JP2011178820A - タイヤトレッド用ゴム組成物およびそれを用いた空気入りタイヤ - Google Patents
タイヤトレッド用ゴム組成物およびそれを用いた空気入りタイヤ Download PDFInfo
- Publication number
- JP2011178820A JP2011178820A JP2010041331A JP2010041331A JP2011178820A JP 2011178820 A JP2011178820 A JP 2011178820A JP 2010041331 A JP2010041331 A JP 2010041331A JP 2010041331 A JP2010041331 A JP 2010041331A JP 2011178820 A JP2011178820 A JP 2011178820A
- Authority
- JP
- Japan
- Prior art keywords
- rubber
- parts
- mass
- tire
- rubber composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】天然ゴム40〜80質量部およびジエン系ゴム(但し前記天然ゴムを除く)20〜60質量部からなるゴム成分100質量部に対し、窒素吸着比表面積が250〜450m2/gのカーボンブラックを80〜150質量部および樹脂を30〜80質量部配合してなることを特徴とするタイヤトレッド用ゴム組成物と、該ゴム組成物をトレッド(3)に使用した空気入りタイヤ。
【選択図】図1
Description
グリップ性能を高めるために、高いガラス転移温度(Tg)のスチレン−ブタジエン共重合体ゴム(SBR)を配合する技術がある。しかし、この技術では走行初期のグリップ性能と耐摩耗性が犠牲になるという問題がある。また、小粒径のカーボンブラックを多量に配合する、あるいは高い軟化点の粘着性付与樹脂を配合する、などの技術も知られている。しかし、これらの技術はグリップ性能の向上に効果はあるものの、前者はグリップ性能が持続せず耐摩耗性も劣り、後者は走行初期グリップ性能が犠牲になるという問題点がある。
すなわち本発明は以下のとおりである。
1.天然ゴム40〜80質量部およびジエン系ゴム(但し前記天然ゴムを除く)20〜60質量部からなるゴム成分100質量部に対し、
窒素吸着比表面積が250〜450m2/gのカーボンブラックを80〜150質量部および樹脂を30〜80質量部配合してなることを特徴とするタイヤトレッド用ゴム組成物。
2.前記ジエン系ゴムが、ガラス転移温度−35〜0℃のスチレン−ブタジエン共重合体ゴムであることを特徴とする前記1に記載のタイヤトレッド用ゴム組成物。
3.前記樹脂が、軟化点80〜170℃のテルペン系樹脂であることを特徴とする前記1または2に記載のタイヤトレッド用ゴム組成物。
4.前記1〜3のいずれかに記載のタイヤトレッド用ゴム組成物をトレッドに使用した空気入りタイヤ。
図1において、空気入りタイヤは左右一対のビード部1およびサイドウォール2と、両サイドウォール2に連なるトレッド3からなり、ビード部1、1間に繊維コードが埋設されたカーカス層4が装架され、カーカス層4の端部がビードコア5およびビードフィラー6の廻りにタイヤ内側から外側に折り返されて巻き上げられている。トレッド3においては、カーカス層4の外側に、ベルト層7がタイヤ1周に亘って配置されている。また、ビード部1においてはリムに接する部分にリムクッション8が配置されている。
以下に説明する本発明のタイヤトレッド用ゴム組成物は、とくにトレッド3に有用である。
本発明で使用されるゴム成分は、天然ゴム40〜80質量部およびジエン系ゴム(但し前記天然ゴムを除く)20〜60質量部から構成される。なお、前記天然ゴムおよびジエン系ゴムの合計量は100質量部とする。
