JP2015042607A - 強化ガラス及び強化用ガラス - Google Patents
強化ガラス及び強化用ガラス Download PDFInfo
- Publication number
- JP2015042607A JP2015042607A JP2014133838A JP2014133838A JP2015042607A JP 2015042607 A JP2015042607 A JP 2015042607A JP 2014133838 A JP2014133838 A JP 2014133838A JP 2014133838 A JP2014133838 A JP 2014133838A JP 2015042607 A JP2015042607 A JP 2015042607A
- Authority
- JP
- Japan
- Prior art keywords
- glass
- tempered glass
- less
- compressive stress
- mpa
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
(1)ガラス組成として、モル%で、SiO2 50〜80%、Al2O3 10〜30%、B2O3 0〜6%、Na2O 5〜25%、MgO 0〜10%を含有し、実質的にAs2O3、Sb2O3、PbO及びFを含有しない。
(2)ガラス組成として、モル%で、SiO2 50〜80%、Al2O3 10〜30%、B2O3 0〜6%、Na2O 5〜25%、MgO 0〜10%、CaO 0〜5%を含有し、実質的にAs2O3、Sb2O3、PbO及びFを含有しない。
(3)ガラス組成として、モル%で、SiO2 50〜80%、Al2O3 10〜30%、B2O3 0〜6%、Na2O 5〜25%、K2O 0〜10%、MgO 0〜10%、CaO 0〜5%を含有し、実質的にAs2O3、Sb2O3、PbO及びFを含有しない。
(4)ガラス組成として、モル%で、SiO2 50〜80%、Al2O3 12〜18%、B2O3 0〜3%、Na2O 12〜18%、K2O 0〜2%、MgO 0.1〜4%、CaO 0〜2%を含有し、実質的にAs2O3、Sb2O3、PbO及びFを含有しない。
(5)ガラス組成として、モル%で、SiO2 50〜80%、Al2O3 12〜18%、B2O3 0〜3%、Na2O 12〜18%、K2O 0〜8%、MgO 0.1〜4%、CaO 0〜2%を含有し、モル比Na2O/Al2O3が0.6〜1.6であり、実質的にAs2O3、Sb2O3、PbO及びFを含有しない。
(1)ガラス組成として、モル%で、SiO2 50〜80%、Al2O3 12〜19%、B2O3 0〜3%、Na2O 12〜19%、K2O 0〜8%、MgO 0.1〜3%、CaO 0〜2%を含有し、モル比Na2O/Al2O3が0.6〜1.6であり、実質的にAs2O3、Sb2O3、PbO及びFを含有せず、圧縮応力層の圧縮応力値が900MPa以上1500MPa以下、圧縮応力層の厚みが10μm以上60μm以下、歪点が620℃以上、液相温度が1250℃以下、液相粘度が104.5dPa・s以上、104.5dPa・sの粘度でアルミナ耐火物に48時間接触させたとき、接触界面に生じる失透結晶が1個/mm2以下、厚みが0.3〜2.0mm、且つ平板形状である。
(1)ガラス組成として、モル%で、SiO2 50〜80%、Al2O3 10〜30%、B2O3 0〜6%、Na2O 5〜25%、MgO 0〜10%を含有し、実質的にAs2O3、Sb2O3、PbO及びFを含有せず、クラック発生率が80%以下である。
(2)厚みが0.3〜2.0mm、圧縮応力層の圧縮応力値が900MPa以上1500MPa以下、圧縮応力層の厚みが10μm以上60μm以下、歪点が620℃以上、且つクラック発生率が80%以下である。
(3)厚みが0.7〜2.0mm、圧縮応力層の圧縮応力値が1000MPa以上、圧縮応力層の厚みが40μm以上、歪点が620℃以上、クラック発生率が80%以下、△CSが100MPa以下である。
Claims (22)
