CN1170867C - 用聚醚多元醇生产的聚氨酯软泡沫 - Google Patents

用聚醚多元醇生产的聚氨酯软泡沫 Download PDF

Info

Publication number
CN1170867C
CN1170867C CNB008090130A CN00809013A CN1170867C CN 1170867 C CN1170867 C CN 1170867C CN B008090130 A CNB008090130 A CN B008090130A CN 00809013 A CN00809013 A CN 00809013A CN 1170867 C CN1170867 C CN 1170867C
Authority
CN
China
Prior art keywords
foam
weight
parts
polyether
block
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
CNB008090130A
Other languages
English (en)
Chinese (zh)
Other versions
CN1355819A (zh
Inventor
J
J·霍夫曼
P·古普塔
ϣ
M·迪特里希
H·拉贝
J·格雷宁
P·奥姆斯
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Covestro Deutschland AG
Original Assignee
Bayer AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=7911864&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=CN1170867(C) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by Bayer AG filed Critical Bayer AG
Publication of CN1355819A publication Critical patent/CN1355819A/zh
Application granted granted Critical
Publication of CN1170867C publication Critical patent/CN1170867C/zh
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/40—High-molecular-weight compounds
    • C08G18/48—Polyethers
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G65/00—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule
    • C08G65/02—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from cyclic ethers by opening of the heterocyclic ring
    • C08G65/26—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from cyclic ethers by opening of the heterocyclic ring from cyclic ethers and other compounds
    • C08G65/2642—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from cyclic ethers by opening of the heterocyclic ring from cyclic ethers and other compounds characterised by the catalyst used
    • C08G65/2645—Metals or compounds thereof, e.g. salts
    • C08G65/2663—Metal cyanide catalysts, i.e. DMC's
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/40—High-molecular-weight compounds
    • C08G18/48—Polyethers
    • C08G18/4833—Polyethers containing oxyethylene units
    • C08G18/4837—Polyethers containing oxyethylene units and other oxyalkylene units
    • C08G18/4845—Polyethers containing oxyethylene units and other oxyalkylene units containing oxypropylene or higher oxyalkylene end groups
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/40—High-molecular-weight compounds
    • C08G18/48—Polyethers
    • C08G18/4833—Polyethers containing oxyethylene units
    • C08G18/4837—Polyethers containing oxyethylene units and other oxyalkylene units
    • C08G18/485—Polyethers containing oxyethylene units and other oxyalkylene units containing mixed oxyethylene-oxypropylene or oxyethylene-higher oxyalkylene end groups
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/40—High-molecular-weight compounds
    • C08G18/48—Polyethers
    • C08G18/4866—Polyethers having a low unsaturation value
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G2110/00—Foam properties
    • C08G2110/0008—Foam properties flexible
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G2110/00—Foam properties
    • C08G2110/0083—Foam properties prepared using water as the sole blowing agent

Landscapes

  • Chemical & Material Sciences (AREA)
  • Health & Medical Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Organic Chemistry (AREA)
  • Toxicology (AREA)
  • Polyurethanes Or Polyureas (AREA)
  • Materials For Medical Uses (AREA)
  • Polyethers (AREA)
CNB008090130A 1999-06-19 2000-06-06 用聚醚多元醇生产的聚氨酯软泡沫 Expired - Lifetime CN1170867C (zh)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
DE19928156A DE19928156A1 (de) 1999-06-19 1999-06-19 Aus Polyetherpolyolen hergestellte Polyurethan-Weichschäume
DE19928156.4 1999-06-19

Publications (2)

Publication Number Publication Date
CN1355819A CN1355819A (zh) 2002-06-26
CN1170867C true CN1170867C (zh) 2004-10-13

Family

ID=7911864

Family Applications (1)

Application Number Title Priority Date Filing Date
CNB008090130A Expired - Lifetime CN1170867C (zh) 1999-06-19 2000-06-06 用聚醚多元醇生产的聚氨酯软泡沫

Country Status (21)

Country Link
US (1) US6858655B1 (enExample)
EP (1) EP1194468B2 (enExample)
JP (2) JP4768178B2 (enExample)
KR (1) KR100697731B1 (enExample)
CN (1) CN1170867C (enExample)
AT (1) ATE276299T1 (enExample)
AU (1) AU768450B2 (enExample)
BR (1) BR0011777A (enExample)
CA (1) CA2375285C (enExample)
DE (2) DE19928156A1 (enExample)
DK (1) DK1194468T4 (enExample)
ES (1) ES2228545T5 (enExample)
HK (1) HK1047598B (enExample)
MX (1) MXPA01012985A (enExample)
NO (1) NO329941B1 (enExample)
PL (1) PL209418B1 (enExample)
PT (1) PT1194468E (enExample)
SI (1) SI1194468T2 (enExample)
TW (1) TW591045B (enExample)
WO (1) WO2000078837A1 (enExample)
ZA (1) ZA200109264B (enExample)

