CN1255243C - 制作钎焊体的方法及其制得的钎焊体和磨具 - Google Patents

制作钎焊体的方法及其制得的钎焊体和磨具 Download PDF

Info

Publication number
CN1255243C
CN1255243C CNB018227511A CN01822751A CN1255243C CN 1255243 C CN1255243 C CN 1255243C CN B018227511 A CNB018227511 A CN B018227511A CN 01822751 A CN01822751 A CN 01822751A CN 1255243 C CN1255243 C CN 1255243C
Authority
CN
China
Prior art keywords
metal
reducing metal
oxide
cored solder
layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB018227511A
Other languages
English (en)
Chinese (zh)
Other versions
CN1491145A (zh
Inventor
G·M·帕尔姆格伦
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
3M Innovative Properties Co
Original Assignee
3M Innovative Properties Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 3M Innovative Properties Co filed Critical 3M Innovative Properties Co
Publication of CN1491145A publication Critical patent/CN1491145A/zh
Application granted granted Critical
Publication of CN1255243C publication Critical patent/CN1255243C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
    • B23K35/02—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by mechanical features, e.g. shape
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
    • B23K35/001—Interlayers, transition pieces for metallurgical bonding of workpieces
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K1/00—Soldering, e.g. brazing, or unsoldering
    • B23K1/008—Soldering within a furnace
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K1/00—Soldering, e.g. brazing, or unsoldering
    • B23K1/19—Soldering, e.g. brazing, or unsoldering taking account of the properties of the materials to be soldered
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
    • B23K35/02—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by mechanical features, e.g. shape
    • B23K35/0222—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by mechanical features, e.g. shape for use in soldering, brazing
    • B23K35/0233—Sheets, foils
    • B23K35/0238—Sheets, foils layered
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12535—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.] with additional, spatially distinct nonmetal component
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12535—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.] with additional, spatially distinct nonmetal component
    • Y10T428/12611—Oxide-containing component
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12736—Al-base component
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12861—Group VIII or IB metal-base component
    • Y10T428/12951—Fe-base component
    • Y10T428/12972—Containing 0.01-1.7% carbon [i.e., steel]
    • Y10T428/12979—Containing more than 10% nonferrous elements [e.g., high alloy, stainless]

Landscapes

  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Chemical & Material Sciences (AREA)
  • Materials Engineering (AREA)
  • Ceramic Products (AREA)
  • Polishing Bodies And Polishing Tools (AREA)
  • Other Surface Treatments For Metallic Materials (AREA)
CNB018227511A 2001-02-20 2001-06-28 制作钎焊体的方法及其制得的钎焊体和磨具 Expired - Fee Related CN1255243C (zh)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US09/788,784 US6575353B2 (en) 2001-02-20 2001-02-20 Reducing metals as a brazing flux
US09/788,784 2001-02-20

Publications (2)

Publication Number Publication Date
CN1491145A CN1491145A (zh) 2004-04-21
CN1255243C true CN1255243C (zh) 2006-05-10

Family

ID=25145541

Family Applications (1)

Application Number Title Priority Date Filing Date
CNB018227511A Expired - Fee Related CN1255243C (zh) 2001-02-20 2001-06-28 制作钎焊体的方法及其制得的钎焊体和磨具

Country Status (10)

Country Link
US (2) US6575353B2 (enExample)
EP (1) EP1361931A1 (enExample)
JP (1) JP2004523363A (enExample)
KR (1) KR100769747B1 (enExample)
CN (1) CN1255243C (enExample)
AU (1) AU2001275856B2 (enExample)
MY (1) MY136293A (enExample)
RU (1) RU2003125885A (enExample)
TW (1) TWI244418B (enExample)
WO (1) WO2002066200A1 (enExample)

