CN101870808B - 碳纳米管聚氨酯复合材料的制备方法 - Google Patents
碳纳米管聚氨酯复合材料的制备方法 Download PDFInfo
- Publication number
- CN101870808B CN101870808B CN2010102026188A CN201010202618A CN101870808B CN 101870808 B CN101870808 B CN 101870808B CN 2010102026188 A CN2010102026188 A CN 2010102026188A CN 201010202618 A CN201010202618 A CN 201010202618A CN 101870808 B CN101870808 B CN 101870808B
- Authority
- CN
- China
- Prior art keywords
- carbon nano
- preparation
- carbon nanotube
- composite material
- nano tube
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Description
Claims (6)