CN1940174A - 高透湿高防水涂层织物的制造方法 - Google Patents

高透湿高防水涂层织物的制造方法 Download PDF

Info

Publication number
CN1940174A
CN1940174A CN 200510094682 CN200510094682A CN1940174A CN 1940174 A CN1940174 A CN 1940174A CN 200510094682 CN200510094682 CN 200510094682 CN 200510094682 A CN200510094682 A CN 200510094682A CN 1940174 A CN1940174 A CN 1940174A
Authority
CN
China
Prior art keywords
coating
peneration
manufacture method
agent
functions according
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 200510094682
Other languages
English (en)
Inventor
袁小飞
石井正树
稻田康二郎
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Toray Fibers and Textiles Research Laboratories China Co Ltd
Original Assignee
Toray Fibers and Textiles Research Laboratories China Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toray Fibers and Textiles Research Laboratories China Co Ltd filed Critical Toray Fibers and Textiles Research Laboratories China Co Ltd
Priority to CN 200510094682 priority Critical patent/CN1940174A/zh
Publication of CN1940174A publication Critical patent/CN1940174A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高透湿高防水涂层织物的制造方法，包括将聚氨酯聚合物、有机溶剂、拨水剂、成膜剂、交联剂、其他助剂、水混合成织物涂层剂及将制成的织物涂层剂均匀涂布于基布上成涂布，在织物涂层剂未干之际将涂布进行干燥处理等步骤。本发明所制造的涂层织物不但具有优良的防水性和很好的透湿性而且还具有良好的耐摩擦性和丰满柔软的手感等特点。产品耐静水压5000mmH2O以上、透湿Al达8000g/m2·24hr以上、耐洗涤、耐摩擦。这种涂层织物有着广阔的销售前景，它可以用于制作雨衣、登山服、滑雪服、防寒服等，具有较大的经济效益和社会效益。

