JP2018114747A - 銀鏡膜層を備えた表面装飾構造及びその形成方法 - Google Patents
銀鏡膜層を備えた表面装飾構造及びその形成方法 Download PDFInfo
- Publication number
- JP2018114747A JP2018114747A JP2017215329A JP2017215329A JP2018114747A JP 2018114747 A JP2018114747 A JP 2018114747A JP 2017215329 A JP2017215329 A JP 2017215329A JP 2017215329 A JP2017215329 A JP 2017215329A JP 2018114747 A JP2018114747 A JP 2018114747A
- Authority
- JP
- Japan
- Prior art keywords
- compound
- silver mirror
- film layer
- film
- forming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】基体表面に下塗り塗膜12、銀鏡膜層13及び上塗り塗膜14が形成された表面装飾構造10において、銀鏡膜層13は、表面に高分子分散剤が被覆されたナノメーターサイズの銀粒子が積層された状態で膜を形成しており、上塗り塗膜14は、溶媒として、脂肪族炭化水素化合物、10質量%以下の芳香族化合物を含む脂肪族炭化水素化合物溶液及びジイソブチルケトンから選択された少なくとも1種を含むものを用いて形成されたものからなる。下塗り塗膜12、上塗り塗膜14の少なくとも一方には防錆剤が含有されていてもよく、さらには銀鏡膜層13にも防錆剤が含有されていてもよい。
【選択図】図1
Description
基体表面に下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された表面装飾構造において、
前記銀鏡膜層は、ナノメーターサイズの銀粒子が積層された状態で膜を形成しており、
前記上塗り塗膜は、溶媒として、脂肪族炭化水素化合物、10質量%以下の芳香族化合物を含む脂肪族炭化水素化合物溶液及びジイソブチルケトンから選択された少なくとも1種を含むものを用いて形成されたものからなることを特徴とする。
(1)ベンゾトリアゾール系化合物とベンゾエート系化合物。
(2)ベンゾトリアゾール系化合物とヒンダードアミン系化合物。
(3)トリアジン系化合物とヒンダードアミン系化合物。
基体表面に下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された表面装飾構造において、
前記銀鏡膜層は、ナノメーターサイズの銀粒子が積層された状態で膜を形成しており、
前記上塗り塗膜は、極性基を有する樹脂塗膜からなることを特徴とする。
(1)ベンゾトリアゾール系化合物とベンゾエート系化合物。
(2)ベンゾトリアゾール系化合物とヒンダードアミン系化合物。
(3)トリアジン系化合物とヒンダードアミン系化合物。
基体表面に、下塗り塗膜、銀鏡膜層及び上塗り塗膜を順次形成することからなる表面装飾構造の形成方法において、
前記基体の表面に下塗り塗料をスプレー塗装し、乾燥することにより前記下塗り塗膜を形成し、
前記銀鏡膜層を、高分子分散剤が溶解された有機溶媒中にナノメーターサイズの銀粒子が分散されている銀鏡膜層形成用組成液を前記下塗り塗膜が形成された基体上にスプレー塗装し、次いで常温又は加熱下で乾燥することにより形成し、
前記銀鏡膜層の表面に、溶媒として、脂肪族炭化水素化合物、10質量%以下の芳香族化合物を含む脂肪族炭化水素化合物溶液及びジメチルイソブチルケトンから選択された少なくとも1種を含む上塗り塗料をスプレー塗装し、乾燥することにより前記上塗り塗膜を形成することを特徴とする。
(1)ベンゾトリアゾール系化合物とベンゾエート系化合物。
(2)ベンゾトリアゾール系化合物とヒンダードアミン系化合物。
(3)トリアジン系化合物とヒンダードアミン系化合物。
基体表面に、下塗り塗膜、銀鏡膜層及び上塗り塗膜を順次形成することからなる表面装飾構造の形成方法において、
前記基体の表面に下塗り塗料をスプレー塗装し、乾燥することにより前記下塗り塗膜を形成し、
