CN104497219A - 一种高回弹性自修复高分子水凝胶及其制备方法 - Google Patents
一种高回弹性自修复高分子水凝胶及其制备方法 Download PDFInfo
- Publication number
- CN104497219A CN104497219A CN201410773312.6A CN201410773312A CN104497219A CN 104497219 A CN104497219 A CN 104497219A CN 201410773312 A CN201410773312 A CN 201410773312A CN 104497219 A CN104497219 A CN 104497219A
- Authority
- CN
- China
- Prior art keywords
- preparation
- macromolecule hydrogel
- parts
- high resilience
- self
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种高回弹性自修复高分子水凝胶及其制备方法。以质量分数计,该水凝胶原料组分组成包括多异氰酸酯15~20份,亲水聚酯多元醇或亲水聚醚多元醇40~75份,丙烯酸酯类单体1~5份,丙烯酰胺类单体10~15份,扩链剂0.5~2份,表面活性剂1~3份,丙烯酸烷基酯类单体0.1~1份,催化剂0.5~2份;制备时,先制备出丙烯酸酯类单体封端的亲水性聚氨酯大分子单体自组装体和丙烯酸烷基酯胶束;然后与丙烯酰胺类单体在光引发下自由基共聚合。所得自修复高分子水凝胶无需任何修复剂和特定环境的要求下即可完成对自身破损的自修复,并且具有优异的回弹性能和物理机械性能。
Description
技术领域
本发明涉及一种高分子水凝胶的制备方法,特别是一种涉及具有高回弹性和自修复性能的高分子水凝胶及其制备方法。
背景技术
高分子水凝胶的回弹性能是水凝胶的一个重要的性能指标,指的是高分子水凝胶在受力的作用下发生形变后恢复原来形状和性能的能力。然而,在目前所报道的大多数高分子水凝胶中,表现出较差的回弹性能,具体体现在形变恢复时间长,在循环压缩的应力‐应变曲线中有较大的滞后圈。人们在这方面也做了很多工作,并取得一定的成果。主要方法有亲水性的有机高分子材料和无机材料复合、高分子材料结构的设计以及不同高分子材料的复合等。其中,高分子材料结构的设计中,在研究论文“A robust,one‐pot synthesis of highlymechanical and recoverable double network hydrogels using thermoreversible sol‐gelpolysaccharide(Qiang Chen,Lin Zhu,Chao Zhao,Qiuming Wang,and Jie Zheng,Adv.Mater.,2013,25,4171.)”这一研究论文中,作者利用琼脂(Agar)、丙烯酰胺(AM)和N,N′‐亚甲基双丙烯酰胺(MBA)制备出了具有较好回弹性能的双网络高分子水凝胶,其弹性模量在10分钟内的恢复能力达到90%左右,这一水凝胶虽有良好的回弹性能,但无自愈合性能。
