JP2012506480A5 - - Google Patents
Download PDFInfo
- Publication number
- JP2012506480A5 JP2012506480A5 JP2011533261A JP2011533261A JP2012506480A5 JP 2012506480 A5 JP2012506480 A5 JP 2012506480A5 JP 2011533261 A JP2011533261 A JP 2011533261A JP 2011533261 A JP2011533261 A JP 2011533261A JP 2012506480 A5 JP2012506480 A5 JP 2012506480A5
- Authority
- JP
- Japan
- Prior art keywords
- prepreg
- molded
- volatile components
- enclosure
- condensable gas
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Links
- 239000007789 gas Substances 0.000 claims 10
- 239000000853 adhesive Substances 0.000 claims 5
- 230000001070 adhesive Effects 0.000 claims 5
- 239000011159 matrix material Substances 0.000 claims 5
- 229920005989 resin Polymers 0.000 claims 5
- 239000011347 resin Substances 0.000 claims 5
- 229920000311 Fiber-reinforced composite Polymers 0.000 claims 4
- 239000003733 fiber-reinforced composite Substances 0.000 claims 4
- 239000002131 composite material Substances 0.000 claims 3
- 238000010438 heat treatment Methods 0.000 claims 3
- XKRFYHLGVUSROY-UHFFFAOYSA-N argon Chemical compound [Ar] XKRFYHLGVUSROY-UHFFFAOYSA-N 0.000 claims 2
- 230000015572 biosynthetic process Effects 0.000 claims 2
- XLJMAIOERFSOGZ-UHFFFAOYSA-M cyanate Chemical compound [O-]C#N XLJMAIOERFSOGZ-UHFFFAOYSA-M 0.000 claims 2
- 238000005755 formation reaction Methods 0.000 claims 2
- 239000000203 mixture Substances 0.000 claims 2
- 238000000465 moulding Methods 0.000 claims 2
- IJGRMHOSHXDMSA-UHFFFAOYSA-N nitrogen Chemical compound N#N IJGRMHOSHXDMSA-UHFFFAOYSA-N 0.000 claims 2
- 239000002904 solvent Substances 0.000 claims 2
- 125000003903 2-propenyl group Chemical group [H]C([*])([H])C([H])=C([H])[H] 0.000 claims 1
- CMLFRMDBDNHMRA-UHFFFAOYSA-N 2H-1,2-benzoxazine Chemical compound C1=CC=C2C=CNOC2=C1 CMLFRMDBDNHMRA-UHFFFAOYSA-N 0.000 claims 1
- IOJUPLGTWVMSFF-UHFFFAOYSA-N Benzothiazole Chemical compound C1=CC=C2SC=NC2=C1 IOJUPLGTWVMSFF-UHFFFAOYSA-N 0.000 claims 1
- 239000004593 Epoxy Substances 0.000 claims 1
- 239000005977 Ethylene Substances 0.000 claims 1
- 239000004952 Polyamide Substances 0.000 claims 1
- 239000004962 Polyamide-imide Substances 0.000 claims 1
- 239000004693 Polybenzimidazole Substances 0.000 claims 1
- 229920002480 Polybenzimidazole fiber Polymers 0.000 claims 1
- 239000004695 Polyether sulfone Substances 0.000 claims 1
- 229920001721 Polyimide Polymers 0.000 claims 1
- 239000004642 Polyimide Substances 0.000 claims 1
- 239000004721 Polyphenylene oxide Substances 0.000 claims 1