Description

高透湿高防水涂层织物的制造方法
技术领域：
本发明涉及一种涂层织物的制造方法。
背景技术：
现有的防水透湿涂层织物是将聚氨酯聚合物涂层整理剂均匀地涂布于织物上，在织物表面形成一层多孔薄膜而制成的。
常用的聚合物涂层整理剂有溶剂型和水乳型两种。溶剂型涂层整理剂具有容易干燥、制成的涂膜坚韧而有光泽的特点，但是污染比较严重，成本较高。水乳型涂层剂以水为介质，具有不污染环境，成本较低等特点。但水乳型涂层剂烘干时间较长且需要焙烘，工艺较复杂。总而言之，两种类的涂层剂各有其优缺点。
众所周知，透湿和防水是两个相互矛盾的概念，通常要同时获得织物的高透湿性和高防水性效果不是很容易，再加上耐洗涤和耐摩擦就更加不易。
发明内容：
本发明的目的在于提供一种同时具有高透湿、高防水的高透湿高防水涂层织物的制造方法。
本发明的技术解决方案是：
一种高透湿高防水涂层织物的制造方法，其特征是：包括下列步骤：
①将下列重量份的组份混合成织物涂层剂：
聚氨酯聚合物                        100份
有机溶剂                            80～120份
拨水剂                              2～8份
成膜剂                              6～15份
交联剂                              1～3份
其他助剂                            0～20份
水                                  70～130份；
②将制成的织物涂层剂均匀涂布于基布上成涂布，在织物涂层剂未干之际将涂布进行干燥处理。
聚氨酯聚合物是聚醚型聚氨酯、聚酯型聚氨酯。有机溶剂是极性溶剂和/或非极性溶剂。极性溶剂是丁酮、甲基异丁基酮或异丙醇，非极性溶剂是苯、甲苯或二甲苯。交联剂是多官能团脂肪族异氰酸酯类(如UCB交联剂M2、CRL)、聚氮丙啶类、乙烯亚胺类或丙烯酰胺类，拨水剂采用聚硅酮类、碳氟化合物类或全氟烷基丙烯酸酯共和物。聚氨酯聚合物的温度为5～40℃，最好在20～25℃之间。基布为涤纶或尼龙。其他助剂是增白剂、滑性剂，滑性剂为有机硅类的溶液或固体粉末。
干燥处理温度为50～150℃，50℃以下时溶剂得不到充分挥发，150℃以上时溶剂产生爆沸，两者都会使得膜的性能下降，处理时间为30秒～3分钟，最好为1～2.5分钟。在步骤②干燥处理后，还进行定型后处理，定型温度为130～170℃，时间为45秒～1分钟。
本发明所制造的涂层织物不但具有优良的防水性和很好的透湿性而且还具有良好的耐摩擦性和丰满柔软的手感等特点。产品耐静水压5000mmH2O以上、透湿A1达8000g/m2·24hr以上、耐洗涤、耐摩擦。这种涂层织物有着广阔的销售前景，它可以用于制作雨衣、登山服、滑雪服、防寒服等，具有较大的经济效益和社会效益。
下面结合实施例对本发明作进一步说明。
具体实施方式：
实施例1：
一种高透湿高防水涂层织物的制造方法，包括下列步骤：
①将下列重量份的组份混合成织物涂层剂：
聚氨酯聚合物                                100份
极性溶剂丁酮(或甲基异丁基酮、异丙醇)        50份
非极性溶剂苯(或甲苯、二甲苯)                50份
拨水剂                                      4份
成膜剂                                      9份
交联剂                                      2份
滑性剂                                      4份
水                                          90份；
②将制成的织物涂层剂均匀涂布于基布上成涂布，在织物涂层剂未干之际将涂布放入烘箱中进行干燥处理，干燥处理温度为50～150℃(例50℃、100℃、150℃)，处理时间为30秒～3分钟(例30秒、1分钟、2.5分钟、3分钟)。
在步骤②干燥处理后，还进行烘干后处理，烘干温度为130～170℃(例130℃、150℃、170℃)，时间为45秒～1分钟(例45秒、52秒、1分钟)。
其中聚氨酯聚合物是聚醚型聚氨酯(例UCB树脂)或聚酯型聚氨酯。交联剂是多官能团脂肪族异氰酸酯类(如UCB交联剂M2、CRL)、聚氮丙啶类、乙烯亚胺类或丙烯酰胺类，拨水剂采用聚硅酮类、碳氟化合物类或全氟烷基丙烯酸酯共和物(采用日华化学株式会社生产的NDN-7、旭硝子株式会社生产的AG-7600、明成化学工业株式会社生产的AG-970等产品)。成膜剂采用氧化硅类(例大日精化工业株式会社生产的CUT-3产品)聚氨酯聚合物的温度为5～40℃(例5℃、20℃、25℃、40℃)之间。基布为尼龙(或涤纶)，采用涤纶更好。滑性剂为有机硅类的溶液或固体粉末。
得到的产品主要指标(见下表)：
  项目   洗涤0次   ISO 811洗涤5次   ISO 811洗涤20次
  耐静水压(mmH2O)   6530   5840   5430
  透湿度(JIS A1)   8215   8870   9320
  马丁代尔摩擦5000回   5500   -   -
  拨水度   5级   4级   4级
  手感   柔软   柔软   柔软
测试方法和标准
①耐静水压根据JIS1092的标准测试
②透湿性根据JIS1099的标准测试
③涂布量根据通用方法测定。即将基布和涂布分别裁成30×20cm的试样，于110℃的烘箱中烘烤1h，分别称重，求出两者之差，在换算成每平方米增重(干增重)
④手感凭经验评比
⑤拒水性根据JIS1092的标准测试
⑥耐洗涤根据ISO 811和DECATHON TSET METHOD WI034
⑦耐磨擦根据DECATHON TSET METHOD WI007
实施例2：
混合成织物涂层剂的重量组份为：
亲水性聚氨酯聚合物                        100份
极性溶剂丁酮(或甲基异丁基酮、异丙醇)      40份
非极性溶剂苯(或甲苯、二甲苯)              40份
拨水剂                                    8份
成膜剂                                    6份
交联剂                                    1份
滑性剂                                    10份
增白剂                                    10份
水                                        130份；
其中增白粉采用钛白粉等常规涂层织物的增白剂，例大日精化工业株式会社生产的X-2093产品)其余同实施例1。
得到的产品主要指标(见下表)：
  项目   洗涤0次   ISO 811洗涤5次   ISO 811洗涤20次
  耐静水压(mmH2O)   6250   5980   5320
  透湿度(JIS A1)   8317   8950   9470
  马丁代尔摩擦5000回   5400   -   -
  拨水度   5级   4级   4级
  手感   柔软   柔软   柔软
实施例3：混合成织物涂层剂的重量组份为：
亲水性聚氨酯聚合物                        100份
极性溶剂丁酮(或甲基异丁基酮、异丙醇)      60份
非极性溶剂苯(或甲苯、二甲苯)              60份
拨水剂                                    2份
成膜剂                                    15份
交联剂                                    3份
水                                        70份；
其余同实施例1。
得到的产品主要指标(见下表)：
  项目   洗涤0次   ISO 811洗涤5次   ISO 811洗涤20次
  耐静水压(mmH2O)   6820   6390   5840
  透湿度(JIS A1)   8012   8415   9085
  马丁代尔摩擦5000回   6120   -   -
  拨水度   5级   4级   4级
  手感   柔软   柔软   柔软

