JP2005171188A - エポキシ樹脂組成物 - Google Patents
エポキシ樹脂組成物 Download PDFInfo
- Publication number
- JP2005171188A JP2005171188A JP2003416443A JP2003416443A JP2005171188A JP 2005171188 A JP2005171188 A JP 2005171188A JP 2003416443 A JP2003416443 A JP 2003416443A JP 2003416443 A JP2003416443 A JP 2003416443A JP 2005171188 A JP2005171188 A JP 2005171188A
- Authority
- JP
- Japan
- Prior art keywords
- epoxy resin
- substituted
- resin composition
- general formula
- group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】(A)エポキシ樹脂、(B)フェノール系硬化剤、及び(C)硬化促進剤を必須成分とし、(A)エポキシ樹脂が下記一般式(1)で表わされるフェノール樹脂とエピハロヒドリンを反応させることにより得られる、エポキシ当量が150〜330g/eq.、且つ一般式(1)で表わされるフェノール樹脂の水酸基当量から計算した理論値の1.00倍〜1.50倍であるエポキシ樹脂を含有してなるエポキシ樹脂組成物。
【化1】
(式中、R1、R2は互いに同一であっても異なっていてもよく、炭素数1〜10のアルキル基、置換又は無置換のフェニル基、置換又は無置換のアラルキル基である。m、nは平均値で1〜8の数であり、i、jは0〜3の整数である。)
【選択図】なし
Description
水酸基当量はJIS K0070、軟化点はJIS K7234、遊離フェノールはGC法にて測定した。
加水分解性ハロゲンは以下の電位差滴定法にて測定した。
ビーカーに試料1.0 gを精評し、ジオキサン30mlを加え、完全に溶解した。1Nアルコール性KOH 5mlをホールピペットで加えた後、ビーカーに冷却管をつけ、オイルバス中で30分間煮沸還流した。1Nアルコール性KOHは事前に1Lメスフラスコに水酸化カリウム56.1gを秤量し、95.0%エタノールで溶解し調整した。その後ビーカーを冷却し、メタノール5ml、80%アセトン水100mlを加えた。ビーカーに回転子を入れ、硝酸2mlを加え、0.01N硝酸銀標準溶液を用い、電位差滴定装置にて滴定した。次式より加水分解性ハロゲンを計算した。
但し、A:試料の滴定に要した0.01N硝酸銀標準溶液の量(ml)、B:空試験の滴定に要した0.01N硝酸銀標準溶液の量(ml)、C:ハロゲンの原子量、N:硝酸銀標準溶液の規定度、F:硝酸銀標準溶液の力価、W:サンプル量(g)。
これらの促進剤の使用量は効果促進効果が得られれば特に制限はないが、(A)エポキシ樹脂と(B)硬化剤の総量に対して0.1〜10重量%が好ましく、1〜7重量%がより好ましい。
直径50mm高さ3mmの円柱の試験片を成形し、105℃で2時間乾燥した。その後、試験片の質量を精秤した後、85℃/85%RHの恒温恒湿槽に入れた。72時間後に質量を測定し、その質量変化を測定した。
線膨張係数はTMA法(TA instruments社製 TMA 2940 Thermomechanical Analyzerを使用)にて測定した。
温度計、撹拌装置、冷却管を備えた内容量2Lの三口フラスコに、キシレン220g、硫酸130g、を仕込み、90℃に昇温して均一に溶解させた後、35%ホルムアルデヒド水溶液240gを1時間かけて滴下した。滴下終了後、90℃で5時間保持し反応を完了させ、水洗により硫酸を除去した。系内が中性になるまで水洗を繰り返した後、生成物から減圧下でキシレンを留去してキシレン-ホルムアルデヒド樹脂を得た。以後、このキシレン−ホルムアルデヒド樹脂をXF樹脂とする。