在设计自愈合高分子水凝胶的非共价相互作用中,疏水相互作用是一种常用的愈合机制,且在自然界中普遍存在,并且在生物系统的形成和维持生物功能中扮演着非常重要的角色。因此,利用疏水相互作用也是设计和构筑自愈合高分子水凝胶的一种重要方法。在研究论文“Dynamics and large strain behavior of self‐healing hydrogels with and withoutsurfactants(Deniz C.Tuncaboylu,Melahat Sahin,Aslihan Argun,Wilhelm Oppermann and OguzOkay,Macromolecules,2012,45,1991.)”的研究论文中,作者以疏水相互作用设计和构筑了高愈合率和高断裂伸长率的自愈合高分子水凝胶,然而这一水凝胶的回弹性能并不令人满意。
发明内容
本发明的目的在于提供一种无须外界刺激和特定环境要求即可自修复的高分子水凝胶,其在循环压缩测试中的应力与应变在1~5分钟内可恢复到100%,而水凝胶表面的切痕在1~30分钟内可完成修复。
本发明以丙烯酸酯类单体封端的亲水性聚氨酯大分子单体在水中的自组装体为化学交联剂和以含有丙烯酸烷基酯类胶束为物理交联剂,与丙烯酰胺类单体在UV引发下进行自由基共聚合,制备出化学‐物理双网络的高分子水凝胶。本发明聚氨酯大分子单体在水中能自组装成纳米粒子,形成多官能度的化学交联剂,能赋予水凝胶良好的回弹性能;丙烯酸烷基酯类单体发生聚合后的疏水性聚合物链可形成基于疏水相互作用的可逆物理交联点,当水凝胶受到损伤后,疏水链能够通过疏水相互作用再次形成新的网络结构,从而实现水凝胶的自愈合。本发明的聚合物材料体系的合成路线简单,原料易得,材料组成与结构的可调控性较强。
本发明目的通过如下技术方案实现:
一种高回弹性自修复高分子水凝胶的制备方法,包括如下步骤
1)丙烯酸酯类单体封端的亲水聚氨酯大分子单体的合成:将亲水聚酯多元醇或亲水聚醚多元醇和扩链剂搅拌均匀,加热升温至90~130℃,真空脱水,放置降温到60℃以下;然后逐滴加入多异氰酸酯,加完后控制温度在70~90℃下反应3~10小时,逐滴加入丙烯酸类单体和催化剂,反应10~64小时,制得丙烯酸酯类单体封端的亲水聚氨酯大分子单体,真空脱泡后密封冷藏待用;
2)高回弹性自修复高分子水凝胶的制备:将表面活性剂和氯化钠加入到去离子水中,搅拌直至获得透明溶液,然后将丙烯酸烷基酯类单体加入到透明溶液中并搅拌均匀,得到含丙烯酸烷基酯类单体的胶束水溶液;将所述亲水聚氨酯大分子单体加入到去离子水中,超声处理,得亲水聚氨酯大分子单体的自组装体水溶液;将所述胶束水溶液和自组装体水溶液混合均匀,再加入丙烯酰胺类单体和光引发剂,用超声使其完全溶解;在光引发下进行自由基聚合反应30~120分钟,得到高分子水凝胶;
以质量分数计,原料组分组成为:
为进一步实现本发明目的,优选地,所述的多异氰酸酯为异佛尔酮二异氰酸酯、1,6‐六亚甲基二异氰酸酯、甲苯二异氰酸酯、二苯基甲烷‐4,4′‐二异氰酸酯、苯二亚甲基二异氰酸酯、甲基环己基二异氰酸酯、四甲基苯二亚甲基二异氰酸酯、HDI三聚体、IPDI三聚体、TDI三聚体和MDI三聚体中的任一种或多种的混合物。
所述的亲水聚酯多元醇或聚醚多元醇为聚四氢呋喃二醇、聚己二酸乙二醇酯二醇、聚己二酸乙二醇酯‐1,4‐丁二醇酯二醇、聚乙二醇、聚己二酸蓖麻油酯多元醇中的一种或多种的混合物,平均分子量为400到15000g/mol。
