CN110582411A - 印刷用纸 - Google Patents
印刷用纸 Download PDFInfo
- Publication number
- CN110582411A CN110582411A CN201880029037.3A CN201880029037A CN110582411A CN 110582411 A CN110582411 A CN 110582411A CN 201880029037 A CN201880029037 A CN 201880029037A CN 110582411 A CN110582411 A CN 110582411A
- Authority
- CN
- China
- Prior art keywords
- coating layer
- outermost coating
- pigment
- printing paper
- printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种印刷用纸,其在原纸上具有涂敷层,其中,最外涂敷层含有颜料、粘结剂、润滑剂、分散剂和阳离子性树脂,高岭土和碳酸钙的含量相对于颜料100质量份为80质量份以上,而且高岭土与碳酸钙的含量质量比为1:9~6:4,并且最外涂敷层表面满足(I)、(II)和(III)中的至少任一特征。(I):当滴加表面张力为20mN/m的水溶液时,液滴与最外涂敷层的接触角在接触1秒后为40°以上且65°以下。(II):用布里斯托法求出的当接触时间为1秒时表面张力为20mN/m的水溶液的转移量为5.0ml/m2以上且12.0ml/m2以下。(III):点图像的镜面反射光量的最大峰值为2000以上且30000以下。
Description
技术领域
本发明涉及一种印刷用纸,其为面向胶版印刷机的印刷用纸,但也可以用喷墨印刷机进行印刷。
背景技术
喷墨记录方式是通过使墨液的液滴从微细的喷嘴喷出到记录用纸上并使其附着在用纸上从而形成墨点来进行记录的方式。
喷墨记录方式被用于面向家庭和面向SOHO的小型打印机、用于制作POP或海报的宽幅打印机、以及用于生产商业印刷物的按需印刷机。使用的印刷用纸存在从亚光感到光泽感的各种光泽感。从印刷物的成本、印刷物生产率和印刷物的处理方法的角度出发,对用于生产商业文书、DM、书籍、小册子、传单、小论文、产品目录等商业印刷物的印刷用纸和喷墨记录方式中为了代替卤化银照片而开发的照片用纸所要求的品质是不同的。
作为抑制了由墨点的扩散不良所致的图像的白纹(日文:白筋)、且在使用按需喷墨印刷机的高速印刷中也具有高印刷品质的按需喷墨印刷用纸,公知一种按需喷墨印刷用纸,其特征在于,在支撑体上的至少单面,设有含有颜料、粘结剂、表面活性剂和微阳离子性高分子的墨液接受层,微阳离子性高分子的阳离子化度为超过0meq/g且3.00meq/g以下,在向墨液接受层滴加利用Wilhelmy Plate法测得的表面张力为25mN/m的液体时,滴加0.1秒后的液滴与墨液接受层的接触角在10°~40°的范围内(例如,参照专利文献1)。
关于可以通过喷墨记录方式而记录接近胶版印刷等商业印刷的高图像质量图像的记录用墨液、记录用介质、墨液介质套件、墨液记录物、以及喷墨记录方法和喷墨记录装置,公知一种墨液介质套件,该墨液介质套件具有墨液、支撑体、和在该支撑体的至少一侧的面具有涂敷层的记录用介质,用动态扫描吸液计测定的、接触时间100ms时上述墨液向上述记录用介质的转移量为4ml/m2~15ml/m2、且接触时间400ms时上述墨液向上述记录用介质的转移量为7ml/m2~20ml/m2,其中,上述墨液至少含有水、着色剂和润湿剂,且25℃时的表面张力为20mN/m~35mN/m(例如,参照专利文献2)。
对于胶版印刷机、凸版印刷机等刷版(日文:刷版)印刷机而言,形成有印刷图像的“版”是必不可少的。另一方面,按需印刷机则不需要“版”。即,按需印刷机是使图像形成装置按照与图像相关的数字信息在用纸上直接进行印刷的。
有使用喷墨记录方式的按需印刷机、即喷墨印刷机。作为喷墨印刷机的例子,有SCREEN Graphic and Precision Solutions公司的TruepressJet、Miyakoshi公司的MJP系列、柯达公司的Prosper和VERSAMARK、富士胶片公司的JetPress、Hewlett-Packard公司的ColorInkjetWebPress等。
这种喷墨印刷机依赖于印刷的各种条件,但是与面向家庭和面向SOHO的小型喷墨打印机、以及宽幅喷墨打印机相比,彩色印刷速度高达10倍~数十倍,印刷速度为15m/分钟钟以上,更高速时超过100m/分钟。因此,喷墨印刷机有别于面向家庭和面向SOHO的小型喷墨打印机以及宽幅喷墨打印机。
入射至纸的光在纸的表面发生反射,而且在纸的内部发生散射、反射或吸收。这种光的反射、散射、吸收是在纸中发生的物理现象。对于印刷用纸而言,光的反射会影响到人类所感觉到的图像的清晰度、质感和光泽感。特别是对于具有涂敷层的印刷用纸而言,光的反射有强烈影响。
纸的表面所发生的反射中包括镜面反射。镜面反射是指:从试样表面的法线方向分别向相反侧以相同的角度进行入射和受光的光的反射,也被称为正反射。另外,光泽是主要由反射光的强度来决定的视觉属性。
一直以来,尝试用定量性的测定值对人类主观性的光泽感进行评价。例如。作为测定镜面光泽的方法,已知ISO2813:1994和ISO8254-1:1999,另外作为测定图像清晰度的方法,已知JIS K7374:2007(例如,参照非专利文献1~3)。
