CN105463529A - 一种装饰性铜锌合金镀液 - Google Patents

一种装饰性铜锌合金镀液 Download PDF

Info

Publication number
CN105463529A
CN105463529A CN201510976338.5A CN201510976338A CN105463529A CN 105463529 A CN105463529 A CN 105463529A CN 201510976338 A CN201510976338 A CN 201510976338A CN 105463529 A CN105463529 A CN 105463529A
Authority
CN
China
Prior art keywords
plating solution
zinc alloy
alloy plating
copper
ornamental
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510976338.5A
Other languages
English (en)
Inventor
冯正元
冯育华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Venus Craft Plating Decoration Co Ltd
Original Assignee
Suzhou Venus Craft Plating Decoration Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Venus Craft Plating Decoration Co Ltd filed Critical Suzhou Venus Craft Plating Decoration Co Ltd
Priority to CN201510976338.5A priority Critical patent/CN105463529A/zh
Publication of CN105463529A publication Critical patent/CN105463529A/zh
Pending legal-status Critical Current

Abstract

本发明属于电镀液领域，公开了一种装饰性铜锌合金镀液，包括如下组份：甲基磺酸铜70-120g/L，硫酸锌50-60g/L，酒石酸钾钠25-30g/L，柠檬酸钾10-20g/L，3-(3-吡啶基)-丙烯酸1-5g/L，1，2-二氨基环已烷0.6-1.4g/L，N-(3-磺丙基)吡啶内盐0.2-0.5g/L，并用氨水调节pH值为8-10。本发明提供的镀液不仅制作简单、无毒环保、循环稳定性好，且可在较宽的电流范围内使用，电镀得到的镀层均匀光亮。

Description

一种装饰性铜锌合金镀液
技术领域
本发明涉及电镀液领域，具体涉及一种装饰性铜锌合金镀液。
背景技术
铜锌合金镀层具有金黄色的外观，而且还可以在其表面上进行化学着色，以达到特殊的装饰效果，因此，广泛用于装饰性镀层，但由于铜、锌的标准电位相差较大，故不可能从单盐溶液中获得理想的合金镀层，至今仍没有一种能满意的代替氰化镀铜锌合金的电镀液。
尽管采用含有氰化物的铜锌合金电镀液(即氰化铜锌电镀液)所得到的铜锌镀层细致、结合力好，而且电镀液的均镀性、整平性和稳定性也非常好。但是，含氰铜锌合金电镀液严重危害人体健康与环境，而且废水难于治理，其污水处理费用极高。因此亟待开发一种环保稳定的无氰铜锌电镀液。
发明内容
发明目的：针对现有技术中的问题，本发明提供一种装饰性铜锌合金镀液，使得该镀液制备简单、稳定性好、无毒环保、电镀效率高。
技术方案：为实现上述目的，本发明采用以下技术方案：
一种装饰性铜锌合金镀液，包括如下组份：甲基磺酸铜70-120g/L，硫酸锌50-60g/L，酒石酸钾钠25-30g/L，柠檬酸钾10-20g/L，3-(3-吡啶基)-丙烯酸1-5g/L，1，2-二氨基环已烷0.6-1.4g/L，N-(3-磺丙基)吡啶内盐0.2-0.5g/L，并用氨水调节pH值为8-10。
进一步地，电镀液中还添加了20-40g/L的乙二胺作为添加剂。
进一步地，电镀液中还添加了0.5-3g/L的聚乙二醇作为分散剂。
较优的，一种装饰性铜锌合金镀液，包括如下组份：甲基磺酸铜100-120g/L，硫酸锌50-58g/L，酒石酸钾钠25-30g/L，柠檬酸钾15-20g/L，3-(3-吡啶基)-丙烯酸3-5g/L，、1，2-二氨基环已烷0.6-1.1g/L，N-(3-磺丙基)吡啶内盐0.2-0.5g/L，乙二胺20-35g/L，聚乙二醇0.5-3g/L，并用氨水调节pH值为8-10。
本发明还提供了具体的技术方案：一种装饰性铜锌合金镀液，包括如下组份：甲基磺酸铜103g/L，硫酸锌54g/L，酒石酸钾钠26g/L，柠檬酸钾16g/L，3-(3-吡啶基)-丙烯酸3g/L，、1，2-二氨基环已烷1.1g/L，N-(3-磺丙基)吡啶内盐0.2g/L，乙二胺28g/L，聚乙二醇2g/L，并用氨水调节pH值为9.4。
有益效果：与现有技术中的铜锌合金电镀液相比，本发明提供的镀液不仅制作简单、无毒环保、循环稳定性好，且可在较宽的电流范围内使用，电镀得到的镀层均匀光亮。
具体实施方式
下面结合具体实施例对本发明进一步说明，具体实施例的描述本质上仅仅是范例，而不是打算对本发明公开的内容及其应用或使用进行限制。
实施例1
一种装饰性铜锌合金镀液，包括如下组份：甲基磺酸铜120g/L，硫酸锌60g/L，酒石酸钾钠30g/L，柠檬酸钾10g/L，3-(3-吡啶基)-丙烯酸2g/L，1，2-二氨基环已烷1.4g/L，N-(3-磺丙基)吡啶内盐0.5g/L，并用氨水调节pH值为8.3。其中，电镀液中还添加了40g/L的乙二胺作为添加剂，3g/L的聚乙二醇作为分散剂。
实施例2
一种装饰性铜锌合金镀液，包括如下组份：甲基磺酸铜100g/L，硫酸锌58g/L，酒石酸钾钠25g/L，柠檬酸钾20g/L，3-(3-吡啶基)-丙烯酸5g/L，1，2-二氨基环已烷0.6g/L，N-(3-磺丙基)吡啶内盐0.4g/L，并用氨水调节pH值为9.8。其中，电镀液中还添加了乙二胺35g/L和聚乙二醇0.5g/L。
实施例3
一种装饰性铜锌合金镀液，包括如下组份：甲基磺酸铜103g/L，硫酸锌54g/L，酒石酸钾钠26g/L，柠檬酸钾16g/L，3-(3-吡啶基)-丙烯酸3g/L，1，2-二氨基环已烷1.1g/L，N-(3-磺丙基)吡啶内盐0.2g/L，乙二胺28g/L，聚乙二醇2g/L，并用氨水调节pH值为9.4。
将上述实施例1-3中的电镀液置于电镀槽中进行电镀，活化后的铜片作为工作电极，不锈钢作为阳极，在25℃下采用4-6A/dm2的恒电流密度进行电沉积20-30min得到铜锌合金镀层，在金相显微镜下观察，镀层均匀光亮；将该镀液放置三个月后在此使用相同条件进行电镀，得到的镀层性质为发生变化，说明该镀液稳定性良好。
以上实施例只是对本发明的技术构思起到说明示例作用，并不能以此限制本发明的保护范围，本领域技术人员在不脱离本发明技术方案的精神和范围内，进行修改和等同替换，均应落在本发明的保护范围之内。