前記銀鏡膜層を、高分子分散剤が溶解された有機溶媒中にナノメーターサイズの銀粒子が分散されている銀鏡膜層形成用組成液を前記下塗り塗膜が形成された基体上にスプレー塗装し、次いで常温又は加熱下で乾燥することにより形成し、
前記銀鏡膜層の表面に、上塗り塗料として極性基を有する樹脂を含む塗料をスプレー塗装し、乾燥することにより前記上塗り塗膜を形成することを特徴とする。
(1)ベンゾトリアゾール系化合物とベンゾエート系化合物。
(2)ベンゾトリアゾール系化合物とヒンダードアミン系化合物。
(3)トリアジン系化合物とヒンダードアミン系化合物。
(1)イソシアネート基とヒドロキシル基とのウレタン反応によって形成される二液性のアクリルウレタン樹脂塗料、
(2)アミノ基を持つアクリル樹脂とエポキシ基を持つシリコン化合物とを脱水かつ脱アルコール縮合反応によって形成される二液性のアクリルシリコン樹脂塗料、
(3)ウレタン反応と脱水かつ脱アルコール縮合反応が同時におこる二液性又は三液性のウレタン変性アクリルシリコン樹脂塗料、
等が挙げられるが、これに限られるものではなく、フッ素樹脂系塗料、ポリエチレン系塗料、ポリプロピレン系塗料等も用いることができる。
(下塗り塗膜)
最初に、銀鏡膜層を備えた表面装飾構造の課題を確認するための予備実験を行った。アクリルポリオールを主剤とするアクリルウレタン塗料(AT62−2(商品名)、大日本塗料((株))が6質量部、溶媒としてのトルエンが7質量部、ポリイソシアネート硬化剤(アクリタン(商品名)硬化剤、大日本塗料(株))が1質量部となる割合で均一に撹拌・混合し、下塗り塗料を調製した。この下塗り塗料を基材としての標準試験片の表面にスプレー塗装し、次いで、100℃で30分間強制乾燥し、複数の、下塗り塗膜が形成された標準試験片予備実験試料を得た。
銀鏡膜層形成用組成液として前記特許文献3に基づいて作成され、市販されているもの(GLANTZCOAT TypeRT シルバー(商品名)、(株)フェクト)を用い、この銀鏡膜層形成用組成液とシンナー(GLANTZCOAT TypeRT シルバーシンナーT2(商品名)、(株)フェクト)で2倍に希釈してスプレー塗装し、95℃で45分間乾燥して、複数の、下塗り塗膜上に銀鏡膜層が形成された標準試験片予備実験試料を得た。なお、この銀鏡膜層形成用組成液は、有機溶媒中に銀ナノ粒子を主成分として含む分散液であり、他に高分子分散剤が含まれている。この銀鏡膜層形成用組成液のスプレー塗装後には、単に乾燥するのみで銀鏡膜層が形成されるが、ここでは90℃で45分間強制乾燥することにより、それぞれの銀鏡膜層の形成時に各銀鏡膜層の乾燥条件が一定となるようし、形成された銀鏡膜層に室温、湿度等による影響が現れないようにした。
アクリルポリオールを主剤とするアクリルウレタン塗料(AT62−2)が6質量部、溶媒としてのエタノールが7質量部、ポリイソシアネート硬化剤(アクリタン硬化剤)が1質量部となる割合で均一に撹拌・混合し、上塗り塗料を調製した。この上塗り塗料を、銀鏡膜層の表面にスプレー塗装し、次いで、100℃で30分間強制乾燥し、複数の、下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された標準試験片からなる予備実験試料を得た。
(1)JIS K5600−7−1に準拠したクロスカットを形成した表面に対して塩水噴霧試験を行った結果、クロスカット部に変色ないし剥離が認められた(図2参照)。
(2)JIS K5600−7−7に準拠したキセノンアークランプを用いた耐候性促進試験を行ったところ、色調に黄変が認められた。
(3)JIS K5600−5−6に準拠したクロスカットを形成した表面に対して付着性試験を行ったところ、銀鏡膜層と下塗り塗膜との間ないし銀鏡膜層と上塗り塗膜との間に剥離が生じた(図3参照)。
まず、実験例1〜21により、予め下塗り塗装上に形成された銀鏡膜層に対し上塗り塗膜形成用塗料の溶媒を種々変更してスプレー塗装し、乾燥後に銀鏡膜層の変色の程度を目視により確認した。
(下塗り塗膜)
下塗り塗料の主剤としてアルコキシル基を含有するシリコンオリゴマー(GLANZCOAT Type RT プライマーブラックG、(株)フェクト)が6質量部、溶媒としてのエタノールが7質量部、硬化剤(GLANZCOAT type RT プライマー硬化剤U、(株)フェクト)が1質量部となる割合で均一に撹拌・混合し、下塗り塗料を調製した。この下塗り塗料を、基材としての標準試験片の表面にスプレー塗装し、次いで、100℃で30分間強制乾燥し、下塗り塗膜が形成された標準試験片試料を得た。
