CN101117772A - 高强度直涂式刀刮法篷布的制造方法 - Google Patents

高强度直涂式刀刮法篷布的制造方法 Download PDF

Info

Publication number
CN101117772A
CN101117772A CNA2007100705568A CN200710070556A CN101117772A CN 101117772 A CN101117772 A CN 101117772A CN A2007100705568 A CNA2007100705568 A CN A2007100705568A CN 200710070556 A CN200710070556 A CN 200710070556A CN 101117772 A CN101117772 A CN 101117772A
Authority
CN
China
Prior art keywords
tarpaulin
agent
coated
manufacture method
strength direct
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2007100705568A
Other languages
English (en)
Other versions
CN100572654C (zh
Inventor
叶雪康
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Jinda New Material Co ltd
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNB2007100705568A priority Critical patent/CN100572654C/zh
Publication of CN101117772A publication Critical patent/CN101117772A/zh
Application granted granted Critical
Publication of CN100572654C publication Critical patent/CN100572654C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种高强度直涂式刀刮法篷布的制造方法，按下列步骤进行：(1)将一定重量份的组份包括PVC糊树脂、增塑剂、稳定剂、填料、阻燃剂及颜料混合成涂层剂；(2)将混合成的涂层剂研磨和过滤；(3)每100kg涂层剂中加入1～5kg交联剂，均匀涂布于基布上，然后进行烘干处理；(4)经塑化成型后用表面处理剂进行表面处理。本发明所制成的篷布具有防水、防油、防污、阻燃、耐老化、抗剥离等性能，可以用作车厢篷布，车厢侧帘布，开顶集装箱布；火车篷布，轮船篷布；建筑材料，应用于软性屋顶的建筑材料，作成超级市场、体育场馆，景观建筑；用于军事领域，制作成篷房，供野战部队临时休息，战时作指挥部等。