Families Citing this family (46)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3795786B2 (ja) * 2001-10-09 2006-07-12 敬久 山崎 ろう付けしたダイヤモンド及びダイヤモンドのろう付け方法
US7055733B2 (en) * 2002-01-11 2006-06-06 Battelle Memorial Institute Oxidation ceramic to metal braze seals for applications in high temperature electrochemical devices and method of making
US20050076577A1 (en) * 2003-10-10 2005-04-14 Hall Richard W.J. Abrasive tools made with a self-avoiding abrasive grain array
FR2883006A1 (fr) * 2005-03-09 2006-09-15 Carbone Lorraine Equipements G Plaques en acier revetues de zirconium et elements de dispositifs chimiques realises avec de telles plaques
JP4675821B2 (ja) * 2006-04-28 2011-04-27 株式会社豊田中央研究所 ろう付け方法
US20080271384A1 (en) * 2006-09-22 2008-11-06 Saint-Gobain Ceramics & Plastics, Inc. Conditioning tools and techniques for chemical mechanical planarization
KR100896560B1 (ko) * 2007-02-27 2009-05-07 동아금속주름관(주) 스테인 리스 스틸 파이프와 연결구의 브레이징 용접 방법
EP1967312A1 (de) * 2007-03-06 2008-09-10 Siemens Aktiengesellschaft Verfahren zur Lötreparatur eines Bauteils unter Vakuum und einem eingestellten Sauerstoffpartialdruck
JP2010536183A (ja) 2007-08-23 2010-11-25 サンーゴバン アブレイシブズ，インコーポレイティド 次世代酸化物／金属ｃｍｐ用の最適化されたｃｍｐコンディショナー設計
JP5157864B2 (ja) * 2008-01-23 2013-03-06 日立電線株式会社 ろう付け用クラッド材及びろう付け製品
CN101314192B (zh) * 2008-06-04 2011-02-02 哈尔滨工业大学 一种金属材料与非金属复合材料的连接方法
KR101061941B1 (ko) * 2008-12-11 2011-09-05 웰텍코리아 (주) 입방정 질화 붕소(씨비엔)를 접합한 공구의 제조방법 및 그를 이용한 입방정 질화 붕소(씨비엔) 공구
SG174351A1 (en) 2009-03-24 2011-10-28 Saint Gobain Abrasives Inc Abrasive tool for use as a chemical mechanical planarization pad conditioner
CN102484054A (zh) * 2009-06-02 2012-05-30 圣戈班磨料磨具有限公司 耐腐蚀性cmp修整工件及其制造和使用方法
US20110097977A1 (en) * 2009-08-07 2011-04-28 Abrasive Technology, Inc. Multiple-sided cmp pad conditioning disk
JP5542938B2 (ja) 2009-08-14 2014-07-09 サンーゴバン アブレイシブズ，インコーポレイティド 細長い物体に結合させた研磨粒子を含む研磨物品
CN102665988B (zh) * 2009-08-14 2015-11-25 圣戈班磨料磨具有限公司 包括粘结到长形本体上的磨料颗粒的磨料物品及其形成方法
EP2474025A2 (en) 2009-09-01 2012-07-11 Saint-Gobain Abrasives, Inc. Chemical mechanical polishing conditioner
FR2949695B1 (fr) * 2009-09-10 2011-12-23 Commissariat Energie Atomique Procede d'assemblage pour brasage
EP2366484A1 (en) * 2010-03-18 2011-09-21 Siemens Aktiengesellschaft A method for brazing a surface of a metallic substrate
CN102069253A (zh) * 2010-12-29 2011-05-25 哈尔滨电机厂有限责任公司 水冷汽轮发电机水循环系统水接头与连接块钎焊工艺
TW201507812A (zh) 2010-12-30 2015-03-01 聖高拜磨料有限公司 磨料物品及形成方法
US9375826B2 (en) 2011-09-16 2016-06-28 Saint-Gobain Abrasives, Inc. Abrasive article and method of forming
JP5869680B2 (ja) 2011-09-29 2016-02-24 サンーゴバン アブレイシブズ，インコーポレイティド バリア層を有する細長い基板本体に結合した研磨粒子を含む研磨物品及びその形成方法