所述的有机锡催化剂为辛酸亚锡或二月桂酸二丁基锡;所述的叔胺类催化剂为二亚乙基三胺、甲基二乙醇胺、三乙胺或吡啶。
所述的超声处理的时间为5~60分钟。
所述的丙烯酸酯类单体为甲基丙烯酸羟乙酯、丙烯酸羟乙酯和聚乙二醇丙烯酸酯中的一种或多种。
所述的丙烯酰胺类单体为丙烯酰胺、甲基丙烯酰胺、N‐异丙基丙烯酰胺、N‐异丙基甲基丙烯酰胺和二甲胺基丙基丙烯酰胺中的一种或多种。
所述的丙烯酸烷基酯类单体为丙烯酸十八烷基酯、甲基丙烯酸十八烷基酯、丙烯酸十六烷基酯、丙烯酸十二烷基酯、2‐甲基‐2‐丙烯酸十三烷基酯、丙烯酸二十二烷基酯和甲基丙烯酸二十二烷基酯中的一种或多种。
一种高回弹性自修复高分子水凝胶,有上述制备方法制得。所述的高回弹性自修复高分子水凝胶在循环压缩测试中的应力与应变在1~5分钟内恢复到100%,水凝胶表面的切痕在1~30分钟内完成修复。
相对于现有技术,本发明具有以下优点:
一、聚氨酯因其软段和硬段的热力学不相容性导致的微相分离结构使材料具有优异的物理机械性能,利用亲水性聚氨酯大分子单体自组装成的多官能度的化学交联剂能赋予水凝胶良好的回弹性能。该性能近似人体中的软体组织如软骨等所表现出的回弹性,因而在植入并替代人体中坏死的软体组织方面具有重要的价值;另外,在一些生物器件和工业生产中也常要求有优异的回弹性能,因此,本发明所制备的高分子水凝胶具有很好的应用前景。
二、丙烯酸烷基酯类单体发生聚合后的疏水性聚合物链可形成基于疏水相互作用的可逆物理交联点,当水凝胶受到损伤后,疏水链能够通过疏水相互作用再次形成新的网络结构,因此所制备的高分子水凝胶具有自愈合性能;
三、所制备的高分子水凝胶的双网络结构通过协同作用赋予其优异的物理机械性能。其中,聚氨酯中的氨基甲酸酯基能形成氢键,当受力作用时,氢键的解离和缔合很好地分散应力;另外,疏水链物理交联的解离和重新形成也很好的分散应力。因此,二者的协同作用能有效地提高水凝胶的力学性能;
四、本发明所用的原料便宜易得,合成过程无需特殊的条件和设备,合成工艺容易控制;此外,所需的聚氨酯原料已是大量生产的工业品,合成聚氨酯的工艺也基本成熟。工艺简单、成本低。
附图说明
图1为实施例1制得的甲基丙烯酸羟乙酯封端的亲水聚氨酯大分子单体的核磁共振氢谱的谱图。
图2为实施例1制得的高分子水凝胶的红外谱图。
图3(a)为实施例1制得的高分子水凝胶的表面切痕的原始状态的光学照片(修复时间为0分钟)。
图3(b)为实施例1制得的高分子水凝胶的表面切痕自修复5分钟时的切痕修复状态的光学照片。
图3(c)为实施例1制得的高分子水凝胶的表面切痕自修复30分钟时的切痕修复状态的光学照片。
图4为实施例1制得的高分子水凝胶拉伸测试得到的应力‐应变曲线。
图5为实施例1制得的高分子水凝胶循环压缩测试得到的应力‐应变曲线。
图6为实施例3制得的聚乙二醇丙烯酸酯封端的亲水聚氨酯大分子单体的核磁共振氢谱的谱图。
图7为实施例5制得的丙烯酸羟乙酯封端的亲水聚氨酯大分子单体的核磁共振氢谱的谱图。
具体实施方式
为更好地理解本发明,下面结合附图和实施例对本发明作进一步的说明,但本发明的实施方式不限于此。
实施例1