前記ジエン系ゴムとしては、イソプレンゴム(IR)、ブタジエンゴム(BR)、スチレン−ブタジエン共重合体ゴム(SBR)、アクリロニトリル−ブタジエン共重合体ゴム(NBR)等が挙げられる。これらは、単独で用いてもよく、2種以上を併用してもよい。
天然ゴム(NR)の配合量が40質量部未満では、走行初期のグリップ性能および耐摩耗性が悪化する。逆に80質量部を超えると、グリップ持続性が悪化するので好ましくない。
さらに好ましい配合量は、天然ゴム50〜70質量部およびジエン系ゴム(但し前記天然ゴムを除く)30〜50質量部である。
SBRのTgが−35℃以上であることにより、トレッドが発熱した後に充分なグリップ性能が提供される。また、SBRのTgが0℃以下であることにより、走行初期のグリップ性能がさらに向上する。
本発明で使用されるカーボンブラックは、窒素吸着比表面積(N2SA)が250〜450m2/gである必要がある。上記範囲を外れると本発明の効果を奏することができない。なお、窒素吸着比表面積(N2SA)はJIS K6217−2に準拠して求めた値である。さらに好ましい窒素吸着比表面積(N2SA)は、300〜400m2/gである。
本発明で使用される樹脂は、例えば、テルペン系樹脂、ロジン系樹脂等の天然樹脂、石油系樹脂、石炭系樹脂、フェノール系樹脂、キシレン系樹脂等の合成樹脂が挙げられる。中でもテルペン系樹脂が好ましく、テルペン系樹脂としては、α−ピネン樹脂、β−ピネン樹脂、リモネン樹脂、水添リモネン樹脂、ジペンテン樹脂、テルペンフェノール樹脂、テルペンスチレン樹脂、芳香族変性テルペン樹脂、水素添加テルペン樹脂等が挙げられる。また本発明において、テルペン系樹脂の軟化点は80〜170℃であることが望ましい。軟化点が80℃以上であることにより、走行初期、ならびに連続走行時における充分なグリップ性能が得られ、また耐摩耗性も向上する。また軟化点が170℃以下であることにより、走行初期のグリップ性能が向上する。
本発明のタイヤトレッド用ゴム組成物は、各種充填剤を配合することができる。充填剤としてはとくに制限されず、用途により適宜選択すればよいが、例えば無機充填剤等が挙げられる。無機充填剤としては、例えばシリカ、クレー、タルク、炭酸カルシウム等を挙げることができる。
本発明のタイヤトレッド用ゴム組成物は、天然ゴム40〜80質量部およびジエン系ゴム(但し前記天然ゴムを除く)20〜60質量部からなるゴム成分100質量部に対し、
窒素吸着比表面積が250〜450m2/gのカーボンブラックを80〜150質量部および樹脂を30〜80質量部配合してなることを特徴とする。
樹脂の配合量が30質量部未満であると、充分なグリップ性能が得られないので好ましくない。逆に80質量部を超えると、走行初期グリップ性能が犠牲になり好ましくない。
樹脂のさらに好ましい上記配合量は、40〜70質量部である。
サンプルの調製
表1に示す配合(質量部)において、加硫促進剤および硫黄を除く成分を55リットルのニーダーで15分間混練した後、ニーダー外に放出させてロールでシート状にし、室温まで冷却した。続いて、該組成物を同ニーダーに再度入れ、加硫促進剤および硫黄を加えて混練し、タイヤトレッド用ゴム組成物を得た。
上記のように調製された各種ゴム組成物をトレッドに用いた195/55R15サイズの試験タイヤを作製した。次に、試験タイヤを4輪車両の4輪に装着し、1周2.2kmのサーキットをDRY条件下、可能限界スピードで10周連続走行した。
グリップ初期性能:高速走行の際の走行初期のグリップ性能を評価するため、1〜3周の周回タイムの平均値を求め、比較例1のゴム組成物をトレッドに使用したタイヤで得られた1〜3周の周回タイムの平均値を対照基準とした場合に、以下のように5段階で評価した:
5:対照基準に対して0.5秒以上速い場合、
4:対照基準に対して0.2秒以上0.5秒未満速い場合、
3:対照基準に対して±0.2秒未満である場合、