Families Citing this family (43)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE10108484A1 (de) 2001-02-22 2002-09-05 Bayer Ag Verbessertes Verfahren zur Herstelung von Polyetherpolyolen
DE10108485A1 (de) * 2001-02-22 2002-09-05 Bayer Ag Verbessertes Verfahren zur Herstellung von Polyetherpolyolen
JP4715002B2 (ja) * 2001-02-27 2011-07-06 旭硝子株式会社 軟質ポリウレタンフォームの製造方法
WO2002088148A1 (en) 2001-04-30 2002-11-07 The Regents Of The University Of Michigan Isoreticular metal-organic frameworks, process for forming the same, and systematic design of pore size and functionality therein,with application for gas storage
DE10143195A1 (de) * 2001-09-04 2003-03-20 Basf Ag Integriertes Verfahren zur Herstellung von Polyurethan-Schäumen
US20030078311A1 (en) 2001-10-19 2003-04-24 Ulrich Muller Process for the alkoxylation of organic compounds in the presence of novel framework materials
DE10226415A1 (de) * 2002-06-13 2003-12-24 Basf Ag Verfahren zur Herstellung von Polyetheralkoholen
US7094811B2 (en) 2002-10-03 2006-08-22 Bayer Corporation Energy absorbing flexible foams produced in part with a double metal cyanide catalyzed polyol
DE10259184B3 (de) 2002-12-18 2004-09-09 Bayer Ag Stabile Polyoldispersionen und daraus hergestellte Polyurethanformkörper und ihre Verwendung
ATE466865T1 (de) 2003-05-09 2010-05-15 Univ Michigan Mofs mit einer hohen oberfläche und methode zu deren herstellung
DE10324998A1 (de) * 2003-06-03 2004-12-23 Basf Ag Herstellung von Polyetheralkoholen unter Verwendung der DMC-Katalyse
DE102004013408A1 (de) * 2004-03-18 2005-10-06 Basf Ag Polyetheralkohole und Verfahren zur Herstellung von Polyetheralkoholen zur Polyurethansynthese
DE102004047524A1 (de) * 2004-09-28 2006-03-30 Basf Ag Verfahren zur Herstellung von Polyurethan-Weichschaumstoffen
CN101189244A (zh) 2004-10-22 2008-05-28 密歇根大学董事会 共价连接的有机骨架和多面体
BRPI0516890A (pt) * 2004-10-26 2008-09-23 Dow Global Technologies Inc processo para preparar um poliéter, composição de poliéter e composição iniciadora
DE102004062540A1 (de) * 2004-12-24 2006-07-06 Bayer Materialscience Ag Polyurethan-Hartschaumstoffe, ein Verfahren zu ihrer Herstellung sowie ihre Verwendung
PT1874459E (pt) 2005-04-07 2016-02-08 Univ Michigan Alta adsorção de gás numa estrutura microporosa organometálica com locais metálicos abertos
WO2007038508A2 (en) 2005-09-26 2007-04-05 The Regents Of The University Of Michigan Metal-organic frameworks with exceptionally high capacity for storage of carbon dioxide at room-temperature
PL1988996T3 (pl) 2006-02-28 2018-01-31 Univ Michigan Regents Otrzymywanie szkieletów zeolitu z grupami funkcyjnymi
TW200801060A (en) * 2006-02-28 2008-01-01 Asahi Glass Co Ltd Flexible polyurethane foam and process for producing the same
US20070299153A1 (en) * 2006-06-23 2007-12-27 Hager Stanley L Viscoelastic foams with slower recovery and improved tear
DE102007002555A1 (de) * 2007-01-17 2008-07-24 Bayer Materialscience Ag Doppelmetallcyanid-Katalysatoren für die Herstellung von Polyetherpolyolen
US20090012195A1 (en) * 2007-07-05 2009-01-08 Neff Raymond A Resin composition for use in forming a polyurethane article with increased comfort
CN101121784B (zh) * 2007-08-07 2010-05-19 江苏钟山化工有限公司 一种蓖麻油基聚醚多元醇的合成方法
US8901187B1 (en) 2008-12-19 2014-12-02 Hickory Springs Manufacturing Company High resilience flexible polyurethane foam using MDI
US20100160470A1 (en) * 2008-12-23 2010-06-24 Smiecinski Theodore M Flexible Polyurethane Foam
US8604094B2 (en) 2008-12-23 2013-12-10 Basf Se Flexible polyurethane foam and method of producing same
US8906975B1 (en) 2009-02-09 2014-12-09 Hickory Springs Manufacturing Company Conventional flexible polyurethane foam using MDI
US20110230581A1 (en) * 2010-03-17 2011-09-22 Bayer Materialscience Llc Process for the production of polyether polyols with a high ethylene oxide content
EP2560944A4 (en) * 2010-04-23 2014-03-26 Bayer Materialscience Llc POLYOLS SUITABLE FOR THE MANUFACTURE OF A HOT-REFILLED FOAM WITH HIGH QUANTITY OF RENEWABLE RESOURCES
MX344909B (es) * 2010-05-14 2017-01-11 Basf Se Métodos para producir polieteroles.
AU2011293802B2 (en) * 2010-08-24 2014-03-27 Dow Global Technologies Llc Ethylene oxide/propylene oxide polyether polyols and polyurethanes made therefrom
EP2758443B1 (en) * 2011-09-21 2019-02-27 Dow Global Technologies LLC Polyurethanes made using mixtures of tertiary amine compounds and lewis acids as catalysts
SG10201604976RA (en) 2011-12-20 2016-08-30 Bayer Ip Gmbh Hydroxy-aminopolymers and method for producing same
KR101448684B1 (ko) * 2012-12-11 2014-10-13 삼두종합기술주식회사 폴리에테르의 제조방법
MX382310B (es) * 2013-05-30 2025-03-13 Dow Global Technologies Llc Polioles híbridos.
CN103722637A (zh) * 2013-12-27 2014-04-16 哈尔滨市合众聚氨酯制品有限公司 大孔径聚酯型聚氨酯软泡的生产方法及使用的分流装置
US11518841B2 (en) * 2017-07-20 2022-12-06 Bionanofoam Llc Bio-based and hydrophilic polyurethane prepolymer and foam made therefrom
US11597793B2 (en) * 2016-07-21 2023-03-07 Bionanofoam Llc Bio-based and hydrophilic polyurethane prepolymer mixture
US10975190B2 (en) * 2016-07-21 2021-04-13 Bionanofoam Llc Bio-based and hydrophilic polyurethane prepolymer and foam made therefrom
PT3526267T (pt) * 2016-10-17 2023-07-12 Basf Se Compósito de pu reforçado com tecido espaçador 3d e sua utilização
EP3920860B1 (de) * 2019-02-07 2024-05-29 Basf Se Polyurethanweichschaumstoffe mit hoher wasseraufnahmefähigkeit
CN111072915A (zh) * 2019-12-11 2020-04-28 山东省海洋化工科学研究院 一种聚氨酯泡沫组合物及利用该组合物制备聚氨酯泡沫的方法

