JP2012087240A - 光学用粘着シート、光学フィルムおよび表示装置 - Google Patents
光学用粘着シート、光学フィルムおよび表示装置 Download PDFInfo
- Publication number
- JP2012087240A JP2012087240A JP2010236316A JP2010236316A JP2012087240A JP 2012087240 A JP2012087240 A JP 2012087240A JP 2010236316 A JP2010236316 A JP 2010236316A JP 2010236316 A JP2010236316 A JP 2010236316A JP 2012087240 A JP2012087240 A JP 2012087240A
- Authority
- JP
- Japan
- Prior art keywords
- sensitive adhesive
- pressure
- adhesive sheet
- weight
- adhesive layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】60℃、95%RHの環境下に120時間保存した後の水分率が0.65重量%以上であり、動的粘弾性測定により測定される85℃におけるせん断貯蔵弾性率が5.0×104〜5.0×105Paである粘着剤層を少なくとも有し、下記の定荷重剥離試験により測定される、被着体をポリエチレンテレフタレート板とした時の剥離距離が30mm以下であり、かつ被着体をアクリル板とした時の剥離距離が30mm以下であることを特徴とする光学用粘着シートを提供する。
【選択図】なし
Description
本発明の粘着剤層は、60℃、95%RHの環境下に120時間保存した後(直後)の水分率が、0.65重量%以上(例えば、0.65〜5.0重量%)であり、好ましくは0.65〜3.0重量%、より好ましくは0.75〜3.0重量%である。水分率を0.65重量%以上とすることにより、加湿による粘着シートの白濁化が生じないため、該粘着シートを用いた製品の表示部の視認性や外観を悪化させない。
(試料の調製及び水分率の測定)
本発明の粘着シートから、本発明の粘着剤層を約0.2g採取したものを試料として用いる。具体的には、本発明の粘着シートが基材レスタイプの両面粘着シートの場合には、例えば、剥離ライナーを剥離し、一方の粘着面にアルミニウム箔を貼り付け、粘着剤層の重さが約0.2gとなるように切り出したものを試料として用いることができる。また、本発明の粘着シートが基材付きの粘着シートの場合には、例えば、基材付きの粘着シートから粘着剤層約0.2gをかき取って採取したものを試料として用いることができる。
前記試料を60℃、95%RHの環境下に120時間保存した後、該試料(60℃、95%RHの環境下で120時間保存後の試料)の秤量を行い、次いで、下記の加熱気化装置に入れ、150℃に加熱した時に発生したガスを下記の電量滴定式水分測定装置の滴定セル内に導入する。そして、前記電量滴定式水分測定装置により、下記の測定条件にて試料中の水分量(μg)を測定し、60℃、95%RHの環境下に120時間保存後の本発明の粘着剤層1gあたり(本発明の粘着剤層のみからなる両面粘着シートの場合には、上記試料の重量からアルミホイルの重量を除いた重量1gあたり)の水分量を求め、粘着剤層の水分率(重量%)を算出する。なお、測定回数(n数)は、例えば、2回が好ましい。
(分析装置)
加熱気化装置:三菱化学(株)製、「VA−06型」
電量滴定式水分測定装置:三菱化学(株)製、「CA−06型」
(測定条件)
方法:加熱気化法/150℃加熱
陽極液:アクアミクロンAKX
陰極液:アクアミクロンCXU
(ゲル分率の測定方法)
本発明の粘着シートから本発明の粘着剤層:約0.1gを採取し、平均孔径0.2μmの多孔質テトラフルオロエチレンシート(商品名「NTF1122」、日東電工(株)製)に包んだ後、凧糸で縛り、その際の重量を測定し、該重量を浸漬前重量とする。なお、該浸漬前重量は、粘着剤層(上記で採取した本発明の粘着剤層)と、テトラフルオロエチレンシートと、凧糸との総重量である。また、テトラフルオロエチレンシートと凧糸との合計重量も測定しておき、該重量を包袋重量とする。
