CN103443361A - 防水生生物附着片材和防水生生物附着涂料 - Google Patents
防水生生物附着片材和防水生生物附着涂料 Download PDFInfo
- Publication number
- CN103443361A CN103443361A CN201280014733XA CN201280014733A CN103443361A CN 103443361 A CN103443361 A CN 103443361A CN 201280014733X A CN201280014733X A CN 201280014733XA CN 201280014733 A CN201280014733 A CN 201280014733A CN 103443361 A CN103443361 A CN 103443361A
- Authority
- CN
- China
- Prior art keywords
- biological attachment
- aquatic biological
- coating
- fluororesin
- aquatic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
提供不会污染水域、可长期发挥出较高的防止水生生物附着的效果的防水生生物附着片材、以及安装了防水生生物附着片材的防水生生物附着面板和水中结构物。本发明涉及防水生生物附着片材，其特征在于，该片材含有氟树脂；以及防水生生物附着涂料，其特征在于，该涂料含有氟树脂。
Description
【技术领域】
本发明涉及防水生生物附着片材，该片材用于安装于水中结构物来防止水生生物附着于水中结构物；以及防水生生物附着涂料，该涂料能够涂布于水中结构物来防止水生生物附着于水中结构物。
【背景技术】
在各种水中结构物、例如发电厂的海水取水施设等中，在其表面大量附着、生长有茗荷介、海鞘类、龙介虫、贻贝、褶纹冠蚌(カラスガイ)、苔藓虫、青海苔、石莼等水生生物(海生生物)，其可能会引起功能降低或功能障碍。以往一般采取的是定期刮除所附着的水生生物等机械除去方法，近年来开发出了各种防污涂料，主要通过将其应用于水中结构物的表面来防止水生生物的附着。
作为防污涂料，有含有有机锡化合物、氧化亚铜、吡硫鎓锌、吡硫鎓铜等毒性防污剂的防污涂料。例如，在专利文献1中提出了一种防污涂料组合物以及形成该防污涂料组合物的涂膜而构成的防污面板，该防污涂料组合物含有粘结剂与忌避剂，该粘结剂由淀粉或淀粉分解物中的羟基被1种或2种以上的脂肪酰基取代而成的淀粉脂肪酸酯形成；形成涂膜通过涂膜形成要素在水中的可溶化而缓慢释放上述忌避剂。
但是，尽管可防止水生生物的附着、生长，但由于使用毒性防污剂，因而从涂料的制造和涂布时的环境安全卫生方面考虑不优选；而且在水中毒性防污剂由涂膜缓慢溶出，长期来看可能会污染水域。
另外，作为具有防止水生生物的附着、生长的效果、不含有毒性防污剂的涂料，在专利文献2中提出了一种防止水中生物附着的涂料组合物，该组合物含有室温固化性有机硅树脂和硅油。
此外，在专利文献3中提出了一种防止水生生物或生理物质附着用树脂组合物，该组合物含有表面亲水化用的水解性有机金属化合物与粘合剂用树脂，可形成表面对水接触角小于70度的涂布层或膜。
【现有技术文献】
【专利文献】
专利文献1：日本特开2006-233160号公报