但是,上述方法有时不足以评价人类主观性的光泽感。作为用定量性的测定值来评价用上述方法无法获得的人类的主观性的光泽感的方法和测定装置,已知下述的点图像的镜面反射光分布测定方法和点图像的镜面反射光分布测定装置,所述点图像的镜面反射光分布测定方法的特征在于,包含下述工序:以点图像为光源利用准直透镜生成平行光的工序、使该平行光入射至试样的工序、接受入射至该试样的该平行光的镜面反射光并利用准直透镜成像而恢复为点图像的工序、和测定该成像点图像的光量分布的工序,其中,包含由所测定的该成像点图像的光量分布计算该试样的变角光度(日文:変角光度)和偏角光度(日文:偏角光度)的工序;所述点图像的镜面反射光分布测定装置的特征在于,包含下述单元:以点图像为光源利用准直透镜生成平行光的单元、使该平行光入射至试样的单元、接受该入射至试样的该平行光的镜面反射光并利用准直透镜成像而恢复为点图像的单元、和测定该成像点图像的光量分布的单元,其中,包含由所测定的该成像点图像的光量分布来计算该试样的变角光度和偏角光度的单元(例如,参照专利文献3)。
在点图像的镜面反射光分布测定中,将点图像输入光学系统、并且将输出的点图像与原点图像进行比较,如果发生点图像扩大的现象则通常图像会模糊。
现有技术文献
专利文献
专利文献1:日本特开2017-13261号公报
专利文献2:日本特开2007-216664号公报
专利文献3:日本专利第5204723号公报
非专利文献
非专利文献1:ISO2813:1994“Paints and varnishes-Determination ofspecular gloss of non-metallic paint films at 20°,60°and 85°”
非专利文献2:ISO8254-1:1999“Paper and board-Measurement of speculargloss-Part1:75°gloss with a converging beam,TAPPI method”
非专利文献3:JIS K7374:2007“Plastics-Determination of image clarity”
发明内容
发明要解决的课题
随着按需印刷机的普及,印刷用纸不仅要应对刷版印刷机,还需要应对按需印刷机。特别是需要可应用于商业印刷物的生产中较多使用的胶版印刷机和喷墨印刷机。
就胶版印刷机而言,附着于刷版的墨液隔着胶布而接触并被转印于印刷用纸,从而生产印刷物。就喷墨印刷机而言,从与用纸不接触的微细喷嘴将墨滴喷出到印刷用纸上,从而生产印刷物。由于这种印刷机制的差异,胶版印刷机的墨液具有粘合性且色材含量浓度高。喷墨印刷机的墨液具有流动性且色材含量浓度低。
因此,为了解决下述课题,即实现具有胶版印刷机适应性且用喷墨印刷机也能印刷的印刷用纸这一课题,期望逐个解决如下所述的细化的课题的方法。
第一课题如下。
将以往的面向胶版印刷机的印刷用纸用于喷墨印刷机时,具有发生印刷部分的透印和印刷部分的点扩散不良的缺点。“透印”是指:墨液没有止于印刷侧的面而是达到原纸的深部,从而从印刷面的背面侧可辨识印刷部分的现象。商业印刷物多数情况下进行双面印刷,透印的发生会使商业印刷物的价值降低。“点扩散不良”是指:在墨液与印刷用纸碰撞并被其吸收的过程中墨滴在纸的平面方向扩散不足的现象。因此,由墨滴形成的点的重叠不足,在图像部产生脱墨、在纸的输送方向产生白色条纹。这被称为“白纹”,会使商业印刷物的价值降低。
第二课题如下。
将以往的面向胶版印刷机的印刷用纸用于喷墨印刷机时,随着印刷速度变快,印刷用纸的墨液吸收性方面产生部分偏差,有时印刷部分的颜色浓度(日文:色濃度)变得不均。其原因在于,喷墨印刷机的墨液具有流动性且色材含量浓度低。
另外,随着印刷速度变快而印刷用纸不能顺利进行墨液接受时,有时在印刷部分点再现性下降。点再现性下降则图像质量变差。其原因在于,印刷速度快则用纸输送速度相应变快,附着于印刷用纸表面的墨滴在落到用纸表面时会流动。即,落在用纸表面的墨滴所形成的点变形或点的轮郭变得不清晰,从而引起图像质量下降。
另外,当喷墨印刷机的墨液中所含的墨液溶剂到达原纸时,有时原纸会由于纤维的伸缩而发生波动(日文:波打ち)。由于墨液溶剂而发生的波动会引起喷墨印刷机的打印头与纸的接触故障、或印刷后加工时的尺寸不良故障等。
第三课题如下。
将以往的面向胶版印刷机的印刷用纸用于喷墨印刷机时,有时随着印刷速度加快而墨液的吸收不能追随、产生印刷污染。另外,包含5号以下的小字的印刷部分有时作为文字是难以识别的。一般将是否可作为文字来识别称为辨识性,辨识性表示文字的观察容易程度。例如,就绿色用纸上的蓝色文字或白色用纸上的黄色文字而言,辨识性下降。
我们认为,产生印刷污染或作为文字难以识别的原因在于胶版印刷机与喷墨印刷机的印刷方法和墨液的差异。
另外,随着印刷速度变快而墨液在印刷用纸上的定影不足时,存在用手擦拭印刷物则墨液剥离的情况。海报、小册子、产品目录、POP、DM和广告页等商业印刷物与手接触的较多,不会发生墨液剥离这一点很重要。
本发明的目的在于,提供一种虽为具有对胶版印刷机的适应性的印刷用纸但为了可以用喷墨印刷机进行印刷,而针对喷墨印刷机具有下述品质的印刷用纸。
针对第一课题,提供具有下述品质的印刷用纸:
(1)印刷部分的显色优异(显色性)
(2)印刷部分的透印得到抑制(耐透印性)
(3)印刷部分的点扩散不良得到抑制(耐点扩散不良性)。
针对第二课题,提供具有下述品质的印刷用纸:
(4)印刷部分的颜色浓度均匀(颜色浓度均匀性)。
(5)印刷部分的点再现性优异(点再现性)。
(6)印刷部分的波动得到抑制(耐波动性)。
针对第三课题,提供具有下述品质的印刷用纸:
(7)印刷污染得到抑制(耐印刷污染性)
(8)小文字的辨识性优异(文字辨识性)
(9)印刷部分的墨液剥离得到抑制(耐擦蹭性)。
用于解决课题的方案
本发明人们进行了深入研究,结果通过以下方案实现了本发明的目的。
[1]一种印刷用纸,其具有原纸和位于上述原纸的至少单面的1层以上的涂敷层,在上述涂敷层中,以原纸为基准位于最外侧的最外涂敷层至少含有颜料、粘结剂、润滑剂、分散剂和阳离子性树脂,最外涂敷层中的颜料包含高岭土和碳酸钙,高岭土和碳酸钙的含量相对于最外涂敷层中的颜料100质量份为80质量份以上,而且高岭土与碳酸钙在最外涂敷层中的含量质量比为1:9~6:4,并且上述印刷用纸满足以下特征(I)、(II)和(III)中的至少任一特征。
(I):对于印刷用纸的具有最外涂敷层那一侧,当滴加表面张力为20mN/m的水溶液时,液滴与最外涂敷层的接触角在接触1秒后为40°以上且65°以下。
