JP2002522645A - 低温の選択的肌焼き工程 - Google Patents

低温の選択的肌焼き工程

Info

Publication number
JP2002522645A
JP2002522645A JP2000565205A JP2000565205A JP2002522645A JP 2002522645 A JP2002522645 A JP 2002522645A JP 2000565205 A JP2000565205 A JP 2000565205A JP 2000565205 A JP2000565205 A JP 2000565205A JP 2002522645 A JP2002522645 A JP 2002522645A
Authority
JP
Japan
Prior art keywords
product
carburizing
carbon
mask
alloy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
JP2000565205A
Other languages
English (en)
Other versions
JP2002522645A5 (ja
Inventor
ウイリアムズ，ピーター・シー
マークス，ステイーブン・ブイ
Original Assignee
スウエイジロク・カンパニー
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by スウエイジロク・カンパニー filed Critical スウエイジロク・カンパニー
Publication of JP2002522645A publication Critical patent/JP2002522645A/ja
Publication of JP2002522645A5 publication Critical patent/JP2002522645A5/ja
Ceased legal-status Critical Current

Abstract

(57)【要約】 低温の浸炭により、選択的に肌焼きされた鋼製品は、クロム包含のニッケル又は鉄を基礎にした合金（例えば、ステンレス鋼）から製造された本体を含み、その本体の第１の部分は第１の硬度特徴を有し、本体の第２の部分は第２の硬度特徴を有し、第２の部分は本体全体より小さく、実質的にカーバイドを含まない。低温浸炭による選択的肌焼きの一方法は、浸炭される予定の製品の表面領域上に炭素遮蔽マスクを適用すること、浸炭されるこれらの表面領域を活性化すること、カーバイドが容易に形成する温度より低い温度で、活性化された表面領域中に炭素を拡散させること、及び炭素遮蔽マスクを除去すること、の段階を含む。

Description

【発明の詳細な説明】
【０００１】 （発明の技術分野） 本発明は例えば管接合フェルールのような、ステンレス鋼及びその他の合金の
製品の加工法に関する。より具体的には、本発明は、実質的にカーバイド(carbi
des)の形成を伴わずにこれらの製品を選択的肌焼きする工程に関する。
【０００２】 （発明の背景） 周知のように、ステンレス鋼は数々の部品及び集成体に一般に使用されている
。一例は管の末端を接合するための流体接合体の一部として使用されるフェルー
ルである。ステンレス鋼が使用されなければならない程度は適用により変動する
であろう。例えば半導体及び生物工学の分野における幾つかの、高度に純粋なシ
ステムにおいては、例えば３１６Ｌのような、より低い炭素のステンレス鋼が一
般に使用される。ステンレス鋼のための数々の化学物質が使用され、そしてステ
ンレス鋼以外では、その他のクロム含有のニッケル又は鉄を基礎にした合金が知
られ、使用されている。
【０００３】 幾つかのステンレス鋼合金の一つの利点は、それらが、他の鋼合金材料よりも
硬度が比較的低い点である。フェルールのような、幾つかの適用における結果と
して、ステンレス鋼の製品又は部品には、一般にそして本明細書で、肌焼きと称
される硬化表面が提供される。肌焼きの考えは、その表面を基礎金属合金より硬