- 102000014961 Protein Precursors Human genes 0.000 claims 1
- 108010078762 Protein Precursors Proteins 0.000 claims 1
- 239000003570 air Substances 0.000 claims 1
- 150000001336 alkenes Chemical class 0.000 claims 1
- 229910052786 argon Inorganic materials 0.000 claims 1
- 230000001174 ascending Effects 0.000 claims 1
- 238000009835 boiling Methods 0.000 claims 1
- 239000003795 chemical substances by application Substances 0.000 claims 1
- 125000003700 epoxy group Chemical group 0.000 claims 1
- 150000002148 esters Chemical class 0.000 claims 1
- OTMSDBZUPAUEDD-UHFFFAOYSA-N ethane Chemical compound CC OTMSDBZUPAUEDD-UHFFFAOYSA-N 0.000 claims 1
- VGGSQFUCUMXWEO-UHFFFAOYSA-N ethene Chemical compound C=C VGGSQFUCUMXWEO-UHFFFAOYSA-N 0.000 claims 1
- 125000002534 ethynyl group Chemical group [H]C#C* 0.000 claims 1
- 239000000835 fiber Substances 0.000 claims 1
- 239000001307 helium Substances 0.000 claims 1
- 229910052734 helium Inorganic materials 0.000 claims 1
- SWQJXJOGLNCZEY-UHFFFAOYSA-N helium(0) Chemical compound [He] SWQJXJOGLNCZEY-UHFFFAOYSA-N 0.000 claims 1
- UFHFLCQGNIYNRP-UHFFFAOYSA-N hydrogen Chemical compound [H][H] UFHFLCQGNIYNRP-UHFFFAOYSA-N 0.000 claims 1
- 239000001257 hydrogen Substances 0.000 claims 1
- 229910052739 hydrogen Inorganic materials 0.000 claims 1
- 150000003949 imides Chemical class 0.000 claims 1
- 150000002576 ketones Chemical class 0.000 claims 1
- PEEHTFAAVSWFBL-UHFFFAOYSA-N maleimide Chemical compound O=C1NC(=O)C=C1 PEEHTFAAVSWFBL-UHFFFAOYSA-N 0.000 claims 1
- VNWKTOKETHGBQD-UHFFFAOYSA-N methane Chemical compound C VNWKTOKETHGBQD-UHFFFAOYSA-N 0.000 claims 1
- 238000000034 method Methods 0.000 claims 1
- 229910052754 neon Inorganic materials 0.000 claims 1
- GKAOGPIIYCISHV-UHFFFAOYSA-N neon(0) Chemical compound [Ne] GKAOGPIIYCISHV-UHFFFAOYSA-N 0.000 claims 1
- 229910052757 nitrogen Inorganic materials 0.000 claims 1
- 239000001301 oxygen Substances 0.000 claims 1
- MYMOFIZGZYHOMD-UHFFFAOYSA-N oxygen Chemical compound O=O MYMOFIZGZYHOMD-UHFFFAOYSA-N 0.000 claims 1
- 229910052760 oxygen Inorganic materials 0.000 claims 1
- ISWSIDIOOBJBQZ-UHFFFAOYSA-N phenol Chemical compound OC1=CC=CC=C1 ISWSIDIOOBJBQZ-UHFFFAOYSA-N 0.000 claims 1
- 150000002989 phenols Chemical class 0.000 claims 1
- 229920002496 poly(ether sulfone) Polymers 0.000 claims 1
- 229920002647 polyamide Polymers 0.000 claims 1
- 239000011528 polyamide (building material) Substances 0.000 claims 1
- 229920002312 polyamide-imide Polymers 0.000 claims 1