次に、本発明の粘着剤層をテトラフルオロエチレンシートで包み凧糸で縛ったもの(「サンプル」と称する)を、酢酸エチルで満たした50ml容器に入れ、23℃にて7日間静置する。その後、容器からサンプル(酢酸エチル処理後)を取り出して、アルミニウム製カップに移し、130℃で2時間、乾燥機中で乾燥して酢酸エチルを除去した後、重量を測定し、該重量を浸漬後重量とする。
そして、下記の式からゲル分率を算出する。
ゲル分率(重量%)=(A−B)/(C−B)×100
(上記式において、Aは浸漬後重量であり、Bは包袋重量であり、Cは浸漬前重量である。)
(酢酸エチル抽出における可溶分(ゾル分)の重量平均分子量の測定方法)
本発明の粘着シートから本発明の粘着剤層:約0.1gを採取し、平均孔径0.2μmの多孔質テトラフルオロエチレンシート(商品名「NTF1122」、日東電工(株)製)に包んだ後、凧糸で縛る。
次に、上記本発明の粘着剤層をテトラフルオロエチレンシートで包み凧糸で縛ったものを、酢酸エチルで満たした50ml容器に入れ、23℃にて7日間静置する。その後、容器中の酢酸エチル溶液(抽出されたゾル分を含む)を取り出して、減圧乾燥させて、溶媒(酢酸エチル)を揮発させ、ゾル分を得る。
上記ゾル分をテトラヒドロフラン(THF)に溶解させて、ゲルパーミエーションクロマトグラフ(GPC)法によりゾル分の重量平均分子量を測定する。
[測定サンプルの調製]
アクリル系ポリマーを10mM−LiBr+10mM−リン酸/DMF溶液(溶離液)に溶解させ、前記アクリル系ポリマーの濃度が2.0g/Lの溶液を調製し、一晩放置した後、前記溶液を0.45μmメンブレンフィルターでろ過し、ろ液を測定サンプルとして用いる。
[測定装置及び測定条件]
測定装置:商品名「HLC−8120GPC」(東ソー(株)製)
カラム:商品名「TSKgel,SuperAWM−H+superAW4000+superAW2500」(東ソー(株)製)
カラムサイズ:各6.0mmI.D.×150mm
溶離液:10mM−LiBr+10mM−リン酸/DMF
流量:0.4mL/min
検出器:示差屈折計(RI)
カラム温度(測定温度):40℃
注入量:20μL
1/Tg = W1/Tg1+W2/Tg2+・・・+Wn/Tgn
上記式中、Tgはアクリル系ポリマーのガラス転移温度(単位:K)、Tgiはモノマーiがホモポリマーを形成した際のガラス転移温度(単位:K)、Wiはモノマーiの全モノマー成分中の重量分率を表す(i=1、2、・・・・n)。なお、上記はアクリル系ポリマーがモノマー1、モノマー2、・・・、モノマーnのn種類のモノマー成分から構成される場合の計算式である。
(1)アクリル系ポリマーを構成するモノマー成分全量(100重量%)に対して、メタクリル酸メチルを5〜20重量%、アクリル酸2−エチルヘキシルを35〜80重量%、N−ビニル−2−ピロリドンを5〜20重量%、アクリル酸2−ヒドロキシエチルを10〜25重量%含有するモノマー成分から構成されたアクリル系ポリマー100重量部、およびイソシアネート系架橋剤0.01〜5.0重量部を含む粘着剤組成物より形成された粘着剤層。
(2)アクリル系ポリマーを構成するモノマー成分全量(100重量%)に対して、メタクリル酸メチルを5〜20重量%、アクリル酸n−ブチルを35〜80重量%、N−ビニル−2−ピロリドンを5〜20重量%、アクリル酸2−ヒドロキシエチルを10〜25重量%含有するモノマー成分から構成されたアクリル系ポリマー100重量部、およびイソシアネート系架橋剤0.01〜5.0重量部を含む粘着剤組成物より形成された粘着剤層。
本発明の粘着シートが他の粘着剤層を有する場合、他の粘着剤層としては、特に限定されず、例えば、ウレタン系粘着剤、アクリル系粘着剤、ゴム系粘着剤、シリコーン系粘着剤、ポリエステル系粘着剤、ポリアミド系粘着剤、エポキシ系粘着剤、ビニルアルキルエーテル系粘着剤、フッ素系粘着剤などの公知の粘着剤から形成された公知慣用の粘着剤層が挙げられる。なお、上記粘着剤は単独で、又は2種以上を組み合わせて用いることができる。