专利文献2：日本特开2010-13591号公报
专利文献3：国际公开第01/60923号小册子
【发明内容】
【发明所要解决的课题】
但是，这些涂料还得不到充分的防止水生生物附着的效果。
本发明的目的在于提供防水生生物附着片材，该片材不会污染水域、可长期发挥出较高的防止水生生物附着的效果；以及防水生生物附着面板和水中结构物，其安装有防水生生物附着片材。
本发明的目的还在于提供防水生生物附着涂料，该涂料不会污染水域、可长期发挥出较高的防止水生生物附着的效果；以及防水生生物附着面板和水中结构物，其应用了防水生生物附着涂料。
【解决课题的手段】
本发明人进行了深入研究，结果发现，在含有氟树脂的片材和涂膜的表面几乎没有水生生物附着，从而完成了本发明。
即，本发明涉及防水生生物附着片材，其特征在于，该片材含有氟树脂。本发明还涉及防水生生物附着涂料，其特征在于，该涂料含有氟树脂。
【发明的效果】
本发明的防水生生物附着片材不含有毒性防污剂亦可发挥出较高的防止水生生物附着的效果，氟树脂本身在化学上也极为稳定，因而不会污染水域，可长期发挥出较高的防止水生生物附着的效果。
应用了本发明的防水生生物附着涂料的基材不含有毒性防污剂亦可发挥出较高的防止水生生物附着的效果，氟树脂本身在化学上也极为稳定，因而不会污染水域，可长期发挥出较高的防止水生生物附着的效果。
【具体实施方式】
本发明涉及防水生生物附着片材，其特征在于，该片材含有氟树脂。
作为水生生物，可以举出茗荷介类、贻贝、海葵类、牡蛎、海鞘类、水螅虫、羽苔虫、各种水生微生物、各种海藻类(管枝藻、马尾藻、石莼、青海苔等)、各种硅藻类、环形动物(螺旋虫、丝管虫等)、海绵动物(柚球状海绵(ユズダマカイメン)等)等。
上述氟树脂只要具有明确的熔点就没有特别限定，优选为不溶于溶剂的树脂。
上述氟树脂的熔点优选为100℃～347℃、更优选为150℃～322℃。
上述熔点如下进行测定：在升温速度10℃/分钟的条件下使用差示扫描量热计进行测定，得到热熔解曲线，将与该热熔解曲线的最大值对应的温度作为熔点。
上述氟树脂优选为具有衍生自至少一种含氟烯键式单体的重复单元的均聚物或共聚物。上述氟树脂可以通过仅将含氟烯键式单体聚合而成，也可以将含氟烯键式单体与不具有氟原子的烯键式单体聚合而成。
上述氟树脂优选具有来自下述含氟烯键式单体的重复单元，该含氟烯键式单体选自由氟化乙烯〔VF〕、四氟乙烯〔TFE〕、偏二氟乙烯〔VdF〕、三氟氯乙烯〔CTFE〕、六氟丙烯〔HFP〕、六氟异丁烯、CH2=CZ1(CF2)nZ2(式中，Z1为H或F，Z2为H、F或Cl，n为1～10的整数。)所表示的单体、CF2=CF-ORf1(式中，Rf1表示碳原子数为1～8的全氟烷基。)所表示的全氟(烷基乙烯基醚)〔PAVE〕、以及CF2=CF-O-CH2-Rf2(式中，Rf2表示碳原子数为1～5的全氟烷基。)所表示的烷基全氟乙烯基醚衍生物组成的组中的至少一种。
上述氟树脂可以具有来自不具有氟原子的烯键式单体的重复单元，从维持耐热性及耐化学药品性等的方面考虑，具有来自碳原子数为5以下的烯键式单体的重复单元也是优选形态之一。上述氟树脂还优选具有选自由乙烯、丙烯、1-丁烯、2-丁烯、氯化乙烯、偏二氯乙烯和不饱和羧酸组成的组中的至少一种非含氟烯键式单体。