甲基丙烯酸羟乙酯类单体封端的亲水聚氨酯大分子单体的合成:以质量分数计,先将75份的聚乙二醇和1份1,4‐丁二醇加入到250毫升三口烧瓶中,搅拌均匀,加热至90℃真空脱泡3小时后,放置降温到60℃以下;然后逐滴加入20份异佛尔酮二异氰酸酯,加完后控制温度在70℃下反应10小时,逐滴加入3份甲基丙烯酸羟乙酯和1份二月桂酸二丁基锡,反应64小时,制得甲基丙烯酸羟乙酯封端的亲水聚氨酯大分子单体,真空脱泡后密封冷藏待用;
高回弹性自修复高分子水凝胶的制备:以质量分数计,将2.5份十二烷基磺酸钠和0.2份氯化钠加入到40份的去离子水中,搅拌直至获得透明的溶液,然后将0.1份丙烯酸十八烷基酯加入到溶液中并搅拌均匀得到含丙烯酸十八烷基酯的胶束水溶液;将0.4份甲基丙烯酸羟乙酯封端的亲水聚氨酯大分子单体加入到去40份去离子水中,超声处理5分钟即得甲基丙烯酸羟乙酯封端的亲水聚氨酯大分子单体自组装体水溶液;接着将胶束水溶液和自组装体水溶液混合均匀,再加入15份丙烯酰胺单体和0.3份光引发剂ɑ‐酮戊二酸,用超声使其完全溶解;在光引发下进行自由基聚合反应30分钟,得到高分子水凝胶。
图1为本实施例制得的甲基丙烯酸羟乙酯封端的亲水聚氨酯大分子单体的核磁共振氢谱的谱图,在这一谱图上可以观察到化学位移在0.89~1.27ppm处的归属于异佛尔酮二异氰酸酯中的甲基上的氢,在3.66ppm处的归属于聚乙二醇中亚甲基上的氢,1.87ppm处是HEMA上-C(CH3)=CH2链段上甲基的质子峰,属于-C(CH3)=CH2上的碳碳双键上两个氢的峰分别在5.51ppm和6.06ppm处可以观察到,说明本实施例确实得到了甲基丙烯酸羟乙酯封端的亲水聚氨酯大分子单体。该大分子单体的分子量约为16400。
从本实施例制得的水凝胶的红外谱图(图2)中可以看出,在1540cm-1处出现聚氨酯中的酰胺II的吸收峰,且在1250cm-1处出现了聚氨酯C-N的伸缩振动,2922cm-1和2856cm-1分别为甲基和亚甲基的的伸缩振动吸收峰,1705cm-1为C=O的伸缩振动吸收峰,表明确实得到了所设计的高分子水凝胶。
将本实施例中制得的高分子水凝胶,用刀片在水凝胶上划一切痕,置于室温环境中;随即用光学显微镜观察和拍摄在不同修复时间的切痕修复状况,所得到的光学照片如图3(a)、图3(b)和图3(c)所示;图3(a)、图3(b)和图3(c)分别是样品表面的切痕在修复时间分别为0分钟、5分钟和30分钟的照片。与图3(a)所示的未修复的照片相比,当修复时间达到30分钟的时候(见图3(c)),样品表面的切痕得到了明显地修复。
将本实施例制得的水凝胶样品进行拉伸性能测试,得到图4的应力‐应变曲线。从图中可以看出,水凝胶样的断裂伸长率均大于1800%,拉伸强度高于130kPa,体现出优异的力学性能。
将本实施例制得的水凝胶样品进行循环压缩测试,得到图5的应力‐应变曲线。从恢复的曲线看,基本上没有出现较大滞后圈,第二次压缩的曲线与第一次压缩的曲线基本重合,从恢复速度来讲,所制备的水凝胶应力与应变在1分钟内恢复到100%,表明了水凝胶具有优异的回弹性能,该性能在现有关于此类材料的文献报道中是很鲜见的。本发明所制备的高分子水凝胶在植入并替代人体中坏死的软体组织方面具有重要的应用价值。
实施例2