銀鏡膜層形成用組成液として前記特許文献3に基づいて調製され、市販されているもの(GLANTZCOAT TypeRT シルバー)を用い、この銀鏡膜層形成液をとシンナー(GLANTZCOAT TypeRT シルバーシンナーT2)で2倍に希釈してスプレー塗装し、100℃で30分間乾燥して下塗り塗膜上に銀鏡膜層が形成された標準試験片を得た。なお、この銀鏡膜層形成用組成液も、有機溶媒中に銀ナノ粒子を主成分として含む分散液であり、他に高分子分散剤が含まれている。この銀鏡膜層形成液のスプレー塗装後には、単に乾燥するのみで銀鏡膜層が形成されるが、各実験例の全てにおいて、100℃で30分間乾燥することにより、銀鏡膜層の形成時に各銀鏡膜層の乾燥条件が一定となるようして、形成された銀鏡膜層に室温、湿度等による影響が現れないようにした。
上塗り塗料の主剤としてアルコキシル基を含有するシリコンオリゴマー(GLANZCOAT Type RT プライマートップ、(株)フェクト)が10質量部、溶媒としてのエタノールが7質量部、硬化剤(GLANZCOAT type RT トップ硬化剤G、(株)フェクト)が1質量部の割合となるように均一に撹拌・混合し、上塗り塗料を調製した。この上塗り塗料を、銀鏡膜層の表面にスプレー塗装し、次いで、100℃で30分間強制乾燥し、標準試験片の表面に下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された実験例1の銀鏡膜層形成試料を得た。なお、ここで用いられた上塗り塗料は透明塗膜である。
下塗り塗料及び上塗り塗料の溶媒として、エタノールに換えてイソプロピルアルコールを用いた他は実験例1の場合と同様にして、標準試験片の表面に下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された実験例2の銀鏡膜層形成試料を得た。
下塗り塗料及び上塗り塗料の溶媒として、エタノールに換えてブタノールを用いた他は実験例1の場合と同様にして、標準試験片の表面に下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された実験例3の銀鏡膜層形成試料を得た。
下塗り塗料及び上塗り塗料の溶媒として、エタノールに換えて酢酸エチルを用いた他は実験例1の場合と同様にして、標準試験片の表面に下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された実験例4の銀鏡膜層形成試料を得た。
下塗り塗料及び上塗り塗料の溶媒として、エタノールに換えて酢酸ブチルを用いた他は実験例1の場合と同様にして、標準試験片の表面に下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された実験例5の銀鏡膜層形成試料を得た。
下塗り塗料及び上塗り塗料の溶媒として、エタノールに換えてプロピレングリコールモノメチルエーテルアセテートを用いた他は実験例1の場合と同様にして、標準試験片の表面に下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された実験例6の銀鏡膜層形成試料を得た。
下塗り塗料及び上塗り塗料の溶媒として、エタノールに換えてメチルエチルケトンを用いた他は実験例1の場合と同様にして、標準試験片の表面に下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された実験例7の銀鏡膜層形成試料を得た。
下塗り塗料及び上塗り塗料の溶媒として、エタノールに換えてジイソブチルケトンを用いた他は実験例1の場合と同様にして、標準試験片の表面に下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された実験例8の銀鏡膜層形成試料を得た。
下塗り塗料及び上塗り塗料の溶媒として、エタノールに換えてメチルイソブチルケトンを用いた他は実験例1の場合と同様にして、標準試験片の表面に下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された実験例9の銀鏡膜層形成試料を得た。
