CN1991227B - 一种低渗透率的家用空调软管 - Google Patents
一种低渗透率的家用空调软管 Download PDFInfo
- Publication number
- CN1991227B CN1991227B CN200510135490A CN200510135490A CN1991227B CN 1991227 B CN1991227 B CN 1991227B CN 200510135490 A CN200510135490 A CN 200510135490A CN 200510135490 A CN200510135490 A CN 200510135490A CN 1991227 B CN1991227 B CN 1991227B
- Authority
- CN
- China
- Prior art keywords
- carbon black
- glue
- screen layer
- interior
- nylon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明旨在提供一种的渗透率低的家用空调软管及生产方法，包括内尼龙屏蔽层，内胶层，中尼龙屏蔽层，中胶层，编织层，外胶层六部分，内、中胶层由氯化丁基橡胶：40-45％、氧化镁：3.5-4.5％、防老剂RD：0.6-1.0％硬脂酸：0.4-0.6％、碳黑：30-40％、轻质碳酸钙：15-20％、氧化锌：1.5-2.0％、硫磺：0.6-0.9％、促进剂：0.6-1.0％制成，胶层由三元乙丙橡胶：35-40％、氯丁橡胶：10-12％、氧化锌：2.0-2.5％、氧化镁：0.4-0.5％、硬脂酸：0.4-0.6％、酚醛树脂：0.4-0.6％、碳黑：36-45％、石蜡油：5.0-6.5％、硫化剂S：0.2-0.4％、促进剂：0.655-0.915％制成，该软管渗透率低、使用寿命长，使用效果好。
Description
技术领域
本发明涉及一种家用空调设备，尤其是一种家用空调用软管，具体地说是一种制冷剂传输软管。
背景技术
现有的空调用制冷剂传输软管结构为尼龙屏蔽层，内胶层，编织层，外胶层四部分或内胶层，屏蔽层，中胶层，编织层，外胶层五部分，其胶层以氯化丁基橡胶为主要原料混炼制成，但在混炼中主要原料的配比，及促进剂、碳黑类型及其它辅助剂的类型剂配比影响着胶层的抗疲劳，现有产品受上述因素及加工工艺的影响，使用寿命短，导致制冷剂R-134a渗透量大，浪费严重，污染环境。
发明内容
本发明旨在提供一种渗透率低、使用寿命长，使用效果好的体家用空调制冷剂传输软管。
本发明的技术解决方案是：
一种渗透率低的家用空调软管，其特征是：由内尼龙屏蔽层，内胶层，中尼龙屏蔽层，中胶层，编织层，外胶层六部分。
所述的内、中胶层由下列重量成分的原料制成：
氯化丁基橡胶 40-45％
氧化镁 3.5-4.5％
防老剂RD 0.6-1.0％
硬脂酸 0.4-0.6％
碳黑 30-40％
轻质碳酸钙 15-20％
氧化锌 1.5-2.0％
硫磺 0.6-0.9％
促进剂 0.6-1.0％
所述的碳黑包括碳黑N550、碳黑N660，其中，
碳黑N550 6.0-10.0％
碳黑N660 24.0-28.0％
所述的促进剂包括促进剂DM、促进剂TMTD；
所述的外胶层由下列重量成分的原料制成：
三元乙丙橡胶 35-40％