(II):对于印刷用纸的具有最外涂敷层那一侧,用布里斯托法(日文:ブリストー法)求出的当接触时间为1秒时表面张力为20mN/m的水溶液的转移量为5.0ml/m2以上且12.0ml/m2以下。
(III):在印刷用纸的最外涂敷层的表面,点图像的镜面反射光量的最大峰值为2000以上且30000以下。
根据上述[1],印刷用纸具有对胶版印刷机的适应性,并且,针对喷墨印刷机,通过满足特征(I)而可以具有第一课题即显色性、耐透印性和耐点扩散不良性的品质,通过满足特征(II)而可以具有第二课题即颜色浓度均匀性、点再现性和耐波动性的品质,且通过满足特征(III)而可以具有第三课题即耐印刷污染性、文字辨识性和耐擦蹭性的品质。
[2]根据上述[1]所述的印刷用纸,其具有原纸和位于上述原纸的至少单面的1层以上的涂敷层,在上述涂敷层中,以原纸为基准位于最外侧的最外涂敷层至少含有颜料、粘结剂、润滑剂、分散剂和阳离子性树脂,最外涂敷层中的颜料包含高岭土和碳酸钙,高岭土和碳酸钙的含量相对于最外涂敷层中的颜料100质量份为80质量份以上,而且高岭土与碳酸钙在最外涂敷层中的含量质量比为1:9~6:4,并且上述印刷用纸满足上述特征(I)。
根据上述[2],印刷用纸具有对胶版印刷机的适应性,并且,可以具有针对喷墨印刷机的显色性、耐透印性和耐点扩散不良性的品质。
[3]根据上述[1]所述的印刷用纸,其具有原纸和位于上述原纸的至少单面的1层以上的涂敷层,在上述涂敷层中,以原纸为基准位于最外侧的最外涂敷层至少含有颜料、粘结剂、润滑剂、分散剂和阳离子性树脂,最外涂敷层中的颜料包含高岭土和碳酸钙,高岭土和碳酸钙的含量相对于上述最外涂敷层中的颜料100质量份为80质量份以上,而且高岭土与碳酸钙在最外涂敷层中的含量质量比为1:9~6:4,并且上述印刷用纸满足上述特征(II)。
根据上述[3],印刷用纸具有对胶版印刷机的适应性,并且,可以具有针对喷墨印刷机的颜色浓度均匀性、点再现性和耐波动性的品质。
[4]根据上述[3]所述的印刷用纸,其中,对于印刷用纸的具有最外涂敷层那一侧,测定用布里斯托法求出的当接触时间为0.4秒时表面张力为20mN/m的水溶液的转移量,[用布里斯托法求出的当接触时间为1秒时表面张力为20mN/m的水溶液的转移量]-[用布里斯托法求出的当接触时间为0.4秒时表面张力为20mN/m的水溶液的转移量]的值为0.5ml/m2以上且2.5ml/m2以下。
根据上述[4],印刷用纸的针对喷墨印刷机的颜色浓度均匀性或耐波动性的品质进一步变好。
[5]根据上述[1]所述的印刷用纸,其具有原纸和位于上述原纸的至少单面的1层以上的涂敷层,在上述涂敷层中,以原纸为基准位于最外侧的最外涂敷层至少含有颜料、粘结剂、润滑剂、分散剂和阳离子性树脂,最外涂敷层中的颜料包含高岭土和碳酸钙,高岭土和碳酸钙的含量相对于上述最外涂敷层中的颜料100质量份为80质量份以上,而且高岭土与碳酸钙在最外涂敷层中的含量质量比为1:9~6:4,并且上述印刷用纸满足上述特征(III)。
根据上述[5],印刷用纸具有对胶版印刷机的适应性,并且,可以具有针对喷墨印刷机的耐印刷污染性、文字辨识性和耐擦蹭性的品质。
附图说明
图1是用于测定点图像的镜面反射光量的装置的概略图。
具体实施方式
以下详细说明本发明。
本发明的印刷用纸具有原纸和位于上述原纸的至少单面的涂敷层。在上述涂敷层中,以原纸为基准位于最外侧的最外涂敷层至少含有颜料、粘结剂、润滑剂、分散剂和阳离子性树脂。
本发明中,“具有涂敷层”是指:在用电子显微镜观察用纸的截面时,具有与原纸可区别的明确的涂敷层的用纸。例如,将树脂成分、聚合物成分进行涂敷,所涂敷的上述成分为少量并被原纸吸收,结果在用电子显微镜观察印刷用纸的截面时不具有与原纸可区别的明确的层,则这种情况不属于“具有涂敷层”。
原纸是对纸料进行抄制而成的抄制纸,所述纸料是在选自LBKP(Leaf BleachedKraft Pulp,短纤维漂白硫酸盐浆)、NBKP(Needle Bleached Kraft Pulp,针叶木漂白硫酸盐浆)等化学纸浆、GP(Groundwood Pulp,磨木浆)、PGW(Pressure GroundWood pulp,压力磨石磨木浆)、RMP(Refiner Mechanical Pulp,木片磨木浆)、TMP(ThermoMechanicalPulp,热磨机械浆)、CTMP(ChemiThermoMechanical Pulp,化学热磨机械浆)、CMP(ChemiMechanical Pulp,化学机械浆)、CGP(ChemiGroundwood Pulp,化学机械木浆)等机械纸浆和DIP(DeInked Pulp,脱墨废纸浆)等旧纸纸浆中的至少1种纸浆中,根据需要配合轻质碳酸钙、重质碳酸钙、滑石、粘土、高岭土等各种填料以及施胶剂、定影剂、助留剂、阳离子性树脂、多价阳离子盐等阳离子化剂、造纸增强剂等各种添加剂而成的。此外,原纸中包括对抄制纸实施压光处理、利用淀粉或聚乙烯醇等的表面施胶处理、或表面处理等而得的铜版纸(日文:上質紙)。此外,原纸中包括实施表面施胶处理或表面处理后进行压光处理而得的铜版纸。
纸料中,可以在不损害本发明的期望效果的范围内适当配合作为其它添加剂的颜料分散剂、增粘剂、流动性改良剂、消泡剂、抑泡剂、脱模剂、发泡剂、渗透剂、着色染料、着色颜料、荧光增白剂、紫外线吸收剂、抗氧化剂、防腐剂、防霉剂、耐水化剂、润湿纸力增强剂、干燥纸力增强剂等中的一种或两种以上。
涂敷层可以通过将涂敷层涂敷液进行涂敷并干燥而设置在原纸的至少单面。涂敷层为1层或2层以上。在涂敷层中,将以原纸为基准位于最外侧的涂敷层称为最外涂敷层。在涂敷层为1层时,该涂敷层即为最外涂敷层。最外涂敷层至少含有颜料、粘结剂、润滑剂、分散剂和阳离子性树脂。需要说明的是,对于存在于原纸和最外涂敷层之间的涂敷层,在颜料、粘结剂、润滑剂、分散剂和阳离子性树脂各自的有无和种类方面没有特别限定。
涂敷层的各涂敷量没有特别限定。优选的涂敷量以干燥固体成分量计每一面在5g/m2以上且30g/m2以下的范围内。在涂敷层为2层以上时,为它们的合计值。在涂敷层为2层以上时,优选最外涂敷层以干燥固体成分量计占每单面涂敷量的70质量%。