下塗り塗料及び上塗り塗料の溶媒として、エタノールに換えてシクロヘキサノンを用いた他は実験例1の場合と同様にして、標準試験片の表面に下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された実験例10の銀鏡膜層形成試料を得た。
下塗り塗料及び上塗り塗料の溶媒として、エタノールに換えてエチレングリコールモノメチルエーテルを用いた他は実験例1の場合と同様にして、標準試験片の表面に下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された実験例11の銀鏡膜層形成試料を得た。
下塗り塗料及び上塗り塗料の溶媒として、エタノールに換えて3−メトキシ−1−ブタノールを用いた他は実験例1の場合と同様にして、標準試験片の表面に下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された実験例12の銀鏡膜層形成試料を得た。
下塗り塗料及び上塗り塗料の溶媒として、エタノールに換えてトルエンを用いた他は実験例1の場合と同様にして、標準試験片の表面に下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された実験例13の銀鏡膜層形成試料を得た。
下塗り塗料及び上塗り塗料の溶媒として、エタノールに換えてキシレンを用いた他は実験例1の場合と同様にして、標準試験片の表面に下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された実験例13の銀鏡膜層形成試料を得た。
下塗り塗料及び上塗り塗料の溶媒として、エタノールに換えてソルベントナフサ系溶媒(ソルベッソ200(商品名)、東燃ゼネラル石油(株))を用いた他は実験例1の場合と同様にして、標準試験片の表面に下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された実験例15の銀鏡膜層形成試料を得た。
下塗り塗料及び上塗り塗料の溶媒として、エタノールに換えてn−ヘキサンを用いた他は実験例1の場合と同様にして、標準試験片の表面に下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された実験例16の銀鏡膜層形成試料を得た。
下塗り塗料及び上塗り塗料の溶媒として、エタノールに換えてn−へプタンを用いた他は実験例1の場合と同様にして、標準試験片の表面に下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された実験例17の銀鏡膜層形成試料を得た。
下塗り塗料及び上塗り塗料の溶媒として、エタノールに換えてシクロヘキサンを用いた他は実験例1の場合と同様にして、標準試験片の表面に下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された実験例18の銀鏡膜層形成試料を得た。
下塗り塗料及び上塗り塗料の溶媒として、エタノールに換えてエチルシクロヘキサンを用いた他は実験例1の場合と同様にして、標準試験片の表面に下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された実験例19の銀鏡膜層形成試料を得た。
下塗り塗料及び上塗り塗料の溶媒として、エタノールに換えてミネラルスピリット(芳香族炭化水素≦10質量%)を用いた他は実験例1の場合と同様にして、標準試験片の表面に下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された実験例20の銀鏡膜層形成試料を得た。
下塗り塗料及び上塗り塗料の溶媒として、エタノールに換えてミネラルスピリット(芳香族炭化水素>10vol)を用いた他は実験例1の場合と同様にして、標準試験片の表面に下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された実験例21の銀鏡膜層形成試料を得た。
上述のようにして形成された実験例1〜21の各銀鏡膜層形成試料について、目視により変色の程度を測定した。結果は、変色の程度として、
(1)実質的に均一な銀鏡膜層が得られ、光輝性にムラが見られなかったものを「○」、
(2)部分的に光輝性に僅かなムラが見られたものを「△」、
(3)光輝性にはっきりと大きなムラが見られたものを「×」、
