがより好ましく、21.0〜50.0cNであるのがさらに好ましく、25.0〜50.0cNであるのがなお好ましく、25.0〜45.0cNであるのがなおさら好ましく、32.0〜42.0cNまたは34.0cN〜42.0cNなど、30.0〜45.0cNであるのが最も好ましく、
(b)v30溶融延伸性が210超〜300mm/sなど、200mm/sを超え、220超〜300mm/sであるのがより好ましく、225mm/sを超えるのがさらに好ましく、225〜300mm/sであるのがなお好ましく、250〜290mm/sまたは253〜290mm/sなど、230〜290mm/sであるのがなおさら好ましい。
(a)メルトフローレートMFR2(230℃)が、15.0g/10分以下であり、0.5〜15.0g/10分の範囲内であるのがより好ましく、1.5〜15.0g/10分の範囲内など、1.0〜15.0g/10分の範囲内であるのがなお好ましく、
(b)F30溶融強度が20.0超〜50.0cNなど、20.0cNを超え、21.0cNを超えるのがより好ましく、21.0〜50.0cNであるのがさらに好ましく、25.0〜50.0cNであるのがなお好ましく、25.0〜45.0cNであるのがなおさら好ましく、32.0〜42.0cNまたは34.0〜42.0cNなど、30.0〜45.0cNであるのが最も好ましく、
(c)v30溶融延伸性が200mm/sを超え、220超〜300mm/sなど、210超〜300mm/sであるのが好ましく、225mm/sを超えるのがより好ましく、225〜300mm/sであるのがさらに好ましく、250〜290mm/sまたは253〜290mm/sなど、230〜290mm/sであるのがなお好ましい。
(a)高溶融強度プロピレンホモポリマー(H‐HMS‐PP)である場合には、
(i)プロピレンと、
(ii)二官能性不飽和モノマー(類)および/または多官能性不飽和低分子量ポリマー(類)と
から誘導される単位を含み、
あるいは
(b)高溶融強度ランダムプロピレンコポリマー(R‐HMS‐PP)である場合には、
(i)プロピレンと、
(ii)エチレンおよび/またはC4〜C12α‐オレフィン、例えば1‐ブテンおよび/または1‐ヘキセン、好ましくはエチレン(erthylene)と、
(iii)二官能性不飽和モノマー(類)および/または多官能性不飽和低分子量ポリマー(類)と
から誘導される単位を含む。
ジビニルアニリン、m‐ジビニルベンゼン、p‐ジビニルベンゼン、ジビニルペンタン、およびジビニルプロパン等のジビニル化合物、
アクリル酸アリル、メタクリル酸アリル、マレイン酸アリルメチルおよびアリルビニルエーテル等のアリル化合物、
1,3‐ブタジエン、クロロプレン、シクロヘキサジエン、シクロペンタジエン、2,3‐ジメチルブタジエン、ヘプタジエン、ヘキサジエン、イソプレンおよび1,4‐ペンタジエン等のジエン、
芳香族および/または脂肪族ビス(マレイミド)ビス(シトラコンイミド)、ならびにこれらの不飽和モノマーの混合物
でありうる。
ポリブタジエン、特にポリマー鎖中の異なるミクロ構造、すなわち1,4‐シス、1,4‐トランスおよび1,2‐(ビニル)が主に1,2‐(ビニル)構成であるもの
ポリマー鎖中に1,2‐(ビニル)を有するブタジエンおよびスチレンのコポリマー
である。
上述のように、高溶融強度ポリプロピレン(HMS‐PP)は修飾ポリプロピレンであり、ポリプロピレン(PP)を熱分解フリーラジカル形成剤と任意に二官能性不飽和モノマー(類)と、および/または多官能性不飽和低分子量ポリマー(類)と反応させることにより得られる。ポリプロピレン(PP)は、直鎖ポリプロピレン(l‐PP)であるのが好ましい。
(a)F30溶融強度が1.0cNを超え、2.0cNを超えるのが好ましく、1.0〜68.0cN未満の範囲内であるのがより好ましく、1.5〜65.0cNの範囲内であるのがさらに好ましく、2.0〜60.0cNの範囲内であるのがなお好ましく、2.5〜45.0cNの範囲内など、2.5〜50.0cNの範囲内であるのがなおさら好ましく、