くするために、炭素又はその他の成分を増加することによりその部分の表面に材
料の比較的薄い層を形成することである。本明細書は炭素の増加による製品の肌
焼きに関連する。従って、製品は製品表面に標準となる化学物質の基礎金属の柔
軟性を伴わずに、ステンレス鋼の所望の二次成形適性をバルクで保持する。
【０００４】 ステンレス鋼合金の部品は一般に浸炭として知られた工程により肌焼きされる
。浸炭は製品の表面中に炭素原子が拡散される工程である。フェルールのような
幾つかの適用においては、本明細書では選択的肌焼きと称される、フェルールの
ある部分又は領域のみを肌焼きすることが望ましい。既知の選択的肌焼き工程は
高温で実施される。しかし、約１０００°Ｆ（５３８℃）を越える高温（ステン
レス鋼合金に対して）で実施される肌焼き工程は硬化された表面でカーバイドの
形成を促進する。
【０００５】 従って、クロム含有のニッケル又は鉄を基礎にした合金から製造された製品の
形態にあり、カーバイドの形成を伴わずに製品の全面積より少ない表面領域上を
選択的に肌焼きされる新規の製品を提供することが望まれる。カーバイドの形成
を促進しない低温における選択的肌焼きの浸炭工程を提供することが発明の更な
る目的である。
【０００６】 （発明の要約） 発明の一態様に従うと、クロム含有のニッケル又は鉄を基礎にした合金を含ん
でなる物体を特徴としてもつ製品が提供され、物体の第１の部分は、第１の硬度
特徴をもち、そして物体の第２の部分は第２の硬度特徴をもち、第２の部分は物
体全体より小さく、実質的にカーバイドを含まない。
【０００７】 本発明はまた、一態様において、製品の選択された表面部分に炭素遮蔽マスク
を配置すること、製品の非マスク表面部分を活性化すること、及び実質的にカー
バイドを含まないままで、製品の非マスク部分を浸炭すること、の段階を含む、
選択的に肌焼きされた製品を製造する方法を想定している。本発明は更に、この
ような工程により製造された製品を想定している。
【０００８】 本発明の数々のアスペクト及び利点は、付記の図面についての好ましい態様の
次の説明から、当業者には明白であろう。
【０００９】 本発明は幾つかの部品の物理的形態及び部品の配列、本明細書において詳細に
説明され、本明細書の一部を形成している付記の図面で示されるであろう好まし
い態様及び方法を採ることができる。
【００１０】 （好ましい態様の詳細な説明） 図１には、通常のフェルール１０が示されている。このフェルール１０は本発
明とともに使用することができる無数の多数の製品及び部品の一例に過ぎない。
発明は本明細書では、３１６タイプのステンレス鋼のフェルールについて説明さ
れているが、これらの説明は例示的本質を意図され、制約的意味で解釈してはな
らない。本発明は肌焼きされることができるクロム含有のニッケル又は鉄を基礎
にした合金から製造されたあらゆる部品又は製品を伴う適用を見いだす。
【００１１】 更に、本明細書においては、好ましい態様は特に、ステンレス鋼合金から製造
された製品について説明されているが、これらの説明は例示的な本質のもので、
制約的意味で解釈してはならない。本発明は、幾つかの例を挙げると、それらに
制約はされないが、合金３１６、合金３１６Ｌ及び合金３０４ステンレス鋼、合
金６００、合金Ｃ−２７６及び合金２０Ｃｂを含む、数々の種類のクロム含有の
鉄又はニッケルを基礎にした合金化学物質に適用できる。
【００１２】 フェルール１０は図１において、部分的断面図のみで示されている。この具体
的なフェルールは２個フェルールシステムの一部として使用される後方フェルー
ルである。これらのフェルール及び、フェルールの幾何構造を含むフェルールシ
ステムは周知で、それらの明細全体が引用により本明細書に完全に取り込まれて
いる、米国特許第４，９１５，４２７号及び３，１０３，３７３号に詳細に説明
されている。
【００１３】 フェルール１０はテーパーされたノーズ部分１２、中央の本体１４及び後部の
駆動表面１６を特徴としてもつ。管接合体において、後部駆動表面１６は、前方
