JP2017519052A - ポリウレタン、その製造方法及び用途 - Google Patents
ポリウレタン、その製造方法及び用途 Download PDFInfo
- Publication number
- JP2017519052A JP2017519052A JP2016535103A JP2016535103A JP2017519052A JP 2017519052 A JP2017519052 A JP 2017519052A JP 2016535103 A JP2016535103 A JP 2016535103A JP 2016535103 A JP2016535103 A JP 2016535103A JP 2017519052 A JP2017519052 A JP 2017519052A
- Authority
- JP
- Japan
- Prior art keywords
- polyurethane
- diisocyanate
- polyol
- alcohol
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
100gの乾燥ポリ(テトラメチレンエーテルグリコール)(PTMEG、分子量:1000)と50.05gの4,4’−メチレンジフェニルジイソシアネート(MDI)を4口反応器で混合した。窒素雰囲気で60℃の温度を保持して反応し、5.6%のNCOを有するポリウレタンプレポリマーを得た。得られたポリウレタンプレポリマーに鎖延長剤としてイソソルビド(Isosorbide)14.6gを添加した後、コーティング処理されたモールド内に投入し、110℃で12時間硬化させた。
鎖延長剤として、イソソルビドとブタンジオール(BD)を下記表1に示した含量で共に使用したことを除いては、実施例A1と同様にして、ポリウレタン試片を製造した。これに対して、実施例A1と同様にして、モジュラス及び引張強度を測定し、その結果を表1に示した。
鎖延長剤として、ブタンジオール(BD)を下記表1に示した含量で使用したことを除いては、実施例A1と同様にして、ポリウレタン試片を製造した。これに対して、実施例A1と同様にして、モジュラス及び引張強度を測定し、その結果を表1に示した。
実施例A2と同種類及び同量の反応物を用い、ポリ(テトラメチレンエーテルグリコール)(PTMEG)、イソソルビド及びブタンジオール(BD)を4口反応器で混合し、室温で固体である4,4’−メチレンジフェニルジイソシアネート(MDI)を別途容器で70℃まで昇温した後、これを前記4口反応器に加えて混合した後、コーティング処理されたモールド内に投入し、110℃で12時間硬化させて、ポリウレタン試片を製造した。これに対して、実施例A1と同様にして、モジュラス及び引張強度を測定し、その結果を表1に示した。
100gの乾燥されたポリ(テトラメチレンエーテルグリコール)(PTMEG、分子量:1000)と50.05gの4,4’−ジフェニルメタンジイソシアネート(MDI)を4口反応器で混合した。窒素雰囲気で、60℃の温度を保持しながら反応して、5.6%のNCOを有するポリウレタンプレポリマーを得た。得られたポリウレタンプレポリマーにイソソルビド14.6gを添加した後、コーティング処理されたモールド内に投入し、110℃で12時間硬化させた。
ポリイソシアネートとして、MDIの代りにイソホロンジイソシアネート(IPDI)を44.46g使用したことを除いては、実施例B1と同様にして、硬化された試片を製造した。これに対して、実施例B1と同様にして、温度条件で加熱して、FT−IRによる分析を行い、その結果を表2に示した。
ポリイソシアネートとして、MDIの代りにナフタレンジイソシアネート(NDI)を42.04g使用したことを除いては、実施例B1と同様にして、硬化された試片を製造した。これに対して、実施例B1と同様にして、温度条件で加熱し、FT−IRによる分析を行い、その結果を表2に示した。