温度計、撹拌装置、冷却管を備えた内容量2Lの三口フラスコに、先に得られたXF樹脂200gにフェノール300g、p−トルエンスルホン酸0.1gを加え、100℃で2時間攪拌した。その後、ホルマリン35g、シュウ酸1.5gを加え3時間攪拌した。反応混合物をメチルイソブチルケトン500gに溶解し、65℃で中性になるまで水洗を繰り返した。次いで減圧下でメチルイソブチルケトン、フェノールを160℃、減圧下で留去して芳香族炭化水素ホルムアルデヒド樹脂変性ノボラック型フェノール樹脂を得た。水酸基当量163g/eq.、150℃における溶融粘度0.21Pa・s、軟化点84℃、遊離フェノール0.1質量%以下であった。またこの樹脂は一般式(1)においてR2=CH3、i=0、j=2、m=2.3、n=1.6であった。
製造例1においてホルムアルデヒドの量を55gに置き換えた以外は、製造例1と同様の操作を行い、芳香族炭化水素ホルムアルデヒド樹脂変性ノボラック型フェノール樹脂を得た。得られた樹脂は水酸基当量170g/eq.、150℃における溶融粘度0.62Pa・s、軟化点95℃、遊離フェノール0.1質量%以下であった。またこの樹脂は一般式(1)においてR2=CH3、i=0、j=2、m=2.9、n=2.1であった。つづいて製造例1と同様の操作を行い、エポキシ樹脂を得た。得られた樹脂はエポキシ当量249g/eq.(水酸基当量から計算した理論値は226g/eq.)、加水分解性ハロゲン500ppm、150℃における溶融粘度は0.48Pa・s、軟化点は80℃であった。
製造例1においてホルムアルデヒドの量を70g、メチルイソブチルケトン、フェノールの留去の温度を120℃に置き換えた以外は、製造例1と同様の操作を行い、芳香族炭化水素ホルムアルデヒド樹脂変性ノボラック型フェノール樹脂を得た。得られた樹脂は水酸基当量190g・/eq.、150℃における溶融粘度4.2Pa・s、軟化点109℃、遊離フェノール3.6質量%であった。またこの樹脂は一般式(1)においてR2=CH3、i=0、j=2、m=9.8、n=7.5であった。つづいて、製造例1において、エピクロロヒドリンの量を440g、イソプロピルアルコールの量を170g、48.5質量%の水酸化ナトリウム水溶液の量を70gとした以外は、製造例1と同様の操作を行い、エポキシ樹脂を得た。得られた樹脂はエポキシ当量296g/eq.(水酸基当量から計算した理論値は246g/eq.)、加水分解性ハロゲン700ppm、150℃における溶融粘度は2.4Pa・s、軟化点は97℃であった。
製造例3においてエピクロロヒドリンの量を230g、イソプロピルアルコールの量を90g、48.5質量%の水酸化ナトリウム水溶液の量を70gとした以外は、製造例1と同様の操作を行い、エポキシ樹脂を得た。得られた樹脂はエポキシ当量372g/eq.(水酸基当量から計算した理論値は246g/eq.)、加水分解性ハロゲン1100ppm、150℃における溶融粘度は5.4Pa・s、軟化点は122℃であった。
表1に示したように、エポキシ樹脂として製造例1〜4で得られたエポキシ樹脂、テトラメチルビフェノールから誘導されたエポキシ樹脂、ビフェノールとテトラメチルビフェノールから誘導されたエポキシ樹脂、ビスフェノールA型エポキシ樹脂、テトラブロモビスフェノールA型エポキシ樹脂又はオルソクレゾールノボラック樹脂から誘導されたエポキシ樹脂、エポキシ樹脂用硬化剤として一般式(1)で表わされるフェノール樹脂、フェノールアラルキル樹脂、ビフェニルフェノール樹脂、フェノール/ベンズアルデヒドノボラック型樹脂、ナフトールアラルキル樹脂、フェノールノボラック樹脂、無機充填剤としてシリカ粉末、硬化促進剤としてトリフェニルホスフィンを用い、さらにカップリング剤としてエポキシシラン、離形剤としてカルナバワックスをそれぞれ用いて、各エポキシ樹脂組成物を配合した。次いで、各配合物をミキシングロールを用いて70〜120℃の温度で5分間溶融混練した。得られた各溶融混合物は薄板状に取り出し冷却した後、粉砕して各成形材料を得た。これらの各成形材料を用い低圧トランスファー成形機で金型温度175℃、成形時間180秒で成形して、各試験片を得、180℃で8時間ポストキュアさせた。ポストキュア後の各試験片の吸湿率、ガラス転移温度、及び密着性、難燃性を試験した結果を表1及び表2に示した。さらに各成形材料により封止された模擬半導体装置の耐ハンダクラック性を試験した結果を表1及び表2に示した。またエポキシ樹脂と硬化剤の混合溶融粘度を表1及び表2に示した。
名 エピコートYX4000H,エポキシ当量:193(g/eq))