本発明の粘着シートが基材を有する場合、基材としては、特に限定されないが、プラスチックフィルム、反射防止(AR)フィルム、偏光板、位相差板などの各種フィルム(例えば、後述の光学フィルム)が挙げられる。上記プラスチックフィルムなどの素材としては、例えば、ポリエチレンテレフタレート(PET)等のポリエステル系樹脂、ポリメチルメタクリレート(PMMA)等のアクリル系樹脂、ポリカーボネート、トリアセチルセルロース(TAC)、ポリサルフォン、ポリアリレート、ポリイミド、ポリ塩化ビニル、ポリ酢酸ビニル、ポリエチレン、ポリプロピレン、エチレン−プロピレン共重合体、商品名「アートン(環状オレフィン系ポリマー;JSR製)」、商品名「ゼオノア(環状オレフィン系ポリマー;日本ゼオン製)」等の環状オレフィン系ポリマーなどのプラスチック材料が挙げられる。なお、これらのプラスチック材料は単独で、又は2種以上を組み合わせて使用することができる。また、上記の「基材」とは、粘着シートを被着体(光学部材等)に使用(貼付)する際には、粘着剤層とともに被着体に貼付される部分である。粘着シートの使用時(貼付時)に剥離されるセパレータ(剥離ライナー)は「基材」には含まない。
本発明の粘着シートは、本発明の粘着剤層を少なくとも有していればよく、特に限定されないが、例えば、本発明の粘着剤層のみからなる基材レスタイプの両面粘着シートであってもよいし、基材の少なくとも一方の表面側に本発明の粘着剤層を有する基材を有するタイプの粘着シートであってもよい。
被着体(PET板)の片面に、粘着シート(幅20mm×長さ60mm)の本発明の粘着剤層側の表面を貼付した後、オートクレーブ中で50℃、5気圧の条件で15分間処理する。その後、23℃、50%RHの条件下で、粘着シートの長さ方向の末端に、PET板の表面と垂直方向(PET板から離れる方向)に100gfの荷重をかけ、23℃、50%RHの条件下で3時間放置し、粘着シートが剥離した長さ(粘着シートの剥離距離)を測定し、「剥離距離(対PET)」とする。
[定荷重剥離試験]
ポリエチレンテレフタレートフィルム[PETフィルム、東洋紡(株)製、商品名「A4300」、長さ100mm×幅30mm、厚さ125μm]の一方の表面に、両面粘着テープを用いてガラス板を貼り合わせて補強した、ポリエチレンテレフタレート板[PET板(PETフィルムとガラス板の貼り合わせ体)、長さ100mm×幅30mm、厚さ2.0mm]の片面(PETフィルム側表面)に、粘着シート(幅20mm×長さ60mm)の本発明の粘着剤層側の表面を貼付した後、オートクレーブ中で50℃、5気圧の条件で15分間処理する。
次いで、図1、図2に示すように、上記PET板11を、粘着シート12を貼付した面が下面になるように水平に設置する。粘着シート12を、長さ方向の末端(片末端)から長さ方向に5mm剥離し、長さ方向の端部(幅方向の中心位置)から、100gの錘13をひもで吊し、粘着シート12の長さ方向の末端に、PET板11の表面と垂直方向に100gfの荷重をかける。
その後、23℃、50%RHの条件下で、3時間放置し、粘着シート12の剥離距離16を測定し、「剥離距離(対PET)」とする。
なお、上記剥離距離は、測定開始時から3時間経過する間に粘着シートが剥離した長さ(長さ方向の距離)であり、測定開始時に粘着シートとPET板が密着している末端位置14から、3時間経過後に粘着シートとPET板が密着している末端位置15までの距離16をいう(図2、図3参照)。
なお、粘着シートが両面粘着シートである場合には、PET板側とは反対側の粘着面上に、厚さ25μmのPETフィルムを貼付(裏打ち)して測定してもよい。
まず、粘着シートを適切な大きさに切り出し、セパレータが設けられている場合にはセパレータを剥離して、粘着面を露出させ試験片とする。両面粘着シートの場合には、一方の粘着面上にはPETフィルム(厚さ25〜50μm)を貼付して、片方の粘着面のみを露出させた形態とする。なお、この際、金属薄膜に貼付する側の粘着面(本発明の粘着シートであれば、本発明の粘着剤層側の表面)を露出させる。試験片の大きさ(粘着面の露出面積)は100cm2が好ましい。
次いで、上記試験片を、温度100℃の純水中に入れ、45分間煮沸し、アクリル酸イオン及びメタクリル酸イオンの煮沸抽出を行う。
次いで、イオンクロマトグラフ法(イオンクロマトグラフィー)により、上記で得られた抽出液中のアクリル酸イオンおよびメタクリル酸イオンの合計量(単位:ng)を測定し、試験片の粘着面(露出した粘着面)の単位面積あたりのアクリル酸イオンおよびメタクリル酸イオンの合計量(単位:ng/cm2)を算出する。イオンクロマトグラフ法(イオンクロマトグラフィー)の測定条件は、特に限定されないが、例えば、下記の条件で測定することができる。