Claims (10)

1、一种高透湿高防水涂层织物的制造方法，其特征是：包括下列步骤：
①将下列重量份的组份混合成织物涂层剂：
聚氨酯聚合物                               100份
有机溶剂                                   80～120份
拨水剂                                     2～8份
成膜剂                                     6～15份
交联剂                                     1～3份
其他助剂                                   0～20份
水                                         70～130份；
②将制成的织物涂层剂均匀涂布于基布上成涂布，在织物涂层剂未干之际将涂布进行干燥处理。
2、根据权利要求1所述的高透湿高防水涂层织物的制造方法，其特征是：聚氨酯聚合物是聚醚型聚氨酯、聚酯型聚氨酯。
3、根据权利要求1或2所述的高透湿高防水涂层织物的制造方法，其特征是：有机溶剂是极性溶剂和/或非极性溶剂。
4、根据权利要求3所述的高透湿高防水涂层织物的制造方法，其特征是：极性溶剂是丁酮、甲基异丁基酮或异丙醇，非极性溶剂是苯、甲苯或二甲苯。
5、根据权利要求1或2所述的高透湿高防水涂层织物的制造方法，其特征是：交联剂是多官能团脂肪族异氰酸酯类、聚氮丙啶类、乙烯亚胺类或丙烯酰胺类，拨水剂采用聚硅酮类、碳氟化合物类或全氟烷基丙烯酸酯共和物。
6、根据权利要求1或2所述的高透湿高防水涂层织物的制造方法，其特征是：聚氨酯聚合物的温度为5～40℃。
7、根据权利要求1或2所述的高透湿高防水涂层织物的制造方法，其特征是：基布为涤纶或尼龙。
8、根据权利要求1或2所述的高透湿高防水涂层织物的制造方法，其特征是：其他助剂是增白剂、滑性剂。
9、根据权利要求1或2所述的高透湿高防水涂层织物的制造方法，其特征是：干燥处理温度为50～150℃，处理时间为30秒～3分钟。
10、根据权利要求1或2所述的高透湿高防水涂层织物的制造方法，其特征是：在步骤②干燥处理后，还进行定型后处理，定型温度为130～170℃，时间为45秒～1分钟。
CN 200510094682 2005-09-28 2005-09-28 高透湿高防水涂层织物的制造方法 Pending CN1940174A (zh)