のフェルール（図示されていない）の後方カムロックの口部中にフェルール１０
のノーズを軸方向に駆動するナットの壁と噛み合う。この動作はなかでも、フェ
ルール１０のノーズ部分１２を半径方向に内側に駆動させて、管の末端をグリッ
プさせる。図１に示されたフェルール１０の幾何構造は、例示的本質のものであ
り、具体的なフェルールシステムに応じて実質的に変動するであろう。フェルー
ル１０はまた、１個のフェルールのシステム中でも使用することができ、その場
合は、ノーズ部分１２が前方の接合素子のカムロック口部中に駆動されるであろ
う。
【００１４】 フェルール１０に対して一般的な、しかし独占的ではない材料は３１６ステン
レス鋼合金である。フェルールを管の末端の増強されたグリップ中に駆動するこ
とができるために、幾つかの適用において、フェルール１０を肌焼きすることが
望ましい。更に、幾つかの適用においては、フェルール１０の一部のみを肌焼き
することも望ましい。例えば、ノーズ部分１２が選択的に肌焼きされる場合は、
多くの場合、フェルールシステムの全体的性能が改善される可能性がある。
【００１５】 本明細書で使用される肌焼きは、フェルール１０のために使用される基礎金属
に比較して表面硬度を増加させるために、フェルール１０の表面に比較的薄い浸
炭層を提供することを意味する。浸炭はフェルール１０を肌焼きするための好ま
しい方法であり、本発明の一アスペクトに従うと、全体部分より小さい、選択さ
れた領域上にフェルール１０の選択的肌焼きを可能にする新規の浸炭工程が使用
される。しかし、全体部分を肌焼きすることが所望される場合にも、本発明の浸
炭工程を使用することはできる。
【００１６】 浸炭は一般に、炭素原子が溶液の基礎合金中に拡散される工程である。炭素原
子をステンレス鋼中に拡散させるためには、酸化クロム層を除去しなければなら
ない。この段階は、一般に、活性化又は脱不動態化として知られている。酸化物
の層は炭素原子に実質的なバリヤーを提供するので、表面を活性化しなければな
らない。一旦活性化させると、表面を、高温における拡散により浸炭させること
ができる。
【００１７】 拡散工程は、例えば１０００°Ｆ（５３８℃）を越える（ステンレス鋼合金に
対して）高温で浸炭を実施することにより促進させることができる。しかし、こ
のような高温の拡散は炭素／クロム分子であるカーバイドを容易に、早急に生成
する可能性がある。カーバイドは場合によっては、基礎合金のクロムを還元させ
る傾向がある。
【００１８】 カーバイドの形成を抑制又は実質的に排斥するために、本発明は、カーバイド
形成促進温度より低い温度で実施される選択的肌焼きのための浸炭工程を想定し
ている。例えば３１６ステンレス鋼のような数々のクロム含有合金に対して、１
０００°Ｆ（５３８℃）を越える浸炭温度では、カーバイドが容易に形成する傾
向がある。従って、本発明の選択的肌焼き工程はステンレス鋼合金に対しては、
約１０００°Ｆ（５３８℃）より低い温度で実施される。浸炭が起こる期間もま
たカーバイドの形成に影響を与える。１０００°Ｆ（５３８℃）より低い温度に
おいても、基礎金属が十分長い期間、炭素源にさらされると、カーバイドを形成
することができる。発明のもう一つのアスペクトに従うと、浸炭はカーバイド形
成促進温度より下で、カーバイドを形成させるよりも短い期間、実施される。従
って、発明は選択的肌焼き工程の期間中、カーバイドの形成を実質的に抑制する
時間−温度プロファイルを想定している。
【００１９】 このような時間−温度プロファイルの一例として、カーバイドは１時間以内の
早さで、１０００°Ｆ（５３８℃）を越える温度で３１６ステンレス鋼において
容易に形成する。しかし、この温度より下、例えば８００〜９５０°Ｆ（４２７
〜５１０℃）の範囲では、特に、より低温の範囲では、カーバイドは約１週間以
上に至るまで形成しないであろう。これは一例に過ぎず、カーバイド形成を抑制
するためのあらゆる具体的な浸炭工程に使用された具体的な時間−温度プロファ
イルは、必ずしもそれらに制約はされないが、浸炭温度及び基礎金属の合金化学