US20130189022A1 (en) * 2011-11-30 2013-07-25 Component Re-Engineering Company, Inc. Hermetically Joined Plate And Shaft Devices
TWI477343B (zh) 2012-06-29 2015-03-21 Saint Gobain Abrasives Inc 研磨物品及形成方法
TW201402274A (zh) 2012-06-29 2014-01-16 Saint Gobain Abrasives Inc 研磨物品及形成方法
TW201404527A (zh) 2012-06-29 2014-02-01 聖高拜磨料有限公司 研磨物品及形成方法
TW201441355A (zh) 2013-04-19 2014-11-01 Saint Gobain Abrasives Inc 研磨製品及其形成方法
EP3129182B1 (en) 2014-04-06 2020-02-19 Diamond Innovations, Inc. Brazed superabrasive assembly with active metal braze joint with stress relieving layer ; method of manufacturing of such assembly
CN104043915B (zh) * 2014-07-09 2016-06-08 哈尔滨正德科技开发有限公司 硬质合金钎焊用三明治夹层式复合钎料的制备方法
USD785339S1 (en) * 2014-10-23 2017-05-02 Griot's Garage, Inc. Hand applicator buffing pad
US10888973B2 (en) 2015-06-25 2021-01-12 3M Innovative Properties Company Methods of making metal bond abrasive articles and metal bond abrasive articles
US10287823B2 (en) 2015-06-25 2019-05-14 Halliburton Energy Services, Inc. Braze joints with a dispersed particulate microstructure
TWI664057B (zh) 2015-06-29 2019-07-01 美商聖高拜磨料有限公司 研磨物品及形成方法
KR102629658B1 (ko) 2016-01-21 2024-01-29 쓰리엠 이노베이티브 프로퍼티즈 캄파니 금속 접합제 및 유리질 접합제 연마 용품의 제조 방법, 및 연마 용품 전구체
CN108242530B (zh) * 2016-12-23 2022-02-22 北京好风光储能技术有限公司 一种锂浆料电池及其负极片
WO2017173009A1 (en) 2016-03-30 2017-10-05 3M Innovative Properties Company Methods of making metal bond and vitreous bond abrasive articles, and abrasive article precursors
KR102427116B1 (ko) 2016-10-25 2022-08-01 쓰리엠 이노베이티브 프로퍼티즈 캄파니 배향된 연마 입자를 포함하는 접합된 연마 용품, 및 그의 제조 방법
WO2021001730A1 (en) 2019-07-02 2021-01-07 3M Innovative Properties Company Methods of making metal bond abrasive articles and metal bond abrasive articles
WO2021038438A1 (en) 2019-08-28 2021-03-04 3M Innovative Properties Company Dental bur, manufacturing method therefor and data stream
DE102019218866A1 (de) * 2019-12-04 2021-06-10 Albert-Ludwigs-Universität Freiburg Verfahren zum Fügen mindestens eines ersten und eines zweiten Fügebereichs, Fügeverbindung und elektronische Komponente sowie Schaltungsanordnung
DE102019135171A1 (de) * 2019-12-19 2021-06-24 Rogers Germany Gmbh Lotmaterial, Verfahren zur Herstellung eines solchen Lotmaterials und Verwendung eines solchen Lotmaterials zur Anbindung einer Metallschicht an eine Keramikschicht
JP2024509814A (ja) 2021-03-05 2024-03-05 サンーゴバン アブレイシブズ，インコーポレイティド 研磨物品及びそれを形成するための方法
CN118591435A (zh) 2021-12-30 2024-09-03 圣戈班磨料磨具有限公司 磨料制品及其形成方法
WO2023130082A1 (en) 2021-12-30 2023-07-06 Saint-Gobain Abrasives, Inc. Abrasive articles and methods for forming same