[イオンクロマトグラフ法の測定条件]
分析装置 : DIONEX社製、DX−320
分離カラム : Ion Pac AS15(4mm×250mm)
ガードカラム : Ion Pac AG15(4mm×50mm)
除去システム : ASRS−ULTRA(エクスターナルモード、100mA)
検出器 : 電気伝導度検出器
溶離液 : 7mM KOH(0〜20分)
45mM KOH(20〜30分)
(溶離液ジェネレーターEG40を使用)
溶離液流量 : 1.0ml/分
試料注入量 : 250μl
モノマー成分として、アクリル酸2−エチルヘキシル(2EHA)63重量部、N−ビニル−2−ピロリドン(NVP)15重量部、メタクリル酸メチル(MMA)9重量部、アクリル酸2−ヒドロキシエチル(HEA)13重量部、重合開始剤として2,2'−アゾビスイソブチロニトリル0.2重量部、及び重合溶媒として酢酸エチル133重量部を、セパラブルフラスコに投入し、窒素ガスを導入しながら1時間撹拌した。このようにして重合系内の酸素を除去した後、65℃に昇温し、10時間反応させ、その後、酢酸エチルを加えて固形分濃度30重量%のアクリル系ポリマー溶液を得た。
表1に示すように、上記アクリル系ポリマー溶液中のアクリル系ポリマー100重量部に対して、架橋剤としてイソシアネート系架橋剤(三井化学(株)製、商品名「タケネートD110N」)を0.3重量部、架橋促進剤としてエチレンジアミンにプロピレンオキシドを付加したポリオール((株)アデカ製、商品名「EDP−300」)を0.2重量部、シランカップリング剤としてγ−グリシドキシプロピルトリメトキシシラン(信越化学工業(株)製、商品名「KBM−403」)0.15重量部を加え、混合し、粘着剤組成物(溶液)を調製した。
次に、上記粘着剤組成物を、剥離ライナー(三菱樹脂(株)製、商品名「MRF75」)の剥離処理面上に、乾燥後の厚さが50μmとなるように塗布し、常圧下、60℃で1分間及び155℃で1分間加熱乾燥し、さらに23℃で120時間エージングを行い、両面粘着シート(基材レス両面粘着シート)を得た。
表1に示すように、イソシアネート系架橋剤「タケネートD110N」の使用量を0.5重量部に変更したこと以外は実施例1と同様にして、粘着剤層の厚さが50μmの両面粘着シート(基材レス両面粘着シート)を得た。
表1に示すように、モノマー成分として、アクリル酸n−ブチル(BA)76重量部、N−ビニル−2−ピロリドン6重量部、メタクリル酸メチル5重量部、アクリル酸2−ヒドロキシエチル13重量部を用い、イソシアネート系架橋剤「タケネートD110N」の使用量を0.5重量部に変更したこと以外は実施例1と同様にして、粘着剤層の厚さが50μmの両面粘着シート(基材レス両面粘着シート)を得た。
表1に示すように、モノマー成分として、アクリル酸n−ブチル72重量部、N−ビニル−2−ピロリドン10重量部、メタクリル酸メチル5重量部、アクリル酸2−ヒドロキシエチル13重量部を用い、イソシアネート系架橋剤「タケネートD110N」の使用量を0.5重量部に変更したこと以外は実施例1と同様にして、粘着剤層の厚さが50μmの両面粘着シート(基材レス両面粘着シート)を得た。
表1に示すように、モノマー成分として、アクリル酸2−エチルヘキシル72重量部、N−ビニル−2−ピロリドン15重量部、アクリル酸2−ヒドロキシエチル13重量部を用い、イソシアネート系架橋剤「タケネートD110N」の使用量を0.5重量部に変更したこと以外は実施例1と同様にして、粘着剤層の厚さが50μmの両面粘着シート(基材レス両面粘着シート)を得た。
表1に示すように、モノマー成分として、アクリル酸2−エチルヘキシル72重量部、メタクリル酸メチル15重量部、アクリル酸2−ヒドロキシエチル13重量部を用い、イソシアネート系架橋剤「タケネートD110N」の使用量を0.5重量部に変更したこと以外は実施例1と同様にして、粘着剤層の厚さが50μmの両面粘着シート(基材レス両面粘着シート)を得た。