(b)v30溶融延伸性が200mm/s未満であり、190mm/s未満であるのが好ましく、100〜200mm/s未満の範囲内であるのがより好ましく、120〜190mm/sの範囲内であるのがさらに好ましく、125〜170mm/sの範囲内など、120〜175mm/sの範囲内であるのがなお好ましい。
(a)ISO1133にしたがって測定したメルトフローレートMFR2(230℃)が0.1〜15.0g/10分または0.2〜15.0g/10分など、0.1〜18.0g/10分の範囲内であり、0.2〜10.0g/10分未満の範囲内であるのがより好ましく、0.2〜9.0g/10分の範囲内であるのがさらに好ましく、0.3〜8.0g/10分の範囲内であるのがなお好ましく、
(b)F30溶融強度が1.0cNを超え、2.0cNを超えるのが好ましく、1.0〜68.0cN未満の範囲内であるのがより好ましく、1.5〜65.0cNの範囲内であるのがさらに好ましく、2.0〜60.0cNの範囲内であるのがなお好ましく、2.5〜45.0cNの範囲内など、2.5〜50.0cNの範囲内であるのがなおさら好ましく、かつ
(c)v30溶融延伸性が200mm/s未満であり、190mm/s未満であるのが好ましく、100〜200mm/s未満の範囲内であるのがより好ましく、120〜190mm/sの範囲内であるのがさらに好ましく、125〜170mm/sの範囲内など、120〜175mm/sの範囲内であるのがなお好ましい。
ポリプロピレン組成物(PC)は、一つ以上の、好ましくは一つの、核形成剤(類)をさらに含む。
本発明のポリプロピレン組成物(PC)の調製の間に、さらなるHMSポリプロピレン(HMS‐PP’)が加えられうる。このさらなるHMSポリプロピレン(HMS‐PP’)は、添加剤(A)および/または一つ以上の核形成剤(NA)、好ましくは核形成剤(NA)と任意に添加剤(A)とを本発明のポリプロピレン組成物(PC)に取り入れるために用いられるのが好ましい。したがって好ましい実施形態では、核形成剤(NA)と任意に添加剤(A)とが添加剤混合物(AM:additive mixture)の形態で本発明のポリプロピレン組成物(PC)に導入され、前記添加剤混合物は、さらなるHMSポリプロピレン(HMS‐PP’)と、核形成剤(NA)と、任意に添加剤(A)とを含み、好ましくはこれらからなる。
添加剤(A)は、高溶融強度ポリプロピレン(HMS‐PP)およびその応用の技術分野で有用な任意の添加物でありうる。したがって、本発明のポリプロピレン組成物において、したがって添加剤混合物(AM)の形態で用いられる添加剤(A)は、抗酸化剤(例えば立体障害フェノール、亜リン酸塩/ホスホナイト、硫黄含有抗酸化剤、アルキルラジカルスカベンジャー、芳香族アミン、ヒンダードアミン安定剤、またはこれらのブレンド)、金属不活性化剤(例えばIrganox MD1024)、またはUV安定剤(例えばヒンダードアミン光安定剤)などの安定剤を含むがこれらに限定されない。その他の典型的な添加剤は、静電気防止剤または防曇剤等の修飾因子(例えばエトキシ化アミンおよびアミド、またはグリセロールエステル)、掃酸剤、発泡剤(blowing agent)、付着剤(例えばポリイソブテン)、潤滑剤および樹脂(イオノマーワックス、PE‐およびエチレンコポリマーワックス、フィッシャー‐トロプシュワックス、モンタン系ワックス、フルオロ系化合物、またはパラフィンワックス)のほか、スリップ剤およびブロッキング防止剤(例えばステアリン酸カルシウム、エルカミド、オレアミド、タルク天然シリカおよび合成シリカ、またはゼオライト)である。