Description

高强度直涂式刀刮法篷布的制造方法
技术领域
本发明属于纺织材料技术领域，具体属于一种直接涂层法篷布的制造方法。
背景技术
篷帆布在人们的日常生产生活中发挥着重要的作用，从仓储用布，到车船用布，到军事野营，都需要用到篷帆布，但目前市场上的篷布产品大多存在断裂、撕裂强度不高、防火性能差、柔软度不够、自清洁性能不好等缺点，客户期待强度高、阻燃性好，拉断、撕裂强度高、具有表面自清洁功能的新产品出现。因此老的产品急需进行升级换代，以满足客户的使用要求，应用于软体车厢、软性屋顶和军事装备等不断拓宽的新的应用领域中。
发明内容
为弥补此类产品在使用中存在的诸多不足，本发明提供了一种高强度直涂式刀刮法篷布的制造方法。
为了解决以上技术问题，本发明采用以下技术方案：一种高强度直涂式刀刮法篷布的制造方法，其特征在于它包括下列步骤：
1)将下列重量份的组份混合成涂层剂：
PVC糊树脂    100份
增塑剂       50～100份
稳定剂       1～5份
填料         5～8 0份
阻燃剂       3～25份
颜料         1～8份
2)将混合成的涂层剂研磨和过滤；
3)每100kg涂层剂中加入1～5kg交联剂，均匀涂布于基布上，然后进行烘干处理；
4)经塑化成型后用表面处理剂进行表面处理。
涂层剂涂覆时，涂布量为100～350g/m2，烘干时的温度为140℃～200℃，塑化时的温度为150℃～210℃。
为了增强防水、防油、防污、阻燃、耐老化、抗剥离的性能，在步骤3)烘干处理后，再涂覆一层步骤2)制得的涂层剂，并进行烘干处理。
PVC糊树脂的国内现有较多品种，如P440，PSM-31，R1069等，可以使用其中的一种，或者同时使用其中的几种，但总重量不变。交联剂中异氰酸酯基团的含量为3％-5％。
增塑剂可以为DOP，DINP或其它品种，增塑剂的加入，可以降低PVC分子链间的作用力，使PVC塑料的玻璃化温度、流动温度与所含微晶的熔点均降低，增塑剂可提高树脂的可塑性，使制品柔软、耐低温性能好。
稳定剂国内也有多种牌号与品种，根据产品的环保要求，稳定剂为液体钡锌稳定剂、液体钙锌稳定剂、有机锡稳定剂中的一种或两种以上。聚氯乙烯在高温时会产生热降解、变色和机械性能恶化，为防止性能下降，需添加稳定剂。其作用机理具体有：1.吸收中和HC1，抑制其自动催化作用。2.置换PVC分子中不稳定的烯丙基氯原子或叔碳氯原子，抑制脱PVC。3.与多烯结构发生加成反应，破坏大共轭体系的形成，减少着色。4.捕捉自由基，阻止氧化反应。
填料可以是500目以上至10000目的碳酸钙，也可以是同样规格的氢氧化铝。填料是用以改善复合材料性能(如硬度、刚度及冲击强度等)，并能降低成本的固体添加剂。填料的作用：①降低成型制品的收缩率，提高制品的尺寸稳定性、表面光洁度、平滑性以及平光性或无光性等；②树脂粘度有效的调节剂；③可满足不同性能要求，提高耐磨性、改善导电性及导热性④可提高颜料的着色效果；5、有增容作用，可降低成本，提高产品在市场上的竞争能力。
阻燃剂在本项目中为复配阻燃剂，可以采用三氧化二锑和硼酸锌复配，重量份配比为硼酸锌：三氧化二锑＝1～1.5∶2.5～3.5，硼酸锌是一种多功能添加剂，具有阻燃、成炭、抑烟、抑阴燃和防止生成熔滴等多种功效，与三氧化二锑复配使用具有化学协同效应，可以使产品的阻燃指标达到不燃。
本配方中所使用颜料为钛白粉、酞菁蓝、酞菁绿、紫B、中铬黄、柠檬黄、炭黑、鲜丽红等中的一种或两种以上。颜料的加入可以使制止品做成各种颜色，会因加入量的不同而得到不同的颜色，制作成多姿多彩的花色和品种。
本产品的基布优选涤纶机织布，表面处理剂为PVDF表面处理剂或丙烯酸酯表面处理剂。
本发明所制成的篷布具有防水、防油、防污、阻燃、耐老化、抗剥离等卓越的性能。可以广泛用作车厢篷布，车厢侧帘布，开顶集装箱布；火车篷布，轮船篷布；建筑材料，应用于软性屋顶的建筑材料，作成超级市场、体育场馆，景观建筑等；应用于军事领域，制作成篷房，供野战部队临时休息，战时作指挥部等。因此具有较好的经济效益和社会效益。
具体实施方式
下面结合实施示例对本发明作进一步说明。
实施例1：一种高强度直涂式刀刮法篷布的制造方法，包括下列步骤：
1)、将下列重量组份混合成涂层剂：
PVC糊树脂(PSM-31)  100份
增塑剂(DOP)        70份
钡锌稳定剂         2.5份
碳酸钙             30份
三氧化二锑         5份
硼酸锌             2份
钛白粉    4份
2)将混合成的涂层剂研磨和过滤，过滤选用80目尼龙网；
3)将1000D*1000D密度为8*8根/厘米的涤纶机织布通过放卷机构匀速地通过涂层机，每100kg涂层剂中加入1.8kg交联剂，交联剂中异氰酸酯基团(-NCO)含量为3％，涂布量为105g/m2，均匀涂布于涤纶机织布上，经烘箱进行烘干处理，烘干的温度为140℃；
4)再经烘箱塑化成型后用进行表面处理，塑化时的温度为200℃，表面处理剂为丙烯酸酯类喷绘表处剂，即得成品。
实施例2：一种高强度直涂式刀刮法篷布的制造方法，包括下列步骤：
1)、将下列重量组份混合成涂层剂：
PVC糊树脂(R1069)  100份
增塑剂(DOP)       68份
钙锌稳定剂        2.5份
碳酸钙            40份
三氧化二锑        11份
硼酸锌            6.5份
酞菁蓝            8份
2)将混合成的涂层剂研磨和过滤，过滤选用100目尼龙网；
3)将1000D*1000D密度为8*8根/厘米的涤纶机织布通过放卷机构匀速地通过涂层机，每100kg涂层剂中加入5kg交联剂，交联剂中异氰酸酯基团(-NCO)含量为4％，均匀涂布于涤纶机织布上，经烘箱进行烘干处理，再经二涂涂台处，再涂覆一层步骤2)制得的涂层剂(即没有加入交联剂的涂层剂)，并进行烘干处理，烘干的温度为200℃；涂布量为200g/m2，再经烘箱塑化成型后用进行表面处理，塑化时的温度为150℃，表面处理剂为丙烯酸酯类喷绘表处剂，即得成品。
实施例3：一种高强度直涂式刀刮法篷布的制造方法，包括下列步骤：
1)、将下列重量组份混合成涂层剂：
PVC糊树脂(P440)    100份
增塑剂(DINP)       75份
有机锡稳定剂       2份
氢氧化铝           30份
硼酸锌             4份
三氧化二锑         8份
紫B                1.5份
2)将混合成的涂层剂研磨和过滤，过滤选用40目尼龙网；
3)将1000D*1000D密度为8*8根/厘米的涤纶机织布通过放卷机构匀速地通过涂层机，每100kg涂层剂中加入3kg交联剂，交联剂中异氰酸酯基团(-NCO)含量为5％，均匀涂布于涤纶机织布上，经烘箱进行烘干处理，再经二涂涂台处，再涂覆一层步骤2)制得的涂层剂(即没有加入交联剂的涂层剂)，并进行烘干处理，烘干的温度为180℃；涂布量为250g/m2，再经烘箱塑化成型后用进行表面处理，塑化时的温度为210℃，表面处理剂为PVDF表面处理剂，即得成品。
所制产品的质量指标如下：
1、厚度：0.5mm
2、断裂强度：2500N/5cm(参照ISO13934-1-1999)
3、剥离强度：无法全过程剥离
4、重量：600g/m2
5、撕破强力：25N/5cm(参照ISO13937-2-2000)
6、阻燃性能：不燃(参照GB/T8410-1994)
产品经丁酮浸泡5min不被丁酮腐蚀。