を含む数々のファクターに左右されるであろう。
【００２０】 図２Ａ〜２Ｄは代表的な方法で（そして部分的断面図で）、ステンレス鋼製品
、本例ではフェルールの選択的肌焼きのための、発明に従う好ましい浸炭工程の
種々の段階を表す。その工程の概括的段階は、１）浸炭されない予定の製品の表
面領域上に炭素遮蔽マスクを適用すること、２）浸炭される表面領域を活性化す
ること、３）活性化された表面領域に炭素を拡散させること、及び４）炭素遮蔽
マスクを取り除くこと、である。段階１）は少なくとも２種類の方法で実施する
ことができ、第１は全体の部分にマスクを適用し、次に浸炭される表面領域に重
なる部分を除去する（例えばエッチングにより）こと、そして第２は炭素遮蔽マ
スクを選択的にのみ適用すること、である。
【００２１】 図２Ａにおいては、製品１０は全表面領域に炭素遮蔽マスク２０を適用されて
いる。図２Ａ〜２Ｄにおいては、様々な層のそれぞれの厚さのような相対的ディ
メンションは表示及び説明の明瞭性及び容易性のために著しく誇張されているこ
とに注意することが重要である。
【００２２】 本態様においては、炭素遮蔽マスク２０は、あらゆる適切な方法、この場合に
は電気メッキにより製品に適用することができる銅から形成されている。
【００２３】 図２Ｂにおいては、次の段階の結果が示されている。銅のマスク２０の部分、
本例ではノーズ領域２２が化学エッチングによるように除去されて、基礎金属を
露出した。エッチング工程はあらゆる数の方法で実施することができる。図示さ
れた例では、ノーズ部分２２は容易にアクセスされ、銅はノーズ部分２２を硝酸
浴中に単に浸漬することによりエッチングすることができる。当該酸は部品１０
の基礎金属を攻撃せずに銅を除去する。
【００２４】 銅が選択的に除去され、製品１０が再度大気中に置かれるとすぐに、露出され
た非マスク部分２２は不動態化又は不活性化され、酸化クロム層を形成する。こ
の不動態化は実質的に大気への露出に伴って瞬時であり、あらゆるステンレス鋼
で起こる。非マスク領域２２上に形成する不動態化酸化物層は炭素遮蔽層である
。非マスクのノーズ部分２２を浸炭するためには非マスク領域２２を活性化させ
る必要がある。
【００２５】 図２Ｃにおいては、鉄の層又はプレート２４が製品１０上に電気メッキされた
、次の段階が示されている。鉄のプレート２４は銅のマスク２０及び非マスク領
域２２の両方に適用される。鉄の層２４は例えば、通常の電気メッキ工程により
適用される。
【００２６】 鉄の層２４は幾つかの重要な機能を果す。第１にメッキ工程が非マスク領域２
２を活性化させる。更なる活性化段階を必要としない。銅の層もまた下にある基
礎金属を活性化するが、銅が炭素忌避層又は遮蔽物であるので、この利点は、浸
炭期間中に使用することはできないことに注目される。第２に、鉄は下にある基
礎金属に炭素原子を容易に通過させることが発見された。言い換えれば、鉄は炭
素遮蔽層ではなく、むしろ本質的に炭素に透過性である。更に、銅の層２２に重
なる鉄は銅に対する遮蔽シールド又はマスクとして働く。
【００２７】 発明の一態様において、炭素原子は製品１０を一酸化炭素（ＣＯ）ガスにさら
すことにより製品１０中に拡散される。炭素原子は、鉄の層２４を通して非マス
クの低炭素基礎金属領域２２中に容易に拡散する。拡散に対する温度はカーバイ
ドの容易な形成を抑制するためには１０００°Ｆ（５３８℃）より下に維持され
る。炭素原子は鉄の層２４を通って、基礎金属を含む固溶体中に拡散する。発明
の本アスペクトに従うと、気体の浸炭を許す選択的肌焼き工程が提供されている
。本態様においては、浸炭ガス混合物は１０００°Ｆ（５３８℃）未満、例えば
８００°Ｆ（４２７℃）ないし９８０°Ｆ（５２７℃）の範囲の温度で、１気圧
において、一酸化炭素及び窒素を含む。拡散工程は製品中に拡散される炭素の量
に応じてこれらのより低い拡散温度で、２週間位までの長さかかる可能性がある
。
【００２８】 当業者は、拡散速度が温度に依存するので、拡散時間が肌焼き表面の深度を決