添加剤(A)は、抗酸化剤(例えば立体障害フェノール、亜リン酸塩/ホスホナイト、硫黄含有抗酸化剤、アルキルラジカルスカベンジャー、芳香族アミン、ヒンダードアミン安定剤、またはこれらのブレンド)、金属不活性化剤(例えばIrganox MD1024)、UV安定剤(例えばヒンダードアミン光安定剤)、静電気防止剤または防曇剤(例えばエトキシ化アミンおよびアミド、またはグリセロールエステル)、掃酸剤、発泡剤(blowing agent)、付着剤(例えばポリイソブテン)、潤滑剤および樹脂(イオノマーワックス、PE‐およびエチレンコポリマーワックス、フィッシャー‐トロプシュワックス、モンタン系ワックス、フルオロ系化合物、またはパラフィンワックス)、スリップ剤(例えばステアリン酸カルシウム)、ブロッキング防止剤(例えばエルカミド、オレアミド、タルク天然シリカおよび合成シリカ、またはゼオライト)、ならびにこれらの混合物からなる群より選択されるのが好ましい。
上述のように、ポリプロピレン組成物(PC)は、高溶融強度ポリプロピレン(HMS‐PP)および核形成剤(NA)を含む。
(a)80.0〜99.90重量部、好ましくは90〜99.90重量部、より好ましくは92〜99.80重量部、なお好ましくは93.0〜99.70重量部、なお好ましくは95.0〜99.70重量部の高溶融強度ポリプロピレン(HMS‐PP)と;
(b)0.10〜15.0重量部、好ましくは0.20〜10.0重量部、より好ましくは0.30〜7.0重量部、最も好ましくは0.30〜5.0重量部の核形成剤(NA)と;
(c)任意に1〜20重量部、好ましくは1〜10重量部、より好ましくは1〜5重量部のさらなる高溶融強度ポリプロピレン(HMS‐PP’)と
を含むのがより好ましい。
(a)F30溶融強度が20.0超〜50.0cNなど、20.0cNを超え、21.0cNを超えるのがより好ましく、21.0〜50.0cNであるのがさらに好ましく、25.0〜50.0cNであるのがなお好ましく、25.0〜45.0cNであるのがなおさら好ましく、32.0〜42.0cNまたは34.0cN〜42.0cNなど、30.0〜45.0cNであるのが最も好ましく、
(b)v30溶融延伸性が200mm/sを超え、220超〜300mm/sなど、210超〜300mm/sであるのが好ましく、225mm/sを超えるのがより好ましく、225〜300mm/sであるのがさらに好ましく、250〜290mm/sまたは253〜290mm/sなど、230〜290mm/sであるのがなお好ましい。
(a)メルトフローレートMFR2(230℃)が、15.0g/10分以下であり、0.5〜15.0g/10分の範囲内であるのが好ましく、0.5〜15.0g/10分の範囲内であるのがより好ましく、1.5〜15.0g/10分の範囲内または1.0〜15.0g/10分の範囲内など、1.0〜15.0g/10分の範囲内であるのがなお好ましく、
(b)F30溶融強度が20.0超〜50.0cNなど、20.0cNを超え、21.0cNを超えるのがより好ましく、21.0〜50.0cNであるのがさらに好ましく、25.0〜50.0cNであるのがなお好ましく、25.0〜45.0cNであるのがなおさら好ましく、32.0〜42.0cNまたは34.0〜42.0cNなど、30.0〜45.0cNであるのが最も好ましく、
(c)v30溶融延伸性が200mm/sを超え、220超〜300mm/sなど、210超〜300mm/sであるのが好ましく、225mm/sを超えるのがより好ましく、225〜300mm/sであるのがさらに好ましく、250〜290mm/sまたは253〜290mm/sなど、230〜290mm/sであるのがなお好ましい。
(a)80.0〜99.90重量部、好ましくは90〜99.90重量部、より好ましくは92〜99.80重量部、なお好ましくは93.0〜99.70重量部の高溶融強度ポリプロピレン(HMS‐PP)と、