表1に示すように、モノマー成分として、アクリル酸2−エチルヘキシル71重量部、N−ビニル−2−ピロリドン15重量部、メタクリル酸メチル9重量部、アクリル酸2−ヒドロキシエチル5重量部を用い、イソシアネート系架橋剤「タケネートD110N」の使用量を0.5重量部に変更したこと以外は実施例1と同様にして、粘着剤層の厚さが50μmの両面粘着シート(基材レス両面粘着シート)を得た。
表1に示すように、モノマー成分として、アクリル酸2−エチルヘキシル77重量部、N−ビニル−2−ピロリドン3重量部、メタクリル酸メチル3重量部、アクリル酸2−ヒドロキシエチル13重量部を用い、イソシアネート系架橋剤「タケネートD110N」の使用量を0.5重量部に変更したこと以外は実施例1と同様にして、粘着剤層の厚さが50μmの両面粘着シート(基材レス両面粘着シート)を得た。
実施例および比較例で得られた粘着シート(両面粘着シート)について、表1に示す測定又は評価を行った。測定方法又は評価方法は下記の通りである。また、実施例および比較例で得られた両面粘着シートの粘着剤層のゲル分率、ゾル分の重量平均分子量(Mw)及び分子量分布(Mw/Mn)は、上述の方法により測定した。
実施例および比較例で得られた両面粘着シートを、幅1cm×長さ2cm(面積:2cm2)のサイズに切り出した。次に、剥離ライナーを剥離し、一方の粘着面にアルミホイルを貼付し、他方の粘着面は開放状態として試験片(「粘着剤層/アルミニウム箔」の構成を有する)を作製した。なお、前記試験片に貼り付けたアルミニウム箔の重量は、粘着シートに貼付する前にあらかじめ測定しておいた。
庫内の条件を60℃、95%RHに調節した恒温恒湿機に前記試験片を入れ、120時間保存した。その後、恒温恒湿機から試験片を取り出し、試験片の重量を測定した。次いで、前記試験片を下記の加熱気化装置に入れ、150℃で10分間加熱した時に発生したガスを下記の電量滴定式水分測定装置の滴定セル内に導入し、前記ガス中の水分量(μg)を測定して、60℃、95%RHの環境下に120時間保存後の粘着剤層中の水分量(μg)を測定した。そして、下記式により60℃、95%RHの環境下で120時間保存した後の粘着剤層の水分率(重量%)を算出した。なお、測定回数(n数)は2回とし、平均値を算出した。
「粘着剤層の水分率(重量%)」=「60℃、95%RHの環境下に120時間保存後の粘着剤層中の水分量(μg)」/(「60℃、95%RHの環境下に120時間保存後の試験片の重量(μg)」−「アルミニウム箔の重量(μg)」)×100
(分析装置)
電量滴定式水分測定装置:三菱化学(株)製、「CA−06型」
加熱気化装置:三菱化学(株)製、「VA−06型」
(測定条件)
方法:加熱気化法/150℃加熱
陽極液:アクアミクロンAKX
陰極液:アクアミクロンCXU
実施例および比較例で得られた両面粘着シートの粘着剤層を積層して、厚さ約1.5mmの粘着剤層の積層体を作製し、試験片とした。
上記試験片を、Rheometric Scientific社製「Advanced Rheometric Expansion System(ARES)」を用いて、周波数1Hzの条件で、−70〜200℃の範囲で昇温速度5℃/分で測定して、85℃におけるせん断貯蔵弾性率及び23℃におけるせん断貯蔵弾性率を算出した。
実施例および比較例で得られた両面粘着シートの一方の粘着面に、アルミ蒸着PETフィルム((株)麗光製、商品名「SZ PET25Al」、厚さ:25μm)を裏打ちし、幅20mm×長さ60mmのテープ片を切り出して、測定用サンプル12(両面粘着シートとアルミ蒸着PETフィルムの貼り合わせ体)とした。
上記測定用サンプル12の粘着面(両面粘着シートの他方の粘着面)を、ポリエチレンテレフタレート板11[PET板(PETフィルム(東洋紡(株)製、商品名「A4300」、厚さ125μm)とガラス板の貼り合わせ体)、長さ100mm×幅30mm、厚さ2.0mm]のPETフィルム側の表面(中央部)に貼り合わせ、オートクレーブ中で50℃、5気圧の条件で15分間処理した。
次いで、PET板11を、クランプを用いて、測定用サンプル12を貼付した面が下側になるように水平に設置した(図1、図2参照)。
図1、図2に示すように、PET板11から、測定用サンプル12を、サンプルの長さ方向の末端から長さ方向に5mm剥離した。さらに、測定用サンプル12の長さ方向の端部(上記剥離した部分)から、100gの錘13をひもで吊るし、PET板11の表面と垂直(下)方向に100gf(0.98N)の荷重をかけた。なお、上記の錘13は、測定用サンプル12の幅方向の中央、長さ方向の末端から5mmの部分に穴を開けて通したひもの先に取り付けた。