定するであろうことを理解するであろう。時間もまた、カーバイドの温度依存性
の形成に関連しているので、使用されている具体的な合金に対してカーバイドの
形成を阻止する時間−温度プロファイルを使用して、所望の焼き肌の深度を達成
するためには、浸炭拡散工程を制御しなければならない。例えば、カーバイドの
形成は時間と温度の関数であるので、深い焼き肌が所望される場合には、カーバ
イドの形成を阻止するために、時間が経過するに従って拡散工程期間に温度を低
下させることが必要かも知れない。拡散温度が低いほど、カーバイド形成を伴わ
ずに、拡散工程がより長く継続することができる。その欠点は、所望の拡散深度
に到達するためにかかる可能性がある追加時間である。しかし、多数の場合、カ
ーバイドが容易に形成する温度より下、例えば３１６ステンレス鋼に対しては１
０００°Ｆ（５３８℃）より下に浸炭温度を維持することにより、製品はカーバ
イドの形成を伴わずに、十分な深度に肌焼きさせることができる。
【００２９】 図２Ｄは浸炭後の最終結果を示している。炭素原子が非マスク部分２２、この
場合はフェルールのノーズ中に拡散された後に、製品の残りの部分より硬い、製
品１０の選択的肌焼き部分３０が形成された。硬化部分３０の相対的厚さは、図
では、明瞭化のために誇張されており、実際的には、例えば０．００１ないし０
．００３インチ（０．０２５４ないし０．０７６２ｍｍ）以下だけの可能性があ
る。浸炭部分の厚さは最終製品の所望の機械的特性及び機能的条件に左右される
であろう。
【００３０】 図２Ｄにおいては、拡散工程が完了後に、鉄の層２４及び銅マスク２０が例え
ばエッチングにより除去された。これらの層の除去は製品１０の不動態化を許し
て、肌焼きノーズ１２の表面領域を含む酸化クロム層を提供する。
【００３１】 好ましい工程に対する様々な代替工程が、当業者に容易に明白であろう。例え
ば、再度電気メッキにより適用される、銀を含む、銅以外の他の金属を炭素マス
クのために使用することができる。幾つかの適用においては、金もまた適したマ
スク金属の可能性がある。その他の金属もまた、適した炭素遮蔽マスク体として
働く。
【００３２】 前記の好ましい工程において、浸炭は例えば、０．５ないし１００％の一酸化
炭素、残りは窒素を含む、１気圧の窒素ガス混合物により実施することができる
。浸炭拡散はカーバイド形成を伴わずに、８００〜９８０°Ｆ（４２７〜５２７
℃）の温度プロファイル範囲で約２週間にわたり起こる可能性がある。
【００３３】 選択的肌焼きのための代替的工程は次のようである。第１に、炭素遮蔽マスク
を肌焼きされない予定の領域上に、製品上に配置する。この段階は本明細書中で
製品に銅マスクを適用するために前記に説明されたものと同様にすることができ
る。非マスク部分を活性化させるために、製品を、炭素遮蔽マスクの攻撃及び移
動を最少にするか又は許容できる程度に制約する時間歴の間、１気圧で高温で、
塩化水素（ＨＣｌ）及び窒素のようなハロゲン化水素ガス混合物にさらす。ＨＣ
ｌは例えば銅マスクを攻撃するであろう。時間とともに、銅は製品から移動する
傾向があり、ＨＣｌガスにより運び去られるであろう。しかし、ＨＣｌは非常に
有効な活性化ガスであるので、活性化時間は短いであろう。従って、製品をＨＣ
ｌガスにさらす時間は銅マスク体の喪失を抑制するのに十分短時間に維持しなけ
ればならない。十分な活性化時間を許すことが要求される場合は、より厚い銅マ
スクを適用することもできる。適した代表的温度−時間プロファイルは、１気圧
で、残りは窒素を伴って１７〜１００％の塩化水素の活性化ガス混合物を使用し
て、約１時間、６００〜６５０°Ｆ（３１５〜３４３℃）である。その他の活性
化ガスは、それに制約はされないが、フッ化水素（ＨＦ）であり、選択された活
性化ガスは一部、使用される時間−温度プロファイルを決定するであろう。これ
らの代替的活性化工程は、活性化−浸炭室が、浸炭される部品の次のバッチが加
工される前に、銅の痕跡をこすり落とす必要があるであろうため、余り好ましく
はない。