(b)0.10〜15.0重量部、好ましくは0.20〜10.0重量部、より好ましくは0.30〜7.0重量部、最も好ましくは0.30〜5.0重量部の核形成剤(NA)と、
(c)任意に1〜20重量部、好ましくは1〜10重量部、より好ましくは1〜5重量部のさらなる高溶融強度ポリプロピレン(HMS‐PP’)と
を含む、ポリプロピレン組成物であって、
ISO1133にしたがって測定したメルトフローレートMFR2(230℃)が、7.0g/10分以下であり、0.5〜15.0g/10分の範囲内であるのがより好ましく、1.5〜15.0g/10分の範囲内または1.0〜15.0g/10分の範囲内など、1.0〜15.0g/10分の範囲内であるのがなお好ましく、
ゲル含量が1.00重量%未満であり、0.80重量%未満であるのが好ましく、0.50重量%未満であるのがより好ましく、
F30溶融強度が20.0超〜50.0cNなど、20.0cNを超え、21.0cNを超えるのがより好ましく、21.0〜50.0cNであるのがさらに好ましく、25.0〜50.0cNであるのがなお好ましく、25.0〜45.0cNであるのがなおさら好ましく、32.0〜42.0cNまたは34.0cN〜42.0cNなど、30.0〜45.0cNであるのが最も好ましく、
v30溶融延伸性が220超〜300mm/sなど、210超〜300mm/sであり、225mm/sを超えるのがより好ましく、225〜300mm/sであるのがさらに好ましく、250〜290mm/sまたは253〜290mm/sなど、230〜290mm/sであるのがなお好ましい、
ポリプロピレン組成物を包含する。
本発明は、本明細書に記載の本発明のポリプロピレン組成物を含む発泡体も特徴とする。発泡体は、本発明によるポリプロピレン組成物を少なくとも70重量%含むのが好ましく、少なくとも80重量%含むのがより好ましく、少なくとも90重量%含むのがより好ましく、少なくとも95重量%含むのがなお好ましい。好ましい実施形態では、発泡体は本発明のポリプロピレン組成物(PC)(発泡工程の後に発泡体中に発泡剤がまだ存在する場合には発泡剤を除く)からなる。
本発明の発泡体は、厚さが1.5mm以下であり、および/または密度が100〜300kg/m3であり、125〜275kg/m3であるのがより好ましく、150〜250kg/m3であるのがより好ましく、175〜225kg/m3であるのが最も好ましい、シートの形態であるのが好ましい。したがって一実施形態では、本発明は、厚さが1.5mm以下であり、および/または密度が100〜300kg/m3であり、125〜275kg/m3であるのがより好ましく、150〜250kg/m3であるのがより好ましく、175〜225kg/m3であるのが最も好ましい、発泡シートを目的とする。
本発明は、本発明の発泡シートとカバー層とを含む多層シートをさらに目的とし、カバー層(CL;cover layer)は密度が少なくとも0.85g/cm3である。
本発明の発泡シートと、
カバー層(CL)であって、密度が少なくとも0.85g/cm3であり、二軸配向ポリプロピレン(BOPP)であるのが好ましいポリプロピレン(CL−PP)を、少なくとも85重量%、好ましくは少なくとも90重量%、最も好ましくは少なくとも95重量%の量含み、および/または厚みが100μmを超えないのが好ましく、5〜40μmであるのがより好ましく、10〜30μmであるのが最も好ましい、カバー層と
を含み、
本発明の発泡シートはカバー層(CL)に直接取り付けられる。
PE:PP重量比が5:95〜95:5であり、5:95〜50:50であるのが好ましく、5:95〜30:70であるのがより好ましく、10:90〜20:80であるのが最も好ましいポリエチレン‐ポリプロピレンブレンド(PE‐PP)を含み、厚みが100μmを超えず、20〜80μmであるのがより好ましく、30〜70μmであるのがなお好ましく、40〜60μmであるのが最も好ましい、接着剤層と、