上記のように荷重をかけた後、23℃、50%RHの条件下で、3時間放置した。測定開始から3時間が経過する間(3時間放置の間)に測定用サンプル12がPET板11に対して剥離した距離(剥離距離)16を測定し、これを剥離距離(対PET板)とした。
なお、上記剥離距離16は、測定用サンプル12の長さ方向における剥離距離であり、測定開始時に両面粘着シートとPET板が密着している末端位置14から、3時間経過後に両面粘着シートとPET板が密着している末端位置15までの距離16をいう(図2、図3参照)。上記剥離距離16は測定用サンプル12の幅方向の中心距離で測定した。
また、PET板の代わりに、アクリル板[PMMA板、三菱レイヨン(株)製、商品名「アクリライト MR−200」、長さ100mm×幅30mm、厚さ1.5mm]を用いたこと以外は、上記と同様にして、剥離距離(対アクリル板)を測定した。
結果はそれぞれ、表1の「剥離距離 対PET」、「剥離距離 対アクリル」の欄に示した。
実施例及び比較例で得られた両面粘着シートの一方の粘着面にPETフィルム(東レ(株)製、「ルミラー S10」、厚さ25μm)を貼付した後、サイズ:幅10cm×長さ10cmのシート片を切り出した。その後、剥離ライナーを剥離し、片面の粘着面だけを露出させた試験片を作製した(粘着面の露出面積:100cm2)。
次いで、前記試験片を、温度100℃の純水(50ml)中に入れ、45分間煮沸し、煮沸抽出を行い、抽出液を得た。
次いで、イオンクロマトグラフ法(イオンクロマトグラフィー)により、上記で得られた抽出液中のアクリル酸イオン及びメタクリル酸イオンの合計量(単位:ng)を測定し、試料の粘着面(露出した粘着面)の単位面積あたりのアクリル酸イオン及びメタクリル酸イオンの合計量(抽出(メタ)アクリル酸イオン量、単位:ng/cm2)を算出した。なお、抽出(メタ)アクリル酸イオンが検出限界未満(検出限界:2.5ng)であった場合には、表1において「ND」と記載した。
[イオンクロマトグラフ法の測定条件]
分析装置 : DIONEX社製、DX−320
分離カラム : Ion Pac AS15(4mm×250mm)
ガードカラム : Ion Pac AG15(4mm×50mm)
除去システム : ASRS−ULTRA(エクスターナルモード、100mA)
検出器 : 電気伝導度検出器
溶離液 : 7mM KOH(0〜20分)
45mM KOH(20〜30分)
(溶離液ジェネレーターEG40を使用)
溶離液流量 : 1.0ml/分
試料注入量 : 250μl
実施例、比較例で得られた両面粘着シートから剥離ライナーを剥離し、該両面粘着シートの一方の粘着面をスライドガラス(松浪硝子(株)製、商品名「MICRO SLIDE GLASS」、品番「S」、厚さ1.3mm、ヘイズ0.1%、水縁磨)に貼り付け、他方の粘着面を導電性PETフィルム(日東電工(株)製、商品名「エレクリスタ V270L−THMP」)のITO膜形成面に貼り付けて、「スライドガラス/両面粘着シート(粘着剤層)/導電性PETフィルム」の構成を有する試験片を作製した。前記試験片のヘイズを、23℃、50%RHの環境下において、ヘイズメータ((株)村上色彩技術研究所製、商品名「HM−150」)を用いて測定し、これを「初期のヘイズ」とした。
次いで、上記試験片を60℃、95%RHの環境下(湿熱環境下)に120時間保存した。その後、上記試験片を23℃、50%RHの環境下に取り出し、取り出した直後のヘイズ(「ヘイズ(直後)」と称する)、23℃、50%RHの環境下に取り出してから30分後のヘイズ(「ヘイズ(30分後)」と称する)、23℃、50%RHの環境下に取り出してから1時間後のヘイズ(「ヘイズ(1時間後)」と称する)、及び23℃、50%RHの環境下に取り出してから2時間後のヘイズ(「ヘイズ(2時間後)」と称する)を測定した。そして、「初期のヘイズ」に対する「ヘイズ(直後)」の上昇幅[=(ヘイズ(直後))−(初期のヘイズ)]、「初期のヘイズ」に対する「ヘイズ(30分後)」の上昇幅[=(ヘイズ(30分後))−(初期のヘイズ)]、「初期のヘイズ」に対する「ヘイズ(1時間後)」の上昇幅[=(ヘイズ(1時間後))−(初期のヘイズ)]、及び「初期のヘイズ」に対する「ヘイズ(2時間後)」の上昇幅[=(ヘイズ(2時間後))−(初期のヘイズ)]をそれぞれ算出し、いずれも5.0%(%ポイント)未満であった場合を○(加湿による白濁化なし)、いずれかが5.0%(%ポイント)以上であった場合を×(加湿による白濁化あり)として判定した。結果は表1の「加湿濁り性」の欄に示した。