可以在原纸的单面或两面具有涂敷层。另外,单面的情况下,在原纸中的与具有涂敷层的那一侧的相反面可以具有现有公知的背涂层。
在原纸上设置涂敷层的方法没有特别限定。例如,可以列举:使用制纸领域中现有公知的涂敷装置和干燥装置,将涂敷层涂敷液进行涂敷并干燥的方法。作为涂敷装置的例子,可列举:逗号涂布机、薄膜施胶压榨涂布机、气刀涂布机、棒刮刀涂布机、棒涂机、刮刀涂布机、凹版涂布机、幕帘涂布机、微凹辊涂布机(日文:Eバーコーター)、膜转移涂布机等。作为干燥装置的例子,可列举:直线隧道式干燥机、拱形干燥机、空气循环干燥机、正弦曲线气浮干燥机等热风干燥机、红外线加热干燥机、利用微波等的干燥机等各种干燥装置。
涂敷层可以实施压光处理。
压光处理是指:使纸在辊间通过而使平滑性和厚度平均化的处理。作为压光处理的装置,可列举例如机械压光机、软压区压光机、超级压光机、多级压光机、多压区压光机等。
本发明的印刷用纸不包括对最外涂敷层实施了浇铸(日文:キャスト)处理的印刷用纸。
本发明的印刷用纸满足以下的特征(I)、(II)和(III)中的至少任一特征。更优选满足选自上述特征(I)~(III)中的2个,进一步优选满足上述特征(I)~(III)中的全部。
(I):对于印刷用纸的具有最外涂敷层那一侧,当滴加表面张力为20mN/m的水溶液时,液滴与最外涂敷层的接触角在接触1秒后为40°以上且65°以下。
(II):对于印刷用纸的具有最外涂敷层那一侧,用布里斯托法求出的当接触时间为1秒时表面张力为20mN/m的水溶液的转移量为5.0ml/m2以上且12.0ml/m2以下。
(III):在印刷用纸的最外涂敷层的表面,点图像的镜面反射光量的最大峰值为2000以上且30000以下。
对上述特征(I)进行说明。
就满足上述特征(I)的印刷用纸而言,在对具有最外涂敷层的那一侧滴加表面张力为20mN/m的水溶液时,液滴与最外涂敷层的接触角在接触1秒后为40°以上且65°以下。就最近的喷墨印刷机而言,为了可以用以往的胶版印刷用纸进行印刷,而倾向于使用表面张力低的墨液。因此,与使用表面张力高的离子交换水的接触角测定相比,通过使用表面张力低的水溶液的接触角测定,能够进行更符合实际的喷墨印刷机的评价。
接触角可以如下测定:将表面张力为20mN/m的水溶液的液滴1μl滴加到印刷用纸的最外涂敷层,在液滴接触印刷用纸的最外涂敷层表面起的1秒后,使用具有图像数据分析装置的市售的接触角测定装置进行测定。可以通过将液滴的形状假定为正球或椭球体的一部分而计算的曲线拟合法来进行图像数据分析。就这种接触角测定装置而言,有例如协和界面科学公司制自动接触角计CA-VP300。本发明中,作为液滴1μl,只要在1μl±20%的范围内即可,若为该范围则不会妨碍测定。
滴加表面张力为20mN/m的水溶液时,如果液滴与最外涂敷层的接触角在接触1秒后小于40°,则不能得到显色性、耐透印性或耐点扩散不良性。滴加表面张力为20mN/m的水溶液时,如果液滴与最外涂敷层的接触角在接触1秒后超过65°,则不能得到显色性或耐点扩散不良性。
水溶液的表面张力是利用Wilhelmy Plate法测定的值。
就在接触角的测定中使用的表面张力为20mN/m的水溶液而言,只要基于WilhelmyPlate法的表面张力为20mN/m即可,例如,可以通过将甘油、聚乙二醇、丙二醇、乙醇或乙二醇等醇类或全氟烷基磺酸等氟系表面活性剂适量添加到离子交换水中而得到。
例如,如日本特开2014-80715号公报、国际公开第2011/001955号小册子等所记载,涂敷层的接触角是制纸领域中现有公知的物理量,可以通过制纸领域中现有公知的方法来调节。例如,可以通过将涂敷量、颜料的种类、颜料的平均粒径、颜料的粒度分布、颜料的形状、颜料的吸油度、粘结剂的种类、分子量或聚合度、水分散性的粘结剂与水溶性的粘结剂的混合比率、颜料与粘结剂的含有比率等各条件组合来实现。特别地,增加亲水性的颜料、增加水溶性的粘结剂比率、减少粘结剂的比例、配合分散剂和阳离子性树脂等离子性化合物、减少涂敷量等则显示出接触角减小的倾向。增加水分散性的粘结剂比率、配合润滑剂、配合具有长链烷基的疏水性相对较强的表面活性剂等则显示出接触角变大的倾向。另外,在所形成的层表面的状态发生变化的情况下,根据最外涂敷层涂敷液的涂敷以及干燥后的压光处理的有无或压光处理条件,从而接触角发生变化。在所形成的层的状态少许发生变化的情况下,根据设置最外涂敷层时的干燥方法从而接触角发生变化。
对上述特征(II)进行说明。
就满足上述特征(II)的印刷用纸而言,对于具有最外涂敷层的那一侧,用布里斯托法求出的当接触时间为1秒时表面张力为20mN/m的水溶液的转移量为5.0ml/m2以上且12.0ml/m2以下。
用布里斯托法求出的水溶液的转移量为如下测定的值:基于J.TAPPI No.51-2000,使用表面张力为20mN/m的水溶液,并且使用狭缝宽度为0.5mm的喷头,测定接触时间为1秒或后述的0.4秒时的吸水量(ml/m2)。
就最近的喷墨印刷机而言,为了可以用以往的胶版印刷用纸进行印刷,而倾向于使用表面张力低的墨液。因此,与使用表面张力高的离子交换水的接触角测定相比,使用表面张力低的水溶液的接触角测定能够进行更符合实际的喷墨印刷机的评价。
对于印刷用纸的具有最外涂敷层的那一侧,如果当接触时间为1秒时表面张力为20mN/m的水溶液的转移量小于5.0ml/m2,则不能得到颜色浓度均匀性。如果水的转移量超过12.0ml/m2,则不能得到点再现性或耐波动性。
本发明的进一步优选的方式为:对于印刷用纸的具有最外涂敷层的那一侧,用布里斯托法求出的当接触时间为1秒时表面张力为20mN/m的水溶液的转移量为5.0ml/m2以上且12.0ml/m2以下、并且测定当接触时间为0.4秒时表面张力为20mN/m的水溶液的转移量,[用布里斯托法求出的当接触时间为1秒时表面张力为20mN/m的水溶液的转移量]-[用布里斯托法求出的当接触时间为0.4秒时表面张力为20mN/m的水溶液的转移量]的值为0.5ml/m2以上且2.5ml/m2以下。其原因在于,使颜色浓度均匀性或耐波动性进一步变好。