Family Cites Families (61)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB516474A (en) 1937-06-28 1940-01-03 Carborundum Co Improvements in or relating to metal bonded abrasive articles
US2746888A (en) 1952-07-05 1956-05-22 Du Pont Method of forming titanium coating on refractory body
US3321828A (en) 1962-01-02 1967-05-30 Gen Electric Aluminum brazing
US3293012A (en) 1962-11-27 1966-12-20 Exxon Production Research Co Process of infiltrating diamond particles with metallic binders
US3588992A (en) 1967-06-16 1971-06-29 Toyoda Machine Works Ltd Manufacturing process for a metal bonded porous substance, particularly a tool made of said substance
US3650714A (en) 1969-03-04 1972-03-21 Permattach Diamond Tool Corp A method of coating diamond particles with metal
JPS576287A (en) 1980-06-11 1982-01-13 Nippon Kokan Kk Recycling of waste hearth material for blooming/soaking pit
US4365995A (en) 1980-07-14 1982-12-28 Daido Metal Company Ltd. Method of producing multi-layer sliding material
JPS5767142A (en) * 1980-10-08 1982-04-23 Hitachi Ltd Low-temperature aluminum solder
JPS5768287A (en) 1980-10-16 1982-04-26 Kobe Steel Ltd Production of composite material
JPS5938491A (ja) * 1982-08-27 1984-03-02 住友電気工業株式会社 複合焼結体工具およびその製造法
US4457113A (en) 1982-02-24 1984-07-03 Super-Cut, Inc. Protected super-abrasive grinding tool
DE3216934C1 (de) 1982-05-06 1983-08-25 Daimler-Benz Ag, 7000 Stuttgart Verfahren zum wasserstoff-undurchlaessigen Hartverloeten austenitischer Stahlbauteile
JPS59134655A (ja) * 1983-01-21 1984-08-02 Hitachi Ltd 研削装置
US4929511A (en) 1983-12-06 1990-05-29 Allied-Signal Inc. Low temperature aluminum based brazing alloys
JPS60131875A (ja) * 1983-12-20 1985-07-13 三菱重工業株式会社 セラミツクと金属の接合法
US4738689A (en) 1984-03-20 1988-04-19 General Electric Company Coated oxidation-resistant porous abrasive compact and method for making same
WO1986001433A1 (en) 1984-08-24 1986-03-13 The Australian National University Diamond compacts and process for making same
US4610934A (en) * 1985-01-17 1986-09-09 Kennecott Corporation Silicon carbide-to-metal joint and method of making same
US4850523A (en) * 1988-02-22 1989-07-25 General Electric Company Bonding of thermally stable abrasive compacts to carbide supports
US5024680A (en) 1988-11-07 1991-06-18 Norton Company Multiple metal coated superabrasive grit and methods for their manufacture
EP0374475B1 (en) 1988-12-23 1993-06-09 International Business Machines Corporation Soldering and bonding of semiconductor device contacts
US4925457B1 (en) 1989-01-30 1995-09-26 Ultimate Abrasive Syst Inc Method for making an abrasive tool
US5024860A (en) 1989-05-24 1991-06-18 Ethyl Corporation Rocket motor insulation using phosphonitrilic elastomeric compositions
DE69030669T2 (de) 1989-11-08 1997-09-11 Alloy Surfaces Co., Inc., Wilmington, Del. Metallbehandlung im hinblick auf eine nachfolgende beschichtung und aktivierung
US5126207A (en) 1990-07-20 1992-06-30 Norton Company Diamond having multiple coatings and methods for their manufacture
US5100048A (en) 1991-01-25 1992-03-31 Alcan International Limited Method of brazing aluminum
US5380390B1 (en) 1991-06-10 1996-10-01 Ultimate Abras Systems Inc Patterned abrasive material and method
WO1992022398A1 (en) 1991-06-10 1992-12-23 Allied-Signal Inc. Rapidly solidified aluminum-magnesium base brazing alloys
HUT62831A (en) 1991-09-12 1993-06-28 Gen Electric Method for producing covered cubed leather-nitride abrasive grain, abrasive grain and grinding tool by using the same