氯丁橡胶 10-12％
氧化锌 2.0-2.5％
氧化镁 0.4-0.5％
硬脂酸 0.4-0.6％
酚醛树脂 0.4-0.6％
碳黑 36-45％
石蜡油 5.0-6.5％
硫化剂S 0.2-0.4％
促进剂 0.655-0.915％
所述的碳黑包括碳黑N550、碳黑N660，其中，
碳黑N550 20-25％
碳黑N660 16-20％
所述的促进剂为促进剂DM、促进剂TMTD、促进剂DTDM，其中，
促进剂 0.5-0.65％
促进剂TMTD 0.005-0.015％
促进剂DTDM 0.15-0.25％
一种的渗透率低的家用空调软管的生产方法，包括下列步骤：
(1)内、中胶层混炼压出：将氯化丁基橡胶、氧化镁、防老剂RD、硬脂酸进行加压密炼，然后将碳黑N550、碳黑N660、轻质碳酸钙加入进行密炼，然后将混练胶排出，在开炼机上加入氧化锌、硫磺、促进剂DM、促进剂TMTD进行混炼，然后将胶料压出。
(2)内、中尼龙屏蔽层压出：将尼龙树脂加入尼龙挤出机中挤出。
(3)外胶层混炼压出：将三元乙丙橡胶、氯丁橡胶、氧化锌、氧化镁、硬脂酸、酚醛树脂、防老剂丁进行加压密炼，然后将碳黑N550、碳黑N660、石蜡油加入进行密炼，然后将混练胶排出，在开炼机上加入硫化剂S、促进剂DM、促进剂DTDM、促进剂TMTD进行混炼，然后将胶料压出。
(4)将尼龙树脂在挤出机挤出后，将步骤(1)得到的内胶在挤出机挤出包覆在内尼龙屏蔽层上后，再将尼龙树脂挤出包覆在内胶上，将步骤(1)得到的内胶在挤出机挤出包覆在内中尼龙屏蔽层上后，进行编织，然后将步骤(3)得到的外胶包覆在编织层上，经硫化处理后脱芯。
如上所述的低渗透率的家用空调软管的生产方法，内、中尼龙屏蔽层压出，其内、中尼龙屏蔽层的厚度为0.18mm；混炼时，温度升到70℃时，减压一次，温度升到80℃时，减压一次，温度升到100℃时，提上顶栓排胶，硫化时蒸汽压力为0.45MPa，硫化温度为150±2℃，硫化时间为46分钟。
具体实施方式
下面结合实例说明该发明的具体实施方式：
实施例1：一种渗透率低的家用空调软管，由内尼龙屏蔽层，内胶层，中尼龙屏蔽层，中胶层，编织层，外胶层六部分，
内、中胶层由下列重量成分的原料制成：
氯化丁基橡胶 43％
氧化镁 3.5％
防老剂RD 0.8％
碳黑N550 7.0％
碳黑N660 26.0％
硬脂酸 0.4％
轻质碳酸钙 16％
氧化锌 1.6％
硫磺 0.8％
促进剂DM 0.45％
促进剂TMTD 0.45％
外胶层由下列重量成分的原料制成：
三元乙丙橡胶 37％
氯丁橡胶 11％
氧化锌 2.3％
氧化镁 0.45％
硬脂酸 0.46％
酚醛树脂 0.52％
碳黑N550 22.35％
碳黑N660 19％
石蜡油 5.8％
硫化剂S 0.26％
促进剂DM 0.6％
促进剂TMTD 0.01％
促进剂DTDM 0.25％
一种的渗透率低的家用空调软管的生产方法，包括下列步骤：
(1)内、中胶层混炼压出：将氯化丁基橡胶、氧化镁、防老剂RD、硬脂酸进行加压密炼，然后将碳黑N550、碳黑N660、轻质碳酸钙加入进行密炼，然后将混练胶排出，在开炼机上加入氧化锌、硫磺、促进剂DM、促进剂TMTD进行混炼，然后将胶料压出。
(2)内、中尼龙屏蔽层压出：将尼龙树脂加入尼龙挤出机中挤出；