对于印刷用纸的具有最外涂敷层的那一侧,用布里斯托法求出的当接触时间为0.4秒时表面张力为20mN/m的水溶液的转移量优选为4.5ml/m2以上且9.5ml/m2以下。
水溶液的表面张力是利用Wilhelmy Plate法测定的值。
就转移量的测定中使用的表面张力为20mN/m的水溶液而言,只要是利用WilhelmyPlate法得到的表面张力为20mN/m即可,例如,可以通过将甘油、聚乙二醇、丙二醇、乙醇或乙二醇等醇类或全氟烷基磺酸等氟系表面活性剂适量添加到离子交换水中而得到。
例如,如日本专利第5081592号所记载,水溶液的转移量是制纸领域中现有公知的物理量,可以通过制纸领域中现有公知的方法调节。例如,可以通过将涂敷量、颜料的种类、颜料的平均粒径、颜料的粒度分布、颜料的形状、颜料的吸油度、粘结剂的种类、分子量或聚合度、水分散性的粘结剂与水溶性的粘结剂的混合比率、颜料与粘结剂的含有比率等各条件组合来实现。特别地,增加亲水性的颜料、增加水溶性的粘结剂比率、减少粘结剂的比例、配合分散剂和阳离子性树脂等离子性化合物、减少涂敷量等则显示出转移量变多的倾向。增加水分散性的粘结剂比率、配合润滑剂、配合具有长链烷基的疏水性相对较强的表面活性剂等则显示出转移量减少的倾向。另外,在所形成的层表面的状态发生变化的情况下,根据最外涂敷层涂敷液的涂敷以及干燥后的压光处理的有无或压光处理条件,从而转移量发生变化。在所形成的层的状态少许发生变化的情况下,根据设置最外涂敷层时的干燥方法,转移量发生变化。
对上述特征(III)进行说明。
就满足上述特征(III)的印刷用纸而言,在最外涂敷层的表面,点图像的镜面反射光量的最大峰值为2000以上且30000以下。优选的是点图像的镜面反射光量的最大峰值为超过2000且30000以下。在印刷用纸的最外涂敷层的表面,如果点图像的镜面反射光量的最大峰值小于2000则不能得到文字辨识性。如果点图像的镜面反射光量的最大峰值超过30000则不能得到耐擦蹭性。
关于点图像的镜面反射光量和最大峰值,例如,可以通过点图像的镜面反射光量测定装置求出,该镜面反射光量测定装置为利用中央精机公司制的光学类设备的记载于专利文献3的包含入射装置、样品台和受光装置(参照图1)的装置。作为试样,使用印刷用纸,使入射光在印刷用纸的最外涂敷层表面发生镜面反射,将反射的光作为测定光来进行测定。如图1所示,入射装置(1)所具有的光源使用LED灯,通过该入射装置(1)所具有的准直透镜使点图像(直径100μm)成为平行光并入射到置于样品台(3)上的印刷用纸、即试样(4),将镜面反射后的平行光用受光装置(2)所具有的准直透镜成像而恢复为点图像。利用该受光装置(2)所具有的CMOS相机等,以二维的光量分布的形式对点图像进行测定,得到点图像的镜面反射光量分布。点图像的镜面反射光量分布中,x轴和y轴为分布位置(由CMOS相机等的像素或图像分析软件决定),z轴为光量。由得到的点图像的镜面反射光量分布求出最大峰。最大峰是指1个或1个以上的峰中最高的峰。
需要说明的是,本发明中,CMOS相机为1024像素×1024像素。另外,关于测定光量,按照以三菱制纸公司制用纸BWアートポスト256g/m2表面为基准达到约40000的方式调整光源的LED灯。另外,在测定印刷用纸的点图像的镜面反射光量时,在图1中,将相对于样品台(3)的从法线(5)起的角度=θ(6)设为75度。
点图像的镜面反射光量的最大峰值与光泽感有关,可以与光泽感同样地利用制纸领域中现有公知的方法调节。例如,可以通过将涂敷量、颜料的种类、颜料的平均粒径、颜料的粒度分布、颜料的形状、颜料与粘结剂的含有比率等各条件组合来实现。特别地,使颜料的种类、比率、粘结剂的比例减少、配合分散剂、增加涂敷量等则显示出点图像的镜面反射光量的最大峰值变大的倾向。使粘结剂比例增加、配合润滑剂、阳离子性树脂和具有长链烷基的疏水性相对较强的表面活性剂等则显示出点图像的镜面反射光量的最大峰值变小的倾向。另外,在所形成的层表面的状态发生变化的情况下,根据最外涂敷层涂敷液的涂敷以及干燥后的压光处理的有无或压光处理条件,从而点图像的镜面反射光量的最大峰值发生变化。在所形成的层的状态少许发生变化的情况下,根据设置最外涂敷层时的干燥方法,从而点图像的镜面反射光量的最大峰值发生变化。
印刷用纸的最外涂敷层至少含有颜料、粘结剂、润滑剂、分散剂和阳离子性树脂。
通过最外涂敷层中,特定的材料配合与特定的接触角范围的协同效应,从而印刷用纸具有对胶版印刷机的适应性,并且可以得到针对喷墨印刷机的显色性、耐透印性和耐点扩散不良性。在不满足特定的材料配合和特定的接触角范围的组合时,印刷用纸不能得到针对喷墨印刷机的显色性、耐透印性和耐点扩散不良性中的全部特性。
另外,通过在最外涂敷层中,特定的材料配合与特定的转移量范围的协同效应,从而印刷用纸具有对胶版印刷机的适应性,并且可以得到针对喷墨印刷机的颜色浓度均匀性、点再现性和耐波动性。在不满足特定的材料配合和特定的转移量范围的组合时,印刷用纸不能得到针对喷墨印刷机的颜色浓度均匀性、点再现性和耐波动性中的任意者。
另外,通过在最外涂敷层中,特定的材料配合与特定的点图像的镜面反射光量的最大峰值范围的协同效应,印刷用纸具有对胶版印刷机的适应性,并且可以得到针对喷墨印刷机的耐印刷污染性、文字辨识性和耐擦蹭性。当不满足特定的材料配合和特定的点图像的镜面反射光量的最大峰值范围的组合时,印刷用纸不能得到针对喷墨印刷机的耐印刷污染性、文字辨识性和耐擦蹭性中的任意者。
最外涂敷层的颜料包含高岭土和碳酸钙。
最外涂敷层中的高岭土与碳酸钙的含量质量比为高岭土:碳酸钙=1:9~6:4。从针对喷墨印刷机的印刷适应性的角度出发,碳酸钙优选为重质碳酸钙。
最外涂敷层中,除了高岭土和碳酸钙以外还可以含有现有公知的颜料。作为现有公知的颜料的例子,可列举:滑石、缎光白、锌钡白、氧化钛、氧化锌、二氧化硅、氧化铝、氢氧化铝、活性白土、硅藻土等无机颜料、以及塑料颜料等有机颜料。最外涂敷层中,可以将这些颜料中的一种或两种以上组合并与高岭土和碳酸钙并用。
最外涂敷层的颜料中,高岭土和碳酸钙所占的比例为80质量%以上。