で表した。結果を纏めて表1に示した。
実験例22〜26としては、溶媒として市販のシンナー(トルエン35質量%、酢酸エチル65質量%)にミネラルスピリット(芳香族炭化水素の含有量が10質量%未満のもの)をそれぞれ10質量%(実験例22)、30質量%(実験例23)、50質量%(実験例24)、80質量%(実験例25)及び90質量%(実験例26)となるように添加して希釈したものを用いた場合の銀鏡膜層の光輝性に対する影響を調べた。すなわち、下塗り塗装及び上塗り塗装の溶媒として、前記のシンナーにミネラルスピリットを添加したものを使用した以外は実験例1の場合と同様にして、標準試験片の表面に下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された実験例22〜26の銀鏡膜層形成試料を作成し、目視により銀鏡膜層の光輝性の程度について確認した。結果を纏めて表2に示した。
実験例27〜34では、上塗り塗膜中に紫外線吸収剤及び光安定剤を添加して銀鏡膜層形成試料を作成し、キセノンアークランプを用いた耐候性促進試験を行った際の変色の程度を目視により測定することにより、紫外線吸収剤及び光安定剤の添加による耐変色性試験を行った。
表3に示した結果からすると、紫外線吸収剤としてベンゾトリアゾール系化合物、光安定剤としてヒンダードアミン系化合物を用いると良好な耐変色性が得られることが分かった。そこで、実験例35としては、紫外線吸収剤としてのベンゾトリアゾール系化合物の添加割合を0.5質量%から15.0質量%まで、光安定剤としてのヒンダードアミン系化合物を0.5質量%から5.0質量%まで、それぞれマトリクス状に変化させ、その他は実験例27〜34の場合と同様にして、標準試験片の表面に下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された複数の実験例35の銀鏡膜層形成試料を作成し、実験例27〜34の場合と同様にして耐候性促進試験を行った。結果は、表4に纏めて示した。
実験例36〜41では、上塗り塗膜及び下塗り塗膜中に防錆剤を添加して銀鏡膜層形成試料を作成し、上塗り塗膜形成後の銀鏡膜層の変色の程度を調査した。すなわち、防錆剤として市販のトリアゾール系化合物(実験例36)、トリアジン系化合物(実験例37)、ベンゾチアゾール系化合物(実験例38)、脂肪酸アミド系化合物(実験例39)、リン酸エステルのアミン塩(実験例40)及び亜リン酸エステル系化合物(実験例41)をそれぞれ上塗り塗料の全体積に対して5質量%となる割合で添加し、その他は実験例16の場合と同様にして、標準試験片の表面に下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された実験例36〜41の銀鏡膜層形成試料を得た。
表5に示した結果から、防錆剤としてはトリアゾール系のものが好ましいことがわかったので、実験例42〜46では市販のトリアゾール系防錆剤の含有割合を上塗り塗料及び下塗り塗料の全体積に対して、1質量%(実験例42)、2質量%(実験例43)、5質量%(実験例44)、10質量%(実験例45)及び20質量%(実験例46)と変化させて添加し、実験例36〜41の場合と同様にして変色の程度を作成した。結果を纏めて表6に示した。
実験例1〜46では、上塗り塗膜及び下塗り塗膜形成用塗料としてアルコキシル基を含有するシリコンオリゴマーを主剤としてものを用いた例を示したが、実験例47ではアクリルウレタン塗料(アクリディックA801P(商品名)、DIC(株))、実験例48では実験例1〜46で用いたものとは異なるアルコキシル基を含有するシリコンオリゴマー塗料(FOC100(商品名)、フェクト(株))、実験例49ではアクリルシリコン塗料(B1161(商品名)、DIC(株))、アクリルメラミン塗料(ARBT100(商品名)、久保孝ペイント(株))、実験例50ではエポキシ塗料(GRクリヤー(商品名)、カシュー(株))、実験例50ではメタクリル酸ラッカー(アクリディックA−166(商品名)、DIC(株))をそれぞれ用い、その他は実験例16の場合と同様にして、標準試験片の表面に下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された実験例47〜52の銀鏡膜層形成試料を複数個ずつ作成した。ただし、それぞれの塗料の硬化剤添加割合及び乾燥条件は、それぞれの塗料のカタログ値に基づいて、それぞれの塗料に応じて最適な値となるように調製してある。
