CN103339713B - 用于降低soi结构的器件层中的金属含量的方法以及通过该方法制造的soi结构 - Google Patents
用于降低soi结构的器件层中的金属含量的方法以及通过该方法制造的soi结构 Download PDFInfo
- Publication number
- CN103339713B CN103339713B CN201280007174.XA CN201280007174A CN103339713B CN 103339713 B CN103339713 B CN 103339713B CN 201280007174 A CN201280007174 A CN 201280007174A CN 103339713 B CN103339713 B CN 103339713B
- Authority
- CN
- China
- Prior art keywords
- silicon
- device layer
- layer
- silicon device
- insulated substrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
Claims (43)