最外涂敷层的粘结剂为现有公知的粘结剂。作为现有公知的粘结剂的例子,可列举:淀粉及其各种改性淀粉、羧甲基纤维素、羟乙基纤维素等纤维素衍生物、酪蛋白、明胶、大豆蛋白、普鲁兰多糖、阿拉伯胶、刺梧桐树胶、白蛋白等天然高分子树脂或其衍生物、聚乙烯基吡咯烷酮、聚乙烯醇及其各种改性聚乙烯醇、聚丙二醇、聚乙二醇、马来酸酐系树脂、丙烯酸系树脂、甲基丙烯酸酯-丁二烯系树脂、苯乙烯-丁二烯系树脂、乙烯-乙酸乙烯酯系树脂或利用含有羧基等官能团的单体对这些各种树脂进行官能团改性而得的树脂、三聚氰胺树脂、脲树脂等热固化合成树脂等粘结剂、聚氨酯树脂、不饱和聚酯树脂、聚乙烯醇缩丁醛、醇酸树脂乳胶等。最外涂敷层含有选自这些粘结剂中的一种或两种以上。
最外涂敷层的粘结剂优选为选自淀粉及其各种改性淀粉、聚乙烯醇及其的各种改性聚乙烯醇、以及苯乙烯-丁二烯系树脂中的一种或两种以上。
最外涂敷层中的粘结剂的含量相对于最外涂敷层中的颜料100质量份优选为3质量份以上且40质量份以下,更优选为5质量份以上且25质量份以下。
最外涂敷层的润滑剂为现有公知的润滑剂。作为现有公知的润滑剂的例子,可列举:高级脂肪酸盐、蜡类和有机硅化合物等。作为高级脂肪酸盐,可列举例如:月桂酸盐、油酸盐、棕榈酸盐、硬脂酸盐、肉豆蔻酸盐等高级脂肪酸金属盐(例如这些的钠盐、钾盐、锌盐、钙盐)、以及月桂酸铵、油酸铵、棕榈酸铵、硬脂酸铵、肉豆蔻酸铵等高级脂肪酸铵盐。作为蜡类,可列举例如:植物性蜡、动物性蜡、褐煤蜡、石蜡、合成蜡(烃系合成蜡、聚乙烯乳液系蜡、高级脂肪酸酯、脂肪酸酰胺、酮·胺类、氢化油等)、聚丙烯和聚四氟乙烯聚合物等脂肪族烃及其衍生物。作为有机硅化合物,可列举例如:聚烷基硅氧烷及其衍生物、二甲基硅油、甲基苯基硅油、烷基改性硅油、烷基·芳烷基改性硅油、氨基改性硅油、聚醚改性硅油、高级脂肪酸改性硅油、羧基改性硅油、氟改性硅油、环氧改性硅油等。最外涂敷层可以含有选自这些润滑剂中的一种或两种以上。
最外涂敷层的润滑剂优选为高级脂肪酸盐。
最外涂敷层中的润滑剂的含量在每一面优选为0.01g/m2以上且0.3g/m2以下。
最外涂敷层的分散剂是用于使颜料等水不溶性物质在水溶液中分散的材料,是现有公知的分散剂。作为现有公知的分散剂的例子,可列举:聚羧酸钠等聚羧酸系树脂、聚丙烯酸钠等丙烯酸系树脂、苯乙烯-丙烯酸系树脂、异丁烯-马来酸系树脂、磺化聚苯乙烯系树脂、聚乙烯醇和改性聚乙烯醇、缩合磷酸盐等。最外涂敷层可以含有选自这些分散剂中的一种或两种以上。
最外涂敷层的分散剂优选为选自聚羧酸系树脂和丙烯酸系树脂中的一种或两种以上。
最外涂敷层中的分散剂的含量在每一面优选为0.001g/m2以上且0.1g/m2以下。分散剂中存在与粘结剂重复的材料。但是,作为分散剂使用的材料与粘结剂相比,在最外涂敷层中的含量明显较少,另外,分散剂与粘结剂相比分子量小,因此可以进行区别。通过粘结剂的存在从而颜料能够分散,但通过使最外涂敷层含有分散剂,从而可以使显色性和耐点扩散不良性变好、使点再现性变好、或者使耐印刷污染性或文字辨识性变好。
最外涂敷层的阳离子性树脂是现有公知的阳离子性树脂。优选的阳离子性树脂是含有质子容易配位、溶解于水时解离而呈阳离子性的伯~叔胺或季铵盐的聚合物或低聚物。另外,优选的阳离子性树脂是阳离子化度超过0meq/g且为3meq/g以下的低阳离子或阳离子化度超过3meq/g的高阳离子性树脂。在此,阳离子化度是利用胶体滴定法测定的值。
作为现有公知的阳离子性树脂的例子,可列举:聚乙烯亚胺、多胺和改性多胺、聚乙烯基吡啶、聚酰胺胺、聚乙烯基胺、改性聚酰胺、聚丙烯酰胺、聚烯丙基胺、聚甲基丙烯酸二烷基氨基乙酯、聚丙烯酸二烷基氨基乙酯、聚二烷基氨基乙基甲基丙烯酰胺、聚二烷基氨基乙基丙烯酰胺、聚乙烯基苄基三甲基氯化铵、聚二烯丙基二甲基氯化铵、烯丙基二甲基氯化铵与丙烯酰胺等的共聚物、二甲基胺-环氧氯丙烷缩聚物等脂肪族单胺与环氧卤丙烷化合物的缩聚物或二亚乙基三胺-环氧氯丙烷缩聚物等脂肪族多胺与环氧卤丙烷化合物的缩聚物、多胺聚酰胺环氧氯丙烷、双氰胺-甲醛缩聚物、双氰胺二亚乙基三胺缩聚物、聚环氧胺、聚酰胺-环氧树脂、三聚氰胺树脂、以及脲系树脂。最外涂敷层含有选自这些阳离子性树脂中的一种或两种以上。阳离子性树脂的平均分子量没有特别限定。平均分子量优选为500以上且100000以下,更优选为1000以上且60000以下。
最外涂敷层的阳离子性树脂优选为改性多胺或改性聚酰胺。
最外涂敷层中的阳离子性树脂的含量在每一面优选为0.01g/m2以上且0.5g/m2以下。
最外涂敷层可根据需要还含有涂敷纸领域中现有公知的各种添加剂。作为添加剂的例子,可列举增粘剂、流动性改良剂、消泡剂、发泡剂、渗透剂、着色颜料、着色染料、荧光增白剂、紫外线吸收剂、抗氧化剂、防腐剂、防霉剂等。
实施例
以下利用实施例进一步详细说明本发明。需要说明的是,本发明不受这些实施例限定。这里,“质量份”和“质量%”表示干燥固体成分量或实质成分量的各“质量份”和“质量%”。涂敷层的涂敷量表示干燥固体成分量。
<原纸>
向包含100质量份的滤水度为400mlcsf的LBKP纸浆浆料中,添加作为填料的碳酸钙8质量份、两性淀粉1.0质量份、硫酸铝0.8质量份、内添施胶剂而制备纸料,将该纸料用长网抄纸机进行抄制,用施胶压榨装置使淀粉附着于所得到的抄制纸的两面,进行机械压光处理,从而制作出原纸。
<最外涂敷层涂敷液>
利用下述物质制备最外涂敷层涂敷液。
用上述物质进行配合,用水进行混合·分散而调整为48质量%浓度。
<实施例(I)-1~(I)-14和比较例(I)-1~(I)-15的印刷用纸>
按照以下的步骤制作印刷用纸。
在原纸上用刮刀涂布机将最外涂敷层涂敷液进行两面涂敷,然后干燥。再在干燥后实施压光处理。涂敷量设为每一面14g/m2。
滴加表面张力为20mN/m的水溶液时,接触1秒后液滴与最外涂敷层的接触角主要通过颜料、润滑剂、分散剂和阳离子性树脂的配合来调整、并通过压光处理来辅助地调整。表面张力为20mN/m的水溶液按照向离子交换水中添加丙二醇和氟系表面活性剂而使得基于Wilhelmy Plate法测得的表面张力为20mN/m的方式来制备。
[表1]
<显色性的评价>