(3)外胶层混炼压出：将三元乙丙橡胶、氯丁橡胶、氧化锌、氧化镁、硬脂酸、酚醛树脂、防老剂丁进行加压密炼，然后将碳黑N550、碳黑N660、石蜡油加入进行密炼，然后将混练胶排出，在开炼机上加入硫化剂S、促进剂DM、促进剂DTDM、促进剂TMTD进行混炼，然后将胶料压出；
(4)将尼龙树脂在挤出机挤出后，将步骤(1)得到的内胶在挤出机挤出包覆在内尼龙屏蔽层上后，再将尼龙树脂挤出包覆在内胶上，将步骤(1)得到的内胶在挤出机挤出包覆在内、中尼龙屏蔽层上后，进行编织，然后将步骤(3)得到的外胶包覆在编织层上，经硫化处理后脱芯。
如上所述的低渗透率的家用空调软管的生产方法，内、中尼龙屏蔽层压出，其内、中尼龙屏蔽层的厚度为0.16mm；混炼时，温度升到70℃时，减压一次，温度升到80℃时，减压一次，温度升到100℃时，提上顶栓排胶，硫化时蒸汽压力为0.45MPa，硫化温度为150±2℃，硫化时间为50分钟。
实施例2：一种渗透率低的家用空调软管，由内尼龙屏蔽层，内胶层，中尼龙屏蔽层，中胶层，编织层，外胶层六部分。
内、中胶层由下列重量成分的原料制成：
氯化丁基橡胶 41％
氧化镁 3.8％
防老剂RD 0.6％
硬脂酸 0.55％
碳黑N550 7.65％
碳黑N660 25％
轻质碳酸钙 18％
氧化锌 1.7％
硫磺 0.7％
促进剂DM 0.45％
促进剂TMTD 0.55％
外胶层由下列重量成分的原料制成：
三元乙丙橡胶 36％
氯丁橡胶 11.5％
氧化锌 2.2％
氧化镁 0.42％
硬脂酸 0.47％
酚醛树脂 0.52％
碳黑N550 23％
碳黑N660 19％
石蜡油 5.7％
硫化剂S 0.32％
促进剂DM 0.64％
促进剂TMTD 0.01％
促进剂DTDM 0.22％
实施例3：一种渗透率低的家用空调软管，由内尼龙屏蔽层，内胶层，中尼龙屏蔽层，中胶层，编织层，外胶层六部分。
内、中胶层由下列重量成分的原料制成：
氯化丁基橡胶 42.5％
氧化镁 4.1％
防老剂RD 0.66％
硬脂酸 0.47％
碳黑N550 7.0％
碳黑N660 26.75％
轻质碳酸钙 15.3％
氧化锌 1.55％
硫磺 0.72％
促进剂DM 0.47％
促进剂TMTD 0.48％
外胶层由下列重量成分的原料制成：
三元乙丙橡胶 39％
氯丁橡胶 10.2％
氧化锌 2.35％
氧化镁 0.47％
硬脂酸 0.52％
酚醛树脂 0.55％
碳黑N550 23.4％
碳黑N660 17％
石蜡油 5.4％
硫化剂S 0.23％
促进剂DM 0.64％
促进剂TMTD 0.01％
促进剂DTDM 0.23％
一种的渗透率低的家用空调软管的生产方法，包括下列步骤：
(1)内、中胶层混炼压出：将氯化丁基橡胶、氧化镁、防老剂RD、硬脂酸进行加压密炼，然后将碳黑N550、碳黑N660、轻质碳酸钙加入进行密炼，然后将混练胶排出，在开炼机上加入氧化锌、硫磺、促进剂DM、促进剂TMTD进行混炼，然后将胶料压出。
(2)内、中尼龙屏蔽层压出：将尼龙树脂加入尼龙挤出机中挤出。
(3)外胶层混炼压出：将三元乙丙橡胶、氯丁橡胶、氧化锌、氧化镁、硬脂酸、酚醛树脂、防老剂丁进行加压密炼，然后将碳黑N550、碳黑N660、石蜡油加入进行密炼，然后将混练胶排出，在开炼机上加入硫化剂S、促进剂DM、促进剂DTDM、促进剂TMTD进行混炼，然后将胶料压出。