Claims (5)

1.一种装饰性铜锌合金镀液，其特征在于，包括如下组份：甲基磺酸铜70-120g/L，硫酸锌50-60g/L，酒石酸钾钠25-30g/L，柠檬酸钾10-20g/L，3-(3-吡啶基)-丙烯酸1-5g/L，1，2-二氨基环已烷0.6-1.4g/L，N-(3-磺丙基)吡啶内盐0.2-0.5g/L，并用氨水调节pH值为8-10。
2.根据权利要求1所述的装饰性铜锌合金镀液，其特征在于，电镀液中还添加了20-40g/L的乙二胺作为添加剂。
3.根据权利要求1所述的装饰性铜锌合金镀液，其特征在于，电镀液中还添加了0.5-3g/L的聚乙二醇作为分散剂。
4.根据权利要求1所述的装饰性铜锌合金镀液，其特征在于，包括如下组份：甲基磺酸铜100-120g/L，硫酸锌50-58g/L，酒石酸钾钠25-30g/L，柠檬酸钾15-20g/L，3-(3-吡啶基)-丙烯酸3-5g/L，、1，2-二氨基环已烷0.6-1.1g/L，N-(3-磺丙基)吡啶内盐0.2-0.5g/L，乙二胺20-35g/L，聚乙二醇0.5-3g/L，并用氨水调节pH值为8-10。
5.根据权利要求1-4任一项所述的装饰性铜锌合金镀液，其特征在于，包括如下组份：甲基磺酸铜103g/L，硫酸锌54g/L，酒石酸钾钠26g/L，柠檬酸钾16g/L，3-(3-吡啶基)-丙烯酸3g/L，、1，2-二氨基环已烷1.1g/L，N-(3-磺丙基)吡啶内盐0.2g/L，乙二胺28g/L，聚乙二醇2g/L，并用氨水调节pH值为9.4。
CN201510976338.5A 2015-12-23 2015-12-23 一种装饰性铜锌合金镀液 Pending CN105463529A (zh)