使用Miyakoshi公司的喷墨印刷机MJP20MX-7000,用水性颜料墨液在印刷速度:150m/分钟的条件下印刷6000m的评价图像。评价图像设为以下图像:将黑色、青色、品红色、黄色的各单色以及除黑色以外的其它3色墨液所构成的2重色(红色、绿色、蓝色)总计7种颜色的满版图像部图案以3cm×3cm的方形无间隙地在横向上配置为一列而成的图像。关于显色性,目视观察各颜色满版部图像的印刷部分,按照下述基准进行评价。本发明中,若为3~5的评价则视为印刷用纸具有显色性。
5:颜色浓度和颜色鲜艳度均良好。
4:颜色浓度或颜色鲜艳度比“5”差但大体上良好。
3:颜色浓度和颜色鲜艳度在实用上没有问题。
2:颜色浓度或颜色鲜艳度比“3”差,实用上有问题。
1:颜色浓度和颜色鲜艳度均差,实用上有问题。
<耐透印性的评价>
使用Miyakoshi公司的喷墨印刷机MJP20MX-7000,用水性颜料墨液在印刷速度:150m/分钟的条件下印刷6000m的评价图像。评价图像设为如下图像:将黑色的满版图像部图案以10cm×10cm的方形纵横排列而配置的图像。从黑色满版图像部的相反面侧,使用JISP 8148:2001中规定的白色度测定方法进行白色度测定,计算“无印刷的白色部的白色度(光学%)”-“黑色满版图像部的白色度(光学%)”,评价印刷用纸的墨液的耐透印性。使用日本电色公司制PF-10,在标准板上放置一片样品,在UV截止的条件下进行白色度的测定。本发明中,若为3~5的评价则视为印刷用纸具有耐透印性。
5:小于10光学%。
4:10光学%以上、小于13光学%。
3:13光学%以上、小于16光学%。
2:16光学%以上、小于19光学%。
1:19光学%以上。
<耐点扩散不良性的评价>
使用Miyakoshi公司的喷墨印刷机MJP20MX-7000,用水性颜料墨液在印刷速度:150m/分钟的条件下印刷6000m的评价图像。评价图像设为如下图像:将黑色、青色、品红色、黄色的各单色以及除黑色以外的其它3色墨液所构成的2重色(红色、绿色、蓝色)总计7种颜色的满版图像部图案以3cm×3cm的方形无间隙地在横向上配置为一列而成的图像。关于耐点扩散不良性,在各色满版部图像的印刷部分,目视观察由于点扩散不良而产生的白纹的辨识性,按照下述基准进行评价。本发明中,若为3~5的评价则视为印刷用纸具有耐点扩散不良性。
5:确认不到白纹。
4:确认不到白纹,但可略微确认到由浓淡差导致的条纹。
3:确认不到白纹,但可以确认到浅色条纹。
2:可以确认到浅浅的白纹。
1:可以清楚地确认到白纹。
将评价结果示于表1。
由表1可知,相当于本发明的实施例(I)-1~(I)-14具有显色性、耐透印性和耐点扩散不良性。另一方面,可知不满足本发明的构成的比较例(I)-1~(I)-15未能具有这些效果。
<实施例(II)-1~(II)-16和比较例(II)-1~(II)-18的印刷用纸>
按照以下的步骤制作印刷用纸。
在原纸上用刮刀涂布机将最外涂敷层涂敷液进行两面涂敷,然后干燥。再在干燥后实施压光处理。涂敷量设为每一面14g/m2。
用布里斯托法求出的表面张力为20mN/m的水溶液的转移量主要通过颜料、润滑剂、分散剂和阳离子性树脂的配合来调整、并通过压光处理和干燥温度的时间控制来辅助地调整。表面张力为20mN/m的水溶液按照向离子交换水中添加丙二醇和氟系表面活性剂而使得基于Wilhelmy Plate法测得的表面张力为20mN/m的方式来制备。
[表2]
<颜色浓度均匀性的评价>
使用Miyakoshi公司的喷墨印刷机MJP20MX-7000,用水性颜料墨液在印刷速度:150m/分钟的条件下印刷6000m的评价图像。评价图像设为以下图像:将黑色、青色、品红色、黄色的各单色以及除黑色以外的其它3色墨液所构成的2重色(红色、绿色、蓝色)总计7种颜色的满版图像部图案以3cm×3cm的方形无间隙地在横向上配置为一列而成的图像。关于颜色浓度均匀性,目视观察各色满版部图像的印刷部分,按照下述基准进行评价。在本发明中,若为3~5的评价则视为印刷用纸具有颜色浓度均匀性。
5:颜色浓度均匀。
4:某些颜色的情况下,浓度极略微地不均匀。
3:颜色浓度略微地不均匀。
2:颜色浓度在局部不均匀。
1:印刷部分整体上颜色浓度不均匀。
<点再现性的评价>
使用Miyakoshi公司的喷墨印刷机MJP20MX-7000,用水性颜料墨液在印刷速度:150m/分钟的条件下,印刷6000m的使用日本标准协会发行的标准图像数据(图像名称:N5A)的评价图像。关于点再现性,在显微镜下对印刷图像进行目视观察,观察落下的点形状相对于正圆的变形程度和点的轮郭的清晰度,按照下述基准进行评价。本发明中,若为3~5的评价则视为印刷用纸具有点再现性。
5:正圆且清晰。
4:大体上为正圆且清晰。
3:相对于正圆稍微变形,清晰度稍微欠缺。但是实用上没问题。
2:相对于正圆有些变形,清晰度有些欠缺。
1:相对于正圆变形,清晰度欠缺。
<耐波动性的评价>
使用Miyakoshi公司的喷墨印刷机MJP20MX-7000,用水性颜料墨液在印刷速度:150m/分钟的条件下印刷6000m的评价图像。评价图像设为如下图像:将黑色、青色、品红色、黄色的各单色以及除黑色以外的其它3色墨液所构成的2重色(红色、绿色、蓝色)总计7种颜色的满版图像部图案以15cm×30cm的方形无间隙地在纵向上配置为一列而成的图像。关于耐波动性,目视观察各色满版部图像的印刷部分,按照下述基准进行评价。本发明中,若为3~5的评价则视为印刷用纸具有耐波动性。
5:印刷部分不呈波状。
4:刚印刷后呈波状但立即平滑化。
3:印刷部分呈波状,但程度轻,实用上不成问题。
2:印刷部分呈波状,程度明显,实用上有时成为问题。
1:印刷部分呈波状,程度明显较大,成为印刷不良。
将评价结果示于表2。
由表2可知,相当于本发明的实施例(II)-1~(II)-16具有颜色浓度均匀性、点再现性和耐波动性。另一方面,可知不满足本发明的构成的比较例(II)-1~(II)-18未能具有这些效果。
主要根据实施例(II)-1~(II)-5和实施例(II)-9~(II)-14与实施例(II)-15~(II)-16的对比可知,对于印刷用纸的具有最外涂敷层那一侧,[用布里斯托法求出的当接触时间为1秒时表面张力为20mN/m的水溶液的转移量]-[用布里斯托法求出的当接触时间为0.4秒时表面张力为20mN/m的水溶液的转移量]的值优选为0.5ml/m2以上且2.5ml/m2以下。