(4)将尼龙树脂在挤出机挤出后，将步骤(1)得到的内胶在挤出机挤出包覆在内尼龙屏蔽层上后，再将尼龙树脂挤出包覆在内胶上，将步骤(1)得到的内胶在挤出机挤出包覆在内中尼龙屏蔽层上后，进行编织，然后将步骤(3)得到的外胶包覆在编织层上，经硫化处理后脱芯。
如上所述的低渗透率的家用空调软管的生产方法，内、中尼龙屏蔽层压出，其内、中尼龙屏蔽层压出的厚度为0.15mm；混炼时，温度升到70℃时，减压一次，温度升到80℃时，减压一次，温度升到100℃时，提上顶栓排胶，硫化时蒸汽压力为0.45MPa，硫化温度为150±2℃，硫化时间为55分钟。
Claims (4)
1.一种低渗透率的家用空调软管，包括内尼龙屏蔽层，内胶层，中尼龙屏蔽层，中胶层，编织层，外胶层六部分，其特征在于，所述的内、中胶层由下列重量成分的原料制成：
氯化丁基橡胶 40-45％
氧化镁 3.5-4.5％
防老剂RD 0.6-1.0％
硬脂酸 0.4-0.6％
碳黑 30-40％
轻质碳酸钙 15-20％
氧化锌 1.5-2.0％
硫磺 0.6-0.9％
促进剂 0.6-1.0％
所述的碳黑包括碳黑N550、碳黑N660，其中，
碳黑N550 6.0-10.0％
碳黑N660 24.0-28.0％
所述的促进剂包括促进剂DM、促进剂TMTD；
所述的外胶层由下列重量成分的原料制成：
三元乙丙橡胶 35-40％
氯丁橡胶 10-12％
氧化锌 2.0-2.5％
氧化镁 0.4-0.5％
硬脂酸 0.4-0.6％
酚醛树脂 0.4-0.6％
碳黑 36-45％
石蜡油 5.0-6.5％
硫化剂S 0.2-0.4％
促进剂 0.655-0.915％
所述的碳黑包括碳黑N550、碳黑N660，其中，
碳黑N550 20-25％
碳黑N660 16-20％
所述的促进剂为促进剂DM、促进剂TMTD、促进剂DTDM，其中，
促进剂DM 0.5-0.65％
促进剂TMTD 0.005-0.015％
促进剂DTDM 0.15-0.25％。
2.一种权利要求1所述低渗透率的家用空调软管的生产方法，包括下列步骤：
(1)内、中胶层混炼压出：将氯化丁基橡胶、氧化镁、防老剂RD、硬脂酸进行加压密炼，然后将碳黑N550、碳黑N660、轻质碳酸钙加入进行密炼，然后将混练胶排出，在开炼机上加入氧化锌、硫磺、促进剂DM、促进剂TMTD进行混炼，然后将胶料压出；
(2)内、中尼龙屏蔽层压出：将尼龙树脂加入尼龙挤出机中挤出；
(3)外胶层混炼压出：将三元乙丙橡胶、氯丁橡胶、氧化锌、氧化镁、硬脂酸、酚醛树脂、防老剂丁进行加压密炼，然后将碳黑N550、碳黑N660、石蜡油加入进行密炼，然后将混练胶排出，在开炼机上加入硫化剂S、促进剂DM、促进剂DTDM、促进剂TMTD进行混炼，然后将胶料压出；
(4)将尼龙树脂在挤出机挤出后，将步骤(1)得到的内胶在挤出机挤出包覆在内尼龙屏蔽层上后，再将尼龙树脂挤出包覆在内胶上，将步骤(1)得到的内胶在挤出机挤出包覆在内、中尼龙屏蔽层上后，进行编织，然后将步骤(3)得到的外胶包覆在编织层上，经硫化处理后脱芯。
3.根据权利要求2所述低渗透率的家用空调软管的生产方法，其特征是：内、中尼龙屏蔽层压出，其内、中尼龙屏蔽层的压出厚度为0.14-0.20mm。
4.根据权利要求2所述的低渗透率的家用空调软管的生产方法，混炼时，温度升到70℃时，减压一次，温度升到80℃时，减压一次，温度升到100℃时，提上顶栓排胶，硫化时蒸汽压力为0.45MPa，硫化温度为150±2℃，硫化时间为45-55分钟。