高回弹性自修复高分子水凝胶的制备:以质量分数计,将3份十二烷基磺酸钠和0.1份氯化钠加入到20份的去离子水中,搅拌直至获得透明的溶液,然后将1份丙烯酸十八烷基酯加入到溶液中并搅拌均匀得到含丙烯酸十八烷基酯的胶束水溶液;将0.6份实施例1制备的甲基丙烯酸羟乙酯封端的亲水聚氨酯大分子单体加入到去30份去离子水中,超声处理60分钟,即得甲基丙烯酸羟乙酯封端的亲水聚氨酯大分子单体自组装体水溶液;接着将胶束水溶液和自组装体水溶液混合均匀,再加入10份丙烯酰胺单体和0.2份光引发剂2‐羟基‐2‐甲基‐1‐苯基丙酮,用超声使其完全溶解;在光引发下进行自由基聚合反应120分钟,得到高分子水凝胶。
所制得的高分子水凝胶的在循环压缩测试中的应力与应变在3分钟内恢复到100%,而水凝胶表面的切痕在10分钟内完成修复,表明了所制备的高分子水凝胶具有高的回弹性和自修复性能。
实施例3
聚乙二醇丙烯酸酯封端的亲水聚氨酯大分子单体的合成:以质量分数计,先将40份的聚乙二醇和0.5份1,4‐丁二醇和0.5份三羟甲基丙烷加入到250毫升三口烧瓶中,搅拌均匀,加热至130℃真空脱泡2小时后,放置降温到60℃以下;然后逐滴加入15份异佛尔酮二异氰酸酯,加完后控制温度在90℃下反应3小时,逐滴加入3份甲基丙烯酸羟乙酯和1份二月桂酸二丁基锡,反应10小时,制得甲基丙烯酸羟乙酯封端的亲水聚氨酯大分子单体,真空脱泡后密封冷藏待用;
从聚乙二醇丙烯酸酯封端的亲水聚氨酯大分子单体的核磁共振氢谱的谱图(图6)中可以看出,在化学位移0.8~1.0ppm处为异佛尔酮二异氰酸酯中的甲基上的氢,3.5~3.66ppm为聚乙二醇中亚甲基上的氢,5.5和6.0ppm为聚乙二醇丙烯酸酯上双键的氢,1.9ppm为聚乙二醇丙烯酸酯甲基上的氢,说明本实施例确实得到了聚乙二醇丙烯酸酯封端的亲水聚氨酯大分子单体。该大分子单体的分子量约为17500。
高回弹性自修复高分子水凝胶的制备:以质量分数计,将2份十八烷基二甲基苄基氯化铵和0.1份氯化钠加入到50份的去离子水中,搅拌直至获得透明的溶液,然后将0.5份丙烯酸二十二烷基酯加入到溶液中并搅拌均匀得到含丙烯酸二十二烷基酯的胶束水溶液;将0.2份聚乙二醇丙烯酸酯封端的亲水聚氨酯大分子单体加入到去20份去离子水中,超声10分钟即得甲基丙烯酸羟乙酯封端的亲水聚氨酯大分子单体自组装体水溶液;接着将胶束水溶液和自组装体水溶液混合均匀,再加入15份N‐异丙基甲基丙烯酰胺单体和0.2份光引发剂2‐羟基‐4‐(2‐羟乙氧基)‐2‐甲基苯丙酮,用超声使其完全溶解;在光引发下进行自由基聚合反应30分钟,得到高分子水凝胶。
所制得的高分子水凝胶的在循环压缩测试中的应力与应变在5分钟内恢复到100%,而水凝胶表面的切痕在1分钟内完成修复,表明了所制备的高分子水凝胶具有高的回弹性和自修复性能。
实施例4
高回弹性自修复高分子水凝胶的制备:将2.5份十二烷基磺酸钠和0.3份氯化钠加入到30份的去离子水中,搅拌直至获得透明的溶液,然后将0.1份丙烯酸十八烷基酯加入到溶液中并搅拌均匀得到含丙烯酸十八烷基酯的胶束水溶液;将0.5份实施例3所制备的聚乙二醇丙烯酸酯封端的亲水聚氨酯大分子单体加入到去40份去离子水中,超声20分钟即得甲基丙烯酸羟乙酯封端的亲水聚氨酯大分子单体自组装体水溶液;接着将胶束水溶液和自组装体水溶液混合均匀,再加入10份丙烯酰胺单体和0.2份光引发剂ɑ‐酮戊二酸,用超声使其完全溶解;在光引发下进行自由基聚合反应60分钟,得到高分子水凝胶。
所制得的高分子水凝胶的在循环压缩测试中的应力与应变在1分钟内恢复到100%,而水凝胶表面的切痕在4分钟内完成修复,表明了所制备的高分子水凝胶具有高的回弹性和自修复性能。