接着剤層の第一側部に直接取り付けられた本発明の発泡シートと、
接着剤層の第二側部に直接取り付けられたカバー層(CL)であって、密度が少なくとも0.85g/cm3であり、二軸配向ポリプロピレン(BOPP)であるのが好ましいポリプロピレン(CL−PP)を、少なくとも85重量%、好ましくは少なくとも90重量%、最も好ましくは少なくとも95重量%の量含み、および/または厚みが100μmを超えないのが好ましく、5〜40μmであるのがより好ましく、10〜30μmであるのが最も好ましい、カバー層と
を含む。
本発明は、本発明による発泡シートまたは多層シートを含む物品をさらに目的とし、物品は本発明による多層シートを含むのが好ましい。
上で既に概説したように、高溶融強度ポリプロピレン(HMS‐PP)は、ポリプロピレン(PP)、好ましくは直鎖ポリプロピレン(l‐PP)を用いて生産される。その方法は、ポリプロピレン(PP)を熱分解フリーラジカル形成剤と任意に二官能性不飽和モノマー(類)と、および/または多官能性不飽和低分子量ポリマー(類)と反応させ、これにより高溶融強度ポリプロピレン(HMS‐PP)を得る、ステップ(a)を少なくとも含む。
アシルペルオキシド:ベンゾイルペルオキシド、4‐クロロベンゾイルペルオキシド、3‐メトキシベンゾイルペルオキシド、および/またはメチルベンゾイルペルオキシド。
本発明は、容器等の物品の生産のための、本発明によるポリプロピレン組成物(PC)、本発明による発泡シートまたは本発明による多層シートの使用をさらに目的とする。
別段の定めがない限り、以下の用語および決定方法の定義が以上の本発明の一般的説明にも以下の実施例にも当てはまる。
コモノマー含量は、当技術分野で周知の方法で、定量的13C核磁気共鳴(NMR:nuclear magnetic resonance)分光法により較正した基本的帰属の後、定量的フーリエ変換赤外分光法(FTIR:Fourier transform infrared spectroscopy)により決定する。薄膜を250μmの厚さにプレスし、スペクトルを透過モードで記録する。
本明細書に記載される試験は、ISO16790:2005にしたがう。
約2gのポリマー(mp)を秤量し、秤量した金属のメッシュに入れる(mp+m)。メッシュ中のポリマーを、沸騰キシレンを含むソックスレー装置で5時間抽出する。その後、溶離剤を新しいキシレンに交換し、もう1時間沸騰を続ける。その後、メッシュを乾燥し、再び秤量する(mXHU+m)。式mXHU+m−mm=mXHUにより得られる熱キシレン不溶分の質量(mXHU)を、ポリマーの重量(mp)と比較して、キシレン可溶分の分率(mXHU/mp)を得る。
ポリマーサンプルに、粒度分布試験を行った。ふるい分析は、以下のサイズのワイヤメッシュスクリーンを有するふるいの入れ子カラムを含んだ:>20μm、>32μm、>63μm、>100μm、>125μm、>160μm、>200μm、>250μm、>315μm、>400μm、>500μm、>710μm、>1mm、>1.4mm、>2mm、>2.8mm。スクリーン開口部が最大の上部ふるいにサンプルを注ぎ入れた。カラムの下方のふるいはそれぞれ、一つ上のふるいよりも小さい開口部を有する(上に示したサイズを参照)。底部にレシーバがある。カラムを機械式振とう機内に置いた。振とう機がカラムを振とうした。振とうが完了した後、各ふるい上の材料を秤量した。その後、各ふるいのサンプルの重量を総重量で除算して、各ふるい上に保持された割合を得た。
メジアン粒径d50は、Sedigraph 5100(Micromeritics Corporation)を使用してISO13317‐3にしたがって重力液体沈降により決定される粒径分布[重量パーセント]から計算する。