<实施例(III)-1~(III)-14和比较例(III)-1~(III)-15的印刷用纸>
按照以下的步骤制作印刷用纸。
在原纸上用刮刀涂布机将最外涂敷层涂敷液进行两面涂敷,然后干燥。涂敷量设为每一面14g/m2。
点图像的镜面反射光量的最大峰值主要通过颜料、润滑剂、分散剂和阳离子性树脂的配合来调整、并通过压光处理和干燥装置的每个干燥区的温度控制来辅助地调整。
[表3]
<耐印刷污染性>
使用Miyakoshi公司的喷墨印刷机MJP20MX-7000,用水性颜料墨液在印刷速度:150m/分钟的条件下印刷6000m的评价图像。评价图像设为以下图像:将黑色、青色、品红色、黄色的各单色以及除黑色以外的其它3色墨液所构成的2重色(红色、绿色、蓝色)总计7种颜色的满版图像部图案以3cm×3cm的方形无间隙地在横向上配置为一列而成的图像。关于耐印刷污染性,目视观察存在于印刷部分的印刷污染,根据辨识的程度按照下述基准进行评价。本发明中,若为3~5的评价则视为印刷用纸具有耐印刷污染性。
5:未观察到印刷污染。良好。
4:几乎观察不到印刷污染。大体上良好。
3:略微观察到印刷污染。但是,实用上没问题。
2:观察到少许印刷污染。
1:观察到印刷污染。
<文字辨识性的评价>
使用Miyakoshi公司的喷墨印刷机MJP20MX-7000,用水性颜料墨液在印刷速度:150m/分钟的条件下印刷6000m的评价图像。评价图像设为下述图像:用黑色、青色、品红色、黄色的各单色将5号的文字“お·微·one”重复排列而成的文字列和颠倒文字列的图像。关于文字辨识性,目视观察所印刷的文字列和颠倒文字列的辨识程度,按照下述基准进行评价。本发明中,若为3~5的评价则视为印刷用纸具有文字辨识性。
5:文字可辨识。
4:文字大体上可辨识。
3:虽然有垮倒倾向(日文:潰れ傾向),能够以可理解的程度辨识文字。
2:有垮倒倾向,不能明确地辨识文字。
1:文字不可辨识。
<耐擦蹭性的评价>
使用Miyakoshi公司的喷墨印刷机MJP20MX-7000,用水性颜料墨液在印刷速度:150m/分钟的条件下印刷6000m的评价图像。评价图像设为如下图像:将黑色、青色、品红色、黄色的各单色的满版图像部图案以10cm×10cm的方形无间隙地横向配置成一列而成的图像。印刷24小时后,在以1000g或500g的载荷压住棉纱布的状态下使纱布移动1次而进行擦蹭试验。关于耐擦蹭性,对黑色、青色、品红色、黄色的各满版部图像目视观察墨液的剥离程度,按照下述基准进行评价。本发明中,若为3~5的评价则视为印刷用纸具有耐擦蹭性。
5:在1000g载荷时未观察到剥离。
4:在1000g载荷时略微观察到剥离。
3:在500g载荷时略微观察到剥离。
2:在500g载荷时观察到一些剥离。
1:在500g载荷时显著观察到剥离。
将评价结果示于表3。
由表3可知,相当于本发明的实施例(III)-1~(III)-14具有耐印刷污染性、文字辨识性和耐擦蹭性。另一方面,可知不满足本发明的构成的比较例(III)-1~(III)-15未能具有这些效果。
Claims (5)
1.一种印刷用纸,其具有原纸和位于所述原纸的至少单面的1层以上的涂敷层,在所述涂敷层中,以原纸为基准位于最外侧的最外涂敷层至少含有颜料、粘结剂、润滑剂、分散剂和阳离子性树脂,最外涂敷层中的颜料包含高岭土和碳酸钙,高岭土和碳酸钙的含量相对于最外涂敷层中的颜料100质量份为80质量份以上,而且高岭土与碳酸钙在最外涂敷层中的含量质量比为1:9~6:4,并且所述印刷用纸满足以下特征(I)、(II)和(III)中的至少任一特征:
(I):对于印刷用纸的具有最外涂敷层那一侧,当滴加表面张力为20mN/m的水溶液时,液滴与最外涂敷层的接触角在接触1秒后为40°以上且65°以下,
(II):对于印刷用纸的具有最外涂敷层那一侧,用布里斯托法求出的当接触时间为1秒时表面张力为20mN/m的水溶液的转移量为5.0ml/m2以上且12.0ml/m2以下,
(III):在印刷用纸的最外涂敷层的表面,点图像的镜面反射光量的最大峰值为2000以上且30000以下。
2.根据权利要求1所述的印刷用纸,其具有原纸和位于所述原纸的至少单面的1层以上的涂敷层,在所述涂敷层中,以原纸为基准位于最外侧的最外涂敷层至少含有颜料、粘结剂、润滑剂、分散剂和阳离子性树脂,最外涂敷层中的颜料包含高岭土和碳酸钙,高岭土和碳酸钙的含量相对于最外涂敷层中的颜料100质量份为80质量份以上,而且高岭土与碳酸钙在最外涂敷层中的含量质量比为1:9~6:4,并且所述印刷用纸满足所述特征(I)。
3.根据权利要求1所述的印刷用纸,其具有原纸和位于所述原纸的至少单面的1层以上的涂敷层,在所述涂敷层中,以原纸为基准位于最外侧的最外涂敷层至少含有颜料、粘结剂、润滑剂、分散剂和阳离子性树脂,最外涂敷层中的颜料包含高岭土和碳酸钙,高岭土和碳酸钙的含量相对于所述最外涂敷层中的颜料100质量份为80质量份以上,而且高岭土与碳酸钙在最外涂敷层中的含量质量比为1:9~6:4,并且所述印刷用纸满足所述特征(II)。
4.根据权利要求3所述的印刷用纸,其中,对于印刷用纸的具有最外涂敷层那一侧,测定用布里斯托法求出的当接触时间为0.4秒时表面张力为20mN/m的水溶液的转移量,[用布里斯托法求出的当接触时间为1秒时表面张力为20mN/m的水溶液的转移量]-[用布里斯托法求出的当接触时间为0.4秒时表面张力为20mN/m的水溶液的转移量]的值为0.5ml/m2以上且2.5ml/m2以下。
5.根据权利要求1所述的印刷用纸,其具有原纸和位于所述原纸的至少单面的1层以上的涂敷层,在所述涂敷层中,以原纸为基准位于最外侧的最外涂敷层至少含有颜料、粘结剂、润滑剂、分散剂和阳离子性树脂,最外涂敷层中的颜料包含高岭土和碳酸钙,高岭土和碳酸钙的含量相对于所述最外涂敷层中的颜料100质量份为80质量份以上,而且高岭土与碳酸钙在最外涂敷层中的含量质量比为1:9~6:4,并且所述印刷用纸满足所述特征(III)。