实施例5
丙烯酸羟乙酯类单体封端的亲水聚氨酯大分子单体的合成:以质量分数计,先将45份的聚乙二醇和1份1,4‐丁二醇和0.5份三羟甲基丙烷加入到250毫升三口烧瓶中,搅拌均匀,加热至110℃真空脱泡3小时后,放置降温到60℃以下;然后逐滴加入23份异佛尔酮二异氰酸酯,加完后控制温度在85℃下反应12小时,逐滴加入5份丙烯酸羟乙酯和1份二月桂酸二丁基锡,反应24小时,制得甲基丙烯酸羟乙酯封端的亲水聚氨酯大分子单体,真空脱泡后密封冷藏待用;
从丙烯酸羟乙酯封端的亲水聚氨酯大分子单体的核磁共振氢谱的谱图(图7)中可以看出,在化学位移0.8~1.0ppm处为异佛尔酮二异氰酸酯中的甲基上的氢,3.5~3.6ppm为聚乙二醇中亚甲基上的氢,5.8~6.4ppm为丙烯酸羟乙酯上双键的氢。这一表征结果说明本实施例确实得到了丙烯酸羟乙酯封端的亲水聚氨酯大分子单体。该大分子单体的分子量约为16000。
高回弹性自修复高分子水凝胶的制备:将3份十二烷基苯磺酸钠和0.4份氯化钠加入到50份的去离子水中,搅拌直至获得透明的溶液,然后将0.6份丙烯酸十六烷基酯加入到溶液中并搅拌均匀得到含丙烯酸十六烷基酯的胶束水溶液;将0.4份丙烯酸羟乙酯类单体封端的亲水聚氨酯大分子单体加入到去30份去离子水中,超声20分钟即得甲基丙烯酸羟乙酯封端的亲水聚氨酯大分子单体自组装体水溶液;接着将胶束水溶液和自组装体水溶液混合均匀,再加入12份二甲胺基丙基丙烯酰胺单体和0.3份光引发剂ɑ‐酮戊二酸,用超声使其完全溶解;在光引发下进行自由基聚合反应60分钟,得到高分子水凝胶。
所制得的高分子水凝胶的在循环压缩测试中的应力与应变在5分钟内恢复到100%,而水凝胶表面的切痕在1分钟内完成修复,表明了所制备的高分子水凝胶具有高的回弹性和自修复性能。
实施例6
高回弹性自修复高分子水凝胶的制备:将2.5份十二烷基硫酸钠和0.3份氯化钠加入到20份的去离子水中,搅拌直至获得透明的溶液,然后将0.6份甲基丙烯酸十八烷基酯加入到溶液中并搅拌均匀得到含甲基丙烯酸十八烷基酯的胶束水溶液;将0.5份实施例5所制备的丙烯酸羟乙酯类单体封端的亲水聚氨酯大分子单体加入到去50份去离子水中,超声20分钟即得甲基丙烯酸羟乙酯封端的亲水聚氨酯大分子单体自组装体水溶液;接着将胶束水溶液和自组装体水溶液混合均匀,再加入10份丙烯酰胺单体和0.2份光引发剂2‐羟基‐2‐甲基‐1‐苯基丙酮,用超声使其完全溶解;在光引发下进行自由基聚合反应50分钟,得到高分子水凝胶。
所制得的高分子水凝胶的在循环压缩测试中的应力与应变在4分钟内恢复到100%,而水凝胶表面的切痕在20分钟内完成修复,表明了所制备的高分子水凝胶具有高的回弹性和自修复性能。
Claims (10)
1.一种高回弹性自修复高分子水凝胶的制备方法,其特征在于包括如下步骤:
1)丙烯酸酯类单体封端的亲水聚氨酯大分子单体的合成:将亲水聚酯多元醇或亲水聚醚多元醇和扩链剂搅拌均匀,加热升温至90~130℃,真空脱水,放置降温到60℃以下;然后逐滴加入多异氰酸酯,加完后控制温度在70~90℃下反应3~10小时,逐滴加入丙烯酸类单体和催化剂,反应10~64小时,制得丙烯酸酯类单体封端的亲水聚氨酯大分子单体,真空脱泡后密封冷藏待用;