作为上述氟树脂，优选为选自由聚四氟乙烯〔PTFE〕、聚三氟氯乙烯〔PCTFE〕、乙烯〔Et〕/TFE共聚物〔ETFE〕、Et/三氟氯乙烯〔CTFE〕共聚物、CTFE/TFE共聚物、TFE/HFP共聚物〔FEP〕、TFE/PAVE共聚物〔PFA〕以及聚偏二氟乙烯〔PVdF〕组成的组中的至少一种，更优选为选自由PTFE、PCTFE、ETFE、CTFE/TFE共聚物、FEP和PFA组成的组中的至少一种氟树脂。
作为上述PTFE，只要具有非熔融加工性就没有特别限定，可以为均聚PTFE(ホモPTFE)，也可以为改性PTFE。
作为上述PAVE，可以举出全氟(甲基乙烯基醚)〔PMVE〕、全氟(乙基乙烯基醚)〔PEVE〕、全氟(丙基乙烯基醚)〔PPVE〕、全氟(丁基乙烯基醚)等，其中更优选PMVE、PEVE或PPVE。
作为上述烷基全氟乙烯基醚衍生物，优选Rf2是碳原子数为1～3的全氟烷基的物质，更优选为CF2=CF-O-CH2-CF2CF3。
上述氟树脂更优选为全氟聚合物，进一步优选为选自由PTFE、FEP和PFA组成的组中的至少一种。上述全氟聚合物为在构成聚合物主链的全部碳原子上键合了氟原子的聚合物。
上述氟树脂特别优选为可熔融加工的含氟聚合物，尤其优选为选自由PFA和FEP组成的组中的至少一种。
作为PFA没有特别限定，优选为含有TFE单元70摩尔%～99摩尔%与PAVE单元1摩尔%～30摩尔%的共聚物，更优选为含有TFE单元80摩尔%～98.5摩尔%与PAVE单元1.5摩尔%～20摩尔%的共聚物。TFE单元若小于70摩尔%，则机械物性有降低的倾向；若大于99摩尔%，则熔点过高，成型性有降低的倾向。上述PFA还优选为下述共聚物，该共聚物中，来自能够与TFE和PAVE共聚的单体的单体单元为0.1摩尔%～10摩尔%、TFE单元和PAVE单元合计为90摩尔%～99.9摩尔%。作为能够与TFE和PAVE共聚的单体，可以举出HFP、CZ3Z4=CZ5(CF2)nZ6(式中，Z3、Z4和Z5相同或不同，表示氢原子或氟原子；Z6表示氢原子、氟原子或氯原子；n表示2～10的整数。)所表示的乙烯基单体、以及CF2=CF-OCH2-Rf7(式中，Rf7表示碳原子数为1～5的全氟烷基。)所表示的烷基全氟乙烯基醚衍生物等。
作为FEP没有特别限定，优选为含有TFE单元70摩尔%～99摩尔%与HFP单元1摩尔%～30摩尔%的共聚物，更优选为含有TFE单元80摩尔%～97摩尔%与HFP单元3摩尔%～20摩尔%的共聚物。TFE单元若小于70摩尔%，则有机械物性降低的倾向；若高于99摩尔%，则熔点过高，有成型性降低的倾向。FEP还优选为下述共聚物，该共聚物中，来自能够与TFE和HFP共聚的单体的单体单元为0.1摩尔%～10摩尔%、TFE单元和HFP单元合计为90摩尔%～99.9摩尔%。作为能够与TFE和HFP共聚的单体，可以举出PAVE、烷基全氟乙烯基醚衍生物等。
上述共聚物中各单体的含量可以根据单体的种类将NMR、FT-IR、元素分析、荧光X射线分析适当组合来计算出。
本发明的防水生生物附着片材可以进一步根据需要含有添加剂类。作为这样的添加剂类没有特别限定，可以举出例如流平剂、固体润滑剂、颜料、光亮剂、填充剂、颜料分散剂、表面调节剂、粘度调节剂、紫外线吸收剂、光稳定剂、增塑剂、防发花剂、防擦伤剂、生物忌避剂、防霉剂(防徴剤)、抗菌剂、抗蚀剂、抗静电剂、硅烷偶联剂等。
本发明防水生生物附着片材的厚度优选为0.01mm～5mm、更优选为0.1mm～3mm。