Family Cites Families (32)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE203735C (enExample)
GB1034482A (en) † 1963-01-11 1966-06-29 Lankro Chem Ltd Improvements in or relating to polyethers and polyurethanes obtained therefrom
US3427256A (en) 1963-02-14 1969-02-11 Gen Tire & Rubber Co Double metal cyanide complex compounds
US3427335A (en) 1963-02-14 1969-02-11 Gen Tire & Rubber Co Double metal cyanides complexed with an acyclic aliphatic saturated monoether,an ester and a cyclic ether and methods for making the same
US3427334A (en) 1963-02-14 1969-02-11 Gen Tire & Rubber Co Double metal cyanides complexed with an alcohol aldehyde or ketone to increase catalytic activity
US4143004A (en) † 1974-10-02 1979-03-06 Berol Kemi Ab Process for the preparation of polyurethane foam
IT1058454B (it) † 1976-03-17 1982-04-10 Montedison Spa Tprcedimento per la produzione di schiume poliuretaniche soffici ed extra supersoffici
DE2832253A1 (de) 1978-07-22 1980-01-31 Bayer Ag Verfahren zur herstellung von formschaumstoffen
DD203735A1 (de) * 1981-12-24 1983-11-02 Adw Ddr Verfahren zur kontinuierlichen herstellung von polyetheralkoholen
JP2999789B2 (ja) * 1990-02-23 2000-01-17 旭硝子株式会社 ポリエーテル類の製造方法
JPH0517569A (ja) * 1991-07-08 1993-01-26 Asahi Glass Co Ltd ポリエーテル類の製造方法
JP3358846B2 (ja) * 1992-06-18 2002-12-24 三井武田ケミカル株式会社 低密度超軟質ウレタンフォームの製造方法
US5482908A (en) 1994-09-08 1996-01-09 Arco Chemical Technology, L.P. Highly active double metal cyanide catalysts
US5545601A (en) 1995-08-22 1996-08-13 Arco Chemical Technology, L.P. Polyether-containing double metal cyanide catalysts
US5700847A (en) * 1995-12-04 1997-12-23 Arco Chemical Technology, L.P. Molded polyurethane foam with enhanced physical properties
US5668191A (en) * 1995-12-21 1997-09-16 Arco Chemical Technology, L.P. One-shot cold molded flexible polyurethane foam from low primary hydroxyl polyols and process for the preparation thereof
US5605939A (en) * 1996-01-26 1997-02-25 Arco Chemical Technology, L.P. Poly(oxypropylene/oxyethylene) random polyols useful in preparing flexible high resilience foam with reduced tendencies toward shrinkage and foam prepared therewith
US5627120A (en) 1996-04-19 1997-05-06 Arco Chemical Technology, L.P. Highly active double metal cyanide catalysts
US5689012A (en) 1996-07-18 1997-11-18 Arco Chemical Technology, L.P. Continuous preparation of low unsaturation polyoxyalkylene polyether polyols with continuous additon of starter
US5714428A (en) 1996-10-16 1998-02-03 Arco Chemical Technology, L.P. Double metal cyanide catalysts containing functionalized polymers
US5958994A (en) * 1997-02-25 1999-09-28 Arco Chemical Technology, L.P. Method for decreasing the propensity for phase-out of the high molecular weight component of double metal cyanide-catalyzed high secondary hydroxyl polyoxypropylene polyols
US5783513A (en) * 1997-03-13 1998-07-21 Arco Chemical Technology, L.P. Process for making double metal cyanide catalysts
DE19745120A1 (de) * 1997-10-13 1999-04-15 Bayer Ag Verbesserte Doppelmetallcyanid-Katalysatoren für die Herstellung von Polyetherpolyolen
CA2306378C (en) 1997-10-13 2007-07-17 Bayer Aktiengesellschaft Crystalline double metal cyanide catalysts for producing polyether polyols
US6624286B2 (en) 1997-10-13 2003-09-23 Bayer Aktiengesellschaft Double-metal cyanide catalysts containing polyester for preparing polyether polyols
DE19757574A1 (de) 1997-12-23 1999-06-24 Bayer Ag Verbesserte Doppelmetallcyanid-Katalysatoren für die Herstellung von Polyetherpolyolen
DE19810269A1 (de) 1998-03-10 2000-05-11 Bayer Ag Verbesserte Doppelmetallcyanid-Katalysatoren für die Herstellung von Polyetherpolyolen
US6066683A (en) * 1998-04-03 2000-05-23 Lyondell Chemical Worldwide, Inc. Molded and slab polyurethane foam prepared from double metal cyanide complex-catalyzed polyoxyalkylene polyols and polyols suitable for the preparation thereof
US6008263A (en) † 1998-04-03 1999-12-28 Lyondell Chemical Worldwide, Inc. Molded and slab polyurethane foam prepared from double metal cyanide complex-catalyzed polyoxyalkylene polyols and polyols suitable for the preparation thereof
DE19817676A1 (de) 1998-04-21 1999-10-28 Bayer Ag Verfahren zur aufarbeitungsfreien Herstellung langkettiger Polyetherpolyole
US6063309A (en) * 1998-07-13 2000-05-16 Arco Chemical Technology L.P. Dispersion polyols for hypersoft polyurethane foam
DE19918727A1 (de) * 1999-04-24 2000-10-26 Bayer Ag Langkettige Polyetherpolyole mit hohem Anteil primärer OH-Gruppen