これは、スイスPRECISA Gravimetrics AGの分析およびセミミクロ精密天秤、比重天秤(XS225A)を使用して測定した;試験方法:アルキメデスの応用、サンプルの密度を自動計算する。
発泡体のセルサイズ直径は、光学顕微鏡の台湾(Tawain)CBS実体顕微鏡を使用して決定した。
使用した試験方法は、以下の通りである:
1.発泡材料のストリップを横方向(CD;cross direction)および機械方向(MD;machine direction)に沿って切断する。
2.発泡材料をフラットクランプで保持し、カミソリ刃を用いて微細に削る。
3.顕微鏡を100×に合わせ、発泡材料上への照明を調節する。
4.CDおよびMD方向の特有のセルのそれぞれの長さおよび幅の測定を行い、値を記録する。
5.測定した特有のセルの数を計数し、値を記録する。
6.CDおよびMD方向の特有のセルのそれぞれの全長まで3〜4の接線にわたりセル壁厚の測定を行い、値を記録する。
7.第一測定セル群の下部から開始して、セル群の真ん中まで、セル群の上部までの、三つのストリップ全厚の測定を行う。
8.最下部の完全セルから開始して最上部の完全セルまでの全長測定を行う。
9.最上部の不完全セルの下部がスクリーンの下部に触れるように、顕微鏡視野を移動する。
10.ストリップの約0.200’’〜0.800’’が測定されるまで、新たな特有のセルのそれぞれに対してステップ4〜9を繰り返す。全長およびセル組成が重複しないことを確認する。第一測定後の各全長測定は、前回の最上部の完全セルの上部から現在の最上部の完全セルの上部までをとる。
これは、Mitsutoyo、日本の携帯型表面粗さ測定器、モデルSJ‐310を使用して測定した。表面粗さ測定器(別名粗面計)は、接触表面粗さ測定器である。粗さの決定は完全に自動化され、内蔵ソフトウェアにより行われる。
断熱カップの調製:
以下のステップを適用する。
2.第一ステップで得られたブレンドを、Pitac台湾の第一一軸スクリュ押出機(スクリュ直径90mm;L/D比26)に供給するステップ。押出機は、ポリマーを溶解させるために200℃の温度で運転される(五つの加熱ゾーン:150℃;200℃;200℃;200℃;200℃)。
3.第一一軸スクリュ押出機の最後のセクションに5重量%の液状ブタンを(発泡剤(blowing agent)として)注入し、これにより融解ブレンドを得るステップ。
4.融解ブレンドをPitac台湾(スクリュ直径120mm;L/D比34)の第二一軸スクリュ押出機に通し、これにより融解ブレンドを第二一軸スクリュ押出機の終わりに160℃に冷却する、ステップ。
5.第四ステップの融解ブレンドを第二押出機の最後に配置された押出ダイに通すステップであって、押出機を出る際に融解ブレンドは大気圧への圧力降下にさらされ(圧力差は約100バールである)、この突然の圧力降下によって融解ブレンド中の発泡剤(blowing aget)が膨張し、これにより発泡を達成して発泡構造体を生じ、その後発泡構造体が冷却ドラムで100℃より低い温度で冷却され、これにより200kg/m3の密度および0.7mmの厚さの発泡シートが得られる、ステップ。
6.その後、発泡シートと20μm厚のBOPPフィルムとを台湾YC Groupのインライン押出積層ユニットに通して、発泡シートを台湾(Tawain)LCYの市販のポリプロピレンPC932から作製された基材の一方の側に、BOPPフィルムを前記基板の反対側に積層し、これにより0.7mmの発泡シートと、50μmの基材と、20μmのBOPPフィルムとの3層シートを得る。
7.3層シートをロールに巻くステップ。
8.3層シートを3日間硬化させ、その後、3層シートをPitac台湾(Tawain)の平坦化機で処理して、652mmの幅および762mmの長さの平坦シートを得、同時に3層シートの発泡層にコロナ処理が行われる、ステップ。