【００３４】 製品をガスにさらすことを伴う本明細書に説明された様々な工程は、当業者に
は周知のように、ピット炉（pit furnace）のような、通常の、一般に入手でき
る装置により実施することができる。
【００３５】 代替的工程において、活性化段階が完了後に、活性化ガスはガス室から追い出
されるが、活性化された製品の表面は大気にさらさない、さもないと、製品は即
座に再不動態化されるであろう。活性化ガスは浸炭ガス混合物と室内で置き換わ
る。本例では、浸炭は１気圧において、一酸化炭素、水素及び窒素のガス混合物
を使用して実施される。本例においては、鉄の層なしでは、一酸化炭素ガスは活
性化領域を再不動態化させる傾向をもつであろうため、水素を浸炭ガス混合物に
添加する。代表的ガス混合物は、１気圧において、０．５〜６０容量％の一酸化
炭素及び１０〜５０容量％の水素、残りは窒素である。再度、浸炭拡散は時間−
温度プロファイル内で、そして特に、約１週間（再度、時間のパラメーターは要
求される浸炭深度に応じて変動するであろう）、基礎金属合金において、カーバ
イドの容易な形成を許すか又は促進するであろう温度より下の温度で（例えばス
テンレス鋼合金に対しては１０００°Ｆ（５３８℃）より下、例えば７５０〜９
５０°Ｆ（３９９〜５１０℃）の範囲）で実施される。
【００３６】 浸炭後に、本明細書の最初の方で記載されたように、銅のマスクを除去し、製
品は大気にさらされると不動態化される。
【００３７】 発明は好ましい態様に関して説明されてきた。本明細書を読み、理解すると、
他の人々に、修正及び変更が明らかに浮かぶであろう。それらが付記の請求項又
はそれらの同等物の範囲内に入る限り、それらすべての修正及び変更を含むこと
が意図されている。
【図面の簡単な説明】
【図１】 通常のフェルールの縦断面の立面図である。
【図２Ａ〜２Ｄ】 低温浸炭を使用する選択的肌焼き工程を図面で示している。
───────────────────────────────────────────────────── フロントページの続き (81)指定国 ＥＰ(ＡＴ，ＢＥ，ＣＨ，ＣＹ， ＤＥ，ＤＫ，ＥＳ，ＦＩ，ＦＲ，ＧＢ，ＧＲ，ＩＥ，Ｉ Ｔ，ＬＵ，ＭＣ，ＮＬ，ＰＴ，ＳＥ)，ＯＡ(ＢＦ，ＢＪ ，ＣＦ，ＣＧ，ＣＩ，ＣＭ，ＧＡ，ＧＮ，ＧＷ，ＭＬ， ＭＲ，ＮＥ，ＳＮ，ＴＤ，ＴＧ)，ＡＰ(ＧＨ，ＧＭ，Ｋ Ｅ，ＬＳ，ＭＷ，ＳＤ，ＳＬ，ＳＺ，ＵＧ，ＺＷ)，Ｅ Ａ(ＡＭ，ＡＺ，ＢＹ，ＫＧ，ＫＺ，ＭＤ，ＲＵ，ＴＪ ，ＴＭ)，ＡＥ，ＡＬ，ＡＭ，ＡＴ，ＡＵ，ＡＺ，ＢＡ ，ＢＢ，ＢＧ，ＢＲ，ＢＹ，ＣＡ，ＣＨ，ＣＮ，ＣＵ， ＣＺ，ＤＥ，ＤＫ，ＥＥ，ＥＳ，ＦＩ，ＧＢ，ＧＤ，Ｇ Ｅ，ＧＨ，ＧＭ，ＨＲ，ＨＵ，ＩＤ，ＩＬ，ＩＮ，ＩＳ ，ＪＰ，ＫＥ，ＫＧ，ＫＰ，ＫＲ，ＫＺ，ＬＣ，ＬＫ， ＬＲ，ＬＳ，ＬＴ，ＬＵ，ＬＶ，ＭＤ，ＭＧ，ＭＫ，Ｍ Ｎ，ＭＷ，ＭＸ，ＮＯ，ＮＺ，ＰＬ，ＰＴ，ＲＯ，ＲＵ ，ＳＤ，ＳＥ，ＳＧ，ＳＩ，ＳＫ，ＳＬ，ＴＪ，ＴＭ， ＴＲ，ＴＴ，ＵＡ，ＵＧ，ＵＳ，ＵＺ，ＶＮ，ＹＵ，Ｚ Ａ，ＺＷ

Claims (27)

    【特許請求の範囲】
  1. 【請求項１】 金属合金を含んでなる物体、 第１の硬度特徴をもつ前記物体の第１の部分、及び 第２の硬度特徴をもつ前記物体の第２の部分を含み、 前記第２の部分が物体全体より小さく、実質的にカーバイドを含まない製品。
  2. 【請求項２】 前記物体が、実質的にカーバイドを含まない、浸炭表面領域
    を含んでなる前記第２の部分と、概括的に均質なクロム含有合金を含んでなる、
    請求項１の製品。
  3. 【請求項３】 前記第２の部分が、物体の選択された部位に浸炭領域として
    形成される、請求項１の製品。
  4. 【請求項４】 前記合金がクロム含有の鉄又はニッケルを基礎にした合金を
    含んでなる、請求項１の製品。
  5. 【請求項５】 前記合金がステンレス鋼を含んでなる、請求項４の製品。
  6. 【請求項６】 前記第２の部分が、前記第１の部分より硬い部分を製造する
    ための、前記物体の選択された領域上の炭素含浸表面を含んでなる、請求項１の