本发明防水生生物附着片材的拉伸强度优选为15MPa～100MPa、更优选为20MPa～90MPa。
上述拉伸强度为利用JIS K6891所记载的方法进行测定而得到的值。
本发明的防水生生物附着片材具有柔软性，因而可应用于各种各样的场所。
本发明的防水生生物附着片材可通过利用公知方法对氟树脂进行成型来制造。从生产率的方面出发，适宜通过挤出成型、压缩成型或注射成型来制造。
本发明还涉及防水生生物附着面板，该面板包含基材、以及安装在上述基材上的上述防水生生物附着片材。
作为上述基材，可以举出聚酰亚胺、聚酰胺、聚碳酸酯、聚对苯二甲酸乙二醇酯、氯化乙烯、丙烯酸类树脂等各种塑料；金属；石棉板等建筑材料。
本发明的防水生生物附着面板中，出于防水生生物附着片材可以牢固地安装于基材的理由，优选在防水生生物附着片材与基材之间具有由含有粘接性化合物的组合物形成的粘接层。通过形成粘接层，可以提高防水生生物附着片材与基材的粘接性。作为粘接性化合物，可以举出例如：聚亚芳基硫醚、聚酰胺酰亚胺、聚酰胺(聚酰胺酸)、聚酰亚胺、聚醚砜、聚芳基砜、聚亚芳基醚酮、硅酮橡胶等硅酮系化合物、环氧树脂等。这些粘接性化合物可以仅使用一种，也可将两种以上合用。
本发明的防水生生物附着面板可以在工厂等进行制作。
本发明的防水生生物附着面板例如可如下制造：在本发明的防水生生物附着片材上预先涂布或粘贴含有粘接性化合物的组合物，将其安装于基材，由此来制造该面板。优选在涂布或粘贴含有粘接性化合物的组合物之前对防水生生物附着片材进行等离子体处理或电晕处理等前处理。
由于在本发明的防水生生物附着面板上安装有预先防水生生物附着片材，因而通过将其直接安装于要防止水生生物的附着的结构物，可长期抑制水生生物的附着，也容易在设置结构物的现场进行卸载安装。
本发明还涉及水中结构物，其特征在于，该水中结构物具备防水生生物附着片材。
作为水中结构物，不管是在海水中还是淡水中使用，可以举出各种结构物。此外还可为在水面使用的结构物。例如可示例出下述物品或结构物，但并不限于此。此外，所谓结构物不仅包括桥墩、水路等固定型建造物，还包括船舶等主要进行移动的建造物。
固定型：
桥梁、水泥预制板、消波块、防波堤、管道(パイプライン)等水中建筑物；
水门门扇、海上储罐、浮码头等港湾施设；
海底挖掘设备、海中通信电缆施设等海底作业施设；
导水路、覆水管、水室、取水口、放水口等火力、原子力、潮力、海洋温度差发电施设；
水池、水槽、给水塔、下水道、雨水管等给排水和储藏施设；
整体厨房、水洗便器、浴室、浴槽等家庭内设备
移动型：
船舶的吃水部或船底、潜水艇的外装、螺旋桨、推进器、锚等船舶结构物或附属物；
在水面或水中使用的物品
固定型：
定置网等鱼网、浮标、养鱼池(生簀)、绳子等渔业用物品；
覆水器、水室等火力、原子力、海洋温度差发电用物品；
海中(水中)电缆等海底(水底)敷设物品；
移动型：
水底拖网、绳钩等渔业用物品
本发明还涉及用于防止水生生物附着于水中结构物的方法，其特征在于，该方法包括将上述防水生生物附着片材安装于水中结构物的工序。
安装方法没有特别限定，可以将上述防水生生物附着片材直接安装于水中结构物，也可以将上述防水生生物附着片材安装于基材来制成防水生生物附着面板，之后将防水生生物附着面板安装于水中结构物。片材和面板也可使用接合剂安装于水中结构物，还可使用地脚螺栓等安装工具进行安装。
本发明还涉及防水生生物附着涂料，其特征在于，该涂料含有氟树脂。上述氟树脂中，可直接使用上述氟树脂作为可在本发明的防水生生物附着片材中使用的氟树脂。