9.その後、Komori日本のUVオフセット印刷装置により平坦シートのコロナ処理した表面上に印刷し、Baodear台湾(Tawain)のダイカット処理を通して、ブランク材料を得る。
10.ブランク材料をACE PACK韓国のカップ形成機において用いて、断熱カップを得(この工程の間に、カップの側面用のブランク材料は280℃に加熱される;カップの側面用のブランク材料の表面を少し溶解させて結合できるようにするために、側部封止温度は450℃であるが、カップの底部(80mm幅)用のブランク材料は、カップの底部を得るための成形および穴あけのステップのために100℃に加熱され;その後前記カップの底部が300℃まで加熱され、カップの側面とともに畳まれ;カップの上部の縁どり工程は、カップの側面の底部から遠い側を400℃まで加熱した後、縁どり工程に通すことによって達成される。
Claims (14)
- (a)80.0〜99.90重量部の高溶融強度ポリプロピレン(HMS‐PP)と;
(b)0.10〜5.0重量部の、本明細書に記載のように決定される粒子サイズd50が1μm〜30μmの範囲内の核形成剤(NA)と;
(c)任意に1〜20重量部のさらなる高溶融強度ポリプロピレン(HMS‐PP’)と
を含む、ポリプロピレン組成物(PC)であって、
前記高溶融強度ポリプロピレン(HMS‐PP)と、前記核形成剤(NA)と、存在する場合には前記さらなる高溶融強度ポリプロピレン(HMS‐PP’)との総量は、前記ポリプロピレン組成物(PC)に基づいて少なくとも85重量%である、
ポリプロピレン組成物(PC)。 - 前記核形成剤(NA)はタルクである、請求項1に記載のポリプロピレン組成物(PC)。
- 前記高溶融強度ポリプロピレン(HMS‐PP)は、F30溶融強度が30.0cNを超えおよび/またはv30溶融延伸性が220mm/sを超え、前記F30溶融強度および前記v30溶融延伸性は、ISO16790:2005にしたがって決定される、請求項1〜2のいずれか一項に記載のポリプロピレン組成物(PC)。
- 前記高溶融強度ポリプロピレン(HMS‐PP)は、前記ポリプロピレン組成物(PC)の少なくとも70重量%を構成する、請求項1〜3のいずれか一項に記載のポリプロピレン組成物(PC)。
- 請求項1〜4のいずれか一項に記載のポリプロピレン組成物(PC)を含む、発泡体。
- 厚さが1.5mm以下でありおよび/または密度が150〜250kg/m3であるシートの形態である、請求項5に記載の発泡体。
- 請求項5または6に記載の発泡シートとカバー層(CL)とを含む、多層シートであって、前記カバー層(CL)は、密度が少なくとも0.85g/cm3である、多層シート。
- 前記カバー層(CL)は、ポリプロピレン(CL‐PP)を含む、請求項7に記載の多層シート。
- 前記ポリプロピレン(CL‐PP)は、二軸配向ポリプロピレン(BOPP)である、請求項8に記載の多層シート。
- 請求項1〜4のいずれか一項に記載のポリプロピレン組成物(PC)、請求項5または6のいずれか一項に記載の発泡シートを含むか、あるいは請求項7〜9のいずれか一項に記載の多層シートを含む、物品。
- 前記物品は容器であり、請求項8〜10のいずれか一項に記載の多層シートを含み、前記カバー層は、前記容器の内側に位置する、請求項10に記載の物品。
- 前記物品は容器または請求項11に記載の容器であり、前記容器はボトル、カップ、缶、キャニスタ、ボウルもしくはトレイである、請求項10に記載の物品。
- 請求項5または6に記載の発泡シート、請求項7〜9のいずれか一項に記載の多層シートおよび/あるいは請求項10〜12のいずれか一項に記載の物品を生産するための方法。
- 物品を生産するための、請求項1〜4のいずれか一項に記載のポリプロピレン組成物(PC)、請求項5または6のいずれか一項に記載の発泡シート、あるいは請求項7〜9のいずれか一項に記載の多層シートの使用。