    製品。
  7. 【請求項７】 前記第２の部分が実質的にカーバイドを含まない、請求項６
    の製品。
  8. 【請求項８】 前記物体がフェルールである請求項１の製品。
  9. 【請求項９】 クロム含有合金を含んでなる物体、 第１の硬度特徴をもつ前記物体の第１の部分、及び 物体全体よりも小さい、前記物体の第２の部分を含み、前記第２の部分が前記
    第１の部分に比較して炭素硬化され、実質的にカーバイドを含まない製品。
  10. 【請求項１０】 前記合金がクロム含有の鉄又はニッケルを基礎にした合金
    を含んでなる、請求項９の製品。
  11. 【請求項１１】 前記第２の部分が、物体の選択された部分上の浸炭領域を
    含んでなる、請求項９の製品。
  12. 【請求項１２】 クロム含有製品を選択的に浸炭するための方法であって、 製品の選択された表面部分上に炭素遮蔽マスクを配置すること、 製品の非マスク表面部分を活性化すること、及び 実質的にカーバイドを含まない製品の前記非マスク部分を浸炭すること、 を含んでなる方法。
  13. 【請求項１３】 前記マスクを配置する前記段階が、 製品全体上に炭素遮蔽材料を配置すること、及び 前記遮蔽材料の部分を選択的に除去すること、 の段階を含んでなる、請求項１２の方法。
  14. 【請求項１４】 材料を配置する前記段階が、製品の表面に銅プレートを適
    用することを含んでなる、請求項１３の方法。
  15. 【請求項１５】 前記銅プレートが選択的に除去される、請求項１４の方法
    。
  16. 【請求項１６】 前記活性化段階が少なくとも前記非マスク領域上で製品上
    に金属を電気メッキすることを含んでなる、請求項１２の方法。
  17. 【請求項１７】 前記金属が製品全体上に適用された鉄プレートを含んでな
    る、請求項１６の方法。
  18. 【請求項１８】 前記活性化段階が、高温のハロゲン化水素ガスに前記非マ
    スク部分をさらすことを含んでなる、請求項１２の方法。
  19. 【請求項１９】 前記浸炭段階が、カーバイドが容易に形成する温度より下
    の高温で、水素含有浸炭ガスに、前記活性化部分をさらすことを含んでなる、請
    求項１８の方法。
  20. 【請求項２０】 前記浸炭段階が、カーバイドが容易に形成する温度より下
    の高温の浸炭ガスに前記活性化部分をさらすことを含んでなる、請求項１２の方
    法。
  21. 【請求項２１】 前記マスクが、銅を電気メッキすることにより適用され、
    前記活性化が電気メッキされた鉄により実施される、請求項１２の方法。
  22. 【請求項２２】 前記浸炭段階が、ステンレス鋼合金に対して約１０００°
    Ｆ（５３８℃）を越えない選択された温度範囲で、選択された温度範囲における
    カーバイドの形成に要されるよりも短い時間、約１大気圧で一酸化炭素及び窒素
    のガス混合物により実施される請求項１２の方法。
  23. 【請求項２３】 次の工程、 製品の選択された表面部分上に炭素遮蔽マスクを配置すること、 製品の非マスク表面部分を活性化すること、 カーバイドの形成を実質的に抑制する時間−温度プロファイルを使用して、製
    品の前記非マスク部分を浸炭すること、 により製造された製品。
  24. 【請求項２４】 前記浸炭段階後に、前記マスクを除去する段階を含んでな
    る、請求項２３の工程。
  25. 【請求項２５】 前記浸炭段階後に、前記マスクを除去する段階を含んでな
    る、請求項１２の方法。
  26. 【請求項２６】 炭素遮蔽マスクを配置する段階が、製品の選択された部分
    を銅で電気メッキする段階を含んでなる、請求項１２の方法。
  27. 【請求項２７】 前記浸炭段階が、カーバイドの形成を実質的に抑制する時
    間−温度プロファイルを使用して実施される、請求項１２の方法。
JP2000565205A 1998-08-12 1999-08-12 低温の選択的肌焼き工程 Ceased JP2002522645A (ja)