JP2006052462A - 加工部耐食性に優れる表面処理めっき鋼板 - Google Patents
加工部耐食性に優れる表面処理めっき鋼板 Download PDFInfo
- Publication number
- JP2006052462A JP2006052462A JP2005181140A JP2005181140A JP2006052462A JP 2006052462 A JP2006052462 A JP 2006052462A JP 2005181140 A JP2005181140 A JP 2005181140A JP 2005181140 A JP2005181140 A JP 2005181140A JP 2006052462 A JP2006052462 A JP 2006052462A
- Authority
- JP
- Japan
- Prior art keywords
- mass
- corrosion resistance
- lattice
- phase
- plated steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】 鋼板の片面または両面に、Zn合金めっき層を有するめっき鋼板のめっき層が〔Al/Zn/Zn2 Mgの三元共晶組織〕の素地中に〔Mg2Si相〕と〔Al相〕及び〔Zn2Mg相〕が混在した金属組織を有し、且つ、〔Al相〕の中にブラベー格子の格子面を構成する格子方向の一方の面間隔が2.57Å以上3.15Å以下で他方の面間隔が3.64Å以上4.46Å以下である格子面を持つ金属間化合物を含有するめっき層であって、更にそのめっき層の上層に、水性樹脂(A)の固形分100質量%に対して、金属酸化物粒子(B)を5〜50質量%含有する水性組成物を塗布、乾燥することにより得られる皮膜を形成した加工部耐食性に優れる表面処理めっき鋼板。
【選択図】 図1
Description
そこで、本発明では、上記クロメート処理を行わずに樹脂系皮膜の一層処理を施しためっき鋼板の加工部耐食性を向上させることも同時に目的としている。
(4)(1)乃至(3)のいずれかに記載の金属間化合物の含有量が、1質量%以下であることを特徴とする加工部耐食性に優れる表面処理めっき鋼板。
ブラベー格子の格子面を構成する格子方向の一方の面間隔が2.57Å以上3.15Å以下、他方の面間隔が3.64Å以上4.46Å以下である格子面を持つ金属間化合物をめっき層に添加することにより加工後耐食性が向上する理由は、以下の2つの理由が考えられる。
本発明におけるめっき層の製造方法については、特に限定することなく、通常の無酸化炉方式の溶融めっき法が適用できる。下層としてNiプレめっきを施す場合も通常行われているプレめっき方法を適用すれば良い。
本発明の樹脂系皮膜層には、更に、リン酸化合物(C)を含有することが好ましい。
上記リン酸化合物(C)を含有させた場合、めっき表面にリン酸塩層を形成して不動態化させ耐食性を向上させる。
10:白錆発生なし
9:1%未満
8:1%以上3%未満
7:3%以上5%未満
6:5%以上7%未満
5:7%以上10%未満
4:10%以上15%未満
3:15%以上20%未満
2:20%以上30%未満
1:30%以上
試験結果を表1に示す。
10:白錆発生なし
9:1%未満
8:1%以上3%未満
7:3%以上5%未満
6:5%以上7%未満
5:7%以上10%未満
4:10%以上15%未満
3:15%以上20%未満
2:20%以上30%未満
1:30%以上
試験結果を表3〜8に示す。
Claims (15)
- 鋼板の片面または両面に、Al:4〜10質量%、Mg:1〜5質量%及びブラベー格子の格子面を構成する格子方向の一方の面間隔が2.57Å以上3.15Å以下で他方の面間隔が3.64Å以上4.46Å以下である格子面を持つ金属間化合物を含有し、残部がZn及び不可避的不純物より構成されるZn合金めっき層を有するめっき鋼板のめっき層が〔Al/Zn/MgZn2の三元共晶組織〕の素地中に〔Al相〕及び〔MgZn2相〕が混在した金属組織を有し、且つ、〔Al相〕の中にブラベー格子の格子面を構成する格子方向の一方の面間隔が2.57Å以上3.15Å以下で他方の面間隔が3.64Å以上4.46Å以下である格子面を持つ金属間化合物を含有するめっき層であって、更にそのめっき層の上層に、水性樹脂(A)の固形分100質量%に対して、金属酸化物粒子(B)を5〜50質量%含有する水性組成物を塗布、乾燥することにより得られる皮膜が形成されていることを特徴とする加工部耐食性に優れる表面処理めっき鋼板。
