CN111097410A - 一种钌系氨合成催化剂及其制备方法与应用 - Google Patents
一种钌系氨合成催化剂及其制备方法与应用 Download PDFInfo
- Publication number
- CN111097410A CN111097410A CN201911246502.1A CN201911246502A CN111097410A CN 111097410 A CN111097410 A CN 111097410A CN 201911246502 A CN201911246502 A CN 201911246502A CN 111097410 A CN111097410 A CN 111097410A
- Authority
- CN
- China
- Prior art keywords
- ruthenium
- ammonia synthesis
- synthesis catalyst
- activated carbon
- barium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (14)