本发明的防水生生物附着涂料即使对于复杂形状的结构物也可以以所期望的膜厚形成涂膜，可利用所形成的涂膜长期抑制水生生物在基材上的附着。
从能够容易地设置具有数百至数千微米厚度的涂膜的方面考虑，优选本发明的防水生生物附着涂料为粉体组合物。本发明的防水生生物附着涂料所含有的氟树脂的平均粒径优选为0.1μm～50μm。
上述平均粒径可以使用激光衍射式粒度分布测定机求出。
本发明的防水生生物附着涂料可以含有选自由聚酰胺酰亚胺〔PAI〕、聚酰胺以及聚酰胺酸(聚酰胺酸)组成的组中的至少一种含酰胺基聚合物。上述PAI为具有酰胺基与芳香环及酰亚胺基的缩聚物。作为上述PAI没有特别限定，例如，除现有公知的PAI外，还可使用通过对聚酰亚胺〔PI〕进行氧化而导入了酰胺基的物质。上述聚酰胺为在主链中具有酰胺键(-NH-C(=O)-)的缩聚物。作为上述聚酰胺没有特别限定，可以举出例如：尼龙6、尼龙66、尼龙11、尼龙12等脂肪族聚酰胺；聚对苯二甲酰对苯二胺、聚间苯二甲酰间苯二胺等芳香族聚酰胺等。上述聚酰胺酸为具有酰胺基、以及羧基或羧基的衍生物的缩聚物。作为上述聚酰胺酸没有特别限定，可以举出分子量为数千～数万的聚酰胺酸等。
本发明的防水生生物附着涂料优选含有聚亚芳基硫醚〔PAS〕、优选含有含酰胺基聚合物和PAS这两者。作为上述PAS没有特别限定，可以举出例如聚苯硫醚酮、聚苯硫醚砜、聚亚联苯基硫醚、聚苯硫醚〔PPS〕等，其中适于使用PPS。
上述PAS优选为上述含酰胺基聚合物与上述PAS合计量的1质量%～40质量%，上述氟树脂相对于涂料整体优选为50质量%～95质量%。
本发明的防水生生物附着涂料可以进一步根据需要含有添加剂类。作为这样的添加剂类没有特别限定，可以举出例如流平剂、固体润滑剂、颜料、光亮剂、填充剂、颜料分散剂、表面调节剂、粘度调节剂、紫外线吸收剂、光稳定剂、增塑剂、防发花剂、防擦伤剂、生物忌避剂、防霉剂(防徴剤)、抗菌剂、抗蚀剂、抗静电剂、硅烷偶联剂、防蜡剂(ワキ防止剤)、消光剂等。
本发明的水生生物附着防止涂料可通过将上述氟树脂与必要时的上述成分利用公知方法进行混合、分散来制造。
本发明还涉及防水生生物附着面板，该面板包含基材以及在上述基材上形成的涂膜，该涂膜由上述防水生生物附着涂料形成。
作为上述基材，可以举出聚酰亚胺、聚酰胺、聚碳酸酯、聚对苯二甲酸乙二醇酯、氯化乙烯、丙烯酸类树脂等各种塑料；金属；石棉板等建筑材料。
本发明的防水生生物附着面板中，优选在涂膜与基材之间具有由含有粘接性化合物的组合物(其中不包括氟树脂。)形成的粘接层。通过形成粘接层，可以提高涂膜与基材的粘接性。作为粘接性化合物，可以举出例如：聚亚芳基硫醚、聚酰胺酰亚胺、聚酰胺(聚酰胺酸)、聚酰亚胺、聚醚砜、聚芳基砜、聚亚芳香基醚酮、硅酮橡胶等硅酮系化合物、环氧树脂等。这些粘接性化合物可以仅使用一种，也可将两种以上合用。含有粘接性化合物的组合物可以为液态组合物，也可以为粉体组合物。
本发明的防水生生物附着面板可如下进行制造：通过在基材上涂布含有粘接性化合物的组合物来设置粘接层，在粘接层上涂布本发明的防水生生物附着涂料，由此来制造该面板。
本发明的防水生生物附着面板更优选包含基材、在基材上形成的粘接层(该粘接层由含有氟树脂、含酰胺基聚合物和PAS的液态组合物形成)、以及在粘接层上形成的涂膜(该涂膜由本发明的防水生生物附着涂料形成)。