Claims (10)

1.一种高强度直涂式刀刮法篷布的制造方法，其特征在于它包括下列步骤：
1)将下列重量份的组份混合成涂层剂：
PVC糊树脂  100份
增塑剂     50～100份
稳定剂     1～5份
填料       5～80份
阻燃剂     3～25份
颜料       1～8份
2)将混合成的涂层剂研磨和过滤；
3)每100kg涂层剂中加入1～5kg交联剂，均匀涂布于基布上，然后进行烘干处理；
4)经塑化成型后用表面处理剂进行表面处理。
2.如权利要求1所述的一种高强度直涂式刀刮法篷布的制造方法，其特征在于：在步骤3)烘干处理后，再涂覆一层步骤2)制得的涂层剂，并进行烘干处理。
3.如权利要求1或2所述的一种高强度直涂式刀刮法篷布的制造方法，其特征在于：涂层剂涂覆时，涂布量为100～350g/m2，烘干时的温度为140℃～200℃，塑化时的温度为150℃～210℃。
4.如权利要求1或2所述的一种高强度直涂式刀刮法篷布的制造方法，其特征在于：所述的基布优选涤纶机织布。
5.如权利要求1或2所述的一种高强度直涂式刀刮法篷布的制造方法，其特征在于：所述的填料为碳酸钙或氢氧化铝。
6.如权利要求1或2所述的一种高强度直涂式刀刮法篷布的制造方法，其特征在于：所述交联剂中异氰酸酯基团的含量为3％-5％。
7.如权利要求1或2所述的一种高强度直涂式刀刮法篷布的制造方法，其特征在于：所述的阻燃剂为三氧化二锑、硼酸锌的混合剂，重量份配比为硼酸锌∶三氧化二锑＝1～1.5∶2.5～3.5。
8.如权利要求1或2所述的一种高强度直涂式刀刮法篷布的制造方法，其特征在于：所述的颜料为钛白粉、酞菁蓝、酞菁绿、紫B、中铬黄、柠檬黄、炭黑、鲜丽红中的一种或两种以上。
9.如权利要求1或2所述的一种高强度直涂式刀刮法篷布的制造方法，其特征在于：所述的表面处理剂为PVDF表面处理剂或丙烯酸酯表面处理剂。
10.如权利要求1或2所述的一种高强度直涂式刀刮法篷布的制造方法，其特征在于：所述的稳定剂为液体钡锌稳定剂、液体钙锌稳定剂、有机锡稳定剂中的一种或两种以上。
CNB2007100705568A 2007-08-31 2007-08-31 高强度直涂式刀刮法篷布的制造方法 Expired - Fee Related CN100572654C (zh)