- 表面に圧縮応力層を有する強化ガラスであって、ガラス組成として、モル%で、SiO2 50〜80%、Al2O3 10〜30%、B2O3 0〜6%、Na2O 5〜25%、MgO 0〜10%を含有し、実質的にAs2O3、Sb2O3、PbO及びFを含有しないことを特徴とする強化ガラス。
- ガラス組成として、モル%で、SiO2 50〜80%、Al2O3 12〜18%、B2O3 0〜3%、Na2O 12〜18%、K2O 0〜2%、MgO 0.1〜4%、CaO 0〜2%を含有し、モル比Na2O/Al2O3が0.6〜1.6であることを特徴とする強化ガラス。
- 強化処理前のクラック発生率が80%以下であることを特徴とする請求項1又は2に記載の強化ガラス。
- 圧縮応力層の圧縮応力値が900MPa以上1500MPa以下、且つ圧縮応力層の厚みが10μm以上60μm以下であることを特徴とする請求項1〜3の何れか一項に記載の強化ガラス。
- 歪点が590℃以上であることを特徴とする請求項1〜4の何れか一項に記載の強化ガラス。
- 液相温度が1250℃以下であることを特徴とする請求項1〜5の何れか一項に記載の強化ガラス。
- 液相粘度が104.5dPa・s以上であることを特徴とする請求項1〜6の何れか一項に記載の強化ガラス。
- 104.0dPa・sにおける温度が1400℃以下であることを特徴とする請求項1〜7の何れか一項に記載の強化ガラス。
- 104.5dPa・sの粘度でアルミナ耐火物に48時間接触させたとき、接触界面に生じる失透結晶が1個/mm2以下であることを特徴とする請求項1〜8の何れか一項に記載の強化ガラス。
- 平板形状であることを特徴とする請求項1〜9の何れか一項に記載の強化ガラス。
- 厚みが0.3〜2.0mmであることを特徴とする請求項1〜10の何れか一項に記載の強化ガラス。
- オーバーフローダウンドロー法で成形されてなることを特徴とする請求項1〜11の何れか一項に記載の強化ガラス。
- タッチパネルディスプレイに用いることを特徴とする請求項1〜12の何れか一項に記載の強化ガラス。
- 携帯電話のカバーガラスに用いることを特徴とする請求項1〜12の何れか一項に記載の強化ガラス。
- 太陽電池のカバーガラスに用いることを特徴とする請求項1〜12の何れか一項に記載の強化ガラス。
- ディスプレイの保護部材に用いることを特徴とする請求項1〜12の何れか一項に記載の強化ガラス。
- ガラス組成として、モル%で、SiO2 50〜80%、Al2O3 12〜18%、B2O3 0〜3%、Na2O 12〜18%、K2O 0〜2%、MgO 0.1〜4%、CaO 0〜2%を含有し、モル比Na2O/Al2O3が0.6〜1.6であり、実質的にAs2O3、Sb2O3、PbO及びFを含有せず、圧縮応力層の圧縮応力値が900MPa以上1500MPa以下、圧縮応力層の厚みが10μm以上60μm以下、歪点が590℃以上、液相温度が1250℃以下、液相粘度が104.5dPa・s以上、強化処理前のクラック発生率が80%以下、104.5dPa・sの粘度でアルミナ耐火物に48時間接触させたとき、接触界面に生じる失透結晶が1個/mm2以下、厚みが0.3〜2.0mm、且つ平板形状であることを特徴とする強化ガラス。
- ガラス組成として、モル%で、SiO2 50〜80%、Al2O3 10〜30%、B2O3 0〜6%、Na2O 5〜25%、MgO 0〜10%を含有し、実質的にAs2O3、Sb2O3、PbO及びFを含有しないことを特徴とする強化用ガラス。
- クラック発生率が80%以下であることを特徴とする請求項18に記載の強化用ガラス。
- 厚みが0.3〜2.0mm、圧縮応力層の圧縮応力値が900MPa以上1500MPa以下、圧縮応力層の厚みが10μm以上60μm以下、歪点が590℃以上、且つクラック発生率が80%以下であることを特徴とする強化用ガラス。
- 厚みが0.7〜2.0mm、圧縮応力層の圧縮応力値が1000MPa以上、圧縮応力層の厚みが40μm以上、歪点が620℃以上、且つクラック発生率が80%以下であることを特徴とする強化用ガラス。
- △CSが100MPa以下であることを特徴とする請求項18〜21の何れか一項に記載の強化用ガラス。