涂膜的膜厚优选为100μm～5000μm。上述膜厚为利用JIS K5600的方法进行测定而得到的值。
本发明还涉及水中结构物，该水中结构物具备由上述防水生生物附着涂料形成的涂膜。水中结构物如上文所详述。
本发明还涉及用于防止水生生物附着于基材或水中结构物的方法，其特征在于，该方法包括将上述防水生生物附着涂料涂布至基材或水中结构物的工序。
涂布防水生生物附着涂料的方法没有特别限制，可利用公知的方法进行涂布。在防水生生物附着涂料为粉体组合物的情况下，静电涂布法为适宜的。
【实施例】
接下来举出实施例对本发明进行说明，但本发明并不仅限定于所述实施例。
制备例1
使用新东工业社制造的碾压机BSC-25型对通过悬浮聚合得到的四氟乙烯-全氟烷基乙烯基醚共聚物(TFE/PAVE=98/2(摩尔比)、熔点304℃)进行压缩，使所得到的片材为真比重的90%以上，接下来利用破碎(解砕)机破碎成约10mm径，使用奈良机械制作所社制造的粉碎机Cosmomizer N-1型对所得破碎物进行粉碎。这样得到的粉碎品A的平均粒径为56μm。
制备例2
使用新东工业社制造的碾压机BSC-25型对通过悬浮聚合得到的四氟乙烯-六氟丙烯共聚物(TFE/HFP=93/7(摩尔比)、熔点268℃)进行压缩，使所得到的片材为真比重的90%以上，接下来利用破碎机破碎成约10mm径，使用奈良机械制作所社制造的粉碎机Cosmomizer N-1型对所得破碎物进行粉碎。这样得到的粉碎品B的平均粒径为34μm。
实施例1
在SUS304的面板基材上涂布包含四氟乙烯-全氟烷基乙烯基醚共聚物、聚苯硫醚和聚酰胺酰亚胺的液态组合物(TFE-PAVE共聚物/聚苯硫醚/聚酰胺酰亚胺=80/5/15(质量比))，从而来设置粘接层(干燥膜厚52μm)。在其上通过静电涂布法反复涂布3次粉碎品A，从而来设置涂膜(膜厚210μm)。由此来制作试验面板A。
实施例2
在SUS304的面板基材上涂布包含四氟乙烯-六氟丙烯共聚物、聚苯硫醚和聚酰胺酰亚胺的液态组合物(TFE-HFP共聚物/聚苯硫醚/聚酰胺酰亚胺=80/5/15(质量比))，从而来设置粘接层(干燥膜厚55μm)。在其上通过静电涂布法反复涂布3次粉碎品B，从而来设置涂膜(膜厚196μm)。由此来制作试验面板B。
实施例3
在施以电晕处理的由四氟乙烯-全氟烷基乙烯基醚共聚物形成的片材(TFE/PAVE=98/2(摩尔比)、厚度0.1mm)上涂布丙烯酸系粘合剂(DA-400、商品名、Front研究所社制造)，将其粘贴在石棉板的面板基材上。由此来制作试验面板C。
实施例4
在施以电晕处理的由四氟乙烯-六氟丙烯共聚物形成的片材(TFE/HFP=93/7(摩尔比)、厚度0.1mm)上涂布丙烯酸系粘合剂(DA-400、商品名、Front研究所社制造)，将其粘贴在石棉板的面板基材上。由此来制作试验面板D。
比较例1
在SUS304的面板基材上，首先涂布Zeffle隔热涂料底漆(大金工业社制造)作为含有粘接性化合物的组合物，由此设置粘接层(干燥膜厚41μm)。在其上涂布GK570(大金工业社制造固化型树脂清漆)来设置涂膜(膜厚34μm)。由此来制作试验面板E。
比较例2
在SUS304的面板基材上上，首先涂布Zeffle隔热涂料底漆(大金工业社制造)作为含有粘接性化合物的组合物，由此设置粘接层(干燥膜厚47μm)。在其上涂布在GK570(大金工业社制造固化型树脂清漆)100重量份中添加了二甲基硅油4重量份而成的物质来设置涂膜(膜厚32mm)。由此来制作试验面板F。