実験例47〜52の測定結果から、上塗り塗膜及び下塗り塗膜の主剤としては極性基としてOH基を有しているものが密着性が良好となることがわかったので、実験例53〜55では、同一種類の主剤であるが、OH価が異なる複数の塗料を用いてそれぞれ上塗り塗膜及び下塗り塗膜の密着性について調査した。すなわち、上塗り塗膜及び下塗り塗膜の主剤として、実験例53ではOH価が「50」のアクリルウレタン塗料(アクリディックA801P(商品名)、DIC(株))、実験例54ではOH価が「25」のアクリルウレタン塗料(アクリディックA837(商品名)、DIC(株))及び実験例55ではOH価が「15」のアクリルウレタン塗料(アクリディック57−773(商品名)、DIC(株))をそれぞれ用い、その他は実験例16の場合と同様にして、標準試験片の表面に下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された実験例53〜55の銀鏡膜層形成試料を複数個ずつ作成し、実験例47〜52の場合と同様にして密着性の試験を行った。ただし、それぞれの塗料の硬化剤添加割合及び乾燥条件は、それぞれの塗料のカタログ値に基づいて、それぞれの塗料に応じて最適な値となるように調製してある。結果を纏めて表8に示した。
11…基体
12…下塗り塗膜
13…銀鏡膜層
14…上塗り塗膜
Claims (22)
- 基体表面に下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された表面装飾構造において、
前記銀鏡膜層は、ナノメーターサイズの銀粒子が積層された状態で膜を形成しており、
前記上塗り塗膜は、溶媒として、脂肪族炭化水素化合物、10質量%以下の芳香族化合物を含む脂肪族炭化水素化合物溶液及びジイソブチルケトンから選択された少なくとも1種を含むものを用いて形成されたものからなることを特徴とする表面装飾構造。 - 前記脂肪族炭化水素化合物は、n−ヘキサン、n−へプタン、シクロヘキサン、エチルシクロヘキサンから選択された少なくとも1種であることを特徴とする、請求項1に記載の表面装飾構造。
- 前記下塗り塗膜は、前記上塗り塗膜と同種のものであることを特徴とする、請求項1に記載の表面装飾構造。
- 前記上塗り塗膜及び前記下塗り塗膜の少なくとも一方は、下記(1)〜(3)のいずれかの組み合わせの紫外線吸収剤及び光安定剤を含むことを特徴とする、請求項1に記載の表面装飾構造。
(1)ベンゾトリアゾール系化合物とベンゾエート系化合物。
(2)ベンゾトリアゾール系化合物とヒンダードアミン系化合物。
(3)トリアジン系化合物とヒンダードアミン系化合物。 - 前記上塗り塗膜、前記下塗り塗膜及び前記銀鏡膜層の少なくとも一方は、防錆剤として、トリアゾール系化合物、トリアジン系化合物、ベンゾチアゾール系化合物、脂肪酸アミド系化合物、リン酸エステルのアミン塩及び亜リン酸エステル系化合物から選択される少なくとも1種を含むことを特徴とする、請求項1〜4のいずれかに記載の表面装飾構造。
- 基体表面に下塗り塗膜、銀鏡膜層及び上塗り塗膜が形成された表面装飾構造において、
前記銀鏡膜層は、ナノメーターサイズの銀粒子が積層された状態で膜を形成しており、
前記上塗り塗膜は、極性基を有する樹脂塗膜からなることを特徴とする、表面装飾構造。 - 上記極性基は、OH基又はNH2基であることを特徴とする、請求項6に記載の表面装飾構造。
- 前記上塗り塗膜は、アクリルウレタン樹脂塗膜、ポリウレタン樹脂塗膜、シリコン樹脂塗膜、アクリルシリコン樹脂塗膜又はアクリルメラミン樹脂塗膜からなることを特徴とする、請求項6に記載の表面装飾構造。
- 前記下塗り塗膜は、前記上塗り塗膜と同種のものであることを特徴とする、請求項6に記載の表面装飾構造。
- 前記上塗り塗膜及び前記下塗り塗膜の少なくとも一方は、下記(1)〜(3)のいずれかの組み合わせの紫外線吸収剤及び光安定剤を含むことを特徴とする、請求項6に記載の表面装飾構造。
(1)ベンゾトリアゾール系化合物とベンゾエート系化合物。
(2)ベンゾトリアゾール系化合物とヒンダードアミン系化合物。
