CN1190810C - 电容器包覆用聚酯基热收缩管 - Google Patents
电容器包覆用聚酯基热收缩管 Download PDFInfo
- Publication number
- CN1190810C CN1190810C CNB011368071A CN01136807A CN1190810C CN 1190810 C CN1190810 C CN 1190810C CN B011368071 A CNB011368071 A CN B011368071A CN 01136807 A CN01136807 A CN 01136807A CN 1190810 C CN1190810 C CN 1190810C
- Authority
- CN
- China
- Prior art keywords
- resin
- capacitor
- polyester
- shrinkable tube
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
Description
组分 | 性能 | ||||||||
A | B | C | D | E | F | G | H | ||
实施例 | 1 | 95.4 | 5 | 0.5 | 2.5 | 30 | 0.1 | 2 | 0.82 |
2 | 95.4 | 5 | 1.5 | 2.5 | 30 | 0.1 | 2 | 0.81 | |
3 | 95.4 | 5 | 2.5 | 2.5 | 30 | 0.1 | 2 | 0.79 | |
4 | 91.95 | 10 | 0.5 | 5 | 20 | 0.05 | 3 | 0.84 | |
5 | 85.9 | 5 | 0.5 | 10 | 20 | 0.1 | 4 | 0.82 | |
对比实施例 | 1 | 95.4 | 5 | - | 2.5 | 30 | 0.1 | 2 | 0.84 |
2 | 95.4 | 5 | 5 | 2.5 | 30 | 0.1 | 2 | 0.77 | |
3 | 97.9 | 5 | 0.5 | - | - | 0.1 | 2 | 0.69 | |
4 | 67.9 | 5 | 1.5 | 30 | 30 | 0.1 | 2 | 0.81 | |
5 | 94.0 | 5 | 0.5 | 2.5 | 30 | 1.5 | 2 | 0.82 | |
备注:)A:共聚物树脂的重量百分含量(wt.%)B:共聚物树脂中NDC(萘二甲酸)的摩尔百分含量(mol%)C:共聚物树脂中外加颗粒的重量百分含量(wt.%)D:含颜料的PBT(聚对苯二甲酸丁二酯)的重量百分含量(wt.%)E:PBT中颜料的重量百分含量(wt.%)F:硬脂酸钠的重量百分含量(wt.%)G:弹性体的重量百分含量(wt.%)H:含NDC的共聚物树脂的特性粘度(dl/g) |
滑爽性 | 包覆附着性能 | 耐湿热性能 | 耐高温性能 | ||
实施例 | 1 | 614 | ○ | ○ | ○ |
2 | 477 | ○ | ○ | ○ | |
3 | 389 | ○ | ○ | ○ | |
4 | 683 | ○ | ○ | ○ | |
5 | 588 | ○ | ○ | ○ | |
对比实施例 | 1 | 1,024 | ○ | ○ | ○ |
2 | 321 | ○ | × | × | |
3 | 602 | ○ | × | × | |
4 | 512 | × | × | × | |
5 | 564 | × | × | × |
Claims (3)