CN1234766C - 导电聚甲醛材料及其制备方法 - Google Patents

导电聚甲醛材料及其制备方法 Download PDF

Info

Publication number
CN1234766C
CN1234766C CN 02137916 CN02137916A CN1234766C CN 1234766 C CN1234766 C CN 1234766C CN 02137916 CN02137916 CN 02137916 CN 02137916 A CN02137916 A CN 02137916A CN 1234766 C CN1234766 C CN 1234766C
Authority
CN
China
Prior art keywords
conductive
polyoxymethylene
polyformaldehyde material
conductive polyformaldehyde
carbon black
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 02137916
Other languages
English (en)
Other versions
CN1389513A (zh
Inventor
吴建业
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 02137916 priority Critical patent/CN1234766C/zh
Publication of CN1389513A publication Critical patent/CN1389513A/zh
Application granted granted Critical
Publication of CN1234766C publication Critical patent/CN1234766C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明涉及一种导电聚甲醛材料及其制备方法,所述的导电聚甲醛材料由聚甲醛、碳黑和二丁酯增塑剂组成,聚甲醛、碳黑、二丁酯的重量比为100∶25-30∶5-6。该材料的制备方法为:将配备好的导电聚甲醛材料组合物放入混拌机中加热拌匀;再由剂出机挤出造粒成导电聚甲醛材料,所述的挤出机分四段温度进行控制,进料口为60~65℃,第二节为110~120℃,第三节为140~150℃,第四节为160~170℃;挤出后,再经过水槽冷却后,经牵引机到造粒机拉成导电聚甲醛原料。

Description

导电聚甲醛材料及其制备方法
技术领域:
本发明涉及一种导电聚甲醛材料及其制备方法。
背景技术:
聚甲醛材料作为一种工程塑料已得到广泛应用,但现有聚甲醛塑料为非导电性材料,从而使其不能成为一种导电材料,得以进一步应用。
发明内容:
本发明目的在于提供一种导电聚甲醛材料,使其能作为一种导电材料得到进一步应用。
本发明的技术解决方案是用聚甲醛塑料和以炭黑导电材料为主的填充剂聚合造粒而成,成为一种具有导电性能的新的聚甲醛材料。
该导电聚甲醛材料包括聚甲醛和碳黑,聚甲醛与碳黑的重量比为100∶25-30。随着炭黑填充料的加入基体聚甲醛,使聚甲醛电阻急剧降低,达到所要求的导电率,但聚甲醛的基质受到一定的下降,例如拉伸强度、拉伸模量等受到一定的影响,此时,最好增添一定数量的增塑剂来提高导电聚甲醛材料的物理性能。增塑剂为二丁酯,聚甲醛、碳黑、二丁酯的重量比为100∶25-30∶5-6。
导电聚甲醛材料可用作诸如打火机点火装置的导电翘板,汽配导电配件及电器导电配件等。导电聚甲醛原料,可根据需要和用途,用塑料注塑机注射成所需的产品。
本发明使普通的非导电聚甲醛材料增加导电性能,既保持原聚甲醛材料特有的物理性能,同时能作为导电材料得到进一步应用。该导电材料的应用,可使诸如打火机点火装置等电器产品构造简单化,从而扩大聚甲醛材料的应用范围。
具体实施方式:
本实施例为一种导电聚甲醛材料的组成及制备简要过程。
取100公斤聚甲醛,25公斤炭黑和5公斤二丁酯放入混拌机中加热拌匀,再由剂出机挤出造粒成导电聚甲醛材料。挤出机分四段温度进行控制,进料口为60~65℃,第二节为110~120℃,第三节为140~150℃,第四节为160~170℃为宜。挤出后,再经过水槽冷却后,经牵引机到造粒机拉成导电聚甲醛原料。

Claims (2)

1、一种导电聚甲醛材料,其特征是由聚甲醛、碳黑和二丁酯增塑剂组成,聚甲醛、碳黑、二丁酯的重量比为100∶25-30∶5-6。
2、一种权利要求1所述的导电聚甲醛材料的制备方法,其特征是该方法包括以下次序的工艺步骤:将配备好的导电聚甲醛材料组合物放入混拌机中加热拌匀;再由剂出机挤出造粒成导电聚甲醛材料,所述的挤出机分四段温度进行控制,进料口为60~65℃,第二节为110~120℃℃,第三节为140~150℃,第四节为160~170℃;挤出后,再经过水槽冷却后,经牵引机到造粒机拉成导电聚甲醛原料。
CN 02137916 2002-07-04 2002-07-04 导电聚甲醛材料及其制备方法 Expired - Fee Related CN1234766C (zh)