- 鋼板の片面または両面に、Al:4〜22質量%、Mg:1〜5質量%、Si:0.5質量%以下及びブラベー格子の格子面を構成する格子方向の一方の面間隔が2.57Å以上3.15Å以下で他方の面間隔が3.64Å以上4.46Å以下である格子面を持つ金属間化合物を含有し、残部がZn及び不可避的不純物より構成されるZn合金めっき層を有するめっき鋼板のめっき層が〔Al/Zn/MgZn2の三元共晶組織〕の素地中に〔Mg2 Si相〕と〔Al相〕及び〔MgZn2相〕が混在した金属組織を有し、且つ、〔Al相〕の中にブラベー格子の格子面を構成する格子方向の一方の面間隔が2.57Å以上3.15Å以下で他方の面間隔が3.64Å以上4.46Å以下である格子面を持つ金属間化合物を含有するめっき層であって、更にそのめっき層の上層に、水性樹脂(A)の固形分100質量%に対して、金属酸化物粒子(B)を5〜50質量%含有する水性組成物を塗布、乾燥することにより得られる皮膜が形成されていることを特徴とする加工部耐食性に優れる表面処理めっき鋼板。
- 請求項1乃至2のいずれかに記載の金属間化合物の結晶系が、立方晶、正方晶、斜方晶、単斜晶、六方晶のいずれかであることを特徴とする加工部耐食性に優れる表面処理めっき鋼板。
- 請求項1乃至3のいずれかに記載の金属間化合物の含有量が、1質量%以下であることを特徴とする加工部耐食性に優れる表面処理めっき鋼板。
- ブラベー格子の格子面を構成する格子方向の一方の面間隔が2.57Å以上3.15Å以下、他方の面間隔が3.64Å以上4.46Å以下である格子面を持つ金属間化合物を結晶核とし、Al相のデンドライトの一次アームが[110]方向に成長していることを特徴とする請求項1乃至4のいずれかに記載の加工部耐食性に優れる表面処理めっき鋼板。
- 水性樹脂(A)が水性ポリエステル樹脂、水性ポリウレタン樹脂、水性エポキシ樹脂、水性アクリル樹脂及び水性ポリオレフィン樹脂からなる群より選択される少なくとも1種であることを特徴とする請求項1乃至5のいずれかに記載の加工部耐食性に優れる表面処理めっき鋼板。
- 金属酸化物粒子(B)がSi、Ti、Al、Zrからなる群より選択される少なくとも1種の金属元素からなることを特徴とする請求項1乃至6のいずれかに記載の加工部耐食性に優れる表面処理めっき鋼板。
- 水性組成物が、更に、リン酸化合物(C)を水性樹脂(A)の固形分100質量%に対して0.01〜20質量%含有することを特徴とする請求項1乃至7のいずれかに記載の加工部耐食性に優れる表面処理めっき鋼板。
- 水性組成物が、更に、シランカップリング剤、架橋性ジルコニウム化合物及び架橋性チタン化合物からなる群から選択される少なくとも1種の架橋剤(D)を水性樹脂(A)の固形分100質量%に対して0.1〜50質量%含有することを特徴とする請求項1乃至8のいずれかに記載の加工部耐食性に優れる表面処理めっき鋼板。
- 水性組成物が、更に、アミノ樹脂、ポリイソシアネート化合物、そのブロック体、エポキシ化合物及びカルボジイミド化合物からなる群から選択される少なくとも1種の架橋剤(E)を水性樹脂(A)の固形分100質量%に対して0.1〜50質量%含有することを特徴とする請求項1乃至9のいずれかに記載の加工部耐食性に優れる表面処理めっき鋼板。
- 水性組成物が、更に、バナジウム化合物、タングステン化合物及びモリブデン化合物からなる群より選択される少なくとも1種の防錆剤(F)を水性樹脂(A)の固形分100質量%に対して0.01〜20質量%含有することを特徴とする請求項1乃至10のいずれかに記載の加工部耐食性に優れる表面処理めっき鋼板。
- 水性組成物が、更に、ポリフェノール化合物(G)を水性樹脂(A)の固形分100質量%に対して0.1〜50質量%含有することを特徴とする請求項1乃至11のいずれかに記載の加工部耐食性に優れる表面処理めっき鋼板。
- 水性組成物が、更に、固形潤滑剤(H)を水性樹脂(A)の固形分100質量%に対して0.1〜30質量%含有することを特徴とする請求項1乃至12のいずれかに記載の加工部耐食性に優れる表面処理めっき鋼板。
- 固形潤滑剤(H)が粒径0.1〜5.0μmのポリオレフィンワックスであることを特徴とする請求項13に記載の加工部耐食性に優れる表面処理めっき鋼板。
- 水性組成物を塗布、乾燥することにより得られる皮膜が0.1〜5g/m2の付着量で形成されていることを特徴とする請求項1乃至14のいずれかに記載の加工部耐食性に優れる表面処理めっき鋼板。