JP2009532522A - ポリオキシメチレン及び高構造化カーボンブラックをベースとする導電性樹脂混合物 - Google Patents
ポリオキシメチレン及び高構造化カーボンブラックをベースとする導電性樹脂混合物 Download PDFInfo
- Publication number
- JP2009532522A JP2009532522A JP2009502823A JP2009502823A JP2009532522A JP 2009532522 A JP2009532522 A JP 2009532522A JP 2009502823 A JP2009502823 A JP 2009502823A JP 2009502823 A JP2009502823 A JP 2009502823A JP 2009532522 A JP2009532522 A JP 2009532522A
- Authority
- JP
- Japan
- Prior art keywords
- polyoxymethylene
- weight
- carbon black
- polyalkylene glycol
- metal oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
一態様においては、本発明は、ポリオキシメチレン、ポリエチレングリコール、金属酸化物、高構造化カーボンブラック、及び櫛型ポリマーを含むポリオキシメチレン混合物である。
下記の%の記載は重量基準の%を指す。本発明において用いる高構造化カーボンブラックは、275mL/100g以上の最小ジブチルフタレート吸収を有することを特徴とする。好適な高構造化カーボンブラックとしては、例えば、330mL/100gのDBP吸収を有するKetjenblack Black(登録商標)EC300J、480mL/100gのDBP吸収を有するKetjenblack Black EC-600JD(Akzo Nobel)、370mL/100gのDBP吸収を有するBrintex(登録商標)XE2(Degussa, Inc.)などのような超導電性ファーネスブラックが挙げられる。導電性ポリオキシメチレン樹脂を形成するのに用いる有用で商業的に入手できる高構造化カーボンブラックは、KETJENBLACK(登録商標)EC(Akzo Chemieの製品)である。種々の公知のカーボンブラックの等級、及びそれらの製造元の詳細な議論は、米国特許5,373,046に与えられており、ここで詳しく述べる必要はない。
R1O(R2O)n−(R3O)m−R4
(式中、R1及びR4は、水素、1〜30個の炭素原子を有するアルキル基、1〜30個の炭素原子を有するアシル基、及び1〜30個の炭素原子を有するアルキルフェニル基を表し;R2及びR3は、2〜6個の炭素原子を有する同一か又は異なるアルキレン基を表し;n及びmは、1以上であって、n+m<1000の条件を満足する整数を表す)
によって表されるポリアルキレングリコールが含まれる。本発明において用いるのに好適なポリアルキレングリコールは、10,000〜45,000、特に20,000〜40,000の平均数平均分子量を有する。ポリアルキレングリコール、例えばポリエチレングリコール、ポリプロピレングリコール、又はポリエチレングリコール−ポリプロピレングリコールブロックポリマーは、従来の方法でモノマーとしてアルキレングリコールを重縮合することによって得られる。重合モル数は、好ましくは5〜1,000の範囲、より好ましくは10〜500の範囲である。ポリアルキレングリコールの例としては、ポリエチレングリコールオレイルエーテル(5〜50のエチレンオキシド重合モル数)、ポリエチレングリコールセチルエーテル(5〜20のエチレンオキシド重合モル数)、ポリエチレングリコールステアリルエーテル(5〜30のエチレンオキシド重合モル数)、ポリエチレングリコールラウリルエーテル(5〜30のエチレンオキシド重合モル数)、ポリエチレングリコールトリデシルエーテル(5〜30のエチレンオキシド重合モル数)、ポリエチレングリコールノニルフェニルエーテル(2〜100のエチレンオキシド重合モル数)、及びポリエチレングリコールオクチルフェニルエーテル(4〜50のエチレンオキシド重合モル数)が挙げられる。ポリアルキレングリコールは、個々か又は組み合わせて用いることができる。混合物中のポリアルキレングリコールの量は、好ましくは0.5〜5重量%、特に好ましくは1〜3重量%である。好ましいポリアルキレングリコールは、ポリエチレングリコール及びポリプロピレングリコール、特に好ましくはポリエチレングリコールである。
Claims (10)
- ポリオキシメチレン、ポリアルキレングリコール、金属酸化物、高構造化粒子状カーボンブラック、及び、その1つが他の部分に対してより高い極性を有する2つの別個のタイプの部分を含む櫛型ポリマーを含む熱可塑性成形組成物。
- 重量基準で、ポリオキシメチレンのレベルが30〜98.7%であり、ポリアルキレングリコールのレベルが0.1〜10%であり、金属酸化物のレベルが0.1〜10%であり、高構造化粒子状カーボンブラックのレベルが1〜15%であり、櫛型ポリマーのレベルが0.1〜15%である、請求項1に記載の組成物。
- ポリアルキレングリコールが10,000〜45,000の平均数平均分子量を有する、請求項1に記載の組成物。
- 用いるポリアルキレングリコールがポリエチレングリコール及びポリプロピレングリコールから選択される、請求項1に記載の組成物。
- ポリアルキレングリコールが、20,000〜40,000の平均数平均分子量を有し、0.5〜5重量%の量で存在する、請求項4に記載の組成物。
- ポリアルキレングリコールが1〜3重量%の量で存在し、金属酸化物が酸化亜鉛であって0.5〜3重量%の量で存在する、請求項1に記載の組成物。
- 0.1〜5重量%の、ホルムアルデヒドスカベンジャー及び安定剤から選択される添加剤を更に含む、請求項6に記載の組成物。
- 金属酸化物が0.5〜5重量%の量で存在する、請求項1に記載の組成物。
- 100〜106Ω・cmの体積抵抗率を示す請求項1に記載の組成物からの成形物を含む、燃料システムの射出成形部品。
- 自動車燃料に対して向上した抵抗性を有し、導電性の成形物品を製造する方法であって、該方法が、重量基準で、(A)30〜98.7%のポリオキシメチレンホモポリマー又はコポリマー、(B)0.1〜10%のポリアルキレングリコール、(C)0.1〜10%の金属酸化物、(D)1%〜15%の高構造化カーボンブラック、(E)0.1〜15重量%の、疎水性基及び親水性基の両方を含む櫛型ポリマー、並びに場合によっては(F)0〜50%の、充填剤、強化材料、安定剤、滑剤、可塑剤、顔料、染料、蛍光増白剤、加工助剤、及びこれらの混合物から選択される1種類以上の添加剤を含む溶融した混合物を密閉成形型中に射出することを含み、該成形が100〜106Ω・cmの体積抵抗率を示す、上記方法。