US5232469A (en) 1992-03-25 1993-08-03 General Electric Company Multi-layer metal coated diamond abrasives with an electrolessly deposited metal layer
US5250086A (en) 1992-03-25 1993-10-05 General Electric Company Multi-layer metal coated diamond abrasives for sintered metal bonded tools
US5359770A (en) * 1992-09-08 1994-11-01 General Motors Corporation Method for bonding abrasive blade tips to the tip of a gas turbine blade
ZA941116B (en) 1993-03-05 1994-08-30 Smith International Polycrystalline diamond compact
EP0653264B1 (en) * 1993-05-12 1998-12-16 Nippon Steel Corporation Method of soldering heat resisting alloy having insulating oxide film on its surface, and preheated type exhaust gas cleaning metal support and method of manufacturing the same
US5344062A (en) 1993-06-24 1994-09-06 The Idod Trust Method of forming seamed metal tube
US5346719A (en) 1993-08-02 1994-09-13 General Electric Company Tungsten metallization of CVD diamond
ZA9410384B (en) 1994-04-08 1996-02-01 Ultimate Abrasive Syst Inc Method for making powder preform and abrasive articles made therefrom
GB9407632D0 (en) * 1994-04-18 1994-06-08 Short Brothers Plc An aircraft propulsive power unit
WO1996002332A1 (en) 1994-07-19 1996-02-01 Metaltone Usa, Inc. Water resistant welding rod
US5470014A (en) 1994-09-02 1995-11-28 Aluminum Design Corporation Brazing of aluminum-beryllium alloy
JP3866305B2 (ja) 1994-10-27 2007-01-10 住友電工ハードメタル株式会社 工具用複合高硬度材料
US5697994A (en) 1995-05-15 1997-12-16 Smith International, Inc. PCD or PCBN cutting tools for woodworking applications
JP3522896B2 (ja) * 1995-05-17 2004-04-26 株式会社東芝 真空気密容器用封着材および真空気密容器
KR100255027B1 (ko) * 1995-05-17 2000-05-01 니시무로 타이죠 세라믹 금속접합재 및 이를 사용한 세라믹 금속접합체 제조방법 및 이를 이용하여 제작한 진공기밀용기
US5794838A (en) * 1995-07-14 1998-08-18 Ngk Insulators, Ltd. Ceramics joined body and method of joining ceramics
JP3318470B2 (ja) * 1995-08-08 2002-08-26 新日本製鐵株式会社 金属箔のろう付けおよびハニカム体のろう付け方法
JP3017059B2 (ja) 1995-10-25 2000-03-06 株式会社神戸製鋼所 Ｃｒ−Ｎｉ系ステンレス鋼溶接用高窒素フラックス入りワイヤ
CA2161393A1 (en) 1995-10-25 1997-04-26 Gary R. Adams Galvanizing alloy and process for reactive steels
JP3017063B2 (ja) 1995-11-07 2000-03-06 株式会社神戸製鋼所 Ｃｒ−Ｎｉ系ステンレス鋼の全姿勢溶接用高窒素フラックス入りワイヤ
US5697944A (en) * 1995-11-15 1997-12-16 Interventional Technologies Inc. Universal dilator with expandable incisor
US5725421A (en) 1996-02-27 1998-03-10 Minnesota Mining And Manufacturing Company Apparatus for rotative abrading applications
US5762132A (en) 1996-04-03 1998-06-09 Ford Global Technologies, Inc. Heat exchanger and method of assembly for automotive vehicles
ES2176764T3 (es) 1996-09-04 2002-12-01 Anglo Operations Ltd Procedimiento de fabricacion de un producto abrasivo de union metalica.
US6039641A (en) 1997-04-04 2000-03-21 Sung; Chien-Min Brazed diamond tools by infiltration
US6110031A (en) 1997-06-25 2000-08-29 3M Innovative Properties Company Superabrasive cutting surface
US6358133B1 (en) * 1998-02-06 2002-03-19 3M Innovative Properties Company Grinding wheel
US6123612A (en) 1998-04-15 2000-09-26 3M Innovative Properties Company Corrosion resistant abrasive article and method of making
US6042659A (en) 1998-06-29 2000-03-28 The Idod Trust Method of coating the seams of a welded tube
AU4247100A (en) 1999-04-16 2000-11-02 Edison Welding Institute Soldering alloy
US6416560B1 (en) * 1999-09-24 2002-07-09 3M Innovative Properties Company Fused abrasive bodies comprising an oxygen scavenger metal