実施例、比較例で得られた両面粘着シートの一方の粘着面を、導電性フィルム(日東電工(株)製、商品名「エレクリスタ V270L−THMP」)をあらかじめ140℃で120分間処理したもののITO膜形成面に貼り合わせ、100mm×100mmのフィルム片を作製した。
上記のフィルム片より剥離ライナーを剥離して、他方の粘着面をアクリル板(三菱レイヨン(株)製、商品名「アクリライトL」、サイズ:幅50mm×長さ100mm、厚さ1.0mm)に貼り合わせ、線圧5N/cmの条件で圧着し、「導電性フィルム/両面粘着シート(粘着剤層)/アクリル板」の層構造を有する試験片を作製した。次いで、前記試験片を50℃、24時間の条件でエージングした。
上記試験片を庫内の温度が85℃のオーブン中に入れ、240時間熱処理(耐熱性試験)を行った。熱処理後、試験片の接着界面(粘着剤層と導電性フィルムとの界面)における気泡や浮きの発生の有無を目視にて観察した。また、85℃での耐熱性試験の代わりに、60℃、95%RHの条件で250時間湿熱処理(耐湿熱性試験)を行い、試験片の接着界面における気泡や浮きの発生の有無を観察した。
また、上記アクリル板の代わりに、ポリカーボネート板(PC板)(ハードコートが施されていないポリカーボネート板;帝人化成(株)製、商品名「PC1111」、サイズ:幅50mm×長さ100mm、厚さ1.0mm)を用いた試験片について、上記と同様に、85℃での耐熱性試験、60℃、95%RHでの耐湿熱性試験を行い、試験片の接着界面における気泡や浮きの発生の有無を観察した。
下記の評価基準により耐久性を評価し、結果を表1の「耐久性(発泡剥がれ)」の欄に示した。
耐久性の評価基準:アクリル板を用いた85℃での耐熱性試験および60℃、95%RHでの耐湿熱性試験、PC板を用いた85℃での耐熱性試験および60℃、95%RHでの耐湿熱性試験において、いずれの場合にも気泡や浮きが全く見られなかった場合を耐久性「良好」、いずれかの場合に気泡又は浮きが僅かでも見られた場合には耐久性「不良」と判定した。
実施例、比較例で得られた両面粘着シートの一方の粘着面に、PETフィルム(東レ(株)製、商品名「ルミラー S−10 #25」、厚さ25μm)を貼り合わせ、幅20mm×長さ50mmのサイズに切り出し、試験片とした。
図4及び図5に示すように、導電性PETフィルム22(日東電工(株)製、商品名「エレクリスタ P−400L TNMP」)(サイズ:長さ70mm×幅25mm)の両端部に15mm幅で銀ペーストを塗布し、その導電面(ITO膜形成面22a側)に剥離ライナーを剥離した上記試験片21の粘着面を貼り合わせ、積層体(試験片21と導電性PETフィルム22との積層体)(抵抗値測定サンプル)を作製した。これを、23℃の環境下で24時間放置した後、60℃、95%RHと80℃のそれぞれの環境下で250時間放置し、「貼付直後の抵抗値」に対する「60℃95%RH、250時間放置後の抵抗値」の割合(%)[=(60℃95%RH、250時間放置後の抵抗値)/(貼付直後の抵抗値)×100(%)]、及び、「貼付直後の抵抗値」に対する「80℃、250時間放置後の抵抗値」の割合(%)[=(80℃、250時間放置後の抵抗値)/(貼付直後の抵抗値)×100(%)]をそれぞれ測定した。なお、上記の抵抗値は、日置電気(株)製「3540 ミリオームハイテスタ」を用いて、上記積層体の両端の銀ペースト部分22bに電極をつけて測定した。
「貼付直後の抵抗値」に対する「60℃95%RH、250時間放置後の抵抗値」の割合、及び、「貼付直後の抵抗値」に対する「80℃、250時間放置後の抵抗値」の割合が共に120%未満であれば耐腐食性「良好」、いずれか一方でも120%以上であれば耐腐食性「不良」と判断した。結果は表1における「耐腐食性」の欄に示した。