イソソルビド14.6gの代りに、イソソルビド8.6g及びブタンジオール(BD)3.7gの混合物を使用したことを除いては、実施例B1と同様にして、硬化された試片を製造した。これに対して、実施例B1と同様にして、温度条件で加熱して、FT−IRによる分析を行い、その結果を表2に示した。
イソソルビド14.6gの代りに、イソソルビド5.3g及びブタンジオール(BD)5.3gの混合物を使用したことを除いては、実施例B1と同様にして、硬化された試片を製造した。これに対して、実施例B1と同様にして、温度条件で加熱して、FT−IRによる分析を行い、その結果を表2に示した。
イソソルビド14.6gの代りに、イソソルビド2.0g及びブタンジオール(BD)7.8gの混合物を使用したことを除いては、実施例B1と同様にして、硬化された試片を製造した。これに対して、実施例B1と同様にして、温度条件で加熱して、FT−IRによる分析を行い、その結果を表2に示した。
前記実施例B1で、イソソルビドの代りに、ブタンジオール(BD)を9.0g使用したことを除いては、実施例B1と同様にして、BDの通常硬化温度リン120℃で硬化して試片を製造した。しかし、この比較例で製造されたポリウレタン試料は、100〜200℃の範囲では可逆反応が起こらず、試料の流動性がほとんどなく、イソシアネートの活性を確認することができなく、結果的に可逆反応による自然治癒特性がなかった。
Claims (31)
- ポリウレタンプレポリマー;及び
アンヒドロ糖アルコールによる鎖延長部分;
を含有してなるポリウレタン。 - ポリウレタンプレポリマーが、ポリオールとイソシアネートとの反応生成物である請求項1に記載のポリウレタン。
- ポリオールが、ポリエーテル、ポリアルキレン、ポリエステル、ポリウレタン、ポリカーボネート、又はこれらの組み合わせに基づくポリオールである請求項2に記載のポリウレタン。
- ポリオールが、エーテルポリオール、ポリカーボネートポリオール、アクリル系ポリオール、ポリエステルポリオール、又はこれらの組み合わせである請求項2に記載のポリウレタン。
- イソシアネートが、2,4−若しくは4,4’−メチレンジフェニルジイソシアネート(MDI)、キシリレンジイソシアネート(XDI)、m−若しくはp−テトラメチルキシリレンジイソシアネート(TMXDI)、トルイレンジイソシアネート(TDI)、ジ−若しくはテトラ−アルキルジフェニルメタンジイソシアネート、3,3’−ジメチルジフェニル−4,4’−ジイソシアネート(TODI)、1,3−フェニレンジイソシアネート、1,4−フェニレンジイソシアネート、ナフタレンジイソシアネート(NDI)、4,4’−ジベンジルジイソシアネート、水素化MDI(H12MDI)、1−メチル−2,4−ジイソシアナトシクロヘキサン、1,12−ジイソシアナトドデカン、1,6−ジイソシアナト−2,2,4−トリメチルヘキサン、1,6−ジイソシアナト−2,4,4−トリメチルヘキサン、イソホロンジイソシアネート(IPDI)、テトラメトキシブタン−1,4−ジイソシアネート、ブタン−1,4−ジイソシアネート、ヘキサン−1,6−ジイソシアネート(HDI)、二量体脂肪酸ジイソシアネート、ジシクロヘキシルメタンジイソシアネート、シクロヘキサン−1,4−ジイソシアネート、エチレンジイソシアネート、又はこれらの組み合わせである請求項2に記載のポリウレタン。
- イソシアネートが、4,4’−メチレンジフェニルジイソシアネート、トルエンジイソシアネート、イソホロンジイソシアネート、ナフタレンジイソシアネート、又はこれらの組み合わせである請求項2に記載のポリウレタン。
- アンヒドロ糖アルコールが、イソソルビド、イソマンニド、イソイジド、これらの誘導体、又はそれらの組み合わせである請求項1に記載のポリウレタン。
- ポリウレタンプレポリマーが、ポリ(テトラメチレンエーテルグリコール)と4,4’−メチレンジフェニルジイソシアネートから製造されたものであり、アンヒドロ糖アルコールが、イソソルビドである請求項1に記載のポリウレタン。
- さらに、脂肪族グリコール又は多価アルコールによる鎖延長部分を含有してなる請求項1に記載のポリウレタン。