Also Published As

Publication number Publication date
AU2001275856C1 (en) 2002-09-04
US6858050B2 (en) 2005-02-22
AU2001275856B2 (en) 2007-01-04
CN1491145A (zh) 2004-04-21
MY136293A (en) 2008-09-30
US6575353B2 (en) 2003-06-10
RU2003125885A (ru) 2005-02-27
KR20030074836A (ko) 2003-09-19
EP1361931A1 (en) 2003-11-19
WO2002066200A8 (en) 2003-11-13
JP2004523363A (ja) 2004-08-05
US20020155313A1 (en) 2002-10-24
TWI244418B (en) 2005-12-01
WO2002066200A1 (en) 2002-08-29
KR100769747B1 (ko) 2007-10-23
US20030201308A1 (en) 2003-10-30

Similar Documents

Publication Publication Date Title
CN1255243C (zh) 制作钎焊体的方法及其制得的钎焊体和磨具
AU2001275856A1 (en) Reducing metals as a brazing flux
JP5552543B2 (ja) 接合体
CN102059423B (zh) 一种具有自润滑功能金刚石工具的制作方法
CN102059449B (zh) 钨合金与钽合金的低温扩散焊接方法
CN103459071B (zh) 立方氮化硼烧结体工具
CN103687829A (zh) 钎焊的涂布的含金刚石材料
JP2006521214A (ja) ろう付合金固着済みダイヤモンド工具インサートおよびその製造方法
CN103695898B (zh) 一种钛合金表面金属陶瓷复合涂层及其制备工艺
JPH11106948A (ja) 火花溶着用の電極棒及びその製法、並びに超砥粒含有物層の被覆方法
WO2011074530A1 (ja) 被覆回転ツール
CN103233223B (zh) 铝合金表面熔覆TiC增强Ni3Al基复合涂层的方法
GB2507168A (en) Brazing a diamond body to a carrier body
CN107520766A (zh) 一种激光熔覆工艺制作金属结合剂超硬磨料结构化排布端面磨削砂轮的方法
WO2010137616A1 (ja) 接合体
JP5295129B2 (ja) 炭素材料と銅合金との耐火性アセンブリに関する方法
JP3549424B2 (ja) 硬質焼結体工具及びその製造方法
CN101053981B (zh) 钎焊-热压烧结金刚石工具节块
JP5485117B2 (ja) 接合体
Ma et al. Resistance welding of large-size CBN grits
CN114214693B (zh) 一种盾构机滚刀的表面加工方法
CN112620855A (zh) 钎涂方法及其获得的钎涂后待焊母材
JPH08225376A (ja) ろう付け可能なコバルト含有ｃｂｎ成形体
Mookam et al. A New Technique for Brazing Porous Copper to Copper Substrate Using CuNiSnP Amorphous Filler Metal
JPH10138147A (ja) 鉄鋼用ダイヤモンド切削刃の構造

Legal Events

Date Code Title Description
C06 Publication
PB01 Publication
C10 Entry into substantive examination
SE01 Entry into force of request for substantive examination
C14 Grant of patent or utility model
GR01 Patent grant
C17 Cessation of patent right
CF01 Termination of patent right due to non-payment of annual fee

Granted publication date: 20060510

Termination date: 20130628