比较例3
在SUS304的面板基材上，首先涂布蚀刻底层涂料H(中国涂料社制造)作为含有粘接性化合物的组合物，由此设置粘接层(干燥膜厚38μm)。在其上涂布Bioclean DX(CHUGOKU MARINE PAINTS,Ltd.制造有机硅树脂系组合物)来设置涂膜(膜厚80μm)。由此来制作试验面板G。
防污性评价：
为了防止腺介幼虫(キプリス幼生)(在内湾海域的水中结构物上大量附着的纹藤壶的附着期幼虫)在聚苯乙烯容器内侧的附着，设置目径(目合い)为100μm的浮游生物网，之后在网内侧投入试验面板、海水、腺介幼虫。幼虫数在每一容器内为20～30固体，将容器放置在室温20℃的向阳处(晴所)。投入幼虫7天后将试验面板从容器中取出，通过目视确认幼虫所附着部分占试验面板的面积比例。其结果列于表1。
【表1】
| 试验面板 | 附着状况(%) | |
| 实施例1 | A | 0 |
| 实施例2 | B | 0 |
| 实施例3 | C | 0 |
| 实施例4 | D | 0 |
| 比较例1 | E | 21 |
| 比较例2 | F | 10 |
| 比较例3 | G | 14 |
【工业实用性】
本发明的防水生生物附着片材、防水生生物附着涂料以及防水生生物附着面板可安装于发电厂的导水路管或复水管以及取水口或放水口、港湾设施、浮标、管道、桥梁、海底基地、海底油井掘进设备、船舶等水中结构物。
Claims (15)
1.一种防水生生物附着片材，其特征在于，该片材含有氟树脂。
2.如权利要求1所述的防水生生物附着片材，其中，氟树脂为全氟聚合物。
3.如权利要求1或2所述的防水生生物附着片材，其中，氟树脂为可熔融加工的含氟聚合物。
4.如权利要求1、2或3所述的防水生生物附着片材，其中，氟树脂为四氟乙烯和全氟(烷基乙烯基醚)的共聚物、或者为四氟乙烯和六氟丙烯的共聚物。
5.一种防水生生物附着面板，其中，该面板包含基材以及安装在上述基材上的权利要求1、2、3或4所述的防水生生物附着片材。
6.一种水中结构物，其特征在于，该水中结构物具备权利要求1、2、3或4所述的防水生生物附着片材。
7.用于防止水生生物附着于水中结构物的方法，其特征在于，该方法包括将权利要求1、2、3或4所述的防水生生物附着片材安装于水中结构物的工序。
8.一种防水生生物附着涂料，其特征在于，该涂料含有氟树脂。
9.如权利要求8所述的防水生生物附着涂料，其中，该涂料为粉体组合物。
10.如权利要求8或9所述的防水生生物附着涂料，其中，氟树脂为全氟聚合物。
11.如权利要求8、9或10所述的防水生生物附着涂料，其中，氟树脂为可熔融加工的含氟聚合物。
12.如权利要求8、9、10或11所述的防水生生物附着涂料，其中，氟树脂为四氟乙烯和全氟(烷基乙烯基醚)的共聚物、或者为四氟乙烯和六氟丙烯的共聚物。
13.一种防水生生物附着面板，其中，该面板包含基材以及在上述基材上形成的涂膜，该涂膜由权利要求8、9、10、11或12所述的防水生生物附着涂料形成。
14.一种水中结构物，其中，该水中结构物具备由权利要求8、9、10、11或12所述的防水生生物附着涂料形成的涂膜。
15.用于防止水生生物附着于水中结构物的方法，其特征在于，该方法包括涂布权利要求8、9、10、11或12所述的防水生生物附着涂料的工序。