なお、ブランクとして粘着シートを貼付しない導電性PETフィルムのみで同様の試験を行った結果、「250時間放置前の抵抗値」に対する「250時間放置後の抵抗値」の割合は、80℃の条件では110%、60℃、95%RHの条件では120%であった。
PETフィルム(東洋紡績(株)製、商品名「A4100」、厚さ188μm)の片面上に、スクリーン印刷で厚さ4μmの黒色印刷を3回施し、図6に示すような額縁状の黒色印刷層(印刷層厚さ12μm、外形寸法:長さ60mm×幅42mm)を有するPETフィルム(サイズ:長さ60mm×幅42mm)を作製した。
次いで、実施例および比較例で得られた両面粘着シート(サイズ:長さ60mm×幅42mm)の粘着面(一方の粘着面)を、上記黒色印刷層を有するPETフィルムの黒色印刷層を有する側の表面上に、ラミネータ(線圧:5kg/cm)で貼り合わせた。
さらに、上記の黒色印刷層を有するPETフィルムと両面粘着シートの積層体から剥離ライナーを剥離して、該積層体の粘着面側を、予めガラス基板上に貼り合わせたPETフィルム(東洋紡績(株)製、商品名「A4300」、厚さ125μm)(サイズ:長さ60mm×幅42mm)上に、ラミネータ(線圧:5kg/cm)で貼り合わせ、測定サンプル(図7参照)を作製した。
上記測定サンプルを、オートクレーブを用いて、50℃、0.5MPaの条件下で15分間処理した後、ガラス基板側から目視にて段差部分の気泡、浮きの有無を観察した。段差部分に気泡、浮きが全くない場合には○(段差吸収性良好)、気泡又は浮きが少しでも生じている場合には×(段差吸収性不良)と判定した。なお、結果は、表1における「段差吸収性」の欄に示した。
12 粘着シート(又は測定用サンプル(両面粘着シート/PETフィルム))
13 錘
14 測定開始時に粘着シート(又は測定用サンプル)とPET板又はアクリル板が密着している末端位置
15 3時間経過後に粘着シート(又は測定用サンプル)とPET板又はアクリル板が密着している末端位置
16 剥離距離
21 試験片
21a PETフィルム
21b 粘着シート(両面粘着シート)
22 導電性PETフィルム
22a 導電性PETフィルムのITO膜形成面
22b 導電性PETフィルムの銀ペースト塗布部分
31 PETフィルム
32 黒色印刷層
33 両面粘着シート(アクリル系粘着剤層)
34 PETフィルム
35 ガラス基板
36 段差部分
Claims (7)
- 60℃、95%RHの環境下に120時間保存した後の水分率が0.65重量%以上であり、動的粘弾性測定により測定される85℃におけるせん断貯蔵弾性率が5.0×104〜5.0×105Paである粘着剤層を少なくとも有し、
下記の定荷重剥離試験により測定される、被着体をポリエチレンテレフタレート板とした時の剥離距離が30mm以下であり、かつ被着体をアクリル板とした時の剥離距離が30mm以下であることを特徴とする光学用粘着シート。
定荷重剥離試験:被着体の片面に、粘着シート(幅20mm×長さ60mm)の前記粘着剤層表面を貼付した後、オートクレーブ中で50℃、5気圧の条件で15分間処理する。その後、23℃、50%RHの条件下で、粘着シートの長さ方向の末端に、被着体の表面と垂直方向に100gfの荷重をかけ、3時間経過後の粘着シートの剥離距離を測定する。 - イオンクロマトグラフ法で測定される、純水で100℃、45分の条件で抽出されたアクリル酸イオンおよびメタクリル酸イオンの合計量が、前記粘着剤層の単位面積あたり20ng/cm2以下である請求項1に記載の光学用粘着シート。
- 前記粘着剤層のゲル分率が40〜95%である請求項1又は2に記載の光学用粘着シート。
- 前記粘着剤層が、アクリル系ポリマーを構成するモノマー成分全量(100重量%)に対して、メタクリル酸メチルの含有量が5〜20重量%であるモノマー成分より構成されたアクリル系ポリマーを含む粘着剤層である請求項1〜3のいずれかの項に記載の光学用粘着シート。
- 前記アクリル系ポリマーが、アクリル系ポリマーを構成するモノマー成分全量(100重量%)に対して、水酸基含有モノマーの含有量が10〜25重量%であるモノマー成分より構成されたアクリル系ポリマーである請求項4に記載の光学用粘着シート。
- 請求項1〜5のいずれかの項に記載の光学用粘着シートを有する光学フィルム。
- 請求項1〜5のいずれかの項に記載の光学用粘着シートを有する表示装置。