Also Published As

Publication number Publication date
NO20016196L (no) 2001-12-18
KR100697731B1 (ko) 2007-03-22
PL209418B1 (pl) 2011-08-31
MXPA01012985A (es) 2002-09-02
ZA200109264B (en) 2003-01-29
ES2228545T3 (es) 2005-04-16
JP2003503516A (ja) 2003-01-28
SI1194468T1 (en) 2005-02-28
AU768450B2 (en) 2003-12-11
CA2375285A1 (en) 2000-12-28
DE19928156A1 (de) 2000-12-28
NO20016196D0 (no) 2001-12-18
JP5600079B2 (ja) 2014-10-01
NO329941B1 (no) 2011-01-24
CN1355819A (zh) 2002-06-26
SI1194468T2 (sl) 2011-05-31
HK1047598B (zh) 2005-06-03
EP1194468A1 (de) 2002-04-10
EP1194468B1 (de) 2004-09-15
AU5529500A (en) 2001-01-09
PT1194468E (pt) 2004-12-31
HK1047598A1 (en) 2003-02-28
KR20020013929A (ko) 2002-02-21
ATE276299T1 (de) 2004-10-15
DK1194468T4 (da) 2011-03-07
DE50007798D1 (de) 2004-10-21
TW591045B (en) 2004-06-11
JP4768178B2 (ja) 2011-09-07
EP1194468B2 (de) 2011-01-26
CA2375285C (en) 2009-03-24
WO2000078837A1 (de) 2000-12-28
JP2011099124A (ja) 2011-05-19
US6858655B1 (en) 2005-02-22
PL352110A1 (en) 2003-07-28
ES2228545T5 (es) 2011-05-06
BR0011777A (pt) 2002-03-19
DK1194468T3 (da) 2005-01-17