- 229920002577 polybenzoxazole Polymers 0.000 claims 1
- 229920000515 polycarbonate Polymers 0.000 claims 1
- 239000004417 polycarbonate Substances 0.000 claims 1
- 229920000647 polyepoxide Polymers 0.000 claims 1
- 229920000728 polyester Polymers 0.000 claims 1
- 229920000570 polyether Polymers 0.000 claims 1
- -1 polyethylene terephthalate Polymers 0.000 claims 1
- 229920000139 polyethylene terephthalate Polymers 0.000 claims 1
- 239000005020 polyethylene terephthalate Substances 0.000 claims 1
- 229920003288 polysulfone Polymers 0.000 claims 1
- OZAIFHULBGXAKX-UHFFFAOYSA-N precursor Substances N#CC(C)(C)N=NC(C)(C)C#N OZAIFHULBGXAKX-UHFFFAOYSA-N 0.000 claims 1
- ATUOYWHBWRKTHZ-UHFFFAOYSA-N propane Chemical compound CCC ATUOYWHBWRKTHZ-UHFFFAOYSA-N 0.000 claims 1
- 239000001294 propane Substances 0.000 claims 1
Claims (12)
- シートを形成しマトリックス樹脂を含浸させた繊維を含み、一種または複数の揮発成分を中に含む、少なくとも一つの硬化性プレプレグであって、第一の幾何学構造を有するプレプレグを用意し、
成形装置により、少なくとも一つの硬化性プレプレグを第一の幾何学構造から第ニの幾何学構造に変形して少なくとも一つの成形プレプレグを形成し、
少なくとも一つの成形プレプレグを囲いで取り囲み、ここで、少なくとも一つの成形プレプレグは成形装置によって変形させたものであり、
囲い内の少なくとも一つの成形プレプレグに隣接して囲い内に非凝縮ガスの流れを導入し、
少なくとも一つの成形プレプレグを加熱して、少なくとも一つの成形プレプレグから一種または複数の揮発成分を発生させ、
囲いから非凝縮ガスの少なくとも一部を除去し、その結果少なくとも一つの成形プレプレグから一種または複数の揮発成分が非凝縮ガスによって運び去られ、揮発成分が減少させられた成形プレプレグが形成され、
得られた揮発成分が減少させられた成形プレプレグを硬化させ、固めて、成形複合物部分を形成する
工程を含んでなる、揮発成分が減少させられた成形プレプレグを形成する方法。 - 成形プレプレグのマトリックス樹脂の粘度がより高くなるまで、非凝縮ガスの流れが導入される、請求項1の方法。
- 非凝縮ガスが空気、窒素、酸素、ネオン、アルゴン、メタン、エタン、エチレン、プロパン、水素またはヘリウムおよびそれらの組み合わせ物を含んでなる、請求項1の方法。
- 非凝縮ガスの流れが約0.001〜100ml/秒の間にわたる速度にある、請求項1の方法。
- 非凝縮ガスおよび揮発成分の少なくとも一部の、囲い内への導入およびそれからの除去が同時に実施される、請求項1の方法。
- 囲いがオートクレーブまたはオーブンである、請求項1の方法。
- 成形プレプレグのマトリックス樹脂がエポキシ化合物、エポキシ硬化剤、フェノール化合物、フェノール、シアネート、イミド、ポリイミド、エステル、ポリエステル、ベンゾキサジン、ポリベンゾキサジン、ポリベンゾキサゾン、ポリベンゾキサゾール、ポリベンズイミダゾール、ポリベンゾチアゾール、ポリアミド、ポリアミドイミド、ポリスルホン、ポリエーテル・スルホン、ポリカーボネート、ポリエチレン・テレフタレート、シアネートまたはポリエーテルケトン、それらの組み合わせ物およびそれらの前駆体のいずれかを含んでなる、請求項1の方法。
- マトリックス樹脂が更にエチニル、ナドマレイミド、アリルナドまたはオレフィン・エンドキャップ基を含んでなる、請求項7の方法。
- 揮発成分が減少させられたプレプレグの形成期間中に、形成前の、少なくとも一つの成形プレプレグの総重量に基づいて10重量%未満のマトリックス樹脂がブリードする、請求項7の方法。
- 成形複合物部分が、成形複合物部分の総容量に基づいて約0〜約30容量%の多孔度を有することを特徴とする、請求項1の方法。
- 一種または複数の揮発成分が少なくとも一種の溶媒を含み、少なくとも一つの成形プレプレグの加熱が、少なくとも一つの成形プレプレグの温度の、成形プリプレグ内に含まれる少なくとも一種の溶媒のほぼ沸点である最終の温度への上昇を含む、請求項1の方法。
- 二種以上の繊維強化複合物の構成部品の間の界面内に接着剤を導入し、ここで、接着剤は一種または複数の揮発成分を含み、
二種以上の繊維強化複合物の構成部品を囲いで取り囲み、
囲い内に非凝縮ガスの流れを導入し、
二種以上の繊維強化複合物の構成部品の間の界面内の接着剤を加熱して、接着剤から一種または複数の揮発成分を発生させ、
囲いから非凝縮ガスの少なくとも一部を除去する工程、を含んでなり、
ここで、非凝縮ガスが接着剤から発生される一種または複数の揮発成分を接着剤から運び去る、
繊維強化複合物の構成部品の接着を容易にする方法。