2:対照基準に対して0.2秒以上0.5秒未満遅い場合、
1:対照基準に対して0.5秒以上遅い場合。
グリップ持続性能:高速走行の際のグリップ性能の変化を評価するため、上記の10周の走行のうちの8〜10周の周回タイムの平均値を求め、比較例1のゴム組成物をトレッドに使用したタイヤで得られた8〜10周の周回タイムの平均値を対照基準とした場合に、以下のように5段階で評価した:
5:対照基準に対して0.5秒以上速い場合、
4:対照基準に対して0.2秒以上0.5秒未満速い場合、
3:対照基準に対して±0.2秒未満である場合、
2:対照基準に対して0.2秒以上0.5秒未満遅い場合、
1:対照基準に対して0.5秒以上遅い場合。
結果を表1に併せて示す。
*2:SBR−1(旭化成ケミカルズ(株)製タフデン2330、Tg=−50℃、油展量=SBR100質量部に対し37.5質量部)
*3:SBR−2(旭化成ケミカルズ(株)製タフデン4350、Tg=−22℃、油展量=SBR100質量部に対し50質量部)
*4:SBR−3(日本ゼオン(株)製Nipol NS412、Tg=−6℃、油展量=SBR100質量部に対し50質量部)
*5:カーボンブラック−1(キャボットジャパン(株)製キャボットBLACKPEALS880、窒素吸着比表面積(N2SA)=220m2/g)
*6:カーボンブラック−2(コロンビヤンカーボン社製CD2019、窒素吸着比表面積(N2SA)=340m2/g)
*7:カーボンブラック−3(キャボットジャパン(株)製キャボットBLACKPEALS1300、窒素吸着比表面積(N2SA)=560m2/g)
*8:芳香族変性テルペン樹脂−1(ヤスハラケミカル(株)製YSレジンTO85、軟化点=85±5℃)
*9:芳香族変性テルペン樹脂−2(ヤスハラケミカル(株)製YSレジンTO125、軟化点=125±5℃)
*10:テルペンフェノール樹脂(ヤスハラケミカル(株)製YSポリスターT160、軟化点=160±5℃)
*11:オイル(昭和シェル石油(株)製エキストラクト4号S)
*12:老化防止剤(フレキシス製サントフレックス6PPD)
*13:亜鉛華(正同化学工業(株)製酸化亜鉛3種)
*14:ステアリン酸(日油(株)製ステアリン酸YR)
*15:加硫促進剤(大内新興化学工業(株)製ノクセラーCZ−G)
*16:硫黄(鶴見化学工業(株)製金華印油入微粉硫黄)
これに対し、比較例2は、NRおよび樹脂を配合していないので、グリップ初期性能が悪化し、耐摩耗性も悪化する結果となった。
比較例3は、NRを配合していないので、グリップ初期性能が悪化し、耐摩耗性も悪化する結果となった。
比較例4は、NRの配合量が本発明で規定する下限未満であるので、グリップ初期性能が悪化し、耐摩耗性も悪化する結果となった。
比較例5は、カーボンブラックの窒素吸着比表面積(N2SA)が本発明で規定する上限を超えているので、グリップ初期性能が悪化し、耐摩耗性も悪化する結果となった。
2 サイドウォール
3 トレッド
4 カーカス層
5 ビードコア
6 ビードフィラー
7 ベルト層
8 リムクッション
Claims (4)
- 天然ゴム40〜80質量部およびジエン系ゴム(但し前記天然ゴムを除く)20〜60質量部からなるゴム成分100質量部に対し、
窒素吸着比表面積が250〜450m2/gのカーボンブラックを80〜150質量部および樹脂を30〜80質量部配合してなることを特徴とするタイヤトレッド用ゴム組成物。 - 前記ジエン系ゴムが、ガラス転移温度−35〜0℃のスチレン−ブタジエン共重合体ゴムであることを特徴とする請求項1に記載のタイヤトレッド用ゴム組成物。
- 前記樹脂が、軟化点80〜170℃のテルペン系樹脂であることを特徴とする請求項1または2に記載のタイヤトレッド用ゴム組成物。
- 請求項1〜3のいずれかに記載のタイヤトレッド用ゴム組成物をトレッドに使用した空気入りタイヤ。