- 脂肪族グリコール又は多価アルコールが、炭素数2〜10の脂肪族グリコール又は多価アルコールである請求項9に記載のポリウレタン。
- 脂肪族グリコール又は多価アルコールが、エチレングリコール、プロパンジオール、1,4−ブタンジオール、1,5−ペンタンジオール、1,6−ヘキサンジオール、1,7−ヘプタンジオール、1,8−オクタンジオール、1,10−デカンジオール、二量体脂肪アルコール、グリセロール、ヘキサントリオール、トリメチロールプロパン、ペンタエリトリトール、又はネオペンチルアルコールである請求項9に記載のポリウレタン。
- ポリウレタンプレポリマーとアンヒドロ糖アルコールとを含有してなる混合物を硬化して得られる請求項1に記載のポリウレタン。
- ポリウレタンプレポリマーとアンヒドロ糖アルコールとを含有してなる混合物の硬化反応が、90〜200℃の温度で行われる請求項12に記載のポリウレタン。
- (1)ポリウレタンプレポリマーを製造する工程;
(2)前記ポリウレタンプレポリマーに、アンヒドロ糖アルコールを含有してなる鎖延長剤成分を添加する工程;及び
(3)前記工程(2)で得られた混合物を硬化させる工程;
を含有してなるポリウレタンの製造方法。 - 工程(1)のポリウレタンプレポリマーの製造が、ポリオールとイソシアネートとを反応させることによって行われる請求項14に記載のポリウレタンの製造方法。
- 工程(2)で用いられる鎖延長剤成分の全量を100重量%としたときに、アンヒドロ糖アルコールの含有量が20%以上である請求項14に記載のポリウレタンの製造方法。
- 工程(3)の硬化反応が、90〜200℃の温度で行われる請求項14に記載のポリウレタンの製造方法。
- ポリオール化合物を含む第1成分;及び
イソシアネート化合物を含む第2成分;
を含有し、
前記第1成分及び第2成分のうちの一つ以上が、アンヒドロ糖アルコールを含む2液型組成物。 - レベリング剤、湿潤剤、触媒、老化防止剤、色材、乾燥剤、樹脂、及びワックスからなる群から選択される一つ以上の補助剤を、さらに含む請求項18に記載の2液型組成物。
- 硬化促進剤を、さらに含む請求項18に記載の2液型組成物。
- 色材が、有色顔料又は染料である請求項19に記載の2液型組成物。
- 請求項1〜13のいずれか1項に記載のポリウレタンを100〜200℃の温度に加熱して、用いることを含有してなるポリウレタンの使用方法。
- ポリウレタンプレポリマーが、ポリ(テトラメチレンエーテルグリコール)と4,4’−ジフェニルメタンジイソシアネートとの反応生成物であり、アンヒドロ糖アルコールが、イソソルビドであり、ポリウレタンの加熱温度が、150〜200℃である請求項22に記載のポリウレタンの使用方法。
- ポリウレタンプレポリマーが、ポリ(テトラメチレンエーテルグリコール)とイソホロンジイソシアネートとの反応生成物であり、アンヒドロ糖アルコールが、イソソルビドであり、ポリウレタンの加熱温度が、140〜200℃である請求項22に記載のポリウレタンの使用方法。
- ポリウレタンプレポリマーが、ポリ(テトラメチレンエーテルグリコール)とナフタレンジイソシアネートとの反応生成物であり、アンヒドロ糖アルコールが、イソソルビドであり、ポリウレタンの加熱温度が、180〜200℃である請求項22に記載のポリウレタンの使用方法。
- 100〜200℃の温度で使用可能な、請求項1〜13のいずれか1項に記載のポリウレタンを含有してなるポリウレタン組成物。
- 樹脂組成物、粉体塗料、又はホットメルト接着剤である請求項26に記載のポリウレタン組成物。
- 酸化防止剤、紫外線安定剤、炭素ナノチューブ、金ナノ微粒子、及びこれらの組み合わせからなる群から選択される一つ以上の安定剤を、さらに含む請求項26に記載のポリウレタン組成物。
- レベリング剤、湿潤剤、触媒、老化防止剤、色材、乾燥剤、樹脂、及びワックスからなる群から選択される一つ以上の補助剤を、さらに含む請求項26に記載のポリウレタン組成物。
- 硬化促進剤を、さらに含む請求項26に記載のポリウレタン組成物。
- 色材が、有色顔料又は染料である請求項29に記載のポリウレタン組成物。