(3)トリアジン系化合物とヒンダードアミン系化合物。 - 前記上塗り塗膜、前記下塗り塗膜及び前記銀鏡膜層の少なくとも一方は、防錆剤として、トリアゾール系化合物、トリアジン系化合物、ベンゾチアゾール系化合物、脂肪酸アミド系化合物、リン酸エステルのアミン塩及び亜リン酸エステル系化合物から選択される少なくとも1種を含むことを特徴とする、請求項6〜10のいずれかに記載の表面装飾構造。
- 基体表面に、下塗り塗膜、銀鏡膜層及び上塗り塗膜を順次形成することからなる表面装飾構造の形成方法において、
前記基体の表面に下塗り塗料をスプレー塗装し、乾燥することにより前記下塗り塗膜を形成し、
前記銀鏡膜層を、高分子分散剤が溶解された有機溶媒中にナノメーターサイズの銀粒子が分散されている銀鏡膜層形成用組成液を前記下塗り塗膜が形成された基体上にスプレー塗装し、次いで常温又は加熱下で乾燥することにより形成し、
前記銀鏡膜層の表面に、溶媒として、脂肪族炭化水素化合物、10質量%以下の芳香族化合物を含む脂肪族炭化水素化合物溶液及びジイソブチルケトンから選択された少なくとも1種を含む上塗り塗料をスプレー塗装し、乾燥することにより前記上塗り塗膜を形成することを特徴とする、表面装飾構造の形成方法。 - 前記溶媒の脂肪族炭化水素化合物として、n−ヘキサン、n−へプタン、シクロヘキサン、エチルシクロヘキサンから選択された少なくとも1種を用いることを特徴とする、請求項12に記載の表面装飾構造の形成方法。
- 前記下塗り塗料として前記上塗り塗料と同種のものを用いることを特徴とする、請求項12に記載の表面装飾構造の形成方法。
- 前記上塗り塗料及び前記下塗り塗量の少なくとも一方に、下記(1)〜(3)のいずれかの組み合わせの紫外線吸収剤及び光安定剤を含むものを用いることを特徴とする、請求項12に記載の表面装飾構造の形成方法。
(1)ベンゾトリアゾール系化合物とベンゾエート系化合物。
(2)ベンゾトリアゾール系化合物とヒンダードアミン系化合物。
(3)トリアジン系化合物とヒンダードアミン系化合物。 - 前記上塗り塗料、前記下塗り塗料及び前記銀鏡膜層形成用組成液の少なくとも一方に、防錆剤として、トリアゾール系化合物、トリアジン系化合物、ベンゾチアゾール系化合物、脂肪酸アミド系化合物、リン酸エステルのアミン塩及び亜リン酸エステル系化合物から選択される少なくとも1種を含むものを用いることを特徴とする、請求項12〜15のいずれかに記載の表面装飾構造の形成方法。
- 基体表面に、下塗り塗膜、銀鏡膜層及び上塗り塗膜を順次形成することからなる表面装飾構造の形成方法において、
前記基体の表面に下塗り塗料をスプレー塗装し、乾燥することにより前記下塗り塗膜を形成し、
前記銀鏡膜層を、高分子分散剤が溶解された有機溶媒中にナノメーターサイズの銀粒子が分散されている銀鏡膜層形成用組成液を前記下塗り塗膜が形成された基体上にスプレー塗装し、次いで常温又は加熱下で乾燥することにより形成し、
前記銀鏡膜層の表面に、上塗り塗料として極性基を有する樹脂を含む塗料をスプレー塗装し、乾燥することにより前記上塗り塗膜を形成することを特徴とする、表面装飾構造の形成方法。 - 上記極性基がOH基又はNH2基からなるものを用いることを特徴とする、請求項17に記載の表面装飾構造の形成方法。
- 前記上塗り塗料として、アクリルウレタン樹脂塗料、ポリウレタン樹脂塗料、シリコン樹脂塗料、アクリルシリコン樹脂塗料又はアクリルメラミン樹脂塗料を用いることを特徴とする、請求項17に記載の表面装飾構造の形成方法。
- 前記下塗り塗料として前記上塗り塗料と同種のものを用いることを特徴とする、請求項17に記載の表面装飾構造の形成方法。
- 前記上塗り塗料及び前記下塗り塗量の少なくとも一方として、下記(1)〜(3)のいずれかの組み合わせの紫外線吸収剤及び光安定剤を含むものを用いることを特徴とする、請求項17に記載の表面装飾構造の形成方法。
(1)ベンゾトリアゾール系化合物とベンゾエート系化合物。
(2)ベンゾトリアゾール系化合物とヒンダードアミン系化合物。
(3)トリアジン系化合物とヒンダードアミン系化合物。 - 前記上塗り塗料、前記下塗り塗料及び前記銀鏡膜層形成用組成液の少なくとも一方に、防錆剤として、トリアゾール系化合物、トリアジン系化合物、ベンゾチアゾール系化合物、脂肪酸アミド系化合物、リン酸エステルのアミン塩及び亜リン酸エステル系化合物から選択される少なくとも1種を含むものを用いることを特徴とする、請求項17〜21のいずれかに記載の表面装飾構造の形成方法。