2)高回弹性自修复高分子水凝胶的制备:将表面活性剂和氯化钠加入到去离子水中,搅拌直至获得透明溶液,然后将丙烯酸烷基酯类单体加入到透明溶液中并搅拌均匀,得到含丙烯酸烷基酯类单体的胶束水溶液;将所述亲水聚氨酯大分子单体加入到去离子水中,超声处理,得亲水聚氨酯大分子单体的自组装体水溶液;将所述胶束水溶液和自组装体水溶液混合均匀,再加入丙烯酰胺类单体和光引发剂,用超声使其完全溶解;在光引发下进行自由基聚合反应30~120分钟,得到高分子水凝胶;
以质量分数计,原料组分组成为:
所述的扩链剂为1,4‐丁二醇、一缩二乙二醇、三羟甲基丙烷、乙二醇、丙三醇、1,4‐环己二醇和间苯二酚羟基醚中的一种或多种;
所述的光引发剂为2‐羟基‐2‐甲基‐1‐苯基丙酮、1‐羟基环己基苯基甲酮、2,4,6‐三甲基苯甲酰基‐二苯基氧化膦、二苯甲酮、2‐羟基‐4‐(2‐羟乙氧基)‐2‐甲基苯丙酮、2‐羟基‐2‐甲基‐1‐[4‐(2‐羟基乙氧基)苯基]‐1‐丙酮和ɑ‐酮戊二酸中的一种或多种;
所述催化剂为有机锡催化剂或叔胺类催化剂;
所述的表面活性剂为十二烷基苯磺酸钠、十二烷基硫酸钠、十八烷基二甲基苄基氯化铵和十六烷基三甲基溴化铵中的一种或多种。
2.根据权利要求书1所述的高回弹性自修复高分子水凝胶的制备方法,其特征在于,所述的多异氰酸酯为异佛尔酮二异氰酸酯、1,6‐六亚甲基二异氰酸酯、甲苯二异氰酸酯、二苯基甲烷‐4,4′‐二异氰酸酯、苯二亚甲基二异氰酸酯、甲基环己基二异氰酸酯、四甲基苯二亚甲基二异氰酸酯、HDI三聚体、IPDI三聚体、TDI三聚体和MDI三聚体中的任一种或多种的混合物。
3.根据权利要求书1所述的高回弹性自修复高分子水凝胶的制备方法,其特征在于,所述的亲水聚酯多元醇或聚醚多元醇为聚四氢呋喃二醇、聚己二酸乙二醇酯二醇、聚己二酸乙二醇酯‐1,4‐丁二醇酯二醇、聚乙二醇、聚己二酸蓖麻油酯多元醇中的一种或多种的混合物,平均分子量为400到15000g/mol。
4.根据权利要求书1所述的高回弹性自修复高分子水凝胶的制备方法,其特征在于,所述的有机锡催化剂为辛酸亚锡或二月桂酸二丁基锡;所述的叔胺类催化剂为二亚乙基三胺、甲基二乙醇胺、三乙胺或吡啶。
5.根据权利要求书1所述的高回弹性自修复高分子水凝胶的制备方法,其特征在于,所述的超声处理的时间为5~60分钟。
6.根据权利要求书1所述的高回弹性自修复高分子水凝胶的制备方法,其特征在于,所述的丙烯酸酯类单体为甲基丙烯酸羟乙酯、丙烯酸羟乙酯和聚乙二醇丙烯酸酯中的一种或多种。
7.根据权利要求书1所述的高回弹性自修复高分子水凝胶的制备方法,其特征在于,所述的丙烯酰胺类单体为丙烯酰胺、甲基丙烯酰胺、N‐异丙基丙烯酰胺、N‐异丙基甲基丙烯酰胺和二甲胺基丙基丙烯酰胺中的一种或多种。
8.根据权利要求书1所述的高回弹性自修复高分子水凝胶的制备方法,其特征在于,所述的丙烯酸烷基酯类单体为丙烯酸十八烷基酯、甲基丙烯酸十八烷基酯、丙烯酸十六烷基酯、丙烯酸十二烷基酯、2‐甲基‐2‐丙烯酸十三烷基酯、丙烯酸二十二烷基酯和甲基丙烯酸二十二烷基酯中的一种或多种。
9.一种高回弹性自修复高分子水凝胶,其特征在于其由权利要求1‐8任一项所述制备方法制得。
10.根据权利要求9所述的高回弹性自修复高分子水凝胶,其特征在于,所述的高回弹性自修复高分子水凝胶在循环压缩测试中的应力与应变在1~5分钟内恢复到100%,水凝胶表面的切痕在1~30分钟内完成修复。