Similar Documents

Publication Publication Date Title
CN1170867C (zh) 用聚醚多元醇生产的聚氨酯软泡沫
CN1281650C (zh) 粘弹性聚氨酯
CN1174022C (zh) 环氧烷开环聚合用催化剂及其制造方法和用途
CN1262584C (zh) 具有改进的水解稳定性的聚氨酯高弹体
CN1104452C (zh) 具有致密表面和多孔芯层的弹性聚氨酯模塑制件的生产方法
CN1152905C (zh) 新颖聚氧化烯多元醇和制备开环聚合物的方法
JP7250806B2 (ja) 軟質ポリウレタンフォーム
CN101056911A (zh) 软质聚氨酯泡沫塑料的制造方法
CN110402263B (zh) 具有降低的温度敏感性的粘弹性聚氨酯泡沫
HK1044345A1 (zh) 改進濕强度和脫模時間的聚氨酯高彈體以及適於其製備的聚氧亞烷基多元醇
CN1310990C (zh) 泡沫聚氨酯的挠性模制品及其用途
TW201116548A (en) Process for production of flexible polyurethane foam
CN1121578A (zh) 绝热材料及其生产方法
CN1240743C (zh) 多异氰酸酯组合物和由这些多异氰酸酯组合物制造具有低的湿态老化压缩形变的低密度软泡沫塑料的方法
CN1046295C (zh) 聚氨酯及其制备方法和制备聚氨酯泡沫体的方法
CN101031600A (zh) 生产柔性聚氨酯泡沫材料的方法
EP4056615A1 (en) Novel in-situ formed polyols, a process for their preparation, foams prepared from these in-situ formed polyols and a process for their preparation
CN1668664A (zh) 含聚合物改性剂的聚异氰酸酯和聚氨酯及其用途
CN1039423C (zh) 软质泡沫塑料的制备方法
JP2005088591A (ja) 離型剤、プラスチック成形およびそれら製品の製造方法
CN1847281A (zh) 软质聚氨酯泡沫板用聚异氰酸酯以及使用其的软质聚氨酯泡沫板的制造方法
JP2001106789A (ja) シリコーンポリエーテル共重合体及びそれらのポリウレタン軟質成形フォームにおける使用
HK1147102A1 (en) Method for producing supersoft polyurethane

Legal Events

Date Code Title Description
C06 Publication
PB01 Publication
C10 Entry into substantive examination
SE01 Entry into force of request for substantive examination
C14 Grant of patent or utility model
GR01 Patent grant
ASS Succession or assignment of patent right

Owner name: CARCOUSTICS TECHCONSULT GMBH

Free format text: FORMER OWNER: BAYER AKTIENGESELLSCHAFT

Effective date: 20120731

C41 Transfer of patent application or patent right or utility model
TR01 Transfer of patent right

Effective date of registration: 20120731

Address after: Germany Leverkusen

Patentee after: Carcoustics Techconsult GmbH

Address before: Germany Leverkusen

Patentee before: Bayer Aktiengesellschaft

EE01 Entry into force of recordation of patent licensing contract

Application publication date: 20020626

Assignee: Bayer Material Science (China) Co., Ltd.

Assignor: Carcoustics Techconsult GmbH

Contract record no.: 2012990000854

Denomination of invention: Polyurethane foams produced from polyether polyols

Granted publication date: 20041013

License type: Common License

Record date: 20121128

LICC Enforcement, change and cancellation of record of contracts on the licence for exploitation of a patent or utility model
C56 Change in the name or address of the patentee
CP03 Change of name, title or address

Address after: Leverkusen, Germany

Patentee after: BAYER MATERIALSCIENCE AG

Address before: Germany Leverkusen

Patentee before: Carcoustics Techconsult GmbH

CX01 Expiry of patent term
CX01 Expiry of patent term

Granted publication date: 20041013