*2: B;ビフェニル型エポキシ樹脂(ジャパンエポキシレジン社商品名 エピコー
トYL6121H,エポキシ当量:172(g/eq),)
*3: C;ビスフェノールA型エポキシ樹脂(ジャパンエポキシレジン社商品名
エピコートYL6810,エポキシ当量:172(g/eq),)
*4: D;クレゾ−ルノボラック型エポキシ樹脂(ジャパンエポキシレジン社商品名
エピコート180S62,エポキシ当量:197(g/eq))
*5: E;臭素化エポキシ樹脂(日本化薬社商品名 BREN-S、エポキシ当量:385
(g/eq)、臭素含量:48%)
*6: F;フェノールアラルキル樹脂(明和化成社商品名 MEH-7800S,水酸基当
量:175(g/eq),軟化点:75(℃)
*7: G;芳香族炭化水素ホルムアルデヒド樹脂変性ノボラック型フェノール樹脂
(三菱瓦斯化学社商品名 ニカノールGLP,水酸基当量:163(g/eq),
軟化点:86(℃)
*8: H;フェノール/ベンズアルデヒドノボラック型樹脂(ジャパンエポキシレジ ン社商品名 エピキュアYLH1027,水酸基当量:150(g/eq)),軟 化点:82(℃)
*9: I;ビフェニルフェノール樹脂(明和化成社商品名 MEH-7851S,水酸基当 量:205(g/eq),軟化点:75(℃)
*10: J;ナフトールアラルキル樹脂(明和化成社商品名 MEH-7700,水酸基当量:
140(g/eq),軟化点:96(℃)
*11: K;フェノールノボラック樹脂(群栄化学社商品名 レヂトップPSM4261,水酸
基当量:103(g/eq),軟化点:85℃)
*12: 溶融シリカ粉末(龍森社商品名 RD-8)
*13: エポキシシラン(信越化学工業社商品名 KBM-403)
*14: エポキシ樹脂と硬化剤のみを混合溶融させてICI粘度計により測定。
*15: EMMI−1−66
*16: TMA法
*17: 85℃、85%RH、72時間後の吸湿率
*18: アルミピール試験
*19: 80ピンQFP16個を85℃、85%RHにおいて72時間吸湿後、260℃ハンダ浴に10秒
間浸漬し、クラックの発生した個数を求めた。
*20: UL94
Claims (10)
- (A)エポキシ樹脂、(B)フェノール系硬化剤、及び(C)硬化促進剤を必須成分とし、(A)エポキシ樹脂が下記一般式(1)で表わされるフェノール樹脂とエピハロヒドリンを反応させることにより得られる、エポキシ当量が150〜330g/eq.、且つ一般式(1)で表わされるフェノール樹脂の水酸基当量から計算した理論値の1.00倍〜1.50倍であるエポキシ樹脂を含有してなるエポキシ樹脂組成物。
- 前記(B)フェノール系硬化剤が前記一般式(1)又は下記一般式(2)で表わされるフェノール樹脂であることを特徴とする請求項1記載のエポキシ樹脂組成物。
- 前記一般式(1)で表わされるフェノール樹脂とエピハロヒドリンを反応させることにより得られるエポキシ樹脂の加水分解性ハロゲンが1000ppm以下、軟化点が50〜120℃、150℃における溶融粘度が0.9Pa・s以下である請求項1〜3のいずれか1項に記載のエポキシ樹脂組成物。
- 前記一般式(1)で表わされるフェノール樹脂の遊離フェノールが3質量%以下であることを特徴とする請求項1〜4のいずれか1項に記載のエポキシ樹脂組成物。
- 前記(A)エポキシ樹脂、(B)硬化剤の150℃における混合溶融粘度が0.9Pa・ s以下である請求項1〜5のいずれか1項に記載のエポキシ樹脂組成物。
- 前記一般式(1)で表わされるフェノール樹脂とエピハロヒドリンを反応させることにより得られるエポキシ樹脂がエポキシ樹脂全体の70質量%より多いことを特徴とする請求項1〜6のいずれか1項に記載のエポキシ樹脂組成物。
- 無機充填材として、破砕型及び/又は球状の、溶融及び/又は結晶シリカ粉末を組成物の70〜95質量%配合してなる請求項1〜7のいずれか1項に記載のエポキシ樹脂組成物。
- 難燃付与成分としてハロゲン化合物及び/又はアンチモン化合物を含まず、その硬化物がUL−94規格のV−0を満足する難燃性を有する請求項1〜8のいずれか1項に記載のエポキシ樹脂組成物。
- 請求項8及び請求項9のいずれか1項に記載のエポキシ樹脂組成物を含有する硬化性樹脂組成物を硬化してなるエポキシ樹脂硬化物。